Next Article in Journal
Positive Effects of UV-Photofunctionalization of Titanium Oxide Surfaces on the Survival and Differentiation of Osteogenic Precursor Cells—An In Vitro Study
Next Article in Special Issue
Acid-Triggered Release of Eugenol and Fluoride by Desensitizing Macro- and Nanoparticles
Previous Article in Journal
Why Is Tantalum Less Susceptible to Bacterial Infection?
Previous Article in Special Issue
Inhibition of Demineralization of Dentin by Fluoride-Containing Hydrogel Desensitizers: An In Vitro Study
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
JFB
Volume 13
Issue 4
10.3390/jfb13040263
jfb-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mechanical Properties of Ti-Nb-Cu Alloys for Dental Machining Applications

by
Masatoshi Takahashi
*,
Kotaro Sato
,
Genichi Togawa
and
Yukyo Takada
Division of Dental Biomaterials, Tohoku University Graduate School of Dentistry, 4-1 Seiryo-machi, Aoba-ku, Sendai 980-8575, Japan
*
Author to whom correspondence should be addressed.
J. Funct. Biomater. 2022, 13(4), 263; https://doi.org/10.3390/jfb13040263
Submission received: 20 October 2022 / Revised: 7 November 2022 / Accepted: 21 November 2022 / Published: 22 November 2022
(This article belongs to the Special Issue State of the Art in Dental Materials)
Browse Figures
Versions Notes

Abstract

:
Titanium has excellent biocompatibility and good corrosion resistance and is extensively used in dental implants and denture bases. However, pure titanium lacks the strength for use in dental prostheses that require relatively high strength. We developed 15 different types of Ti-Nb-Cu alloys and investigated their alloy phases and mechanical properties, including tensile and yield strength, elongation after fracture, and Vickers hardness. The alloy phases of Ti-8%Nb-2%Cu and Ti-13%Nb-2%Cu were α + β, while those of Ti-5%Nb-5%Cu and Ti-10%Nb-5%Cu were α + Ti2Cu. The tensile strength and hardness of these alloys were significantly higher than those of titanium; however, their elongation was less. In particular, the yield strength of these alloys was more than twice that of titanium. These differences in mechanical properties are attributable to solid–solution strengthening and precipitation strengthening. Other compositions with an alloy phase of α + β + Ti2Cu or β + Ti2Cu had high hardness but not high strength. These results suggest that the Ti-8%Nb-2%Cu, Ti-5%Nb-5%Cu, Ti-13%Nb-2%Cu, and Ti-10%Nb-5%Cu alloys can be applied to dental prostheses, which are subject to very high forces from accessories such as long-span bridges, clasps, implant-retained superstructures, and narrow-diameter implants.

1. Introduction

Ti, which has excellent biocompatibility and good corrosion resistance, is extensively used in dental implants and denture bases. In Japan, fully cast and resin-veneered Ti crowns have been covered by the medical insurance system since 2020 and 2022, respectively. Ti is expected to replace precious metal and cobalt–chromium alloys in dental applications. However, pure Ti lacks the strength for use in dental prostheses such as bridges and clasps, which require relatively high strength. These prostheses are usually manufactured with high-strength metallic materials classified as types 4 and 5 according to the ISO 22674 criteria, including hardened type 4 dental casting gold alloys and cobalt–chromium alloys [1,2]. Narrow-diameter implants used in cases of insufficient alveolar bone or minimally invasive treatment also require high strength materials [3,4].
Although Ti alloys containing aluminum (Al), vanadium (V), and niobium (Nb), such as Ti-6Al-4V, Ti-6Al-7Nb, and commercially pure grade 4 Ti containing impurities, are available [5], there are concerns regarding the safety of the alloying elements V and Al [6,7]. In addition, the machinability of these alloys is worse than that of pure Ti [8,9], which is difficult to cut and has poor machinability and grindability [10,11]. Pure Ti also has properties that cannot be avoided in casting, such as its high melting point, high reactivity with investment materials at high temperatures, large casting shrinkage, and difficulty in applying casting pressure due to its small specific gravity. Cutting, grinding, and polishing of materials is essential when fabricating dental prostheses. If Ti could be cut easily, it could be used to manufacture dental prostheses using computer-aided design and manufacturing (CAD/CAM). To improve the mechanical properties and machinability of Ti and expand its application in dentistry, we have been developing Ti alloys not containing Al or V [12,13,14,15,16].
We found that the binary Ti alloys made with Ti-Nb and Ti-copper (Cu) have excellent mechanical properties and machinability. The tensile strength, yield strength, and hardness of Ti-Nb alloys increased with increasing Nb content. The strength of 30mass% Nb (hereafter, “%” stands for “mass%”) was more than twice that of Ti, and its elongation after fracture was about 10% [12]. In a grindability test performed using a carborundum wheel, the grinding amount of the Ti-30% Nb alloy was twice that of pure Ti at grinding speeds of 500 m/min and 750 m/min [12]. Further, the strength, yield strength, and hardness of Ti-Cu alloys increased with an increase in the Cu content. The strength of the 5% Cu alloy was more than twice that of Ti, and its elongation was more than 5% [13]. The grinding amount of the Ti-Cu alloy containing 5% Cu was significantly higher than that of Ti at grinding speeds of more than 750 m/min, and it increased significantly at higher speeds [14]. The grinding amount of this alloy at a speed of 1500 m/min was 2.9 times that of Ti. The yield strength and elongation of the 30% Nb and 5% Cu alloys were comparable to those of the hardened type 4 dental casting alloy and cobalt–chromium alloys. They may therefore be applicable in denture bases and clasps. They are also the candidate Ti alloys for CAD/CAM owing to their excellent grindability. In addition, Ti-Cu alloys have good properties such as corrosion resistance, biocompatibility, and antibacterial properties [17,18,19,20,21,22,23].
To further increase the strength and grindability of Ti alloys, we used the elements of the binary alloys to develop ternary alloys. We focused on the three compositions of Ti-6%Nb-4%Cu, Ti-18%Nb-2%Cu, and Ti-24%Nb-1%Cu, which are located between the Ti-30% Nb and Ti-5% Cu alloys on the Ti-Nb-Cu ternary composition diagram. The strength of these Ti-Nb-Cu alloys was higher than that of the base Ti-30% Nb and Ti-5% Cu alloys [24]. In addition, their grindability was superior to that of Ti [25]. Through this series of studies, we discovered the potential of Ti-Nb-Cu alloys for use with CAD/CAM. Ti-Nb-Cu alloys with antibacterial and shape-memory properties have also been developed [26,27].
Phase diagrams are essential for alloy development. Although various binary phase diagrams have been presented, ternary phase diagrams are complex, and only a limited number of element combinations exist. Because no ternary Ti-Nb-Cu phase diagram had been developed before, we constructed a Ti-Nb-Ti2Cu pseudo-ternary phase diagram to serve as a development map in our recent study [28]. This phase diagram showed that the Ti-Nb-Cu alloys had phases such as α + β, α + Ti2Cu, and α + β + Ti2Cu. In general, alloy phases are related to their mechanical properties, and compositions with phases α + β, α + Ti2Cu, and α + β + Ti2Cu are expected to have good mechanical properties. Therefore, in this study, Ti-Nb-Cu alloys with various compositions and phases were developed and their mechanical properties were investigated.

2. Materials and Methods

2.1. Alloy Design and Preparation

Experimental ternary Ti-Nb-Cu alloys of the following fifteen different compositions were designed; these are the same as those investigated for the construction of the phase diagram in our previous study [28]: Ti-8%Nb-2%Cu (8Nb2Cu), Ti-5%Nb-5%Cu (5Nb5Cu), Ti-13%Nb-2%Cu (13Nb2Cu), Ti-10%Nb-5%Cu (10Nb5Cu), Ti-5%Nb-10%Cu (5Nb10Cu), Ti-10%Nb-7.5%Cu (10Nb7.5Cu), Ti-15%Nb-5%Cu (15Nb5Cu), Ti-10%Nb-10%Cu (10Nb10Cu), Ti-20%Nb-5%Cu (20Nb5Cu), Ti-20%Nb-7.5%Cu (20Nb7.5Cu), Ti-20%Nb-10%Cu (20Nb10Cu), Ti-10%Nb-20%Cu (10Nb20Cu), Ti-30%Nb-5%Cu (30Nb5Cu), Ti-30%Nb-7.5%Cu (30Nb7.5Cu), and Ti-30%Nb-10%Cu (30Nb10Cu) (Figure 1).
The required quantities of Ti (>99.8%, grade S-90, Osaka Titanium Technologies, Amagasaki, Japan), Nb (9.9%, H.C. Starck, Goslar, Germany), and Cu (>99.99%, Research Institute for Electric and Magnetic Materials, Sendai, Japan) were weighed and melted in an argon arc melting furnace to produce a 30 g alloy ingot, as described previously [28]. An ingot of pure Ti was prepared in the same manner.

2.2. Preparation of Specimens

The alloy ingots were cast into a mold made of a magnesia investment (Symbion-TC, i-Cast Co., Ltd., Kyoto, Japan) using a titanium casting machine for dentistry (Autocast HC-III, GC, Tokyo, Japan) at 200 °C, followed by bench-cooling. Slabs of dimensions 3.5 mm × 8.5 mm × 30.5 mm were used for the X-ray diffraction (XRD) experiments, hardness tests, and microstructural observations, while specimens with a diameter of 3.0 mm and gauge length of 15 mm were used for the tensile tests. Hardened surface layers of cast slabs were removed by abrading to a depth of 250 µm with 180–800 grit silicon carbide abrasive papers.

2.3. Phase Identification

XRD experiments were performed on an X-ray diffractometer (D2 PHASER, Bruker AXS, Tokyo, Japan) over a 2θ range of 30°–80° using Cu Kα radiation (30 kV, 10 mA). The peaks were identified according to the Crystallography Open Database.

2.4. Metallography

The cast slabs were cut into specimens of dimensions 8 mm × 8 mm × 3 mm. The specimens were embedded in epoxy resin and only one surface was exposed. The exposed surface was sequentially polished using diamond suspensions with particle sizes of 15, 6, 3, and 1 µm. The mirror-polished surfaces were etched with an etching solution (HF:HNO3:H2O = 1:4:25) and then observed using an optical microscope (PMG3-614U, Olympus, Tokyo, Japan).

