Next Article in Journal
Insights on the Modulation of SIRT5 Activity: A Challenging Balance
Previous Article in Journal
Synthesis and Evaluation of Anti-HIV Activity of Mono- and Di-Substituted Phosphonamidate Conjugates of Tenofovir
Previous Article in Special Issue
Prompt and Long-Lived Anti-Kasha Emission from Organic Dyes
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 27
Issue 14
10.3390/molecules27144448
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation of Polycarbonate-ZnO Nanocomposite Films: Surface Investigation after UV Irradiation

by
Babak Jaleh
1,*,
Sara Hamzehi
2,
Reza Sepahvand
2,
Saeid Azizian
3,
Mahtab Eslamipanah
1,
Reza Golbedaghi
4,*,
Alireza Meidanchi
5 and
Rui Fausto
6,*
1
Physics Department, Bu-Ali Sina University, Hamedan 65174, Iran
2
Physics Department, Lorestan University, Khorramabad 68151, Iran
3
Department of Physical Chemistry, Faculty of Chemistry, Bu-Ali Sina University, Hamedan 65174, Iran
4
Department of Chemistry, Payame Noor University (PNU), Tehran 19395-4697, Iran
5
Department of Physics, Payame Noor University (PNU), Tehran 19395-4697, Iran
6
CQC-IMS, Department of Chemistry, University of Coimbra, 3004-525 Coimbra, Portugal
*
Authors to whom correspondence should be addressed.
Molecules 2022, 27(14), 4448; https://doi.org/10.3390/molecules27144448
Submission received: 23 June 2022 / Revised: 8 July 2022 / Accepted: 9 July 2022 / Published: 12 July 2022
(This article belongs to the Special Issue Exclusive Papers from Editorial Board Members of the Photochemistry Section of Molecules)
Browse Figures
Versions Notes

Abstract

:
Polycarbonate (PC)-ZnO films with different percentages of ZnO were prepared by a solution stirring technique and subjected to ultraviolet (UV; λ = 254 nm) irradiation. Structural parameters of the samples and the effects of UV irradiation on the surface properties of the PC and PC-ZnO nanocomposites were evaluated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), water contact angle (WCA) measurements, and a Vickers microhardness (HV) tester. The XRD patterns of the nanocomposite films were found to show an increase in crystallinity with the increasing ZnO nanoparticles percentage. The WCA was found to be reduced from 90° to 17° after 15 h of UV irradiation, which could be ascribed to the oxidation of the surface of the samples during the irradiation and exposure of the ZnO nanoparticles, a result that is also supported by the obtained XPS data. The microhardness value of the PC-ZnO films including 30 wt.% ZnO enhanced considerably after UV radiation, which can also be attributed to the exposition of the ZnO nanoparticles after photodegradation of the PC superficial layer of the nanocomposite films.

1. Introduction

Polymer composites are a class of materials with prominent physicochemical properties, where a polymer acts as the matrix and micro-, macro-, or nanomaterials as the filler [1]. Researchers have reported that nanofillers (e.g., carbon nanotubes or nano-semiconductors) can improve some features of polymers, such as their electrical conductivity and mechanical behavior [2,3,4,5,6]. Accordingly, polymer nanocomposites (PNCs) are interesting for the industry due to their enhanced properties, and have been receiving applications in fields such as environmental remediation, energy storage, and biomedicine [7]. PNCs have also been used successfully in solar cells and light-emitting diodes because of their enhanced thermal conductivity properties [8]. There are different approaches for the preparation of PNCs, such as sol–gel, mixing with inorganic filler, solution processing, extrusion, and melt processing [9].
Polycarbonate (PC) is an amorphous thermoplastic polymer with a high hardness and transparency. It is known as an “optical polymer” and has been used in a variety of optical systems due to its chemical stability and good optical properties. In recent years, the optical and mechanical features of PC-based nanocomposites have been evaluated [10,11,12,13], with different materials such as metal oxides and ceramics being used as nanofillers [13,14,15,16,17].
The changes in the surface of polymers after UV radiation have been the subject of intense investigation because UV light can damage the PNCs [18,19], strongly affecting their mechanical properties, especially plasticity. During the UV irradiation of PC, the carbonate groups absorb UV light, inducing chain-scission and free-radical formation. Consequently, small molecules can crosslink with the free-radicals, affecting the structure and properties of the polymer [20]. To prevent the degradation of polymers subjected to UV radiation, the use of UV stabilizers (UV-filters) is one of the most commonly used approaches [21]. Zinc oxide (ZnO) powder is a well-known UV-filter for polymer protection against UV radiation. ZnO nanoparticles (NPs) are a nontoxic and low-cost semiconductor with two different crystalline structures with specific physical and chemical properties: hexagonal wurtzite and cubic zinc blende; the wurtzite form is more stable and, hence, more appropriate for practical uses [22]. Generally, ZnO NPs with a 3.3 eV bandgap can absorb UV light and, thus, are widely used in sunscreen and the cosmetics industries, UV light-emitting devices, and photocatalytic processes [23].
Another important property of polymers is wettability. Controlling the wettability of surfaces is very important for some industries, such as the petroleum and brine industries [24,25]. Wettability measurement via contact angle (CA) evaluation is a common route for the study of the dynamic and static properties of the surfaces of solids [26]. Generally, CA is measured between a solid surface and a liquid (frequently water) droplet, which depends on surface characteristics such as roughness, contamination, deformation, and chemical composition. When the measured CA is higher than 90°, the solid surface is hydrophobic, while a CA smaller than 90° indicates a hydrophilic surface [27,28]. To change the wettability, various techniques have been used for the modification of surfaces such as heat treatment, chemical methods, UV–Vis irradiation, and laser/plasma treatment. According to some reports, the presence of semiconductor materials such as ZnO and TiO2 NPs is effective in wettability improvement [20,29,30].
Considering their useful properties, TiO2 NPs and ZnO NPs have been utilized as nanofillers in PNCs to enhance the mechanical and optical properties [31]. For instance, Eskandari et al. reduced the bandgap of PC by adding TiO2 and ZnO NPs [13]. Moreover, the hardness of the PC was increased by increasing the content of metal oxide NPs. Compared to other inorganic metal oxides, such as TiO2 NPs, ZnO NPs are more interesting due to their higher activity, even in small amounts [32]. There have been many reports on ZnO deposited on PC using different methods, such as the electric field-assisted chemical method [33], blade coating [34], solution mixing [35], electrochemical deposition [36,37], and radiofrequency magnetron sputtering [38]. Furthermore, the doping of the ZnO NPs with metals such as Mg, Al, Cu, and Ag has been used to enhance the physical and chemical properties of ZnO. For example, Charde and coworkers loaded Cu-doped ZnO NPs on PC (PC/ZnCu) and then evaluated the thermal, thermo-mechanical, and tribological features of the PC/ZnCu nanocomposite with interesting results [14]. In another report, Ga-doped ZnO was supported on a PC substrate by magnetron sputtering, and the chemical bonding between the Ga-doped ZnO and the PC was then being investigated by the analysis of the X-ray photoelectron spectra (XPS) of the material [39]. However, the effect of UV irradiation on the ZnO NPs composed with PC through a simple solution stirring method has not been studied previously.
Hence, in the present study, a facile physical mixing method was used for the preparation of PC-ZnO nanocomposite films with different ZnO percentages. The effects of UV light on the surface features of PC and PC-ZnO were investigated through the evaluation of surface changes (composition, roughness, wettability, hardness) and photoluminescence upon UV irradiation.

2. Experimental

2.1. Materials and Methods

PC and ZnO nanopowders (particles size < 100 nm, surface area 10–25 m2/g and molecular weight of 81.39) were purchased from Bayer and Aldrich, respectively. A low-pressure mercury vapor lamp (TUV 30W, Philips, Amsterdam, Holland) with an emission at 254 nm was used as the UV irradiation source at room temperature in air.
X-ray diffraction (XRD; Italstructure, ADP200) with λ = 1.5405 Å was used for the structure determinations. Wetting of the PC and PC-ZnO films was investigated using the CA measurement of the water droplets. The chemical information of the sample’s surface was obtained via XPS (Bestec GmbH, equipped with an Al Kα X-ray source at 1486.6 eV). All measurements were performed in an analyzer chamber with pressure at ~5 × 10−8 mbar, and binding energies were calibrated using the characteristic carbon feature C1s = 284.7 eV. Atomic force microscopy (AFM) analysis (Nanosurf Nia) was used to determine the morphology and roughness of the films. A Buehler (model 60044) microhardness tester with a microscope was used to perform the HV test; the samples were indented with a Vickers diamond pyramid indenter with a square base and a 136° pyramid angle. Photoluminescence (PL) spectra were obtained in a Perkin Elmer Ls 55 luminescence spectrometer at room temperature using a xenon lamp as the excitation source (λ = 259 nm).

2.2. Synthesis of PC-ZnO Nanocomposite Films

The solvent evaporation method was used for the PC-ZnO nanocomposite film preparation. First, 1.0 g of PC was dissolved in 30.0 mL of dichloromethane using a stirrer at room temperature to obtain a uniform solution. Then, various percentages of ZnO NPs (10, 20, and 30 wt.%) were dispersed in 20 mL of dichloromethane under sonication for 30 min and added to the PC suspension and stirred for 5 h. The resulting solution was poured into a Petri dish and the PC-ZnO film was acquired through the solvent evaporation method in an oven kept at 40 °C. The obtained film had a thickness of ~100 μm.

3. Results and Discussion

3.1. XRD Characterization of ZnO NPs, and PC-ZnO Films

The structure of the ZnO NPs, PC, and PC-ZnO films was investigated using XRD analysis. XRD patterns of the PC and ZnO NPs samples are shown in Figure 1a,b, respectively. According to Figure 1a, the XRD pattern of PC is characterized by a broad feature extending over the 2θ range of 12° to 26°. For the ZnO NPs, as shown in Figure 1b, (101) was the strongest diffraction peak, indicating the dominant growth direction of the ZnO NPs. The XRD patterns obtained for the PC-ZnO films (10, 20, and 30 wt.%) are shown in Figure 1c–e.
The crystallite average diameter size (D) of the ZnO NPs in the PC-ZnO samples can be evaluated by means of Scherer’s equation [40]. A crystallite average diameter of 8.02 nm was obtained (see Table 1).
In addition, since the ZnO NPs have a hexagonal unit cell with two lattice parameters (‘a’ and ‘c’), Bragg’s law can be used to estimate the lattice parameters [41]. The calculated lattice parameters for ZnO in the PC-ZnO nanocomposite are given in Table 1, and are in agreement with those of pure ZnO (JCPDS 36-1451), indicating that the presence of PC does not influence the crystal structure of the ZnO.

