Next Article in Journal
Development of Oil and Gas Stimulation Fluids Based on Polymers and Recycled Produced Water
Previous Article in Journal
Biodegradation of Polylactic Acid-Based Bio Composites Reinforced with Chitosan and Essential Oils as Anti-Microbial Material for Food Packaging
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 13
Issue 22
10.3390/polym13224020
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

The Influence of Helium Dielectric Barrier Discharge Jet (DBDjet) Plasma Treatment on Bathocuproine (BCP) in p-i-n-Structure Perovskite Solar Cells

by
Chung-Yueh Shih
1,2,
Jian-Zhi Huang
3,
Mei-Hsin Chen
4,
Cheng-Che Hsu
5,
Chih-I Wu
3,
I-Chun Cheng
3,6,7 and
Jian-Zhang Chen
1,2,7,*
1
Graduate Institute of Applied Mechanics, National Taiwan University, Taipei City 10617, Taiwan
2
Advanced Research Center for Green Materials Science and Technology, National Taiwan University, Taipei City 10617, Taiwan
3
Graduate Institute of Photonics and Optoelectronics, National Taiwan University, Taipei City 10617, Taiwan
4
Department of Electro-Optical Engineering, National Taipei University of Technology, Taipei City 10608, Taiwan
5
Department of Chemical Engineering, National Taiwan University, Taipei City 10617, Taiwan
6
Department of Electrical Engineering, National Taiwan University, Taipei City 10617, Taiwan
7
Innovative Photonics Advanced Research Center (i-PARC), National Taiwan University, Taipei City 10617, Taiwan
*
Author to whom correspondence should be addressed.
Polymers 2021, 13(22), 4020; https://doi.org/10.3390/polym13224020
Submission received: 18 October 2021 / Revised: 15 November 2021 / Accepted: 17 November 2021 / Published: 20 November 2021
(This article belongs to the Section Polymer Processing and Engineering)
Browse Figures
Versions Notes

Abstract

:
A bathocuproine (BCP) layer is typically used as the hole-blocking layer in p-i-n-structure perovskite solar cells (PSCs) between PC61BM and Ag electrodes. Before evaporating the Ag, we used a low-temperature (<40 °C) atmospheric-pressure dielectric barrier discharge jet (DBDjet) to treat the BCP with different scan rates. The main purpose of this was to change the contact resistance between the BCP layer and the Ag electrodes through surface modification using a DBDjet. The best power conversion efficiency (PCE) of 13.11% was achieved at a DBDjet scan rate of 2 cm/s. The He DBDjet treatment introduced nitrogen to form C−N bonds and create pits on the BCP layer. This deteriorated the interface between the BCP and the follow-up deposited-Ag top electrode. Compared to the device without the plasma treatment on the BCP layer, the He DBDjet treatment on the BCP layer reduced photocurrent hysteresis but deteriorated the fill factor and the efficiency of the PSCs.

1. Introduction

In the past few years, organic-inorganic hybrid perovskite solar cells (PSCs) have gained attention due to their high power conversion efficiency (PCE) and low cost [1,2,3,4,5,6,7,8,9]. In 2013, the first p-i-n-structure PSC was fabricated and it had a PCE of 3.9% [10]. Nowadays, p-i-n-structure PSCs with PCEs exceeding 22% are being fabricated [11].
A conventional p-i-n structure-PSC comprises a hole transport layer (HTL), a perovskite, and an electron transport layer (ETL). The contact resistance between the PCBM and the metal is due to the energy band mismatch. To reduce the charge combination, bathocuproine (BCP), LiF, and ZnO are commonly used as nanometer-thick buffer layers that are placed between the ETL and the metal electrode. For instance, Seo et al., optimized the [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) thickness through the insertion of a LiF layer in PSCs and fabricated a device with a PCE exceeding 14%. Qiu et al. also found that the PSC with a PCBM/ZnO bilayer stored in air for a short duration exhibited a better device performance [12,13,14,15,16,17,18,19,20,21,22]. Chen et al. noted that a BCP buffer layer reduces charge accumulation and recombination at the ETL/metal electrode interface; furthermore, they found that a BCP buffer layer of suitable thickness not only results in excellent photovoltaic (PV) performance, but also provides an encapsulation effect that enhances the device stability [23]. The use of BCP in PSCs has been widely investigated. However, the surface modification of BCP with plasma treatment in a PSC system has not yet been reported.
Atmospheric-pressure plasma (APP) can be operated at a regular pressure without using a vacuum system. Typical APP technologies include corona discharge and dielectric barrier discharge (DBD) with or without a high-speed jet rate for cooling and for bringing out the reactive plasma species [24,25,26]. In biomedicine [27,28,29] and agriculture [30,31] applications, low-temperature APP has been extensively used because it can avoid thermal damage. In other applications, the effects of heat and reactive plasma species can be synergized to realize the ultrafast processing of materials [32,33,34,35]. Atmospheric-pressure plasma has been used for processing PSCs in various ways. Hilt et al. converted sprayed perovskite precursor films using a plasma jet [36]. Ameen et al. processed the ZnO quantum dots ETL of PSCs on a flexible substrate [37]. Homola et al. used air plasma to process mesoporous TiO2 for PSCs made on a glass substrate [38].
Our research group has worked on the APP processing of PSCs for several years. Previously, we used a portable surface-diffusion DBD device to treat the perovskite layer for both p-i-n and n-i-p PSCs. With the use of a proper processing time, the efficiency of PSCs can be improved [39,40]. The same surface-diffusion DBD device was also applied to treat the PEDOT:PSS film of PSCs [41]. A 500 °C arc APP jet was used to post-treat the NiO HTL of the PSCs to improve their performance [42]. A <40 °C helium (He) DBDjet was also used for treating the NiO HTL of the PSCs for better performance [43]. The same DBDjet was also used for stripping the polyvinylpyrrolidone outside the jet-sprayed Ag nanowire electrodes of fully solution-processed n-i-p structure PSCs to improve the device performance [44]. Most recently, this DBDjet was also used to treat low-temperature TiO2 nanoparticle ETLs of PSCs on a polyethylene naphthalate substrate [45]. In this study, we used a scan-mode He DBDjet to treat the BCP layer of p-i-n PSCs (FTO/NiO/perovskite/PC61BM/BCP/Ag) with different scan rates (3, 2, 1, and 0.5 cm/s) and investigated the influence of the He DBDjet treatment on the BCP layer. An inverted PSC with a BCP layer was found to degrade at temperatures higher than 85 °C. Hence, in this work, the He DBDjet plasma treatment on the BCP layer was performed while keeping the working temperature below 40 °C (Figure 1), thereby avoiding thermal damage [46,47]. Therefore, the major effect resulted from the reactive plasma species. Furthermore, we investigated the performance of PSCs in which the BCP layer was treated using the He DBDjet before the Ag electrode deposition.

2. Materials and Methods

2.1. PSC Fabrication

A 2 cm × 2 cm fluorine-doped tin oxide (FTO, TEC7, sheet resistance: ~8 Ω sq −1, SCiKET, Taoyuan, Taiwan) glass substrate was sequentially cleaned using deionized water, acetone, isopropanol, and a UV-ozone cleaner for 15 min. A NiO precursor solution was prepared by dissolving 0.5 M nickel acetate (99.998%, trace metals basis, Sigma-Aldrich, St. Louis, MO, USA) and ethanolamine (99.5%, Sigma-Aldrich, St. Louis, MO, USA) in ethanol (99%, anhydrous alcohol, Echo Chemical Co. Ltd., Miaoli, Taiwan) and stirring overnight at 60 °C. Then, the NiO precursor solution was spin-coated on the FTO substrate at 6000 rpm for 40 s and calcined on the hot plate at 325 °C for 10 min. The resulting NiO layer served as the HTL. The sample was then immediately transferred into a nitrogen-filled glove box. The perovskite precursor solution was prepared by dissolving 578 mg of PbI2 (99.999%, metals basis, Alfa Aesar, MA, USA) and 200 mg of CH3NH3I (MAI, 98%, UniRegion Bio-Tech, Taoyuan, Taiwan) in 1 mL of dimethylformamide (99.8%, Sigma-Aldrich, St. Louis, MO, USA) with stirring at 500 rpm at 60 °C for 12 h. The perovskite film was deposited on the NiO film through a one-step method. The resulting perovskite film was annealed at 100 °C for 10 min. Then, 1 mL of PC61BM (99.5%, UniRegion Bio-Tech, Taoyuan, Taiwan) doped with 2 μL of DMOAP (42% methanol solution, Sigma-Aldrich, St. Louis, MO, USA) was spin-coated on the perovskite film at 2000 rpm for 30 s. Next, BCP (0.5 mg mL−1 in 2-propano, Alfa Aesar, MA, USA) was spin-coated on the PC61BM film at 6000 rpm for 20 s and then annealed at 75 °C for 15 min. Then, the BCP was scanned once by He DBDjet plasma at scan rates of 0.5, 1, and 2 cm/s. The gap between the sample and the bottom of the quartz tube was fixed at 1 mm in the He DBDjet treatment process. Finally, Ag (99.99%, Gredmann, Taipei, Taiwan) electrodes were deposited by e-beam evaporation. The thickness of the Ag layer was 85 nm. These electrodes (specifically, cathodes) were controlled to have an area of 0.09 cm2 (0.3 cm × 0.3 cm) on each cell via a shadow mask. The He DBDjet-scanned samples were then compared with the untreated sample.

2.2. Characterization

The surface morphology of BCP was inspected using scanning electron microscopy (SEM, JSM-7800F Prime, JEOL, Tokyo, Japan). The surface chemical bonding status was surveyed by a custom-made X-ray photoelectron spectroscopy (XPS) system (PHI 5400 XPS system, PHI, Chanhassen, MN, USA). The external quantum efficiency (EQE) of the PSCs was measured using a quantum efficiency analyzer (Enlitech, QE-R3011, Kaohsiung, Taiwan). The electrochemical performance was evaluated by electrochemical impedance spectroscopy (EIS) using an electrochemical workstation (Autolab PGSTAT204, Metrohm, Utrecht, The Netherlands). The current density–voltage (J–V) curve of the PSC was measured using a sourcemeter (B2902A, Agilent, Santa Clara, CA, USA) under the illumination of simulated AM1.5 light (Sun 2000 Solar Simulator, ABET, Milford, CT, USA).

3. Results and Discussion

3.1. SEM Analysis

Figure 2 demonstrates surface images of the BCP films without and with the He DBDjet plasma treatment. After the He DBDjet treatment on the BCP layer at a lower scan rate, some pits could be clearly seen on the BCP layer. Further, the number of pits increased as the scan rate decreased. This suggests that the BCP layer likely suffered surface oxidation and damage during the plasma treatment.

