Prediction Model of Shrinkage Crack Propagation in Cross-Section of Timber Components

Abstract

Shrinkage cracks severely affect the safety of wood structures. Therefore, the moisture stress distribution of shrinkage cracks should be analyzed, and the interface crack depth of wood components predicted. In this paper, the equilibrium conditions, physical conditions, geometric conditions, and coordination equations of the disk humidity stress under a moisture content gradient Δw are deduced by referring to the elastic analytical solution model of temperature stress. Moreover, the humidity stress distribution equation is established, which is verified via the finite element method. The critical water content and shrinkage crack depth prediction models are further deduced based on the humidity stress distribution. The usability of the model is further verified using the test data of actual engineered wood components. The results demonstrate that the moisture stress is not determined by the initial moisture content W_i, equilibrium moisture content W_e, or member size but by moisture content gradient Δw. The shrinkage crack prediction model of wood components in cross-section can be applied to actual engineering prediction to provide a theoretical basis for the reinforcement measures and safety evaluation of wood structures.

1. Introduction

Timber is a biopolymeric, hygroscopic, and anisotropic composite material. Shrinkage cracks are commonly observed in wood buildings, as shown in Figure 1. The crack depth in cross-section can significantly affect the durability of timber components. Generally, the generation and expansion of shrinkage cracks involve the following three steps, as illustrated in Figure 2: a moisture content gradient Δw caused by environmental change, humidity stress distribution caused by uneven dimensional changes in different directions, and shrinkage cracks.

Generally, the humidity stress distribution is critical for the further analysis of shrinkage cracks. So far, wood shrinkage experiments for testing the humidity stress distribution have garnered much attention. Kang [1] applied the ring slice method to study the relationship between the radial moisture content distribution and chordwise strain of a tree disc under high-frequency vacuum drying and concluded that cracking is mainly related to the radial distribution of moisture content. Svensson [2] measured the radial humidity stress distribution of Norway spruce under different moisture contents and concluded that the humidity stress inside the wooden component is highly correlated with the relative humidity history, and the change in humidity generates larger humidity stress inside the component. Jönsson [3,4,5], similar to Svensson, conducted a sample test and measured the humidity stress inside each sample via a nondestructive testing method and cut strip release method. The results demonstrated that a change in relative humidity leads to a change in the humidity stress on the outer surface of the wood from 0.66 MPa to 0.34 MPa, whereas the change in the internal humidity stress varies from −0.11 MPa to 0.85 MPa. Moreover, the maximum humidity tensile stress exceeds the transverse grain tensile strength of the wood. Gereke [6] studied the humidity stress in a cross-laminated timber (CLT) wood board via the cutting strip release method and finite element simulation and found that the material of the CLT intermediate layer has a significant effect on its internal humidity stress. Fragiacomo [7] studied the influence of different types of environments on the internal humidity stress of the components. The results demonstrated that the change in relative humidity in the natural environment can cause high-humidity stresses inside components, even exceeding the transverse grain tensile strength of wood, resulting in cracking. After studying the surface hardening and residual deformation of beech during drying, Morihiko [8] found the surface and inner layers of wood to be under tensile and compression deformation at the beginning of drying, respectively. Mohager [9] conducted long-term loading tests on glulam beams processed from pine under cyclic changes in external relative humidity (15–90%). Notably, the change in humidity has an influence on the deformation recovery after unloading. Cheng [10] studied the changes in internal moisture content, strain, and stress during wood curing. During the curing period, the wood was placed in the constant temperature and humidity test environment box, with the temperature and humidity setting of 65 °C and 70%, respectively. The results demonstrated that wood curing treatment reduces the difference between moisture content and internal stress in wood. Gao [11] studied the stress distribution through humidity cycling experiments on larch and sylvestris. Arends [12] studied the effect of asymmetric moisture distribution on the change in board stress. Moreover, the author designed experiments to derive the moisture diffusion coefficient and linear hygroscopic expansion coefficient of wood to analyze the stress induced by the exposure of one side of the oak board to moisture. Liu [13] studied the effect of relative humidity on the shrinkage stress in elm wood during drying. The results demonstrated that the shrinkage stress gradually increases during drying and tends to stabilize after peaking.

However, theoretical analyses of the humidity stress distribution in the cross-sections of timber components remain scarce. Wang [14] investigated the relationship between drying stress and cracks from a microscopic perspective and found that wood is prone to stress concentration during drying. When the drying stress exceeds the tensile strength of the wood, the wood will crack. Kawa [15] described the rheological properties of wood through a viscoelastic anisotropic stress–strain relationship and established a stress function with free shrinkage, actual shrinkage, and inelastic strain as parameters. Chen [16] applied the Luikov heat and mass transfer model to perform finite element analysis on the temperature and humidity stress of the horizontal grain caused by cyclic changes in ambient temperature and humidity in glulam straight and curved beams. The calculation revealed that the glulam beams are subject to additional stresses due to changes in ambient temperature and humidity, the maximum stress of temperature stress is 0.016 MPa, and the humidity stress can reach 2.6 MPa. Gereke [17] applied a three-dimensional material model considering elastic deformation, moisture-induced expansion, and mechanical adsorption creep to study the effect of material parameters on the numerical simulation results. They further analyzed the stress caused by changes in water content. Angst [18] numerically simulated the distribution and development of moisture-induced stress in the cross-section of glulam during the moisture absorption process and found that the local stress was significantly greater than the average stress. Gao [11] established a finite element model based on the wood humidity cycle test and deduced a formula for calculating the temperature and humidity stress of the wood, and the results of the two were in good agreement. Arends [19] utilized the diffusion equation and linear elasticity theory to analyze the stress distribution caused by a single-side exposure of an oak board to moisture.

