Next Article in Journal
Bioactive Inks Development for Osteochondral Tissue Engineering: A Mini-Review
Next Article in Special Issue
TiO2 Nanoparticle-Loaded Poly(NIPA-co-NMA) Fiber Web for the Adsorption and Photocatalytic Degradation of 4-Isopropylphenol
Previous Article in Journal
Alginate NiFe2O4 Nanoparticles Cryogel for Electrochemical Glucose Biosensor Development
Previous Article in Special Issue
Synthesis of Oxidant Functionalised Cationic Polymer Hydrogel for Enhanced Removal of Arsenic (III)
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Gels
Volume 7
Issue 4
10.3390/gels7040273
gels-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Novel Thermosensitive-co-Zwitterionic Sulfobetaine Gels for Metal Ion Removal: Synthesis and Characterization

by
Eva Oktavia Ningrum
1,2,
Takehiko Gotoh
2,*,
Wirawan Ciptonugroho
3,
Achmad Dwitama Karisma
1,
Elly Agustiani
1,
Zela Marni Safitri
1 and
Muhammad Asyam Dzaky
1
1
Department of Industrial Chemical Engineering, Faculty of Vocational Studies, Institut Teknologi Sepuluh Nopember, Kampus ITS Sukolilo, Surabaya 60111, Indonesia
2
Department of Chemical Engineering, Graduate School of Advanced Science and Engineering, Hiroshima University, Kagamiyama 1-4-1, Higashi-Hiroshima 739-8527, Japan
3
Chemical Engineering Department, Faculty of Engineering, Sebelas Maret University, Jalan Ir. Sutami 36A, Surakarta 57126, Indonesia
*
Author to whom correspondence should be addressed.
Gels 2021, 7(4), 273; https://doi.org/10.3390/gels7040273
Submission received: 21 November 2021 / Revised: 6 December 2021 / Accepted: 14 December 2021 / Published: 17 December 2021
(This article belongs to the Special Issue Removing Hazardous Materials from Water Using Polymer Hydrogel)
Browse Figures
Versions Notes

Abstract

:
Zwitterionic betaine polymers are promising adsorbents for the removal of heavy metal ions from industrial effluents. Although the presence of both negative and positively charged groups imparts them the ability to simultaneously remove cations and anions, intra- and/or inter-chain interactions can significantly reduce their adsorption efficiencies. Therefore, in this study, novel gels based on crosslinked co-polymers of thermosensitive N-isopropylacrylamide (NIPAAM) and zwitterionic sulfobetaine N,N-dimethylacrylamido propyl ammonium propane sulfonate (DMAAPS) were synthesized, characterized, and evaluated for ion removal. Fourier-transform infrared (FTIR) and proton nuclear magnetic resonance (1H NMR) analyses confirmed the success of the co-polymerization of NIPAAM and DMAAPS to form poly(NIPAAM-co-DMAAPS). The phase transition temperature of the co-polymer increased with increasing DMAAPS content in the co-polymer, indicating temperature-dependent amphiphilic behavior, as evidenced by contact angle measurements. The ion adsorption analyses of the poly(NIPAAM-co-DMAAPS) gels indicated that co-polymerization increased the molecular distance and weakened the interaction between the DMAAPS-charged groups (SO3− and N+), thereby increasing the ion adsorption. The results confirmed that, with a low concentration of DMAAPS in the co-polymer gels (~10%), the maximum amount of Cr3+ ions adsorbed onto the gel was ~58.49% of the sulfonate content in the gel.

1. Introduction

Water quality degradation is a critical concern worldwide. This severity is reflected in the United Nations Sustainable Development Goals (SDGs), where water quality-related concerns are assigned with SDG numbers of 6 and 14 [1]. Hypothetically, the manufacturing industries are a dominant contributor to the degradation of water quality [2], as many of them release pollutants, including heavy metals such as Pb, Cr, Cu, Cd, Ni, and Zn, to the nearby water bodies [3]. These metals may cause critical health problems when they accumulate in the human body. The Cr3+ ion, in particular, has a considerable negative impact on the environment due to its binding affinity toward proteins and nucleic acids [4,5].
According to the World Health Organization, heavy metals may cause several types of diseases, ranging from allergic reactions to cancer [6]. Therefore, certain threshold limits have been set to regulate the disposal of these metals. For example, the Cr(VI) concentration in the inland surface water and potable water should not exceed 0.1 mg/L and 0.05 mg/L, respectively [6,7].
Over the years, several methods have been developed to reduce the concentration of heavy metals in water, including chemical precipitation, electrochemical reduction, activated carbon adsorption, ion exchange, and reverse osmosis [7]. These methods have been proven effective in reducing Cr concentration in drinking water. However, they still exhibit some drawbacks, such as high energy requirements, incomplete metal removal, and high sludge production [7]. Adsorption is another promising and economical method. The efficacy of adsorption in reducing heavy metal concentrations highly depends on the type of adsorbent. To date, several classes of adsorbents based on their origin have been developed. For example, bio-adsorbents are obtained from algae, microbial bio-mass, or non-living bio-mass, such as bark, lignin, and crustacean shells. These types of adsorbents are often preferred from an economic perspective.
Zwitterionic polymers contain equimolar amounts of homogenous anionic and cationic groups on their chains [8]. When these oppositely charged moieties are combined, the polymers exhibit ultra-hydrophilicity while preserving an overall charge neutrality [9]. This hydrophilicity enables zwitterionic polymers to be significantly effective in non-specific protein adsorption, making these materials excellent candidates for long-term anti-fouling applications [10,11]. Zwitterionic polymers have unique structures, enabling them to exhibit various properties, such as overall charge neutrality, hydration capacity, high hydrophilicity, and anti-polyelectrolyte effects in aqueous solutions; they can also behave as solid dipole pairs and have thus attracted increasing interest from many researchers [12,13]. The anti-polyelectrolyte effect enables zwitterionic polymers to frequently undergo chain expansion as their ionic strength increases in water [14]. As one of the most recent technological advances, zwitterionic polymers have emerged as a promising class of adsorbents for heavy metal ion removal. The presence of both positive and negative charges in the polymer structure improves its metal removal efficiency and selectivity [15]. Zwitterionic polymers demonstrate good adsorption capacities for Pb2+ and Cu2+, suggesting a good prospect for commercial use on an industrial scale [16]. They do not dissolve in water if the temperature is below their upper critical solution temperature (UCST) [17]. At temperatures below the UCST, the zwitterionic polymer exists in a collapsed coil condition owing to its intra- and/or inter-chain interactions. However, at temperatures above the UCST, thermal energy can overcome these interactions [18]. The use of zwitterionic polymers as adsorbents is recognized as one of the methods to selectively adsorb ions because both anions and cations in the solution have the ability to bond with oppositely charged groups [19,20]. Moreover, zwitterionic betaine polymers can simultaneously adsorb both anions and cations in liquid waste [21].
Thermoresponsive polymers have also attracted considerable interest owing to their reversible phase-transition behavior at lower critical solution temperatures (LCSTs). To extend the applications of zwitterionic materials, thermoresponsive co-polymers containing zwitterionic monomers have been synthesized [22,23,24]. Poly(N-isopropylacrylamide) (poly[NIPAAM]) is a thermosensitive polymer exhibiting an LCST of 32–34 °C. The UCSTs and LCSTs of polymers containing both thermosensitive NIPAAM and sulfobetaine monomer [24] can be varied by introducing specific ions [25] or zwitterions [26,27,28,29] or by varying the temperature, type of salt, or polymer concentration [30]. NIPAAM hydrogels swell in water at temperatures below the LCST and shrink with increasing temperature. Furthermore, minor temperature changes around the LCST cause rapid swelling–de-swelling transitions [31,32,33]. Due to their unique characteristic, thermosensitive NIPAAM-based polymer adsorbents have been used to adsorb and detect various heavy metal ions, such as Pb [34,35,36], Cu [37,38,39], Ni [40], Co [41,42], and Mn [43] ions. Moreover, poly(NIPAAM)-based microgels containing metal organic frameworks (MOFs) have been employed for the adsorption/desorption of selected analytes from aqueous environments [44].
Zwitterionic polymers and gels have been synthesized and characterized for the adsorption process. For instance, our previous study [45] demonstrated the simultaneous adsorption of cations and anions by a poly zwitterionic sulfobetaine ((N,N-dimethylacrylamido propyl) ammonium propane sulfonate) poly(DMAAPS) gel. However, in a KI solution, the adsorption capacity of the poly(DMAAPS) gel was ~13.7% of the sulfonate content (100 mmol/L) of the gel, which was relatively low. Therefore, this present study aimed to improve the ion adsorption capacity of the gel via co-polymerization between NIPAAM and DMAAPS in a specific molar ratio. The addition of the NIPAAM unit to poly zwitterionic sulfobetaine could reduce the inter- and intra-chain interactions and polymer chain entanglements of the polymer, potentially enhancing its ion adsorption.
In this study, poly(NIPAAM-co-DMAAPS) gels were used to adsorb ions in an aqueous solution. The co-polymerization between the thermosensitive monomer NIPAAM and zwitterionic betaine DMAAPS allowed the adsorption to be controlled by temperature. Notably, a previous study on the co-polymerization of sulfobetaine zwitterionic polymers and thermosensitive gels only emphasized the synthesis and properties of the gel or polymer independently [46]. To address the paucity of information concerning such polymers, this study aimed to elucidate the relationship between the adsorption capacity of the poly(NIPAAM-co-DMAAPS) gels in target solutions of chromium(III) nitrate (Cr(NO3)3) and other gel or polymer properties, such as the swelling ability, phase transition temperature, wettability, and visual analysis. The effects of the NIPAAM:DMAAPS ratio and temperature on the properties of each gel and polymer were investigated. Moreover, the ion adsorptions of the gels were compared with that of the zwitterionic polysulfobetaine homopolymer gel reported in our previous study [21].

