Structural and Thermo-Mechanical Properties of Poly(ε-Caprolactone) Modified by Various Peroxide Initiators
Next Article in Special Issue
Isoprene Polymerization: Catalytic Performance of Iminopyridine Vanadium(III) Chloride versus Vanadium(III) Chloride
Previous Article in Journal
Morphology, Crystallinity, and Molecular Weight of Poly(ε-caprolactone)/Graphene Oxide Hybrids
Previous Article in Special Issue
Development of Large-Scale Stopped-Flow Technique and its Application in Elucidation of Initial Ziegler–Natta Olefin Polymerization Kinetics
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 7
10.3390/polym11071100
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Copolymerization of Norbornene and Styrene with Anilinonaphthoquinone-Ligated Nickel Complexes

by
Samiul Islam Chowdhury
,
Ryo Tanaka
,
Yuushou Nakayama
and
Takeshi Shiono
*
Graduate School of Engineering, Hiroshima University, Hiroshima 739-8527, Japan
*
Author to whom correspondence should be addressed.
Polymers 2019, 11(7), 1100; https://doi.org/10.3390/polym11071100
Submission received: 4 June 2019 / Revised: 24 June 2019 / Accepted: 26 June 2019 / Published: 28 June 2019
(This article belongs to the Special Issue Catalytic Polymerization)
Browse Figures
Review Reports Versions Notes

Abstract

:
Poly(norbornene-co-styrene)s were synthesized by the use of anilinonaphthoquinone-ligated nickel complexes [Ni(C10H5O2NAr)(Ph)(PPh3): 1a, Ar = C6H3-2,6-iPr; 1b, Ar = C6H2-2,4,6-Me; 1c, Ar = C6H5] activated with modified methylaluminoxane (MMAO) or B(C6F5)3 in toluene. The effects of the cocatalysts were more significant than those of the nickel complexes, and MMAO gave higher activity than B(C6F5)3. The structural characterizations of the products indicated the formation of statistical norbornene copolymers. An increase of the styrene ratio in feed led to an increase in the incorporated styrene (S) content of the resulting copolymer. The molecular weight of the copolymer decreased with increasing the S ratio in feed at 70 °C. The copolymerization activity, using MMAO as a cocatalyst, decreased with lowering of the temperature from 70 to 0 °C, accompanied by an increase in the molecular weight of the copolymer. The S incorporation up to 59% with Mn of 78,000 was achieved by the 1b-B(C6F5)3 catalytic system. The glass transition temperatures of the norbornene (N)/S copolymers determined by differential scanning calorimetry, decreased from 329 to 128 °C according to the S content.

Graphical Abstract

1. Introduction

The polymerization of cycloolefins such as norbornene (N) has been one of the key developments in the area of polymer chemistry because of its vast range of applications [1,2,3]. There are three types of mechanism for polymerization of N, which are ring-opening metathesis polymerization (ROMP) [4,5], cationic or radical polymerization [6,7,8,9], and coordination–insertion polymerization [10,11,12]. Each route of the polymerization leads to the polymers with different structures and properties. Polynorbornenes (PNBs) produced by coordination–insertion polymerization show excellent physical properties, such as good heat and chemical resistance, high decomposition temperature, high optical transparency, and low dielectric constant [13,14], but exhibit some negative properties such as brittleness and glass transition temperature (Tg) close to the decomposition temperature due to the presence of a rigid ring in the polymer chain.
The inferior properties of PNBs can be improved in cyclic olefin copolymers (COCs). The most representative COC is a copolymer of N and ethylene (E) [15]. The properties of COCs can be easily controlled by a kind of comonomer, comonomer content, and sequence distribution. Copolymerization of N with 1-alkene was also reported to modify the physical properties [16,17,18,19,20,21,22,23,24]. The introduction of styrene (S) should decrease the birefringence of COCs [25] because PNB and polystyrene possess positive and negative birefringence, respectively. Several examples of the copolymerization of N with S have been reported. The first N/S copolymerization was achieved by Ni-based catalysts using methylaluminoxane (MAO) as a cocatalyst [26]. Afterwards, some nickel and copper catalysts were used to synthesize N/S copolymers [27,28,29,30,31,32,33]. The S incorporation was improved by β-diketiminato nickel complexes [34]. The highest S incorporation was 52.4%, with the highest S feed ratio of 83%, but the Mw value was around 103. Recently, bis(β-ketoamino) copper complexes were used for copolymerization of N and S, whereas the results were almost the same as those of β-diketiminato nickel complexes [35].
We have also reported N/S copolymerization by an ansa-fluorenylamidodimethyltitanium-based catalyst and shown the potentiality of the copolymer as a plastic substrate for flexible display materials [25]. However, the maximum S incorporation in the N/S copolymer with sufficient molecular weight was approximately 5 mol %. We have synthesized N/E/S terpolymer by using the same catalyst and obtained a zero-birefringence terpolymer with the S content of 12%, but the introduction of E unit (58 mol %) caused a significant drop of the Tg to 86 °C [36].
Therefore, we are interested in the copolymerization of N with S to obtain high molecular weight copolymers with controlled S content. We have previously reported that anilinonaphthoquinone-ligated nickel complexes activated with B(C6F5)3 as a cocatalyst exhibit high activity for N polymerization to give high molecular weight polymer soluble in cyclohexane [37]. In the present paper, we report the N/S copolymerization using nickel complexes [Ni(C10H5O2NAr)(Ph)(PPh3): 1a, Ar = C6H3-2,6-iPr; 1b, Ar = C6H2-2,4,6-Me; 1c, Ar = C6H5], where 1c was newly synthesized in this work, in the presence of modified MAO (MMAO) or B(C6F5)3 (Figure 1).

2. Materials and Methods

2.1. Materials

All manipulations were carried out under a nitrogen atmosphere using standard Schlenk techniques. All solvents were refluxed and distilled over sodium/benzophenone or calcium hydride. Norbornene was purified by stirring it over calcium hydride at 60 °C for one day, and then distilled. The stock solution of N (5.5 M) was prepared in toluene. Styrene (Wako Chemical Co. Ltd., Odawara, Japan) was dried over CaH2, and then freshly distilled under vacuum prior to use. Modified methylaluminoxane (MMAO) solution (6.6 wt % in toluene) and toluene solution of B(C6F5)3 were donated from Tosoh Finechem. Co. (Tokyo, Japan) and used as received. The nickel complexes 1a,1b were synthesized according to the literature and the references therein [38,39]. The complex 1c was synthesized using a similar procedure to that for 1a and 1b (Supporting Information).

2.2. Analytical Procedure

Molecular weights and molecular weight distributions of polymers were determined by gel permeation chromatography (GPC) with a Viscotec HT-350 GPC (Malvern, Great Malvern, UK) with one guard column and two 30 cm columns. This system was equipped with a triple-detection array consisting of a differential refractive index (DRI) detector, a two-angle (7, 90) light scattering (LS) detector, and a four-bridge capillary viscosity detector. Polymer characterization was carried out at 150 °C using o-dichlorobenzene as an eluent, and calibrated with polystyrene standards. The 1H and 13C NMR spectra of polymers were measured at room temperature on a Bruker 500M Hz instrument (Bruker, Rheinstetten, Germany) operated by the pulse Fourier-transform mode. Sample solution of 13C NMR was prepared in CDCl3 up to 10 wt %, and the pulse angle was 45°, and about 8000–10,000 scans were accumulated in pulse repetition of 5.0 s. The central peak of CDCl3 (7.13 ppm for 1H and 77.13 ppm for 13C NMR) was used as an internal reference. Differential scanning calorimetry (DSC) was performed on a SII EXSTER 600 system (Seiko Instruments Inc., Chiba, Japan) under nitrogen atmosphere. Thermal history difference in the polymers was eliminated by first heating the specimen to 380 °C, cooling from 10 to 20 °C/min, and then recording the second DSC scan at a heating rate of 10 °C/min.

2.3. Copolymerization of N and S

In a typical procedure, prescribed amounts of N and S in toluene solution were introduced into a 100 mL round-bottomed glass flask. Then, the cocatalyst (0.24 mL 500 µmol of MMAO toluene solution or 1 mL 20 µmol of B(C6F5)3 toluene solution) and 1 mL of the nickel complex (5 µmol) solution in toluene were syringed into the well-stirred monomer solution in this order, and the total solution volume was made up to 25 mL by adding toluene. The copolymerization was conducted under continuous stirring for a required time under a certain temperature as controlled using an external oil or ice bath. The copolymerization was terminated by adding 300 mL of acidic methanol (methanol/concentrated hydrochloric acid, 95: 5 in volume). The resulting precipitated polymer was collected by filtration, adequately washed with methanol, and dried in vacuum at 60 °C for 6 h.

3. Results and Discussion

3.1. Homopolymerization of N and S

Homopolymerizations of N and S were performed using 1-MMAO at 70 °C in toluene. The results are shown in Table 1. In the N polymerization, complex 1a displayed the highest activity, and gave the polymer with the highest molecular weight among the complexes used. The opposite trends were observed in S polymerization, but the differences were not significant.

3.2. Copolymerization of N and S

Copolymerizations of N with S were then conducted under the same conditions by changing S in feed from 10 to 40 mmol, with 40 mmol of N (Scheme 1).
The results are summarized in Table 1. The nickel complexes showed moderate activity for N/S copolymerization. The N/S feed ratio did not significantly affect the catalytic activity, and all the complexes showed lower activity in the copolymerizations than in homopolymerizations. The low activity in the copolymerization could be ascribed to slow cross-propagation because of the steric hindrance between these comonomers. Complex 1a, which showed the highest activity in N polymerization, also showed the highest activity in N/S copolymerization among the complexes used (Table 1, Run 3).
The N/S copolymers were not only soluble in chloroform, but also in cyclohexane, similar to the PNB obtained by the same catalytic system. The incorporation of S in the produced copolymers was investigated by 1H NMR in CDCl3. A typical 1H NMR spectrum of the copolymer (Run 15) is illustrated in Figure 2i. No resonances are observed from 5.0 to 6.0 ppm, which is assigned to the vinylene protons of the polymer obtained via ring-opening metathesis polymerization (ROMP) [40].
The signals assignable to the aliphatic protons of the N and S units (HN1–4 and HS5) are observed in the range of 0.8–2.4 ppm. The signals attributed to the aromatic protons of the S units (HS1–3) are observed in the range of 6.5–7.1 ppm. Particularly, the signal of the methine proton of the S unit (HS4) adjacent to the N unit can be observed at 2.85 ppm. The 1H NMR spectra of the polymers obtained under the highest styrene concentration (Table 1, Run 3, 9 and 15) are shown in Supplementary Figure S5.
A typical 13C NMR spectrum of the copolymer (Run 15) is shown in Figure 2ii. According to the reported assignment of the N/S copolymer, [34] the signals of each chemical shift region were assigned as follows: 145.7 ppm for C1, 127.3 ppm for C2, 127.9 ppm for C3, 125.6 for C4, 41.5–44.2, and 40.5 ppm for C5 and C6 of the S segment, 47.1–52.5 ppm for C3, 38–39.7 ppm for C2, 34.5–37 ppm for C4, and 29.4–31.9 ppm for C1 of the N unit. A clear observation of the phenyl-carbons of the S units in the regions of 125–145 ppm also indicates the presence of the S units in the N/S copolymer. These results are similar to those obtained in the previously reported nickel–MAO catalytic system and confirm the random distribution of S unit in the obtained N/S copolymer [34].
The incorporation of S increased with increasing S concentration in the monomer feed ratio. The highest S content in the N/S copolymer was achieved to be 36% at 1:1 feed ratio by complex 1c probably because of less interaction between the ligand substituent and the aromatic ring of S.
The molecular weight of N/S copolymer was measured by GPC. The increase of S concentration in feed caused the decrease in the molecular weights of the produced polymers accompanied by the increase in the number of polymer chains, which is ascribed to β-hydrogen elimination of the increased styryl propagation end [41]. Unimodal distribution (Mw/Mn ≈ 2) indicates that the copolymerization should take place at a single active site (Supplementary Figure S6).

3.3. Effect of Polymerization Temperature on N/S Copolymerization:

The influence of reaction temperature on N/S copolymerization was studied using 1-MMAO at the fixed feeding ratio (N/S = 4:1 in molar ratio), because the low S feed ratio gave high molecular weight N/S copolymer. The results are summarized in Table 2.
The copolymerization activity decreased with lowering the temperature from 70 to 0 °C. The highest activity around 70 kg polymer/(mol Ni h) for the copolymerization was achieved at 70 °C in each system. On the other hand, the S content and the Mn value monotonously increased with lowering of the polymerization temperature (Supplementary Figure S7), and the N/S copolymer with 32 mol % of S and 61,000 of Mn was obtained at 0 °C by 1c-MMAO (Table 2, Run 25, Figure 3i). This Mn value would be the highest among the N/S copolymers reported so far [25,34,35]. The molecular weight distribution became narrow with decreasing the polymerization temperature. A decreased Mn value of the copolymers obtained with an increase in the reaction temperature is ascribed to the chain transfer at high temperature [32].
The Tg values of N/S copolymers were analyzed by DSC. The Tg value declined with an increase of S content as shown in Figure 3ii. The highest value of 329 °C (Supplementary Figure S8), and the lowest value of 172 °C, were detected for the copolymers with 4 and 32 mol % of S, respectively (Table 2, Run 6 and 25). A previous study has shown that the Tg value of the PNBs obtained with this catalyst was over 400 °C [37]. The Tg value of polystyrene is 100 °C. The single Tg value in the DSC curves reveal that N and S were uniformly distributed in the N/S copolymers obtained by the present catalysts.

3.4. N/S Copolymerization by 1-B(C6F5)3:

We found the considerable effects of temperature on N/S copolymerization using the 1-MMAO system. We observed significant effects of B(C6F5)3 in E polymerization [38] and N polymerization [37] with 1a, which were ascribed to the formation of zwitterionic nickel species [39].
Thus, the N/S copolymerization (N/S = 4:1 in molar ratio) by the 1-B(C6F5)3 system, was conducted at different temperatures (30, 50, and 70 °C) to investigate the cocatalyst effect.
The activity of the B(C6F5)3 system was lower than that of the MMAO system. The incorporation of S increased with lowering the temperature, as was observed in the 1-MMAO system. The S incorporation was almost four times higher than those of the copolymers produced by the 1-MMAO system. The highest S incorporation was observed at 30 °C (Supplementary Figure S9), 51~59% with the Mn values (Supplementary Figure S10) of 43,000~78,000 (Table 3, Run 28, 31, and 34).
In order to evaluate the effects of the cocatalysts on N/S copolymerization, the monomer reactivity ratios of 1b were determined at 70 °C (Supplementary Table S1). The Fineman–Ross plots of 1b-MMAO and 1b-B(C6F5)3 for N/S copolymerization are shown in Figure 4i and 4ii, respectively. The monomer reactivity ratios were determined to be rN = 6.34 and rS = 0.39 for 1b-MMAO, and rN = 0.93 and rS = 0.13 for 1b-B(C6F5)3, indicating the better copolymerization ability of the B(C6F5)3 cocatalyst. The reactivity ratios of 1c-MMAO were also determined to evaluate the effects of the complexes (Supplementary Figure S11). The values rN = 2.16 and rS = 0.26 indicate the better copolymerization ability of 1c than 1b.
The Tg values determined by DSC are shown in Table 3 and are plotted against S content in Figure 3ii. The plot is in good accordance with that of the MMAO system, but extends to the higher S content as indicated by the monomer reactivity ratios. The lowest Tg value of 128 °C (Supplementary Figure S12) was obtained by the copolymer with S content of 59 mol % and Mn of 78,000 (Table 3, Run 31). The 1-B(C6F5)3 system gave the copolymers with high molecular weights and high S contents, compared with the 1-MMAO system, although the activity was low.
The lower activity would be due to the deactivation by impurities in the absence of scavenging reagents. Therefore, we conducted N/S copolymerization with 1a-B(C6F5)3 in the presence of the reaction mixture of tBu3Al and 2,6-tBu2-p-cresol. The addition of the scavenger increased the activity, keeping the same S content and the Mn value reached 103,000 (Table 3, Run 35). The results indicate the potentiality of 1-B(C6F5)3 for N/S copolymerization.

3.5. Optical Property of the N/S Copolymer

The light transmittance of the N/S copolymer thin film with the thickness about 100 µm is displayed in Supplementary Figure S13 (Table 3, Run 35). The copolymer showed the transmittance above 85% in the visible light region (300–800 nm).

4. Conclusions

Copolymerizations of N and S were achieved by anilinonaphthoquinone-ligated nickel-complexes using MMAO or B(C6F5)3 as cocatalyst. The 1-MMAO system showed higher activity than the 1-B(C6F5)3 system, whereas the latter system produced the copolymers with higher molecular weight and higher styrene incorporation. The molecular weights of N/S copolymers obtained by 1-B(C6F5)3 were the highest among those of the copolymers reported previously using nickel-, copper-, and titanium-based catalytic systems.

Supplementary Materials

The following are available online at https://www.mdpi.com/2073-4360/11/7/1100/s1, Synthesis of ligand 1c; Figure S1 1H NMR spectrum of ligand 1c; Figure S2 13C NMR spectrum of ligand 1c; Synthesis of complex 1c; Figure S3 1H NMR spectrum of complex 1c; Figure S4 31P NMR spectrum of complex 1c; Figure S5 1H NMR spectra of N/S copolymers obtained by Run 15, Run 9, and Run 3; Figure S6 GPC traces of N/S copolymers obtained by Run 7, Run 8, and Run 9; Figure S7 1H NMR spectra of N/S copolymers obtained by Run 25, Run 22, and Run 19; Figure S8 DSC curves of N/S copolymers obtained by Run 6 and Run 17; Figure S9 1H NMR spectra of N/S copolymers obtained by Run 31 and Run 34; Figure S10 GPC traces of N/S copolymers obtained by Run 30 and Run 33; Figure S11 Fineman–Ross plot for N/S copolymerization by 1c-MMAO; Table S1 Effects of monomer ratio of N/S copolymerization by 1b-B(C6F5)3; Figure S12 DSC curve of N/S copolymer obtained by Run 31; Figure S13 the light transmittance of N/S copolymer thin film obtained by run 35.

Author Contributions

Conceptualization, T.S.; methodology, S.I.C. and R.T.; polymer synthesis, S.I.C; analysis, S.I.C., R.T. and Y.N.; writing—original draft preparation, S.I.C.; editing, T.S.; review, R.T. and Y.N.; funding acquisition, T.S.

Funding

Partial financial support from a Grant-in-Aid for Scientific Research from the Japan Society for the Promotion of Science (No. 18H02036).

Acknowledgments

This work was supported in part by a Grant-in-Aid for Scientific Research from the Japan Society for the Promotion of Science (No. 18H02036). Cocatalysts were kindly donated by Tosoh Finechem Co.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Chen, M.; Zou, W.P.; Cai, Z.G.; Chen, C.L. Norbornene homopolymerization and copolymerization with ethylene by phosphine- sulfonate nickel catalysts. Polym. Chem. 2015, 6, 2669–2676. [Google Scholar] [CrossRef]
  2. Pei, L.X.; Tang, Y.; Gao, H.Y. Homo- and Copolymerization of Ethylene and Norbornene with Anilido–Imine Chromium Catalysts. Polymers 2016, 8, 69. [Google Scholar] [CrossRef] [PubMed]
  3. Meng, J.F.; Li, X.; Ni, X.F.; Shen, Z.Q. High transparent alternate copolymer of norbornene with isoprene catalyzed by bis(phenoxy–imine) titanium complex. RSC Adv. 2016, 6, 19351–19356. [Google Scholar] [CrossRef]
  4. Gilliom, L.R.; Grubbs, R.H. Titanacyclobutanes derived from strained, cyclic olefins: The living polymerization of norbornene. J. Am. Chem. Soc. 1986, 108, 733–742. [Google Scholar] [CrossRef]
  5. Nguyen, S.T.; Johnson, L.K.; Grubbs, R.H.; Ziller, J.W. Ring-opening metathesis polymerization (ROMP) of norbornene by a Group VIII carbene complex in protic media. J. Am. Chem. Soc. 1992, 114, 3974–3975. [Google Scholar] [CrossRef] [Green Version]
  6. Kennedy, J.P.; Makowski, H.S. Carbonium Ion Polymerization of Norbornene and Its Derivatives. J. Macromol. Sci. Chem. 1967, A1, 345–370. [Google Scholar] [CrossRef]
  7. Gaylord, N.G.; Mandal, B.M.; Martan, M. Peroxide-induced polymerization of norbornene. J. Polym. Sci. Polym. Lett. Ed. 1976, 14, 555–559. [Google Scholar] [CrossRef]
  8. Gaylord, N.G.; Deshpande, A.B. Structure of “vinyl-type” polynorbornenes prepared with ziegler-natta catalysts. J. Polym. Sci. Polym. Lett. Ed. 1976, 14, 613–617. [Google Scholar] [CrossRef]
  9. Gaylord, N.G.; Deshpande, A.B.; Mandal, B.M.; Martan, M. Poly-2,3- and 2,7-Bicyclo[2.2.1]hept-2-enes: Preparation and Structures of Polynorbornenes. J. Macromol. Sci. Chem. 1977, A11, 1053–1070. [Google Scholar] [CrossRef]
  10. Rush, S.; Reinmuth, A.; Risse, W. Palladium(II)-Catalyzed Olefin Addition Polymerizations of 3,3-Dialkyl-Substituted Cyclopropenes. Macromolecules 1997, 30, 7375–7385. [Google Scholar] [CrossRef]
  11. Goodall, L.; McIntosh III, L.H.; Rhodes, L.F. New catalysts for the polymerization of cyclic olefins. Macromol. Symp. 1995, 89, 421–432. [Google Scholar] [CrossRef]
  12. Seehof, N.; Mehler, C.; Breunig, S.; Risse, W. Pd2+ catalyzed addition polymerizations of norbornene and norbornene derivatives. J. Mol. Catal. 1992, 76, 219–228. [Google Scholar] [CrossRef]
  13. Grove, N.R.; Kohl, P.A.; Allen, S.A.B.; Jayaraman, S.; Shick, R. Functionalized Polynorbornene Dielectric Polymers: Adhesion and Mechanical Properties. J. Polym. Sci. Part. B Polym. Phys. 1999, 37, 3003–3010. [Google Scholar] [CrossRef]
  14. Janiak, C.P.; Lassahn, G. The Vinyl Homopolymerization of Norbornene. Macromol. Rapid Commun. 2001, 22, 479–492. [Google Scholar] [CrossRef]
  15. Boggioni, L.; Tritto, I. State of the art of cyclic olefin polymers. MRS Bull. 2013, 38, 245–251. [Google Scholar] [CrossRef]
  16. He, X.; Deng, Y.; Jiang, X.; Wang, Z.; Yang, Y.; Han, Z.; Chen, D. Copolymerization of norbornene and butyl methacrylate at elevated temperatures by a single centre nickel catalyst bearing bulky bis(α-diimine) ligand with strong electron-withdrawing groups. Polym. Chem. 2017, 8, 2390–2396. [Google Scholar] [CrossRef]
  17. Shiono, T.; Sugimoto, M.; Hasan, T.; Cai, Z.; Ikeda, T. Random Copolymerization of Norbornene with Higher 1-Alkene with ansa-Fluorenylamidodimethyltitanium Catalyst. Macromolecules 2008, 41, 8292–8294. [Google Scholar] [CrossRef]
  18. Cai, Z.; Harada, R.; Nakayama, Y.; Shiono, T. Highly Active Living Random Copolymerization of Norbornene and 1-Alkene with ansa-Fluorenylamidodimethyltitanium Derivative: Substituent Effects on Fluorenyl Ligand. Macromolecules 2010, 43, 4527–4531. [Google Scholar] [CrossRef]
  19. Xing, Y.; Chen, Y.; He, X.; Nie, H. Nickel(II) complexes bearing the bis(β-ketoamino) ligand for the copolymerization of norbornene with a higher 1-alkene. J. Appl. Polym. Sci. 2012, 124, 1323–1332. [Google Scholar] [CrossRef]
  20. Liu, Y.M.; Ouyang, M.; He, X.H.; Chen, Y.W.; Wang, K.T. Novel Ni and Pd(benzocyclohexan-ketonaphthylimino)2 complexes for copolymerization of norbornene with octane. J. Appl. Polym. Sci. 2013, 128, 216–223. [Google Scholar] [CrossRef]
  21. Zhao, W.; Nomura, K. Copolymerizations of Norbornene and Tetracyclododecene with α-Olefins by Half-Titanocene Catalysts: Efficient Synthesis of Highly Transparent, Thermal Resistance Polymers. Macromolecules 2016, 49, 59–70. [Google Scholar] [CrossRef]
  22. Zhao, W.; Nomura, K. Design of Efficient Molecular Catalysts for Synthesis of Cyclic Olefin Copolymers (COC) by Copolymerization of Ethylene and α-Olefins with Norbornene or Tetracyclododecene. Catalysts 2016, 6, 175. [Google Scholar] [CrossRef]
  23. He, X.; Deng, Y.; Han, Z.; Yang, Y.; Chen, D. Highly symmetric single nickel catalysts bearing bulky bis(α-diimine) ligand: Synthesis, characterization, and electron-effects on copolymerization of norbornene with 1-alkene at elevated temperarure. J. Polym. Sci: Part. A Polym. Chem. 2016, 54, 3495–3505. [Google Scholar] [CrossRef]
  24. Hasan, T.; Ikeda, T.; Shiono, T. Ethene−Norbornene Copolymer with High Norbornene Content Produced by ansa-Fluorenylamidodimethyltitanium Complex Using a Suitable Activator. Macromolecules 2004, 37, 8503–8509. [Google Scholar] [CrossRef]
  25. Ban, H.; Hagihara, H.; Tsunogae, Y.; Cai, Z.; Shiono, T. Highly thermostable and low birefringent norbornene-styrene copolymers with advanced optical properties: A potential plastic substrate for flexible displays. J. Polym. Sci. Part. A Polym. Chem. 2011, 49, 65–71. [Google Scholar] [CrossRef]
  26. Peruch, F.; Cramail, H.; Deffieux, A. Homopolymerization and copolymerization of styrene and norbornene with Ni-based/MAO catalysts. Macromol. Chem. Phys. 1998, 199, 2221–2227. [Google Scholar] [CrossRef]
  27. Zhao, C.T.; Ribeiro, M.D.R.; Portela, M.F.; Pereira Nunes, S.T. Homo- and copolymerisation of norbornene and styrene with nickel bis(acetyl acetonate)/methylaluminoxane system. Eur. Polym. J. 2001, 37, 45–54. [Google Scholar] [CrossRef]
  28. Mi, X.; Ma, Z.; Wang, L.; Ke, Y.; Hu, Y. Homo- and Copolymerization of Norbornene and Styrene with Pd- and Ni-Based Novel Bridged Dinuclear Diimine Complexes and MAO. Macromol. Chem. Phys. 2003, 204, 868–876. [Google Scholar] [CrossRef]
  29. Suzuki, H.; Matsumura, S.; Satoh, Y.; Sogoh, K.; Yasuda, H. Random copolymerizations of norbornene with other monomers catalyzed by novel Ni compounds involving N- or O-donated ligands. React. Funct. Polym. 2004, 58, 77–91. [Google Scholar] [CrossRef]
  30. Gao, H.; Chen, Y.; Zhu, F.; Wu, Q. Copolymerization of norbornene and styrene catalyzed by a novel anilido–imino nickel complex/methylaluminoxane system. J. Polym. Sci. Part. A Polym. Chem. 2006, 44, 5237–5246. [Google Scholar] [CrossRef]
  31. Bao, F.; Ma, R.; Jiao, Y. Homo- and copolymerization of norbornene with styrene catalyzed by a series of copper(II) complexes in the presence of methylaluminoxane. Appl. Organomet. Chem. 2006, 20, 368–374. [Google Scholar] [CrossRef]
  32. Bao, F.; Lu, X.; Chen, Y. Copolymerization of Norbornene and Styrene Catalyzed by a Series of Bis(β-ketoamine) Nickel(II) Complexes in the Presence of Methylaluminoxane. Polym. Bull. 2007, 58, 495–502. [Google Scholar] [CrossRef]
  33. Ogata, K.; Nishimura, N.; Yunokuchi, T.; Toyota, A. Copolymerization of tetracyclododecene or norbornene with styrene in the presence of Ni(II) complex/MAO catalytic system: First example for transition metal catalyzed copolymerization of tetracyclododecene with styrene. J. Appl. Polym. Sci. 2008, 108, 1562–1565. [Google Scholar] [CrossRef]
  34. Li, Y.; Wu, Q.; Shan, M.; Gao, M. Copolymerization of styrene and norbornene with β-diketiminato nickel/methylaluminoxane catalytic system. Appl. Organomet. Chem. 2012, 26, 225–229. [Google Scholar] [CrossRef]
  35. Feng, Q.; Chen, D.; Feng, D.; Jiao, L.; Peng, Z.; Pei, L. Synthesis of poly(norbornene-co-styrene) copolymers containing high styrene incorporation using bis(β-ketoamino) copper catalysts. J. Polym. Res. 2014, 21, 497. [Google Scholar] [CrossRef]
  36. Ban, H.T.; Nishii, K.; Tsunogae, Y.; Shiono, T. Synthesis and characterization of norbornene–ethylene–styrene terpolymers with a substituted ansa-fluorenylamidodimethyltitanium-based catalyst. J. Polym. Sci. Part A Polym. Chem. 2007, 45, 2765–2773. [Google Scholar] [CrossRef]
  37. Okada, M.; Nakayama, Y.; Shiono, T. Highly soluble polynorbornene prepared by an anilinonaphthoquinone-ligated nickel complex via coordination-insertion polymerization. J. Organomet. Chem. 2015, 384–387. [Google Scholar] [CrossRef]
  38. Okada, M.; Nakayama, Y.; Ikeda, T.; Shiono, T. Synthesis of Uniquely Branched Polyethylene by Anilinonaphthoquinone Ligated Nickel Complex Activated with Tris(pentafluorophenyl)borane. Macromol. Rapid Commun. 2006, 27, 1418–1423. [Google Scholar] [CrossRef]
  39. Okada, M.; Nakayama, Y.; Shiono, T. Synthesis of anilinonaphthoquinone-based nickel complexes and their application for olefin polymerization. J. Organomet. Chem. 2007, 692, 5183–5189. [Google Scholar] [CrossRef] [Green Version]
  40. Ivin, K.J.; Mol, J.C. Olefin Metathesis and Metathesis Polymerization; Academic Press: San Diego, CA, USA, 1997; p. 407. [Google Scholar]
  41. Benedikt, G.M.; Elce, E.; Goodall, B.L.; Kalamarides, H.A.; McIntosh, L.H.; Rhodes, L.F.; Selvy, K.T.; Andes, C.; Oyler, K.; Sen, A. Copolymerization of Ethene with Norbornene Derivatives Using Neutral Nickel Catalysts. Macromolecules 2002, 35, 8978–8988. [Google Scholar] [CrossRef]
Polymers 11 01100 g001 550
Figure 1. Anilinonaphthoquinone-ligated nickel complexes used in this study.
Figure 1. Anilinonaphthoquinone-ligated nickel complexes used in this study.
Polymers 11 01100 g001
Polymers 11 01100 sch001 550
Scheme 1. N/S copolymerization with Ni catalyst.
Scheme 1. N/S copolymerization with Ni catalyst.
Polymers 11 01100 sch001
Polymers 11 01100 g002 550
Figure 2. 1H NMR (i) and 13C NMR (ii) spectra of N/S copolymer obtained by Run 15 (CDCl3, rt, 500 MHz).
Figure 2. 1H NMR (i) and 13C NMR (ii) spectra of N/S copolymer obtained by Run 15 (CDCl3, rt, 500 MHz).
Polymers 11 01100 g002
Polymers 11 01100 g003 550
Figure 3. (i) GPC traces of N/S copolymers: a, Run 24; b, Run 25 (ii) S content versus Tg plot obtained by Ni complexes: ◆, MMAO; ▲, B(C6F5)3.
Figure 3. (i) GPC traces of N/S copolymers: a, Run 24; b, Run 25 (ii) S content versus Tg plot obtained by Ni complexes: ◆, MMAO; ▲, B(C6F5)3.
Polymers 11 01100 g003
Polymers 11 01100 g004 550
Figure 4. Fineman–Ross plots for copolymerization of N/S by 1b with (i) MMAO and (ii) B(C6F5)3.
Figure 4. Fineman–Ross plots for copolymerization of N/S by 1b with (i) MMAO and (ii) B(C6F5)3.
Polymers 11 01100 g004
Table
Table 1. Effects of monomer ratio of norbornene (N)/styrene (S) copolymerization by 1-MMAO.
Table 1. Effects of monomer ratio of norbornene (N)/styrene (S) copolymerization by 1-MMAO.
RunN/S a
(mmol/mmol)		ComplexYield
(g)		Act. bfSc
(mol%)		Mn
(103)		Mw/MndNe
(µmol)
140/001a1.1022004701.92.3
240/101a0.36724192.418.9
340/401a0.651301662.5108.3
400/401a0.52104100111.547.2
540/001b0.5410702662.22.0
640/101b0.37744192.719.5
740/201b0.31628121.725.8
840/301b0.30601293.033.3
940/401b0.44881982.955.0
1000/401b0.65130100121.654.2
1140/001c0.5811503091.61.9
1240/101c0.367210132.027.7
1340/201c0.326416101.532.0
1440/301c0.31621981.938.6
1540/401c0.40803673.057.1
1600/401c0.65130100141.746.4
Copolymerization conditions: Ni = 5 μmol, temperature = 70 °C, time = 1 h, Al/Ni = 100 (molar ratio), toluene (total volume 25 mL). a Norbornene and styrene in feed. b Activity = kg(polymer)mol(Ni)−1 h−1. c fS is the content of S in the N/S copolymer determining by 1H NMR spectrum. d Determined by GPC. e Number of polymer chains determined from yield and Mn.
Table
Table 2. Effects of temperature of N/S copolymerization by 1-MMAO.
Table 2. Effects of temperature of N/S copolymerization by 1-MMAO.
RunComplexTemperature
(°C)		Yield (g)Activity afSb
(mol%)		Mnc
(103)		Mw/MncTgd
21a700.36724192.4321
171a500.27547262.2289
181a300.14289272.0267
191a00.132620552.1219
61b700.37744192.7329
201b500.27549242.2263
211b300.204012272.3252
221b00.112230571.5175
121c700.367210132.0251
231c500.295816182.2227
241c300.244821541.5212
251c00.142732611.5172
Copolymerization conditions: Ni = 5 μmol, Al/Ni = 100 (molar ratio), N/S = 4:1 (molar ratio), toluene (total volume 25 mL) time 1 h. a Activity = kg(polymer)mol(Ni)−1 h−1. b fS is the content of S in the N/S copolymer determining by 1H NMR spectrum. c Determined by GPC. d Determined by DSC.
Table
Table 3. Effects of temperature of N/S copolymers by 1-B(C6F5)3.
Table 3. Effects of temperature of N/S copolymers by 1-B(C6F5)3.
RunComplexTemperature
(°C)		Yield
(g)		Activity afSb
(mol%)		Mnc
(103)		Mw/MncTgd
261a700.1262617361.9220
271a500.0721522401.7215
281a300.0531151431.9153
291b700.0881818382.0251
301b500.0671430551.6183
311b300.033759781.9128
321c700.0821727382.5189
331c500.034730392.1180
341c300.030653462.0139
35[e]1a700.33066171031.4232
Copolymerization conditions: Ni = 5 μmol, B/Ni = 4 (molar ratio), N/S = 4:1 (molar ratio), toluene (total volume 25 mL) time = 1 h. a Activity = kg(polymer)mol(Ni) −1 h−1. b fS is the content of S in the N/S copolymer determining by 1H NMR spectrum. c Determined by GPC. d Determined by DSC. e B(C6F5)3/tBuAl/BHT = 1:10:20.

Share and Cite

MDPI and ACS Style

Chowdhury, S.I.; Tanaka, R.; Nakayama, Y.; Shiono, T. Copolymerization of Norbornene and Styrene with Anilinonaphthoquinone-Ligated Nickel Complexes. Polymers 2019, 11, 1100. https://doi.org/10.3390/polym11071100

AMA Style

Chowdhury SI, Tanaka R, Nakayama Y, Shiono T. Copolymerization of Norbornene and Styrene with Anilinonaphthoquinone-Ligated Nickel Complexes. Polymers. 2019; 11(7):1100. https://doi.org/10.3390/polym11071100

Chicago/Turabian Style

Chowdhury, Samiul Islam, Ryo Tanaka, Yuushou Nakayama, and Takeshi Shiono. 2019. "Copolymerization of Norbornene and Styrene with Anilinonaphthoquinone-Ligated Nickel Complexes" Polymers 11, no. 7: 1100. https://doi.org/10.3390/polym11071100

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.