More recently, researchers have started to pay attention to the contribution of wood shrinkage cracking. Zhao [20] dried a 30 mm thick birch tray at a constant temperature of 40 °C and 60 °C and gradually decreasing relative humidity. The author also studied its drying characteristics (drying curve and rate, drying curve and moisture content gradient of heartwood and sapwood, and water content and strain distribution along the radial direction) and drying cracking characteristics (generation period, location, morphology). The research demonstrated that the roundness and cross-sectional area of the tree disc are the main factors affecting the total crack length and the average crack width. Fan [21] conducted a tracking test of the air-drying process in larch and evaluated the changes in wood moisture content and shrinkage cracks with time. Ample statistics on the position, shape, and depth of shrinkage cracks in the components were generated, and a large amount of test data were accumulated. Based on the experimental data of Fan, Wang [22] obtained the variation law of the relative depth of lateral shrinkage cracks with water content. Angellier [23] conducted creep fracture tests on small specimens of double cantilever beams made of Douglas fir and white fir. Initial cracks with an initial length of 50 mm were set at the left end of each 700 mm long specimen, and they were placed in an environment where the temperature was 25 °C, whereas the relative humidity was periodically changed between 40% and 90%. The relationship between the crack length, moisture content of the specimen, and time during the test was established. The results demonstrated that the starting point of crack propagation occurred in the dehumidification stage. The white fir broke almost completely after three drying and wetting cycles, whereas the Douglas fir was not completely destroyed after more than four cycles. Chen [24] studied moisture transfer and the formation and propagation of cross-section shrinkage cracks in six cylindrical Anhui fir trees in a dry environment. Different specimens with cracks at the same position had almost the same crack growth rate, although the crack initiation time was different.

The aforementioned literature reveals that the humidity stress distribution and prediction of shrinkage crack are very complicated. Although the research results collected by some scholars are extensive, the following shortcomings persist. (1) Notably, most of the abovementioned studies treated the influencing factors of humidity stress. However, cross-sectional theoretical analytical models or even related approximate models are almost nonexistent. (2) Generally, the crack depth of wood components is roughly predicted by testing actual engineering components. However, a model for predicting crack depth according to environmental and material factors has yet to be established. (3) Some inaccurate shrinkage crack depth prediction models have not been verified using tests or actual engineering tracking data.

Considering the prediction of shrinkage cracks in cross-section and the above gaps, this article is structured as follows: In Section 2, an accurate humidity stress distribution analytical solution is derived in detail and verified via ABAQUS. Simultaneously, the prediction expressions of critical moisture content gradient and dry shrinkage crack depth are proposed in Section 3. The shrinkage crack depth prediction model is supported by practical wood component detection in Section 4. Finally, conclusions from this study are highlighted in Section 5.

2. Humidity Stress Distribution

An accurate humidity stress distribution expression analysis is a prerequisite for an efficient prediction model of shrinkage crack propagation in cross-section—specifically, an analytical solution.

2.1. Analytical Solution of Stress Distribution

Assuming that the water content drops uniformly by Δw, the cross-section shrinks uniformly from the dotted line to the solid line, as shown in Figure 3. The sector block with the included angle θ, outer side of the section δ_R(R) = Rα_RΔw, corresponding deformation value of the hoop during radial contraction (the difference between the dashed line and the solid line in the sector range) δ′_T(R) = Rθ − (R − δ_R)θ = δRθ = Rθα_RΔw, and tangential contraction value δ_T(R) = Rθα_TΔw are considered.

The radial compressive stress in the surrounding material should be 0 (ρ = R). The smaller the ρ value is, the larger the compressive stress value (stress increment dσ_R > 0) and compressive deformation value. Moreover, radial compression deformation reduces the difference between the total radial deformation (shrinkage deformation and stress deformation) and the tangential shrinkage deformation, thus reducing the tangential tensile stress. When ρ < ρ₀, the radial compressive stress increment dσ_R < 0, and the tangential tensile stress transforms into compressive stress. The compressive stress always acts in the radial direction, and its value gradually increases from 0 on the outside.

At the position ρ = ρ₀, the circumferential shrinkage deformation is equal to the sum of the radial shrinkage deformation and the compression deformation. When ρ < ρ₀, the sum of the radial shrinkage deformation and the compression deformation is greater than the tangential shrinkage deformation, and the tangential direction must have compression deformation to meet the deformation coordination condition.

Taking the microelement as an example (as shown in Figure 3c), the equilibrium differential equation and the deformation coordination equation should be established and the physical conditions (stress–strain relationship and dry shrinkage–moisture content relationship, both of which are linear relationships) applied. Notably, the radial shrinkage deformation at the ρ position can be expressed as δ_R(ρ) = ρα_RΔw (in the case of uniform water content distribution), but the compression deformation needs to be integrated from 0 to R. The tangential direction is uniform due to axial symmetry, regardless of whether the deformation is shrinkage or stretching. When α_R = α_T, the uniform shrinkage meets the deformation coordination condition, and no tangential tensile stress occurs. Because α_T > α_R, the tangential shrinkage deformation is greater than the uniform shrinkage deformation, and tensile deformation must be present to meet the deformation coordination condition.

2.1.1. Balance Condition

The radial force balance condition (pull is positive) is established according to the force analysis of the microelement body in Figure 3c, as given in Equation (1).

$$\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }=\frac{{\sigma }_{\mathrm{T}}-{\sigma }_{\mathrm{R}}}{\rho }, {\sigma }_{\mathrm{T}}=\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+{\sigma }_{\mathrm{R}}$$

(1)

2.1.2. Constitutional Relationship

The force strain in the radial and circumferential directions in orthotropic materials is shown in Equation (2).

$$\left\{\begin{array}{l} {\epsilon }_{\mathrm{R}}=\frac{{\sigma }_{\mathrm{R}}-{\nu }_{\mathrm{RT}}{\sigma }_{\mathrm{T}}}{E_{\mathrm{R}}}=\frac{{\sigma }_{\mathrm{R}}}{E_{\mathrm{R}}}-\frac{{\nu }_{\mathrm{RT}}}{E_{\mathrm{R}}}\left[\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+{\sigma }_{\mathrm{R}}\right]\Rightarrow {\epsilon }_{\mathrm{R}}=\frac{(1-{\nu }_{\mathrm{RT}}){\sigma }_{\mathrm{R}}}{E_{\mathrm{R}}}-\frac{{\nu }_{\mathrm{RT}}}{E_{\mathrm{R}}}\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }\\ {\epsilon }_{\mathrm{T}}=\frac{{\sigma }_{\mathrm{T}}-{\nu }_{\mathrm{TR}}{\sigma }_{\mathrm{R}}}{E_{\mathrm{T}}}=\frac{\rho }{E_{\mathrm{T}}}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+\frac{{\sigma }_{\mathrm{R}}}{E_{\mathrm{T}}}-\frac{{\nu }_{\mathrm{TR}}{\sigma }_{\mathrm{R}}}{E_{\mathrm{T}}}\Rightarrow {\epsilon }_{\mathrm{T}}=\frac{\rho }{E_{\mathrm{T}}}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+\frac{{\sigma }_{\mathrm{R}}(1-{\nu }_{\mathrm{TR}})}{E_{\mathrm{T}}}\end{array}\right.$$

(2)

The radial shrinkage deformation δ_R,sh(ρ) and the radial force deformation are expressed by Equations (3) and (4).

$${\delta }_{\mathrm{R},\mathrm{sh}}(\rho )={\alpha }_{\mathrm{R}}{\displaystyle {\int }_o^{\rho }\Delta w(t)\mathrm{d}r}=\rho {\alpha }_{\mathrm{R}}\Delta w\left(t\right)$$

(3)

$$\begin{array}{l} {\delta }_{\mathrm{R},\mathrm{F}}={\displaystyle {\int }_0^{\rho }{\epsilon }_{\mathrm{R}}(r)}\mathrm{d}r\\ \Rightarrow {\delta }_{\mathrm{R},\mathrm{F}}=\frac{(1-{\nu }_{\mathrm{RT}})}{E_{\mathrm{R}}}{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}-\frac{{\nu }_{\mathrm{RT}}}{E_{\mathrm{R}}}{\displaystyle {\int }_0^{\rho }r\mathrm{d}{\sigma }_{\mathrm{R}}}\\ \Rightarrow {\delta }_{\mathrm{R},\mathrm{F}}=\frac{(1-{\nu }_{\mathrm{RT}})}{E_{\mathrm{R}}}{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}-\frac{{\nu }_{\mathrm{RT}}}{E_{\mathrm{R}}}\left[\rho {\sigma }_{\mathrm{R}}-{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}\right]\\ \Rightarrow {\delta }_{\mathrm{R},\mathrm{F}}=\frac{1}{E_{\mathrm{R}}}{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}-\frac{{\nu }_{\mathrm{RT}}\rho {\sigma }_{\mathrm{R}}}{E_{\mathrm{R}}}\end{array}$$

(4)

The tangential shrinkage deformation and the tangential force deformation are expressed by Equations (5) and (6).

$${\delta }_{\mathrm{T},\mathrm{sh}}(\rho )=\rho \mathrm{d}\theta {\alpha }_{\mathrm{T}}\Delta w\left(t\right)$$

(5)

$$\begin{array}{l} {\delta }_{\mathrm{T},\mathrm{F}}(\rho )=\rho \mathrm{d}\theta {\epsilon }_T\\ \Rightarrow {\delta }_{\mathrm{T},\mathrm{F}}=\rho \mathrm{d}\theta [\frac{\rho }{E_{\mathrm{T}}}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+\frac{{\sigma }_{\mathrm{R}}(1-{\nu }_{\mathrm{TR}})}{E_{\mathrm{T}}}]\\ \Rightarrow {\delta }_{\mathrm{T},F}=\mathrm{d}\theta [\frac{{\rho }^2}{E_{\mathrm{T}}}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+\frac{\rho {\sigma }_{\mathrm{R}}(1-{\nu }_{\mathrm{TR}})}{E_{\mathrm{T}}}]\end{array}$$

(6)

2.1.3. Geometric Condition

The displacement coordination conditions are shown in Equation (7).

$${\delta }_{\mathrm{T}}=\mathrm{d}\theta {\delta }_{\mathrm{R}};{\delta }_{\mathrm{T},\mathrm{F}}(\rho )+{\delta }_{\mathrm{T},\mathrm{sh}}(\rho )=\mathrm{d}\theta [{\delta }_{\mathrm{R},\mathrm{F}}(\rho )+{\delta }_{\mathrm{R},\mathrm{sh}}(\rho )]$$

(7)

2.1.4. Fundamental Equation

The displacement coordination condition is shown in Equation (8).

$$\begin{gathered} \frac{{\rho }^2}{E_{\mathrm{T}}}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+\frac{\rho {\sigma }_{\mathrm{R}}(1-{\nu }_{\mathrm{TR}})}{E_{\mathrm{T}}}+\rho {\alpha }_{\mathrm{T}}\Delta w\left(t\right)=\frac{1}{E_{\mathrm{R}}}{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}-\frac{{\nu }_{\mathrm{RT}}\rho {\sigma }_{\mathrm{R}}}{E_{\mathrm{R}}}+\rho {\alpha }_{\mathrm{R}}\Delta w\left(t\right) \\ {\rho }^2\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+(1-{\nu }_{\mathrm{TR}})\rho {\sigma }_{\mathrm{R}}+{\alpha }_{\mathrm{E}}{\nu }_{\mathrm{RT}}\rho {\sigma }_{\mathrm{R}}-{\alpha }_{\mathrm{E}}{\displaystyle {\int }_0^{\rho }{\sigma }_{\mathrm{R}}\mathrm{d}r}+\rho ({\alpha }_{\mathrm{T}}-{\alpha }_{\mathrm{R}})E_{\mathrm{T}}\Delta w\left(t\right)=0 \end{gathered}$$

(8)

ρ obtained from the above formula is expressed in Equation (9).

$$\begin{array}{l}{\rho }^2\frac{{\mathrm{d}}^2{\sigma }_{\mathrm{R}}}{\mathrm{d}{\rho }^2}+2\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+(1-{\nu }_{\mathrm{TR}}){\sigma }_{\mathrm{R}}+(1-{\nu }_{\mathrm{TR}})\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+{\alpha }_{\mathrm{E}}{\nu }_{\mathrm{RT}}{\sigma }_{\mathrm{R}}\\ +{\alpha }_{\mathrm{E}}{\nu }_{\mathrm{RT}}\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }-{\alpha }_{\mathrm{E}}{\sigma }_{\mathrm{R}}+K=0\\ \end{array}$$

(9)

The above formula is then simplified as Equation (10).

$${\rho }^2\frac{{\mathrm{d}}^2{\sigma }_{\mathrm{R}}}{\mathrm{d}{\rho }^2}+3\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+{\sigma }_{\mathrm{R}}(1-{\alpha }_{\mathrm{E}})+K=0$$

(10)

Among them, α_E = E_T/E_R, K = E_T(α_T − α_R)Δw(t).

2.1.5. Boundary Conditions

Boundary condition 1 is given in Equation (11).

$${\displaystyle {\int }_0^R{\sigma }_{\mathrm{T}}\mathrm{d}\rho }=0, \rho =R,{\sigma }_R=0$$

(11)

Boundary condition 2 is given in Equation (12).

σ_R(R) = 0

(12)

2.1.6. Solution

Let ρ = e^t, then t = lnρ:

$$\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }=\frac{1}{\rho }\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}t}, \frac{{\mathrm{d}}^2{\sigma }_{\mathrm{R}}}{\mathrm{d}{\rho }^2}=\frac{1}{{\rho }^2}\frac{{\mathrm{d}}^2{\sigma }_{\mathrm{R}}}{\mathrm{d}{t}^2}-\frac{1}{{\rho }^2}\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}t}$$

(13)

The differential equation is transformed into Equation (14).

$$\frac{{\mathrm{d}}^2{\sigma }_{\mathrm{R}}}{\mathrm{d}{t}^2}+2\frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}t}+{\sigma }_{\mathrm{R}}(1-{\alpha }_{\mathrm{E}})=-K$$

(14)

The characteristic equation and solution are expressed in Equation (15).

$$\left\{\begin{array}{l}{r}^2+2r+(1-{\alpha }_{\mathrm{E}})=0\\ r_1=-1+\sqrt{{\alpha }_{\mathrm{E}}}\\ r_2=-1-\sqrt{{\alpha }_{\mathrm{E}}}\end{array}\right.$$

(15)

The general solution of the homogeneous equation is given in Equation (16).

$${\sigma }_{\mathrm{R}}=C_1{e}^{r_{1}t}+C_2{e}^{r_{2}t}=C_1{\rho }^{r_1}+C_2{\rho }^{r_2}$$

(16)

The special solutions are presented in Equation (17).

$$\left\{\begin{array}{l}{\sigma }_{\mathrm{R}}=C_3\\ C_3(1-{\alpha }_{\mathrm{E}})=-K\end{array}\right.\Rightarrow C_3=-\frac{K}{(1-{\alpha }_{\mathrm{E}})}$$

(17)

The general solution is expressed in Equations (18)–(20).

$$\left\{\begin{array}{l}{\sigma }_{\mathrm{R}}=C_1{\rho }^{-(1-\sqrt{{\alpha }_{\mathrm{E}}})}+C_2{\rho }^{-(1+\sqrt{{\alpha }_{\mathrm{E}}})}-\frac{K}{(1-{\alpha }_{\mathrm{E}})}\\ {\sigma }_{\mathrm{T}}=\rho \frac{\mathrm{d}{\sigma }_{\mathrm{R}}}{\mathrm{d}\rho }+{\sigma }_{\mathrm{R}}\Rightarrow {\sigma }_{\mathrm{T}}=C_1\sqrt{{\alpha }_{\mathrm{E}}}{\rho }^{-(1-\sqrt{{\alpha }_{\mathrm{E}}})}-C_2\sqrt{{\alpha }_{\mathrm{E}}}{\rho }^{-(1+\sqrt{{\alpha }_{\mathrm{E}}})}-\frac{K}{(1-{\alpha }_{\mathrm{E}})}\end{array}\right.$$

(18)

$${\displaystyle {\int }_0^R{\sigma }_{\mathrm{T}}\mathrm{d}\rho }=0\Rightarrow {\mathrm{C}}_2=0$$

(19)

$${\sigma }_R\left(R\right)=0\Rightarrow C_1{R}^{-(1-\sqrt{{\alpha }_{\mathrm{E}}})}-\frac{K}{(1-{\alpha }_{\mathrm{E}})}=0\Rightarrow C_1=\frac{K{R}^{(1-\sqrt{{\alpha }_{\mathrm{E}}})}}{(1-{\alpha }_{\mathrm{E}})}$$

(20)

The stress distribution in the disc under uniform moisture content is shown in Figure 3, and the stress distribution conforms to Equation (21).

$$\left\{\begin{array}{l}{\sigma }_{\mathrm{R}}=-\frac{K}{1-{\alpha }_{\mathrm{E}}}\left[1-{(\rho /R)}^{(\sqrt{{\alpha }_{\mathrm{E}}}-1)}\right]\\ {\sigma }_{\mathrm{T}}=-\frac{K}{1-{\alpha }_{\mathrm{E}}}\left[1-\sqrt{{\alpha }_{\mathrm{E}}}{(\rho /R)}^{(\sqrt{{\alpha }_{\mathrm{E}}}-1)}\right]\end{array}\right.$$

(21)

The position where the tangential stress is equal to zero ρ₀ is calculated as Equation (22).

$${\rho }_0/R=\exp \left(\frac{0.5\ln {\alpha }_{\mathrm{E}}}{(1-\sqrt{{\alpha }_{\mathrm{E}}})}\right)$$

(22)

2.2. Numerical Simulation of Stress Distribution

ABAQUS 6.14, a finite element analysis software package, has a mature heat transfer function module. Because the heat transfer and humidity transfer of wood components are similar, the ABAQUS heat transfer module is used to analyze the humidity field of wood components. The key parameters and governing equations are presented in

Table 1. Parameters analogy of unsteady heat and moisture transfer.

Heat Transfer		Humidity Transfer
Temperature	T(K)	Moisture content	W (%)
Initial temperature	Ti	Initial moisture content	Wi
Ambient temperature	Te	Equilibrium moisture content	We
Surface temperature of the object	Ts	Surface moisture content	Ws
Thermal conductivity	α (m2/s)	Water diffusion coefficient	D (m2/s)
Surface heat exchange coefficient	h (W/m2/K)	Surface humidity divergence coefficient	S (m/s)

and

Table 2. Analogy of two-dimensional Fick’s law governing equations for unsteady heat and moisture transfer.

Coordinates	Heat Transfer	Humidity Transfer
Cartesian coordinates	$\frac{\partial T}{\partial t}=\alpha \left(\frac{{\partial }^{2}T}{\partial x^2}+\frac{{\partial }^{2}T}{\partial y^2}+\frac{{\partial }^{2}T}{\partial z^2}\right)$	$\frac{\partial W}{\partial t}=D\left(\frac{{\partial }^{2}W}{\partial x^2}+\frac{{\partial }^{2}W}{\partial y^2}+\frac{{\partial }^{2}W}{\partial z^2}\right)$
Cylindrical coordinates	$\frac{1}{\alpha }\frac{\partial T}{\partial t}=\frac{1}{r}\frac{\partial }{\partial r}\left(r\frac{\partial T}{\partial r}\right)+\frac{{\partial }^{2}T}{\partial z^2}$	$\frac{1}{D}\frac{\partial W}{\partial t}=\frac{1}{r}\frac{\partial }{\partial r}\left(r\frac{\partial W}{\partial r}\right)+\frac{{\partial }^{2}W}{\partial z^2}$
Spherical coordinates	$\frac{1}{\alpha }\frac{\partial T}{\partial \theta }=\frac{1}{r^2}\frac{\partial }{\partial r}\left(r^2\frac{\partial T}{\partial r}\right)+\frac{1}{r^2{\sin }^2\phi }\left(\frac{{\partial }^{2}T}{\partial {\phi }^2}\right)$	$\frac{1}{D}\frac{\partial W}{\partial \theta }=\frac{1}{r^2}\frac{\partial }{\partial r}\left(r^2\frac{\partial W}{\partial r}\right)+\frac{1}{r^2{\sin }^2\phi }\left(\frac{{\partial }^{2}W}{\partial {\phi }^2}\right)$

.

To verify the correctness of the above analytical solution of the humidity stress, this section compares and analyzes the above models using ABAQUS. The finite element calculation is converted using the existing temperature field of the finite element analysis software, and the mesh size is approximately 2.5 mm. The finite element modeling method and material parameters comprise the authors’ results. The main parameters and material parameters of the model are listed in

Table 3. Parameters of finite element models.

Group	Geometric Shape	Radius × Length R × L (mm)	Wi (%)	We (%)	Moisture Content Distribution Form	Restrictions
a	Disc	100 × 0	25	15	Uniform Δw = 10%	Circle center
b	Disc	100 × 0	15	5	Uniform Δw = 10%	Circle center
c	Disc	100 × 0	35	25	Uniform Δw = 10%	Circle center
d	Disc	50 × 0	25	15	Uniform Δw = 10%	Circle center
e	Disc	150 × 0	25	15	Uniform Δw = 10%	Circle center
f	Disc	100 × 0	20	15	Uniform Δw = 5%	Circle center
g	Disc	100 × 0	30	15	Uniform Δw = 15%	Circle center
h	Cylinder	100 × 300	25	15	Uniform Δw = 10%	Both ends of circle center
i	Cylinder	100 × 1000	25	15	Uniform Δw = 10%	Both ends of circle center

and

Table 4. Parameters of material.

Directions	Elastic Modulus (MPa)	Compressive Strength (MPa)	Tensile Strength (MPa)	Shrinkage/Swelling Coefficient (%)
R	ER = 1048 (16.1%)	fc,R = 3.07 (12.23%)	ft,R = 3.07 (12.23%)	αR = 0.139
T	ET = 594 (22.7%)	fc,T = 2.67 (13.44%)	ft,T = 2.67 (13.44%)	αT = 0.255
L	EL = 12,888 (6.9%)	fc,L = 36.25 (10.43%)	ft,L = 36.25 (10.43%)	αL = 0.019
Directions	Poisson ratio	Shear modulus (MPa)
RT	vRT = 0.43	GRT = 232
RL	vRL = 0.03	GRT = 967
TL	vTL = 0.02	GRT = 773

, respectively.

The typical finite element results from the above modeling method and material parameters are listed in Figure 4 and Figure 5.

The humidity stress distribution from the finite element analysis is shown in Figure 5, where the finite element analysis and theoretical calculation are designated FEA and TC, respectively. The proposed theoretical calculations of humidity stress distribution were highly consistent with the finite element analysis. Notably, the humidity stress expressions proposed in this research are reasonable and accurate.

Both radial stress and tangential stress curves were smooth. The radial stress is always compressive, whereas the tangential stress changes from compressive stress to tensile stress at the center of the circle. Therefore, tangential stress always has a critical point of tensile and compressive stress.

Furthermore, moisture stress is independent of initial moisture content W_i, equilibrium moisture content W_e, and member size but is related to the moisture content gradient Δw. Notably, if the cylinder cross-sectional transfer coefficient is 0, the stress distribution of the cylinder cross-section is the same as that of the disk under the same Δw. The three-dimensional cylindrical humidity stress distribution can be replaced by the two-dimensional disk for further calculations.

3. Prediction of Dry Shrinkage Crack Depth

3.1. Basic Assumption

Basic assumption: the shrinkage deformation of the cracked part is assumed to be unconstrained, and the residual stress is ignored: it can be considered stress-free. The cracked part has no constraint in the deformation of the uncracked part, and the stress of the uncracked part is equivalent to the stress of a disk with a radius of ρ_c (=R − d_c). When the difference in water content change does not exceed Δw_cr again, the crack is closed, and the stress of the uncracked part returns to the initial state (stress-free state). In contrast, when the difference in water content change exceeds Δw_cr again, it continues to expand, and the cumulative extended depth is equivalent to a one-time change in water cut.

To verify the validity of the above assumptions, the finite element simulation method is utilized. The verification involves (1) establishing a finite element model of presplit wood members; (2) setting a load condition for a specific moisture content change difference (greater than Δwcr); (3) extracting the stress distribution of wood members at any cracking position as cracking proceeds, especially the tangential stress at the critical position of the crack and the cracked position (cracking of the wood members will expand during calculation for the finite element model); and (4) comparing the critical position of the crack, the cracked position, and the tangential direction of the theoretical calculation model before cracking. Notably, if the tangential stress at the cracked position is much smaller than that at the critical position of the crack and the value obtained from the calculation results of the theoretical calculation model before cracking, and the critical position of the crack is close to that from the calculation results of the theoretical calculation model before cracking, the assumptions can be verified. The finite element model results were those obtained by the authors. The models are displayed in

Table 5. Basic parameters of the validation models.

Model	Geometric	Radius R	n	Crack Distribution	Preset Crack Depth	Δw
M1	Disc	R = 50 mm	1	-	10% of the radius (5 mm)	10%
M2	Disc	R = 50 mm	2	Equiangular distribution, 180°	10% of the radius (5 mm)	10%
M3	Disc	R = 50 mm	3	Equiangular distribution, 120°	10% of the radius (5 mm)	10%
M4	Disc	R = 50 mm	4	Equiangular distribution, 90°	10% of the radius (5 mm)	10%

and Figure 6.

The finite element calculation results of the above model are listed in Figure 7 and

Table 6. Comparison of basic assumptions between the finite element model and the theoretical model.

Model- dc/R	σR,c (MPa)	σR,c0-F (MPa)	σR,c0-T (MPa)	$\frac{{\mathit{\sigma }}_{\mathit{R}\mathbf{c}0}-\mathbf{F}}{{\mathit{\sigma }}_{\mathit{R},\mathbf{c}0}-\mathbf{T}}$	Model- dc/R	σR,c (MPa)	σR,c0-F (MPa)	σR,c0-T (MPa)	$\frac{{\mathit{\sigma }}_{\mathit{R},\mathbf{c}0}-\mathbf{F}}{{\mathit{\sigma }}_{\mathit{R},\mathbf{c}0}-\mathbf{T}}$
M2-0.3	0.64	3.11	3.91	0.80	M4-0.3	0.27	3.26	3.91	0.83
M2-0.4	0.18	3.41	3.91	0.87	M4-0.4	1.01	3.23	3.91	0.83
M2-0.5	0.00	3.60	3.91	0.92	M4-0.5	1.05	3.06	3.91	0.78
M2-0.6	−0.05	3.63	3.91	0.93	M4-0.6	−0.03	3.01	3.91	0.77
M2-0.7	−0.07	3.20	3.91	0.82	M4-0.7	−0.05	2.99	3.91	0.76
Average of $\frac{{\sigma }_{R,\mathrm{c}0}-\mathrm{F}}{{\sigma }_{R,\mathrm{c}0}-\mathrm{T}}$: 0.83

. Noticeably, the tangential stress at the cracked position is much smaller than that at the critical position of the crack and the values from the calculation results of the theoretical calculation model before cracking.

3.2. Critical Moisture Content Gradient Δw_cr

When σ_T (ρ = R) = f_t,T, the periphery of the wood member is cracked, and the critical moisture content gradient Δw_cr can be obtained via Equations (23) and (24).

$${\sigma }_{\mathrm{T}}(\rho =R)=-\frac{K}{1+\sqrt{{\alpha }_{\mathrm{E}}}}=-\frac{E_{\mathrm{T}}({\alpha }_{\mathrm{T}}-{\alpha }_{\mathrm{R}})\Delta w_{\mathrm{cr}}}{1+\sqrt{{\alpha }_{\mathrm{E}}}}$$

(23)

$$\Delta w_{\mathrm{cr}}=-\frac{(1+\sqrt{{\alpha }_{\mathrm{E}}})f_{\mathrm{t},\mathrm{T}}}{E_{\mathrm{T}}({\alpha }_{\mathrm{T}}-{\alpha }_{\mathrm{R}})}$$

(24)

According to Equation (22), the position at which the tangential stress is equal to zero ρ₀ is unaffected by Δw. At the position ρ₀, the radial shrinkage deformation and the compression deformation are just equal to the circumferential shrinkage deformation. At r > ρ₀, tensile strain in the tangential direction is required to satisfy the coordinated displacement relationship. At the position r < ρ₀, the radial shrinkage deformation and the compression deformation exceed the circumferential shrinkage deformation, and circumferential compressive strain is required to meet the displacement coordination condition.

3.3. Dry Shrinkage Crack Depth

The stress distribution before and after cracking of the wood member based on the basic assumptions mentioned above is shown in Figure 8.

The hoop tensile stress at ρ_c is equal to f_T, as shown in Equations (25)–(27).

$$-\frac{E_{\mathrm{T}}({\alpha }_{\mathrm{T}}-{\alpha }_{\mathrm{R}})\Delta w}{1-{\alpha }_E}\left[1-\sqrt{{\alpha }_E}{({\rho }_{\mathrm{c}}/R)}^{(\sqrt{{\alpha }_E}-1)}\right]=f_{\mathrm{T}}=-\frac{E_{\mathrm{T}}({\alpha }_{\mathrm{T}}-{\alpha }_{\mathrm{R}})\Delta w_{\mathrm{cr}}}{1+\sqrt{{\alpha }_E}}$$

(25)

$$\frac{\Delta w}{1-\sqrt{{\alpha }_E}}\left[1-\sqrt{{\alpha }_E}{({\rho }_{\mathrm{c}}/R)}^{(\sqrt{{\alpha }_E}-1)}\right]=\Delta w_{\mathrm{cr}}$$

(26)

$$1-\sqrt{{\alpha }_E}{({\rho }_{\mathrm{c}}/R)}^{(\sqrt{{\alpha }_E}-1)}=\frac{\Delta w_{\mathrm{cr}}(1-\sqrt{{\alpha }_E})}{\Delta w}$$

(27)

ρ_c/R and d_c/R are, respectively, expressed by Equations (28) and (29).

$${\rho }_{\mathrm{c}}/R=\exp \left[\frac{\ln \sqrt{{\alpha }_E}-\ln \left(1-(1-\sqrt{{\alpha }_E})\Delta w_{\mathrm{cr}}/\Delta w\right)}{1-\sqrt{{\alpha }_E}}\right]$$

(28)

$$d_{\mathrm{c}}/R=1-\exp \left[\frac{\ln \sqrt{{\alpha }_E}-\ln \left(1-(1-\sqrt{{\alpha }_E})\Delta w_{\mathrm{cr}}/\Delta w\right)}{1-\sqrt{{\alpha }_E}}\right]$$

(29)

The estimated calculated crack depth is shown in Figure 9.

4. Validation

4.1. Detection

The detected wood components were taken from old demolished residential houses located in Tianjin (117.2° E, 39.13° N) and Liuzhou (109.42° E, 24.33° N), China. These components were previously used as beams and columns, and their diameters ranged between 15 and 35 cm. These detected samples are from different environments, components, and tree species, mainly to verify the accuracy of crack depth prediction model (Equation (1)) through multiple parameters. The collectors recorded the relevant information of these wood components in detail, including the service life Y_d, tree species, use environment, component type, and rain conditions. It should be noted that all detected wood components are untreated wood. The detected wood components are presented in Figure 10.

The detected parameters included the crack depth d_c,i, quantity of shrinkage cracks n, circumference of wood components c, and distance from the crack to the pith R_i. The average relative crack depth d_c/R is calculated from Equation (30). The basic parameters and detection results for the wood components are listed in

Table 7. Necessary parameters and detected results of wood components.

Region	No.	Name	Species	c (mm)	n	Rain Conditions	Yd (Year)	dc/R-E	Δwcr (%)	Δw (%)	dc/R-T	Ratio (E/T)
Tianjin	1	TJ-Yu-42	Elm	552	4	✓, light	42	0.37	6.36	9.56	0.31	1.19
	2	TJ-Yu-60	Elm	540	5	✓, light	60	0.30	6.36	9.56	0.31	0.97
	3	TJ-Yang-60	Poplar	622	3	✓, light	60	0.40	5.90	9.56	0.38	1.05
	4	TJ-Liu-36	Willow	582	1	✓, light	36	0.24	7.30	9.56	0.23	1.06
	5	TJ-Song-52	Pine	514	7	✓, light	52	0.25	7.18	9.56	0.24	1.03
	6	TJ-Yu-52	Elm	647	4	✓, light	52	0.22	6.36	9.56	0.31	0.71
	7	TJ-Yang-42	Poplar	583	2	✓, light	42	0.49	5.90	9.56	0.38	1.29
	8	TJ-Yang-52	Poplar	563	4	✓, light	52	0.42	5.90	9.56	0.38	1.10
	9	TJ-Liu-60	Willow	608	1	✓, light	60	0.16	7.30	9.56	0.23	0.70
	10	TJ-Huai-36	Sophora	498	5	✓, light	36	0.22	7.20	9.56	0.20	1.12
	11	TJ-Yu-36	Elm	547	2	✓, light	36	0.40	6.36	9.56	0.31	1.29
	12	TJ-Huai-60	Sophora	616	10	✓, light	60	0.25	7.62	9.56	0.20	1.25
Liuzhou	13	LZ-Sha-70(a)	Spruce	962	4	x	70	0.44	6.10	9.13	0.37	1.19
	14	LZ-Sha-70(b)	Spruce	694	3	x	70	0.48	6.10	9.13	0.37	1.29
	15	LZ-Sha-60	Spruce	724	9	x	60	0.36	6.10	9.13	0.37	0.97
	16	LZ-Sha-55	Spruce	953	6	x	55	0.35	6.10	9.13	0.37	0.95
	17	LZ-Sha-50	Spruce	949	5	x	50	0.46	6.10	9.13	0.37	1.24
	18	LZ-Sha-45	Spruce	942	7	x	45	0.34	6.10	9.13	0.37	0.92
	19	LZ-Sha-40(a)	Spruce	725	6	x	40	0.37	6.10	9.13	0.37	1.00
	20	LZ-Sha-40(b)	Spruce	956	7	x	40	0.31	6.10	9.13	0.37	0.84
	21	LZ-Sha-30(a)	Spruce	704	5	x	30	0.39	6.10	9.13	0.37	1.05
	22	LZ-Sha-30(b)	Spruce	650	5	x	30	0.39	6.10	9.13	0.37	1.05
	23	LZ-Sha-30(c)	Spruce	659	5	x	30	0.33	6.10	9.13	0.37	0.89
	24	LZ-Sha-30(d)	Spruce	661	4	x	30	0.36	6.10	9.13	0.37	0.97
	25	LZ-Sha-30(e)	Spruce	629	5	x	30	0.44	6.10	9.13	0.37	1.19
	26	LZ-Sha-25	Spruce	602	6	x	25	0.36	6.10	9.13	0.37	0.97
	27	LZ-Sha-20	Spruce	617	6	x	20	0.39	6.10	9.13	0.37	1.05
	28	LZ-Sha-15	Spruce	645	7	x	15	0.34	6.10	9.13	0.37	0.92
	29	LZ-Sha-10	Spruce	617	5	x	10	0.45	6.10	9.13	0.37	1.22
Average ratio (E/T):1.051             Dispersion coefficient of Ratio (E/T): 15.10%

Note: If the relative crack depth d_c/R is less than 0.05, it is ignored. The lowercase letters (a) to (e) represent different samples of detected components with the same tree species and the same service life.

.

$$\frac{d_{\mathrm{c}}}{R}=\frac{\left(\frac{d_{\mathrm{c}}{}_{,1}}{R_1}+\frac{d_{\mathrm{c}}{}_{,2}}{R_2}+\dots +\frac{d_{\mathrm{c}}{}_{,n}}{R_n}\right)}{n}$$

(30)

4.2. Comparison

The calculation of the moisture content gradient Δw is based on the meteorological temperature (T), humidity (RH), and precipitation (pp) in the external environment where these components were used. Bulcke [25] and Ladislav [26] provided a calculation method for moisture content that considers precipitation factors. This calculation method takes into account the impact of the rain period and the drying period on the moisture content of wood, with a rough linear relationship. Tianjin and Liuzhou have a temperate monsoon climate and subtropical monsoon climate, respectively. Furthermore, taking the 2017 data as an example, the meteorological data of the two regions are shown in Figure 11.

The wood components from Tianjin were placed in outdoor environment; thus, determining the moisture content necessitates considering rainwater factors. The annual water content gradient of Tianjin from 1951 to 2018 is based on the calculation method provided by Bulcke [25] and Ladislav [26]. The average moisture content gradient is then considered as Δw. In contrast, the wood components from Liuzhou were used in an indoor environment, so the moisture content can be calculated from Equation (31) [27]. Additionally, this paper uses the abovementioned method to calculate the annual moisture content gradient in Liuzhou from 1951 to 2018, and the average moisture content gradient is considered as Δw.

$$w=0.01{\left[\frac{-T\ln (1-RH)}{0.13{(1-\frac{T}{647.1})}^{-6.46}}\right]}^{\frac{T^{0.75}}{110}}$$

(31)

where w represents moisture content; T and RH are the temperature and relative humidity, respectively.

The detection result of average relative crack depth d_c/R-E was compared with the calculation result d_c/R-T from Equation (29), and the comparison results are presented in Table 7 and Figure 12. The mechanical performance parameters of the wood materials considered were all sourced from the literature, books, and specifications [28,29,30,31,32,33]; in the absence of consistent data, the corresponding data of the approximate tree species were considered.

Figure 12 shows that the calculation results and the detection results are roughly similar, and most errors are within 30%. The errors are attributable to the following reasons: (1) The information is not completely accurate due to the age and variety of the detected wood components. Some detection components come from private demolished buildings, and these components have not been accurately recorded with sufficient information, only vague information. (2) The mechanical properties of wood materials are highly discrete. Some detection components only have one sample and approximate data are used in the calculation by references [28,29,30,31,32,33]. (3) The moisture content of the external environment involves an approximate calculation method, which cannot be completely accurate at present.

In general, the predicted shrinkage crack depth model is feasible. First, the calculation of the humidity stress of wood components was verified via the finite element method. Second, the crack depth was inferred from the humidity stress distribution. Finally, the rationality of the crack depth calculation model was verified using old wooden components.

4.3. Application of Prediction Model

Based on the above research results, the prediction model can be applied to practical wood engineering. Three steps are critical for application prediction model of practical wood engineering, as illustrated in Figure 13. Calculating the moisture content gradient Δw is the first step, and local meteorological data (temperature, humidity, and precipitation) needs to be collected before calculation. The second step is to calculate the critical moisture content gradient Δw_cr, which requires obtaining the wood parameters before. The final step is to predict the depth of the crack based on the calculation results of the first two steps.

5. Conclusions

This study highlights several important issues that are relevant to understanding the humidity stress distribution and shrinkage crack depth prediction model of timber components. The analytical solution of humidity stress was verified using finite element analysis. The shrinkage crack depth prediction model was validated using practical engineering detection data. The following are the main conclusions drawn:

(1)

The theoretical calculation of the humidity stress distribution proposed in this paper is in good agreement with the finite element results. Therefore, the expression of humidity stress is accurate and can provide a reliable basis for subsequent calculations.

(2)

The tangential stress of the disc is manifested as compressive stress at the center of the circle while tensile stress at the circumference. There is a continuous change from the center of the circle to the circumference, and a critical tension–compression point r exists. In contrast, the radial stress is always compressive from r = 0 to r = 1.

(3)

The moisture stress is not determined by the initial moisture content W_i, equilibrium moisture content W_e, or member size but by the difference in moisture content Δw.

(4)

The distribution of humidity stress in the cross-section of a three-dimensional cylinder is consistent with that of a two-dimensional disk under the same conditions. Furthermore, the three-dimensional cylindrical humidity stress distribution can be simplified as a two-dimensional disk for further calculation.

(5)

An approximate shrinkage crack depth prediction model based on reasonable humidity stress expressions was proposed. Although this has scope for engineering application development, several issues that must first be clarified in detail persist, including approximately similar maximum tensile stress and wood tensile strength and the fact that the crack tip stress and residual stress were ignored.

(6)

The abovementioned shrinkage crack prediction model was verified via practical engineering testing. The test data are in good agreement with the theoretical calculation data of the model. The above model can be applied to actual engineering prediction to provide a theoretical basis for the reinforcement measures and the safety evaluation of wood structures.

(7)

The proposed three-step application process provide a basis on the prediction of shrinkage crack in practical wood engineering for further research.