2. Results and Discussion

2.1. Fourier-Transform Infrared Spectroscopy (FTIR) Analysis

Figure 1 shows the FTIR spectra of poly(NIPAAM-co-DMAAPS) gels with concentration ratios of 100:0, 95:5, 90:10, 85:15, and 80:20. It was observed that the spectra changed due to the concentration variation. The difference in the functional groups of each constituent monomer and co-polymer was observed based on the presence of CH2=CH vinyl groups in the wavelength range of 900–1000 cm−1, which determines the success of the co-polymerization. In NIPAAM, the vinyl bond (CH2=CH) band was observed at 960 cm−1, whereas in DMAAPS, it was observed at 980 cm−1. However, in the spectrum of poly(NIPAAM-co-DMAAPS), this band was absent, indicating the successful co-polymerization of NIPAAM and DMAAPS. Additionally, with increasing DMAAPS concentration (5, 10, 15, 20, and then 100%), the intensity of the band corresponding to SO3− (1170; 1181) also increased. All the functional group spectra in Figure 1 are in good agreement with our previous report [47] for poly(NIPAAM-co-DMAAPS), which shows that NIPAAM-co-DMAAPS is indeed the prepared co-polymer gel.
The wavenumber of each functional groups of poly(NIPAAM-co-DMAAPS) gels and its constituent monomer is shown in Table 1 which represent the FTIR spectra of Figure 1.

2.2. Proton Nuclear Magnetic Resonance (1H NMR) Analysis

The chemical structures of the monomers and the resulting co-polymers were further confirmed using 1H NMR spectroscopy. The 1H NMR spectra of the NIPAAM and DMAAPS are displayed in Figure 2a,b, respectively. The two monomers were characterized by the presence of two peak signals between 5.5 and 6.5 ppm in the spectra, corresponding to the vinyl bond present in each monomer. Upon polymerization, these signals completely disappeared and peaks at 1.46 and 1.90 ppm (Figure 2c) appeared, indicating the head-to-tail polymerization required to assemble the polymeric structure of poly(NIPAAM-co-DMAAPS).

2.3. Phase Transition Temperature Analysis

The LCST of a co-polymer indicates its phase transition in a solution. The LCST of a co-polymer can be determined by measuring the UV light transmittance of solution of the co-polymer under gradual heating. Figure 3 shows the temperature dependence of the transmittance of solutions of poly(NIPAAM-co-DMAAPS) in Cr(NO3)3 or water with various polymer concentrations (1 and 10 g/L) and monomer ratios. Subsequently, it was observed that increasing the NIPAAM ratio in the co-polymer resulted in the shift of LCST to lower temperatures, regardless of the co-polymer concentration. For H2O charged with 1 g/L co-polymer, the low NIPAAM ratios of 80:20 and 85:15 resulted in a light transmittance of approximately 100% throughout the given temperature range, revealing that the LCST is greater than 70 °C. The LCST was detected by the gradual decrease in transmittance starting at 70 °C as the NIPAAM ratio was increased to 90:10. A gradual decrease in LCST then occurred at 45 °C as the ratio was increased to 95:5. Further increasing the NIPAAM ratio to 100:0 lowered the LCST to 33 °C. Furthermore, when Cr(NO3)3 was added to the solution, 100% transmittance could not be achieved even at a temperature as low as 30 °C. In this case, the initial transmittance through the solution started at 80%, which slightly decreased with temperature. In this ionic solution, the co-polymer with the 80:20 NIPAAM ratio exhibited no significant drop in transmittance throughout the applied temperature range, suggesting that the LCST is greater than 70 °C. As the ratio was increased to 85:15, 90:10, 95:5, and 100:0, the LCST decreased to approximately 68, 54, 45 and 33 °C, respectively. Notably, as the NIPAAM ratio in the co-polymer was very high, the LCSTs were no longer influenced by the presence of Cr3+ ions, as observed at NIPAAM ratios of 95:5 and 100:0. This decrease in LCST is in agreement with a previous report on the aqueous co-polymer of P(NIPAm-coZw10%) solutions [25] and can be explained as a combination of several effects: changes in the water structure in the polymer hydration sheath and changes in the interactions between the polymer and the solvent due to the presence of metal ions/salts [25,48,49].
The changes in the LCST were examined when the solution was enriched with 10 g/L of co-polymer. Irrespective of the temperature, the co-polymer with the low NIPAAM ratio of 80:20 could maintain approximately 100% transmittance through H2O; a similar trend was observed for this polymer at a lower concentration (1 g/L). However, further increasing the NIPAAM content to 85:15, 90:10, 95:5, and then 100:0 significantly decreased the LCST to 65, 51, 41, and 33 °C, respectively. Moreover, the LCST of 10 g/L of poly(NIPAAM-co-DMAAPS) in an aqueous Cr3+ solution was studied. As expected, the ionic solution contributed to the reduced light transmittance of the polymer, even at very low temperatures. Similar to the ionic solution with 1 g/L of poly(NIPAAM-co-DMAAPS), the LCST for the co-polymer with an 80:20 NIPAAM ratio was unrecognizable throughout the applied temperature range. Furthermore, changing the NIPAAM ratio to 85:15, 90:10, 95:15, and then 100:0 gave LCSTs of 64, 50, 41, and 33 °C, respectively. These results reveal that, in solutions with higher co-polymer content, the presence of the Cr3+ ions does not affect the LCST. For pure poly(NIPAAM), Cr3+ ions and the co-polymer concentration did not influence the LCST, which remained at 33 °C.
The decrease in the LCSTs with increasing NIPAAM concentrations in water and Cr(NO3)3 solutions can be explained by the dominant properties of NIPAAM. When the NIPAAM ratio is high, the hydrophobic interactions between the hydrophobic backbone and the isopropyl group become considerably stronger and change the conformation of the co-polymer. The LCSTs of the co-polymer in water were found to be higher than those of the co-polymer in Cr(NO3)3. This was attributed to the ionic interactions of the ions in the Cr(NO3)3 solution (Cr3+ and NO3−) with the charged groups of DMAAPS (SO3− and N+). However, at low ion concentrations, the number of ions available to disrupt the interactions of the SO3− and N+ groups in poly(DMAAPS) was restricted. Therefore, only partial dissociation occurred, inducing chain mobility that consequently enhanced the inter-chain interactions, resulting in the aggregation of the co-polymer, as indicated by the decrease in the LCST.