2.5. Hardness Tests

The Vickers hardness of the specimens was evaluated using a micro Vickers hardness tester (HM-221, Mitutoyo, Kawasaki, Japan) with a 1.961 N load and 15 s dwell time. Tests (n = 9) were performed at three randomly chosen points on each specimen.

2.6. Tensile Tests

Tensile testing of each specimen was performed at room temperature at a crosshead speed of 0.5 mm/min on a universal testing machine (AG-IS, Shimadzu, Kyoto, Japan) (n = 6). The ultimate tensile strength, yield strength at 0.2% nonproportional extension, and elongation after fracture were determined. The fractured surfaces of the tensile specimens were examined by scanning electron microscopy (SEM; JSM-6060, JEOL, Tokyo, Japan) after testing.

2.7. Statistical Analysis

The obtained data were statistically analyzed with SPSS software version 28 using one-way ANOVA and Tukey’s HSD test at a significance level of α = 0.05.

3. Results

3.1. XRD Findings

Table 1 lists the alloy phases identified by XRD. The peaks in the XRD pattern of the experimental Ti-Nb-Cu alloy in this study matched those of α-Ti, β-Ti, and Ti2Cu. The 5Nb5Cu, 5Nb10Cu, and 10Nb5Cu alloys had the α + Ti2Cu phase. The 8Nb2Cu, 13Nb2Cu, 15Nb5Cu, and 20Nb5Cu alloys had the α + β phase. The 10Nb7.5Cu, 10Nb10Cu, 20Nb7.5Cu, 20Nb10Cu, and 10Nb20Cu alloys had the α + β + Ti2Cu phase. The 30Nb5Cu alloy had a single β phase, and the 30Nb7.5Cu and 30Nb10Cu alloys had a β + Ti2Cu phase.

3.2. Metallography

Among the Ti-Nb-Cu alloys investigated in this study, typical metallographic structures of various alloy phases were selected and are shown in Figure 2. The alloy phases of 5Nb10Cu and 10Nb5Cu were α + Ti2Cu. Acicular structures, characteristic of α phase, were observed over the entire surface of the specimen. It was difficult to confirm the precipitation of Ti2Cu. The alloy phases of 8Nb2Cu and 20Nb5Cu were α + β. The specimens showed that the acicular α phase precipitated within the equiaxed β grains. The alloy phases of 20Nb10Cu and 10Nb20Cu were α + β + Ti2Cu, and precipitated acicular α and Ti2Cu were found in the β grains. In addition, the β grains were surrounded by Ti2Cu in the 10Nb20Cu specimen. The alloy phase of 30Nb5Cu was a single β; equiaxed β structures were observed over the entire surface of the specimen. The alloy phase of 30Nb10Cu was β + Ti2Cu. In this specimen, Ti2Cu was precipitated along the β grain boundaries and in the equiaxed β grains.

3.3. Vickers Hardness

Figure 3 presents the Vickers hardness values of the Ti-Nb-Cu alloys. The hardness of all Ti-Nb-Cu alloys was significantly (p < 0.01) higher than that of Ti. The hardness values of the 10Nb7.5Cu, 10Nb10Cu, 20Nb5Cu, and 20Nb7.5Cu alloys were particularly high, exceeding 400. When the total amount of the added elements was the same, the alloy hardness increased with increasing Cu content, except for the 20Nb10Cu and 10Nb20Cu alloys.

3.4. Tensile Test

Figure 4 shows the tensile and yield strengths obtained. The tensile and yield strengths of the 8Nb2Cu, 5Nb5Cu, 13Nb2Cu, and 10Nb5Cu alloys were significantly greater than those of Ti (p < 0.01). No significant difference in the tensile and yield strengths of Ti and Nb-Cu alloys was observed. The tensile strengths of the 5Nb5Cu and 13Nb2Cu alloys were over 700 MPa, more than 1.9 times that of Ti. They had a yield strength of 530 MPa or higher, and the 5Nb5Cu alloy (574 MPa) had the highest yield strength, which was 2.2 times that of Ti. The tensile strengths of the 15Nb5Cu and 20Nb5Cu alloys were significantly greater than that of Ti (p < 0.05), but there was no significant difference in the yield strength (p > 0.05). The elongations of the six Ti-Nb-Cu alloys were approximately 3%-4%, which was significantly (p < 0.01) lower than that of Ti (22%).
The elongation of the Ti-Nb-Cu alloys, other than the above six compositions, was very small (less than 1%). Therefore, their yield strengths could not be determined. The tensile strength of these alloys was less than or equal to that of Ti. The tensile strength of the Ti-Nb-Cu alloys with more than 7.5% Cu content, except for 10Nb20Cu, was lower than that of Ti.

3.5. Observation of Fracture Surface after Tensile Test

Figure 5 shows the SEM image of the fracture surface after the tensile test. Numerous dimples were finely distributed on the fracture surface of ductile alloys with the above six compositions and Ti. The dimples observed on the 20Nb5Cu and 15Nb5Cu alloys were larger than those on the other compositions. A cleavage fracture was observed in the alloy with an elongation of less than 1%. In addition, microshrinkage or many porosities were observed on all specimens. Figure 6 shows an example of porosity.

