Magneto-Mechanical and Thermal Properties of Nd-Fe-B-Epoxy-Bonded Composite Materials
Previous Article in Special Issue
Nonlinear Mechanical Property of 3D Braided Composites with Multi-Types Micro-Distortion: A Quantitative Evaluation
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 15
Issue 8
10.3390/polym15081895
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Influence of Biochar and Bio-Oil Loading on the Properties of Epoxy Resin Composites

by
Pamela Hidalgo
1,*,
Luis Salgado
1,
Nayadeth Ibacache
2 and
Renato Hunter
2
1
Department of Industrial Processes, Faculty of Engineering, Universidad Católica de Temuco, Rudecindo Ortega 02950, Temuco 4780000, Chile
2
Department of Mechanical Engineering, Universidad de La Frontera, Casilla 54-D, Temuco 4811230, Chile
*
Author to whom correspondence should be addressed.
Polymers 2023, 15(8), 1895; https://doi.org/10.3390/polym15081895
Submission received: 1 March 2023 / Revised: 7 April 2023 / Accepted: 9 April 2023 / Published: 15 April 2023
(This article belongs to the Special Issue Resin-Based Polymer Materials and Related Applications)
Browse Figures
Versions Notes

Abstract

:
In this study, we evaluated the use of bio-oil and biochar on epoxy resin. Bio-oil and biochar were obtained from the pyrolysis of wheat straw and hazelnut hull biomass. A range of bio-oil and biochar proportions on the epoxy resin properties and the effect of their substitution were investigated. TGA curves showed improved thermal stability for degradation temperature at the 5% (T5%), 10% (T10%), and 50% (T50%) weight losses on bioepoxy blends with the incorporation of bio-oil and biochar with respect to neat resin. However, decreases in the maximum mass loss rate temperature (Tmax) and the onset of thermal degradation (Tonset) were obtained. Raman characterization showed that the degree of reticulation with the addition of bio-oil and biochar does not significantly affect chemical curing. The mechanical properties were improved when bio-oil and biochar were incorporated into the epoxy resin. All bio-based epoxy blends showed a large increase in Young’s modulus and tensile strength with respect to neat resin. Young’s modulus was approximately 1955.90 to 3982.05 MPa, and the tensile strength was between 8.73 and 13.58 MPa for bio-based blends of wheat straw. Instead, in bio-based blends of hazelnut hulls, Young´s modulus was 3060.02 to 3957.84 MPa, and tensile strength was 4.11 to 18.11 Mpa.

1. Introduction

In recent years, many efforts have been devoted to utilizing lignocellulosic biomass as a valuable chemical resource for synthesizing polymers. Different methods have been developed to obtain a wide range of products from biomass, such as chemical and thermochemical processes [1]. Thermochemical processes mainly used for converting biomass into chemicals are combustion, pyrolysis, gasification, and liquefaction [2,3]. For example, some researchers have attempted to substitute liquefied wood with epoxy resin. Liquefied wood has high reactivity because of the large amount of phenolic OH groups and alcoholic OH groups [1,4,5,6]. Other studies reported the use of wood pyrolysis bio-oil [7,8].
In general, wood pyrolysis bio-oil is composed of water, acids, alcohols, aldehydes, esters, ketones, phenols, guaiacols, syringols, furans, lignin-derived phenols, and extractible terpenes with multifunctional groups [9,10,11,12]. Wood pyrolysis bio-oil is use since it contains phenols, aromatic hydrocarbons, and neutral components that can be substituted in the epoxy resin [13,14]. The availability of bio-oil -OH groups to epoxy resin is important in the cross-linking process, which is attributable to the reaction between the epoxide and hydroxyl (-OH) of bio-oil, which is an important factor that influences the bonding ability of the modified resin [8].
Moreover, epoxy resins are very versatile in nature. They are one of the most important classes of thermosetting polymers and are widely used as matrices for fiber-reinforced composite materials and as structural adhesives [15]. They are amorphous, highly cross-linked polymers, and this structure results in these materials possessing various desirable properties, such as greater tensile strength and modulus, uncomplicated processing, fine thermal and chemical resistance, and dimensional stability [16]. However, higher costs and brittleness limit its application in industry [17]. To improve its properties, fillers and additives have been incorporated, such as silica nanoparticles, montmorillonite, granite powder, carbon nanotubes, and wood dust [18,19,20]. It has been proven that the effect of wood dust on mechanical properties increases [15], and carbon nanotube/epoxy nanocomposite reinforcement improves thermal and mechanical properties [19,20]. Moreover, the effect of modifiers such as resorcinol phenyl phosphate on mineral fillers such as diorite on the physicochemical and deformation strength properties of epoxy-based composites has been studied [18].
At the same time, in the past few decades, research and engineering interest has been focused on the use of lignocellulosic biomass for obtaining green composites due to its recyclability and biodegradability, such as the use of wood pyrolysis bio-oils and biochar on the properties of epoxy composites.
Wood pyrolysis bio-oils (or liquid fraction) are obtained from biomass pyrolysis under anoxic conditions (non-oxidizing atmospheres) at high temperatures (~500 °C). Pyrolysis is one process of thermal decomposition of the biomass organic matrix resulting in the conversion of biomass into energy and chemical products, consisting of bio-oil, biochar, and non-condensable gas products (pyrolytic gas) [2]. Depending on the heating rate and residence time, aimed at maximizing either the bio-oil or biochar yields, biomass pyrolysis can be classified into three main types: slow or conventional, fast, and flash pyrolysis. [2,21,22,23,24].
Biochar has been used traditionally as a soil amendment due to its high nutrient contents (macro- and micro-nutrients). The concentration of respective nutrient elements varies over a wide range, depending primarily on the biomass type and pyrolysis conditions [21,25,26]. Recently, it has been used in materials applications, such as carbon fillers, because of its ability to improve the mechanical, electrical, and thermal properties of the final product [27,28,29]. With respect to bio-oil, studies have focused on blending it with epoxy resin. The results from these findings have confirmed the comparative lap-shear strength of bio-oil-based epoxy resins to commercial-grade epoxy resin and higher resistance to moisture [7].
This manuscript studies the use of pyrolytic products in epoxy resin composites. The effect of different biochar and bio-oil loadings on the epoxy composite was studied. Bio-oil and biochar were blended into the resin to form a cross-linked copolymer network structure, where the degree of reticulation, thermal stability, and mechanical performance were analyzed. This work provides an alternative for biomass revaluation of wheat straw and hazelnut hulls through pyrolysis to develop a novel epoxy resin cross-linked with bio-oil and biochar, thus analyzing the effect of pyrolytic products on the properties of the epoxy composite.