2.4. Visual Analysis of Color Change

Figure 4 shows the photographs of the 1 g/L aqueous poly(NIPAAM-co-DMAAPS) solutions with various monomer ratios at different temperatures. All the samples exhibited a clear appearance at 31 °C. As the temperature was increased to 32 °C, the poly(NIPAAM-co-DMAAPS) solution with a monomer ratio of 100:0 (tube a) exhibited a color/turbidity change. This is consistent with previous studies [25,50,51], which reported that poly(NIPAAM) homopolymer chains undergo reversible collapse or swelling in aqueous solutions above or below their transition temperatures/LCSTs, which is approximately 32–34 °C for the co-polymer in the present study. Furthermore, the solutions with the NIPAAM:DMAAPS ratios of 95:5 (tube b), 90:10 (tube c), and 85:15 (tube d) exhibited turbidity at 41, 52, and 70 °C, respectively. However, the solution in tube d was only slightly turbid at 70 °C. Moreover, no turbidity was observed at temperatures higher than 70 °C, suggesting the high miscibility of the co-polymer with the lowest NIPAAM:DMAAPS ratio. These observations suggest that the color change with temperature becomes less pronounced as the NIPAAM content decreases. This result correlates strongly with the decrease of LCST from 55 to 33 °C as the NIPAAM content increased from 90:10 to 100:0 (as shown in Figure 3a). The slight turbidity of tube d at 70 °C also corresponds with the minor decay in transmittance at this temperature. Similarly, a transmittance of approximately 100% can be achieved with the 80:20 NIPAAM ratio, which is in an agreement with the clear appearance of tube d. This observation suggests that decreasing the NIPAAM ratio gradually leads to the emergence of the DMAAPS character in the co-polymer, resulting in stronger interactions between the H2O molecules and DMAAPS moieties. Therefore, the co-polymer becomes more hydrophilic even at elevated temperature. These results are consistent with the observations made by Takeoka et al. [52]; in their study, the color of the thermosensitive pre-gel solution was tuned by controlling the amount of monomer.

2.5. Contact Angle Analysis

The static contact angle is the contact angle where the interfacial area between the liquid and solid phase does not change during the measurement. The measurement of static contact angles can be used to characterize the wettability or hydrophilic/hydrophobic properties of the poly(NIPAAM-co-DMAAPS) co-polymers. If the contact angle is less than 90°, the surface is hydrophilic, whereas if the angle is greater than 90°, the surface is hydrophobic. Furthermore, if the contact angle is between 150° and 180°, the surface is considered to be super-hydrophobic [53]. However, in several cases, the hydrophilic co-polymers have a contact angle greater than 90°. This occurs because the applied temperature during the measurement can affect the water droplet. In some cases, the water droplet temperatures are higher than the desired temperature. Figure 5 shows the contact angle created at the interface of poly(NIPAAM-co-DMAAPS) and the water droplet at various temperatures. For the co-polymer with a monomer ratio of 80:20, the contact angle remained <90° even at 70 °C. Moreover, this droplet exhibited turbidity, indicating that this co-polymer was hydrophilic at the tested temperatures. Under such conditions, the co-polymers were miscible, and the surface was hydrophilic. The hydrophobicity can be marked at 70 °C, as the NIPAAM ratio was set to 85:15. Upon increasing the NIPAAM ratio in the co-polymer from 90:10 to 100:0, the contact angle was >90° at 50 and 30 °C, respectively. Notably, the temperatures at which the hydrophobicity was first noticed were always higher than the LCSTs of the corresponding co-polymers. The hydrophobic character also contributed to the immiscibility of the co-polymer in water. Additionally, a red dashed line was created to denote the temperatures at which the hydrophobicity appeared. The co-polymers located on the left side are regarded as hydrophilic, and those on the right side are hydrophilic. Furthermore, the appearances of the droplets were observed at different temperatures. Figure 5 shows that the droplets turn clear when the contact angles are close to 90°. In contrast, cloudy droplets exhibit smaller contact angles. The color of the droplets might be influenced by their interaction with the co-polymer film. When the contact angle is small, the water droplets strongly interact with the co-polymer film beneath them. Furthermore, some fractions of the co-polymer may infiltrate the water droplet, and the concentration of this co-polymer within the droplet could increase over time, even in a small volume of water. At some point, the concentration of co-polymer exceeds a critical concentration for the phase transition, leading to the increased immiscibility. The enhanced immiscibility could suppress the transmittance, resulting in a droplet with a milky appearance.

2.6. Cr3+ Ion Adsorption

The Cr3+ adsorptions of the poly(NIPAAM-co-DMAAPS)s gels are shown in Figure 6a. The adsorption was performed isothermally at 30 °C and 70 °C. A similar trend can be observed for both the temperatures, whereby the amount of adsorbed Cr3+ decreased with the increasing NIPAAM ratio from 80:20 to 90:10. Further enrichment of the NIPAAM ratio to 95:15 did not significantly improve the ion adsorption. This suppressed adsorption capacity is caused by the high NIPAAM content; at higher NIPAAM ratios, the fraction of DMAAPS in the co-polymer is much lower, leading to the depletion of the SO3− and N+ sites that actively adsorb the Cr3+ ions. In addition to the monomer ratio, temperature can also affect the adsorption of Cr3+ ions. For the NIPAAM ratio of 80:20, a decrease in temperature from 70 to 30 °C enhanced the gel adsorption capacity for Cr3+ from 0.065 to 0.072 mmol/g dry-gel, respectively, which is almost twice that of pure DMAAPS for trivalent cations, as reported previously [21]. This improvement was observed for all the monomer ratios, suggesting that adsorption is more favorable at reduced temperature.
This observation is consistent with our previous study [21] in that, at high temperatures, the thermal motion weakens the interaction between the SO3− and N+ groups of DMAAPS, owing to the charge dissociation. Moreover, the study also revealed that the highest adsorption capacity of poly(DMAAPS) was 0.039 mmol/g dry-gel. Accordingly, this result provides evidence that the co-polymerization of NIPAAM with DMAAPS could increase the molecular distance. This is because the NIPAAM units in the co-polymer filled the spaces between the DMAAPS units. Consequently, the interaction between SO3− and N+ in the DMAAPS-charged groups is reduced. It eventually promotes the pairing of ions from the solution with the charged groups of the co-polymer, resulting in enhanced Cr3+ ion adsorption. In addition, these results also suggest that using a small concentration of DMAAPS in the co-polymerization is more favorable. With only 5–10% DMAAPS in the gel, similar ion adsorption to that of the poly(DMAAPS) homopolymer gel could be achieved. At this concentration, the maximum amount of Cr3+ ions adsorbed by a 10 mmol/L Cr(NO3)3 solution of 0.0454 mmol/g of gel was estimated to be ~58.49% of the sulfonate content in the gel.
The swelling degrees of poly(NIPAAM-co-DMAAPS) gels with various monomer ratios are shown in Figure 6b. As can be observed, at 70 °C (red line), the NIPAAM concentration does not affect the swelling degrees of the gels. This behavior could be explained by the relatively much higher concentration of NIPAAM compared to DMAAPS, which caused the gel characteristics to be predominantly influenced by the properties of NIPAAM. Thus, at a higher temperature (70 °C), all gels tended to shrink, and the swelling degree was almost the same. In contrast, at a lower temperature (30 °C), the swelling degree gradually decreased with increasing NIPAAM concentration, and at 95% NIPAAM, the swelling degree was almost similar to that at 70 °C. This low swelling degree is also associated with the low ion adsorption by the gel (Figure 6a), which is due to its low DMAAPS content. Moreover, it was observed that the swelling degree at both temperatures was constant below 85% NIPAAM. This could be attributed to the impaired repulsion of DMAAPS chains by the adsorbed Cr3+ ions or the ionic crosslinking between SO3− and Cr3+ ions.
The maximum amount of Cr3+ adsorbed by the poly(NIPAAM-co-DMAAPS)s gels is relatively high, i.e., 1852 mg/g, in comparison with the adsorption capacity of related adsorbents reported in previous studies, as listed in Table 2.
To clearly understand the relationship between the properties of the co-polymers and gels, the results of various analyses are summarized in Table 3 and Table 4.
It is clear that the operating conditions (i.e., temperature and monomer concentrations utilized in the preparation of the gels and co-polymers) significantly affects their properties. In the case of co-polymers, when the temperature was higher than the LCST, hydrophobicity was observed, as evidenced by their >90° contact angles. The co-polymer solutions were opaque and milky-white in appearance. This hydrophobic nature of the co-polymers also made the gels denser, as indicated by the lower swelling degree and lesser ionic interactions with the ions (Cr3+ and NO3−) in the Cr(NO3)3 solution.
Moreover, when the temperature was lower than the LCST, the co-polymers exhibited hydrophilicity, as indicated by their <90° contact angle and the co-polymer solutions appeared transparent. The hydrophilic nature of co-polymers made the gels less dense, resulting in a higher degree of swelling. Consequently, more ionic interactions occurred between the gels and the ions in the Cr(NO3)3 solution, resulting in increased ion adsorption, particularly for the gels with high DMAAPS concentration. In future studies, the adsorption capacity, kinetics, and isotherm models of poly(NIPAAM-co-DMAAPS) gels can be investigated for various ions and solutions. Furthermore, the exact composition of each prepared gel can be further evaluated with respect to its correlation with the gel adsorption capacity.

3. Conclusions

Poly(NIPAAM-co-DMAAPS) co-polymers and gels were synthesized with various monomer ratios. The structures of the monomers and co-polymers were determined using FTIR and 1H NMR spectroscopies. The results of the phase transition temperature analysis showed that an increase in the DMAAPS concentration increased the LCST of the co-polymer, changing the co-polymer from hydrophobic to hydrophilic. The visual nature of the co-polymers in solution was also significantly affected by the monomer ratio. The co-polymers with high NIPAAM content exhibited a turbidity change in solution at higher temperatures and >90° contact angles. The ion adsorption tests confirmed that the co-polymerization of NIPAAM with DMAAPS increased the molecular distance and weakened the interactions between the DMAAPS-charged groups (SO3− and N+), leading to enhanced ion adsorption. This observation suggests that using a lower concentration of DMAAPS via its co-polymerization with NIPAAM is more efficient than using a poly(DMAAPS) homopolymer gel. Nevertheless, the adsorption temperature must be adjusted to a value lower than the LCST of the co-polymer to achieve a higher ion adsorption capacity. Therefore, the operating temperature and DMAAPS concentration must be considered while designing co-polymers and gels for adsorption applications. In addition, future studies should elucidate the reversibility (adsorption/desorption) and ion selectivity of these co-polymers in a multi-ion solution at various temperatures and with a wider range of monomer concentrations.

4. Materials and Methods

4.1. Materials

NIPAAM and N,N-dimethylaminopropyl acrylamide (DMAPAA) were purchased from KJ Chemicals (Tokyo, Japan) and purified via n-hexane re-crystallization and vacuum distillation, respectively. 1,3-Propanesulfate (PS) and N,N′-methylenebisacrylamide (MBAA) were purchased from Tokyo Chemical Industry (Tokyo, Japan) and used as received without further purification. N,N,N′,N′-tetramethylethylenediamine (TEMED) and ammonium peroxide (APS) were purchased from Sigma–Aldrich (Burlington, MA, USA) and used as received without further purification. Cr(NO3)3 was purchased from Merck Millipore (Jakarta, Indonesia) and used as received without further purification.

4.2. Methods

4.2.1. Monomer Synthesis

DMAAPS was synthesized from the ring-opening reaction of DMAPAA and PS [45]. A solution of PS (75 g) and acetonitrile (75 g) was added dropwise into the solution of DMAPAA (100 g) and acetonitrile (200 g) for 90 min under stirring at 30 °C. The mixture was continuously stirred for 16 h, and the solution was then left to stand for 2 d. The white crystals formed were then filtered, re-washed with acetone (500 mL), and oven-dried at 50 °C for 24 h. The chemical structures of NIPAAM and DMAAPS are shown in Figure 7.

4.2.2. Synthesis of Poly(NIPAAM-co-DMAAPS) Co-Polymers and Gels

Poly(NIPAAM-co-DMAAPS) co-polymers and gels were synthesized via free radical polymerization using a solution consisting of monomers (NIPAAM and DMAAPS), an initiator (APS), an accelerator (TEMED), and water. The NIPAAM:DMAAPS molar ratios were fixed at 100:0, 95:5, 90:10, 85:15, and 80:20. Typically, NIPAAM, DMAAPS, and TEMED (2 mol/L) were dissolved in distilled water to a total volume of 100 mL. This solution was then introduced into a three-neck separable flask and sealed. The solution was purged using ultra-high-purity nitrogen gas for 10 min to remove dissolved oxygen. Then, a similarly purged APS solution (2 mmol/L, 20 mL) was added to the reaction mixture. The polymerization reaction proceeded at 10 °C under continuous nitrogen flow and stirring for 6 h. The polymer was then separated and washed with distilled water through membrane dialysis with a molecular weight cut off of 12,000–14,000 (CelluSep T3, Membrane Filtration Products, Seguin, TX, USA) for one week. Poly(NIPAAM-co-DMAAPS) gels were synthesized using the same method, along with the addition of MBAA (30 mmol/L) as a crosslinker, in the same manner as outlined in previous studies [47,67]. The gel was washed with distilled water for 7 d. The water was changed every 12 h. The gel was dried on a Teflon paper placed in a Petri dish covered with a plastic film with small holes to decrease the gel drying rate. After drying, the gel was crushed into a 90-mesh size and used for the adsorption tests.

4.2.3. Characterization

FTIR spectroscopy (Nicolet IS10, Thermo Fisher Scientific, Waltham, MA. USA) was performed in the wavenumber range of 4000–500 cm−1 to identify the functional groups of NIPAAM, DMAAPS, and poly(NIPAAM-co-DMAAPS) gel. 1H NMR spectroscopy (MR400 DD2, Agilent, Santa Clara, CA, USA) was used to elucidate the chemical structure of poly(NIPAAM-co-DMAAPS) gel. The samples (20 mg) were dissolved in D2O solvent (1 mL).
The transition temperature of the samples was analyzed by observing the transmittance changes using UV–vis spectroscopy (V-630, Jasco Corp, Tokyo, Japan) with temperature control. The transmittance changes as a function of temperature were measured at a wavelength of 600 nm. The LCST can be determined at a temperature where the transmittance value is 50%. The LCST was obtained by heating the sample from 10 °C to 70 °C to observe changes in the sample transparency. Sample solutions (1 g/L) were placed in a cuvette equipped with a heater coil and heated at a rate of 1 °C/min. The transition temperature was also observed visually as the solutions changed from transparent to milky white.
Contact angle analysis was used to determine the hydrophobic/hydrophilic properties of the co-polymer. A sample solution (5 g/L) was dropped on a glass slide, uniformly spread by a spin coater, and then dried under vacuum at 50 °C for 30 min. Contact angle measurements were taken 60 s after water (~0.05 mL) was dropped onto the dried co-polymer surface to allow the droplet to stabilize. The internal contact angle was obtained from the line contact angle of the liquid–gas interface using co-polymer surface as the baseline. The visual analysis aimed to visually observe the phase transition of the co-polymer solution, as shown by the change in solution turbidity. If the solution was transparent, the component was completely miscible. Conversely, if the solution was milky white, the component was deemed immiscible. Images for contact angle and visual analyses were acquired using a Canon EOS 700D camera (50 mm lens, aperture f/8, shutter speed 1/500 s, ISO 200).
Atomic absorption spectroscopy (AAS) (Model 210 VGP, Buck Scientific, USA) was used to measure the ion concentrations before and after the adsorption by the gel in the target solution. The adsorption experiment was carried out by placing the dry-gel (1 g) in a glass bottle containing 20 mL of a 10 mmol/L Cr(NO3)3 solution. The bottle was put in a water bath heated to the desired temperature, and the gel-containing solution was then stirred for 12 h to allow the gel to achieve adsorption equilibrium. To determine the concentration of the cation (Cr3+) in the solution after adsorption, the gels were removed from the solution and filtered following centrifugation at 3000 rpm for 10 min.
In addition, the swelling degrees of the gels were determined using a 10 mmol/L Cr(NO3)3 solution at various temperatures to achieve equilibrium swelling for 24 h using a cathetometer, as reported previously [19]. The swelling degree is defined as the ratio of the swollen gel diameter to the dry-gel diameter.

Author Contributions

Conceptualization, E.O.N. and T.G.; methodology, Z.M.S., M.A.D., E.O.N. and T.G.; validation, A.D.K., E.A., Z.M.S. and M.A.D.; formal analysis, A.D.K. and W.C.; funding acquisition, E.O.N. and T.G.; investigation, A.D.K., W.C. and E.O.N.; data curation, E.A., W.C., E.O.N. and A.D.K.; writing—original draft preparation, E.O.N., Z.M.S. and M.A.D.; writing—review and editing, E.O.N., T.G. and W.C. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Penelitian Dasar Unggulan Perguruan Tinggi 2021, grant number 943/PKS/ITS/2021, from the Ministry of Research, Technology, and Higher Education of Indonesia (Kemenristek/BRIN).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data are contained within the article.

Acknowledgments

The authors thank Toni Suharto for analysis of phase transition temperature.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Desa, U.N. Transforming Our World: The 2030 Agenda for Sustainable Development; United Nations: San Francisco, CA, USA, 2016. [Google Scholar]
  2. Agliardi, E.; Pinar, M.; Stengos, T. Air and Water Pollution over Time and Industries with Stochastic Dominance. Stoch. Environ. Res. Risk Assess. 2017, 31, 1389–1408. [Google Scholar] [CrossRef] [Green Version]
  3. Nagajyoti, P.C.; Lee, K.D.; Sreekanth, T.V.M. Heavy Metals, Occurrence and Toxicity for Plants: A Review. Environ. Chem. Lett. 2010, 8, 199–216. [Google Scholar] [CrossRef]
  4. Taha, A.A.; Qiao, J.; Li, F.; Zhang, B. Preparation and Application of Amino Functionalized Mesoporous Nanofiber Membrane via Electrospinning for Adsorption of Cr3+ from Aqueous Solution. J. Environ. Sci. 2012, 24, 610–616. [Google Scholar] [CrossRef]
  5. Bernardo, G.-R.R.; Rene, R.-M.J. Chromium (III) Uptake by Agro-Waste Biosorbents: Chemical Characterization, Sorption–Desorption Studies, and Mechanism. J. Hazard. Mater. 2009, 170, 845–854. [Google Scholar] [CrossRef]
  6. Tchounwou, P.B.; Yedjou, C.G.; Patlolla, A.K.; Sutton, D.J. Heavy Metal Toxicity and the Environment in Molecular, Clinical and Environmental Toxicology; Luch, A., Ed.; Springer: Berlin/Heidelberg, Germany, 2012; Volume 101, pp. 133–164. [Google Scholar]
  7. Sheng, P.X.; Ting, Y.-P.; Chen, J.P.; Hong, L. Sorption of Lead, Copper, Cadmium, Zinc, and Nickel by Marine Algal Biomass: Characterization of Biosorptive Capacity and Investigation of Mechanisms. J. Colloid Interface Sci. 2004, 275, 131–141. [Google Scholar] [CrossRef]
  8. Lowe, A.B.; McCormick, C.L. Synthesis and Solution Properties of Zwitterionic Polymers. Chem. Rev. 2002, 102, 4177–4190. [Google Scholar] [CrossRef] [PubMed]
  9. Mi, L.; Jiang, S. Integrated Antimicrobial and Nonfouling Zwitterionic Polymers. Angew. Chem.-Int. Ed. 2014, 53, 1746–1754. [Google Scholar] [CrossRef] [PubMed]
  10. Lin, W.; Zhang, J.; Wang, Z.; Chen, S. Development of Robust Biocompatible Silicone with High Resistance to Protein Adsorption and Bacterial Adhesion. Acta Biomater. 2011, 7, 2053–2059. [Google Scholar] [CrossRef] [PubMed]
  11. Inoue, Y.; Nakanishi, T.; Ishihara, K. Elastic Repulsion from Polymer Brush Layers Exhibiting High Protein Repellency. Langmuir 2013, 29, 10752–10758. [Google Scholar] [CrossRef]
  12. Chang, R.; Tian, Y.; Yu, Z.; Sun, C.; Jin, Z. Preparation and Characterization of Zwitterionic Functionalized Starch Nanoparticles. Int. J. Biol. Macromol. 2019, 142, 395–403. [Google Scholar] [CrossRef] [PubMed]
  13. Manuscript, A. Molecular simulations and understanding of antifouling zwitterionic polymer brushes. J. Mater. Chem. B 2020, 8, 3814–3828. [Google Scholar] [CrossRef]
  14. Su, Y.; Li, C. Controlled Adsorption of Bovine Serum Albumin on Poly (Acrylonitrile)–Based Zwitterionic Membranes. React. Funct. Polym. 2008, 68, 161–168. [Google Scholar] [CrossRef]
  15. Asiabi, H.; Yamini, Y.; Shamsayei, M. Highly Selective and Efficient Removal of Arsenic (V), Chromium (VI) and Selenium (VI) Oxyanions by Layered Double Hydroxide Intercalated with Zwitterionic Glycine. J. Hazard. Mater. 2017, 339, 239–247. [Google Scholar] [CrossRef]
  16. Liu, J.; Ma, Y.; Xu, T.; Shao, G. Preparation of Zwitterionic Hybrid Polymer and Its Application for the Removal of Heavy Metal Ions from Water. J. Hazard. Mater. 2010, 178, 1021–1029. [Google Scholar] [CrossRef] [PubMed]
  17. Ningrum, E.O.; Sakohara, S.; Gotoh, T.; Suprapto; Humaidah, N. The effect of cation and anion species on the transition AND adsorption behaviors of thermosensitive sulfobetaine gel—Based adsorbent. Int. J. Technol. 2019, 10, 443–452. [Google Scholar] [CrossRef] [Green Version]
  18. Salamone, J.C.; Volksen, W.; Olson, A.P.; Israel, S.C. Aqueous Solution Properties of a Poly (Vinyl Imidazolium Sulphobetaine). Polymer 1978, 19, 1157–1162. [Google Scholar] [CrossRef]
  19. Ningrum, E.O.; Sakohara, S.; Gotoh, T.; Suprapto; Humaidah, N. Correlating Properties between Sulfobetaine Hydrogels and Polymers with Different Carbon Spacer Lengths. Polymer 2020, 186, 122013. [Google Scholar] [CrossRef]
  20. Ningrum, E.O.; Bagus, A.; Sakohara, S.; Suprapto; Humaidah, N. Reversible Adsorption-Desorption of Zn (Ii) and Pb (Ii) in Aqueous Solution by Thermosensitive-Sulfobetaine Gel. Mater. Sci. Forum 2019, 964, 221–227. [Google Scholar] [CrossRef]
  21. Ningrum, E.O.; Murakami, Y.; Ohfuka, Y.; Gotoh, T.; Sakohara, S. Investigation of Ion Adsorption Properties of Sulfobetaine Gel and Relationship with Its Swelling Behavior. Polymer 2014, 55, 5189–5197. [Google Scholar] [CrossRef]
  22. Kali, G.; Vavra, S.; László, K.; Iván, B. Thermally Responsive Amphiphilic Conetworks and Gels Based on Poly (N-Isopropylacrylamide) and Polyisobutylene. Macromolecules 2013, 46, 5337–5344. [Google Scholar] [CrossRef] [Green Version]
  23. Chang, Y.; Chen, W.-Y.; Yandi, W.; Shih, Y.-J.; Chu, W.-L.; Liu, Y.-L.; Chu, C.-W.; Ruaan, R.-C.; Higuchi, A. Dual-Thermoresponsive Phase Behavior of Blood Compatible Zwitterionic Copolymers Containing Nonionic Poly (N-Isopropyl Acrylamide). Biomacromolecules 2009, 10, 2092–2100. [Google Scholar] [CrossRef]
  24. Zhao, Y.; Bai, T.; Shao, Q.; Jiang, S.; Shen, A.Q. Thermoresponsive Self-Assembled NiPAm-Zwitterion Copolymers. Polym. Chem. 2015, 6, 1066–1077. [Google Scholar] [CrossRef]
  25. Obiweluozor, F.O.; GhavamiNejad, A.; Hashmi, S.; Vatankhah-Varnoosfaderani, M.; Stadler, F.J. A NIPAM–Zwitterion Copolymer: Rheological Interpretation of the Specific Ion Effect on the LCST. Macromol. Chem. Phys. 2014, 215, 1077–1091. [Google Scholar] [CrossRef]
  26. Hashmi, S.; Vatankhah-Varnoosfaderani, M.; Ghavami Nejad, A.; Obiweluozor, F.O.; Du, B.; Stadler, F.J. Self-Associations and Temperature Dependence of Aqueous Solutions of Zwitterionically Modified N-Isopropylacrylamide Copolymers. Rheol. Acta 2015, 54, 501–516. [Google Scholar] [CrossRef]
  27. Ilčíková, M.; Tkáč, J.; Kasák, P. Switchable Materials Containing Polyzwitterion Moieties. Polymers 2015, 7, 2344–2370. [Google Scholar] [CrossRef]
  28. Arotçaréna, M.; Heise, B.; Ishaya, S.; Laschewsky, A. Switching the inside and the Outside of Aggregates of Water-Soluble Block Copolymers with Double Thermoresponsivity. J. Am. Chem. Soc. 2002, 124, 3787–3793. [Google Scholar] [CrossRef]
  29. Maeda, Y.; Mochiduki, H.; Ikeda, I. Hydration Changes during Thermosensitive Association of a Block Copolymer Consisting of LCST and UCST Blocks. Macromol. Rapid Commun. 2004, 25, 1330–1334. [Google Scholar] [CrossRef]
  30. Virtanen, J.; Arotçaréna, M.; Heise, B.; Ishaya, S.; Laschewsky, A.; Tenhu, H. Dissolution and Aggregation of a Poly (NIPA-Block-Sulfobetaine) Copolymer in Water and Saline Aqueous Solutions. Langmuir 2002, 18, 5360–5365. [Google Scholar] [CrossRef]
  31. Iizawa, T.; Taketa, H.; Maruta, M.; Ishido, T.; Gotoh, T.; Sakohara, S. Synthesis of Porous Poly (N-isopropylacrylamide) Gel Beads by Sedimentation Polymerization and Their Morphology. J. Appl. Polym. Sci. 2007, 104, 842–850. [Google Scholar] [CrossRef]
  32. Tokuyama, H.; Yazaki, N. Preparation of Poly (N-Isopropylacrylamide) Hydrogel Beads by Circulation Polymerization. React. Funct. Polym. 2010, 70, 967–971. [Google Scholar] [CrossRef]
  33. Gotoh, T.; Nakatani, Y.; Sakohara, S. Novel Synthesis of Thermosensitive Porous Hydrogels. J. Appl. Polym. Sci. 1998, 69, 895–906. [Google Scholar] [CrossRef]
  34. Ju, X.-J.; Zhang, S.-B.; Zhou, M.-Y.; Xie, R.; Yang, L.; Chu, L.-Y. Novel Heavy-Metal Adsorption Material: Ion-Recognition P (NIPAM-Co-BCAm) Hydrogels for Removal of Lead (II) Ions. J. Hazard. Mater. 2009, 167, 114–118. [Google Scholar] [CrossRef] [PubMed]
  35. Chen, A.-L.; Yu, H.-R.; Ju, X.-J.; Xie, R.; Wang, W.; Chu, L.-Y. Visual Detection of Lead (II) Using a Simple Device Based on P (NIPAM-Co-B18C6Am) Hydrogel. RSC Adv. 2014, 4, 26030–26037. [Google Scholar] [CrossRef]
  36. Zhang, M.; Li, Y.; Yang, Q.; Huang, L.; Chen, L.; Ni, Y.; Xiao, H. Temperature and PH Responsive Cellulose Filament/Poly (NIPAM-Co-AAc) Hybrids as Novel Adsorbent towards Pb (II) Removal. Carbohydr. Polym. 2018, 195, 495–504. [Google Scholar] [CrossRef]
  37. Cheng, J.; Shan, G.; Pan, P. Temperature and PH-Dependent Swelling and Copper (II) Adsorption of Poly (N-Isopropylacrylamide) Copolymer Hydrogel. RSC Adv. 2015, 5, 62091–62100. [Google Scholar] [CrossRef]
  38. Yamashita, K.; Nishimura, T.; Nango, M. Preparation of IPN-type Stimuli-Responsive Heavy-Metal-Ion Adsorbent Gel. Polym. Adv. Technol. 2003, 14, 189–194. [Google Scholar] [CrossRef]
  39. Tokuyama, H.; Iwama, T. Temperature-Swing Solid-Phase Extraction of Heavy Metals on a Poly (N-Isopropylacrylamide) Hydrogel. Langmuir 2007, 23, 13104–13108. [Google Scholar] [CrossRef] [PubMed]
  40. Yan, F.; Wang, M.; Cao, D.; Guo, S.; Chen, L. Preparation of Thermosensitive, Calix[4]Arene Incorporated P(NIPAM-Co-HBCalix) Hydrogel as a Reusable Adsorbent of Nickel(II) Ions. J. Polym. Sci. Part A Polym. Chem. 2013, 51, 2401–2408. [Google Scholar] [CrossRef]
  41. Shahid, M.; Farooqi, Z.H.; Begum, R.; Arif, M.; Irfan, A.; Azam, M. Extraction of Cobalt Ions from Aqueous Solution by Microgels for In-Situ Fabrication of Cobalt Nanoparticles to Degrade Toxic Dyes: A Two Fold-Environmental Application. Chem. Phys. Lett. 2020, 754, 137645. [Google Scholar] [CrossRef]
  42. Naseem, K.; Farooqi, Z.H.; Begum, R.; Ur Rehman, M.Z.; Ghufran, M.; Wu, W.; Najeeb, J.; Irfan, A. Synthesis and Characterization of Poly (N-Isopropylmethacrylamide-Acrylic Acid) Smart Polymer Microgels for Adsorptive Extraction of Copper (II) and Cobalt (II) from Aqueous Medium: Kinetic and Thermodynamic Aspects. Environ. Sci. Pollut. Res. 2020, 27, 28169–28182. [Google Scholar] [CrossRef] [PubMed]
  43. Zdravković, A.; Nikolić, L.; Ilić-Stojanović, S.; Nikolić, V.; Najman, S.; Mitić, Ž.; Ćirić, A.; Petrović, S. The Removal of Heavy Metal Ions from Aqueous Solutions by Hydrogels Based on N-Isopropylacrylamide and Acrylic Acid. Polym. Bull. 2018, 75, 4797–4821. [Google Scholar] [CrossRef] [Green Version]
  44. Allegretto, J.A.; Giussi, J.M.; Moya, S.E.; Azzaroni, O.; Rafti, M. Synthesis and Characterization of Thermoresponsive ZIF-8@ PNIPAm-Co-MAA Microgel Composites with Enhanced Performance as an Adsorption/Release Platform. RSC Adv. 2020, 10, 2453–2461. [Google Scholar] [CrossRef] [Green Version]
  45. Ningrum, E.O.; Ohfuka, Y.; Gotoh, T.; Sakohara, S. Effects of Specific Anions on the Relationship between the Ion-Adsorption Properties of Sulfobetaine Gel and Its Swelling Behavior. Polymer 2015, 59, 144–154. [Google Scholar] [CrossRef]
  46. Schmid, A.J.; Schroeder, R.; Eckert, T.; Radulescu, A.; Pich, A.; Richtering, W. Synthesis and Solution Behaviour of Stimuli-Sensitive Zwitterionic Microgels. Colloid Polym. Sci. 2015, 293, 3305–3318. [Google Scholar] [CrossRef]
  47. Ningrum, E.O.; Purwanto, A.; Rosita, G.C.; Bagus, A. The Properties of Thermosensitive Zwitterionic Sulfobetaine NIPAM-Co-DMAAPS Polymer and the Hydrogels: The Effects of Monomer Concentration on the Transition Temperature and Its Correlation with the Adsorption Behavior. Indones. J. Chem. 2020, 20, 324–335. [Google Scholar] [CrossRef] [Green Version]
  48. Eeckman, F.; Amighi, K.; Moës, A.J. Effect of Some Physiological and Non-Physiological Compounds on the Phase Transition Temperature of Thermoresponsive Polymers Intended for Oral Controlled-Drug Delivery. Int. J. Pharm. 2001, 222, 259–270. [Google Scholar] [CrossRef]
  49. Costioli, M.D.; Fisch, I.; Garret-Flaudy, F.; Hilbrig, F.; Freitag, R. DNA Purification by Triple-helix Affinity Precipitation. Biotechnol. Bioeng. 2003, 81, 535–545. [Google Scholar] [CrossRef]
  50. Lu, Y.; Chen, T.; Mei, A.; Chen, T.; Ding, Y.; Zhang, X.; Xu, J.; Fan, Z.; Du, B. Solution Behaviors and Microstructures of PNIPAm- P123-PNIPAm Pentablock Terpolymers in Dilute and Concentrated Aqueous Solutions. Phys. Chem. Chem. Phys. 2013, 15, 8276–8286. [Google Scholar] [CrossRef]
  51. Ionov, L.; Synytska, A.; Diez, S. Temperature-Induced Size-Control of Bioactive Surface Patterns. Adv. Funct. Mater. 2008, 18, 1501–1508. [Google Scholar] [CrossRef]
  52. Takeoka, Y.; Watanabe, M. Tuning Structural Color Changes of Porous Thermosensitive Gels through Quantitative Adjustment of the Cross-Linker in Pre-Gel Solutions. Langmuir 2003, 19, 9104–9106. [Google Scholar] [CrossRef]
  53. Jung, Y.C.; Bhushan, B. Contact Angle, Adhesion and Friction Properties of Micro-and Nanopatterned Polymers for Superhydrophobicity. Nanotechnology 2006, 17, 4970. [Google Scholar] [CrossRef]
  54. Mydin, N.M.B.M.; Mubarak, N.M.; Nizamuddin, S.; Siddiqui, M.T.H.; Baloch, H.A.; Abdullah, E.C.; Khalid, M. Multiwall Carbon Nanotube Promising Route for Removal of Chromium from Wastewater via Batch Column Mechanism. IOP Conf. Ser. Mater. Sci. Eng. 2019, 495, 12061. [Google Scholar] [CrossRef] [Green Version]
  55. Zhang, T.; Wang, Y.; Kuang, Y.; Yang, R.; Ma, J.; Zhao, S.; Liao, Y.; Mao, H. Adsorptive Removal of Cr3+ from Aqueous Solutions Using Chitosan Microfibers Immobilized with Plant Polyphenols as Biosorbents with High Capacity and Selectivity. Appl. Surf. Sci. 2017, 404, 418–425. [Google Scholar] [CrossRef]
  56. Mahmoud, M.E.; Abdou, A.E.H.; Sobhy, M.E. Engineered Nano-Zirconium Oxide-Crosslinked-Nanolayer of Carboxymethyl Cellulose for Speciation and Adsorptive Removal of Cr (III) and Cr (VI). Powder Technol. 2017, 321, 444–453. [Google Scholar] [CrossRef]
  57. Mohamed, H.S.; Soliman, N.K.; Abdelrheem, D.A.; Ramadan, A.A.; Elghandour, A.H.; Ahmed, S.A. Adsorption of Cd2+ and Cr3+ Ions from Aqueous Solutions by Using Residue of Padina Gymnospora Waste as Promising Low-Cost Adsorbent. Heliyon 2019, 5, e01287. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  58. Liu, M.; Zhang, H.; Zhang, X.; Deng, Y.; Liu, W.; Zhan, H. Removal and Recovery of Chromium (III) from Aqueous Solutions by a Spheroidal Cellulose Adsorbent. Water Environ. Res. 2001, 73, 322–328. [Google Scholar] [CrossRef] [PubMed]
  59. Oumani, A.; Mandi, L.; Berrekhis, F.; Ouazzani, N. Removal of Cr3+ from Tanning Effluents by Adsorption onto Phosphate Mine Waste: Key Parameters and Mechanisms. J. Hazard. Mater. 2019, 378, 120718. [Google Scholar] [CrossRef] [PubMed]
  60. Xu, S.; Pan, D.; Wu, Y.; Fan, J.; Wu, N.; Gao, L.; Li, W.; Xiao, G. Catalytic Conversion of Xylose and Xylan into Furfural over Cr3+/P-SBA-15 Catalyst Derived from Spent Adsorbent. Ind. Eng. Chem. Res. 2019, 58, 13013–13020. [Google Scholar] [CrossRef]
  61. Tao, E.; Ma, D.; Yang, S.; Sun, Y.; Xu, J.; Kim, E.J. Zirconium Dioxide Loaded Montmorillonite Composites as High-Efficient Adsorbents for the Removal of Cr3+ Ions from Tanning Wastewater. J. Solid State Chem. 2019, 277, 502–509. [Google Scholar]
  62. Maneechakr, P.; Mongkollertlop, S. Investigation on Adsorption Behaviors of Heavy Metal Ions (Cd2+, Cr3+, Hg2+ and Pb2+) through Low-Cost/Active Manganese Dioxide-Modified Magnetic Biochar Derived from Palm Kernel Cake Residue. J. Environ. Chem. Eng. 2020, 8, 104467. [Google Scholar] [CrossRef]
  63. Tahergorabi, M.; Esrafili, A.; Kermani, M.; Shirzad-Siboni, M. Application of Thiol-Functionalized Mesoporous Silica-Coated Magnetite Nanoparticles for the Adsorption of Heavy Metals. Desalin. Water Treat. 2016, 57, 19834–19845. [Google Scholar] [CrossRef]
  64. Abuhatab, S.; El-Qanni, A.; Al-Qalaq, H.; Hmoudah, M.; Al-Zerei, W. Effective Adsorptive Removal of Zn2+, Cu2+, and Cr3+ Heavy Metals from Aqueous Solutions Using Silica-Based Embedded with NiO and MgO Nanoparticles. J. Environ. Manag. 2020, 268, 110713. [Google Scholar] [CrossRef] [PubMed]
  65. Taha, G.M. Utilization of Low-Cost Waste Material Bagasse Fly Ash in Removing of Cu2+, Ni2+, Zn2+, and Cr3+ from Industrial Waste Water. Groundw. Monit. Remediat. 2006, 26, 137–141. [Google Scholar] [CrossRef] [Green Version]
  66. Kang, S.-Y.; Lee, J.-U.; Moon, S.-H.; Kim, K.-W. Competitive Adsorption Characteristics of Co2+, Ni2+, and Cr3+ by IRN-77 Cation Exchange Resin in Synthesized Wastewater. Chemosphere 2004, 56, 141–147. [Google Scholar] [CrossRef] [PubMed]
  67. Suharto, T.; Goto, T.; Nakai, S. Simultaneous Adsorption of Cation and Anion by Thermosensitive Hydrogels. In Proceedings of the MATEC Web of Conferences: 18th Asian Pacific Confederation of Chemical Engineering Congress (APCChE 2019), Sapporo, Japan, 23–27 September 2019; EDP Sciences: Les Ulis, France, 2021; Volume 333, p. 11007. [Google Scholar]
Gels 07 00273 g001 550
Figure 1. FTIR spectra of NIPAAM, DMAAPS, and poly(NIPAAM-co-DMAAPS) gels.
Figure 1. FTIR spectra of NIPAAM, DMAAPS, and poly(NIPAAM-co-DMAAPS) gels.
Gels 07 00273 g001
Gels 07 00273 g002 550
Figure 2. 1H NMR spectra of DMAAPS (a) and NIPAAM (b) monomer and the resulting poly(DMAAPS-co-NIPAAM) (c). The NIPAAM:DMAAPS molar ratio is 95:5.
Figure 2. 1H NMR spectra of DMAAPS (a) and NIPAAM (b) monomer and the resulting poly(DMAAPS-co-NIPAAM) (c). The NIPAAM:DMAAPS molar ratio is 95:5.
Gels 07 00273 g002
Gels 07 00273 g003 550
Figure 3. Phase transition temperature of poly(NIPAAM-co-DMAAPS) at polymer concentration of (a) 1 g/L and (b) 10 g/L. Heating rate = 1 °C/min in water and Cr(NO3)3 solution.
Figure 3. Phase transition temperature of poly(NIPAAM-co-DMAAPS) at polymer concentration of (a) 1 g/L and (b) 10 g/L. Heating rate = 1 °C/min in water and Cr(NO3)3 solution.
Gels 07 00273 g003
Gels 07 00273 g004 550
Figure 4. Photographs of H2O containing 1 g/L co-polymers with different monomer ratios (NIPAAM:DMAAPS): (a) 100:0, (b) 95:5, (c) 90:10, (d) 85:15, and (e) 80:20 at various temperatures.
Figure 4. Photographs of H2O containing 1 g/L co-polymers with different monomer ratios (NIPAAM:DMAAPS): (a) 100:0, (b) 95:5, (c) 90:10, (d) 85:15, and (e) 80:20 at various temperatures.
Gels 07 00273 g004
Gels 07 00273 g005 550
Figure 5. Contact angle analysis of co-polymers at different temperatures.
Figure 5. Contact angle analysis of co-polymers at different temperatures.
Gels 07 00273 g005
Gels 07 00273 g006 550
Figure 6. (a) Adsorption of Cr3+ by poly(NIPAAM-co-DMAAPS) gels at different temperatures. (b) Swelling degree of poly(NIPAAM-co-DMAAPS) gels at different temperatures.
Figure 6. (a) Adsorption of Cr3+ by poly(NIPAAM-co-DMAAPS) gels at different temperatures. (b) Swelling degree of poly(NIPAAM-co-DMAAPS) gels at different temperatures.
Gels 07 00273 g006
Gels 07 00273 g007 550
Figure 7. Chemical structure of (a) NIPAAM and (b) DMAAPS.
Figure 7. Chemical structure of (a) NIPAAM and (b) DMAAPS.
Gels 07 00273 g007
Table
Table 1. Functional groups observed in FTIR spectra of NIPAAM, DMAAPS, and poly(NIPAAM-co-DMAAPS) gels.
Table 1. Functional groups observed in FTIR spectra of NIPAAM, DMAAPS, and poly(NIPAAM-co-DMAAPS) gels.
No.Functional GroupsWavenumber (cm−1)
NIPAAMDMAAPSNIPAAM:DMAAPS = 80:20NIPAAM:DMAAPS = 85:15NIPAAM:DMAAPS = 90:10NIPAAM:DMAAPS = 95:5
1C=C960980----
2CO-NH154715561540154015371538
3C-H296829742934297029702970
4C-N106110381036103610371037
5C=O162016251634163516321634
6N-H327932733276328032813289
7S-O-11811170117011701170
Table
Table 2. Comparison of different adsorbents toward the Cr3+ ions 1.
Table 2. Comparison of different adsorbents toward the Cr3+ ions 1.
AdsorbentSurface Area (m2/g)Adsorption Capacity (mg/g)Temperature (°C)pHConcentration (mg/L)Ref.
MWCNTs-24.9-72–10[54]
CM-BT-20.90305.52[55]
Nano-ZrO2-Glu-CMC24.1358.2257-[56]
RPG-39.86258100[57]
Spheroidal cellulose adsorbent containing the carboxyl anionic group-72.62541920[58]
PW15.1297.23503.4340[59]
P-SBA-1570163.6304100[60]
ZrO2-MMT-172.41507–830[61]
CP-Fe-Mn89.385319.92304.30100[62]
TF-SCMNPs-1.12510400[63]
PVP/SiO2873.6297.7307100[4]
NiO-MgO SBNs48209.5255.550–400[64]
Bagasse fly ash4802.4825630[65]
Amberlite IRN-77 cation exchange resin-46.95254,8100[66]
poly(NIPAAM-co-DMAAPS)-185.2307330This study
1 Abbreviations. MWCNTs: multi-wall carbon nanotubes. CM-BT: immobilizing bayberry tannin (BT, a typical natural polyphenol) onto chitosan microfiber (CM). Nano-ZrO2-Glu-CMC: crosslinking of nanolayer carboxymethyl cellulose (CMC) onto the surface of nano-zirconium oxide (Nano-ZrO2) using glutaraldehyde. RPG: brown macroalga Padina gymnospora. PW: phosphate mine waste. P-SBA-15: phosphoric acid—modified. ZrO2-MMT: zirconium dioxide-loaded montmorillonite composites. CP-Fe-Mn: MnO2-modified magnetic bio-char. TF-SCMNPs: thiol-functionalized mesoporous silica-coated magnetite nanoparticles. PVP/SiO2: amino (-NH2) functionalized mesoporous polyvinyl pyrrolidone composite nanofiber membranes. NiO-MgO SBNs: nickel and magnesium oxides embedded into silica.
Table
Table 3. Analysis results for co-polymers (phase transition temperature, contact angle, visual) and gels (swelling degree and ion adsorption) with various monomer ratios at 30 °C.
Table 3. Analysis results for co-polymers (phase transition temperature, contact angle, visual) and gels (swelling degree and ion adsorption) with various monomer ratios at 30 °C.
Molar Ratios of NIPAAM and DMAAPSLCST (°C)Temperature (30 °C)
Contact Angle (°)VisualSwelling Degree (-)Ion Adsorption
(mmol/g dry-gel)
95:05:0041.07286.64hydrophilic, 1.750.0489
transparent
90:10:0051.0776.84hydrophilic,2.8440.0454
transparent
85:15:0064.90452.52hydrophilic, 4.6950.0555
transparent
80:20:00>8052.72hydrophilic, 4.4440.0712
transparent
Table
Table 4. Analysis results for co-polymers (phase transition temperature, contact angle, visual) and gels (swelling degree and ion adsorption) with various monomer ratios at 70 °C.
Table 4. Analysis results for co-polymers (phase transition temperature, contact angle, visual) and gels (swelling degree and ion adsorption) with various monomer ratios at 70 °C.
Molar Ratios of NIPAAM and DMAAPSNIPAAM Concentration
(mmol/L)		LCST (°C)Temperature (70 °C)
Contact Angle (°)VisualSwelling Degree (-)Ion Adsorption
(mmol/g dry-gel)
95:05:0095041.07292.73hydrophobic,1.1430.027
milky white
90:10:0090051.0794.33hydrophobic,0.9030.0223
milky white
85:15:0085064.90495.98hydrophobic, 1.4550.045
opaque
80:20:00800>8074.46hydrophilic, 1.760.0627
transparent
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Ningrum, E.O.; Gotoh, T.; Ciptonugroho, W.; Karisma, A.D.; Agustiani, E.; Safitri, Z.M.; Dzaky, M.A. Novel Thermosensitive-co-Zwitterionic Sulfobetaine Gels for Metal Ion Removal: Synthesis and Characterization. Gels 2021, 7, 273. https://doi.org/10.3390/gels7040273

AMA Style

Ningrum EO, Gotoh T, Ciptonugroho W, Karisma AD, Agustiani E, Safitri ZM, Dzaky MA. Novel Thermosensitive-co-Zwitterionic Sulfobetaine Gels for Metal Ion Removal: Synthesis and Characterization. Gels. 2021; 7(4):273. https://doi.org/10.3390/gels7040273

Chicago/Turabian Style

Ningrum, Eva Oktavia, Takehiko Gotoh, Wirawan Ciptonugroho, Achmad Dwitama Karisma, Elly Agustiani, Zela Marni Safitri, and Muhammad Asyam Dzaky. 2021. "Novel Thermosensitive-co-Zwitterionic Sulfobetaine Gels for Metal Ion Removal: Synthesis and Characterization" Gels 7, no. 4: 273. https://doi.org/10.3390/gels7040273

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop