Novel Cobalt Complex as an Efficient Catalyst for Converting CO₂ into Cyclic Carbonates under Mild Conditions

Abstract

Based on the ligand H₂dpPzda (1), a novel cobalt complex [Co(H₂dpPzda)(NCS)₂]·CH₃OH(2) has been synthesized and characterized. The Complex 2 exhibited excellent catalytic performance for converting CO₂ into cyclic carbonates under mild conditions. For propylene oxide (PO) and CO₂ synthesis of propylene carbonate (PC), the catalytic system showed a remarkable TOF as high as 29,200 h⁻¹. The catalytic system also showed broad substrate scope of epoxide. Additionally, the catalyst could be recycled to maintain the integrity of the structure and remained equal to the level of its catalytic activity even after seven catalytic rounds. Additionally, a possible catalytic mechanism was proposed due to the high catalytic activity which might be owing to the synergism of Lewis acidic metal centers and N group.

1. Introduction

As one of the main gases that produce the greenhouse effect, CO₂ destroys the ecological balance of nature and threatens the survival of various organisms. At the same time, its cheapness, abundance and safety make it one of the main research directions of green chemistry [1,2,3]. Indeed, the synthesis of cyclic carbonates with epoxides is one of the most effective routes to utilize carbon dioxide resources. Cyclic carbonate has quite a lot of application as an intermediate for many chemical syntheses [4,5]. Therefore, there have been many studies on the catalytic synthesis of cyclic carbonates over the past few decades.

The cycloaddition reaction of epoxide and CO₂ is generally carried out over various catalysts, including metal complexes [6,7,8], metal oxides [9], molecular sieves [10], ionic liquids [11,12] and organic catalysts [13,14,15]. Among these catalysts, metal complexes show superiority due to their easy-to-synthetize, high stability, and abundant spatial structure. However, it has been reported in the past that most of the catalysts for converting CO₂ into cyclic carbonates are insufficient, such as harsh reaction conditions, excessive catalyst loading, and the need for solvent to be added. On the other hand, most homogeneous catalysts are non-recycled. Therefore, it is urgently needed to synthesize catalysts with more stable, higher recyclability that can work under milder reaction conditions.

Owing to multiple metal coordination sites and the intermolecular interaction, supramolecular metal catalysts with high catalytic activity and selectivity have emerged as highly promising materials for wide applications, including the cycloaddition reaction of CO₂ [16,17,18]. It has been found that the nitrogen-containing heterocyclic group possessed by the oligopyrazinediamine ligand has various coordination modes, which can be combined with transition metals under neutral conditions (for example, nickel, manganese, iron, cobalt, etc.) to form a series of metal-organic coordination compounds. Interestingly, a supramolecular catalyst with an oligopyrazinediamine ligand can be synthesized by optimizing the synthesis process [19,20,21,22].

Herein, H₂dpPzda(1) [22] was used as a ligand, and we have designed and synthesized a novel cobalt complex [Co(H₂dpPzda)(NCS)₂]·CH₃OH(2) (Scheme 1). Complex 2, which was used as a catalyst for the cycloaddition of CO₂ and epoxides under mild conditions, exhibited excellent catalytic performance with high selectivity and yield and turnover frequency (TOF). Additionally, the insolubility of Complex 2 in the reactants and products allows the catalyst to be easily recycled by simple centrifugation with almost no loss. Therefore, we propose a possible mechanism that the synergism of Lewis acidic metal centers and N group make it highly catalytically active.

2. Results and Discussion

2.1. Structure and Characterization

Complex 2 was synthesized when Co(NCS)₂ reacted with the ligand H₂dpPzda in methanol. The experimental conditions, data collection, structural analysis, correction methods and crystal data of the complex related to X-ray diffraction analysis were shown in Table S1. The main bond lengths were listed in Table S2.