3.2. XPS Analysis

All binding energies were referenced to C1s (284.8 eV). Figure 3 shows the structure of BCP. Figure 4 shows the XPS C1s spectra of the BCP film with and without the He DBDjet treatment and a superimposed XPS C1s spectra. The peaks at 284.8 and 285.9 eV corresponded to C–C and C–N, respectively [48]. Table 1 lists the contents of the corresponding deconvolution peaks. Owing to the reaction between the BCP and the reactive plasma species of the He DBDjet, the intensity of the C–C binding energy peak decreased, as seen in Figure 4f. Then, under the He DBDjet treatment, a lower scan rate resulted in a decrease in the proportion of C–N bonds, as shown in Table 1. However, the amounts of C−N bonds in the samples with the DBDjet scanning were all larger than in those without the DBDjet treatment. This suggests that the environmental nitrogen may participate in the plasma reaction and introduce nitrogen species to the sample. This is evidenced in our previous studies regarding the processing of DBDjet materials [43,49]; reactive nitrogen species are clearly identified in the optical emission spectra of the He DBD jet plasma. These reactive nitrogen species may react with the BCP to form C–N bonds in the first instance. With a higher plasma processing time—i.e., a smaller DBDjet scan rate—the amount of C–N bonds will be lower in turn, possibly owing to the more vigorous plasma reaction or damage to the BCP layer. From the results shown in Figure 4 and Table 1, it may be reasonable to assume that the reactive plasma species in the He DBDjet reacted with the BCP to produce pits (i.e., damage), as seen in the SEM results.

3.3. External Quantum Efficiency Analysis

The EQE and corresponding integrated photocurrent curve of the p-i-n-structure PSCs with the He DBDjet treatment on the BCP film are illustrated in Figure 5. The results indicate that the He DBDjet treatment slightly deteriorated the EQE and the corresponding integrated photocurrent. The wavelength range of 650 to 750 nm had the greatest influence. The integrated photocurrent decreased from 16.387 (without DBDjet treatment) to 15.031 mA cm−2 (with DBDjet treatment at the lowest scan rate of 0.5 cm/s). At the lowest scan rate of 0.5 cm/s, the plasma influencing time is longer; therefore, the EQE degradation was more apparent. Additional degradation apparently occurred in the wavelength range of 300–400 nm at a DBDjet scan rate of 0.5 cm/s. The EQE possibly decreased due to more interface charge accumulation or radiative recombination [13,23]. Because the DBDjet plasma working temperature was below 40 °C, this result was mainly attributed to the reactive plasma species.

3.4. Electrochemical Impedance Spectroscopy Analysis

Figure 6 shows a Nyquist plot of the EIS. Its inset shows the equivalent circuit for analyses. Further, Table S1 lists the EIS fitting parameters. R1, R2, and R3 correspond to the series resistance, charge transporting resistance, and recombination resistance, respectively [42,50]. Because the same FTO substrates and top electrodes were used for the devices, the R1 is almost the same for the devices. A smaller R1 and R2 could provide benefits through the encouragement of photogenerated carriers and transportation to the corresponding HTL and ETL [51]. The R2 increased (higher charge transporting resistance) after the He DBDjet treatment on the BCP layer. More specifically, the R2 monotonically increased with a decrease in the He DBDjet scan rate. This suggests that the carrier transport between the BCP layer and the Ag was degraded [42] after the DBDjet treatment.

3.5. Statistical Analysis of PV Parameters

Figure 7 presents the J–V curves of the PSCs with the He DBDjet treatment on the BCP layer at different scan rates (reverse scan). Table 2 lists the corresponding photovoltaic parameters. The PV parameters include the open circuit voltage (Voc), short circuit current density (Jsc), fill factor (F.F.), and PCE. The results show that the use of plasma treatment (i.e., with a smaller DBDjet scan rate) on the BCP layer for a longer time deteriorated the PSCs’ performance. Compared to the PSCs without the He DBDjet treatment, the PSCs with the He DBDjet treatment exhibited smaller hysteresis, defined as (PCE (forward scan)—PCE (reverse scan))/PCE (forward scan), as shown in Figure S1 [4,52,53]. Many parameters influence the J–V hysteresis behavior of the PSCs, such as the voltage range, scan direction, scan rate, architecture, and precondition of PSCs [54,55,56,57,58,59,60,61,62,63]. In this case, without the He DBDjet treatment on the BCP layer, the unbalanced electron and hole transport rates as well as interface defects may cause photocurrent hysteresis [4,52,53]. Figures S2 and S3, and Table S2 show the statistical data for five batches of PSCs with He DBDjet treatment on the BCP. No apparent degradation was found in Voc or Jsc, and the results show that a longer plasma treatment time on the BCP led to a lower F.F., in keeping with the SEM results. The pits on the BCP layer led to an unsmooth film morphology, in turn resulting in a low F.F. and a low EQE owing to the leakage current [64,65]. Further, the performance under a reverse scan was much poorer than that under a forward scan after He DBDjet treatment. Thus, the hysteresis of the PSC with He DBDjet treatment on the BCP reduced, as seen in Table S2.

4. Conclusions

This study investigated the influence of He DBDjet plasma treatment on a BCP layer. The best PCE of 13.11% was achieved in a PSC subjected to He DBDjet treatment at a scan rate of 2 cm/s. EQE and EIS results indicated that the He DBDjet treatment negatively affected the electronic states of BCP used as a HBL for PSCs. He DBDjet treatment introduced nitrogen to form C−N bonds and produce pits on the BCP layer. This deteriorated the interface of the BCP and the follow-up deposited-Ag top electrode. Compared with the reference cell (i.e., no plasma treatment), He DBDjet treatment on the BCP layer deteriorated the PSCs’ performance. In particular, it impacted the F.F. of the PSCs. Furthermore, the hysteresis of the PSC decreased after He DBDjet treatment on the BCP layer.

Supplementary Materials

The following are available online at www.mdpi.com/article/10.3390/polym13224020/s1: Figure S1: Hysteresis of PSCs without/with He DBDjet plasma treatment on BCP; Figure S2: PV parameters of PSCs with He DBDjet treatment on BCP (forward scan); Figure S3: PV parameters of PSCs with He DBDjet treatment on BCP (reverse scan); Figure S4. Cross-sectional view SEM images of the samples. Table S1: EIS fitting parameters; Table S2: PV parameters of PSCs with He DBDjet treatment on BCP.

Author Contributions

Conceptualization, J.-Z.C.; methodology, C.-Y.S. and J.-Z.C.; formal analysis, J.-Z.H. and C.-Y.S.; investigation, C.-Y.S. and J.-Z.C.; resources, M.-H.C., C.-C.H., C.-I.W., I.-C.C. and J.-Z.C.; data curation, C.-Y.S.; writing—original draft preparation, C.-Y.S. and J.-Z.C.; writing—review and editing, J.-Z.C.; supervision, J.-Z.C.; project administration, J.-Z.C. All authors have read and agreed to the published version of the manuscript.

Funding

We gratefully acknowledge funding support from the Advanced Research Center for Green Materials Science and Technology from The Featured Area Research Center Program of the Higher Education Sprout Project by the Ministry of Education (110L9006) and the Ministry of Science and Technology in Taiwan (MOST 108-2221-E-002-088-MY3, MOST 110-2634-F-002-043). This work is also partly supported by the Ministry of Science and Technology of Taiwan under grant no. MOST 110-3116-F-002-002.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The relevant data are all included in the paper and in the Supplementary Materials.

Acknowledgments

Thanks to C.-S. Lin and Y.-T. Lee of Instrumentation Center, National Taiwan University for FEG-SEM experiments.

Conflicts of Interest

The authors declare no conflict of interest and that no animal or human participants were involved in this study.

References

  1. Liu, G.; Liu, Z.; Wang, L.; Xie, X. An organic-inorganic hybrid hole transport bilayer for improving the performance of perovskite solar cells. Chem. Phys. 2021, 542, 111061. [Google Scholar] [CrossRef]
  2. Zhang, Y.; Kirs, A.; Ambroz, F.; Lin, C.T.; Bati, A.S.; Parkin, I.P.; Shapter, J.G.; Batmunkh, M.; Macdonald, T.J. Ambient fabrication of organic–inorganic hybrid perovskite solar cells. Small Methods 2021, 5, 2000744. [Google Scholar] [CrossRef]
  3. Seo, S.; Park, I.J.; Kim, M.; Lee, S.; Bae, C.; Jung, H.S.; Park, N.-G.; Kim, J.Y.; Shin, H. An ultra-thin, un-doped NiO hole transporting layer of highly efficient (16.4%) organic–inorganic hybrid perovskite solar cells. Nanoscale 2016, 8, 11403–11412. [Google Scholar] [CrossRef] [PubMed]
  4. Ren, C.; He, Y.; Li, S.; Sun, Q.; Liu, Y.; Wu, Y.; Cui, Y.; Li, Z.; Wang, H.; Hao, Y. Double electron transport layers for efficient and stable organic-inorganic hybrid perovskite solar cells. Org. Electron. 2019, 70, 292–299. [Google Scholar] [CrossRef]
  5. Heo, J.H.; Shin, D.H.; Lee, M.L.; Kang, M.G.; Im, S.H. Efficient organic–inorganic hybrid flexible perovskite solar cells prepared by lamination of polytriarylamine/CH3NH3PbI3/anodized Ti metal substrate and graphene/PDMS transparent electrode substrate. ACS Appl. Mater. Interfaces 2018, 10, 31413–31421. [Google Scholar] [CrossRef] [PubMed]
  6. Bouclé, J.; Herlin-Boime, N. The benefits of graphene for hybrid perovskite solar cells. Synth. Met. 2016, 222, 3–16. [Google Scholar] [CrossRef]
  7. Xu, X.; Sun, L.; Shen, K.; Zhang, S. Organic and hybrid organic-inorganic flexible optoelectronics: Recent advances and perspectives. Synth. Met. 2019, 256, 116137. [Google Scholar] [CrossRef]
  8. Zhao, T.; Wang, D.; Shuai, Z. Doping optimization of organic-inorganic hybrid perovskite CH3NH3PbI3 for high thermoelectric efficiency. Synth. Met. 2017, 225, 108–114. [Google Scholar] [CrossRef]
  9. Kanemitsu, Y.; Okano, M.; Yamada, Y. Light emission from thin film solar cell materials: An emerging infrared and visible light emitter. ECS J. Solid State Sci. Technol. 2017, 7, R3102. [Google Scholar] [CrossRef]
  10. Jeng, J.Y.; Chiang, Y.F.; Lee, M.H.; Peng, S.R.; Guo, T.F.; Chen, P.; Wen, T.C. CH3NH3PbI3 perovskite/fullerene planar-heterojunction hybrid solar cells. Adv. Mater. 2013, 25, 3727–3732. [Google Scholar] [CrossRef]
  11. Zheng, X.; Hou, Y.; Bao, C.; Yin, J.; Yuan, F.; Huang, Z.; Song, K.; Liu, J.; Troughton, J.; Gasparini, N. Managing grains and interfaces via ligand anchoring enables 22.3%-efficiency inverted perovskite solar cells. Nat. Energy 2020, 5, 131–140. [Google Scholar] [CrossRef]
  12. Liu, T.; Chen, K.; Hu, Q.; Zhu, R.; Gong, Q. Inverted perovskite solar cells: Progresses and perspectives. Adv. Energy Mater. 2016, 6, 1600457. [Google Scholar] [CrossRef]
  13. Castro-Hermosa, S.; Wouk, L.; Bicalho, I.S.; de Queiroz Corrêa, L.; de Jong, B.; Cinà, L.; Brown, T.M.; Bagnis, D. Efficient fully blade-coated perovskite solar cells in air with nanometer-thick bathocuproine buffer layer. Nano Res. 2021, 14, 1034–1042. [Google Scholar] [CrossRef]
  14. Shibayama, N.; Kanda, H.; Kim, T.W.; Segawa, H.; Ito, S. Design of BCP buffer layer for inverted perovskite solar cells using ideal factor. APL Mater. 2019, 7, 031117. [Google Scholar] [CrossRef] [Green Version]
  15. Seo, J.; Park, S.; Kim, Y.C.; Jeon, N.J.; Noh, J.H.; Yoon, S.C.; Seok, S.I. Benefits of very thin PCBM and LiF layers for solution-processed p–i–n perovskite solar cells. Energy Environ. Sci. 2014, 7, 2642–2646. [Google Scholar] [CrossRef]
  16. Liu, X.; Yu, H.; Yan, L.; Dong, Q.; Wan, Q.; Zhou, Y.; Song, B.; Li, Y. Triple cathode buffer layers composed of PCBM, C60, and LiF for high-performance planar perovskite solar cells. ACS Appl. Mater. Interfaces 2015, 7, 6230–6237. [Google Scholar] [CrossRef]
  17. Duan, L.; Chen, Y.; Yuan, J.; Zong, X.; Sun, Z.; Wu, Q.; Xue, S. Dopant-free X-shaped DA type hole-transporting materials for pin perovskite solar cells. Dye. Pigment. 2020, 178, 108334. [Google Scholar] [CrossRef]
  18. Wang, B.; Zeng, Q.; Sun, Z.; Xue, S.; Liang, M. Molecularly engineering of truxene-based dopant-free hole-transporting materials for efficient inverted planar perovskite solar cells. Dye. Pigment. 2019, 165, 81–89. [Google Scholar] [CrossRef]
  19. Chen, Q.; Li, X.; Jiu, T.; Ma, S.; Li, J.; Xiao, X.; Zhang, W. Tetrathiafulvalene derivative as a new hole-transporting material for highly efficient perovskite solar cell. Dye. Pigment. 2017, 147, 113–119. [Google Scholar] [CrossRef]
  20. Feng, X.; Huan, Y.; Zheng, C.; Tan, C.; Meng, H.; Liu, B.; Gao, D.; Huang, W. A series of porphyrins as interfacial materials for inverted perovskite solar cells. Org. Electron. 2020, 77, 105522. [Google Scholar] [CrossRef]
  21. Qiu, W.; Buffiere, M.; Brammertz, G.; Paetzold, U.W.; Froyen, L.; Heremans, P.; Cheyns, D. High efficiency perovskite solar cells using a PCBM/ZnO double electron transport layer and a short air-aging step. Org. Electron. 2015, 26, 30–35. [Google Scholar] [CrossRef]
  22. He, B.; Wang, R.; Lu, H.; Ji, Y.; Song, Q.; Tang, X.; Jin, Y.; Wu, F.; Zhu, L. Alkyl chain engineering on tetraphenylethylene-diketopyrrolopyrrole-based interfacial materials for efficient inverted perovskite solar cells. Org. Electron. 2019, 69, 13–19. [Google Scholar] [CrossRef]
  23. Chen, C.; Zhang, S.; Wu, S.; Zhang, W.; Zhu, H.; Xiong, Z.; Zhang, Y.; Chen, W. Effect of BCP buffer layer on eliminating charge accumulation for high performance of inverted perovskite solar cells. RSC Adv. 2017, 7, 35819–35826. [Google Scholar] [CrossRef] [Green Version]
  24. Schutze, A.; Jeong, J.Y.; Babayan, S.E.; Park, J.; Selwyn, G.S.; Hicks, R.F. The atmospheric-pressure plasma jet: A review and comparison to other plasma sources. IEEE Trans. Plasma Sci. 1998, 26, 1685–1694. [Google Scholar] [CrossRef] [Green Version]
  25. Laroussi, M.; Akan, T. Arc-free atmospheric pressure cold plasma jets: A review. Plasma Process. Polym. 2007, 4, 777–788. [Google Scholar] [CrossRef]
  26. Winter, J.; Brandenburg, R.; Weltmann, K. Atmospheric pressure plasma jets: An overview of devices and new directions. Plasma Sources Sci. Technol. 2015, 24, 064001. [Google Scholar] [CrossRef]
  27. Graves, D.B. Low temperature plasma biomedicine: A tutorial review. Phys. Plasmas 2014, 21, 080901. [Google Scholar] [CrossRef] [Green Version]
  28. Choi, J.; Mohamed, A.A.H.; Kang, S.K.; Woo, K.C.; Kim, K.T.; Lee, J.K. 900-MHz nonthermal atmospheric pressure plasma jet for biomedical applications. Plasma Process. Polym. 2010, 7, 258–263. [Google Scholar] [CrossRef]
  29. Rusu, L.-C.; Ardelean, L.C.; Jitariu, A.-A.; Miu, C.A.; Streian, C.G. An insight into the structural diversity and clinical applicability of polyurethanes in biomedicine. Polymers 2020, 12, 1197. [Google Scholar] [CrossRef]
  30. Ito, M.; Oh, J.S.; Ohta, T.; Shiratani, M.; Hori, M. Current status and future prospects of agricultural applications using atmospheric-pressure plasma technologies. Plasma Process. Polym. 2018, 15, 1700073. [Google Scholar] [CrossRef]
  31. Štěpánová, V.; Slavíček, P.; Kelar, J.; Prášil, J.; Smékal, M.; Stupavská, M.; Jurmanová, J.; Černák, M. Atmospheric pressure plasma treatment of agricultural seeds of cucumber (Cucumis sativus L.) and pepper (Capsicum annuum L.) with effect on reduction of diseases and germination improvement. Plasma Process. Polym. 2018, 15, 1700076. [Google Scholar] [CrossRef]
  32. Hao, Y.-C.; Nurzal, N.; Chien, H.-H.; Liao, C.-Y.; Kuok, F.-H.; Yang, C.-C.; Chen, J.-Z.; Yu, I.-S. Application of atmospheric-pressure-plasma-jet modified flexible graphite sheets in reduced-graphene-oxide/polyaniline supercapacitors. Polymers 2020, 12, 1228. [Google Scholar] [CrossRef] [PubMed]
  33. Cheng, P.-Y.; Lu, N.-H.; Lu, Y.-S.; Chen, C.-H.; Lee, Y.-L.; Chen, J.-Z. Surface modification of FeCoNiCr medium-entropy alloy (MEA) using octadecyltrichlorosilane and atmospheric-pressure plasma jet. Polymers 2020, 12, 788. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  34. Chen, J.-Z.; Wang, C.; Hsu, C.-C.; Cheng, I.-C. Ultrafast synthesis of carbon-nanotube counter electrodes for dye-sensitized solar cells using an atmospheric-pressure plasma jet. Carbon 2016, 98, 34–40. [Google Scholar] [CrossRef]
  35. Wu, T.-J.; Chou, C.-Y.; Hsu, C.-M.; Hsu, C.-C.; Chen, J.-Z.; Cheng, I.-C. Ultrafast synthesis of continuous Au thin films from chloroauric acid solution using an atmospheric pressure plasma jet. RSC Adv. 2015, 5, 99654–99657. [Google Scholar] [CrossRef]
  36. Hilt, F.; Hovish, M.Q.; Rolston, N.; Brüning, K.; Tassone, C.J.; Dauskardt, R.H. Rapid route to efficient, scalable, and robust perovskite photovoltaics in air. Energy Environ. Sci. 2018, 11, 2102–2113. [Google Scholar] [CrossRef]
  37. Ameen, S.; Akhtar, M.S.; Seo, H.-K.; Nazeeruddin, M.K.; Shin, H.-S. An insight into atmospheric plasma jet modified ZnO quantum dots thin film for flexible perovskite solar cell: Optoelectronic transient and charge trapping studies. J. Phys. Chem. C 2015, 119, 10379–10390. [Google Scholar] [CrossRef]
  38. Homola, T.s.; Pospisil, J.; Shekargoftar, M.; Svoboda, T.s.; Hvojnik, M.; Gemeiner, P.; Weiter, M.; Dzik, P. Perovskite solar cells with low-cost TiO2 mesoporous photoanodes prepared by rapid low-temperature (70 °C) plasma processing. ACS Appl. Energy Mater. 2020, 3, 12009–12018. [Google Scholar] [CrossRef]
  39. Tsai, J.-H.; Cheng, I.-C.; Hsu, C.-C.; Chueh, C.-C.; Chen, J.-Z. Feasibility study of atmospheric-pressure dielectric barrier discharge treatment on CH3NH3PbI3 films for inverted planar perovskite solar cells. Electrochim. Acta 2019, 293, 1–7. [Google Scholar] [CrossRef]
  40. Chen, Z.-C.; Cheng, Y.; Lin, C.-C.; Li, C.-S.; Hsu, C.-C.; Chen, J.-Z.; Wu, C.-I.; Cheng, I.-C. In-situ atmospheric-pressure dielectric barrier discharge plasma treated CH3NH3PbI3 for perovskite solar cells in regular architecture. Appl. Surf. Sci. 2019, 473, 468–475. [Google Scholar] [CrossRef]
  41. Li, T.-E.; Tsai, J.-H.; Cheng, I.-C.; Hsu, C.-C.; Chen, J.-Z. Atmospheric-pressure surface-diffusion dielectric-barrier discharge (SDDBD) plasma surface modification of PEDOT: PSS. Synth. Met. 2019, 256, 116114. [Google Scholar] [CrossRef]
  42. Lin, C.-I.; Tsai, J.-H.; Chen, J.-Z. Scanning atmospheric-pressure plasma jet treatment of nickel oxide with peak temperature of ∼500 °C for fabricating p–i–n structure perovskite solar cells. RSC Adv. 2020, 10, 11166–11172. [Google Scholar] [CrossRef]
  43. Tsai, J.-H.; Cheng, I.-C.; Hsu, C.-C.; Chen, J.-Z. Low-temperature (<40 °C) atmospheric-pressure dielectric-barrier-discharge-jet treatment on nickel oxide for p–i–n structure perovskite solar cells. ACS Omega 2020, 5, 6082–6089. [Google Scholar] [CrossRef]
  44. Fan, C.-F.; Tsai, J.-H.; Liao, Y.-C.; Cheng, I.-C.; Hsu, C.-C.; Chen, J.-Z. Low temperature (<40 °C) atmospheric-pressure dielectric-barrier-discharge-jet (DBDjet) plasma treatment on jet-sprayed silver nanowires (AgNWs) electrodes for fully solution-processed nip structure perovskite solar cells. ECS J. Solid State Sci. Technol. 2020, 9, 055016. [Google Scholar] [CrossRef]
  45. Mallela, M.S.; Tsai, J.-H.; Huang, J.-Z.; Hsu, C.-c.; Chen, M.-H.; Wu, C.-I.; Chen, J.Z.; Cheng, I.-C. Dielectric barrier discharge jet processed TiO2 nanoparticle layer for flexible perovskite solar cells. J. Phys. D Appl. Phys. 2021, 55, 034003. [Google Scholar] [CrossRef]
  46. Conings, B.; Drijkoningen, J.; Gauquelin, N.; Babayigit, A.; D’Haen, J.; D’Olieslaeger, L.; Ethirajan, A.; Verbeeck, J.; Manca, J.; Mosconi, E. Intrinsic thermal instability of methylammonium lead trihalide perovskite. Adv. Energy Mater. 2015, 5, 1500477. [Google Scholar] [CrossRef]
  47. Zheng, X.; Jiang, T.; Bai, L.; Chen, X.; Chen, Z.; Xu, X.; Song, D.; Xu, X.; Li, B.; Yang, Y.M. Enhanced thermal stability of inverted perovskite solar cells by interface modification and additive strategy. RSC Adv. 2020, 10, 18400–18406. [Google Scholar] [CrossRef]
  48. Huang, Y.-L.; Baji, A.; Tien, H.-W.; Yang, Y.-K.; Yang, S.-Y.; Ma, C.-C.M.; Liu, H.-Y.; Mai, Y.-W.; Wang, N.-H. Self-assembly of graphene onto electrospun polyamide 66 nanofibers as transparent conductive thin films. Nanotechnology 2011, 22, 475603. [Google Scholar] [CrossRef]
  49. Cheng, P.-Y.; Tsai, J.-H.; Chen, J.-Z. Hydrophilic patterning of octadecyltrichlorosilane (OTS)-coated paper via atmospheric-pressure dielectric-barrier-discharge jet (DBDjet). Cellulose 2020, 27, 10293–10301. [Google Scholar] [CrossRef]
  50. Chen, W.; Wu, Y.; Liu, J.; Qin, C.; Yang, X.; Islam, A.; Cheng, Y.-B.; Han, L. Hybrid interfacial layer leads to solid performance improvement of inverted perovskite solar cells. Energy Environ. Sci. 2015, 8, 629–640. [Google Scholar] [CrossRef]
  51. Hu, W.; Xu, C.Y.; Niu, L.B.; Elseman, A.M.; Wang, G.; Liu, D.B.; Yao, Y.Q.; Liao, L.P.; Zhou, G.D.; Song, Q.L. High open-circuit voltage of 1.134 V for inverted planar perovskite solar cells with sodium citrate-doped PEDOT: PSS as a hole transport layer. ACS Appl. Mater. Interfaces 2019, 11, 22021–22027. [Google Scholar] [CrossRef] [PubMed]
  52. Kang, D.H.; Park, N.G. On the current–voltage hysteresis in perovskite solar cells: Dependence on perovskite composition and methods to remove hysteresis. Adv. Mater. 2019, 31, 1805214. [Google Scholar] [CrossRef]
  53. Wu, C.-G.; Chiang, C.-H.; Tseng, Z.-L.; Nazeeruddin, M.K.; Hagfeldt, A.; Grätzel, M. High efficiency stable inverted perovskite solar cells without current hysteresis. Energy Environ. Sci. 2015, 8, 2725–2733. [Google Scholar] [CrossRef]
  54. Kim, H.-S.; Jang, I.-H.; Ahn, N.; Choi, M.; Guerrero, A.; Bisquert, J.; Park, N.-G. Control of I–V hysteresis in CH3NH3PbI3 perovskite solar cell. J. Phys. Chem. Lett. 2015, 6, 4633–4639. [Google Scholar] [CrossRef] [PubMed]
  55. Snaith, H.J.; Abate, A.; Ball, J.M.; Eperon, G.E.; Leijtens, T.; Noel, N.K.; Stranks, S.D.; Wang, J.T.-W.; Wojciechowski, K.; Zhang, W. Anomalous hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 2014, 5, 1511–1515. [Google Scholar] [CrossRef]
  56. Tress, W.; Marinova, N.; Moehl, T.; Zakeeruddin, S.M.; Nazeeruddin, M.K.; Grätzel, M. Understanding the rate-dependent J–V hysteresis, slow time component, and aging in CH 3 NH 3 PbI 3 perovskite solar cells: The role of a compensated electric field. Energy Environ. Sci. 2015, 8, 995–1004. [Google Scholar] [CrossRef]
  57. Chen, B.; Yang, M.; Zheng, X.; Wu, C.; Li, W.; Yan, Y.; Bisquert, J.; Garcia-Belmonte, G.; Zhu, K.; Priya, S. Impact of capacitive effect and ion migration on the hysteretic behavior of perovskite solar cells. J. Phys. Chem. Lett. 2015, 6, 4693–4700. [Google Scholar] [CrossRef]
  58. Wei, J.; Zhao, Y.; Li, H.; Li, G.; Pan, J.; Xu, D.; Zhao, Q.; Yu, D. Hysteresis analysis based on the ferroelectric effect in hybrid perovskite solar cells. J. Phys. Chem. Lett. 2014, 5, 3937–3945. [Google Scholar] [CrossRef]
  59. Xiao, Z.; Bi, C.; Shao, Y.; Dong, Q.; Wang, Q.; Yuan, Y.; Wang, C.; Gao, Y.; Huang, J. Efficient, high yield perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers. Energy Environ. Sci. 2014, 7, 2619–2623. [Google Scholar] [CrossRef]
  60. Chen, B.; Zheng, X.; Yang, M.; Zhou, Y.; Kundu, S.; Shi, J.; Zhu, K.; Priya, S. Interface band structure engineering by ferroelectric polarization in perovskite solar cells. Nano Energy 2015, 13, 582–591. [Google Scholar] [CrossRef] [Green Version]
  61. Chen, H.-W.; Sakai, N.; Ikegami, M.; Miyasaka, T. Emergence of hysteresis and transient ferroelectric response in organo-lead halide perovskite solar cells. J. Phys. Chem. Lett. 2015, 6, 164–169. [Google Scholar] [CrossRef] [PubMed]
  62. Chen, B.; Yang, M.; Priya, S.; Zhu, K. Origin of J–V hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 2016, 7, 905–917. [Google Scholar] [CrossRef]
  63. Umeyama, T.; Matano, D.; Shibata, S.; Baek, J.; Ito, S.; Imahori, H. Thermal precursor approach to pristine fullerene film as electron selective layer in perovskite solar cells. ECS J. Solid State Sci. Technol. 2017, 6, M3078. [Google Scholar] [CrossRef]
  64. Yuan, D.-X.; Yuan, X.-D.; Xu, Q.-Y.; Xu, M.-F.; Shi, X.-B.; Wang, Z.-K.; Liao, L.-S. A solution-processed bathocuproine cathode interfacial layer for high-performance bromine–iodine perovskite solar cells. Phys. Chem. Chem. Phys. 2015, 17, 26653–26658. [Google Scholar] [CrossRef] [PubMed]
  65. Cabrera-Espinoza, A.; Collavini, S.; Delgado, J.L. Doping strategies of organic n-type materials in perovskite solar cells: A chemical perspective. Sustain. Energy Fuels 2020, 4, 3264–3281. [Google Scholar] [CrossRef]
Polymers 13 04020 g001 550
Figure 1. (a) Working temperature and (b) infrared thermal image during DBDjet processing.
Figure 1. (a) Working temperature and (b) infrared thermal image during DBDjet processing.
Polymers 13 04020 g001
Polymers 13 04020 g002 550
Figure 2. Top-view SEM images of BCP films (a,b) without and (c–j) with DBDjet treatment under scan rates of (c,d) 3, (e,f) 2, (g,h) 1, and (i,j) 0.5 cm/s.
Figure 2. Top-view SEM images of BCP films (a,b) without and (c–j) with DBDjet treatment under scan rates of (c,d) 3, (e,f) 2, (g,h) 1, and (i,j) 0.5 cm/s.
Polymers 13 04020 g002
Polymers 13 04020 g003 550
Figure 3. Structure of BCP.
Figure 3. Structure of BCP.
Polymers 13 04020 g003
Polymers 13 04020 g004 550
Figure 4. XPS of C1s spectra of BCP film (a) as-deposited and (b–e) with He DBDjet treatment with scan rates of (b) 3, (c) 2, (d) 1, and (e) 0.5 cm/s. (f) Superimposed XPS C1s spectra.
Figure 4. XPS of C1s spectra of BCP film (a) as-deposited and (b–e) with He DBDjet treatment with scan rates of (b) 3, (c) 2, (d) 1, and (e) 0.5 cm/s. (f) Superimposed XPS C1s spectra.
Polymers 13 04020 g004
Polymers 13 04020 g005 550
Figure 5. EQE and corresponding integrated photocurrent curves of p-i-n PSCs with He DBDjet treatment on the BCP layer.
Figure 5. EQE and corresponding integrated photocurrent curves of p-i-n PSCs with He DBDjet treatment on the BCP layer.
Polymers 13 04020 g005
Polymers 13 04020 g006 550
Figure 6. The Nyquist plot of EIS.
Figure 6. The Nyquist plot of EIS.
Polymers 13 04020 g006
Polymers 13 04020 g007 550
Figure 7. J–V curves of PSCs with He DBDjet treatment on the BCP layer (reverse scan).
Figure 7. J–V curves of PSCs with He DBDjet treatment on the BCP layer (reverse scan).
Polymers 13 04020 g007
Table
Table 1. XPS deconvolution results for C1s spectra of the BCP film.
Table 1. XPS deconvolution results for C1s spectra of the BCP film.
%C–CC–N
BCP as-deposited97.812.19
BCP He DBDjet 3 cm/s87.5612.44
BCP He DBDjet 2 cm/s94.555.45
BCP He DBDjet 1 cm/s92.657.35
BCP He DBDjet 0.5 cm/s94.245.76
Table
Table 2. Photovoltaic parameters of PSCs without/with He DBDjet treatment on the BCP layer.
Table 2. Photovoltaic parameters of PSCs without/with He DBDjet treatment on the BCP layer.
Voc (V)Jsc (mA/cm2)F.F. (%)PCE (%)
No plasma treatmentForward1.0716.6364.7111.46
Reverse1.0817.2178.6014.62
Scan rate 3 cm/sForward1.0516.6265.8311.52
Reverse1.0516.9172.0812.76
Scan rate 2 cm/sForward1.0717.3362.5011.57
Reverse1.0717.7868.7213.11
Scan rate 1 cm/sForward1.0717.1662.2611.40
Reverse1.0717.5366.2612.41
Scan rate 0.5 cm/sForward1.0516.8853.019.36
Reverse1.0417.2556.2010.06
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Shih, C.-Y.; Huang, J.-Z.; Chen, M.-H.; Hsu, C.-C.; Wu, C.-I.; Cheng, I.-C.; Chen, J.-Z. The Influence of Helium Dielectric Barrier Discharge Jet (DBDjet) Plasma Treatment on Bathocuproine (BCP) in p-i-n-Structure Perovskite Solar Cells. Polymers 2021, 13, 4020. https://doi.org/10.3390/polym13224020

AMA Style

Shih C-Y, Huang J-Z, Chen M-H, Hsu C-C, Wu C-I, Cheng I-C, Chen J-Z. The Influence of Helium Dielectric Barrier Discharge Jet (DBDjet) Plasma Treatment on Bathocuproine (BCP) in p-i-n-Structure Perovskite Solar Cells. Polymers. 2021; 13(22):4020. https://doi.org/10.3390/polym13224020

Chicago/Turabian Style

Shih, Chung-Yueh, Jian-Zhi Huang, Mei-Hsin Chen, Cheng-Che Hsu, Chih-I Wu, I-Chun Cheng, and Jian-Zhang Chen. 2021. "The Influence of Helium Dielectric Barrier Discharge Jet (DBDjet) Plasma Treatment on Bathocuproine (BCP) in p-i-n-Structure Perovskite Solar Cells" Polymers 13, no. 22: 4020. https://doi.org/10.3390/polym13224020

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop