Next Article in Journal
Highly Efficient Asymmetric Morita–Baylis–Hillman Reaction Promoted by Chiral Aziridine-Phosphines
Next Article in Special Issue
Synthesis of Oxygenated Hydrocarbons from Ethanol over Sulfided KCoMo-Based Catalysts: Influence of Novel Fiber- and Powder-Activated Carbon Supports
Previous Article in Journal
Conversion of Weathered Coal into High Value-Added Humic Acid by Magnetically Recoverable Fe3O4/LaNiO3 Nanocatalysts under Solid-Phase Grinding Conditions
Previous Article in Special Issue
Preparation and Catalytic Hydrodechlorination Property of Nano Bimetallic Catalyst Pd–Ni/γAl2O3–SiO2
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 12
Issue 4
10.3390/catal12040393
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Liquid-Phase Selective Hydrogenation of Furfural to Furfuryl Alcohol over Ferromagnetic Element (Fe, Co, Ni, Nd)-Promoted Pt Catalysts Supported on Activated Carbon

by
Sureeporn Saknaphawuth
1,
Patcharaporn Weerachawanasak
2,
Laemthong Chuenchom
3,
Piyasan Praserthdam
1 and
Joongjai Panpranot
1,4,5,*
1
Center of Excellence on Catalysis and Catalytic Reaction Engineering, Department of Chemical Engineering, Faculty of Engineering, Chulalongkorn University, Bangkok 10330, Thailand
2
Department of Chemistry, Faculty of Science, King Mongkut’s Institute of Technology Ladkrabang, Bangkok 10520, Thailand
3
Department of Chemistry, Faculty of Science, Prince of Songkla University, Songkhla 90112, Thailand
4
Bio-Circular-Green-Economy Technology & Engineering Center, BCGeTEC, Department of Chemical Engineering, Faculty of Engineering, Chulalongkorn University, Bangkok 10330, Thailand
5
Department of Chemical & Petroleum Engineering, Faculty of Engineering, Technology and Built Environment, UCSI University, Kuala Lumpur 56000, Malaysia
*
Author to whom correspondence should be addressed.
Catalysts 2022, 12(4), 393; https://doi.org/10.3390/catal12040393
Submission received: 9 February 2022 / Revised: 28 March 2022 / Accepted: 29 March 2022 / Published: 31 March 2022
(This article belongs to the Special Issue Novel Bimetallic Catalysts: Synthesis, Characterization, Evaluation, and Application)
Browse Figures
Versions Notes

Abstract

:
Ferromagnetic element (x = Fe, Co, Ni, and Nd)-promoted Pt/AC catalysts were prepared by co-impregnation method or physical mixing and tested in the liquid-phase hydrogenation of furfural to furfuryl alcohol (FA) under mild conditions (50 °C and 20 bar H2) using water and methanol as the solvent. Among the various catalysts studied, the 0.15FePt/AC exhibited complete conversion of furfural with an FA selectivity of 74% after only 1 h of reaction time in water. The promotional effect of the bimetallic catalysts became less pronounced when methanol was used as the solvent and a 2-furaldehyde dimethyl acetal solvent product was formed. The superior catalyst performances were correlated with the higher Pt dispersion, the presence of low coordination Pt sites, and the strong Pt–Fe interaction as characterized by X-ray diffraction, H2 temperature-programmed reduction (H2-TPR), N2 physisorption, and infrared spectroscopy of the adsorbed CO (CO-IR). However, to simply use a magnet for catalyst separation, 0.5 wt% Fe was the minimum Fe loading on the Pt/AC. The 0.5FePt/AC still exhibited good magnetic properties after the third consecutive runs.

Graphical Abstract

1. Introduction

The energy crisis and environmental pollution have currently been confronting human life due to increasing global energy consumption. Alternative energy resources such as solar, hydropower, wind, geothermal, and biomass have been extensively explored. Renewable biomass is a promising resource to use as feedstock instead of fossil fuel for the production of many petrochemical products. Furfural, a biomass-derived chemical produced by the acid-catalyzed dehydration of xylose [1], can be converted into a wide range of value-added derivative molecules [2]. Approximately 62% of the furfural produced is transformed into furfuryl alcohol (FA) by selective hydrogenation reaction [3]. FA is an interesting high-value chemical and important chemical in the fine chemical industry of lubricants, adhesives, drug intermediates, and dispersing agents and in the polymer industry of phenolic resin, furfural resin, and furan resin [4].
The selective hydrogenation of furfural to FA is an interesting reaction because furfural contains two powerful functional groups, an aldehyde (C=O) and a conjugated system (C=C–C=C) [2]. To produce FA, furfural is hydrogenated at the aldehyde group (C=O) and then transformed into FA. The catalytic hydrogenation of furfural to FA is usually performed either in the gas or liquid phase [5,6,7,8]. Compared to the gas-phase hydrogenation process, liquid-phase hydrogenation of furfural has the advantages of high selectivity and low energy consumption [9]. In the present industrial processes of furfural production, copper chromite (Cu–Cr) is being used as the catalyst for both liquid-phase and gas-phase furfural hydrogenation [10], performing under high-temperature (between 130 and 200 °C) and high-pressure (up to 30 bar) conditions. Although copper chromite exhibits good activity and selectivity toward FA, serious environmental pollution due to toxicity of Cr species is being concerned [11]. A variety of Cr-free catalysts have been investigated, including precious metal catalysts such as Pt [11,12,13,14,15,16], Ru [17,18], and Pd [19,20] and nonprecious metal catalysts such as Co [21], Cu [22,23], and Ni [24,25]. Among these catalysts, Pt exhibits good catalytic performances for selective hydrogenation of furfural to FA under mild conditions. The addition of a second metal including Co, Ni, and Fe has resulted in significant improvement of Pt-based catalysts for FA production. Liu et al. [26] prepared a bimetallic catalyst by adding Fe, Co, and Ni as promoters by a co-impregnation method and tested in the hydrogenation of furfural at 100 °C, 30 bar H2 for 5 h. All the promoters exhibited a positive effect on furfural hydrogenation, especially Fe and Ni, in which furfural conversion and FA and tetrahydrofurfuryl alcohol (THFA) selectivity were significantly improved. Tolek et al. [27] reported the performances of bimetallic PtCo/TiO2 with 0.7 wt% Pt and 0–0.4 wt% Co selective furfural hydrogenation to FA. The Pt-0.2Co/TiO2 catalyst showed the best performance with 100% conversion of furfural and 97.5% selectivity towards FA. Dohade and Dhepe [28] also indicated that Pt–Co supported on activated carbon presented the most improved activity compared to the monometallic catalyst when the reaction was carried out at 180 °C for 8 h. Although the improvement of Pt catalysts promoted by ferromagnetic elements such as Fe and Ni as promoters for Pt catalysts in the hydrogenation of furfural to FA has been demonstrated, the comparison of the catalytic performances among them as well as their magnetic properties have been reported to a lesser extent, especially under different solvents. In the liquid-phase reaction, carbon powders are extremely difficult to separate from the solution and typically require complex and expensive steps such as filtration or centrifugation. The magnetic properties of catalysts make catalyst separation easy by using a simple external magnet. The magnetic properties of catalysts have been utilized in the hydrogenation of furfural to furfuryl alcohol over a Ni–Fe alloy [29] and Fe(NiFe)O4−SiO2 nanoparticle catalysts [30]. Both catalytic and magnetic properties of carbon-supported Pt catalysts with ferromagnetic element promoters have not yet been reported.
In this work, we aimed to compare the liquid-phase hydrogenation of furfural to FA using various ferromagnetic elements (x = Fe, Co, Ni, and Nd)-promoted Pt/activated carbon catalysts under relatively mild reaction conditions (50 °C and 20 bar H2) using water and methanol as the solvent. The structural–activity relationship was investigated by means of X-ray diffraction, H2 temperature-programmed reduction (H2-TPR), N2 physisorption, and infrared spectroscopy of the adsorbed CO (CO-IR). The magnetic properties and reusability of the catalysts were also discussed.

2. Experimental

2.1. Catalyst Preparation

The Pt/AC (0.5 wt%), FePt/AC (0.5 wt% Pt and 0.1–10 wt% Fe), and 0.15MPt/AC (0.5 wt% Pt and 0.15 wt% M: Ni and Co) were prepared by co-impregnation method using commercial activated carbon (C = 90.81%, O = 9.02% and P = 0.18%), tetraammineplatinum (II) chloride hydrate ((Pt (NH3)4Cl2·xH2O), 99.99%, Sigma-Aldrich, Darmstadt, Germany), ferric nitrate nonahydrate (FeN3O9.9H2O, ≥97.0%, Fluka, Buchs, Switzerland), cobalt (II) nitrate hexahydrate (Co(NO3)2·6H2O, ≥98.0%, Carlo Erba, Milano, Italy), and nickel (II) nitrate hexahydrate (Ni(NO3)2·6H2O, ≥98.0%, ACS, Darmstadt, Germany), as C, Pt, Fe, Co, and Ni precursors, respectively. The Pt and the second metal precursors were dissolved in deionized water, and then the aqueous solution was slowly dropped onto the activated carbon. The impregnated catalysts were dried overnight at 110 °C in an oven. Finally, the catalysts were calcined in N2 at 500 °C for 2 h. The catalysts were denoted as Pt/AC and xMPt/AC when x was wt% and M was the second metal. The 0.15NdPt/AC (0.5 wt% Pt and 0.15 wt% Nd) was prepared by physical mixing. Firstly, the Pt/AC catalyst from impregnation was mixed with neodymium powder (<400 μm, Nd ≥ 99.0%, Sigma-Aldrich, Darmstadt, Germany) in toluene at room temperature and stirred for 40 min for uniform mixing. The solvent was removed from the mixture by centrifugation and washed by DI water. Then, the solid catalyst was dried at 110 °C overnight and calcined at 500 °C for 2 h in N2 flow. The catalysts were denoted as 0.15NdPt/AC.

2.2. Catalyst Characterization

The H2-TPR measurements were carried out to determine reducibility and reduction temperature of the Pt-based catalysts. A quartz U-tube reactor was used, and all the catalyst samples were pretreated with a N2 flow (25 mL/min, 1 h, 150 °C). The TPR profiles were obtained by passing carrier gas (10% H2 in nitrogen) through the catalyst samples (25 mL/min, ramping from room temperature to 800 °C at 10 °C/min). The BET (Brunauer–Emmett–Teller) surface area, average pore size diameter, and pore size distribution were determined by physisorption of N2 using a Micromeritics ASAP 2020, Micromeritics Instrument, Norcross, U.S.A. The morphologies of the catalysts were determined by JEOL-6400 scanning electron microscope, JEOL, Tokyo, Japan, and the elemental distribution over the catalyst surface was determined by Link Isis Series 300 program energy dispersive X-ray spectroscopy, respectively. The XRD patterns were collected using a Bruker D8 Advance with a Ni filter and Cu Kα radiation. The platinum active sites were determined by CO pulse chemisorption technique using a Micromeritics ChemiSorb 2750 (pulse chemisorption system), Micromeritics Instrument, Norcross, U.S.A. The FTIR spectra of adsorbed CO were collected using FTIR-620 spectrometer (JASCO, Tokyo, Japan) with a MCT detector at a wavenumber resolution of 2 cm−1. The sample was heated to 500 °C and reduced by H2 for 2 h. The actual metal loadings were determined by inductive coupled plasma-optical emission spectroscopy (ICP-OES) technique.

2.3. Catalyst Activity

The catalyst activity was tested in liquid-phase selective hydrogenation of furfural to furfuryl alcohol. Reactions were performed in a 100 mL stainless steel autoclave reactor (JASCO, Tokyo, Japan). Prior to the catalyst test, the catalysts were reduced under H2 flow (25 cm3 /min) at 500 °C for 2 h. For the furfural hydrogenation reaction, approximately 50 mg of catalyst, 50 µL of furfural, and 10 mL of solvent were added into reactor. Then, reactor was purged with hydrogen three times for removing the air. After that, the reaction was performed at 50 °C, 2 MPa of H2 under stirring. The hydrogenation of furfural was carried out at 50 °C for 2 h in methanol and 1 h in water. After completion of the reaction, the reactor was cooled to below room temperature with an ice-water mixture and depressurized carefully. For methanol solvent, the liquid products were analyzed by a gas chromatograph Shimadzu GC-2014 (Shimadzu, Kyoto, Japan) equipped with a flame ionization detector (FID), and the Rxt-5 capillary column with 30 M length and 0.32 mm inside diameter were used. Then, 0.2 µL was injected into the column and helium was used as a carrier gas. In the case of distilled water solvent, the liquid products were analyzed with high-performance liquid chromatography (Shimadzu 20A) equipped with column Aminex HPX-87H (300 × 7.8 mm). The injection volume was 10 µL, and the absorbance detector wavelength was set at 215 nm. The mobile phase was composed of 86% H3PO4 0.1 N and 14% acetonitrile (HPLC grade), and the flow rate was 0.4 mL min−1.

3. Results and Discussion

3.1. Catalyst Characterization

The XRD patterns of Pt/AC and Pt-based bimetallic catalysts prepared by impregnation and physical mixing in the range of diffraction angles (2Ɵ) between 20° and 80° are shown in Figure 1. The characteristic diffraction peaks at 2θ = 24.4°, 35.5°, and 43.3° could be attributed to graphitized activated carbon [31,32]. However, the higher intensity of the diffraction peak at 2θ = 35.5° was clearly observed on 5FePt/AC and 10FePt/AC, which could possibly be due to the overlap of the diffraction peak of iron, which occurred at around 35.7° [33]. There were no characteristic diffraction peaks corresponding to platinum, cobalt, nickel, and neodymium species detected for all the catalysts due probably to the low amounts of metal present and/or high dispersion of these metals on the carbon supports and/or very the small crystallite size of these metal particles.
Nitrogen adsorption isotherms for the Pt/AC and Pt-based bimetallic catalysts are shown in Figure 2. All the catalyst samples exhibited type I isotherm, and the stepwise increase in the adsorption branch expressed the presence of both micropores and mesopores. The ICP-OES, N2 physisorption, and CO chemisorption results are given in Table 1. The actual loadings of Pt and the second metals were close to their nominal values. For a similar second-metal loading (e.g., 0.15MPt/AC), the calculated atomic ratios of Pt:M were in the range of 0.66–1.57. The BET surface area, the pore volume, and the pore diameters are summarized in Table 1. All the prepared supported carbon catalysts exhibited high surface area in the range of 755–988 m2/g, with the 0.15FePt/AC having the highest surface area of 988 m2/g. For the lowest Fe loading 0.1FePt/AC, the BET surface area was not significantly different from the monometallic Pt/AC (804 and 793 m2/g, respectively). The BET surface area of the bimetallic xMPt/AC (M = Fe, Co, and Ni) with x = 0.15–5 wt% was higher than that of Pt/AC. Such results suggest that the second metal may be highly dispersed as small particles on the external surface of the AC supports, which could create heterogeneity and roughness that led to an increased BET surface area. The Fe dispersion would be maximized on the 0.15FePt/AC so that it exhibited the highest BET surface area (smallest Fe particles). As the Fe loading increased, larger Fe particles would form, and as the consequence the surface area decreased. The lowest BET surface area, 755 m2/g, was observed on the highest Fe loading 10FePt/AC.
The morphologies and elemental distribution of the catalyst samples were investigated by SEM and EDX. The SEM images of Pt/AC and xMPt/AC are shown in Figure 3. All the catalysts showed non-uniform particle size and shape. There were no significant differences in the catalyst morphology when a second metal was added by co-impregnation and physical mixing technique. Moreover, the EDX results from the various 0.15MPt/AC catalysts confirmed the existence of Pt, Fe, Co, Ni, and Nd on the catalyst surface and that the metal could be highly dispersed on the surface.
The magnetic properties were tested by using a simple external magnet to separate the catalyst from liquid media (Figure 4). The efficiency of the magnetic separation is highly dependent on the amount of ferromagnetic elements. The minimum %wt. of Fe loading on the Pt/AC to make the catalyst separable from the liquid by a magnet was determined to be 0.5 wt% Fe. The superior catalyst separation by magnet is demonstrated for higher Fe loadings such as 5% and 10% of Fe loadings.
The characteristic of the surface of dispersed Pt particles was further studied by FTIR of the adsorbed CO on the Pt/AC and Pt-based bimetallic catalysts (Figure 5). The CO adsorption band at around 2070–2100 cm−1 suggests a linear type of CO adsorption [34], and it has been reported that linear-type adsorbed CO dominated on small Pt particles [35]. For the Pt/AC, the adsorption band at 2108 cm−1 could be attributed to the CO adsorbed on a coordinated Pt surface such as Pt(111) and Pt(100), whereas the band at 2070 cm−1 was attributed to the low coordinated Pt sites such as the edge, kink, and corner ones. For all the bimetallic catalysts, the adsorption bands of both positions were slightly shifted towards a higher wavenumber compared to that of Pt/AC. The ratios of CO adsorption on low coordination Pt atoms at edge sites and Pt terrace (111) and (100) are given in Table 1. It can be seen that all the bimetallic catalysts exhibited larger relative quantity of less-coordinated Pt atoms on the edge, kink, and corner, especially for the 0.15 FePt/AC catalyst. In addition, the IR spectra relating to CO adsorbed species of Fe, Co, Ni, and Nd were not detected. Such results are similar to those previously reported by Einaga et al. [36] and Pisduangdaw et al. [37].
The amounts of CO chemisorption on the Pt/AC and 0.15MPt/AC catalyst are demonstrated in Table 1. The number of surface Pt-active atoms on all the Pt catalysts derived from the CO uptake are ranging between 0.82–5.69 × 1018 molecules of CO in the order: 0.15FePt/AC > 0.15CoPt/AC > 0.15NdPt/AC > Pt/AC > 0.15NiPt/AC. The relatively low CO uptake on 0.15NiPt/AC may be due to the partial coverage of the second metal on the Pt surface and/or alloy formation, resulting in a low amount of active Pt surface.
The H2-TPR measurements were carried out to study the reduction behaviors of the monometallic Pt/AC and bimetallic 0.15MPt/AC catalysts, and the results are shown in Figure 6. Both monometallic Pt/AC and bimetallic 0.15MPt/AC catalysts exhibited three reduction peaks at 230–270 °C, 300–350 °C, and 370–700 °C. The first reduction peak of the Pt/AC catalyst was associated with the reduction of Pt oxide to Pt metal [16]. When the second metals Fe, Co, Ni, and Nd were introduced into the monometallic Pt catalysts, the reduction temperature for PtOx was lower due probably to the formation of smaller Pt oxide particles (higher Pt dispersion) and/or the interaction between the second metal and Pt in the bimetallic catalysts [9]. The second reduction peak was typically correlated to the reduction of Pt species interacting with the carbon support. Among the various ferromagnetic-element-promoted Pt/AC catalysts, the second reduction peak was higher and shifted to a higher reduction temperature only when Fe was added, which indicated a stronger interaction between the metal and carbon support and/or a Pt–Fe alloy [26]. The third reduction peaks were the carbon gasification process to form CH4. It had been reported that the formation of methane generally occurs in the temperature range of 390–800 °C [26].

3.2. Catalytic Reaction Study

The catalytic activities of the prepared catalysts were evaluated in the liquid-phase hydrogenation of furfural to furfuryl alcohol under mild reaction conditions (temperature of 50 °C and H2 pressure of 2 MPa). All the catalysts were reduced at 500 °C in H2 flow for 2 h before the reaction test. In a liquid-phase reaction, the choice of solvent usually has an impact on the catalytic activity [13]. In this study, methanol and water were used as the medium to investigate the solvent effect in the hydrogenation of furfural, and the results are summarized in Table 2. The addition of ferromagnetic metal on the Pt/AC catalysts showed different effects on the catalytic performances in the furfural hydrogenation, depending on the solvent used. Using methanol as the solvent, a slight improvement on the FA yield was found on the 0.15%FePt/AC catalyst (36.4%) compared to the Pt/AC (31.3%). Whilst the other bimetallic 0.15%CoPt/AC and 0.15%NiPt/AC catalysts exhibited much lower FA yields at 22.3% and 11.3%, respectively. In addition, the furfural conversion and FA selectivity decreased with increasing Fe loading from 0.15 to 5 and 10 wt%, especially for the 10FePt/AC that showed the lowest performance. Besides, the 2-furaldehyde dimethyl acetal solvent product (SP), which is the side reaction product that occurred from the methanol reacted with furfural, was found when using methanol as the solvent. SP was normally observed in alcohols solvent, not only methanol but also ethanol, isopropanol, etc. [11,13]. The other by-products include 2-methylfuran and 1-pentanol, which were formed via hydrogenolysis of FA and ring-opening of 2-methylfuran, respectively [2].
The catalytic activity of various amounts of Fe loading and other bimetallic 0.15MPt/AC catalysts was also examined in the aqueous-phase hydrogenation of furfural to FA at 50 °C and 2 MPa H2, 1 h reaction time using water as the solvent (Table 2). Unlike the use of methanol solvent, when the reaction was carried out in water, all the PtFe/AC showed higher furfural conversion than the monometallic Pt/AC, except for the 10FePt/AC. The conversion of furfural varied in the order: 0.15FePt/AC (100%) = 0.1FePt/AC (100%) > 0.2FePt/AC (91.9%) > 5FePt/AC (83.6%) > Pt/AC (81.8%) >> 10FePt/AC (58.4%). In addition, the FA selectivity decreased in the order: 0.15FePt/AC (74.1%) > 0.2FePt/AC (65.6%) > 0.1FePt/AC (57.4%) > 5FePt/AC (56.6%) > Pt/AC (45.2%) ∼ 10FePt/AC (41.4%). The results indicated that the xFePt/AC series with the small amount of Fe (0.1–0.5 wt%) could improve both furfural conversion and FA selectivity of the Pt/AC catalysts, especially in water solvent. The superior catalyst performances were attributed to high Pt dispersion and a strong interaction between Pt and the carbon support and/or the formation of a Pt–Fe alloy [26,38]. The role of Fe to enhance the selectivity of carbonyl compound (C=O) reduction has been suggested by Ananthan S.A. et al. that Pt–Fe sites favored the di- σCO adsorption, which promoted the activation of the C=O group over the supported Pt–Fe catalysts [39].
Furthermore, the catalytic performances of Pt/AC, 0.15FePt/AC, 0.15CoPt/AC, 0.15NiPt/AC, and 0.15NdPt/AC were also investigated in water solvent. The hydrogenation of furfural to FA can occur from hydrogenation of the aldehyde group (C=O). The conversion of furfural of the Pt-based bimetallic catalysts were ranged between 75.5–100%. Improvement in furfural conversion by co-impregnation was correlated to high Pt dispersion with higher Pt active sites as determined by CO chemisorption. Surprisingly, 0.15NdPt/AC with higher Pt sites results revealed lower hydrogenation activity in the furfural hydrogenation than the monometallic Pt/AC. It is likely that the physical mixing of Nd power and Pt/AC catalyst led to poor Pt–Nd interaction. From the H2-TPR, the second reduction peak, which was attributed to the Pt species that strongly interacted with the support, became flattened on the 0.15NdPt/AC. In other words, the addition of Nd could weaken the Pt–support interaction. Hence, the catalyst was less active under the reaction conditions despite its high dispersion. The FA selectivity of all the other 0.15 MPt/AC catalysts (Co, Ni, Nd) was not much different at around 32.6–47.6% and was similar to those obtained on the monometallic Pt/AC catalyst (45.2%). The highest conversion of furfural and FA selectivity on the 0.15FePt/AC was in accordance with the high dispersion with high Pt active sites and the strongest Pt–Fe or Pt–C interaction and/or a Pt–Fe alloy as indicated by the shift of the reduction temperature in the H2-TPR profiles. Moreover, the hydrogenation of the aldehyde group (C=O) would preferentially proceed on less-coordinated Pt sites such as the edge, corner, and kink.
Considering the solvent effect between methanol and water on all the Pt-based bimetallic catalysts, the use of water exhibited higher conversion and selectivity than methanol, although a shorter reaction time was used (1 h). It can be concluded that the activity and product selectivity in furfural hydrogenation over Pt-based bimetallic catalysts were promoted by the higher polar solvent. It is generally accepted that hydrogenation of α- and β-unsaturated aldehydes is controlled by hydrogen solubility, solvent polarity, and the interaction between the catalyst and solvent [40]. A comparison between the Pt-based catalyst in this study and those reported in the literature is summarized in Table 3. At state-of-the-art, the highest furfural conversion (>99%) with FA selectivity (>99%) could be obtained on the Pt/NC-BS-500 catalyst in water solvent but under more severe conditions (100 °C and 2 MPa H2), longer reaction time (4 h), and higher amount of Pt loading (5 wt%) [16]. The carbon support material from bamboo shoots was prepared in two steps, including a hydrothermal treatment and a carbonization process, and Pt-supported on carbon was prepared using an ultrasound-assisted reduction method. The catalysts in this study achieved similar conversion with relatively high FA selectivity under milder reaction conditions. The beneficial effect of water solvent was also emphasized.
The 0.5FePt/AC catalyst was chosen for recyclability tests because it contained the minimum loading of Fe that made the catalyst separable from the liquid by a magnet. The results are shown in Figure 7. After the reaction, the catalyst was separated by a magnet, washed with DI water three times, dried in an oven at 110 °C overnight, and used under the same reaction conditions in water solvent. It was found that the conversion of furfural and FA selectivity decreased after the first run but were not significantly changed in the consecutive run. During the first run, some large Pt particles with weak metal–support interaction could be leached out from the carbon support. Comparison of the EDX of the fresh and spent catalyst after the third run is shown in Table 4. The differences in the O/C ratios suggest the deposition of carbon species from the liquid phase under the conditions used. The XPS results of C 1s (Table 5) also suggest the increase of C−O−C and O−C=O species on the spent catalysts compared to the fresh one, of which more than 90% was C−C species [43]. The Fe 2p peaks on both fresh and spent catalysts at around 711.2–711.4 eV were attributed to Fe3+ in Fe2O3 [44], and the amounts were not significantly different (<1 wt%). After the third cycle run, the 0.5FePt/AC catalyst still maintained the magnetic properties and could be separated by a magnet (Figure 8).

4. Conclusions

The liquid-phase selective hydrogenation of furfural to FA under mild conditions (50 °C and 20 bar H2) was studied over various ferromagnetic elements (x = Fe, Co, Ni, and Nd)-promoted Pt/activated carbon catalysts. Among the ferromagnetic elements, the 0.15FePt/AC catalyst exhibited the best improvement of catalyst performances in terms of FA yield in both methanol and water solvent, which was attributed to the highest Pt dispersion with low coordinated Pt sites, and the strong Pt–Fe interaction as revealed by CO chemisorption and FTIR of the adsorbed CO results. The highest FA yield was 74% in water. For all the Pt-based bimetallic catalysts, the use of water medium showed higher furfural conversion and FA selectivity than methanol, despite a shorter reaction time used (1 h). The minimum Fe loading was 0.5 wt% to make the bimetallic catalysts separable by a simple magnet. The activities and selectivity of the 0.5FePt/AC slightly dropped after the first cycle but remained stable afterward. The catalysts, however, still exhibited magnetic properties after the consecutive runs.

Author Contributions

S.S.: Methodology, Investigation, Formal analysis, Writing—original draft, P.W.: Formal analysis, L.C.: Resources, Formal analysis, Supervision, P.P.: Resources, J.P.: Supervision, Conceptualization, Formal analysis, Writing—review and editing, Funding acquisition. All authors have read and agreed to the published version of the manuscript.

Funding

National Research Council of Thailand (NRCT)—Research Team Promotion grant—Joongjai Panpraont, the Thailand Science Research and Innovation (IRN62W00001).

Acknowledgments

The financial supports from the National Research Council of Thailand (Research Team Promotion Grant-Joongjai Panpranot) and the Thailand Science Research and Innovation (IRN62W0001) are gratefully acknowledged.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Mariscal, R.; Maireles-Torres, P.; Ojeda, M.; Sádaba, I.; Granados, M.L. Furfural: A renewable and versatile platform molecule for the synthesis of chemicals and fuels. Energy Environ. Sci. 2016, 9, 1144–1189. [Google Scholar] [CrossRef]
  2. Yan, K.; Wu, G.; Lafleur, T.; Jarvis, C. Production, properties and catalytic hydrogenation of furfural to fuel additives and value-added chemicals. Renew. Sustain. Energy Rev. 2014, 38, 663–676. [Google Scholar] [CrossRef]
  3. Peleteiro, S.; Rivas, S.; Alonso, J.L.; Santos, V.; Parajó, J.C. Furfural production using ionic liquids: A review. Bioresour. Technol. 2016, 202, 181–191. [Google Scholar] [CrossRef]
  4. Sun, D.; Sato, S.; Ueda, W.; Primo, A.; Garcia, H.; Corma, A. Production of C4 and C5 alcohols from biomass-derived materials. Green Chem. 2016, 18, 2579–2597. [Google Scholar] [CrossRef]
  5. Nagaraja, B.M.; Padmasri, A.H.; Raju, B.D.; Rao, K.R. Vapor phase selective hydrogenation of furfural to furfuryl alcohol over Cu–MgO coprecipitated catalysts. J. Mol. Catal. A Chem. 2007, 265, 90–97. [Google Scholar] [CrossRef]
  6. Wu, J.; Shen, Y.; Liu, C.; Wang, H.; Geng, C.; Zhang, Z. Vapor phase hydrogenation of furfural to furfuryl alcohol over environmentally friendly Cu–Ca/SiO2 catalyst. Catal. Commun. 2005, 6, 633–637. [Google Scholar] [CrossRef]
  7. Sharma, R.V.; Das, U.; Sammynaiken, R.; Dalai, A.K. Liquid phase chemo-selective catalytic hydrogenation of furfural to furfuryl alcohol. Appl. Catal. A Gen. 2013, 454, 127–136. [Google Scholar] [CrossRef]
  8. Yan, K.; Jarvis, C.; Lafleur, T.; Qiao, Y.; Xie, X. Novel synthesis of Pd nanoparticles for hydrogenation of biomass-derived platform chemicals showing enhanced catalytic performance. RSC Adv. 2013, 3, 25865–25871. [Google Scholar] [CrossRef]
  9. Jia, P.; Lan, X.; Li, X.; Wang, T. Highly active and selective NiFe/SiO2 bimetallic catalyst with optimized solvent effect for the liquid-phase hydrogenation of furfural to furfuryl alcohol. ACS Sustain. Chem. Eng. 2018, 6, 13287–13295. [Google Scholar] [CrossRef]
  10. Jia, P.; Lan, X.; Li, X.; Wang, T. Deactivation mechanistic studies of copper chromite catalyst for selective hydrogenation of 2-furfuraldehyde. J. Catal. 2013, 299, 336–345. [Google Scholar]
  11. Taylor, M.J.; Durndell, L.J.; Isaacs, M.A.; Parlett, C.M.; Wilson, K.; Lee, A.F.; Kyriakou, G. Highly selective hydrogenation of furfural over supported Pt nanoparticles under mild conditions. Appl. Catal. B Environ. 2016, 180, 580–585. [Google Scholar] [CrossRef]
  12. Merlo, A.B.; Vetere, V.; Ruggera, J.F.; Casella, M.L. Bimetallic PtSn catalyst for the selective hydrogenation of furfural to furfuryl alcohol in liquid-phase. Catal. Commun. 2009, 10, 1665–1669. [Google Scholar] [CrossRef]
  13. Chen, X.; Zhang, L.; Zhang, B.; Guo, X.; Mu, X. Highly selective hydrogenation of furfural to furfuryl alcohol over Pt nanoparticles supported on g-C3N4 nanosheets catalysts in water. Sci. Rep. 2016, 6, 28558. [Google Scholar] [CrossRef]
  14. Biradar, N.S.; Hengne, A.A.; Birajdar, S.N.; Swami, R.; Rode, C.V. Tailoring the product distribution with batch and continuous process options in catalytic hydrogenation of furfural. Org. Process Res. Dev. 2014, 18, 1434–1442. [Google Scholar] [CrossRef]
  15. Wang, C.; Guo, Z.; Yang, Y.; Chang, J.; Borgna, A. Hydrogenation of furfural as model reaction of bio-oil stabilization under mild conditions using multiwalled carbon nanotube (MWNT)-supported pt catalysts. Ind. Eng. Chem. Res. 2014, 53, 11284–11291. [Google Scholar] [CrossRef]
  16. Liu, X.; Zhang, B.; Fei, B.; Chen, X.; Zhang, J.; Mu, X. Tunable and selective hydrogenation of furfural to furfuryl alcohol and cyclopentanone over Pt supported on biomass-derived porous heteroatom doped carbon. Faraday Discuss 2017, 202, 79–98. [Google Scholar] [CrossRef] [PubMed]
  17. Aldosari, O.F.; Iqbal, S.; Miedziak, P.J.; Brett, G.L.; Jones, D.R.; Liu, X.; Edwards, J.K.; Morgan, D.J.; Knight, D.K.; Hutchings, G.J. Pd–Ru/TiO2 catalyst—An active and selective catalyst for furfural hydrogenation. Catal. Sci. Technol. 2016, 6, 234–242. [Google Scholar] [CrossRef] [Green Version]
  18. Musci, J.J.; Merlo, A.B.; Casella, M.L. Aqueous phase hydrogenation of furfural using carbon-supported Ru and RuSn catalysts. Catal. Today 2017, 296, 43–50. [Google Scholar] [CrossRef]
  19. Garcia-Olmo, A.J.; Yepez, A.; Balu, A.M.; Prinsen, P.; Garcia, A.; Maziere, A.; Len, C.; Luque, R. Activity of continuous flow synthesized Pd-based nanocatalysts in the flow hydroconversion of furfural. Tetrahedron 2017, 73, 5599–5604. [Google Scholar] [CrossRef]
  20. Lee, J.; Woo, J.; Nguyen-Huy, C.; Lee, M.S.; Joo, S.H.; An, K. Highly dispersed Pd catalysts supported on various carbons for furfural hydrogenation. Catal. Today 2020, 350, 71–79. [Google Scholar] [CrossRef]
  21. Audemar, M.; Ciotonea, C.; De Oliveira Vigier, K.; Royer, S.; Ungureanu, A.; Dragoi, B.; Dumitriu, E.; Jérôme, D. Selective hydrogenation of furfural to furfuryl alcohol in the presence of a recyclable cobalt/SBA-15 catalyst. ChemSusChem 2015, 8, 1885–1891. [Google Scholar] [CrossRef] [PubMed]
  22. Jiménez-Gómez, C.P.; Cecilia, J.A.; Moreno-Tost, R.; Maireles-Torres, P. Selective furfural hydrogenation to furfuryl alcohol using Cu-based catalysts supported on clay minerals. Top. Catal. 2017, 60, 1040–1053. [Google Scholar] [CrossRef]
  23. Villaverde, M.M.; Bertero, N.M.; Garetto, T.F.; Marchi, A.J. Selective liquid-phase hydrogenation of furfural to furfuryl alcohol over Cu-based catalysts. Catal. Today 2013, 213, 87–92. [Google Scholar] [CrossRef]
  24. Kotbagi, T.V.; Gurav, H.R.; Nagpure, A.S.; Chilukuri, S.V.; Bakker, M.G. Highly efficient nitrogen-doped hierarchically porous carbon supported Ni nanoparticles for the selective hydrogenation of furfural to furfuryl alcohol. RSC Adv. 2016, 6, 67662–67668. [Google Scholar] [CrossRef] [Green Version]
  25. Gong, W.; Chen, C.; Zhang, H.; Zhang, Y.; Zhang, Y.; Wang, G.; Zhao, H. Highly selective liquid-phase hydrogenation of furfural over N-doped carbon supported metallic nickel catalyst under mild conditions. Mol. Catal. 2017, 429, 51–59. [Google Scholar] [CrossRef]
  26. Liu, L.; Lou, H.; Chen, M. Selective hydrogenation of furfural over Pt based and Pd based bimetallic catalysts supported on modified multiwalled carbon nanotubes (MWNT). Appl. Catal. A Gen. 2018, 550, 1–10. [Google Scholar] [CrossRef]
  27. Tolek, W.; Khruechao, K.; Pongthawornsakun, B.; Mekasuwandumrong, O.; Aires, F.J.C.S.; Weerachawanasak, P.; Panpranot, J. Flame spray-synthesized Pt-Co/TiO2 catalysts for the selective hydrogenation of furfural to furfuryl alcohol. Catal. Commun. 2021, 149, 106246. [Google Scholar] [CrossRef]
  28. Dohade, M.G.; Dhepe, P.L. One pot conversion of furfural to 2-methylfuran in the presence of PtCo bimetallic catalyst. Clean Technol. Environ. Policy 2017, 20, 703–713. [Google Scholar] [CrossRef]
  29. Putro, W.S.; Hara, T.; Ichikuni, N.; Shimazu, S. Efficiently recyclable and easily separable Ni-Fe alloy catalysts for chemoselective hydrogenation of biomass-derived furfural. Chem. Lett. 2017, 46, 149–151. [Google Scholar] [CrossRef]
  30. Halilu, A.; Ali, T.H.; Atta, A.Y.; Sudarsanam, P.; Bhargava, S.K.; Abd Hamid, S.B. Highly Selective hydrogenation of biomass-derived furfural into furfuryl alcohol using a novel magnetic nanoparticles catalyst. Energy Fuels 2016, 30, 2216–2226. [Google Scholar] [CrossRef]
  31. Liu, X.-Y.; Huang, M.; Ma, H.-L.; Zhang, Z.-Q.; Gao, J.-M.; Zhu, Y.-L.; Han, X.-L.; Guo, X.-Y. Preparation of a carbon-based solid acid catalyst by sulfonating activated carbon in a chemical reduction process. Molecules 2010, 15, 7188–7196. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  32. Chen, H.; He, D.; He, Q.; Jiang, P.; Zhou, G.; Fu, W. Selective hydrogenation of p-chloronitrobenzene over an Fe promoted Pt/AC catalyst. RSC Adv. 2017, 7, 29143–29148. [Google Scholar] [CrossRef] [Green Version]
  33. Dorniani, D.; Hussein, M.Z.B.; Kura, A.U.; Fakurazi, S.; Shaari, A.H.; Ahmad, Z. Preparation of Fe(3)O(4) magnetic nanoparticles coated with gallic acid for drug delivery. Int. J. Nanomed. 2012, 7, 5745–5756. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  34. Yoshida, H.; Igarashi, N.; Fujita, S.I.; Panpranot, J.; Arai, M. Influence of crystallite size of TiO2 supports on the activity of dispersed pt catalysts in liquid-phase selective hydrogenation of 3-nitrostyrene, nitrobenzene, and styrene. Catal. Lett. 2014, 145, 606–611. [Google Scholar] [CrossRef]
  35. Corma, A.; Serna, P.; Concepción, P.; Calvino, J.J. Transforming nonselective into chemoselective metal catalysts for the hydrogenation of substituted nitroaromatics. J. Am. Chem. Soc. 2008, 130, 8748–8753. [Google Scholar] [CrossRef] [PubMed]
  36. Einaga, H.; Urahama, N.; Tou, A.; Teraoka, Y. CO oxidation over TiO2-supported Pt–Fe catalysts prepared by coimpregnation methods. Catal. Lett. 2014, 144, 1653–1660. [Google Scholar] [CrossRef]
  37. Pisduangdaw, S.; Mekasuwandumrong, O.; Fujita, S.I.; Arai, M.; Yoshida, H.; Panpranot, J. One step synthesis of Pt–Co/TiO2 catalysts by flame spray pyrolysis for the hydrogenation of 3-nitrostyrene. Catal. Commun. 2015, 61, 11–15. [Google Scholar] [CrossRef]
  38. Da Silva, A.B.; Jordão, E.; Mendes, M.J.; Fouilloux, P. Selective hydrogenation of cinnamaldehyde with Pt And Pt-Fe catalysts: Effects of the support. Braz. J. Chem. Eng. 1998, 15, 140–144. [Google Scholar] [CrossRef]
  39. Ananthan, S.A.; Narayanan, V. Liquid-phase hydrogenation of citral over Pt_TiO2 and Pt-Fe_TiO2 catalysts. Asian J. Chem. 2011, 23, 183–188. [Google Scholar]
  40. Von Arx, M.; Mallat, T.; Baiker, A. Unprecedented selectivity behaviour in the hydrogenation of an α,β-unsaturated ketone: Hydrogenation of ketoisophorone over alumina-supported Pt and Pd. J. Mol. Catal. A Chem. 1999, 148, 275–283. [Google Scholar] [CrossRef]
  41. Fuente-Hernández, A.; Lee, R.; Béland, N.; Zamboni, I.; Lavoie, J.M. Reduction of Furfural to Furfuryl Alcohol in Liquid Phase over a Biochar-Supported Platinum Catalyst. Energies 2017, 10, 286. [Google Scholar] [CrossRef]
  42. Chen, B.; Li, F.; Huang, Z.; Yuan, G. Tuning catalytic selectivity of liquid-phase hydrogenation of furfural via synergistic effects of supported bimetallic catalysts. Appl. Catal. A Gen. 2015, 500, 23–29. [Google Scholar] [CrossRef]
  43. Shchukarev, A.; Korolkov, D. XPS study of group IA carbonates. Open Chem. 2004, 2, 347–362. [Google Scholar] [CrossRef] [Green Version]
  44. Biesinger, M.C.; Payne, B.P.; Grosvenor, A.P.; Lau, L.W.; Gerson, A.R.; Smart, R.S.C. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 2011, 257, 2717–2730. [Google Scholar] [CrossRef]
Catalysts 12 00393 g001 550
Figure 1. XRD pattern of Pt-based catalyst: (a) AC, (b) Pt/AC, (c) 0.1FePt/AC, (d) 0.15FePt/AC, (e) 0.2FePt/AC, (f) 5FePt/AC, (g) 10FePt/AC, (h) 0.15CoPt/AC, (i) 0.15NiPt/AC, and (j) 0.15NdPt/AC.
Figure 1. XRD pattern of Pt-based catalyst: (a) AC, (b) Pt/AC, (c) 0.1FePt/AC, (d) 0.15FePt/AC, (e) 0.2FePt/AC, (f) 5FePt/AC, (g) 10FePt/AC, (h) 0.15CoPt/AC, (i) 0.15NiPt/AC, and (j) 0.15NdPt/AC.
Catalysts 12 00393 g001
Catalysts 12 00393 g002 550
Figure 2. Nitrogen adsorption/desorption results of Pt-based catalysts.
Figure 2. Nitrogen adsorption/desorption results of Pt-based catalysts.
Catalysts 12 00393 g002
Catalysts 12 00393 g003 550
Figure 3. SEM images of (a) Pt/AC, (b) 0.15FePt/AC, (c) 5FePt/AC, (d) 10FePt/AC, (e) 0.15CoPt/AC, (f) 0.15NiPt/AC, and (g) 0.15NdPt/AC catalysts and the corresponding elemental mapping images of (h) platinum, (i) iron, (j) cobalt, (k) nickel, and (l) neodymium on 0.15MPt/AC.
Figure 3. SEM images of (a) Pt/AC, (b) 0.15FePt/AC, (c) 5FePt/AC, (d) 10FePt/AC, (e) 0.15CoPt/AC, (f) 0.15NiPt/AC, and (g) 0.15NdPt/AC catalysts and the corresponding elemental mapping images of (h) platinum, (i) iron, (j) cobalt, (k) nickel, and (l) neodymium on 0.15MPt/AC.
Catalysts 12 00393 g003
Catalysts 12 00393 g004 550
Figure 4. Magnetic separation of (a) 0.15FePt /AC, (b) 0.5FePt/AC, (c) 1FePt/AC, (d) 2FePt/AC, (e) 3FePt/AC, (f) 4FePt/AC, (g) 5FePt/AC, and (h) 10FePt/AC.
Figure 4. Magnetic separation of (a) 0.15FePt /AC, (b) 0.5FePt/AC, (c) 1FePt/AC, (d) 2FePt/AC, (e) 3FePt/AC, (f) 4FePt/AC, (g) 5FePt/AC, and (h) 10FePt/AC.
Catalysts 12 00393 g004
Catalysts 12 00393 g005 550
Figure 5. CO-IR result of the Pt-based catalysts.
Figure 5. CO-IR result of the Pt-based catalysts.
Catalysts 12 00393 g005
Catalysts 12 00393 g006 550
Figure 6. H2 temperature-programmed reduction profiles of the catalysts.
Figure 6. H2 temperature-programmed reduction profiles of the catalysts.
Catalysts 12 00393 g006
Catalysts 12 00393 g007 550
Figure 7. Catalyst recyclability with the 0.5FePt/AC catalysts for the conversion of furfural to furfuryl alcohol.
Figure 7. Catalyst recyclability with the 0.5FePt/AC catalysts for the conversion of furfural to furfuryl alcohol.
Catalysts 12 00393 g007
Catalysts 12 00393 g008 550
Figure 8. Magnetic separation of 0.5FePt/AC catalyst (a) after 1st cycle run and (b) after 3rd cycle run.
Figure 8. Magnetic separation of 0.5FePt/AC catalyst (a) after 1st cycle run and (b) after 3rd cycle run.
Catalysts 12 00393 g008
Table
Table 1. Atomic ratio, N2 physisorption properties, CO-IR analysis, and active sites of Pt-based catalysts.
Table 1. Atomic ratio, N2 physisorption properties, CO-IR analysis, and active sites of Pt-based catalysts.
CatalystICP Results (Metal Loading, wt%) aAtomic Ratio
(Pt/M) b		N2 Physisorption PropertiesThe Ratio of CO Adsorption on Pt Atom at Edge Sites and Pt Terrace dActive Sites
(×1018 Molecule CO/g cat.) e
PtM
(M = Fe, Co, or Ni)		Surface Area
(m2/g)		Pore Volume
(cm3/g) c		Average Pore Size
(nm) c
Pt/AC0.51--8040.0923.50.090.95
0.1FePt/ACn.d.n.d.n.d.7930.1103.4n.d.n.d.
0.15FePt/AC0.530.230.669880.1023.20.475.69
0.2FePt/ACn.d.n.d.n.d.8520.1063.3n.d.n.d.
5FePt/AC0.504.700.038600.1293.1n.d.n.d.
10FePt/AC0.429.500.0137550.1093.9n.d.n.d.
0.15CoPt/AC0.520.101.579150.1043.40.212.94
0.15NiPt/AC0.470.160.888260.1103.40.340.82
0.15NdPt/AC0.48n.d.n.d.7800.0943.50.161.85
n.d. = not determined. a Metal loading measured by ICP-OES. b Calculated from percentage of metal loading. c Calculated from BJH desorption method. d Based on CO-IR result. e Based on CO-chemisorption.
Table
Table 2. Catalytic reaction of the selective hydrogenation of furfural to furfuryl alcohol over the prepared catalysts.
Table 2. Catalytic reaction of the selective hydrogenation of furfural to furfuryl alcohol over the prepared catalysts.
CatalystSolventReaction Time (h)Conversion (%)Selectivity (%)
FASPOthers a
Pt/ACMethanol253.958.04.137.9
0.15FePt/ACMethanol264.156.86.037.2
5FePt/ACMethanol247.610.41.188.5
10FePt/ACMethanol214.107.093.0
0.15CoPt/ACMethanol262.935.41.563.1
0.15NiPt/ACMethanol226.742.421.336.3
Pt/ACWater181.845.2-54.8
0.1FePt/ACWater110057.4-42.6
0.15FePt/ACWater110074.1-25.9
0.2FePt/ACWater191.965.6-34.4
0.5FePt/ACWater195.958.1-41.9
5FePt/ACWater183.656.6-43.4
10FePt/ACWater158.441.4-58.6
0.15CoPt/ACWater188.147.6-52.4
0.15NiPt/ACWater196.732.6-67.4
0.15NdPt/ACWater175.532.6-67.4
Reaction (50 μL furfural in 10 mL solvent) at 50 ℃ with a 50 mg catalyst under 2 MPa of H2 for 120 min in methanol and 60 min in water and catalysts were reduced at 500 °C, 2 h in H2 flow. a Based on GC–MS analysis, the by-products include 2-methylfuran and 1-pentanol.
Table
Table 3. Comparison of the prepared catalysts and reported in the literature for the liquid-phase hydrogenation of furfural.
Table 3. Comparison of the prepared catalysts and reported in the literature for the liquid-phase hydrogenation of furfural.
No.CatalystsPreparation MethodReaction ConditionsSolventReaction Time (h)Reaction ResultsRef.
Conversion (%)Selectivity (%)
10.15FePt/ACCo-impregnation50 °C, 2 MPa H2H2O110074.1This work
2Pt-Fe/MWNTCo-impregnation100 °C, 3 MPa H2Ethanol595.291.8[26]
Pt-Fe/H-ACCo-impregnation100 °C, 10.3 MPa H2Ethanol535.533.4
Pt-Fe/ACCo-impregnation100 °C, 10.3 MPa H2Ethanol552.928.6
Pt-Ni/MWNTCo-impregnation100 °C, 10.3 MPa H2Ethanol595.984.1
Pt-Co/MWNTCo-impregnation100 °C, 10.3 MPa H2Ethanol586.780.3
35%Pt@TECNUltrasound-assisted reduction100 °C, 1 MPa H2H2O5>99>99[13]
5%Pt@TECNUltrasound-assisted reduction100 °C, 2 MPa H2H2O19898
43%Pt/BCWet impregnation210 °C, 10.3 MPa H2Toluene260.879.2[41]
53%Pt/ACWet impregnation180 °C, 1 MPa H2Isopropanol810071[28]
6Pt/NC-BS-500Ultrasound-assisted reduction100 °C, 1 MPa H2H2O4>99>99[16]
7Pt-Sn0.3/SiO2Controlled surface reaction100 °C, 1 MPa H22-propanol8>9096.2[12]
8Pt-Re/TiO2-ZrO2Co-impregnation130 °C, 5 MPa H2Ethanol810095.7[42]
Pt-In/TiO2-ZrO2Co-impregnation130 °C, 5 MPa H2Ethanol873.374.9
Pt-Sn/TiO2-ZrO2Co-impregnation130 °C, 5 MPa H2Ethanol898.347.8
Table
Table 4. EDX results of fresh and spent 0.5 FePt/AC catalysts after 3rd cycle.
Table 4. EDX results of fresh and spent 0.5 FePt/AC catalysts after 3rd cycle.
0.5FePt/ACEDX (wt%)Ratio O/C
COPtFe
Fresh90.576.421.861.90.066
Spent 3rd cycle94.23.411.640.790.036
Table
Table 5. XPS results of fresh and spent 0.5 FePt/AC catalysts after 3rd cycle.
Table 5. XPS results of fresh and spent 0.5 FePt/AC catalysts after 3rd cycle.
FreshAfter 3rd Cycle
Binding Energy (eV)Mass (%)Binding Energy (eV)Mass (%)
C 1s285.068.71285.043.39
288.96.57286.626.89
288.712.60
O 1s533.724.30533.416.23
Fe 2p711.40.42711.20.90
Ratio O/C 0.323 0.196
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Saknaphawuth, S.; Weerachawanasak, P.; Chuenchom, L.; Praserthdam, P.; Panpranot, J. Liquid-Phase Selective Hydrogenation of Furfural to Furfuryl Alcohol over Ferromagnetic Element (Fe, Co, Ni, Nd)-Promoted Pt Catalysts Supported on Activated Carbon. Catalysts 2022, 12, 393. https://doi.org/10.3390/catal12040393

AMA Style

Saknaphawuth S, Weerachawanasak P, Chuenchom L, Praserthdam P, Panpranot J. Liquid-Phase Selective Hydrogenation of Furfural to Furfuryl Alcohol over Ferromagnetic Element (Fe, Co, Ni, Nd)-Promoted Pt Catalysts Supported on Activated Carbon. Catalysts. 2022; 12(4):393. https://doi.org/10.3390/catal12040393

Chicago/Turabian Style

Saknaphawuth, Sureeporn, Patcharaporn Weerachawanasak, Laemthong Chuenchom, Piyasan Praserthdam, and Joongjai Panpranot. 2022. "Liquid-Phase Selective Hydrogenation of Furfural to Furfuryl Alcohol over Ferromagnetic Element (Fe, Co, Ni, Nd)-Promoted Pt Catalysts Supported on Activated Carbon" Catalysts 12, no. 4: 393. https://doi.org/10.3390/catal12040393

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.