2. Materials and Methods

2.1. Methodology

Wheat straw and hazelnut hulls, and residual biomass generated in southern Chile, were used for the production of bio-oil and biochar. The epoxy resin, bisphenol A diglycidyl ether (DGEBA, molecular weight: 340.41 g/mol, CAS N° 1675-54-3) and tetraethylene entaamine (TEPA, molecular weight: 189.3 g/mol CAS N° 112-57-2), used as curing agents, were purchased from Sigma–Aldrich (Santiago, Chile). All chemicals were used as received and were of reagent grade.

2.2. Experimental Setup and Procedure

2.2.1. Pyrolysis of Biomass

The biomass of wheat straw and hazelnut hulls was converted into biochar and bio-oil using a slow pyrolysis process operated under atmospheric pressure, with heating controlled by a data acquisition instrument. The pyrolysis of the samples was carried out at a temperature of 600 °C, with a residence time of the biomass in the pyrolyzer of approximately 3 h to ensure complete conversion. The reactor was continuously injected with nitrogen (1000 mL min−1). Then, the biochar was separated, milled, and fractioned using a sieve N°200 (U.S.A. Standard testing sieve, size < 75 µm). The bio-oil was collected and filtered to remove char particles using #1 Whatman paper. The characterization of pyrolysis products is shown in Table 1 and Table 2.
Compounds in bio-oil shown Table 2 were analyzed on a gas chromatograph (GC–MS-QP 2010 PLUS, Shimadzu, Kyoto, Japan), and it was configured under the following conditions: an HP5-MS fused silica capillary column (30 m × 0.25 mm × 0.25 mm); an oven temperature starting at 308 °K, rising to 453 °K at 5 °K min−1, and then up to 573 °K at 20 °K min−1; an injector temperature of 523 °K; helium (99.999%) used as a carrier gas at pressure mode control (10 kPa) and a flow rate of 0.56 cm3 min−1; a transfer line and ion source at 523 °K; electron energy at 70 eV. A quadrupole mass detector was operated in electron impact ionization mode. Data were obtained using the software GCMS solution (v2.53) and mass spectra databases (NIST08 and NIST08s). The samples were prepared by diluting 20 mg of bio-oil in 1 mL of acetone as the solvent, and fluoranthene was used as an internal standard.

2.2.2. Preparation of Bio-Based Epoxy Blends

The epoxy resin was blended with bio-oil at weight proportions of 5% and 10%. Acetone pretreatment of the samples (bio-oil/DGEBA) was carried out according to Liu et al. (2017). The pretreated mixtures were then blended with biochar at weight proportions of 5% and 10% (as shown in Table 2) and then used in the preparation of bio-based epoxy blends.
Bio-based epoxy blends were prepared using TEPA as a curing agent. The bio-oil/DGEBA/biochar mixture and curing agent were homogeneously mixed in 1:0.1 weight proportions and then stirred for 10 min until a complete dispersion of biochar was reached. The dispersion of biochar is challenging due to the dense nature of the epoxy resin because increasing the weight fraction of biochar in epoxy increases the viscosity of epoxy [31]. Subsequently, blends were degassed in a vacuum desiccator attached to a vacuum pump to remove the entrapped air, poured into a silicone mold, cured at 50 °C for 8 h, postcured at 65 °C for 12 h in an oven (Memmert UF-260 universal), and stored at room temperature.

2.3. Analytical Techniques

2.3.1. Thermogravimetric Analysis (TGA)

The thermal degradation of the bio-based epoxy blends was carried out using a thermogravimetric analyzer (DTG-60H, Shimadzu). Twenty milligrams of the sample was heated from 20 to 800 °C at a 10 °C/min heating rate under a nitrogen atmosphere. The weight loss of the sample was recorded as a function of the temperature.
In this way, the onset degradation temperature (Tonset), the end degradation temperature (Tendset), the temperature associated with a mass loss of 5%, 10%, and 50% (T5%, T10%, and T50%), the maximum mass loss rate temperature (Tmax), and the residual mass at 800 °C (Rm800) were determined.

2.3.2. Raman Spectroscopy

All the samples were prepared according to the previous procedure for bio-based epoxy blends, using TEPA as a curing agent. The Raman spectra were registered using the Unchained Labs Raman spectrometer (model Hound, equipped with the 785 nm laser line). The samples were manually placed, and spectra were recorded from 300 to 3300 cm−1 with 1.5 cm−1 resolution. The laser spot was focused onto the sample by a 50× magnification objective lens of an Olympus microscope. The degree of reticulation (α) using the Raman spectra was calculated as:
∝ = 100 ∗ I 1275 O − I 1275 t I 1275   O
where I 1275   O is the normalized intensity of the 1275 cm−1 peak at the beginning and I 1275 t is the normalized intensity at time t. The peaks were normalized by dividing their intensities by that of the 1160 cm−1 peak corresponding to the phenyl ring [32].

2.3.3. Mechanical Analysis

Mechanical properties (tensile strength, tensile deformation, and modulus) were determined in a universal testing machine (model 3369, INSTRON, Norwood, MA, USA) and were evaluated according to ASTM D638. A type IV test specimen with a thickness of 4 mm was used (Figure 1). The samples were prepared using TEPA as a curing agent and were poured into a silicone mold according to the model for their preparation. The curing process was implemented in a Memmert UF-260 universal oven (Memmert, Schwabach, Germany) for 8 h at 50 °C and postcured at 65 °C for 12 h. Data acquisition and processing were performed using Instron Bluehill® Lite (version 2.24) software. The tests were performed at room temperature, considering a constant displacement speed of 1 mm/min. An extensometer was used to measure specimen displacement.

3. Results and Discussion

3.1. Thermal Degradation Properties

Figure 2 shows variations in the TGA and derivative TGA (DTGA) curves of neat epoxy resin and the bio-based epoxy blends. The temperatures corresponding to mass loss are presented in Table 3. The first step of the TGA curve is attributable to the dehydration of water, which occurs between room temperature and 120 °C [33]. The weight loss during the dehydration stage was approximately 7% for neat resin and 2% for bio-based epoxy blends of wheat straw. The neat epoxy resin showed Tonset at 320 °C and Tendset at 420 °C, with 3.04% residual mass. For blends of wheat straw, Tonset was between 295 and 320 °C, Tendset was approximately 420 °C, and the residual mass was between 2.76 and 15.05%, indicating that the addition of biochar and bio-oil produced a change in the thermal degradation. The Tendset values are practically unaffected by biochar and bio-oil addition, as opposed to Tonset.
For blends of hazelnut hulls, Tonset was between 300 and 325 °C, Tendset was approximately 400 °C, and the residual mass was between 12.05 and 15.50%.
In addition, T5%, T10%, and T50% progressively increased with bio-oil and biochar incorporation with respect to neat resin. Higher T50% values with 10% bio-oil were observed independent of the biochar dosage of wheat straw, and T5% and T10% values slightly increased with increasing biochar dosage. This can be due to aromatic compounds of bio-oil, such as phenolic hydroxyls, that could react with the epoxy groups of resin, increasing the thermal stability [8], and the bio-oil of wheat straw has higher aromatic compounds than the bio-oil of hazelnut hull (such as phenol and aromatic hydrocarbons), as shown in Table 2. Bio-oil of the hazelnut hulls contained 35.47% aromatic compounds instead of 43.04% of the bio-oil of wheat straw that could be substituted in the epoxy resin.
From the DTGA curves, the maximum mass loss rate temperature (Tmax) reached was 365.72 °C in the neat resin, which is attributable to the degradation of the epoxy group. However, the addition of bio-oil and biochar produced a lower degradation resistance with respect to the neat epoxy resin, as observed in the derivative mass loss curves, diminishing the temperature associated with the maximum mass loss rate. The residual mass to 800 °C for neat epoxy resin was near 3%. However, in general, bio-oil and biochar incorporation led to an increase in Rm800.

3.2. Cross-Linking Analysis

Figure 3 shows the Raman spectra of uncured DGEBA, cured DGEBA, and cured bio-based epoxy blends. The Raman band corresponding to epoxide vibration is at 1275 cm−1, and the intensity of this peak is linearly dependent on the concentration of epoxide groups in the resin mixture [32,34]. During chemical curing, epoxide groups in epoxy resin react with hardeners, forming a highly cross-linked three-dimensional network, diminishing the peak intensity at 1275 cm−1 corresponding to the epoxide group, as observed in the Raman spectra of cured DGEBA and cured bio-based epoxy blends. This can be interpreted as the consumption of the free epoxide groups during the vitrification of the epoxy resin curing process [35]. In addition, a -CH2 stretching band at 2835 cm−1 associated with the formed link between the amine group of the hardener and the epoxy group of the resin has been observed in cured samples [36]. With respect to the Raman band of the -OH group present in the bio-oil, the region that appears, in accordance with the literature, is approximately 3000–3500 cm−1 [37,38,39,40,41]. However, this band is not observed in the samples. This confirmed the consumption of -OH groups upon reaction with DGEBA to generate a chemical bond [8]. Biochar infiltrates into resin through its pores, forming strong bonding, producing an increase in mechanical properties and enhancing cross-linking [28]. Other Raman peaks at 1112 cm−1, 1186 cm−1, and 1608 cm−1 are assigned to resin backbone vibrations that remain unchanged throughout the curing reaction. Raman peaks at 1112 cm−1 and 1186 cm−1 correspond to the C–C stretch. The Raman peak at 1608 cm−1 is assigned to the stretching of the phenyl ring [42]
The degree of crosslinking in the bio-based epoxy blend is approximately 70%, comparable to 72.161% of cured neat epoxy resin. This could indicate that bio-oil containing mainly phenols and aromatic hydrocarbons was substituted into the epoxy resin. Thus, incorporating bio-oil and biochar slightly modifies the epoxy group’s degree of reticulation (see Table 4). The addition of bio-oil and biochar does not significantly affect the mobility of molecules in chemical curing. The mobility of molecules diminishes during the curing process, thus increasing the degree of cross-linking [43,44].
For the bio-based epoxy blend, when increasing the biochar and bio-oil content obtained from wheat straw from 5% to 10%, a slight increase in the degree of crosslinking, approximately 70 to 72%, respectively, was observed. Moreover, in samples with 5% and 10% biochar, and with 5% bio-oil obtained from hazelnut hull, a mild decrease in the degree of crosslinking was observed. This could be due to the higher particle size of biochar. Instead, for a bio-oil content of 10%, no significant change in the degree of crosslinking was observed. This is indicative that aromatic compounds of bio-oil react with the epoxy group.

3.3. Mechanical Properties

Figure 4 shows the stress–strain curves of the neat epoxy resin and bio-based epoxy blends of wheat straw and hazelnut hulls. Table 5 shows the mechanical properties of the samples tested. All bio-based epoxy blends with biochar and bio-oil show a high increase in Young’s modulus with respect to neat resin. Young´s modulus was approximately 1955.90–3982.05 MPa for bio-based blends of wheat straw and 3060.02–3957.84 MPa for hazelnut hull.
With respect to tensile strength, in general, an increase was observed with respect to neat resin. For epoxy blends, biochar-bio-oil from wheat straw was in the range of 8.73 and 13.58 MPa. Instead, tensile strength was 4.11 and 18.11 Mpa for blends with biochar and bio-oil from hazelnut hulls. However, a low tensile strength was observed when a 5:10 proportion of bio-oil:biochar (BO5BC10) was added to the epoxy resin of hazelnut hulls. This proportion produced a decrease in cross-linking of the sample (as shown in Table 4), which could be due to deviation from the optimal stoichiometric ratio, leading to a reduction in tensile strength. For optimum cross-linking to occur, without affecting its properties, the precise molar ratio of the epoxy to hydroxyl group blend is critical before curing, while ensuring the highest thermal and mechanical properties of the bio-modified polymer [13,45].
Moreover, an increase in tensile strength with the addition of biochar at 5 to 10% was observed, with a higher use of biochar from hazelnut hull as a filler. This increase could be due to biochar particle size. The filler particle size of biochar of hazelnut hulls is higher than that of wheat straw, as shown in Table 1. The filler particle size is another important factor that contributes to composite properties. It has been reported that the particle size of filler can greatly alter composite properties, and a decrease in mechanical properties has been observed with very small particle sizes. This decrease is because of greater interfacial adhesion between the matrix, and filler having a smaller particle size [46]. Moreover, a factor contributing to the decline in tensile strength is the aspect ratio of the filler [47]. A larger aspect ratio decreases the tensile modulus of the composite, and this increases with particle size [48,49].

4. Conclusions

Bio-oil and biochar were successfully incorporated into epoxy resin, increasing mechanical properties, such as tensile strength and Young’s modulus with respect to neat resin. The aromatic compounds of the bio-oil participated in the cross-linked network and did not significantly modify the degree of cross-linking with the increase in bio-oil. Moreover, biochar improves the mechanical properties with respect to neat resin, but this improvement is more significant using smaller filler particle sizes. A decreased thermal stability upon the addition of biochar and bio-oil compared to the thermal degradation of the neat polymer was observed. The onset of thermal degradation for neat resin was observed at 320 °C; however, with the addition of biochar and bio-oil, the temperature for degradation was between 295 °C and 325 °C, and within 2.95% and 15.50% biochar content. This study is industrially novel because the greatest improvement has occurred in mechanical properties with bio-oil and biochar incorporation into epoxy resin without the risk of diminishing thermal properties.

Author Contributions

P.H.: Writing—original draft, Conceptualization, Methodology, Investigation, Project administration, Funding acquisition; L.S.: Investigation, Formal analysis; R.H.: Writing—review & editing. N.I.: Formal analysis. All authors have read and agreed to the published version of the manuscript.

Funding

This work was funded by CONICYT- FONDECYT Project N° 11221146.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare that they have no known competing financial interest or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Kobayashi, M.; Tukamoto, K.; Tomita, B. Application of Liquefied Wood to a New Resin System—Synthesis and Properties of Liquefied Wood/Epoxy Resins. Holzforschung 2000, 54, 93–97. [Google Scholar] [CrossRef]
  2. Kan, T.; Strezov, V.; Evans, T.J. Lignocellulosic biomass pyrolysis: A review of product properties and effects of pyrolysis parameters. Renew. Sustain. Energy Rev. 2016, 57, 1126–1140. [Google Scholar] [CrossRef]
  3. Elliott, D.; Beckman, D.; Bridgwater, A.; Diebold, J.; Gevert, S.; Solantausta, Y. Developments in direct thermochemical liquefaction of biomass: 1983–1990. Energy Fuels 1991, 5, 399–410. [Google Scholar] [CrossRef]
  4. Kishi, H.; Akamatsu, Y.; Noguchi, M.; Fujita, A.; Matsuda, S.; Nishida, H. Synthesis of epoxy resins from alcohol-liquefied wood and the mechanical properties of the cured resins. J. Appl. Polym. Sci. 2011, 120, 745–751. [Google Scholar] [CrossRef]
  5. Kishi, H.; Fujita, A.; Miyazaki, H.; Matsuda, S.; Murakami, A. Synthesis of wood-based epoxy resins and their mechanical and adhesive properties. J. Appl. Polym. Sci. 2006, 102, 2285–2292. [Google Scholar] [CrossRef]
  6. Wu, C.-C.; Lee, W.-J. Curing behavior and adhesion properties of epoxy resin blended with polyhydric alcohol-liquefied Cryptomeria japonica wood. Wood Sci. Technol. 2011, 45, 559–571. [Google Scholar] [CrossRef]
  7. Asafu-Adjaye, O.A.; Street, J.; Bansode, A.; Auad, M.L.; Peresin, M.S.; Adhikari, S.; Liles, T.; Via, B.K. Fast Pyrolysis Bio-Oil-Based Epoxy as an Adhesive in Oriented Strand Board Production. Polymers 2022, 14, 1244. [Google Scholar] [CrossRef]
  8. Liu, Y.; Via, B.K.; Pan, Y.; Cheng, Q.; Guo, H.; Auad, M.L.; Taylor, S. Preparation and characterization of epoxy resin cross-linked with high wood pyrolysis bio-oil substitution by acetone pretreatment. Polymers 2017, 9, 106. [Google Scholar] [CrossRef] [Green Version]
  9. Mao, A.; Shi, S.Q.; Steele, P. Flakeboard bonded with polymeric diphenylmethane diisocyanate/bio-oil adhesive systems. For. Prod. J. 2011, 61, 240–245. [Google Scholar] [CrossRef]
  10. Hilten, R.N.; Das, K. Comparison of three accelerated aging procedures to assess bio-oil stability. Fuel 2010, 89, 2741–2749. [Google Scholar] [CrossRef]
  11. Pütün, A.E.; Özcan, A.; Pütün, E. Pyrolysis of hazelnut shells in a fixed-bed tubular reactor: Yields and structural analysis of bio-oil. J. Anal. Appl. Pyrolysis 1999, 52, 33–49. [Google Scholar] [CrossRef]
  12. Paul, A.S.; Panwar, N.L.; Salvi, B.L.; Jain, S.; Sharma, D. Experimental investigation on the production of bio-oil from wheat straw. Energy Sources Part A Recovery Util. Environ. Eff. 2020, 1–16. [Google Scholar] [CrossRef]
  13. Wei, N.; Via, B.K.; Wang, Y.; McDonald, T.; Auad, M.L. Liquefaction and substitution of switchgrass (Panicum virgatum) based bio-oil into epoxy resins. Ind. Crops Prod. 2014, 57, 116–123. [Google Scholar] [CrossRef]
  14. Xu, J.; Brodu, N.; Mignot, M.; Youssef, B.; Taouk, B. Synthesis and characterization of phenolic resins based on pyrolysis bio-oil separated by fractional condensation and water extraction. Biomass Bioenergy 2022, 159, 106393. [Google Scholar] [CrossRef]
  15. Kumar, R.; Kumar, K.; Sahoo, P.; Bhowmik, S. Study of mechanical properties of wood dust reinforced epoxy composite. Procedia Mater. Sci. 2014, 6, 551–556. [Google Scholar] [CrossRef] [Green Version]
  16. Song, X.; Zheng, S.; Huang, J.; Zhu, P.; Guo, Q. Miscibility, morphology and fracture toughness of tetrafunctional epoxy resin/poly (styrene-co-acrylonitrile) blends. J. Mater. Sci. 2000, 35, 5613–5619. [Google Scholar] [CrossRef]
  17. Pan, Y.; Pan, Y.; Cheng, Q.; Liu, Y.; Essien, C.; Via, B.; Wang, X.; Sun, R.; Taylor, S. Characterization of epoxy composites reinforced with wax encapsulated microcrystalline cellulose. Polymers 2016, 8, 415. [Google Scholar] [CrossRef] [Green Version]
  18. Bekeshev, A.; Mostovoy, A.; Kadykova, Y.; Akhmetova, M.; Tastanova, L.; Lopukhova, M. Development and analysis of the physicochemical and mechanical properties of diorite-reinforced epoxy composites. Polymers 2021, 13, 2421. [Google Scholar] [CrossRef]
  19. Bao, X.; Wu, F.; Wang, J. Thermal degradation behavior of epoxy resin containing modified carbon nanotubes. Polymers 2021, 13, 3332. [Google Scholar] [CrossRef]
  20. Hameed, A.; Islam, M.; Ahmad, I.; Mahmood, N.; Saeed, S.; Javed, H. Thermal and mechanical properties of carbon nanotube/epoxy nanocomposites reinforced with pristine and functionalized multiwalled carbon nanotubes. Polym. Compos. 2015, 36, 1891–1898. [Google Scholar] [CrossRef]
  21. Balat, M.; Balat, M.; Kırtay, E.; Balat, H. Main routes for the thermo-conversion of biomass into fuels and chemicals. Part 1: Pyrolysis systems. Energy Convers. Manag. 2009, 50, 3147–3157. [Google Scholar] [CrossRef]
  22. Demirbas, M.F.; Balat, M. Biomass pyrolysis for liquid fuels and chemicals: A review. J. Sci. Ind. Res. 2007, 66, 797–804. [Google Scholar]
  23. Akhtar, J.; Amin, N.S. A review on operating parameters for optimum liquid oil yield in biomass pyrolysis. Renew. Sustain. Energy Rev. 2012, 16, 5101–5109. [Google Scholar] [CrossRef]
  24. Zhang, S.; Yan, Y.; Li, T.; Ren, Z. Upgrading of liquid fuel from the pyrolysis of biomass. Bioresour. Technol. 2005, 96, 545–550. [Google Scholar] [CrossRef] [PubMed]
  25. Hossain, M.K.; Strezov, V.; Chan, K.Y.; Ziolkowski, A.; Nelson, P.F. Influence of pyrolysis temperature on production and nutrient properties of wastewater sludge biochar. J. Environ. Manag. 2011, 92, 223–228. [Google Scholar] [CrossRef]
  26. Lee, Y.; Park, J.; Ryu, C.; Gang, K.S.; Yang, W.; Park, Y.-K.; Jung, J.; Hyun, S. Comparison of biochar properties from biomass residues produced by slow pyrolysis at 500 C. Bioresour. Technol. 2013, 148, 196–201. [Google Scholar] [CrossRef] [PubMed]
  27. Giorcelli, M.; Savi, P.; Khan, A.; Tagliaferro, A. Analysis of biochar with different pyrolysis temperatures used as filler in epoxy resin composites. Biomass Bioenergy 2019, 122, 466–471. [Google Scholar] [CrossRef]
  28. Matykiewicz, D. Biochar as an effective filler of carbon fiber reinforced bio-epoxy composites. Processes 2020, 8, 724. [Google Scholar] [CrossRef]
  29. Minugu, O.P.; Gujjala, R.; Shakuntala, O.; Manoj, P.; Chowdary, M.S. Effect of biomass derived biochar materials on mechanical properties of biochar epoxy composites. Proc. Inst. Mech. Eng. Part C J. Mech. Eng. Sci. 2021, 235, 5626–5638. [Google Scholar] [CrossRef]
  30. Hidalgo, P.; Navia, R.; Hunter, R.; Coronado, G.; Gonzalez, M. Synthesis of carbon nanotubes using biochar as precursor material under microwave irradiation. J. Environ. Manag. 2019, 244, 83–91. [Google Scholar] [CrossRef]
  31. Shahabaz, S.; Mehrotra, P.; Kalita, H.; Sharma, S.; Naik, N.; Noronha, D.J.; Shetty, N. Effect of Al2O3 and SiC Nano-Fillers on the Mechanical Properties of Carbon Fiber-Reinforced Epoxy Hybrid Composites. J. Compos. Sci. 2023, 7, 133. [Google Scholar] [CrossRef]
  32. Merad, L.; Cochez, M.; Margueron, S.; Jauchem, F.; Ferriol, M.; Benyoucef, B.; Bourson, P. In-situ monitoring of the curing of epoxy resins by Raman spectroscopy. In New Achievements in Materials and Environmental Sciences Names; EDP Sciences: Les Ulis, France, 2007; pp. 155–158. [Google Scholar]
  33. Rowell, R.M. Handbook of Wood Chemistry and Wood Composites; CRC Press: Boca Raton, FL, USA, 2005. [Google Scholar]
  34. Lyon, R.; Chike, K.; Angel, S. In situ cure monitoring of epoxy resins using fiber-optic Raman spectroscopy. J. Appl. Polym. Sci. 1994, 53, 1805–1812. [Google Scholar] [CrossRef]
  35. Vašková, H.; Křesálek, V. Raman spectroscopy of epoxy resin crosslinking. In Proceedings of the 13th WSEAS International Conference on Automation Control, Modeling & Simulation (ACMOS’11), Lanzarote, Canary Islands, Spain, 27–29 May 2011. [Google Scholar]
  36. Farquharson, S.; Smith, W.; Rose, J.; Shaw, M. Correlations between molecular (Raman) and macroscopic (rheology) data for process monitoring of thermoset composite. J. Process Anal. Chem. 2002, 7, 45–53. [Google Scholar]
  37. Adar, F. Introduction to interpretation of Raman spectra using database searching and functional group detection and identification. Spectroscopy 2016, 31, 16–23. [Google Scholar]
  38. Marina, A.; Man, Y.C.; Amin, I. Virgin coconut oil: Emerging functional food oil. Trends Food Sci. Technol. 2009, 20, 481–487. [Google Scholar] [CrossRef]
  39. Pershin, S. Raman spectroscopy of the OH group vibrations in structural complexes of liquid water. Opt. Spectrosc. 2005, 98, 543–554. [Google Scholar] [CrossRef]
  40. Bock, P.; Gierlinger, N. Infrared and Raman spectra of lignin substructures: Coniferyl alcohol, abietin, and coniferyl aldehyde. J. Raman Spectrosc. 2019, 50, 778–792. [Google Scholar] [CrossRef]
  41. Lukić, I.; Kesić, Ž.; Zdujić, M.; Skala, D. Vegetable oil as a feedstock for biodiesel synthesis. In Vegetable Oil; Holt, B., Ed.; Nova Science Publishers, Inc.: Hauppauge, NY, USA, 2016; pp. 83–128. [Google Scholar]
  42. Hardis, R.; Jessop, J.L.; Peters, F.E.; Kessler, M.R. Cure kinetics characterization and monitoring of an epoxy resin using DSC, Raman spectroscopy, and DEA. Compos. Part A Appl. Sci. Manuf. 2013, 49, 100–108. [Google Scholar] [CrossRef] [Green Version]
  43. Okabe, T.; Oya, Y.; Tanabe, K.; Kikugawa, G.; Yoshioka, K. Molecular dynamics simulation of crosslinked epoxy resins: Curing and mechanical properties. Eur. Polym. J. 2016, 80, 78–88. [Google Scholar] [CrossRef] [Green Version]
  44. Baroncini, E.A.; Kumar Yadav, S.; Palmese, G.R.; Stanzione, J.F., III. Recent advances in bio-based epoxy resins and bio-based epoxy curing agents. J. Appl. Polym. Sci. 2016, 133, 44103. [Google Scholar] [CrossRef] [Green Version]
  45. Auad, M.L.; Nutt, S.R.; Stefani, P.M.; Aranguren, M.I. Rheological study of the curing kinetics of epoxy–phenol novolac resin. J. Appl. Polym. Sci. 2006, 102, 4430–4439. [Google Scholar] [CrossRef]
  46. Spanoudakis, J.; Young, R. Crack propagation in a glass particle-filled epoxy resin: Part 1 Effect of particle volume fraction and size. J. Mater. Sci. 1984, 19, 473–486. [Google Scholar] [CrossRef]
  47. Ogunsona, E.O.; Misra, M.; Mohanty, A.K. Sustainable biocomposites from biobased polyamide 6, 10 and biocarbon from pyrolyzed miscanthus fibers. J. Appl. Polym. Sci. 2017, 134, 44221. [Google Scholar] [CrossRef]
  48. Tandon, G.P.; Weng, G.J. The effect of aspect ratio of inclusions on the elastic properties of unidirectionally aligned composites. Polym. Compos. 1984, 5, 327–333. [Google Scholar] [CrossRef]
  49. Das, C.; Tamrakar, S.; Kiziltas, A.; Xie, X. Incorporation of biochar to improve mechanical, thermal and electrical properties of polymer composites. Polymers 2021, 13, 2663. [Google Scholar] [CrossRef]
Polymers 15 01895 g001 550
Figure 1. Geometric dimensions of dogbone specimens Type IV (ASTM D638).
Figure 1. Geometric dimensions of dogbone specimens Type IV (ASTM D638).
Polymers 15 01895 g001
Polymers 15 01895 g002 550
Figure 2. TGA (a) and derivative weight loss (DTGA) (b) curves for cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of wheat straw. TGA (c) and derivative weight loss (DTGA) (d) curves for cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of hazelnut hulls.
Figure 2. TGA (a) and derivative weight loss (DTGA) (b) curves for cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of wheat straw. TGA (c) and derivative weight loss (DTGA) (d) curves for cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of hazelnut hulls.
Polymers 15 01895 g002
Polymers 15 01895 g003a 550Polymers 15 01895 g003b 550
Figure 3. Raman spectra of (a) uncured neat epoxy resin (DGEBA), cured neat epoxy resin (DGEBA), and cured bio-based epoxy blends of wheat straw and (b) uncured neat epoxy resin (DGEBA), cured neat epoxy resin (DGEBA), and cured bio-based epoxy blends of hazelnut hulls.
Figure 3. Raman spectra of (a) uncured neat epoxy resin (DGEBA), cured neat epoxy resin (DGEBA), and cured bio-based epoxy blends of wheat straw and (b) uncured neat epoxy resin (DGEBA), cured neat epoxy resin (DGEBA), and cured bio-based epoxy blends of hazelnut hulls.
Polymers 15 01895 g003aPolymers 15 01895 g003b
Polymers 15 01895 g004a 550Polymers 15 01895 g004b 550
Figure 4. Representative stress–strain curves of (a) cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of wheat straw and (b) cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of hazelnut hulls.
Figure 4. Representative stress–strain curves of (a) cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of wheat straw and (b) cured neat epoxy resin (DGEBA) and cured bio-based epoxy blends of hazelnut hulls.
Polymers 15 01895 g004aPolymers 15 01895 g004b
Table
Table 1. Properties of biomass and biochar pyrolyzed at 600 °C. Adapted with permission from Hidalgo et al (2019) [30].
Table 1. Properties of biomass and biochar pyrolyzed at 600 °C. Adapted with permission from Hidalgo et al (2019) [30].
Fixed Carbon (%)Volatile Matter (%)Ash (%)Moisture (%)N (%)C (%)H (%)O (%)H/C Molar RatioO/C Molar RatioMean Particle Size (μm)Surface Area (m2/g)Pore Volume (cm3/g)Pore Diameter (Ȧ)
Feedstock
Wheat straw16.1170.414.758.610.6343.115.8150.451.620.80
Hazelnut hull37.3251.71.378.890.1135.986.0057.912.001.18
Biochar pyrolyzed
Wheat straw61.8917.4415.614.840.3666.272.2131.160.400.1811.7 ± 0.7 *57.3880.0110.4
Hazelnut hull88.275.864.651.214.3689.821.704.120.230.00220.9 ± 0.6 **18.0330.00510.5
Accumulate size distribution of biochar particles: * 25%: 5.3 μm, 50%: 10.2 μm, 75%: 15.1 μm; ** 25%: 7.1 μm, 50%: 20.1 μm, 75%:25.5 μm.
Table
Table 2. Composition of bio-oil.
Table 2. Composition of bio-oil.
Relative Content (%)
CompositionWheat StrawHazelnut Hull
Aromatic compound:
Aromatic hydrocarbon6.677.1
Phenols36.3728.37
Aliphatic hydrocarbons26.2418
Ketone10.229.22
Ether-20
Amine5-
Non identified10.517.31
Table
Table 3. Thermal degradation behaviors for cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
Table 3. Thermal degradation behaviors for cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
SampleTonset
(°C) a		Tendset
(°C) b		T5%
(°C) c		T10%
(°C) d		T50%
(°C) e		Tmax
(°C) f		Rm800
(%) g
DGEBA32042073.01222.37363.9365.723.04
Wheat straw
BO5BC5305420278.17307.78401.31338.3112.35
BO5BC10320422280.27317.93386.87365.1115.05
BO10BC5300425269.13295453.46323.332.76
BO10BC10295420277.59303.22452.53325.9911.06
Hazelnut hull
BO5BC5300400291.44312.52412.83338.1912.83
BO5BC10320425286.93323.04385.50367.8512.05
BO10BC5325420290.55321.94387.33361.3613.54
BO10BC10320420293.30325.29389.71365.0815.50
a Initial degradation temperature (°C). b Final degradation temperature (°C). c 5% weight loss temperature (°C). d 10% weight loss temperature (°C). e 50% weight loss temperature (°C). f maximum mass loss rate temperature (°C). g Residue (wt%) at 800 °C.
Table
Table 4. The degree of crosslinking for cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
Table 4. The degree of crosslinking for cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
SampleDegree of Crosslinking (α)
DGEBA72.161
Wheat straw
BO5BC570.014
BO5BC1071.686
BO10BC570.965
BO10BC1071.832
Hazelnut hull
BO5BC572.879
BO5BC1069.881
BO10BC571.739
BO10BC1071.630
Table
Table 5. Mechanical properties of cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
Table 5. Mechanical properties of cured neat epoxy resin (DGEBA) and bio-based epoxy blends.
SampleTensile
Strength
(MPa)		Max.
Deformation
(mm/mm)		Young’s
Modulus
(MPa)
DGEBA7.52 ± 1.090.0101093.69 ± 128.83
Wheat straw
BO5BC510.96 ± 1.820.0052519.38 ± 194.37
BO5BC1013.58 ± 3.970.0101955.90 ± 83.35
BO10BC58.73 ± 0.850.003091.31 ± 362.84
BO10BC1013.02 ± 9.30.0053982.05 ± 582.65
Hazelnut hull
BO5BC514.04 ± 6.300.0063060.02 ± 252.49
BO5BC104.11 ± 1.860.0033138. ±19.55
BO10BC510.93 ± 2.490.0053270.30 ± 1470.47
BO10BC1018.11 ± 3.350.0053957.84 ± 130.91
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Hidalgo, P.; Salgado, L.; Ibacache, N.; Hunter, R. Influence of Biochar and Bio-Oil Loading on the Properties of Epoxy Resin Composites. Polymers 2023, 15, 1895. https://doi.org/10.3390/polym15081895

AMA Style

Hidalgo P, Salgado L, Ibacache N, Hunter R. Influence of Biochar and Bio-Oil Loading on the Properties of Epoxy Resin Composites. Polymers. 2023; 15(8):1895. https://doi.org/10.3390/polym15081895

Chicago/Turabian Style

Hidalgo, Pamela, Luis Salgado, Nayadeth Ibacache, and Renato Hunter. 2023. "Influence of Biochar and Bio-Oil Loading on the Properties of Epoxy Resin Composites" Polymers 15, no. 8: 1895. https://doi.org/10.3390/polym15081895

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.