Correction: Park, K.; Withey, P. General View of Rhenium-Rich Particles along Defect Grain Boundaries Formed in Nickel-Based Single-Crystal Superalloy Turbine Blades: Formation, Dissolution and Comparison with Other Phases. Crystals 2021, 11, 1201

There was an error in the original publication [1]. In

Table 1. Compositions (at pct) of raw material and several phases and particles measured by STEM-EDX [16,17].

Element	Raw	γ	γ′	TCP	Re-Rich	Re-W
Al	13.6	6.3	15.6	2.4	2.5	1.0
Ti	0.1	0.0	0.1	0.1	0.1	0.0
Cr	1.8	4.1	1.0	4.0	1.7	15.3
Co	3.2	5.9	2.7	6.3	3.8	14.2
Nb	0.0	0.0	0.0	0.0	0.0	0.0
Mo	0.3	0.3	0.0	0.6	3.0	2.7
Ta	3.0	3.6	4.6	5.2	0.7	2.6
W	1.9	3.4	2.4	16.2	3.8	21.3
Re	2.4	5.9	0.0	41.0	61.6	21.9
Ni	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.

’s caption, the “wt %” must be corrected to “at pct”. The authors apologize for any inconvenience caused and state that the scientific conclusions are unaffected.