4. Discussion

4.1. Alloy Phases and Mechanical Properties

In this study, we investigated the mechanical properties of Ti-Nb-Cu alloys of various compositions developed in our previous study, which was aimed at constructing a Ti-Nb-Ti2Cu pseudophase diagram [28]. Therefore, these findings related to the alloy phases and microstructures are consistent with those of the previous study.
The mechanical properties of metallic materials are closely related to the alloy phases. To further elucidate the relationship between the mechanical properties and alloy phases, the hardness and tensile strength values of the alloys are plotted in the Ti-Nb-Ti2Cu pseudophase diagrams in Figure 7 and Figure 8, in which data from previous studies have also been summarized.
Considering the α + Ti2Cu alloy phase, the hardness of the 5Nb5Cu alloy was greater than that of the 6Nb4Cu alloy in the α-single phase. This may be attributable to precipitation hardening of Ti2Cu in addition to solid solution strengthening of α. The hardness further increased when the amount of solid solution in α-Ti also increased (10Nb5Cu) or the amount of Ti2Cu increased (5Nb10C). Its strength was also greater than that of Ti owing to solid solution strengthening and precipitation strengthening. The yield strengths of the 5Nb5Cu and 10Nb5Cu alloys were similar to those of the 6Nb4Cu alloy, but their tensile strength was lower. This may be because precipitation of Ti2Cu resulted in a decrease in the elongation. The 5Nb10C alloy, which contains a large amount of Ti2Cu, had remarkably less elongation, and its yield strength could not be determined.
In the α + β alloy phase, the hardness increased with increasing the total amount of added elements. Solid solution strengthening was considered to have a strong effect. On comparing the 18Nb2Cu, 15Nb5Cu, 24Nb1Cu, and 20Nb5Cu alloys with the same amount of added elements, the hardness of the two alloys with the most Cu content was found to be greater. Because the phases of these compositions are at the borderline between α + β and α + β + Ti2Cu, some Ti2Cu undetected by XRD may have precipitated. The strength of the α+ β-type alloy was greater than that of Ti. This two-phase alloy contains acicular α in the residual β phase, resulting in precipitation strengthening. In addition to the solid solution strengthening of the α and β phases, the α + β structure contributes to the high strength. Its strength can be enhanced further by heat treatment [29]. The strength of the 15Nb5Cu and 20Nb5Cu alloys was not significantly high. As described above, this is probably because a small amount of Ti2Cu precipitated, and the elongation decreased.
The hardness of the region with the three-phase coexistence of α + β + Ti2Cu, except for the 10Nb20Cu alloy, was remarkably high in this study. This may be due to solid solution hardening and precipitation hardening of α and Ti2Cu. The hardness of Ti2Cu has been reported to be 451 [30]. Because the 10Nb20Cu alloy has the highest Ti2Cu content, it was originally predicted to have the greatest hardness. According to the equilibrium phase diagram of the binary Ti-Cu system [31], the peritectic reaction (β Ti) + L → Ti2Cu occurs at 1005 °C in the composition range of 17.2% to 43.3% Cu. Most Ti2Cu present in the 10Nb20Cu alloy is Ti2Cu crystallized by a peritectic reaction during the cooling process of casting. According to previous studies on the microstructure of the 10Nb20Cu alloy, Ti2Cu surrounds the β and α grains [28]. Compared with other α + β + Ti2Cu alloys, the 10Nb20Cu alloy has abundant Ti2Cu, which is mainly crystallized; therefore, the effect of precipitation hardening of Ti2Cu on the 10Nb20Cu alloy is small. On the other hand, in relation to the strength of the region with the three-phase coexistence of α + β + Ti2Cu, its tensile strength did not improve because extensive precipitation of Ti2Cu led to less elongation.
The 30Nb-5Cu alloy was expected to exhibit greater elongation because it is a body-centered cubic crystal of β-Ti, but it did not. Its hardness is greater but its tensile strength is the same as that of Ti. Since a metastable ω phase, which is a brittle phase, was present in the dental cast Ti-30%Nb [12], some ω undetected by XRD may also exist in 30Nb5Cu. Cu acts as a β-phase stabilizer for Ti and shifts the α-β transformation temperature to the low-temperature side, making it easier for the ω-phase to appear. In addition, because the 30Nb5Cu alloy is located at the boundary between the β and β + Ti2Cu phases, it is possible that it contained Ti2Cu in amounts not detected by XRD. Ti2Cu precipitated when the amount of Cu added to the 30Nb5Cu alloy increased, and the alloy phase changed to β + Ti2Cu. Precipitation of Ti2Cu in the β matrix increased its hardness, but its strength decreased owing to the decrease in elongation. Other Ti-Nb-based ternary alloys, such as Ti-Nb-tin (Sn), Ti-Nb-molybdenum (Mo), and Ti-Nb-iron (Fe) alloys, have also been developed to enhance the performance of the Ti-Nb alloys of β titanium. Sn increases the strength of Ti-Nb alloys and lowers the elastic modulus of the alloy [32]. Fe increases the strength of Ti-Nb alloys, although the ω phase may precipitate depending on the composition and render the alloy embrittled [33,34]. Mo enhances the superelasticity of Ti-Nb alloys [35]. Thus, the various added elements have different roles and influence the alloy properties differently.

4.2. Dental Application of Ti-Nb-Cu Alloys

For dental application, the alloys must demonstrate elongation after fracture. ISO 22674 requires alloys to have an elongation of 2% or more [2]. Among the Ti-Nb-Cu alloys examined in this study, dimples, which are characteristic of ductile fracture, were observed on the fracture surfaces of compositions that satisfied the ISO criterion. The dimple size is affected by the properties of the matrix, second-phase particles, relative strength between the matrix and second-phase particles, and bonding strength of the interface [36]. The dimple size on the fracture surface of the compositions near β (20Nb5Cu and 15Nb5Cu) was larger than that near α (8Nb2Cu and 13Nb2Cu). The fracture surface images of the 20Nb5Cu alloy were very similar to those of the 18Nb2Cu and 24Nb1Cu alloys obtained in a previous study [24]. The fracture surface appeared to follow the main matrix phase. Although the elongation of the experimental alloys in this study was approximately 3–4%, which is by no means large, it is close to the elongation (approximately 3–5%) shown by typical α + β, Ti-6Al-4V, and Ti-6Al-7Nb alloys [37,38]. Because microshrinkage or porosities were observed in all samples, it is possible that the elongation was small owing to their influence. Alternatively, the solid solution of oxygen in the alloy during casting may have reduced the elongation. The melting point of Ti alloys decreases with the addition of Cu but increases with the addition of Nb [31]. A composition with high Nb content may have a higher melting point than Ti, which implies that it takes longer to melt, increasing the risk of oxidation during melting for casting. Based on this, the Ti-Nb-Cu alloy may be unsuitable for casting. Wrought Ti-Nb-Cu alloys should exhibit greater elongation. Machining wrought Ti-Nb-Cu alloys with CAD/CAM milling will result in better-performing prostheses. Although the machinability of the Ti-Nb-Cu alloys designed in this study was not investigated, some recently investigated Ti-Nb-Cu alloys exhibited improved grindability [25]. A common feature of Ti alloys with excellent grindability is the presence of a second phase instead of a single α phase [39]. The ductile Ti-Nb-Cu alloys in this study were α + β or α + Ti2Cu and were expected to have good machinability.
Considering the ISO criteria for metal dental materials, the yield strength and elongation of the 8Nb2Cu, 5Nb5Cu, 13Nb2Cu, and 10Nb5Cu alloys match types 4 and 5 and can be used for large prostheses and implant superstructures. In addition, the tensile strength of these alloys is equivalent to that of commercially pure grade 4 Ti (550–750 MPa) and American Society for Testing and Materials/American Society of Mechanical Engineers grade 4 (550 MPa or higher) used for narrow-diameter implants [1,40]; therefore, it is likely that these alloys could be used for narrow-diameter implants. The yield strengths of the 15Nb5Cu and 20Nb5Cu alloys satisfied the ISO type 3 criterion, but their elongation was insufficient. The hardness of the 8Nb2Cu and 13Nb2Cu alloys was comparable to that of hardened type 4 dental gold casting alloys (237–264) [1], and that of the 5Nb5Cu and 10Nb5Cu alloys was equal to or slightly lower than that of Ti-6Al-4V alloys (320–341) [1,41]. The hardness of the 15Nb5Cu and 20Nb5Cu alloys was equivalent to that of cobalt–chromium alloys (350–390) [1]. All Ti-Nb-Cu alloys had suitable hardness for dental applications.
Compositions with less than 1% elongation are unsuitable for clinical application. Among the Ti-Nb-Cu alloys described in this study, compositions with a Cu content of 7.5% or more did not exhibit sufficient elongation regardless of the Nb content. No dimples were observed on the fracture surfaces of these compositions after the tensile test, and either cleavage or pseudo-cleavage fractures were observed. Binary Ti-Cu alloys have shown a large drop in elongation at 5% Cu content and in brittleness at 10% Cu [13]. As an alloying element for Ti, Cu can effectively improve its strength and hardness with the addition of some Ag or Au, but the decrease in elongation is remarkable [13]. Therefore, the upper limit for the Cu content in the alloy should be 5%. The 15Nb5Cu and 20Nb5Cu alloys, in which dimples were observed, may exhibit greater elongation. If the elongation of these alloys increased slightly, they would match the ISO type 3 criteria, making them applicable in dentistry.
Copper cytotoxicity may be a concern for dental applications of Ti-Nb-Cu alloys. However, according to Takada et al., although the amount of Cu ions released from Ti2Cu was higher than that released from αTi in the NaCl solution, the amount released from Ti2Cu was 1/10 times smaller than that from type 4 gold alloys under the same conditions [18]. In addition, many studies aiming at implant applications have been conducted on binary Ti-Cu alloys, and good results have been achieved in many cases [21,22,23]. Therefore, Ti-Nb-Cu alloys should be suitable for dental applications.

5. Conclusions

In this study, we developed Ti-Nb-Cu alloys with an aim of improving their machining characteristics for dental applications. The 8Nb2Cu, 5Nb5Cu, 13Nb2Cu, and 10Nb5Cu Ti alloys demonstrated good potential for use in fabricating high-strength dental prostheses. We plan to investigate the machinability of these alloys in the future.