3.2. X-ray Photoelectron Spectroscopy (XPS) Analysis

XPS has been applied to evaluate the chemical state of elements and functional groups of the PC and PC-ZnO nanocomposites before and after UV treatment. The XPS spectra confirmed the presence of oxygen and carbon in the samples, as revealed by the two peaks at 284.7 eV and 532.1 eV, attributed to the C 1s and O 1s electrons, respectively. The pure PC sample had an initial amount of oxygen that increased after UV irradiation (λ = 254 nm, for 15 h) by ca. 19% due to oxidation of the PC film surface (Table 2 and Figure 2a,b). The XPS analysis was also performed for the PC-ZnO (30 wt.%) nanocomposite film due to its high hydrophobicity compared with the other synthesized films. As shown in Figure 2c,d, the Zn peak did not appear in the XPS spectrum of the PC-ZnO sample, suggesting that a thin layer of PC formed on the ZnO nanoparticles. Similar to the pristine PC film, the percentage of oxygen increased after UV irradiation due to the sample’s oxidation. The O percent increase was, however, larger than that observed for the PC sample, with the observed increase amounting to ca. 28% (see Table 2).
Changes in the functional groups in the samples were determined by analysis at high-resolution of the XPS spectral regions corresponding to the C1s and O1s features (Figure 3 and Figure 4). Figure 3a,c demonstrates that the C1s peak, containing three components at 284.7, 286.5 and 288.8 eV, which are assigned to carbon atoms in C–C/C–H, C–O and C=O fragments, respectively, split into four components at 284.7 eV (C–C/C–H), 286.5 eV (C–O), 287.8 eV (C=O),and 289.2 eV (O–C=O) after UV irradiation of the both PC and PC-ZnO films (Figure 3b,d). On the other hand, as seen in Figure 4, the O 1s peak of both the PC and PC-ZnO samples showed two components before and after UV irradiation at 531.7 (C=O) and 533.2 (C–O), with the component at 533.1 eV increasing in relative intensity after irradiation. The percentages of different types of bonds involving C and O, as evaluated from the relative component-band intensities of peaks of C1s and O1s, are given in Table 3 and Table 4, respectively. As seen in these tables, the UV irradiation increased the percentages of C–O and C=O bonds compared to the C–C/C–H bonds and led to the appearance of new features due to photo-oxidation (as shown in Section 3.4, these changes also cause changes in the wetting capability of the surfaces, increasing their hydrophilic character [17]).

3.3. AFM Measurements

The obtained 2D and 3D AFM images of PC-ZnO with 10, 20 and 30 ZnO wt.% before and after UV irradiation are shown in Figure 5a–d. As depicted in Figure 5a, after UV irradiation (λ = 254 nm, for 15 h) of the pure PC, the surface of the film became more rugged. The observed changes are characterized in more detail in Table 5, as expressed in the values of the estimated average area roughness (Sa) and root mean square roughness (Sq). As seen in the table, for the pristine PC sample, the area roughness increased upon UV irradiation: Sa, from 1.7 to 2.7 nm, and Sq, from 2.9 to 5 nm. The addition of ZnO to PC caused a considerable increase in the surface roughness (see Figure 5b–d and Table 5), which increased even more after UV irradiation for all ZnO wt.%. Therefore, it can be concluded that both the increase in the ZnO percentage and UV-irradiation substantially increased the PC surface roughness.

3.4. Surface Wettability

The surface wettability of the samples was measured using the water droplet method. The water contact angle (WCA) was measured for the PC and PC-ZnO 30 wt.% samples before and after different times (4 h, 8 h, 10 h, 12 h, and 15 h) of exposure to UV irradiation. The WCA of five water drops was measured in different positions of the surfaces and averaged. The results are given in Table 6.
The WCA on the non-irradiated PC-ZnO nanocomposite (90°) was found to be similar to that measured on the pristine non-irradiated PC surface (91%). However, UV irradiation was found to be more efficient in reducing the WCA in the case of the nanocomposite (from 90 to 17°, after 15 h of irradiation) than for the pure PC film (91 to 27°), which was due to the presence of ZnO NPs on the film surface after photodegradation of the thin layer of PC by the UV radiation. As concluded from the XPS results analysis made in Section 3.2, following the film photodegradation process, functional groups such as carboxylate and carboxylic acid moieties appeared on the sample surface, leading to an increase in the polarity of the surface, and, consequently, an increase in its hydrophilicity.
When ZnO NPs are placed on the PC-ZnO films, the wetting changes can be described by the following mechanisms [42]:
Electron-(e−)/hole-(h+) pairs are formed on the ZnO surface when the energy of the UV light is higher than or equal to the ZnO bandgap:
ZnO + 2hυ → 2h+ + 2e−
The surface oxygen vacancies are then produced through the reaction between some of the holes and lattice oxygen (O2−):
O2− + h+ → O1−
O1− + h+ → ½ O2 + VO (oxygen vacancy)
Water and oxygen compete to adsorb on these defect sites. In particular, water molecules can be coordinated into the VO sites, causing the dissociative adsorption of the water molecules on the surface. These defective sites are more suitable for hydroxyl group (OH−) adsorption compared with oxygen adsorption [42,43]. Accordingly, the wetting of the irradiated surface including ZnO NPs is changed from a hydrophobic to a hydrophilic state due to the adsorption of OH− groups. Therefore, the WCA of the PC-ZnO is drastically reduced after UV treatment.

3.5. Microhardness

The Vickers hardness number (Hv) for the studied samples was determined at the load of 50 g for a constant loading time of 30 s (Table 7). An increase in the microhardness value was observed with increasing ZnO NP content in the composite. Irradiation of the pristine PC material did not significantly change the microhardness of the sample. On the other hand, for the nanocomposite materials, due to the ZnO NPs appearance at the surface due to the UV-induced photodegradation (as above-mentioned), the microhardness of the PC-ZnO samples was enhanced considerably after 15 h of UV irradiation, with the larger increase observed for the sample with the highest content of ZnO NPs (see Table 7).

3.6. Photoluminescence Studies

Figure 6 displays the transient PL spectra of the PC-ZnO films at room temperature. The main features were observed at 426, 440 and in the 476 nm region, and were seen for all the studied samples. The band at 426 nm was a typical near band edge UV emission of ZnO, indicating direct recombination of excitons through an exciton–exciton collision process [44]. The peak observed at 440 nm after the addition of ZnO corresponded to the blue-violet emission of ZnO NPs, most probably originating from zinc interstitial and zinc vacancy point defects [45,46]. The bands around 476 nm (blue) resulted from transitions involving interstitial oxygen. In addition, a green emission at 500 nm was observed, which was attributed to the transmission of an electron near the conductive band to a deeply trapped hole in the oxygen vacancy without electrons. Moreover, it was ascribed to doubly charged oxygen vacancy centers at the surface [47,48,49]. According to the obtained data, the PL intensities of the PC-ZnO (3 wt.%) were enhanced compared to PC, and then gradually decreased by increasing the ZnO NP content (10, 20 and 30 wt.%). The interactions of PC with the ZnO NPs caused the latter create an alternative pathway for the relaxation of the excited electrons, resulting in a smaller probability of radiative emission [50].

4. Conclusions

In summary, a simple solution mixing method was employed for the preparation of PC and PC-ZnO films, which were subsequently subjected to UV irradiation (λ = 254 nm). The films were characterized using XRD, XPS, AFM, and a Vickers microhardness tester.
The XRD patterns of ZnO NPs are consistent with the hexagonal phase of ZnO and show that the nanocomposite films had an increased degree of crystallinity with the ZnO nanoparticle percentage.
According to the XPS spectra, the oxygen content at the surface of the PC-ZnO films increased upon UV irradiation, which created a hydrophilic surface.
AFM analysis showed that the roughness of the PC-ZnO nanocomposites increased due to the exposure of ZnO NPs after UV irradiation.
Wetting changes of the PC and PC-ZnO nanocomposites after irradiation were also investigated by measurement of the WCA. The WCA on the non-irradiated PC-ZnO nanocomposite was found to be similar to that measured on the pristine non-irradiated PC surface. However, UV irradiation was found to be more efficient in reducing the WCA in the case of the nanocomposite (from 90 to 17°, after 15 h of irradiation) than for the pure PC film (91 to 27°). The observed super-hydrophilicity of the PC-ZnO nanocomposites after 15 h of UV irradiation was attributed to the presence of ZnO NPs on the film surface after photodegradation of the thin layer of PC by UV radiation.

Author Contributions

Conceptualization, B.J.; methodology, B.J., S.H. and R.S.; formal analysis, S.H., A.M. and R.F.; writing—original draft preparation, B.J., S.H. and M.E.; writing—review and editing, B.J., S.A., R.G. and R.F.; All authors have read and agreed to the published version of the manuscript.

Funding

R.F. acknowledges financial support from the Portuguese Science Foundation (“Fundação para a Ciência e a Tecnologia”—FCT) Projects CQC UIDB/00313/2020 and UIDP/00313/2020, also co-funded by FEDER/COMPETE 2020-EU. The financial support of the Bu-Ali Sina University for this research is appreciated.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Harito, C.; Bavykin, D.V.; Yuliarto, B.; Dipojono, H.K.; Walsh, F.C. Polymer nanocomposites having a high filler content: Synthesis, structures, properties, and applications. Nanoscale 2019, 11, 4653–4682. [Google Scholar] [CrossRef] [PubMed]
  2. Radzuan, N.A.M.; Sulong, A.B.; Sahari, J. A review of electrical conductivity models for conductive polymer composite. Int. J. Hydrogen Energy 2017, 42, 9262–9273. [Google Scholar] [CrossRef]
  3. Radzuan, N.A.M.; Zakaria, M.Y.; Sulong, A.B.; Sahari, J. The effect of milled carbon fibre filler on electrical conductivity in highly conductive polymer composites. Compos. B Eng. 2017, 110, 153–160. [Google Scholar] [CrossRef]
  4. Arash, B.; Wang, Q.; Varadan, V.K. Mechanical properties of carbon nanotube/polymer composites. Sci. Rep. 2014, 4, 6479. [Google Scholar] [CrossRef]
  5. Arjomandi, J.; Keramat Irad Mossa, N.; Jaleh, B. Electrochemical synthesis and In situ spectroelectrochemistry of conducting NMPy-TiO2 and ZnO polymer nanocomposites for Li secondary battery applications. J. Appl. Polym. Sci. 2015, 132, 41526. [Google Scholar] [CrossRef]
  6. Jaleh, B.; Shahbazi, N.; Jabbari, A. Optical and Thermal Properties of Polycarbonate-TiO2 Nanocomposite Film. Synth. React. Inorg. Met.-Org. Nano-Met. Chem. 2016, 46, 602–607. [Google Scholar] [CrossRef]
  7. Abdulkadir, A.; Sarker, T.; He, Q.; Guo, Z.; Wei, S. Mössbauer spectroscopy of polymer nanocomposites. In Spectroscopy of Polymer Nanocomposites; Elsevier: Amsterdam, The Netherlands, 2016; pp. 393–409. [Google Scholar]
  8. Zhai, S.; Zhang, P.; Xian, Y.; Zeng, J.; Shi, B. Effective thermal conductivity of polymer composites: Theoretical models and simulation models. Int. J. Heat Mass Transf. 2018, 117, 358–374. [Google Scholar] [CrossRef]
  9. Dhillon, A.; Kumar, D. Recent advances and perspectives in polymer-based nanomaterials for Cr (VI) removal. In New Polymer Nanocomposites for Environmental Remediation; Elsevier: Amsterdam, The Netherlands, 2018; pp. 29–46. [Google Scholar]
  10. Abbasi, S.; Carreau, P.J.; Derdouri, A. Flow induced orientation of multiwalled carbon nanotubes in polycarbonate nanocomposites: Rheology, conductivity and mechanical properties. Polymer 2010, 51, 922–935. [Google Scholar] [CrossRef] [Green Version]
  11. Cho, B.-G.; Hwang, S.-H.; Park, M.; Park, J.K.; Park, Y.-B.; Chae, H.G. The effects of plasma surface treatment on the mechanical properties of polycarbonate/carbon nanotube/carbon fiber composites. Compos. B Eng. 2019, 160, 436–445. [Google Scholar] [CrossRef]
  12. Aden, M.; Roesner, A.; Olowinsky, A. Optical characterization of polycarbonate: Influence of additives on optical properties. J. Polym. Sci. Part B Polym. Phys. 2010, 48, 451–455. [Google Scholar] [CrossRef]
  13. Eskandari, M.; Liavali, M.N.; Malekfar, R.; Taboada, P. Investigation of Optical Properties of Polycarbonate/TiO2/ZnO Nanocomposite: Experimental and DFT Calculations. J. Inorg. Organomet. Polym. Mater. 2020, 30, 5283–5292. [Google Scholar] [CrossRef]
  14. Charde, S.J.; Sonawane, S.S.; Rathod, A.P.; Sonawane, S.H.; Shimpi, N.G.; Parate, V.R. Copper-doped zinc oxide nanoparticles: Influence on thermal, thermo mechanical, and tribological properties of polycarbonate. Polym. Compos. 2018, 39, E1398–E1406. [Google Scholar] [CrossRef]
  15. Khutia, M.; Joshi, G.M.; Deshmukh, K.; Pandey, M. Optimization of dielectric constant of polycarbonate/polystyrene modified blend by ceramic metal oxide. Polym. Plast. Technol. Eng. 2015, 54, 383–389. [Google Scholar] [CrossRef]
  16. Delavar, M.; Bakeri, G.; Hosseini, M. Fabrication of polycarbonate mixed matrix membranes containing hydrous manganese oxide and alumina nanoparticles for heavy metal decontamination: Characterization and comparative study. Chem. Eng. Res. Des. 2017, 120, 240–253. [Google Scholar] [CrossRef]
  17. Jaleh, B.; Mohammadtaheri, S.; Shahbazi, N.; Azizian, S. Influence of O2 Plasma on Surface Properties of PC-TiO2 Nanocomposite Film. Int. J. Polym. Anal. Charact. 2015, 20, 733–742. [Google Scholar] [CrossRef]
  18. Qu, C.; Hu, J.; Liu, X.; Li, Z.; Ding, Y. Morphology and mechanical properties of polyimide films: The effects of UV irradiation on microscale surface. Materials 2017, 10, 1329. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  19. Jaleh, B.; Nasri, A.; Shahbazi, N.; Nikfarjad, H. Surface properties of UV irradiated CR-39 polymer before and after chemical etching and registration of fingerprints on CR-39. Radiat. Meas. 2017, 101, 22–28. [Google Scholar] [CrossRef]
  20. Jaleh, B.; Shahbazi, N. Surface properties of UV irradiated PC-TiO2 nanocomposite film. Appl. Surf. Sci. 2014, 313, 251–258. [Google Scholar] [CrossRef]
  21. Senatova, S.L.; Senatov, F.S.; Kuznetsov, D.V.; Stepashkin, A.A.; Issi, J.P. Effect of UV-radiation on structure and properties of PP nanocomposites. J. Alloys Compd. 2017, 707, 304–309. [Google Scholar] [CrossRef]
  22. Król, A.; Pomastowski, P.; Rafińska, K.; Railean-Plugaru, V.; Buszewski, B. Zinc oxide nanoparticles: Synthesis, antiseptic activity and toxicity mechanism. Adv. Colloid Interface Sci. 2017, 249, 37–52. [Google Scholar] [CrossRef]
  23. Mirzaei, H.; Darroudi, M. Zinc oxide nanoparticles: Biological synthesis and biomedical applications. Ceram. Int. 2017, 43, 907–914. [Google Scholar] [CrossRef]
  24. Pu, W.-F.; Yuan, C.-D.; Wang, X.-C.; Sun, L.; Zhao, R.-K.; Song, W.-J.; Li, X.-F. The wettability alteration and the effect of initial rock wettability on oil recovery in surfactant-based enhanced oil recovery processes. J. Dispers. Sci. Technol. 2016, 37, 602–611. [Google Scholar] [CrossRef]
  25. Tian, H.; Wang, M. Molecular dynamics for ion-tuned wettability in oil/brine/rock systems. AIP Adv. 2017, 7, 125017. [Google Scholar] [CrossRef]
  26. Marmur, A.; Della Volpe, C.; Siboni, S.; Amirfazli, A.; Drelich, J.W. Contact angles and wettability: Towards common and accurate terminology. Surf. Innov. 2017, 5, 3–8. [Google Scholar] [CrossRef] [Green Version]
  27. Farazin, J.; Pirgholi-Givi, G.; Azizian-Kalandaragh, Y. Wettability measurement, optical characteristics, and investigation of the quantum confinement effect of ZnS-scotch tape nanocomposite films prepared by successive ionic layer adsorption and reaction (SILAR) method. Phys. B Condens. Matter 2019, 564, 94–103. [Google Scholar] [CrossRef]
  28. Naghdi, S.; Jaleh, B.; Ehsani, A. Electrophoretic deposition of graphene oxide on aluminum: Characterization, low thermal annealing, surface and anticorrosive properties. Bull. Chem. Soc. Jpn. 2015, 88, 722–728. [Google Scholar] [CrossRef]
  29. Majidi, S.; Jaleh, B.; Mohazzab, B.F.; Eslamipanah, M.; Moradi, A. Wettability of Graphene Oxide/Zinc Oxide Nanocomposite on Aluminum Surface Switching by UV Irradiation and Low Temperature Annealing. J. Inorg. Organomet. Polym. Mater. 2020, 30, 3073–3083. [Google Scholar] [CrossRef]
  30. Jaleh, B.; Etivand, E.S.; Mohazzab, B.F.; Nasrollahzadeh, M.; Varma, R.S. Improving wettability: Deposition of TiO2 nanoparticles on the O2 plasma activated polypropylene membrane. Int. J. Mol. Sci. 2019, 20, 3309. [Google Scholar] [CrossRef] [Green Version]
  31. Mohammed, M.; Rozyanty, R.; Mohammed, A.M.; Osman, A.F.; Adam, T.; Dahham, O.S.; Hashim, U.; Noriman, N.Z.; Betar, B.O. Fabrication and characterization of zinc oxide nanoparticle-treated kenaf polymer composites for weather resistance based on a solar UV radiation. BioResources 2018, 13, 6480–6496. [Google Scholar] [CrossRef]
  32. Dimapilis, E.A.S.; Hsu, C.-S.; Mendoza, R.M.O.; Lu, M.-C. Zinc oxide nanoparticles for water disinfection. Sustain. Environ. Res. 2018, 28, 47–56. [Google Scholar] [CrossRef]
  33. Dalvand, R.; Mahmud, S.; Rouhi, J.; Ooi, C.H.R. Well-aligned ZnO nanoneedle arrays grown on polycarbonate substrates via electric field-assisted chemical method. Mater. Lett. 2015, 146, 65–68. [Google Scholar] [CrossRef]
  34. Dhapte, V.; Gaikwad, N.; More, P.V.; Banerjee, S.; Dhapte, V.V.; Kadam, S.; Khanna, P.K. Transparent ZnO/polycarbonate nanocomposite for food packaging application. Nanocomposites 2015, 1, 106–112. [Google Scholar] [CrossRef]
  35. Gaur, M.S.; Rathore, B.S. Structural and thermal properties of swift heavy ion beam irradiated polycarbonate/zinc oxide nanocomposites. J. Therm. Anal. Calorim. 2015, 119, 1105–1112. [Google Scholar] [CrossRef]
  36. Leprince-Wang, Y.; Wang, G.Y.; Zhang, X.Z.; Yu, D.P. Study on the microstructure and growth mechanism of electrochemical deposited ZnO nanowires. J. Cryst. Growth 2006, 287, 89–93. [Google Scholar] [CrossRef]
  37. Leprince-Wang, Y.; Yacoubi-Ouslim, A.; Wang, G.Y. Structure study of electrodeposited ZnO nanowires. Microelectron. J. 2005, 36, 625–628. [Google Scholar] [CrossRef]
  38. Moustaghfir, A.; Rivaton, A.; Tomasella, E.; Mailhot, B.; Cellier, J.; Jacquet, M.; Gardette, J.L. Photostabilization of polycarbonate by ZnO coatings. J. Appl. Polym. Sci. 2005, 95, 380–385. [Google Scholar] [CrossRef]
  39. Gong, L.; Liu, Y.; Jiang, L.; Liu, F. Study on the adhesive mechanism between the Ga doped ZnO thin film and the polycarbonate substrate. Mater. Sci. Semicond. Process. 2017, 66, 105–108. [Google Scholar] [CrossRef]
  40. Venkateswarlu, K.; Bose, A.C.; Rameshbabu, N. X-ray peak broadening studies of nanocrystalline hydroxyapatite by Williamson-Hall analysis. Phys. B Condens. Matter 2010, 405, 4256–4261. [Google Scholar] [CrossRef]
  41. Nasrollahzadeh, M.; Jaleh, B.; Jabbari, A. Synthesis, characterization and catalytic activity of graphene oxide/ZnO nanocompsite. RSC Adv. 2014, 4, 36713–36720. [Google Scholar] [CrossRef]
  42. Khranovskyy, V.; Ekblad, T.; Yakimova, R.; Hultman, L. Surface morphology effects on the light-controlled wettability of ZnO nanostructures. Appl. Surf. Sci. 2012, 258, 8146–8152. [Google Scholar] [CrossRef] [Green Version]
  43. Zhang, Z.; Chen, H.; Zhong, J.; Saraf, G.; Lu, Y. Fast and reversible wettability transitions on ZnO nanostructures. J. Electron. Mater. 2007, 36, 895–899. [Google Scholar] [CrossRef]
  44. Chand, P.; Gaur, A.; Kumar, A. Structural and optical properties of ZnO nanoparticles synthesized at different pH values. J. Alloys Compd. 2012, 539, 174–178. [Google Scholar] [CrossRef]
  45. Liang, Z.; Yu, X.; Lei, B.; Liu, P.; Mai, W. Novel blue-violet photoluminescence from sputtered ZnO thin films. J. Alloys Compd. 2011, 509, 5437–5440. [Google Scholar] [CrossRef]
  46. Srivastava, A.K.; Deepa, M.; Bahadur, N.; Goyat, M.S. Influence of Fe doping on nanostructures and photoluminescence of sol-gel derived ZnO. Mater. Chem. Phys. 2009, 114, 194–198. [Google Scholar] [CrossRef]
  47. Zhou, J.; Wang, Y.; Zhao, F.; Wang, Y.; Zhang, Y.; Yang, L. Photoluminescence of ZnO nanoparticles prepared by a novel gel-template combustion process. J. Lumin. 2006, 119, 248–252. [Google Scholar] [CrossRef]
  48. Wang, Z.; Lin, C.; Liu, X.; Li, G.; Luo, Y.; Quan, Z.; Xiang, H.; Lin, J. Tunable photoluminescent and cathodoluminescent properties of ZnO and ZnO: Zn phosphors. J. Phys. Chem. B 2006, 110, 9469–9476. [Google Scholar] [CrossRef]
  49. Man, M.T.; Kim, J.-H.; Jeong, M.S.; Do, A.-T.T.; Lee, H.S. Oriented ZnO nanostructures and their application in photocatalysis. J. Lumin. 2017, 185, 17–22. [Google Scholar] [CrossRef]
  50. Musa, I.; Massuyeau, F.; Faulques, E.; Nguyen, T.-P. Investigations of optical properties of MEH-PPV/ZnO nanocomposites by photoluminescence spectroscopy. Synth. Met. 2012, 162, 1756–1761. [Google Scholar] [CrossRef]
Molecules 27 04448 g001 550
Figure 1. The XRD patterns of the (a) PC, (b) ZnO NPs, (c) PC-ZnO (10 wt.%), (d) PC-ZnO (20 wt.%), and (e) PC-ZnO (30 wt.%).
Figure 1. The XRD patterns of the (a) PC, (b) ZnO NPs, (c) PC-ZnO (10 wt.%), (d) PC-ZnO (20 wt.%), and (e) PC-ZnO (30 wt.%).
Molecules 27 04448 g001
Molecules 27 04448 g002 550
Figure 2. The XPS survey spectra of the (a) PC, (b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV).
Figure 2. The XPS survey spectra of the (a) PC, (b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV).
Molecules 27 04448 g002
Molecules 27 04448 g003 550
Figure 3. High resolution XPS spectra of the (a) PC, (b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV) in the C1s region.
Figure 3. High resolution XPS spectra of the (a) PC, (b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV) in the C1s region.
Molecules 27 04448 g003
Molecules 27 04448 g004 550
Figure 4. High resolution XPS spectra of the (a) PC, ((b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV) in the O1s region.
Figure 4. High resolution XPS spectra of the (a) PC, ((b) UV irradiated PC (PC + UV), (c) PC-ZnO (30 wt.%), and (d) UV irradiated PC-ZnO (30 wt.%) (PC-ZnO (30 wt.%) + UV) in the O1s region.
Molecules 27 04448 g004
Molecules 27 04448 g005 550
Figure 5. The 2D and 3D AFM images of PC-ZnO with (a) 0, (b) 10, (c) 20, and (d) 30 ZnO wt.% before and after UV irradiation.
Figure 5. The 2D and 3D AFM images of PC-ZnO with (a) 0, (b) 10, (c) 20, and (d) 30 ZnO wt.% before and after UV irradiation.
Molecules 27 04448 g005
Molecules 27 04448 g006 550
Figure 6. The transient PL spectra of the PC-ZnO nanocomposite films.
Figure 6. The transient PL spectra of the PC-ZnO nanocomposite films.
Molecules 27 04448 g006
Table
Table 1. The calculated crystallite size and lattice parameters of the PC-ZnO nanocomposite.
Table 1. The calculated crystallite size and lattice parameters of the PC-ZnO nanocomposite.
Sample2θhkldhkl (Å)D (nm)Lattice Parameters
c (Å)a (Å)c/a
Pure ZnO31.77
34.42		100
002		2.814
2.603		365.2073.2501.602
PC-ZnO (10 wt.%)31.701002.812295.1893.2551.594
34.530022.594
PC-ZnO (20 wt.%)31.90
34.50		100
002		2.29
2.60		295.2023.2481.601
PC-ZnO (30 wt.%)32.041002.79375.1643.2221.602
34.700022.58
Table
Table 2. The C and O percentages (and O/C ratio) in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the XPS spectra.
Table 2. The C and O percentages (and O/C ratio) in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the XPS spectra.
SampleCOO/C
PC69.50%30.50%0.48
PC + UV50.69%49.31%0.97
PC-ZnO (30 wt.%)71.70%28.30%0.40
PC-ZnO (30 wt.%) + UV42.67%57.33%1.34
Table
Table 3. The percentages of C bonds in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the high resolution XPS analysis of the C1s peak.
Table 3. The percentages of C bonds in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the high resolution XPS analysis of the C1s peak.
SampleC–C/C–HC–OC=OO–C=O
PC90.00%7.80%2.20%-
PC + UV72.65%9.64%11.40%6.31%
PC-ZnO (30 wt.%)87.40%3.80%8.80%-
PC-ZnO (30 wt.%) + UV61.97%10.80%15.15%12.08%
Table
Table 4. The percentages of O bonds in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the high resolution XPS analysis of the C1s peak.
Table 4. The percentages of O bonds in the PC and PC-ZnO (30 wt.%) samples before and after UV irradiation, as determined from the high resolution XPS analysis of the C1s peak.
SampleC=OC–O
PC63.26%36.74%
PC + UV58.00%42.00%
PC-ZnO (30 wt.%)63.84%36.16%
PC-ZnO (30 wt.%) + UV50.60%49.39%
Table
Table 5. The area roughness parameters (average area roughness, Sa, and root mean square roughness, Sq) of the AFM images of PC-ZnO with different ZnO wt.%.
Table 5. The area roughness parameters (average area roughness, Sa, and root mean square roughness, Sq) of the AFM images of PC-ZnO with different ZnO wt.%.
PC-ZnO (wt.%)Before UV IrradiationAfter UV Irradiation
Sa (nm)Sq (nm)Sa (nm)Sq (nm)
01.72.92.75.0
1029.543.144.564.4
2054.680.368.192.0
3071.193.379.5100.1
Table
Table 6. The measured water contact angle (WCA) for the pristine and ZnO NPs containing (ZnO wt.30%) PC samples before and along UV irradiation.
Table 6. The measured water contact angle (WCA) for the pristine and ZnO NPs containing (ZnO wt.30%) PC samples before and along UV irradiation.
SampleWCA (°)
PC, PC-ZnO91, 90
PC, PC-ZnO 4 h irradiation58, 44
PC, PC-ZnO 8 h irradiation41, 28
PC, PC-ZnO 10 h irradiation32, 25
PC, PC-ZnO 12 h irradiation31, 20
PC, PC-ZnO 15 h irradiation27, 17
Table
Table 7. The obtained microhardness values (Vickers’ parameter Hv) for the studied samples.
Table 7. The obtained microhardness values (Vickers’ parameter Hv) for the studied samples.
SampleMicrohardness (HV)
PC11.5
PC-ZnO (20 wt.%)12.7
PC-ZnO (30 wt.%)14.33
PC + UV11.4
PC-ZnO (20 wt.%) + UV13.7
PC-ZnO (30 wt.%) + UV20.13
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Jaleh, B.; Hamzehi, S.; Sepahvand, R.; Azizian, S.; Eslamipanah, M.; Golbedaghi, R.; Meidanchi, A.; Fausto, R. Preparation of Polycarbonate-ZnO Nanocomposite Films: Surface Investigation after UV Irradiation. Molecules 2022, 27, 4448. https://doi.org/10.3390/molecules27144448

AMA Style

Jaleh B, Hamzehi S, Sepahvand R, Azizian S, Eslamipanah M, Golbedaghi R, Meidanchi A, Fausto R. Preparation of Polycarbonate-ZnO Nanocomposite Films: Surface Investigation after UV Irradiation. Molecules. 2022; 27(14):4448. https://doi.org/10.3390/molecules27144448

Chicago/Turabian Style

Jaleh, Babak, Sara Hamzehi, Reza Sepahvand, Saeid Azizian, Mahtab Eslamipanah, Reza Golbedaghi, Alireza Meidanchi, and Rui Fausto. 2022. "Preparation of Polycarbonate-ZnO Nanocomposite Films: Surface Investigation after UV Irradiation" Molecules 27, no. 14: 4448. https://doi.org/10.3390/molecules27144448