Complex 2 was a one-dimensional straight chain polymeric structure of neutral molecular type, and its crystal belonged to the Aba2 space group of orthorhombic system. The crystal structure diagram of the Complex 2 was shown in Figure 1a. In the Complex 2, each ligand had four aromatic nitrogen atoms as coordination atoms, the ligand was tetradentate coordination, and the pyrazine ring acted as a bridging ligand to link the small molecular units of the complex into a one-dimensional chain polymerization. Co(II) coordinated with six nitrogen atoms to form an elongated octahedral geometry. The equatorial plane was constructed through four nitrogen atoms, three of which came from one ligand and the fourth nitrogen atom from the pyrazine ring of another ligand. The two nitrogen atoms of the pyrazinyl group and the Co(II) ion were coordinated at the equatorial position. In the axial position, the other two nitrogen atoms were derived from thiocyanate. Adjacent ligands were on the same plane (Co–Co–Co = 180.00°) and the spacing between Co–Co reached 7.14 Å. The bond length of the Co–N (H₂dpPzda) bond varied from 2.121 to 2.202, and the bond length of the Co-N (NCS-) bond was 2.059 Å which indicated that the anionic NCS had strong binding ability to Co(II). The N-C-S participating in the coordination of the N-C-S had an angle of 179.30° and was almost straight. For Co(II) ions, the coordination environment could be considered as an elongated square bipyramid (Figure 1b). All of the bond lengths of Co–N fell into the normal ranges. In Complex 2, the ligand coordinated in a bidentate bridging mode with two ligands in a cis conformation. The hydrogen bonded N2-H2···O1 and O1-H1B···S1 between the amine group, and the thiocyanate and the methanol solvent (Table S3) transformed the one-dimensional chain structure into a two-dimensional plane as shown in Figure 1c.

2.2. Catalytic Activity for CO₂ Fixation

In this section, we designed a series of experiments to explore the potential catalytic performance of compounds 1 and 2. The pyridyl and cobalt metals in 2 could give the catalyst a high density of Lewis-basic and Lewis-acid active sites, giving it multiple functionalities, indicating that they have broad prospects in catalytic applications. Thus, we designed a series of experiments to examine their catalytic activities. As shown in

Table 1. Cycloaddition of CO₂ and propylene oxide (PO) using 1 and 2 ^a.

Entry	Cat	Co-cat	T(°C)	P(bar)	T(h)	Conversions b (%)	TOF c (h−1)
1	-	-	90	10	1	-	-
2	1	-	90	10	1	9	360
3	2	-	90	10	1	16	640
4	-	TBAB	90	10	1	25	-
5	2	TBAB	90	10	1	89	3560
6	2	TBAB	80	10	1	79	3160
7	2	TBAB	70	10	1	63	2520
8	2	TBAB	60	10	1	45	1800
9	2	TBAB	90	15	1	95	3800
10	2	TBAB	90	8	1	84	3360
11	2	TBAB	90	6	1	56	2240
12	2	DMAP	90	10	1	71	1840
13 d	2	TBAB	90	10	1	75	3000
14 e	2	TBAB	90	10	1	62	2480
15 f	2	TBAB	90	10	1	86	3440
16 g	2	TBAB	90	10	1	83	3320
17 h	-	TBAB	120	10	1	19	-
18 h	2	TBAB	120	10	1	73	29,200

^a Reaction conditions: 50 mmol PO, 0.025 mol% catalyst, 0.5 mol% co-catalyst. ^b Determined by ¹H NMR analysis. Selectivity of cyclic carbonates were all >99%. ^c TOF = Conversion/n_cat/h. ^d 0.025 mol% catalyst, 0.25 mol% co-catalyst. ^e 0.025 mol% catalyst, 0.1 mol% co-catalyst. ^f not excluding the air inside the reaction system. ^g 0.2 mL of H₂O was added to the reaction system. ^h Reaction condition: 50 mmol PO, 0.0025 mol% catalyst, 0.5 mol % TBAB.

, the catalyst and the co-catalyst had a significant effect on the cycloaddition of CO₂ and propylene oxide (substrate). We utilized 0.025 mol% complex 2 in combination with 0.5 mol% TBAB as binary catalysts to obtain solvent-free cyclic carbonates under the conditions of 90 °C, 1MPa, which achieved excellent conversion (89%) and showed high catalytic activity with initial turnover frequency (TOF) of up to 3560 h⁻¹ after 1 h reaction (entry 5, Table 1). We compared it with representative catalysts under different conditions so as to evaluate the high catalytic performance of this catalytic system (

Table 2. Representative homogeneous and heterogeneous cobalt catalysts with high TOF used for the synthesis of cyclic carbonates.

Cat.	Co-Cat.	Catalyst/Epoxide (Mole Ratio)	P (MPa)	T (°C)	Time (h)	Conversions (%)	TOF (h−1)	Ref
Co-Salen	DMAP (1)	(Epichlorohydrin) 1:200000	0.1	120	3	5	3333	[23]
Zn(OPO)2	TBAB (0.9)	(propylene epoxide) 1:40000	3	120	1	46	18,400	[24]
Al-iPOP-2	-	(propylene oxide) 1:10000	1	100	4	97	7600	[25]
Mg-porphyrin	-	(1,2-Epoxyhexane) 1:33333	1.7	120	1	36	12,000	[26]
Zn-CMP	TBAB (0.9)	(propylene oxide) 1:25000	3	120	1	29	11,600	[27]
2	TBAB	1:40000	1	120	1	73	29,200	This work

). The results show that the catalytic activity of complex 2 is higher than most of the published catalysts, such as Zn(OPO)₂, Al-iPOP-2, Co-Salen and so on. Considering that co-catalysts such as ammonium salts were effective in improving the catalytic activity of complexes, different co-catalysts (DMAP and TBAB) were tested with the best performance of TBAB (entries 5 and 12, Table 1). Neither 1, 2 nor TBAB alone could catalyze the reaction with satisfactory yields (9%, 16% and 25%, respectively), while the conversion was increased to 89% via the co-existence of 2 and TBAB. However, in the absence of co-catalysts, catalysts 1 and 2 still showed a certain catalytic activity which might be due to the synergism of N groups (entries 2–3, Table 1). The conversion was decreased from 89% to 49% with the temperature dropping from 90 °C to 60 °C, though it showed excellent catalytic activity with relatively high initial TOF >1800 h⁻¹ (entries 5–8, Table 1). Nonetheless, the catalytic activity was less sensitive to CO₂ pressure than temperature. The conversions remained hardly changed when the CO₂ pressure was reduced from 15 to 8 bar, but the conversions would drop dramatically when the pressure dropped to 6 bar (Table 1, entries 9–11). Good yields were still obtained at lower TBAB loading (0.25 mol% and 0.1 mol%, respectively), with the initial TOF of up to 3000 h⁻¹ and 2480 h⁻¹ (entries 13–14, Table 1), respectively. It was noteworthy that the propylene oxide was used without removal of either oxygen or moisture in advance. Besides, air or water (volume ratio = 20%) (entries 15–16, Table 1) had little influence on the reactions in the catalytic process, indicating that complex 2 had better stability in this process. Gratifyingly, the loading of 0.0025 mol% 2 and 0.5 mol% TBAB for the cycloaddition of PO under the conditions of 120 °C, 1MPa after 1 h reaction, brought about a moderate conversion of 73% and a remarkable TOF as high as 29,200 h⁻¹ (entry 18, Table 1). This result proved that the reaction was still extremely active with a little catalyst content.

To further investigate the catalytic performance of complex 2, different epoxy substrates were tested under mild conditions. As shown in

Table 3. Cycloaddition of CO₂ to different epoxide substrates using complex 2 as a catalyst.

Entry	Substrate	Product	Conversion (%)	TOF (h−1)
1			89	3560
2			99	3960
3			98	3920
4			97	3880
5			75	3000
6			99	3960

Reaction conditions: 10 mmol substrates, 0.025 mol% catalyst, 0.05 mol% co-catalyst, 90 °C, 10 bar CO₂, 1 h. Conversions were determined by ¹H NMR analysis. Selectivity of cyclic carbonates were all >99%.

, all terminal expoxides could be converted into the corresponding cyclic carbonates with high yields and selectivities under the conditions of 90 °C and 10 bar CO₂ after 1h reaction. In addition, epichlorohydrin and allyl glycidyl ether exhibited the best catalytic activity with the highest conversions (99%) and TOF (3960 h⁻¹).

The recyclability and stability of a catalyst plays an integral role in practical application [24,28,29]. The recycling experiment was carried out by the optimal reaction conditions obtained under the above experiment, i.e., 60 °C and 10 bar of CO₂ and 12 h. 1 mol% of the catalyst and propylene oxide were placed in an autoclave and passed through 10 bar of CO₂ for 12 h to calculate the yield. Subsequently, the catalyst was recovered by centrifugation, washed and dried, and reused under the same conditions. The IR spectrum of 2 confirmed that the structural integrity of 2 was well maintained after catalysis (Figure 2b). The cycle of the catalytic system was successfully repeated seven times with little change in conversion (Figure 2a).

Considering the mechanism for coupling reaction of epoxides and CO₂ reported earlier, and frontier molecular orbital calculation results (Table S4), we tentatively proposed a possible catalyzed cycloaddition mechanism of complex 2 in Scheme 2 [12,30,31,32]. Firstly, epoxide was activated by the coordination with multiple Lewis acidic metal centers, and intermediate II was formed. Secondly, nucleophilic reagent Br⁻ of TBAB intermediate III was formed. Finally, CO₂, which was polarized by pyridine groups of complex 2 (N-C = OO), was inserted into the M-O epoxide bonds to generate cyclic carbonates and was epoxidized by an internal attack of CO₂ on the C-Br bond with re-generation of the co-catalyst. Experimental evidence showed that besides the high density of Lewis acid active sites, the existence of nitrogen-containing functionalized ligands 1, which was used in combination with TBAB, was used as a catalyst for the model reaction. Either 1 or 2 TBAB alone could also catalyze the reaction with conversions 9% and 16%, respectively. This mechanism denoted that the high catalytic activity might be due to the synergism of Lewis acidic metal centers and N group.

3. Materials and Methods

3.1. Materials and Characterizations

All samples and solvents were of analytical grade and were ready to use. The ligand N,N’-Di(pyridin-2-yl)pyrazine-2,6-diamine(H₂dpPzda) was synthesized following the reported procedure [19]. FT-IR spectra were obtained on a VERTEX-70 Fourier transform infrared spectrometer with a band ranging from 4000 to 400 cm⁻¹. The elemental analysis of complex was performed using Elementar Germany’s Vario MICRO elemental analyzer. The thermogravimetric analysis data of complex was obtained by using America METTLER TOLEDO thermogravimetric analysis. The UV spectrum data of complex was obtained by using Japan Shimadzu UV-2600 ultraviolet spectrophoto-meter. ¹H NMR spectra were recorded on a JEOL ECS400M spectrometer with reference to the solvent signals. A single crystal of size 0.30 × 0.15 × 0.03 mm³ was placed on the diffractometer, and the crystal structure was determined by graphite monochromated Mo Ka (λ = 0.071073 nm) radiation and ω-2θ scanning. All calculations were performed using the SHLXL-97 program and refined with SHELXL-2014 by full-matrix least-squares on |F|2 values. The CCDC data of complex 2 is 1903857.

3.2. Synthesis of Complex 2

A mixture of Co(NCS)₂ (0.42 mmol) and H₂dpPzda (0.38 mmol) in methanol (50 mL) was stirred overnight and then the solution was filtered to remove impurities and concentrated under vacuum. Natural volatilization obtained deep orange single crystals (33% yield). EA (%) C₁₈H₂₀CoN₈O₂S₂: calcd. C 42.94, H 3.97, N 22.27, S 12.72; found: C 43.42, H 3.61, N 22.39, S 12.68; UV-Vis (CH₃OH) λmax/nm (ε/dm³mol⁻¹·cm⁻¹): 206 (1.70 × 10⁵), 208 (2.48 × 10⁵), 360 (1.96 × 10⁵); IR(KBr, cm⁻¹): 3416 (s); 2050 (w); 1635 (s); 1385 (m); 1151 (m); 772 (w); 624 (w).

3.3. Catalytic Procedure

The detailed catalytic procedure was described in our previous work [33]. The catalyst, cocatalyst, and epoxide were sequentially added to a 100 mL high pressure reactor, then the reactor was pressurized to a required pressure with CO₂, and the mixture was heated and stirred for a while. After completion of the reaction, unreacted CO₂ was evacuated to remove pressure, the lid was removed, the product was taken out and separated, and the conversion of the epoxide was analyzed by ¹H NMR spectroscopy.

4. Conclusions

In summary, we have successfully synthesized a novel cobalt complex [Co(H₂dpPzda)(NCS)₂]·CH₃OH (2) with H₂dpPzda (1) as the chelating and bridging ligand. The structure of complex 2 is Co(II) coordinating with six nitrogen atoms to form an elongated octahedral geometry, with the pyrazine ring acting as a bridging ligand to link molecular units of complex 2 into a one-dimensional chain complex.

The complex 2 has been used for CO₂ conversion, and the results have shown that complex 2/TBAB exhibits high catalytic activity for converting CO₂ into cyclic carbonates under mild conditions. The catalyst could be recycled to maintain the integrity of the structure and remained equal to the level of its catalytic activity even after 6 catalytic rounds, indicating that the novel 1 D supramolecular chain catalysts act as relatively robust materials.