Author Contributions

Conceptualization, M.T.; investigation, M.T., K.S., and G.T.; data curation, M.T. and G.T.; funding acquisition, M.T.; writing—original draft preparation, M.T.; formal analysis, G.T.; methodology, K.S.; validation, K.S. and Y.T.; and writing—review and editing, K.S. and Y.T. All authors have read and agreed to the published version of the manuscript.

Funding

This study was partially supported by JSPS KAKENHI, grant number JP21K09930.

Data Availability Statement

The authors confirm that data supporting the findings of this study are available within the article.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript; or in the decision to publish the results.

References

  1. O’Brien, W.J. Tabulated Values of Physical and Mechanical Properties. Dental Materials and Their Selection, 3rd ed.; Quintessence Publishing: Carol Stream, IL, USA, 2002; pp. 309–390. [Google Scholar]
  2. ISO 22674; Dentistry—Metallic Materials for Fixed and Removable Restorations and Appliances. ISO: Geneva, Switzerland, 2016; pp. 1–36.
  3. Pommer, B.; Mailath-Pokorny, G.; Haas, R.; Buseniechner, D.; Millesi, W.; Fürhauser, R. Extra-short (<7mm) and extra-narrow diameter (<3.5mm) implants: A meta-analytic literature review. Eur. J. Oral. Implantol. 2018, 11, 137–146. [Google Scholar]
  4. Bordin, D.; Witek, L.; Fardin, V.P.; Bonfante, E.A.; Coelho, P.G. Fatigue failure of narrow implants with different implant-abutment connection designs. J. Prosthodont. 2018, 27, 659–664. [Google Scholar] [CrossRef] [PubMed]
  5. Osman, R.B.; Swain, M.V. A critical review of dental implant materials with an emphasis on titanium versus zirconia. Materials 2015, 8, 932–958. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  6. Domingo, J.L. Vanadium: A review of the reproductive and developmental toxicity. Reprod. Toxicol. 1996, 10, 175–182. [Google Scholar] [CrossRef]
  7. Bondy, S.C. The neurotoxicity of environmental aluminum is still an issue. Neurotoxicology 2010, 31, 575–581. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  8. Kikuchi, M.; Okuno, O. Machinability evaluation of titanium alloys. Dent. Mater. J. 2004, 23, 37–45. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  9. Tanzil, S.U.; Saifullah, K. A study on machinability of Ti6Al4V—Process and optimization. Tech. Rep. 2017, 1–21. [Google Scholar] [CrossRef]
  10. Ezugwu, E.O.; Wang, Z.M. Titanium alloys and their machinability—A review. J. Mater. Process. Technol. 1997, 68, 262–274. [Google Scholar] [CrossRef]
  11. Veiga, C.; Davim, J.P.; Loureiro, A. Review on machinability of titanium alloys: The process perspective. Rev. Adv. Mater. Sci. 2013, 34, 148–164. [Google Scholar]
  12. Kikuchi, M.; Takahashi, M.; Okuno, O. Mechanical properties and grindability of dental cast Ti-Nb alloys. Dent. Mater. J. 2003, 22, 328–342. [Google Scholar] [CrossRef] [Green Version]
  13. Takahashi, M.; Kikuchi, M.; Takada, Y.; Okuno, O. Mechanical properties and microstructures of dental cast Ti-Ag and Ti-Cu alloys. Dent. Mater. J. 2002, 21, 270–280. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  14. Kikuchi, M.; Takahashi, M.; Okabe, T.; Okuno, O. Grindability of dental cast Ti-Ag and Ti-Cu alloys. Dent. Mater. J. 2003, 22, 191–205. [Google Scholar] [CrossRef] [PubMed]
  15. Takahashi, M.; Kikuchi, M.; Okuno, O. Mechanical properties and grindability of experimental Ti-Au alloys. Dent. Mater. J. 2004, 23, 203–210. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  16. Takahashi, M.; Kikuchi, M.; Okuno, O. Grindability of dental cast Ti-Zr alloys. Mater. Trans. 2009, 50, 859–863. [Google Scholar] [CrossRef] [Green Version]
  17. Akbarpour, M.R.; Mirabad, H.M.; Hemmati, A.; Kim, H.S. Processing and microstructure of Ti-Cu binary alloys: A comprehensive review. Prog. Mater. Sci. 2022, 127, 100933. [Google Scholar] [CrossRef]
  18. Takada, Y.; Okuno, O. Corrosion characteristics of α-ti and Ti2Cu composing Ti-Cu alloys. Dent. Mater. J. 2005, 24, 610–616. [Google Scholar] [CrossRef] [Green Version]
  19. Zhang, E.; Ren, J.; Li, S.; Yang, L.; Qin, G. Optimization of mechanical properties, biocorrosion properties and antibacterial properties of as-cast Ti–Cu alloys. Biomed. Mater 2016, 11, 065001. [Google Scholar] [CrossRef]
  20. Korda, A.A.; Munawaroh, S.; Basuki, E.A. The antimicrobial activity and characterization of the cast titanium copper alloys with variations of copper content. IOP Conf. Ser. Mater. Sci. Eng. 2019, 547, 012002. [Google Scholar] [CrossRef] [Green Version]
  21. Wang, J.; Zhang, S.; Sun, Z.; Wang, H.; Ren, L.; Yang, K. Optimization of mechanical property, antibacterial property and corrosion resistance of Ti-Cu alloy for dental implant. J. Mater. Sci. Technol. 2019, 35, 2336–2344. [Google Scholar] [CrossRef]
  22. Zhang, W.; Zhang, S.; Liu, H.; Ren, L.; Wang, Q.; Zhang, Y. Effects of surface roughening on antibacterial and osteogenic properties of Ti-Cu alloys with different Cu contents. J. Mater. Sci. Technol. 2021, 88, 158–167. [Google Scholar] [CrossRef]
  23. Yi, C.B.; Ke, Z.Y.; Zhang, L.; Tan, J.; Jiang, Y.H.; He, Z. Antibacterial Ti-Cu alloy with enhanced mechanical properties as implant applications. Mater. Res. Express 2020, 7, 105404. [Google Scholar] [CrossRef]
  24. Takahashi, M.; Kikuchi, M.; Takada, Y. Mechanical properties and microstructures of dental cast Ti-6Nb-4Cu, Ti-18Nb-2Cu, and Ti-24Nb-1Cu alloys. Dent. Mater. J. 2016, 35, 564–570. [Google Scholar] [CrossRef]
  25. Takahashi, M.; Kikuchi, M.; Takada, Y. Grindability of Ti-Nb-Cu alloys for dental machining applications. Metals 2022, 12, 861. [Google Scholar] [CrossRef]
  26. Horiuchi, Y.; Nakayama, K.; Inamura, T.; Kim, H.Y.; Wakashima, K.; Miyazaki, S.; Hosoda, H. Effect of Cu addition on shape memory behavior of Ti-18 mol%Nb alloys. Mater. Trans. 2007, 48, 414–421. [Google Scholar] [CrossRef] [Green Version]
  27. Zhao, Z.; Xu, W.; Xin, H.; Yu, F. Microstructure, corrosion and anti-bacterial investigation of novel Ti-xNb-yCu alloy for biomedical implant application. J. Mater. Res. Technol. 2022, 18, 5212–5225. [Google Scholar] [CrossRef]
  28. Sato, K.; Takahashi, M.; Takada, Y. Construction of Ti-Nb-Ti2Cu pseudo-ternary phase diagram. Dent. Mater. J. 2020, 39, 422–428. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  29. Oda, Y. Forefront of dental application of titanium. J. Tokyo Dent. Coll. Soc. 2014, 114, 187–197. [Google Scholar]
  30. Eremenko, V.N.; Buyanov, Y.I.; Prima, S.B. Phase diagram of the system titanium-copper. Powder Met. Met. Ceram. 1966, 5, 494–502. [Google Scholar] [CrossRef]
  31. ASM International Alloy Phase Diagram and Handbook Committee. Section 2: Binary Alloy Phase Diagrams. In ASM Handbook Volume 3: Alloy Phase Diagrams; ASM Int.: Materials Park, OH, USA, 1992; pp. 180–307. [Google Scholar]
  32. Hsu, H.-C.; Wu, S.-C.; Hsu, S.-K.; Syu, J.-Y.; Ho, W.-F. The structure and mechanical properties of as-cast Ti–25Nb–xSn alloys for biomedical applications. Mater. Sci. Eng. A 2013, 568, 1–7. [Google Scholar] [CrossRef]
  33. Lee, C.M.; Ho, W.F.; Ju, C.P.; Chern Lin, J.H. Structure and properties of Titanium–25 niobium–x iron alloys. J. Mater. Sci. Mater. Med. 2002, 13, 695–700. [Google Scholar] [CrossRef]
  34. Hsu, H.-C.; Hsu, S.-K.; Wu, S.-C.; Lee, C.-J.; Ho, W.-F. Structure and mechanical properties of as-cast Ti–5Nb–xFe alloys. Mater. Charact. 2010, 61, 851–858. [Google Scholar] [CrossRef]
  35. Al-Zain, Y.; Kim, H.Y.; Hosoda, H.; Nam, T.H.; Miyazaki, S. Shape memory properties of Ti–Nb–Mo biomedical alloys. Acta Mater. 2010, 58, 4212–4223. [Google Scholar] [CrossRef]
  36. Mori, M. Dimple. J. High Press Inst. Jpn. 1974, 12, 232–235. [Google Scholar] [CrossRef]
  37. Aoki, T.; Okafor, I.C.I.; Watanabe, I.; Hattori, M.; Oda, Y.; Okabe, T. Mechanical properties of cast Ti-6Al-4V-XCu alloys. J. Oral Rehabil. 2004, 31, 1109–1114. [Google Scholar] [CrossRef] [PubMed]
  38. Kobayashi, E.; Doi, H.; Takahashi, M.; Nakano, T.; Yoneyama, T.; Hamanaka, H. Castability and mechanical properties of Ti-6Al-7Nb alloy dental-cast. JJ Dent. Mater. 1995, 14, 406–413. [Google Scholar]
  39. Kikuchi, M. Development of titanium alloys for dental CAD/CAM systems. Kagoshima Univ. Repos. 2014, 34, 41–51. [Google Scholar]
  40. ASM Committee on Titanium and Titanium Alloys. Introduction to Titanium and Its Alloys. In Metals Handbook, Properties and Selection: Stainless Steels, Tool Materials and Special-Purpose Metals Vol. 3, 9th ed.; ASM Press Int.: Materials Park, OH, USA, 1980; pp. 353–360. [Google Scholar]
  41. da Rocha, S.S.; Adabo, G.L.; Henriques, G.E.P.; Nóbilo, M.A.A. Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments. Braz. Dent. J. 2006, 17, 126–129. [Google Scholar] [CrossRef] [PubMed]
Jfb 13 00263 g001 550
Figure 1. Composition of experimental ternary Ti-Nb-Cu alloys. Black dots represent the compositions designed in this study.
Figure 1. Composition of experimental ternary Ti-Nb-Cu alloys. Black dots represent the compositions designed in this study.
Jfb 13 00263 g001
Jfb 13 00263 g002 550
Figure 2. Optical microscopy images of the etched Ti-Nb-Cu alloys.
Figure 2. Optical microscopy images of the etched Ti-Nb-Cu alloys.
Jfb 13 00263 g002
Jfb 13 00263 g003 550
Figure 3. Vickers hardness of the Ti-Nb-Cu alloys. Identical letters indicate a statistically insignificant difference (p > 0.05).
Figure 3. Vickers hardness of the Ti-Nb-Cu alloys. Identical letters indicate a statistically insignificant difference (p > 0.05).
Jfb 13 00263 g003
Jfb 13 00263 g004 550
Figure 4. Tensile and yield strengths of the Ti-Nb-Cu alloys. Identical letters indicate a statistically insignificant difference (p > 0.05).
Figure 4. Tensile and yield strengths of the Ti-Nb-Cu alloys. Identical letters indicate a statistically insignificant difference (p > 0.05).
Jfb 13 00263 g004
Jfb 13 00263 g005 550
Figure 5. Scanning electron micrographs of the fracture surface of Ti-Nb-Cu alloys after the tensile test.
Figure 5. Scanning electron micrographs of the fracture surface of Ti-Nb-Cu alloys after the tensile test.
Jfb 13 00263 g005
Jfb 13 00263 g006 550
Figure 6. Porosity in the fracture surface of the 5Nb5Cu alloy after the tensile test. The arrow indicates the pores.
Figure 6. Porosity in the fracture surface of the 5Nb5Cu alloy after the tensile test. The arrow indicates the pores.
Jfb 13 00263 g006
Jfb 13 00263 g007 550
Figure 7. Hardness and alloy phases of the Ti-Nb-Cu alloys. The black dots indicate data obtained in the present study, and the white dots represent data from previous studies.
Figure 7. Hardness and alloy phases of the Ti-Nb-Cu alloys. The black dots indicate data obtained in the present study, and the white dots represent data from previous studies.
Jfb 13 00263 g007
Jfb 13 00263 g008 550
Figure 8. Tensile strength and alloy phases of the Ti-Nb-Cu alloys. The black dots indicate data obtained in the present study, and the white dots represent data from previous studies.
Figure 8. Tensile strength and alloy phases of the Ti-Nb-Cu alloys. The black dots indicate data obtained in the present study, and the white dots represent data from previous studies.
Jfb 13 00263 g008
Table
Table 1. Alloy phases in Ti-Nb-Cu alloys identified by X-ray diffractometry.
Table 1. Alloy phases in Ti-Nb-Cu alloys identified by X-ray diffractometry.
CompositionAlloy Phase
Ti-8%Nb-2%Cuα + β
Ti-5%Nb-5%Cuα + Ti2Cu
Ti-13%Nb-2%Cuα + β
Ti-10%Nb-5%Cuα + Ti2Cu
Ti-5%Nb-10%Cuα + Ti2Cu
Ti-10%Nb-7.5%Cuα + β + Ti2Cu
Ti-15%Nb-5%Cuα + β
Ti-10%Nb-10%Cuα + β + Ti2Cu
Ti-20%Nb-5%Cuα + β
Ti-20%Nb-7.5%Cuα + β + Ti2Cu
Ti-20%Nb-10%Cuα + β + Ti2Cu
Ti-10%Nb-20%Cuα + β + Ti2Cu
Ti-30%Nb-5%Cuβ
Ti-30%Nb-7.5%Cuβ + Ti2Cu
Ti-30%Nb-10%Cuβ + Ti2Cu
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Takahashi, M.; Sato, K.; Togawa, G.; Takada, Y. Mechanical Properties of Ti-Nb-Cu Alloys for Dental Machining Applications. J. Funct. Biomater. 2022, 13, 263. https://doi.org/10.3390/jfb13040263

AMA Style

Takahashi M, Sato K, Togawa G, Takada Y. Mechanical Properties of Ti-Nb-Cu Alloys for Dental Machining Applications. Journal of Functional Biomaterials. 2022; 13(4):263. https://doi.org/10.3390/jfb13040263

Chicago/Turabian Style

Takahashi, Masatoshi, Kotaro Sato, Genichi Togawa, and Yukyo Takada. 2022. "Mechanical Properties of Ti-Nb-Cu Alloys for Dental Machining Applications" Journal of Functional Biomaterials 13, no. 4: 263. https://doi.org/10.3390/jfb13040263

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop