Next Article in Journal
Influence of Co-Catalysts and Polymerization Conditions on Properties of Poly(anhydride-alt-epoxide)s from ROCOP Using Salen Complexes with Different Metals
Previous Article in Journal
Printability and Tensile Performance of 3D Printed Polyethylene Terephthalate Glycol Using Fused Deposition Modelling
Previous Article in Special Issue
Degradation Behavior In Vitro of Carbon Nanotubes (CNTs)/Poly(lactic acid) (PLA) Composite Suture
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 7
10.3390/polym11071221
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Anionic Polymerization of β-Butyrolactone Initiated with Sodium Phenoxides. The Effect of the Initiator Basicity/Nucleophilicity on the ROP Mechanism

by
Adrian Domiński
1,
Tomasz Konieczny
1,
Magdalena Zięba
1,
Magdalena Klim
1 and
Piotr Kurcok
1,2,*
1
Centre of Polymer and Carbon Materials, Polish Academy of Sciences, 34, M. Curie-Sklodowskiej St., 41-819 Zabrze, Poland
2
Faculty of Mathematics and Natural Science, Jan Dlugosz University in Czestochowa, 13/15, Armii Krajowej Ave., 42-200 Czestochowa, Poland
*
Author to whom correspondence should be addressed.
Polymers 2019, 11(7), 1221; https://doi.org/10.3390/polym11071221
Submission received: 14 June 2019 / Revised: 16 July 2019 / Accepted: 20 July 2019 / Published: 22 July 2019
(This article belongs to the Special Issue Biodegradable Polymers - Where We Are and Where to Going)
Browse Figures
Versions Notes

Abstract

:
It was shown that selected sodium phenoxide derivatives with different basicity and nucleophilicity, such as sodium p-nitrophenoxide, p-chlorophenoxide, 1-napthoxide, phenoxide and p-methoxyphenoxide, are effective initiators in anionic ring-opening polymerization (AROP) of β-butyrolactone in mild conditions. It was found that phenoxides as initiators in anionic ring-opening polymerization of β-butyrolactone behave as strong nucleophiles, or weak nucleophiles, as well as Brønsted bases. The resulting polyesters possessing hydroxy, phenoxy and crotonate initial groups are formed respectively by the attack of phenoxide anion at (i) C2 followed by an elimination reaction with hydroxide formation, (ii) C4 and (iii) abstraction of acidic proton at C3. The obtained poly(3-hydroxybutyrate) possesses carboxylate growing species. The ratio of the observed initial groups strongly depends on the basicity and nucleophilicity of the sodium phenoxide derivative used as initiator. The proposed mechanism of this polymerization describes the reactions leading to formation of observed end groups. Moreover, the possibility of formation of a crotonate group during the propagation step of this polymerization is also discussed.

1. Introduction

Poly(β-hydroxyalkanoate)s (PHAs) are biodegradable and biocompatible aliphatic polyesters [1], considered to be future “green” materials for biomedical, food package or drug delivery applications [2,3,4]. Several PHAs are produced by many different microorganisms [5], but the most well-known is poly([R]-3-hydroxybutyrate) (PHB). Isotactic PHB is a biopolymer produced by microorganisms and used as an energy and carbon source [6]. Synthetic and natural poly(3-hydroxybutyrate)s are very popular for biomedical applications due to their biodegradation and biocompatibility [2,3,4,7]. Poly([R]-3-hydroxybutyrate) is synthesized by biotechnological processes, applying bacterial fermentation of substrates such as sucrose, corn, cane sugar, etc. [8], or as a result of a chemical reaction, i.e., polymerization of β-butyrolactone (4-methyl-2-oxetanone, BL), using coordination, cationic or anionic ring-opening polymerization [9].
Coordination polymerization allows for obtaining atactic, syndiotactic and perfectly isotactic PHB depending on the type of coordination catalyst used as well as the way of conducting the reaction. The most common coordination catalysts are based on metals such as aluminum, tin, yttrium, zinc and lanthane [10,11,12,13]. The polymerization of β-butyrolactone can also be carried out using cationic initiators such as trifluoromethanesulfonic acid or hexafluorophosphate. However, the cationic polymerization is characterized by a low molar mass of the resulting polymer, which seems to be unattractive [14,15].
Anionic ring-opening polymerization (AROP) of BL is considered one of the most interesting methods, due to the simplicity of the reaction, lack of toxicity of the resulting polymer, inexpensive catalysts and the possibility of preparation of tailor-made materials. Additionally, AROP allows for obtaining poly(3-hydroxybutyrate) with the desired microstructure depending on the absolute configuration of the monomer used (R, S or a R,S mixture) and the method of carrying out the reaction [16,17,18]. Since the 1990s, many scientists have described the mechanism of anionic ring-opening polymerization of β-butyrolactone with various initiators, i.e., alkali metal alkoxides, carboxylates, naphthalenides, hydrides or basic organocatalysts. These studies have shown that the initiation step of β-butyrolactone polymerization strongly depends on the type of anionic initiator used [16,18,19,20].
When alkali metal naphthalenide is used in BL anionic polymerization, the initiation of β-lactone ring-opening polymerization occurs as a result of exclusive deprotonation at the C3 carbon of the BL ring by the naphthalenide. The unstable enolate formed in this reaction is rearranged to the crotonic acid salt. The unsaturated acid salt formed is a real initiator of the polymerization, where centers of propagation are carboxylate ions [19,21]. The same situation occurs in the case of applying an alkali metal hydride as an initiator in the BL polymerization process [22,23]. Recently, basic organocatalysts like guanidine (TBD), amidine (DBU) and phosphazene (BEMP) were investigated as β-lactone initiators due to efficient polymerization of BL in mild conditions [24,25]. In addition, Coulembier et al. [26] proved that polymerization of BL initiated with TBD mainly proceeds with initial deprotonation of β-lactone and crotonate with a protonated base counterion (e.g., TBDH+) formed as a real initiator of this polymerization [20,26]. In the case of the β-lactone ring opening with potential covalent linkage initiator-3-hydroxyalkanoate unit formation, there are two main classes of initiators described: weak nucleophiles such as carboxylic acid salts and strong nucleophiles, i.e., alkali metal alkoxides (see Figure 1).
In β-lactones AROP, the initiation reaction by a weak nucleophile, e.g., a salt of carboxylic acids, proceeds according to the SN2 mechanism. The initiator attacks the C4 carbon of the β-lactone ring with alkyl-oxygen bond cleavage (b in Figure 1). The carboxylate ion formed in this reaction is a center of the chain growth. The activity of the initiator and the chain propagation center strongly depend on the cation–anion interactions, the size of the counterion and the solvent polarity. The activity of the initiating system can be easily manipulated [27,28,29,30,31]. When the polymerization initiator is an alkali metal alkoxide, which is a strong base and a strong nucleophile, the reaction proceeds according to the addition–elimination mechanism. The initiator attack occurs at carbonyl carbon C2 and the ring opens in the acyl-oxygen position (a in Figure 1). However, the polymer chain growing center type (alcoholate or carboxylate) strongly depends on the β-lactone structure, i.e., the presence of substituents at the C3 carbon of the lactone ring [32,33]. In the case of β-butyrolactone, the crotonate and 3-hydroxybutyrate salts generated in the preinitiation step are the real initiators in this anionic ROP. The chain growth takes place entirely via carboxylate active centers, which leads to the formation of poly([R,S]-3-hydroxybutyrate) containing hydroxy and crotonate initial groups and carboxylic end groups [34,35,36,37].
The aim of the present work was to investigate the mechanism of anionic ring-opening polymerization of BL initiated with selected sodium phenoxides, i.e., weak nucleophiles/bases with the alkoxide structure of active species. Particular attention was paid to the initiation of polymerization, i.e., the reaction of β-lactone molecule with selected phenoxides possessing different basicity/nucleophilicity.

2. Materials and Methods

2.1. Materials

β-Butyrolactone (+98% Aldrich, Steinheim, Germany) was purified as described in [37]. Phenol and 1-naphthol (both +98% POCH, Gliwice, Poland) were purified by sublimation before use. p-Nitrophenol, p-chlorophenol and p-methoxyphenol (all +99%, Aldrich, Steinheim, Germany) were used as received. All sodium phenoxides were prepared by potentiometric titration of the respective phenol water solution with 1M NaOH. Next the water was stripped-off from the reaction mixture and all obtained salts were dried under vacuum at 60 °C for 48 h. 18-Crown-6 ether (+99% Aldrich, Steinheim, Germany) was dried under vacuum at 55 °C overnight before use. Dowex 50WX8 (Aldrich, Steinheim, Germany) was washed with dry THF before use. DMSO (POCH, Gliwice, Poland) was distilled under reduced pressure over CaH2 followed by two repetitions of reduced pressure distillation over BaO. THF (POCH, Gliwice, Poland) was distilled over a potassium-sodium alloy. CHCl3, hexane, KMnO4, NaOH (all POCH, Gliwice, Poland) were used as received.

2.2. Methods

1H NMR (600 MHz) spectra were recorded using a Bruker-Avance II 600 MHz (Fremont, CA, USA) with Ultrashield Plus Magnets at r.t. in CDCl3 or DMSO-d6 with tetramethylsilane (TMS) as an internal standard.
Size exclusion chromatography (SEC) was conducted in CHCl3 at 35 °C with a flow rate of 1 mL/min, using a Spectra-Physic 8800 gel-permeation chromatograph (Santa Clara, CA, USA), equipped with a PL-gel 5 mm MIXED-E ultra-high efficiency column and Shodex SE 61 differential refractive index detector. Polystyrene standards with a low dispersity mass distribution (Mp ranged from 162 to 19,760 g·mol−1) were used to generate a calibration curve.
Electrospray mass spectrometry (ESI-MSn) was performed using a Finnigan LCQ ion trap mass spectrometer (Finnigan, San Jose, CA, USA). The poly(3-hydroxybutyrate) samples were dissolved in methanol/chloroform mixture (1:1, v/v). The solutions were introduced into the ESI source by continuous infusion at 7 μL·min−1 using the instrument’s syringe pump. The LCQ ESI source was set to an operating voltage of 4.5 kV and the capillary heater was set to 200 °C. Nitrogen was used as the nebulizing gas. Helium was used as the collision and damping gas in the ion trap.
GC-MS was performed using an Agilent gas chromatograph 7890C (HP-5 MS capillary column, 30 m × 0.25 mm × 0.25 μm), coupled with an Agilent mass spectrometer with EI ionization (70 eV). Products were identified using the NIST-EPA-NIH Mass Spectral Database.
Fourier transform infrared (FTIR) spectra were recorded on a Jasco FT-IR 6700 spectrometer (Tokyo, Japan) equipped with a MultiLoop-MIR Silver Halide Probe Set in the region between 2000 and 800 cm−1 with 128 scans.

2.3. General Polymerization Procedure

The polymerizations were performed in an anhydrous atmosphere (glove-box, H2O < 1 ppm). Ring-opening polymerization of β-butyrolactone initiated with selected phenoxide was carried out in dry DMSO (or in THF with the addition of 18-C-6 crown ether in molar ratio 1:1 as a cation-complexing agent) at the monomer concentration equal to 1 mol/L or 8 mol/L at room temperature. Conversion of the monomer was monitored by using FTIR spectroscopy (disappearance of the band derived from the carbonyl group β-butyrolactone at 1820 cm−1). The polymerization reaction was quenched by acidification with Dowex 50WX8. The obtained polymer was precipitated in cold hexane, dried under vacuum to constant weight and characterized by 1H NMR, ESI-MSn and SEC techniques. The filtrate obtained after polymer precipitation was analyzed by using the GC-MS technique.

3. Results and Discussion

In the present work, it is shown that various sodium phenoxides obtained by the use of phenols with different pKa values, such as: p-nitrophenol, p-chlorophenol, 1-napthol, phenol, and p-methoxyphenol, are effective initiators of β-butyrolactone AROP in mild conditions. As mentioned in the Introduction, alkoxides attack at the C2 carbon, while the carboxylic acid salts at the C4 one in the BL monomer. In both cases, there are significant differences in the basicity and nucleophilicity of both types of initiators and different starting groups were observed in the polymer chain as a result. It prompted us to investigate the polymerization of BL initiated with selected sodium phenoxides, i.e., a group of compounds that are weak nucleophiles, but with an alkoxide structure. The basicity/nucleophilicity of these initiators can be easy adjusted by application of an appropriate substituent in the phenoxide ring. In the anionic polymerization of BL initiated with alkali metal alkoxides and carboxylates, usually activation of an initiator is required. In this study, applied sodium phenoxides were activated by sodium counterion complexation with crown ether when the polymerization was carried out in THF or by using the solvent strongly activating anionic initiator i.e., DMSO [27]. Most of AROP experiments were performed in DMSO. Therefore, the basicity of the initiators used, based on the pKa of selected phenols (in DMSO) [38], was as follows: p-NO2PhONa < p-ClPhONa < NapthONa < PhONa < p-CH3OPhONa).
The results presented in Table 1 show that all five selected phenoxides initiated polymerization efficiently, and PHB with a controlled number average molar mass up to 10,000 g/mol with an acceptable level of dispersity (Đ c.a. 1.2) was synthesized. However, it is very important in such polymerization to select the proper conditions of the process. In entries 6–10 (Table 1), the measured MnSEC indicates the loss of PHB molar mass control. This can be explained by the competition of propagation and side reactions, e.g., chain transfer to the polymer proceeding via the E1cB (elimination unimolecular conjugate base) mechanism [39,40], resulting in polymer degradation. Due to low initial monomer concentration (1mol/L), the reaction rate is slow and transfer to the polymer can be competed with propagation. However, when the monomer concentration was increased up to 8 mol/L, it was possible to obtain the polymer with the expected molar mass (see entries 11 and 12). Moreover, chain transfer to the monomer was also possible in this polymerization, although the obtained results seem to indicate that in fact transfer to the polymer is responsible for the significant reduction in molar mass observed in this polymerization (see entries 6–10).
Results of 1H NMR and ESI-MSn analyses revealed that the poly(3-hydroxybutyrate)s obtained in AROP initiated with the selected phenoxides possess carboxyl end groups and three different types of initial groups: crotonate, phenoxy and hydroxy, occurring in different ratios, depending on the phenoxide used. A typical 1H NMR spectrum of low molar mass PHB obtained in the polymerization initiated with sodium phenoxide shows the polymer chain characteristic signals: (CH3 at δ = 1.28 ppm, CH2 = 2.5 ppm, CH = 5.25 ppm) and signals corresponding to initial groups: (HO–CH at δ = 4.2 pm, PhO–CH at 4.8 ppm and CH3CH=CH at 5.8 ppm) (Figure 2).
Analysis of an ESI-MSn spectra (Figure 3) of PHB obtained in the reaction initiated with sodium phenoxide shows three different signals populations in the investigated polymer. The most intensive population (cn) corresponds to adducts of α-hydroxy-ω-carboxylate-PHB chains with Na+, e.g., m/z = 1073.2 g/mol for n = 11. The second signal population (an) assigned to α-crotonate-ω-carboxylate-PHB chain adducts with Na+ (e.g., the peak with m/z = 1141.2 for n = 13) and finally, the population (bn) corresponds to α-phenoxy-ω-carboxylate-PHB chain adducts with Na+ (m/z = 1063.2 for n = 11). These results are clear evidence that the polyester obtained contains molecules with crotonate, phenoxy and hydroxy initial groups and carboxyl end groups.
The nature of PHB chain initial groups confirmed by 1H NMR and ESI-MS indicates that, at the initiation step of AROP, ring-opening of the BL monomer occurs at the acyl-oxygen and alkyl-oxygen positions, i.e., similar to BL polymerization initiated with weak nucleophiles (SN2 at carbon C4) as well as strong nucleophiles (addition–elimination mechanism) (Scheme 1).
The phenoxide anion reacts as a nucleophile in a substitution reaction (i) or as base in an elimination one (ii). The substitution reaction occurs at the C4 and C2 carbon. When the phenoxide behaves like a weak nucleophile and attacks the C4 carbon atom of the BL, the alkyl-oxygen bond scission takes place and respective 3-phenoxybutyrate 1 is formed. As a consequence of this, polymer chains with 3-phenoxybutyrate initial groups and carboxylate growing species are formed.
The chains with hydroxyl initial groups observed in NMR and ESI-MS spectra are formed when the phenoxide reacts like an alkoxide, i.e., by the addition of a phenoxide anion to the lactone with the ring opening in the acyl-oxygen position, according to the nucleophilic substitution mechanism at the carbonyl carbon (C2) giving unstable β-alkoxide ester 2. After the elimination reaction phenyl crotonate 3 and sodium hydroxide were formed [28,33,41]. Presence of phenyl crotonate in the filtrate after polymer isolation was confirmed by the GC-MS technique (see Figure S1 in Supplementary). Then, NaOH reacts with the next BL molecule. As a result of the hydroxyl anion attack on the C2 acyl carbon, proceeding with the acyl-oxygen bond scission, an unstable intermediate product, β-hydroxyester alkoxide 4, is formed. Next in the acid-base reaction, 3-hydroxybutyric acid salt 5 is formed. Such a salt can partially eliminate water with formation of crotonic acid salt. The obtained sodium salts of 3-hydroxyacid and crotonic acid initiate further polymerization according to the mechanism of polymerization with weak nucleophiles and macromolecules with hydroxyl and crotonate initial groups, and carboxylate propagation centers are present in the reaction mixture.
Crotonate initial groups may also be formed when the phenoxide behaves as a Brønsted base, i.e., it abstracts the acidic proton of a monomer methylene group with formation of lactone enolate, which undergoes an elimination reaction to form a crotonate anion, initiating further polymerization. The α-deprotonation reaction generates a phenol, whose presence was confirmed by GC-MS (see Figure S1 in Supplementary). However, the formation of the crotonate end groups, as a result of the chain transfer to the polymer occurring according to the E1cB mechanism, has to also be taken into account. In BL AROP, crotonate end-groups in polyester are usually present and their quantitative elimination seems to be almost impossible.
The growing species in the investigated processes were carboxylate ones, independent of the phenoxide used. However, the ratio of the respective initial group in the polymer strongly depends on the nucleophilicity and basicity of the initiator.
The basicity of the initiators varied across a medium range, as all initiators were synthesized from phenol derivatives with a pKa from 10.2 (p-nitrophenol) to 19.1 (p-methoxyphenol). The second important feature of these phenoxides is their nucleophilicity, which is responsible for the nucleophilic attack at the C2 or C4 carbon of the β-butyrolactone ring respectively. Therefore, the order of the basicity/nucleophilicity (p-NO2PhO−< p-ClPhO− < NapthO− < PhO− < p-CH3OPhO−) of initiators used is important to discuss further results. It was found that the ratio of respective initial groups in obtained polymers strongly depends on the basicity/nucleophilicity of the initiator used (Figure 4).
The presented results indicate that depending on the sodium phenoxide derivatives used as initiators in BL polymerization, the attack at the C4 carbon of the monomer mainly occurs with formation of polymer chains, with 89.8% of 3-phenoxybutyrate initial groups. Low content of polymer chains with crotonate as the initial group (7.9%) is probably due to the monomer elimination reaction and chain transfer to the polymer, both proceeding according to the E1cB mechanism. Observed traces of hydroxyl groups (2.3%) result from the attack of an initiator at the carbonyl carbon (C2) of BL (see Scheme 1). Results showed that increasing nucleophilicity and basicity of the initiator increased the number of initial hydroxyl groups derived from the initiator attack on C2 carbon at the cost of decreasing the amount of phenoxy groups. In the case of polymerization initiated with p-methoxyphenoxide (the most nucleophilic initiator), the resulting polymer possesses 67.2% of chains with 3-hydroxybutyrate initial groups and only 15.9% of phenoxybutyrate ones. Moreover, the increase of initiator basicity affects the α-deprotonation reaction and increases the content of polyester crotonate groups up to 17%. A further increase of initiator basicity results in the entire α-deprotonation reaction, and the polymer formed possesses only crotonate initial groups [22,26].
It is worth noticing that the initiator basicity and nucleophilicity affects only the mechanism and kinetics of the initiation reaction. The kinetics of the chain propagation reaction does not depend on the initiator used, because carboxylate anions are the polymer chain growing species in all described BL anionic polymerizations when the reaction is carried out in the same conditions (solvent, complexing agent, etc.).
In the BL polymerization initiated with sodium naphthoxide, the results are different from the trend observed for the studied phenoxides, although its basicity is located between p-chlorophenoxide and phenoxide. Initial group analysis shows that the naphthoxide anion behaves like a p-nitrophenoxide, i.e., the weakest nucleophile and base from the initiators used. It mainly attacks at the C4 carbon of the BL ring. The resulting polymer possesses mainly 3-naphthoxybutyrate initial groups (89.7%) but also a small content of crotonate (6%) and hydroxyl (4,3%) initial groups is observed. Such behavior is probably caused by a steric effect of the naphthyl ring. According to Burgi and Dunitz [42], a nucleophile attacks the carbonyl carbon along a trajectory, where the angle between the nucleophilic attack path and the orientation of the carbonyl group is higher than 90°. The attack of a large naphthoxide anion at carbonyl carbon C2 of BL is very problematic in such a small and strained ring. Therefore, the attack at the alkyl carbon C4 of the ring is preferred, independent of the initiator basicity/nucleophilicity.

4. Conclusions

It was found that the mechanism of initiation in anionic polymerization of BL strongly depends on the nucleophilicity and basicity of the initiator used. When strong nucleophiles, e.g., alkali metal methoxide, are applied, the initiation reaction occurs via addition-elimination and the initiator is not incorporated into the polymer chain [32,33,34]. In the case of strong bases, such as superbases or potassium hydride, in the initiation reaction, monomer deprotonation at C2 is definitely the main reaction leading to formation of crotonate acting as the real initiator of the polymerization [22,26]. However, weak nucleophiles and bases such as carboxylate anions initiate the BL polymerization process due to a SN2 reaction at the C4 carbon of the monomer. Obtained results of BL polymerization initiated with selected sodium phenoxide derivatives indicate clearly that the structure of the initiator active species does not affect the initiation mechanism. The main factor of the mechanism of β-butyrolactone ring opening is definitely the basicity and nucleophilicity of the initiator and phenoxide with the lowest basicity, i.e., the sodium p-nitrophenolate reacts mainly like a weak nucleophile. The nucleophile attack mainly occurs at the C4 carbon with formation of 3-p-nitrophenoxybutyrate. Analysis of the reaction products also shows generation of small amounts of sodium crotonate and sodium 3-hydroxybutyrate formed in the reaction, where the phenolate behaves as a base (BL α-deprotonation) and strong nucleophile (attack at the carbon C2). Such initiation resulted in formation of macromolecules with phenoxy, hydroxy and crotonate initial groups and carboxylate growing species. In all investigated BL polymerizations initiated with phenoxides, formation of similar polymer end groups was observed, however, the mutual molar ratio of the initial groups significantly depended on phenoxide basicity and nucleophilicity. In the case of the use of sodium p-methoxyphenoxide, the most basic, but also the most nucleophilic of the initiators applied in this study, macromolecules possessing hydroxy initial groups predominated. It is important that, depending on the basicity and the nuleophilicity of the initiator used, the initiation reaction in anionic β-butyrolactone polymerization proceeds in various ways, but ultimately the centers of chain growth are usually carboxylate ones. Therefore, due to a relatively fast initiation reaction, the growth of the chain determines the rate of polymerization, and under similar conditions, the rate of these polymerizations does not depend on the sodium phenoxide derivative used as the initiator. Naturally, the polymerization rate may be controlled by the counterion diameter and/or polarity of the solvent, which affects the growing species nucleophilicity. Moreover, it is important in BL anionic polymerization to select a proper monomer concentration that is favorable for polymer formation to avoid a base-catalyzed polymer degradation reaction.

Supplementary Materials

The following are available online at https://www.mdpi.com/2073-4360/11/7/1221/s1, Figure S1: GC-MS spectrum of filtrate obtained via AROP of BL initiated with sodium phenoxide after polymer precipitation.

Author Contributions

P.K. and A.D. were the main persons involved in the planning of the experiments; A.D. and T.K. were responsible for syntheses of polymers; P.K., A.D., M.Z. and M.K. were responsible for analysis and interpretation; A.D.—writing—original draft preparation; P.K. review and editing.

Funding

This research received no external funding.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Steinbüchel, A. Perspectives for biotechnological production and utilization of biopolymers: Metabolic engineering of polyhydroxyalkanoate biosynthesis pathways as a successful example. Macromol. Biosci. 2001, 1, 1–24. [Google Scholar] [CrossRef]
  2. Philip, S.; Keshavarz, T.; Roy, I. Polyhydroxyalkanoates: biodegradable polymers with a range of applications. J. Chem Technol Biotechnol. 2007, 82, 233–247. [Google Scholar] [CrossRef]
  3. Raza, Z.A.; Abid, S.; Banat, I.M. Polyhydroxyalkanoates: Characteristics, production, recent developments and applications. Int. Biodeter. Biodegr. 2018, 126, 45–56. [Google Scholar] [CrossRef]
  4. Shabina, M.; Afzal, M.; Hameed, S. Bacterial polyhydroxyalkanoates-eco-friendly next generation plastic: Production, biocompatibility, biodegradation, physical properties and applications. Green Chem. Lett. Rev. 2015, 8, 56–77. [Google Scholar] [Green Version]
  5. Anjum, A.; Zuber, M.; Zia, K.M.; Noreen, A.; Anjum, M.N.; Tabasum, S. Microbial production of polyhydroxyalkanoates (PHAs) and its copolymers: A review of recent advancements. Int. J. Biol. Macromol. 2016, 89, 161–174. [Google Scholar] [CrossRef] [PubMed]
  6. Jiang, G.; Hill, D.J.; Kowalczuk, M.; Johnston, B.; Adamus, G.; Iorere, V.; Radecka, I. Carbon Sources for Polyhydroxyalkanoates and an Integrated Biorefinery. Int. J. Mol. Sci. 2016, 17, 1157. [Google Scholar] [CrossRef] [PubMed]
  7. Piddubnyak, V.; Kurcok, P.; Matuszowicz, A.; Głowala, M.; Fiszer-Kierzkowska, A.; Jedliński, Z.; Juzwa, M.; Krawczyk, Z. Oligo-3-hydroxybutyrates as potential carriers for drug delivery. Biomaterials 2004, 25, 5271–5279. [Google Scholar] [CrossRef]
  8. Suriyamongkol, P.; Weselake, R.; Narine, S.; Moloney, M.; Shah, S. Biotechnological approaches for the production of polyhydroxyalkanoates in microorganisms and plants—A review. Biotechnol. Adv. 2007, 25, 148–175. [Google Scholar] [CrossRef]
  9. Tian, H.; Tang, Z.; Zhuang, X.; Chen, X.; Jing, X. Biodegradable synthetic polymers: Preparation, functionalization and biomedical application. Progr. Polym. Sci. 2012, 37, 237–280. [Google Scholar] [CrossRef]
  10. Tang, X.; Chen, E.Y.-X. Chemical synthesis of perfectly isotactic and high melting bacterial poly(3-hydroxybutyrate) from bio-sourced racemic cyclic diolide. Nat. Commun. 2018, 9, 2345. [Google Scholar] [CrossRef]
  11. Fang, J.; Tschan, M.J.L.; Roisnel, T.; Trivelli, X.; Gauvin, R.M.; Thomas, C.M.; Maron, L. Yttrium catalysts for syndioselective β-butyrolactone polymerization: on the origin of ligand-induced stereoselectivity. Polym. Chem. 2013, 4, 360–367. [Google Scholar] [CrossRef]
  12. Rieth, L.R.; Moore, D.R.; Lobkovsky, E.B.; Coates, G.W. Single-Site β-Diiminate Zinc Catalysts for the Ring-Opening Polymerization of β-Butyrolactone and β-Valerolactone to Poly(3-hydroxyalkanoates). J. Am. Chem. Soc. 2002, 124, 15239–15248. [Google Scholar] [CrossRef] [PubMed]
  13. Liu, Y.-C.; Lin, C.-H.; Ko, B.-T.; Ho, R.-M. Ring-Opening Polymerization of β-Butyrolactone Catalyzed by Efficient Magnesium and Zinc Complexes Derived from Tridentate Anilido-Aldimine Ligand. J. Polym. Sci. Polym. Chem. 2010, 48, 5339–5347. [Google Scholar] [CrossRef]
  14. Okamoto, Y. Cationic Ring-Opening Polymerization of Lactones in the presence of alcohol. Makromol. Chem. Macromol. Symp. 1991, 42/43, 117–133. [Google Scholar] [CrossRef]
  15. Jaipuri, F.A.; Bower, B.D.; Pohl, N.L. Protic acid-catalyzed polymerization of β-lactones for the synthesis of chiral polyesters. Tetrahedron: Asymmetr. 2003, 14, 3249–3252. [Google Scholar] [CrossRef]
  16. Jedliński, Z.; Kurcok, P.; Lenz, R.W. First Facile Synthesis of Biomimetic Poly-(R)-3-hydroxybutyrate via Regioselective Anionic Polymerization of (S)-β-Butyrolactone. Macromolecules 1998, 31, 6718–6720. [Google Scholar] [CrossRef]
  17. Jedliński, Z. Regioselective Ring-Opening Anionic Polymerization of β-lactones. Macromol. Symp. 1998, 132, 377–383. [Google Scholar] [CrossRef]
  18. Jedliński, Z.; Kowalczuk, M.; Kurcok, P.; Adamus, G.; Matuszowicz, A.; Sikorska, W.; Gross, R.A.; Xu, J.; Lenz, R.W. Stereochemical Control in the Anionic Polymerization of β-Butyrolactone Initiated with Alkali-Metal Alkoxides. Macromolecules 1996, 29, 3773–3777. [Google Scholar] [CrossRef]
  19. Kowalczuk, M.; Kurcok, P.; Główkowski, W.; Jedliński, Z. New Reactions of Potassium Naphthalenide with β-, γ- and β-Lactones: An Efficient Route to α-Alkyl γ- and β-Lactones and α,β-Unsaturated Carboxylic Acid Esters. J. Org. Chem. 1992, 57, 391–393. [Google Scholar] [CrossRef]
  20. Khalil, A.; Cammas-Marion, S.; Coulembier, O. Organocatalysis Applied to the Ring-Opening Polymerization of β-Lactones: A Brief Overview. J. Polym. Sci. Part A 2019, 57, 657–672. [Google Scholar] [CrossRef]
  21. Jedliński, Z.; Kowalczuk, M. Novel Degradable Engineering Polyesters-Synthesis and Applications. Intern. J. Polymeric Mater. 1994, 24, 253–261. [Google Scholar] [CrossRef]
  22. Kurcok, P.; Matuszowicz, A.; Jedliński, Z. Anionic polymerization of β-lactones initiated with potassium hydride. A convenient route to polyester macromonomers. Macromol. Rapid Commun. 1995, 16, 201–206. [Google Scholar] [CrossRef]
  23. Lenz, R.W.; Jedliński, Z. Anionic and Coordination Polymerization of 3-butyrolactone. Macromol. Symp. 1996, 107, 149–161. [Google Scholar] [CrossRef]
  24. Jaffredo, C.G.; Carpentier, J.-F.; Guillaume, S.M. Controlled ROP of β-Butyrolactone Simply Mediated by Amidine, Guanidine, and Phosphazene Organocatalysts. Macromol. Rapid Commun. 2012, 22, 1938–1944. [Google Scholar] [CrossRef] [PubMed]
  25. Jaffredo, C.G.; Carpentier, J.-F.; Guillaume, S.M. Organocatalyzed controlled ROP of β-lactones towards poly(hydroxyalkanoate)s: from β-butyrolactone to benzyl β-malolactone polymers. Polym. Chem. 2013, 4, 3837–3850. [Google Scholar] [CrossRef]
  26. Moins, S.; Henoumont, C.; De Winter, J.; Khalil, A.; Laurent, S.; Cammas-Marion, S.; Coulembier, O. Reinvestigation of the Mechanism of Polymerization of β-Butyrolactone from 1,5,7-Triazabicyclo [4.4.0]dec-5-ene. Polym. Chem. 2018, 9, 1840–1847. [Google Scholar] [CrossRef]
  27. Kawalec, M.; Śmiga-Matuszowicz, M.; Kurcok, P. Counterion and solvent effects on the anionic polymerization of β-butyrolactone initiated with acetic acid salts. Eur. Polym. J. 2008, 44, 3556–3563. [Google Scholar] [CrossRef]
  28. Kurcok, P.; Jedliński, Z.; Kowalczuk, M. Reactions of β-Lactones with Potassium Alkoxides and Their Complexes with 18-Crown-6 in Aprotic Solvents. J. Org. Chem. 1993, 58, 4219–4220. [Google Scholar] [CrossRef]
  29. Juzwa, M.; Jedliński, Z. Novel Synthesis of Poly(3-hydroxybutyrate). Macromolecules 2006, 39, 4627–4630. [Google Scholar] [CrossRef]
  30. Kurcok, P.; Śmiga, M.; Jedliński, Z. β-Butyrolactone Polymerization Initiated with Tetrabutylammonium Carboxylates: A Novel Approach to Biomimetic Polyester Synthesis. J. Polym. Sci. Polym. Chem. 2002, 40, 2184–2189. [Google Scholar] [CrossRef]
  31. Adamus, G.; Kowalczuk, M. Anionic Ring-Opening Polymerization of β-Alkoxymethyl-Substituted β-Lactones. Biomacromolecules 2008, 9, 696–703. [Google Scholar] [CrossRef] [PubMed]
  32. Jedliński, Z.; Kurcok, P.; Kowalczuk, M.; Matuszowicz, A.; Dubois, P.; Jerome, R.; Kricheldor, H.R. Anionic Polymerization of Pivalolactone Initiated by Alkali Metal Alkoxides. Macromolecules 1996, 28, 7276–7280. [Google Scholar] [CrossRef]
  33. Kurcok, P.; Kowalczuk, M.; Hennek, K.; Jedliński, Z. Anionic Polymerization of β-Lactones Initiated with Alkali-Metal Alkoxides: Reinvestigation of the Polymerization Mechanism. Macromolecules 1992, 25, 2017–2020. [Google Scholar] [CrossRef]
  34. Kurcok, P.; Kowalczuk, M.; Jedliński, Z. Response to “On the Ambident Reactivity of β-Lactones in Their Reactions with Alcoholates Initiating Polymerization”. Macromolecules 1994, 27, 4833–4835. [Google Scholar] [CrossRef]
  35. Grobelny, Z.; Matlengiewicz, M.; Skrzeczyna, K.; Swinarew, A.; Golba, S.; Jurek-Suliga, J.; Michalak, M.; Swinarew, B. Ring-Opening Polymerization of Lactones Initiated with Metal Hydroxide-Activated Macrocyclic Ligands: Determination of Mechanism and Structure of Polymers. Int. J. Polym. Anal. Charact. 2015, 20, 457–468. [Google Scholar] [CrossRef]
  36. Grobelny, Z.; Golba, S.; Jurek-Suliga, J. Ring opening polymerization of β-butyrolactone in the presence of alkali metal salts: investigation of initiation course and determination of polymers structure by MALDI-TOF mass spectrometry. Polym. Bull. 2018. [Google Scholar] [CrossRef]
  37. Kawalec, M.; Coulembier, O.; Gerbaux, P.; Sobota, M.; De Winter, J.; Dubois, P.; Kowalczuk, M.; Kurcok, P. Traces do matter—Purity of 4-methyl-2-oxetanone and its effect on anionic ring-opening polymerization as evidenced by phosphazene superbase catalysis. React. Funct. Polym. 2012, 72, 509–520. [Google Scholar] [CrossRef]
  38. Bordwell pKa Table (Acidity in DMSO). Available online: https://www.chem.wisc.edu/areas/reich/pkatable/ (accessed on 12 June 2019).
  39. Kawalec, M.; Adamus, G.; Kurcok, P.; Kowalczuk, P.; Foltran, I.; Focarete, L.; Scandola, M. Carboxylate induced degradation of poly(3-hydroxybutyrate)s. Biomacromolecules 2007, 8, 1053–1058. [Google Scholar] [CrossRef] [PubMed]
  40. Kawalec, M.; Sobota, M.; Scandola, M.; Kowalczuk, M.; Kurcok, P. A convenient route to PHB macromonomers via anionically controlled moderate-temperature degradation of PHB. J. Polym. Sci., Part A 2010, 48, 5490–5497. [Google Scholar] [CrossRef]
  41. Grobelny, Z.; Stolarzewicz, A.; Morejko, B.; Pisarski, W.; Maercker, A.; Skibinski, A.; Krompiec, S.; Rzepa, J. C–O and Not C–C Bond Cleavage Starts the Polymerization of b-Butyrolactone with Potassium Anions of Alkalide. Macromolecules 2006, 39, 6832–6837. [Google Scholar] [CrossRef]
  42. Borgi, H.B.; Dunitz, J.D.; Lehn, J.M.; Wipff, G. Stereochemistry of reactions paths at carbonyl centres. Tetrahedron 1974, 30, 1563–1572. [Google Scholar] [CrossRef]
Polymers 11 01221 g001 550
Figure 1. β-butyrolactone molecule with carbon description and possible nucleophile attack positions in anionic BL polymerization.
Figure 1. β-butyrolactone molecule with carbon description and possible nucleophile attack positions in anionic BL polymerization.
Polymers 11 01221 g001
Polymers 11 01221 g002 550
Figure 2. 1H NMR spectrum (CDCl3, 600MHz) of poly(3-hydroxybutyrate) obtained via AROP of BL initiated with sodium phenoxide.
Figure 2. 1H NMR spectrum (CDCl3, 600MHz) of poly(3-hydroxybutyrate) obtained via AROP of BL initiated with sodium phenoxide.
Polymers 11 01221 g002
Polymers 11 01221 g003a 550Polymers 11 01221 g003b 550
Figure 3. ESI-MS (positive-ion mode) of poly(3-hydroxybutyrate) obtained via AROP of BL initiated with sodium phenoxide; series an—sodium adducts of α-hydroxy-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1073 is shown in Figure 3b); series bn—sodium adducts of α-crotonate-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1055 is shown in Figure 3c), series cn—α-phenoxy-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1063 is shown in Figure 3a). Index n corresponds to the number of PHB repeating units.
Figure 3. ESI-MS (positive-ion mode) of poly(3-hydroxybutyrate) obtained via AROP of BL initiated with sodium phenoxide; series an—sodium adducts of α-hydroxy-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1073 is shown in Figure 3b); series bn—sodium adducts of α-crotonate-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1055 is shown in Figure 3c), series cn—α-phenoxy-ω-carboxylate-PHB chains (ESI-MS2 fragmentation spectrum (positive-ion mode) of corresponding parent ion m/z 1063 is shown in Figure 3a). Index n corresponds to the number of PHB repeating units.
Polymers 11 01221 g003aPolymers 11 01221 g003b
Polymers 11 01221 sch001 550
Scheme 1. AROP of β-butyrolactone initiated with sodium phenoxide (for simplicity, the Na+ counterion is omitted).
Scheme 1. AROP of β-butyrolactone initiated with sodium phenoxide (for simplicity, the Na+ counterion is omitted).
Polymers 11 01221 sch001
Polymers 11 01221 g004 550
Figure 4. Ratio of crotonate, phenoxy and hydroxy initial groups in the polymer depending on the initiator used (estimated from 1H NMR measurements; pKa values presented in parenthesis correspond to phenols used [38]).
Figure 4. Ratio of crotonate, phenoxy and hydroxy initial groups in the polymer depending on the initiator used (estimated from 1H NMR measurements; pKa values presented in parenthesis correspond to phenols used [38]).
Polymers 11 01221 g004
Table
Table 1. Results of BL polymerization initiated with selected sodium phenoxides a.
Table 1. Results of BL polymerization initiated with selected sodium phenoxides a.
Entry bInitiatorMn,th d [g·mol−1]Mn,NMR e [g·mol−1]Mn,SEC [g·mol−1]Đ
1sodium p-nitrophenoxide1100135013001.19
2sodium p-chlorophenoxide1100115011001.25
3sodium 1-naphtoxide11008008001.22
4sodium phenoxide11009008001.21
5sodium p-methoxyphenoxide11008509501.13
6sodium p-nitrophenoxide10000340038001.62
7sodium p-chlorophenoxide10000305044001.62
8sodium 1-naphtoxide10000300041001.76
9sodium phenoxide10000240046001.90
10sodium p-methoxyphenoxide10000310041001.78
11 csodium phenoxide 100007200102001.27
12 csodium p-nitrophenoxide10000700091001.21
a Polymerizations were carried out in DMSO solvent (BL concentration was 1mol/L) at room temperature up to 100% conversion of monomer; b Polymerization time: entries 1–5: 2 days, entries 6–10: 14 days and entries 11–12: 5 days; c Monomer concentration—8 mol/L; d Calculated form equation: Mnth = [M]0 × 86/[I]0 where [M]0 and [I]0—monomer and initiator concentration, 86—molar mass of BL; e Estimated form 1H NMR from equation: MnNMR = (IpolymCH × 86)/(IPhOCH-+ IHOCH + I=CH).

Share and Cite

MDPI and ACS Style

Domiński, A.; Konieczny, T.; Zięba, M.; Klim, M.; Kurcok, P. Anionic Polymerization of β-Butyrolactone Initiated with Sodium Phenoxides. The Effect of the Initiator Basicity/Nucleophilicity on the ROP Mechanism. Polymers 2019, 11, 1221. https://doi.org/10.3390/polym11071221

AMA Style

Domiński A, Konieczny T, Zięba M, Klim M, Kurcok P. Anionic Polymerization of β-Butyrolactone Initiated with Sodium Phenoxides. The Effect of the Initiator Basicity/Nucleophilicity on the ROP Mechanism. Polymers. 2019; 11(7):1221. https://doi.org/10.3390/polym11071221

Chicago/Turabian Style

Domiński, Adrian, Tomasz Konieczny, Magdalena Zięba, Magdalena Klim, and Piotr Kurcok. 2019. "Anionic Polymerization of β-Butyrolactone Initiated with Sodium Phenoxides. The Effect of the Initiator Basicity/Nucleophilicity on the ROP Mechanism" Polymers 11, no. 7: 1221. https://doi.org/10.3390/polym11071221

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop