The Study of Tool Wear Mechanism Considering the Tool–Chip Interface Temperature during Milling of Aluminum Alloy
Previous Article in Journal
Investigating the Wettability, Rheological, and Tribological Properties of Ammonium-Based Protic Ionic Liquids as Neat Lubricants for Steel–Steel and Steel–Aluminium Contacts
Previous Article in Special Issue
Measurement and Prediction of Sawing Characteristics Using Dental Reciprocating Saws: A Pilot Study on Fresh Bovine Scapula
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Lubricants
Volume 11
Issue 11
10.3390/lubricants11110470
lubricants-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

An Experimental Study on Ultrasonic Vibration-Assisted Turning of Aluminum Alloy 6061 with Vegetable Oil-Based Nanofluid Minimum Quantity Lubrication

by
Guoliang Liu
1,2,*,
Jin Wang
2,
Jintao Zheng
2,
Min Ji
2 and
Xiangyu Wang
3
1
State Key Laboratory of Mechanical Transmission for Advanced Equipment, Chongqing University, Chongqing 400044, China
2
School of Mechanical and Automotive Engineering, Qingdao University of Technology, Qingdao 266520, China
3
School of Mechanical Engineering, University of Jinan, Jinan 250022, China
*
Author to whom correspondence should be addressed.
Lubricants 2023, 11(11), 470; https://doi.org/10.3390/lubricants11110470
Submission received: 4 October 2023 / Revised: 19 October 2023 / Accepted: 31 October 2023 / Published: 2 November 2023
(This article belongs to the Special Issue Friction and Wear of Cutting Tools and Cutting Tool Materials)
Browse Figures
Versions Notes

Abstract

:
Minimum quantity lubrication (MQL) is a potential technology for reducing the consumption of cutting fluids in machining processes. However, there is a need for further improvement in its lubrication and cooling properties. Nanofluid MQL (NMQL) and ultrasonic vibration-assisted machining are both effective methods of enhancing MQL. To achieve an optimal result, this work presents a new method of combining nanofluid MQL with ultrasonic vibration assistance in a turning process. Comparative experimental studies were conducted for two types of turning processes of aluminum alloy 6061, including conventional turning (CT) and ultrasonic vibration-assisted turning (UVAT). For each turning process, five types of lubricating methods were applied, including dry, MQL, nanofluid MQL with graphene nanosheets (GN-MQL), nanofluid MQL with diamond nanoparticles (DN-MQL), and nanofluid MQL with a diamond/graphene hybrid (GN+DN-MQL). A specific cutting energy and areal surface roughness were adopted to evaluate the machinability. The results show that the new method can further improve the machining performance by reducing the specific cutting energy and areal surface roughness, compared with the NMQL turning process and UVAT process. The diamond nanoparticles are easy to embed on the workpiece surface under the UVAT process, which can increase the specific cutting energy and Sa as compared to the MQL method. The graphene nanosheets can produce the interlayer shear effect and be squeezed into the workpiece, thus reducing the specific cutting energy. The results provide a new way for the development of eco-friendly machining.

1. Introduction

Cutting fluid has been frequently used to improve machinability, including reducing cutting forces and temperature, extending tool life, and improving machined surface integrity, since the early 20th century [1]. However, several drawbacks of the traditional flooded cutting fluids have been confirmed. For example, the cost of cutting fluids accounts for 7–17% of the total manufacturing cost, while its effective availability is relatively low [2,3]. It is difficult to provide the fluid into the cutting area. In addition, most of the cutting fluids used in the processing industry are mineral-based oils, which have huge risk to human health and environmental ecology [4]. Therefore, finding a new reliable machining method with green cutting lubrication technologies has been an extremely urgent task.
In recent years, several sustainable cutting methods have been proposed, including dry cutting, minimum quantity lubrication (MQL), cryogenic cutting, and so on [5,6,7]. Dry cutting avoids the usage of cutting fluid during the machining process, but often leads to severe tool wear and damaged machined surface integrity because of the bad lubricating and cooling conditions [8]. Cryogenic cutting employs liquid nitrogen, liquid carbon dioxide, or cryogenic gas as the coolant in the process, providing efficient cooling performance without generating pollutants [9]. However, these cryogenic fluids have limited lubricating properties, and their cost is relatively high. In comparison, MQL mixes compressed gas with a tiny amount of cutting fluid to form a droplet mist and generates a high spraying speed, which can obtain a good lubrification effect with a significantly reduced cutting fluid consumption [10]. Furthermore, researchers proved that the adverse effects of mineral-based cutting fluid on the environment and human health can be greatly eliminated by using vegetable oils as the lubricant media [11]. Vegetable oil-based MQL technology has been adopted by many researchers and proved that it can obtain good cutting performance during the machining of different kinds of materials [12].
However, there is a need for further enhancement of the lubrication and cooling properties of the vegetable oil-based MQL droplet mist. The amount of fluid permeating into the cutting zone is minor, although the compressed gas can generate a high spraying speed of droplet mist. According to the existing research, two primary methods are used to enhance the lubrication and cooling properties of MQL. The first involves improving the heat-conducting and lubricating properties of the lubricant media to achieve an effective lubricating and cooling effect with the limited lubricant media. The second approach involves increasing the effective flow rate of droplet mist into the cutting zone to lead to more lubricant media being produced [13,14].
Adding a proper amount of nanoparticles into the vegetable oils to form the nanofluid minimum quantity lubrication (NMQL) process has been proved to be an effective way for further improving the heat-conducting and lubricating properties of the MQL droplets [15]. Researchers have extensively studied the cutting performance of the NMQL process with various kinds of nanoparticles/nanosheets, such as Al2O3, graphite, CNTs, TiO2, MoS2, hBN, Ag, ZnO, Fe2O3, SiO2, and diamond, in different machining methods, including turning, milling, drilling, and grinding [15,16,17,18,19,20]. It is found that these nanoparticles/nanosheets have different lubricating and cooling properties based on their shape and structural characteristics. The Al2O3 and diamond nanoparticles can reduce the tool-chip/workpiece friction coefficient by transforming the sliding friction into rolling friction [15,16]. MoS2 and graphite have a layered structure with outstanding deposition and film formation properties, which can reduce the friction coefficient by transforming the two sliding metal surfaces to relative slippage of molecular layers [19]. Moreover, the graphite possesses exceptionally high thermal conductivity, ensuring excellent cooling performance during the machining processes [20]. In order to obtain better lubricating and cooling properties, hybrid nanofluid with two or more types of nanoparticles was also designed and tested by some researchers. Sharma et al. [21] performed NMQL turning of AISI 304 steel with Al2O3 and graphite as the hybrid nanofluid, and excellent results were observed by considering surface roughness, cutting force, cutting temperature, and tool wear. Jamil et al. [22] combined Al2O3 and CNT to form a hybrid nanofluid, and then added cryogenic media to enhance the cooling effect, during the machining of TC4 titanium alloy. A good machining performance was observed.
However, cutting tools are in close contact with the workpieces and chips during the conventional continuous cutting processes. Thus, the nanofluids are blocked from entering the tool-chip/tool-workpiece interfaces, making the lubricating and cooling effect unsatisfying, which is a restriction that has to be urgently settled for NMQL machining processes. In recent years, ultrasonic vibration-assisted machining (UVAM) has been a widely and successfully applied technology in the field of turning, grinding, milling, and drilling [23,24]. The high-frequency vibration of cutting tools can transform the continuous cutting process to an intermittent machining process, thus reducing the cutting force, cutting temperature, tool wear, and improving the machined surface integrity. In addition, the interrupted cutting action of ultrasonic vibration can break the close contact between the cutting tool and the workpiece/chip, and produce a pumping phenomenon, which can greatly increase the effective flow rate of the cutting fluid. Therefore, combining UVAM with NMQL may produce satisfactory results. Some researchers have attempted to combining different UVAM technologies with the NMQL method. Hoang et al. [25] combined graphene NMQL with an ultrasonic vibration-assisted deep hole drilling process (UVAD) for AISI SUS 304 stainless steel, and found a higher production rate, longer tool life, and better machining performance in terms of cutting forces and processing ability. Gao et al. [26,27] used different types of hybrid nanofluids as an MQL lubricant in ultrasonic vibration-assisted grinding (UVAG) processes. They all proved that the combination of NMQL and UVAG can further decrease the temperature, grinding forces, and friction coefficient.
The above literature review shows the obvious processing advantages of simultaneously using UVAG/UVAD and NMQL methods; however, the experimental confirmation of processing advantages of combining UVAT and NMQL techniques is missing. Thus, this paper aims to investigate the machining performance of UVAT and NMQL methods on aluminum alloy 6061 to experimentally confirm the feasibility of this new machining method. The experimental tests were conducted for different cooling techniques, including dry, MQL using palm oil, and NMQL using diamond nanoparticles, graphene nanosheets, and a hybrid of diamond/graphene mixed in palm oil. Two modes of turning processes, including conventional turning (CT) and ultrasonic vibration-assisted turning (UVAT), were combined with the above cooling techniques. The machining performance of various methods was fully evaluated and compared in terms of their specific cutting energy and areal surface roughness.

2. Experimental Setup and Scheme

The experimental study design aligns with the scheme presented in Figure 1. All cutting experiments are carried out on a CAK3665 CNC lathe (Shenyang Machine Tool Co., Ltd., Shenyang, Liaoning, China)with a self-developed ultrasonic vibration excitation system, as shown in Figure 2a. The Kennametal CCMT 060204 carbide insert (Kennametal, USA) with a tool nose radius of 0.4 mm is used in this work. After being mounted on the ultrasonic horn, the rake angle γ0, clearance angle α0, and side cutting edge angle Kr of the tool are 0°, 7°, and 5°, respectively, as shown in Figure 2b. Aluminum alloy 6061 is used as the workpiece, and its mechanical properties are shown in Table 1, which were tested by our co-author in a previous study [28]. The radial turning mode is adopted in this work, and ten experiments designed by the single factor experimental design method are shown in Table 2. The cutting speed is selected to guarantee the separation between the tool and chip, while the feed rate and depth of each cut are selected according to the recommendations within the tool manual. During the UVAT processes, an ultrasonic elliptic vibration is applied on the tool nose, and the ultrasonic amplitude in cutting speed direction and depth of cut direction are 3 and 1 μm, respectively. The ultrasonic frequency is 40.8 kHz and the phase difference is 90°. For both MQL and NMQL conditions, the KS-2106 MQL system from Jinzhao Energy Saving Technology Co., Ltd. (Shanghai, China) is adopted. The flow rate for the lubricant is 60 mL/h with a gas pressure of 0.7 MPa. For the NMQL condition, the mass fraction of nanofluids is 0.5%, and the mass ratio of diamond nanoparticles and graphene nanosheets in GN+DN-MQL is 1:1. The size of graphene nanosheets is about 1–3 μm in length and 1–5 nm in thickness. The diameter of diamond nanoparticles is 50 nm. The nanofluid was prepared by dispersing the nanoparticles/nanosheets in palm oil via a two-step method with the Span-80 as the dispersant (mass fraction of 20% of the nanoparticles/nanosheets), i.e., adding a certain amount of nanoparticles/nanosheets and dispersant to base oils followed by sonification (40 kHz, 100 W) for 1 h. According to previous works, the nanoparticles/nanosheets can be dispersed evenly in the palm oil after sonification [29,30].
During the cutting process, the cutting force in the cutting velocity direction for each cutting condition is measured with a YDC-III89B piezoelectric dynamometer (Dalian University of Technology, Dalian, Liaoning, China), and the specific cutting energy is then calculated. After the turning process, the KEYENCE VK-X1000 laser microscope (Tokyo, Japan) is used to observe the surface morphology, and then used to measure the areal surface roughness Sa and Sz. The scanning electron microscope (SEM) and energy dispersive spectrometer (EDS) (ZEISS, Tokyo, Japan) are also used to analyze the machined surface morphology and components. A new insert is used in each cutting process to eliminate the errors induced by tool wear and the mounting error, and three tests are conducted for each machining condition to minimize the experimental error.

3. Results and Discussion

3.1. Specific Cutting Energy

Specific cutting energy refers to the energy consumed for removing per unit volume of a workpiece material [31]. The expression for this is es = Fv/(ap × f), where es is the specific cutting energy, Fv is the cutting force in tangential force, ap is the depth of cut, and f is the feed rate. A lower specific energy indicates an improved lubrication condition [32]. The specific cutting energy of different cutting conditions is shown in Figure 3, and the error bars show the standard deviation of the results among three repetitions. It can be seen from Figure 3 that the ultrasonic vibration reduces the specific cutting energy for all lubrication conditions. It is well-acknowledged that UVAT can reduce the cutting forces by achieving separation between the cutting tool and the chip/workpiece, and thus reduces the specific cutting energy.
It can also be noticed that, during the CT process, the MQL and NMQL methods with different lubricants all generate significantly lower specific cutting energy in comparison to dry cutting. However, there is no obvious difference between the different MQL and NMQL methods. During the CT process, the cutting tool is in close contact with the workpiece and chip during the whole cutting process, and only a small amount of lubricant can permeate into the cutting zone. In this work, the mass fraction of nanoparticles or nanosheets in nanofluids is very low (only 0.5%). In this case, the nanoparticles or nanosheets that can permeate into the tool/chip or tool/workpiece interfaces to exert a lubrication effect are negligible. Thus, the MQL and NMQL methods fail to produce significant differences among each other regarding specific cutting energy. Certainly, the small quantity of lubricant permeating into the cutting zone can still produce remarkable differences in comparison to dry cutting conditions.
On the contrary, during the UVAT process, not only all the MQL and NMQL methods with different lubricants generate lower specific cutting energy than dry cutting, but the NMQL methods with graphene nanosheets, including GN-MQL and GN+DN-MQL, also generate lower specific cutting energy than the MQL method which uses pure palm oil. This means that adding graphene nanosheets into the palm oil can further increase the lubrication effect. This was also confirmed by Jia et al. during their investigation of UVAG processes [33]. The results in Figure 3 also prove that the diamond nanoparticles mixed in palm oil have a negative effect on the lubrication effect. This occurs because the DN-MQL method increases the specific cutting energy more in comparison to the MQL method which uses pure palm oil. The ultrasonic vibration can separate the cutting tool and chip/workpiece, and can thus permeate more of the lubricant into the cutting zone. Therefore, the nanoparticles or nanosheets that permeate into the tool/chip or tool/workpiece interfaces can exert a more obvious lubrication effect, resulting in affecting the specific cutting energy differently, as shown in Figure 3.
As for the different effects of graphene nanosheets and diamond nanoparticles on the specific cutting energy, their effects can be attributed to their different shapes and lubrication mechanisms. It has been proved by molecular dynamics simulations, in our previous work, that the tribological behavior of the nano-diamond is dominated by rolling, while the behavior of graphene nanosheets is governed by the interlayer shear effect [34]. During the UVAT processes, the cutting tool constantly bombards the workpiece surface, which can push the nano-diamond and graphene nanosheets into the workpiece. Furthermore, the workpiece material in this work (aluminum alloy 6061) exhibits a low hardness and high plasticity. Therefore, the near-spherical nano-diamond is easy to be squeezed into the workpiece. Once this happens, the nano-diamond will be tightly wrapped by the high-plastic aluminum alloy, and the rolling bearing effect will be severely weakened. Moreover, the nano-diamonds that are embedded on the workpiece surface can work as hard spots and interact with the cutting tool to increase the friction coefficient. This phenomenon is confirmed by the experimental surface morphology shown in Figure 4. It must be noted that the workpiece is cleaned ultrasonically before being observed. Hence, it is reasonably to believe that the large bulge is embedded on the workpiece surface. The results of elemental analysis (Figure 4) also show that the bulge is a mixture of numerous nano-diamonds and aluminum alloy.
While for the graphene nanosheets, the interlayer shear effect occurs inside the graphene nanosheets. In addition, the graphene nanosheets are relatively large, soft, and more likely to attach to the workpiece and cutting tool surfaces [35]. In this condition, the interlayer shear effect can still work to reduce the cutting forces, even if the graphene nanosheets are squeezed into the workpiece. Figure 5 shows the experimental surface morphology of the UVAT and GN-MQL method. It can be seen that the graphene nanosheets are squeezed into the workpiece and attached onto the surface. However, the 3D images show that there is no definite upward bulge around the graphene nanosheets. In this case, shear sliding occupies the main position and reduces the friction coefficient.

3.2. Areal Surface Roughness

Figure 6 shows the measured areal surface roughness results under different cutting conditions, and the error bars show the standard deviation of measurement results among three repetitions. Sa is the arithmetic average surface roughness and Sz is the maximum peak-to-valley height of the whole measuring area. It can be seen from Figure 6a that the ultrasonic vibration increases the surface roughness during the dry cutting processes, but generates smoother surfaces under MQL and NMQL conditions. In addition, the lubrication methods show different effects on surface roughness Sa under CT and UVAT processes. During the CT process, MQL with palm oil produces a better surface finish quality than the dry cutting condition, and all the NMQL methods further reduce the surface roughness compared to the MQL condition. While in the UVAT process, the NMQL method with nano-diamond, i.e., DN-MQL, generates a rougher surface in comparison to the MQL condition with palm oil.
However, when comparing the results of Sz in Figure 6b, the conclusion is different than the one from above. The ultrasonic vibration reduces Sz during dry and MQL conditions in comparison to the CT processes, but generates larger Sz during all NMQL conditions. Among all different lubrication methods, the MQL condition generates the lowest Sz during both the CT and UVAT processes, and the NMQL methods all reduce Sz in comparison to the dry cutting condition.
Figure 7 shows the surface morphology of the CT and UVAT processes under dry cutting conditions. It can be seen that the ultrasonic vibration generates regular dimples on the machined surface because of the intermittent separation of the cutting tool and workpiece, which increases the average roughness value Sa. However, the ultrasonic vibration amplitude is minor, i.e., 1 μm in the depth of cut direction, and thus the depth of the dimples is very small. Therefore, its effect on surface roughness is minor; thus, the increase rate of Sa is small. On the contrary, the ultrasonic vibration weakened the adhesion between the cutting tool and chip/workpiece, thus reducing the chippings adhered on the machined surfaces. This was also observed by researchers during the UVAG processes [24]. Figure 7a and the EDS results show that the chippings adhered on the machined surfaces are mainly workpiece materials, which are formed by the chips that were squeezed into the surface. Therefore, the Sz value of the UVAT process is lower than that of the CT process.
During the MQL cutting condition, the lubrication effect of palm oil drops can be significantly reinforced via ultrasonic vibration. This can occur as the ultrasonic vibration leads more palm oil drops into the cutting zone. The better lubrication condition can reduce the tool-chip/workpiece adhesion and the side flow of workpiece materials, thus reducing the scallop height between tool paths. This phenomenon can be proved by the 3D images of the surface morphology (Figure 8), and is consistent with the results of Ni et al. [23]. It can be seen from the 3D image, in Figure 8a, that there are obvious plowing marks on the surfaces of the CT process, and the depths of valleys are significantly different. The profile curve fluctuates in a large range from −6.3 μm to 5.7 μm. On the contrary, the surface of the UVAT process, in Figure 8b, is much smoother. The good lubrication condition eliminates the obvious plowing marks. The profile curve in Figure 8b fluctuates in a stable range from −2.7 μm to 4.2 μm. In this case, the surface roughness of the UVAT and MQL process, including the Sa and Sz, is obviously reduced in comparison to the CT and MQL process.
When adding nano-diamond or graphene nanosheets into the oil, the lubrication effect of the UVAT and NMQL process can be further improved, thus reducing the average surface roughness Sa in comparison to the CT processes. On the other hand, the nanoparticles/nanosheets can be squeezed into the workpiece using the vibrating cutting tool, thus generating lots of pits after being washed away, as shown in Figure 9. As a result, the Sz value of the UVAT and NMQL process is greater than that of the CT and NMQL process.
In addition, the larger value of Sz in the UVAT and NMQL process than the UVAT and MQL process can also be attributed to the pits generated with the embedded nanoparticles/nanosheets. It is obvious that the surface of the UVAT and MQL process (as shown in Figure 9d) is uniform, and the microstructure produced with ultrasonic vibration is regular, without obvious random defects. On the contrary, the pits resulting from the embedded nanoparticles/nanosheets can be observed on all surfaces of the UVAT and NMQL process. Furthermore, a comparison of the depth of pits in Figure 9 reveals that the UVAT and GN-NMQL process generates relatively shallow pits (the largest depth of pits is 2.4 μm) in comparison to the NMQL conditions which use a nano-diamond material (the largest depth of pits is 3.1 μm).

4. Conclusions

(1) Combining nanofluid MQL with ultrasonic vibration assistance in turning processes has great potential in further improving the machinability in comparison to the NMQL turning process and UVAT process, and has the ability to reduce the specific cutting energy and areal surface roughness.
(2) Due to the low hardness of aluminum alloy 6061, the diamond nanoparticles are easy to embed onto the workpiece surface under the UVAT process, which can significantly weaken their rolling bearing effect and increase the specific cutting energy compared to the MQL method which uses pure palm oil.
(3) The graphene nanosheets can produce the interlayer shear effect by being squeezed into the workpiece. Therefore, the NMQL method which uses a mixture of graphene nanosheets and nano-diamond/graphene nanosheets can further reduce the specific cutting energy compared to the MQL method which uses pure palm oil.
(4) The ultrasonic vibration can significantly reinforce the lubrication effect of the MQL and NMQL methods. The superior lubrication condition can reduce the tool-chip/workpiece adhesion, cutting tool plowing, and workpiece material side flow, thus reducing the average areal surface roughness Sa compared to the CT and MQL as well as CT and NMQL processes.
(5) During the UVAT processes, the nanoparticles/nanosheets can be squeezed into the workpiece with the vibrating cutting tool, thus generating lots of pits on the machined surfaces. Therefore, the surface roughness of the UVAT and NMQL process is increased more in comparison to the UVAT and MQL process.
(6) Future research should be performed to reveal the cutting performance of the UVAT and NMQL process for different kinds of workpiece materials, such as materials with high strength (titanium alloy, for example) and high hardness (quenched steel, for example). Furthermore, more kinds of nanoparticles/nanosheets should be used during the UVAT and NMQL process and the optimal mass fraction of the nanoparticles/nanosheets should be tested.

Author Contributions

Project administration and writing—original draft preparation, G.L.; methodology, J.W.; data curation, J.Z.; writing—review and editing, M.J.; resources, X.W. All authors have read and agreed to the published version of the manuscript.

Funding

This work is financially supported by the Open Research Fund of State Key Laboratory of Mechanical Transmission for Advanced Equipment, Chongqing University (SKLMT-MSKFKT-202105), National Natural Science Foundation of China (52375446 and 52005281), and Natural Science Foundation of Shandong Province (ZR2020QE181).

Data Availability Statement

Data will be made available on request.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Said, Z.; Gupta, M.; Hegab, H.; Arora, N.; Khan, A.M.; Jamil, M.; Bellos, E. A comprehensive review on minimum quantity lubrication (MQL) in machining processes using nano-cutting fluids. Int. J. Adv. Manuf. Technol. 2019, 105, 2057–2086. [Google Scholar] [CrossRef]
  2. Amiril, S.A.S.; Rahim, E.A.; Syahrullail, S. A review on ionic liquids as sustainable lubricants in manufacturing and engineering: Recent research, performance, and applications. J. Clean. Prod. 2017, 168, 1571–1589. [Google Scholar] [CrossRef]
  3. Yıldırım, Ç.V.; Sarıkaya, M.; Kıvak, T.; Şirin, Ş. The effect of addition of hBN nanoparticles to nanofluid-MQL on tool wear patterns, tool life, roughness and temperature in turning of Ni-based Inconel 625. Tribol. Int. 2019, 134, 443–456. [Google Scholar] [CrossRef]
  4. Abd Rahim, E.; Dorairaju, H. Evaluation of mist flow characteristic and performance in minimum quantity lubrication (MQL) machining. Measurement 2018, 123, 213–225. [Google Scholar] [CrossRef]
  5. Liu, G.L.; Zheng, J.T.; Huang, C.Z.; Sun, S.F.; Liu, X.F.; Dai, L.J.; Wang, X.Y. Coupling effect of micro-textured tools and cooling conditions on the turning performance of aluminum alloy 6061. Adv. Manuf. 2023, 11, 663–681. [Google Scholar] [CrossRef]
  6. Guolong, Z.H.A.O.; Lianjia, X.I.N.; Liang, L.I.; Zhang, Y.; Ning, H.E.; Hansen, H.N. Cutting force model and damage formation mechanism in milling of 70wt% Si/Al composite. Chin. J. Aeronaut. 2023, 36, 114–128. [Google Scholar]
  7. Liu, K.; Zhang, J.; Li, J.; Bao, R.; Zuo, Y.; Liu, H.; Wang, Y. Experiment study of surface formation mechanism during cryogenic turning of PEEK. J. Manuf. Process. 2023, 104, 322–333. [Google Scholar] [CrossRef]
  8. Şirin, Ş.; Sarıkaya, M.; Yıldırım, Ç.V.; Kıvak, T. Machinability performance of nickel alloy X-750 with SiAlON ceramic cutting tool under dry, MQL and hBN mixed nanofluid-MQL. Tribol. Int. 2021, 153, 106673. [Google Scholar] [CrossRef]
  9. Albertelli, P.; Strano, M.; Monno, M. Simulation of the effects of cryogenic liquid nitrogen jets in Ti6Al4V milling. J. Manuf. Process. 2023, 85, 323–344. [Google Scholar] [CrossRef]
  10. He, T.; Liu, N.; Xia, H.; Wu, L.; Zhang, Y.; Li, D.; Chen, Y. Progress and trend of minimum quantity lubrication (MQL): A comprehensive review. J. Clean. Prod. 2022, 386, 135809. [Google Scholar] [CrossRef]
  11. Hybská, H.; Mitterpach, J.; Samešová, D.; Schwarz, M.; Fialová, J.; Veverková, D. Assessment of ecotoxicological properties of oils in water. Arch. Environ. Prot. 2018, 44, 31–37. [Google Scholar]
  12. Sankaranarayanan, R.; Krolczyk, G.M. A comprehensive review on research developments of vegetable-oil based cutting fluids for sustainable machining challenges. J. Manuf. Process. 2021, 67, 286–313. [Google Scholar]
  13. Wang, X.; Li, C.; Zhang, Y.; Ding, W.; Yang, M.; Gao, T.; Ali, H.M. Vegetable oil-based nanofluid minimum quantity lubrication turning: Academic review and perspectives. J. Manuf. Process. 2020, 59, 76–97. [Google Scholar] [CrossRef]
  14. Kumar, A.; Sharma, A.K.; Katiyar, J.K. State-of-the-art in sustainable machining of different materials using nano minimum quality lubrication (NMQL). Lubricants 2023, 11, 64. [Google Scholar] [CrossRef]
  15. Gupta, M.K.; Jamil, M.; Wang, X.; Song, Q.; Liu, Z.; Mia, M.; Imran, G.S. Performance evaluation of vegetable oil-based nano-cutting fluids in environmentally friendly machining of inconel-800 alloy. Materials 2019, 12, 2792. [Google Scholar] [CrossRef]
  16. Yıldırım, Ç.V. Experimental comparison of the performance of nanofluids, cryogenic and hybrid cooling in turning of Inconel 625. Tribol. Int. 2019, 137, 366–378. [Google Scholar] [CrossRef]
  17. Darshan, C.; Jain, S.; Dogra, M.; Gupta, M.K.; Mia, M. Machinability improvement in Inconel-718 by enhanced tribological and thermal environment using textured tool. J. Therm. Anal. Calorim. 2019, 138, 273–285. [Google Scholar] [CrossRef]
  18. Musavi, S.H.; Davoodi, B.; Niknam, S.A. Effects of reinforced nanoparticles with surfactant on surface quality and chip formation morphology in MQL-turning of superalloys. J. Manuf. Process. 2019, 40, 128–139. [Google Scholar] [CrossRef]
  19. Das, A.; Pradhan, O.; Patel, S.K.; Das, S.R.; Biswal, B.B. Performance appraisal of various nanofluids during hard machining of AISI 4340 steel. J. Manuf. Process. 2019, 46, 248–270. [Google Scholar] [CrossRef]
  20. Lim, S.K.; Azmi, W.H.; Jamaludin, A.S.; Yusoff, A.R. Characteristics of Hybrid Nanolubricants for MQL Cooling Lubrication Machining Application. Lubricants 2022, 10, 350. [Google Scholar] [CrossRef]
  21. Sharma, A.K.; Tiwari, A.K.; Dixit, A.R.; Singh, R.K.; Singh, M. Novel uses of alumina/graphene hybrid nanoparticle additives for improved tribological properties of lubricant in turning operation. Tribol. Int. 2018, 119, 99–111. [Google Scholar] [CrossRef]
  22. Jamil, M.; Khan, A.M.; Hegab, H.; Gong, L.; Mia, M.; Gupta, M.K.; He, N. Effects of hybrid Al 2 O 3-CNT nanofluids and cryogenic cooling on machining of Ti–6Al–4V. Int. J. Adv. Manuf. Technol. 2019, 102, 3895–3909. [Google Scholar] [CrossRef]
  23. Ni, C.; Zhu, L. Investigation on machining characteristics of TC4 alloy by simultaneous application of ultrasonic vibration assisted milling (UVAM) and economical-environmental MQL technology. J. Mater. Process. Technol. 2020, 278, 116518. [Google Scholar] [CrossRef]
  24. Kumar, M.N.; Subbu, S.K.; Krishna, P.V.; Venugopal, A. Vibration assisted conventional and advanced machining: A review. Procedia Eng. 2014, 97, 1577–1586. [Google Scholar] [CrossRef]
  25. Hoang, T.D.; Ngo, Q.H.; Chu, N.H.; Mai, T.H.; Nguyen, T.; Ho, K.T.; Nguyen, D. Ultrasonic assisted nano-fluid MQL in deep drilling of hard-to-cut materials. Mater. Manuf. Process. 2022, 37, 712–721. [Google Scholar] [CrossRef]
  26. Gao, T.; Zhang, X.; Li, C.; Zhang, Y.; Yang, M.; Jia, D.; Zhu, L. Surface morphology evaluation of multi-angle 2D ultrasonic vibration integrated with nanofluid minimum quantity lubrication grinding. J. Manuf. Process. 2020, 51, 44–61. [Google Scholar] [CrossRef]
  27. Rabiei, F.; Rahimi, A.R.; Hadad, M.J. Performance improvement of eco-friendly MQL technique by using hybrid nanofluid and ultrasonic-assisted grinding. Int. J. Adv. Manuf. Technol. 2017, 93, 1001–1015. [Google Scholar] [CrossRef]
  28. Wang, J.; Duan, P.; Wang, T.; Wang, X.; Qiao, Y. Effect of Cryogenic Cooling on Mechanical Properties and Cutting Force of 6061 Aluminum Alloy. J. Phys. Conf. Ser. 2023, 2459, 012032. [Google Scholar] [CrossRef]
  29. Zhang, Y.; Li, C.; Jia, D.; Zhang, D.; Zhang, X. Experimental evaluation of the lubrication performance of MoS2/CNT nanofluid for minimal quantity lubrication in Ni-based alloy grinding. Int. J. Adv. Manuf. Technol. 2015, 99, 19–33. [Google Scholar] [CrossRef]
  30. Su, Y.; Gong, L.; Li, B.; Liu, Z.; Chen, D. Performance evaluation of nanofluid MQL with vegetable-based oil and ester oil as base fluids in turning. Int. J. Adv. Manuf. Technol. 2016, 83, 2083–2089. [Google Scholar] [CrossRef]
  31. Shaw, M.C.; Cookson, J.O. Metal Cutting Principles; Oxford University Press: New York, NY, USA, 2005. [Google Scholar]
  32. Liu, G.; Özel, T.; Li, J.; Wang, D.; Sun, S. Optimization and fabrication of curvilinear micro-grooved cutting tools for sustainable machining based on finite element modelling of the cutting process. Int. J. Adv. Manuf. Technol. 2020, 110, 1327–1338. [Google Scholar] [CrossRef]
  33. Jia, D.; Li, C.; Zhang, Y.; Yang, M.; Zhang, X.; Li, R.; Ji, H. Experimental evaluation of surface topographies of NMQL grinding ZrO2 ceramics combining multiangle ultrasonic vibration. Int. J. Adv. Manuf. Technol. 2019, 100, 457–473. [Google Scholar] [CrossRef]
  34. Wang, D.; Zhang, Y.; Zhao, Q.; Jiang, J.; Liu, G.; Li, C. Tribological mechanism of carbon group nanofluids on grinding interface under minimum quantity lubrication based on molecular dynamic simulation. Front. Mech. Eng. 2023, 18, 17. [Google Scholar] [CrossRef]
  35. Hoang, T.D.; Mai, T.H.; Nguyen, V.D. Enhancement of Deep Drilling for Stainless Steels by Nano-Lubricant through Twist Drill Bits. Lubricants 2022, 10, 173. [Google Scholar] [CrossRef]
Lubricants 11 00470 g001
Figure 1. Flow chart of the experimental study.
Figure 1. Flow chart of the experimental study.
Lubricants 11 00470 g001
Lubricants 11 00470 g002
Figure 2. (a) Experimental equipment of the UVAT and NMQL method and (b) the cutting tool angles.
Figure 2. (a) Experimental equipment of the UVAT and NMQL method and (b) the cutting tool angles.
Lubricants 11 00470 g002
Lubricants 11 00470 g003
Figure 3. Specific cutting energy of different cutting conditions.
Figure 3. Specific cutting energy of different cutting conditions.
Lubricants 11 00470 g003
Lubricants 11 00470 g004
Figure 4. (a) SEM and (b) 3D images (×1000) of the surface morphology of the UVAT and DN-MQL method, and (c) EDS results of the bulge.
Figure 4. (a) SEM and (b) 3D images (×1000) of the surface morphology of the UVAT and DN-MQL method, and (c) EDS results of the bulge.
Lubricants 11 00470 g004
Lubricants 11 00470 g005
Figure 5. (a) SEM and (b) EDS images of the surface morphology of the UVAT and GN-MQL method.
Figure 5. (a) SEM and (b) EDS images of the surface morphology of the UVAT and GN-MQL method.
Lubricants 11 00470 g005
Lubricants 11 00470 g006
Figure 6. Areal surface roughness, (a) Sa and (b) Sz, of different cutting conditions.
Figure 6. Areal surface roughness, (a) Sa and (b) Sz, of different cutting conditions.
Lubricants 11 00470 g006
Lubricants 11 00470 g007
Figure 7. SEM images of the surface morphology of (a) CT and (b) UVAT processes under dry cutting conditions and the EDS results of the chipping in (a).
Figure 7. SEM images of the surface morphology of (a) CT and (b) UVAT processes under dry cutting conditions and the EDS results of the chipping in (a).
Lubricants 11 00470 g007
Lubricants 11 00470 g008
Figure 8. Three-dimensional images (×400) of the surface morphology of (a) CT and (b) UVAT processes under MQL condition.
Figure 8. Three-dimensional images (×400) of the surface morphology of (a) CT and (b) UVAT processes under MQL condition.
Lubricants 11 00470 g008
Lubricants 11 00470 g009
Figure 9. Three-dimensional images (×1000) of the surface morphology of UVAT processes under (a) DN-MQL, (b) GN-MQL, (c) GN+DN-MQL, and (d) MQL conditions.
Figure 9. Three-dimensional images (×1000) of the surface morphology of UVAT processes under (a) DN-MQL, (b) GN-MQL, (c) GN+DN-MQL, and (d) MQL conditions.
Lubricants 11 00470 g009
Table 1. The mechanical properties of AA 6061 [28].
Table 1. The mechanical properties of AA 6061 [28].
Density (g/cm3)Tensile Strength (MPa)Elongation (%)Hardness (Hv9.8/MPa)
2.752558.17107.3
Table 2. Cutting test parameters.
Table 2. Cutting test parameters.
Cutting MethodLubrication ConditionCutting Speed v (m/min)Feed Rate f (mm/rev)Depth of Cut ap (mm)
CTDry200.10.1
MQL
GN-MQL
DN-MQL
GN+DN-MQL
UVATDry
MQL
GN-MQL
DN-MQL
GN+DN-MQL
CT: conventional turning; UVAT: ultrasonic vibration-assisted turning; MQL: minimum quantity lubrication with palm oil as lubricant; GN-MQL: MQL using graphene nanosheets mixed in palm oil; DN-MQL: MQL using diamond nanoparticles mixed in palm oil; GN+DN-MQL: MQL using diamond/graphene hybrid mixed in palm oil.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Liu, G.; Wang, J.; Zheng, J.; Ji, M.; Wang, X. An Experimental Study on Ultrasonic Vibration-Assisted Turning of Aluminum Alloy 6061 with Vegetable Oil-Based Nanofluid Minimum Quantity Lubrication. Lubricants 2023, 11, 470. https://doi.org/10.3390/lubricants11110470

AMA Style

Liu G, Wang J, Zheng J, Ji M, Wang X. An Experimental Study on Ultrasonic Vibration-Assisted Turning of Aluminum Alloy 6061 with Vegetable Oil-Based Nanofluid Minimum Quantity Lubrication. Lubricants. 2023; 11(11):470. https://doi.org/10.3390/lubricants11110470

Chicago/Turabian Style

Liu, Guoliang, Jin Wang, Jintao Zheng, Min Ji, and Xiangyu Wang. 2023. "An Experimental Study on Ultrasonic Vibration-Assisted Turning of Aluminum Alloy 6061 with Vegetable Oil-Based Nanofluid Minimum Quantity Lubrication" Lubricants 11, no. 11: 470. https://doi.org/10.3390/lubricants11110470

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop