Next Article in Journal
Mechanically-Induced Catalyzation of MgH2 Powders with Zr2Ni-Ball Milling Media
Next Article in Special Issue
Emissions Control Catalysis
Previous Article in Journal
Numerical Evaluation of Potential Catalyst Savings for Ventilation Air Methane Catalytic Combustion in Helical Coil Reactors with Selective Wall Coating
Previous Article in Special Issue
A Review of Low Temperature NH3-SCR for Removal of NOx
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 9
Issue 4
10.3390/catal9040381
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Catalytic Properties of Double Substituted Lanthanum Cobaltite Nanostructured Coatings Prepared by Reactive Magnetron Sputtering

by
Mohammad Arab Pour Yazdi
1,
Leonardo Lizarraga
2,3,
Philippe Vernoux
2,
Alain Billard
1 and
Pascal Briois
1,*
1
FEMTO-ST Institute (UMR CNRS 6174), Université Bourgogne Franche-Comté, UTBM, 2 Place Lucien Tharradin, F-25200 Montbéliard CEDEX, France
2
Université Lyon, Université Claude Bernard Lyon 1, CNRS—IRCELYON—UMR 5256, 2 avenue A. Einstein, 69626 Villeurbanne, France
3
CIBION, Centro de Investigaciones en Bionanociencias, CONICET, Consejo Nacional de Investigaciones Científicas y Técnicas CONICET, Godoy Cruz 2390, Buenos Aires C1425FQD, Argentina
*
Author to whom correspondence should be addressed.
Catalysts 2019, 9(4), 381; https://doi.org/10.3390/catal9040381
Submission received: 29 March 2019 / Revised: 16 April 2019 / Accepted: 17 April 2019 / Published: 23 April 2019
(This article belongs to the Special Issue Emissions Control Catalysis)
Browse Figures
Review Reports Versions Notes

Abstract

:
Lanthanum perovskites are promising candidates to replace platinum group metal (PGM), especially regarding catalytic oxidation reactions. We have prepared thin catalytic coatings of Sr and Ag doped lanthanum perovskite by using the cathodic co-sputtering magnetron method in reactive condition. Such development of catalytic films may optimize the surface/bulk ratio to save raw materials, since a porous coating can combine a large exchange surface with the gas phase with an extremely low loading. The sputtering deposition process was optimized to generate crystallized and thin perovskites films on alumina substrates. We found that high Ag contents has a strong impact on the morphology of the coatings. High Ag loadings favor the growth of covering films with a porous wire-like morphology showing a good catalytic activity for CO oxidation. The most active composition displays similar catalytic performances than those of a Pt film. In addition, this porous coating is also efficient for CO and NO oxidation in a simulated Diesel exhaust gas mixture, demonstrating the promising catalytic properties of such nanostructured thin sputtered perovskite films.

1. Introduction

The family of perovskite oxides is known for its catalytic properties, hydrothermal stability, high recyclability and low cost compared with Platinum Group Metal (PGM) [1,2,3]. The general formula of perovskites is ABO3 where the larger size A-cation presents a 12-coordination number and the B-cation coordinates with 6 neighboring atoms [4]. Partial substitution of A and/or B atoms with other elements showing redox properties may enhance the catalytic activity due to the generation of structural defects such as anionic or cationic vacancies and/or modification of the oxidation state of B cations to maintain the electro-neutrality [5]. Lanthanum perovskites are promising candidates to replace noble metals (Pt, Pd, etc.) [6,7], especially regarding catalytic oxidation reactions. Lanthanum cobaltite (LaCoO3) is one of the most promising catalysts for the oxidation of gaseous pollutants such as carbon monoxide, unburnt hydrocarbons and nitrogen oxide [7,8]. Lanthanum cobaltites are used in many others fields due to their magnetic properties as well as their mixed ionic and electronic conductivity [9,10,11,12]. Most of these applications require the implementation of thin films that act as electrodes for fuel cells [13], thermoelectric processes [14], sensors [15], and magnetoresistance devices [16]. These electric, magnetic and electrocatalytic properties depend on the composition but also on the microstructure and morphology of coatings, which strongly depend on the preparation method [17,18]. Several techniques are reported for the synthesis of perovskite thin films such as the ground-frost [7], casting in band [18], chemical vapor deposition (CVD) [17], spray painting [19], sol-gel [7], atomic layer deposition (ALD) [20], laser pulsed deposition (PLD) [21], and physical vapor deposition (PVD) [22,23]. Regarding catalytic applications, the development of submicrometric catalytic films may optimize the surface/bulk ratio to save raw materials. Indeed, a thin catalytic coating can combine a large exchange surface with the gas phase with an extremely low loading. This is particularly suitable for air cleaning since gaseous pollutants only lick the surface of the catalyst. In addition, thin catalytic coatings could be deposited on hot substrates such as collector walls in thermal engine exhausts for removing pollutants or of radiators for improving indoor air quality. Few studies on the development of thin perovskite coatings for catalytic applications are reported in the literature [24,25,26]. The challenge lies in preparing adherent, thermally stable and pure crystallized perovskite films without any secondary parasite phase [18], showing appropriate compositions and nanostructures for catalysis [7,8,16,18]. The porosity and the specific surface areas have to be optimized to counter-balance the low quantity of materials involved in submicrometric catalytic coatings. In the present study, we used the cathodic co-sputtering magnetron method in reactive condition to prepare submicrometric nanostructured coatings of perovskites. This technique allows the deposition of pure and adherent coatings of complex oxides with a controlled and reproducible manner, while respecting the environment [27,28]. We have chosen to prepare Sr and Ag-doped lanthanum cobaltite as this perovskite composition is one of the most active for CO oxidation [8]. The partial substitution of La3+ cations by Sr2+ ones improves the thermal stability and then the specific surface area of pure LaCoO3 [29] and also enhances the surface concentration of oxygen vacancies involved in the oxidation catalytic mechanism [30]. The partial substitution of La3+ by Ag+ can also increase the catalytic properties of lanthanum cobaltites for oxidation reactions due to the formation of oxygen vacancies [31] and the stabilisation of Ag nanoparticles on the oxide surface [6,32]. The different parameters (intensities of current applied on the metallic targets, total pressure in the chamber, oxygen partial pressure, etc.) of the reactive magnetron sputtering preparation method were tuned to achieve pure and adherent coatings of LaCoO3 on alumina dense membranes. After a calcination at 500 °C, crystallized and dense cubic perovskite films of around 1.5 µm thick were achieved with the targeted La/Co stoichiometry. Different compositions of La1-x-ySrxAgyCoO3-α (x = 0.13–0.28, y = 0.14–0.48) doped perovskites were sputtered on alumina disks. We found that the incorporation of high contents of Ag can strongly modify the morphology of the coatings, increasing their porosity. The catalytic performance of the perovskite catalytic coatings for CO oxidation was found to be improved by the double substitution of Sr and Ag. The most active composition, La0.40Sr0.1Ag0.48Co0.93O3, displays similar catalytic performances than those of a Pt film, for CO oxidation. In addition, this porous coating is also active for CO and NO oxidation in a simulated Diesel exhaust gas mixture, demonstrating the promising catalytic properties of such nanostructured thin sputtered perovskite films.

2. Results

2.1. Preparation and Characterization of LaCoO3 Catalytic Coatings

Layers of LaCoO3 were synthetized on alumina substrates by using the reactive magnetron sputtering preparation method. Depositions have been performed in a reactive mode, mixing oxygen and argon in the chamber. To achieve the suitable La/Co ratio, the discharge current applied to the Co target was adjusted while maintaining a constant current of 1 A on the La target (Table 1). As expected, the La/Co ratio, estimated by Energy Dispersive Spectroscopy (EDS), decreases with the current dissipated on the Co target (Figure 1). We determined that a current intensity of 0.3 A is required to reach the targeted La/Co ratio. The diffractogram recorded on this as-deposited coating (Figure 2) shows that the layer is amorphous as no peak is detected. The difference between the radii of La3+ (136 pm) and Co3+ cations (72 pm) suggests an amorphous as-deposited coating due to steric effects as predicted by the confusion principle [33,34,35]. Then, a calcination step was performed at different temperatures (from 100 °C to 500 °C) for 2 h in air. X-Ray Diffraction (XRD) patterns (Figure 2), obtained under a Bragg-Brentano configuration (θ/2θ), evidence that the oxide coating crystallizes from 500 °C as a cubic perovskite phase (JCPDS 01-075-0279). This temperature is approximately 100 °C lower than those reported by H. Seim et al. [20] and H.J. Hwang et al. [36] on LaCoO3 films prepared by PLD and sol-gel methods, respectively. This demonstrates that the reactive magnetron sputtering technique is efficient for preparing crystallized lanthanum cobaltite films at rather low temperatures.
This calcination step at 500 °C was performed for all coatings (Figure 3). The thin film with the highest La/Co ratio is not crystallized and only presents small peaks of La2O3 (JCDPS 00-005-0602), probably coming from a high excess of La. On the opposite, for larger atomic ratios, coatings are crystallised with various space groups of the perovskite-type structure. Indeed, the film is cubic (Pm3m space group) for a ratio of 0.87, exhibits a rhomboedric symmetry (R-3c space group) for a ratio of 0.56 and again becomes cubic for a ratio of 0.3.
The morphology of the LaCoO3 coating with the suitable ratio (La/Co = 0.87) was observed by SEM. Figure 4 shows SEM images of the top view and the brittle cross section of the sample before and after the calcination step at 500 °C. The as-deposited coating (Figure 4a,c) covers the surface of the alumina substrate and follows its morphology. This film is quite dense, as shown in the cross-section image (Figure 4a) and adherent with a vitreous appearance characteristic of an amorphous material, in agreement with XRD (Figure 2) [37]. After calcination (Figure 4b), some cracks can be observed especially in the cross section (Figure 4d). The crystallized film is not sticking well with the alumina support and remains quite dense. The cracks were probably formed under stresses during the crystallization or the thermal treatment. In this latter case, the mismatch of thermal expansion coefficients between the perovskite film and the alumina substrate could be at the origin of the delamination (αLaCoO3 ≈ 20 × 10−6 °C−1 [38] and αAl2O3 ≈ 7 × 10−6 °C−1 [39]) of the coating. The thickness of the annealed coating is around 1.5 µm (Figure 4c,d), resulting in a 500 nm.h−1 deposition rate. This result is in agreement with the thickness measured by tactile profilometry.

2.2. Preparation and Characterization of La1-x-ySrxAgyCoO3-α (LSACO) Catalytic Coatings

The experimental parameters used for the synthesis of double substituted cobaltite (denoted as LSACO) coatings on alumina supports are reported in Table 2. The protocol is similar to that developed for the synthesis of pure lanthanum cobaltite (Ar flow rate = 50 sccm, O2 flow rate = 20 sccm, total pressure = 1.5 Pa, draw distance = 45 mm) except the sputtering time which was extended to 4 h to achieve thicker films. The control of the substitution rates of Sr and Ag was achieved by tuning the intensity of the currents dissipated on the metallic targets (Table 2). We assumed that Sr2+ and also Ag+ cations will partially substitute La3+ cations in A sites of the perovskite. This hypothesis is based on the similarity of the ionic radius of La3+ (136 pm) and Ag+ (128 pm) [40]. The Ag content in the perovskites was gradually enhanced by increasing the current applied to the Ag target (LSACO-1 to 4). This was counter-balanced by a progressive decay of the current dissipated to the La target. The Co content has been slightly increased in LSACO-5 compared with LSACO-4, while maintaining constant the Ag, La, and Sr contents (Table 2)
The chemical composition of the as-prepared LSACO coatings was estimated by EDS analysis. Table 3 displays the variations of the atomic percent of each element, without considering the oxygen level which is tricky to quantity by using EDS. The Sr and Ag contents inversely vary in LSACO-1, 2 and 3 while La and Co loadings are fairly stable. Let us note that the chemical composition of LSACO-2 and LSACO-3 is fairly similar with 11 at% of Ag and around 10 and 30 at% of Sr and La, respectively. The high current applied to the Ag target during the preparation of LSACO-4 and LSACO-5 leads to a significant increase in the Ag concentration and a concomitant drop of the La content. In LSACO-4 and LSACO-5, the Ag atomic percent reaches around 25% while the La level is approximately 20%. Surprisingly, the Co concentration decreases in LSACO-5 despite the largest applied current to the Co target. Except LSACO-5, the atomic ratio between cations located in A sites (theoretically La3+, Sr2+ and Ag+) and Co3+ ones located in B sites is close to the target of 1. The morphology of the as-deposited coatings (Figure 5) was found to drastically change with the chemical composition. The LSACO-1 coating only contains few perovskite clusters (Figure 5a, white spots at the top right) dispersed on the surface of the micrometric alumina grains (Figure 5, dark grey), despite of the 4 h deposition time. For LSACO-2 and LSACO-3, the number of perovskite clusters significantly increases on the surface of the alumina grains (white spots in Figure 5b,c). Interestingly, larger starfish shaped perovskites islands are growing on the substrate defects (cavity of alumina substrate or grain boundaries) showing arms like filaments. The morphology of the surface of LSACO-4 and LSACO-5 coatings (Figure 5d,e) are quite different. The alumina substrate is now fairly fully covered by a porous film with a wire-like morphology (Figure 5d,e). These wires have grown parallel to each other, leading void between each other, reaching a length of the order of 1 µm and a diameter of around 100 nm. Therefore, high Ag contents seem to strongly enhance the porosity and then the coverage of the films.
These series of LSACO coatings were annealed at 500 °C for 2 h in air. This calcination step was sufficient to crystallize all the films as a cubic perovskite phase (JCPDS 01-075-0279) whatever the composition. On the other hand, an additional XRD pattern at 44.3° on the diffractogramm of LSACO-4 and LSACO-5, corresponding to (2 0 0) planes of fcc metallic silver, proves the presence of metallic Ag, out of the perovskite structure. These results demonstrate the limited solubility of Ag in the perovskite in agreement with previous studies [32]. For high contents of Ag, reaching 25 at. %, i.e., around 10 at% in the overall oxide including the oxygen atoms, part of Ag is not incorporated into the perovskite structure. No XRD peaks corresponding to Ag° were observed for LSAC0-1, LSACO-2, and LSACO-3 (Figure 6), but the low content of Ag, below 5 at%, makes difficult their detection. Therefore, we cannot exclude the presence of metallic Ag on the surface of these samples.
Figure 7 displays the surface morphology of the calcinated films. The alumina substrates are cracked probably due to the thermal treatment. The LSACO-1 coating only contains isolated perovskites clusters on the surface of alumina grains. As before calcination, the morphology of LSACO-2 and LSACO-3 coatings are similar with perovskite islands mainly located in the cavity and interstices of the alumina substrate. Filaments that were present around of the perovskite clusters have disappeared. Coatings containing high Ag loadings (LSACO-4 and LSACO-5) are the only ones able to fully cover the alumina substrate with a porous wire-like morphology. These nanowires are less ordered than before calcination and interlock, then decreasing the porosity of the film. Ag particles (Figure 7e) can be observed on the surface of LSACO-5 (white particles), confirming that a part of Ag was not incorporated into the perovkiste structure.

2.3. Catalytic Performances of the Perovskite Coatings

2.3.1. Catalytic Performances for CO Oxidation

The catalytic activity of LSACO-2, LSACO-4, and LSACO-5 coatings, containing respectively 11, 25 and 28 at% of Ag, was measured for CO oxidation during heating ramps up to 400 °C. We have selected LSACO-4 and LSACO-5 as these films exhibit a porous and wire-like morphology. We have also tested the catalytic performances for CO oxidation of pure lanthanum cobaltite coatings. These samples have shown no activity below 500 °C in good agreement with their dense morphology. The catalyst LSACO-2 was also tested for comparison as a non-porous and non-covering representative layer. In addition, we have also tested, for comparison, a Pt coating (3 µm thick, 5 mg Pt/cm2) prepared by spray-painting and annealed at 500 °C. Figure 8 displays the Light-off (LO) curves of the different catalytic coatings for CO oxidation. The results show that the catalytic performances increase with the silver content in the film. Values of T20, temperature at 20% conversion, significantly decrease from 280 to 215 °C when increasing the Ag content. Furthermore, the catalytic performances of LSACO-5 are rather close to those of the Pt coating up to 220 °C. This underlines the promising catalytic activity of the sputtered Ag-doped perovskite coating.
Two successive LO up to 400 °C have been performed on LSACO-4 (Figure 9a). The value of T20 increases from 215 to 242 °C during the second LO. This indicates that a modification of the coating morphology during the first LO, most probably due to the Ag particles sintering. Nevertheless, the onset temperature slightly decreases from 175 to 150 °C (Figure 9a). Similar catalytic experiments have been carried out on LSACO-5 (Figure 9b) without any significant modification of the catalytic performances between the two successive LO. This indicates a better stability of the morphology of LSACO-5 in the presence of the reactive mixture up to 400°C compared with LSACO-4. XPS measurements performed after catalytic tests evidence a La surface seggregation with a concommitant drop of the Co concentration. The two catalytic coatings show a similar Ag surface atomic concentration, i.e., around 10 at%, which is far lower from the loading estimated by EDS before the catalytic tests (Table 3). The Ag3d XPS peaks (Figure 10) show a binding energy of Ag3d5/2 at 367.7 eV, attributed to metallic silver. The catalytic properties during the second LO of the two catalytic perovskite coatings are fairly similar, in good agreement with an equivalent Ag surface concentration (Table 4). This confirms the direct link between the surface Ag concentration and the catalytic activity for CO oxidation.

2.3.2. Catalytic Performances in a Model Lean Diesel Exhaust Gas

The catalytic performances of LSACO-4 were explored in a model lean diesel exhaust gas mixture containing 8% O2, 950 ppm CO, 270 ppm NO, 1000 ppm C3H8 and 10% H2O. The LO was recorded up to 375 °C to investigate the low temperature activity. Figure 11 shows the ability of the catalytic coating to oxidize CO and NO into CO2 and NO2, respectively. Below 350 °C, we did not observed any propane oxidation. However, the catalytic coating shows a remarkable activity for NO oxidation from around 225 °C. The NO conversion achieves 30% at 375 °C. CO conversion starts from 250 °C but seems to reach a maximum at only 18% from 350 °C. These results show that, despite a very low mass of catalyst and a complex mixture including the inhibiting effect of H2O, the perovkite catalytic coating can be active at low temperature for low temperature NO and CO oxidation.

3. Materials and Methods

3.1. Preparation of the Catalytic Coatings

LaCoO3 perovskite coatings were synthesized by magnetron sputtering from two metallic targets of La (kurt J. Lekser, purity 99.9%, Hastings, England) and Co (kurt J. Lekser, purity 99.9%). The Alcatel SCM 604 reactor, described elsewhere [33], was a 90-l sputtering chamber where a pressure of 10−4 Pa was maintained by a primary pump assisted by a molecular turbo pump. The La metallic target (thickness = 3 mm; diameter = 50 mm) and the Co one (thickness = 1 mm; diameter = 50 mm) were attached to two magnetrons distant from 120 mm and connected to a pulsed direct current generator (PINACLE+ purchased by advance energy). The distance between the two targets and the substrate holder (DT-S) can be independently modified. The draw distance between the targets and the alumina substrate was adjusted to 45 mm (Table 1). The targets are powered with pulsed currents to avoid any electric micro-arcs that can damage the quality of the films [41]. To avoid any accumulation of positive charge (Ar+) on the targets, the current is periodically stopped for very short dead time of 5 µS. Gases were introduced with mass-flow controllers (Brooks, 5850 SLA, Hatfield, PA, USA) and the total working pressure was measured with a MKS Baratron gauge. Films were deposited on dense alumina pellets (Keral 99, diameter = 16 mm, thickness = 0.60 mm purchased by Kerafol Gmbh, (Koppe Platz 1, Eschenbach i. d. Opf). The synthesis of doped perovskites with Sr and Ag was performed with the addition of two magnetrons into the sputtering chamber and metallic targets of Sr and Ag (thickness = 3 mm diameter = 50 mm, kurt J. Lekser, purity 99.9%). The Sr and Ag targets were powered by a two pulsed direct current generator (PINACLE+ and MDX500 both purchased by advance energy, Metzingen, Germany).

3.2. Characterizations of the Catalytic Coatings

The crystal structure of the coatings was determined thanks to a BRUKER D8 focus X-Ray diffractometer (Co Kα1+α2 radiations, in Bragg Brentano configuration and equipped with a LynxEye linear detector ( Bruker, Billerica, MA, USA). XRD patterns were collected under air during 10 min in the (20–80°) scattering angle range by steps of 0.019°. The surface and the morphology of films were observed with a scanning electron microscope (JEOL JSM 7800F, Akishima, Japan) equipped with an EDS detector allowing the estimation of the chemical composition of samples. The observation of brittle cross section by SEM led also to the determination of the thickness of films. Coating thickness was also determined by the step method with an Altysurf profilometer produced by Altimet society (Marin, France) equipped with tungsten micro force probe inductive allowing an accuracy of about 20 nm. Before each measurement, the calibration of the experimental device was realized with a reference sample number 787569 accredited by CETIM organization.
XPS spectra were recorded for each catalysts on an AXIS Ultra DLD from Kratos Analytical (Manchester, UK) using a monochromatized Al X-ray source (hv = 1486.6 eV) between 0 and 1200 eV with a pass energy of 40 eV. Sample were pretreated at 200 °C in He before measurements to clean the surface. Peaks were referenced using C1S peak of carbon (BE = 284.6 eV).

3.3. Catalytic Activity Measurements

A quartz reactor was operated under continuous flowing conditions at atmospheric pressure. The samples were placed on a fritted quartz, 18 mm in diameter, with the catalytic coating side facing the fritted quartz [42]. Gases were mixed by using mass-flow controllers (Brooks) to generate the different reactive mixtures. H2O vapor was introduced using an atmospheric pressure Pyrex saturator heated at 46 °C. Reactants and products were analyzed using a gas micro-chromatograph (SRA 3000 equipped with two TCD detectors, a molecular sieve and a Porapak Q column for O2, CO, C3H6, and CO2 analysis) and a CO2 Infra-Red analyzer (Horiba VA 3000, Horiba Europe Gmbh, Leichlingen, Germany). NO and NO2 concentrations were measured with IR and UV online analyzers (EMERSON NGA2000).
Reactants were Air Liquide certified standards of NO in He (8000 ppm), C3H8 in He (8005 ppm), CO in He (1%), O2 (99.999%), which could be further diluted in (99.999%). The carbon and nitrogen balance closure was found to be within 2%.

4. Conclusions

Different compositions of La1-x-ySrxAgyCoO3-α (x = 0.13–0.28, y = 0.14–0.48) doped perovskites were synthetized as thin coatings deposited on alumina disks with the cathodic co-sputtering magnetron method in reactive conditions. The control of different parameters during the sputtering process can tune the morphology of the catalytic films. In particular, we found that the incorporation of high Ag loadings can generate covering films with a porous wire-like morphology showing good catalytic activity for CO oxidation. The most active composition, La0.40Sr0.1Ag0.48Co0.93O3, displays similar catalytic performances than those of a Pt film. In addition, this porous coating is also efficient for CO and NO oxidation in a simulated Diesel exhaust gas mixture, demonstrating the promising catalytic properties of such nanostructured thin sputtered perovskite films.

Author Contributions

Investigation, M.A.P.Y. and L.L.; data curation, P.B. and P.V.; writing—original draft preparation, M.A.P.Y, P.B., and P.V.; writing—review and editing, P.B. and P.V.; formal analysis: A.B., P.V. supervision, A.B., P.B. and P.V.; project administration, P.B.; funding acquisition, P.B., P.V. and A.B.

Funding

The research was funded by “ADEME” in the frame of the ADIABACAT project and “Pays de Montbéliard Agglomération”.

Conflicts of Interest

The authors declare no conflict of interest. The founding sponsors had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Fino, D. Diesel emission control: Catalytic filters for particulate removal. Sci. Technol. Adv. Mater. 2007, 8, 93–100. [Google Scholar] [CrossRef]
  2. Wang, X.; Zhang, Y.X.; Li, Q.; Wang, Z.P.; Zhang, Z.L. Identification of active oxygen species for soot combustion on LaMnO3 perovskite. Catal. Sci. Technol. 2012, 2, 1822–1824. [Google Scholar] [CrossRef]
  3. Hernández, W.Y.; Tsampas, M.N.; Zhao, C.; Boreave, A.; Bosselet, F.; Vernoux, P. La/Sr-based perovskites as soot oxidation catalysts for Gasoline Particulate Filters. Catal. Today 2015, 258, 525–534. [Google Scholar] [CrossRef]
  4. Pena, M.A.; Fierro, J.L.G. Chemical Structures and Performance of Perovskite Oxides. Chem. Rev. 2001, 101, 1981–2017. [Google Scholar] [CrossRef] [PubMed]
  5. Ciambelli, P.; Cimino, S.; Lisis, L.; Faticanti, M.; Minelli, G.; Pettiti, I.; Porta, P. La, Ca and Fe oxide perovskites: Preparation, characterization and catalytic properties for methane combustion. Appl. Catal. B 2001, 33, 193–203. [Google Scholar] [CrossRef]
  6. Song, K.S.; Cui, H.X.; Kim, S.D.; Kang, S.K. Catalytic combustion of CH4 and CO on La1−xMxMnO3 perovskites. Catal. Today 1999, 47, 155–160. [Google Scholar] [CrossRef]
  7. Hwang, H.J.; Awano, M. Preparation of LaCoO3 catalytic thin film by the sol–gel process and its NO decomposition characteristics. J. Eur. Ceram. Soc. 2001, 21, 2103–2107. [Google Scholar] [CrossRef]
  8. Teng, F.; Liang, S.; Gaugeu, B.; Zong, R.; Yao, W.; Zhu, Y. Carbon nanotubes-templated assembly of LaCoO3 nanowires at low temperatures and its excellent catalytic properties for CO oxidation. Catal. Commun. 2007, 8, 1748–1754. [Google Scholar] [CrossRef]
  9. Hattori, T.; Matsui, T.; Tsuda, H.; Mabuchi, H.; Morii, K. Fabrication and electric properties of LaCoO3 thin films by ion-beam sputtering. Thin Solid Films 2001, 388, 183–188. [Google Scholar] [CrossRef]
  10. López, M.L.; Arillo, M.A.; Álvarez-Serrano, I.; Martín, P.; Rodríguez, E.; Pico, C.; Veiga, M.L. Random spin configurations of Co cations in LaCo1−xMgxO3 (0 <x ≤ 0.20) perovskite oxides: Magnetic and transport properties. Mater. Chem. Phys. 2010, 120, 387–392. [Google Scholar] [CrossRef]
  11. Uhlenbruck, S.; Tietz, F. High-temperature thermal expansion and conductivity of cobaltites: Potentials for adaptation of the thermal expansion to the demands for solid oxide fuel cells. Mater. Sci. Eng. B 2004, 107, 277–282. [Google Scholar] [CrossRef]
  12. Ullmann, H.; Trofimenko, N.; Tietz, F.; Stöver, D.; Ahmad-Khanlou, A. Correlation between thermal expansion and oxide ion transport in mixed conducting perovskite-type oxides for SOFC cathodes. Solid State Ion. 2000, 138, 79–90. [Google Scholar] [CrossRef]
  13. Ringuedé, A.; Fouletier, J. Oxygen reaction on strontium-doped lanthanum cobaltite dense electrodes at intermediate. Solid State Ion. 2001, 139, 167–177. [Google Scholar] [CrossRef]
  14. Weidenkaff, A.; Robert, R.; Aguirre, M.; Bocher, L.; Lippert, T.; Canulescu, S. Development of thermoelectric oxides for renewable energy conversion technologies. Renew. Energy 2008, 33, 342–347. [Google Scholar] [CrossRef]
  15. Anh, D.T.V.; Olthuis, W.; Bergveld, P. Sensing properties of perovskite oxide La0.5Sr0.5CoO3−δ obtained by using pulsed laser deposition. Sens. Actuators B 2004, 103, 165–168. [Google Scholar] [CrossRef]
  16. Popa, M.; Hong, L.V.; Kakihana, M. Particle morphology characterization and magnetic properties of LaMnO3+d perovskites. Phys. B Condens. Matter 2003, 327, 237–240. [Google Scholar] [CrossRef]
  17. Ngamou, P.H.T.; Bahlawane, N. Chemical vapor deposition and electric characterization of perovskite oxides LaMO3 (M=Co, Fe, Cr and Mn) thin films. J. Solid State Chem. 2009, 182, 849–854. [Google Scholar] [CrossRef]
  18. Popa, M.; Calderón-Moreno, J.M. Lanthanum cobaltite thin films on stainless steel. Thin Solid Films 2009, 517, 1530–1533. [Google Scholar] [CrossRef]
  19. Roche, V.; Siebert, E.; Steil, M.C.; Deloume, J.P.; Roux, C.; Pagnier, T.; Revel, R.; Vernoux, P. Electrochemical promotion of propane deep oxidation on doped lanthanum manganites. Ionics 2008, 14, 235–241. [Google Scholar] [CrossRef]
  20. Seim, H.; Nieminen, M.; Niinisto, L.; Fjellvag, H.; Johansson, L.S. Growth of LaCoO3 thin films from β-diketonate precursors. Appl. Surf. Sci. 1997, 112, 243–250. [Google Scholar] [CrossRef]
  21. Robert, R.; Aguirre, M.H.; Bocher, L.; Trottmann, M.; Heiroth, S.; Lippert, T.; Döbeli, M.; Weidenkaff, A. Thermoelectric properties of LaCo1−xNixO3 polycrystalline samples and epitaxial thin films. Solid State Sci. 2008, 10, 502–507. [Google Scholar] [CrossRef]
  22. Karoum, R.; Roche, V.; Pirovano, C.; Vannier, R.; Billard, A.; Vernoux, P. CGO-based electrochemical catalysts for low temperature combustion of propene. J. Appl. Electrochem. 2010, 40, 1867–1873, ISSN: 0021-891X (Print) 1572-8838 (Online). [Google Scholar] [CrossRef]
  23. Cui, W.Y.; Li, P.; Bai, H.L. Spin-state configuration induced faster spin dynamics in epitaxial La1−xSrxCoO3 thin films. Solid State Commun. 2015, 209–210, 49–54. [Google Scholar] [CrossRef]
  24. Tsiakaras, P.; Athanasiou, C.; Marnellos, G.; Stoukides, M.; Elshof, J.E.T.; Bouwmeester, H.J.M. Methane activation on a La0.6Sr0.4Co0.8Fe0.2O3 perovskite: Catalytic and electrocatalytic results. Appl. Catal. A Gen. 1998, 169, 249–261. [Google Scholar] [CrossRef]
  25. Gaillard, F.; Li, X.; Uray, M.; Vernoux, P. Electrochemical Promotion of Propene Combustion in Air Excess on Perovskite Catalyst. Catal. Lett. 2004, 96, 177–183, ISSN: 1011-372X (Print) 1572-879X (Online). [Google Scholar] [CrossRef]
  26. Vernoux, P.; Lizarraga, L.; Tsampas, M.N.; Sapountzi, F.M.; de Lucas-Consuegra, A.; Valverde, J.L.; Souentie, S.; Vayenas, C.G.; Tsiplakides, D.; Balomenou, S.; et al. Ionically Conducting Ceramics as Active Catalyst Supports. Chem. Rev. 2013, 113, 8192–8260. [Google Scholar] [CrossRef]
  27. Monaghan, D.; Arnell, R.D. Novel PVD films by unbalanced magnetron sputtering. Vacuum 1992, 43, 77–81. [Google Scholar] [CrossRef]
  28. Kelly, P.J.; O’Brien, J.; Arnell, R.D. The production of porous and chemically reactive coatings by magnetron sputtering. Vacuum 2004, 74, 1–10. [Google Scholar] [CrossRef]
  29. Rousseau, S.; Loridant, S.; Delichere, P.; Boreave, A.; Deloume, J.P.; Vernoux, P. La(1−x)SrxCo1−yFeyO3 perovskites prepared by sol–gel method: Characterization and relationships with catalytic properties for total oxidation of toluene. Appl. Catal. B 2009, 88, 438–447. [Google Scholar] [CrossRef]
  30. O’Connell, M.; Norman, A.K.; Huttermann, C.F.; Morris, M.A. Catalytic oxidation over lanthanum-transition metal perovskite materials. Catal. Today 1999, 47, 123–132. [Google Scholar] [CrossRef]
  31. Pecchi, G.; Campos, C.M.; Jiliberto, M.G.; Delgado, E.J.; Fierro, J.L.G. Effect of additive Ag on the physicochemical and catalytic properties of LaMn0.9Co0.1O3.5 perovskite. Appl. Catal. A 2009, 371, 78–84. [Google Scholar] [CrossRef]
  32. Hernández, W.Y.; Lopez-Gonzalez, D.; Ntais, S.; Zhao, C.; Boréave, A.; Vernoux, P. Silver-modified manganite and ferrite perovskites for catalyzed gasoline particulate filters. Appl. Catal. B 2018, 226, 202–212. [Google Scholar] [CrossRef]
  33. Yazdi, M.A.P.; Briois, P.; Georges, S.; Lapostolle, F.; Billard, A. Structural and electrical characterisation of strontium zirconate proton conductor co-sputter deposited coatings. Ionics 2008, 14, 285–291, ISSN: 0947-7047 (Print) 1862-0760 (Online). [Google Scholar] [CrossRef]
  34. Yazdi, M.A.P.; Briois, P.; Billard, A. Influence of the annealing conditions on the structure of BaCe1−xYxO3−α coatings elaborated by DC magnetron sputtering at room temperature. Mater. Chem. Phys. 2009, 117, 178–182. [Google Scholar] [CrossRef]
  35. Creus, J.; Berziou, C.; Cohendoz, S.; Perez, A.; Rébéré, C.; Reffass, M.; Touzain, S.; Allely, C.; Gachon, Y.; Héau, C.; et al. Reactivity classification in saline solution of magnetron sputtered or EBPVD pure metallic, nitride and Al-based alloy coatings. Corros. Sci. 2012, 57, 162–173. [Google Scholar] [CrossRef]
  36. Hwang, H.J.; Moon, J.; Awano, M.; Maeda, K. Sol–Gel Route to Porous Lanthanum Cobaltite (LaCoO3) Thin Films. J. Am. Ceram. Soc. 2004, 83, 2852–2854. [Google Scholar] [CrossRef]
  37. Sanchette, F.; Billard, A.; Frantz, C. Mechanically reinforced and corrosion-resistant sputtered amorphous aluminium alloy coatings. Surf. Coat. Technol. 1998, 98, 1162–1168. [Google Scholar] [CrossRef]
  38. Tietz, F. Thermal expansion of SOFC materials. Ionics 1999, 5, 129–139. [Google Scholar] [CrossRef]
  39. Abe, O.; Taketa, Y.; Haradome, M. The Effect of Various Factors on the Resistance and TCR of RuO2 Thick Film Resistors—Relation Between the Electrical Properties and Particle Size of Constituents, the Physical Properties of Glass and Firing Temperature. Act. Passiv. Electron. Compon. 1988, 13, 67–83. [Google Scholar] [CrossRef]
  40. Shannon, R.D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallogr. 1976, A32, 751–767. [Google Scholar] [CrossRef]
  41. Billard, A.; Perry, F. Techniques de l’ingenieur, M1654. Available online: https://www.techniques-ingenieur.fr/base-documentaire/materiaux-th11/traitements-de-surface-des-metaux-par-voie-seche-et-en-milieu-fondu-42360210/pulverisation-cathodique-magnetron-m1654/ (accessed on 22 April 2019).
  42. Vernoux, P.; Gaillard, F.; Bultel, L.; Siebert, E.; Primet, M. Electrochemical Promotion of Propane and Propene Oxidation on Pt/YSZ. J. Catal. 2002, 208, 412–421. [Google Scholar] [CrossRef]
Catalysts 09 00381 g001 550
Figure 1. Evolution of the atomic La/Co ratio measured by Energy Dispersive Spectroscopy (EDS) as a function of the current dissipated on the Co target (ILa = 1 A). The total pressure is 1.5 Pa.
Figure 1. Evolution of the atomic La/Co ratio measured by Energy Dispersive Spectroscopy (EDS) as a function of the current dissipated on the Co target (ILa = 1 A). The total pressure is 1.5 Pa.
Catalysts 09 00381 g001
Catalysts 09 00381 g002 550
Figure 2. X-Ray diffractograms of LaCoO3 sputtered films prepared with a current dissipated on the Co target of 0.3 A (La/Co = 0.87) after different post-calcination treatments during 2 h in air from 100 °C to 500 °C.
Figure 2. X-Ray diffractograms of LaCoO3 sputtered films prepared with a current dissipated on the Co target of 0.3 A (La/Co = 0.87) after different post-calcination treatments during 2 h in air from 100 °C to 500 °C.
Catalysts 09 00381 g002
Catalysts 09 00381 g003 550
Figure 3. XRD patterns as a function of the atomic composition ratio after calcination treatment at 500 °C for 2 h under air.
Figure 3. XRD patterns as a function of the atomic composition ratio after calcination treatment at 500 °C for 2 h under air.
Catalysts 09 00381 g003
Catalysts 09 00381 g004 550
Figure 4. SEM images of the surface and the brittle cross section of the LaCoO3 sample synthesized with ICo = 0.3 A and ILa = 1 A: (a,c) as deposited coating and (b,d) after calcination treatment at 500 °C for 2 h under air.
Figure 4. SEM images of the surface and the brittle cross section of the LaCoO3 sample synthesized with ICo = 0.3 A and ILa = 1 A: (a,c) as deposited coating and (b,d) after calcination treatment at 500 °C for 2 h under air.
Catalysts 09 00381 g004
Catalysts 09 00381 g005 550
Figure 5. SEM images of the surface morphology of as-deposited LSACO coatings on alumina substrate: (a) LSACO-1, (b) LSACO-2, (c) LSACO-3, (d) LSACO-4, and (e) LSACO-5.
Figure 5. SEM images of the surface morphology of as-deposited LSACO coatings on alumina substrate: (a) LSACO-1, (b) LSACO-2, (c) LSACO-3, (d) LSACO-4, and (e) LSACO-5.
Catalysts 09 00381 g005
Catalysts 09 00381 g006 550
Figure 6. XRD patterns after the calcination treatment at 500 °C for 2 h under air of the different LSACO coatings.
Figure 6. XRD patterns after the calcination treatment at 500 °C for 2 h under air of the different LSACO coatings.
Catalysts 09 00381 g006
Catalysts 09 00381 g007 550
Figure 7. SEM images of the surface morphology of calcined LSACO coatings on alumina substrate: (a) LSACO-1, (b) LSACO-2, (c) LSACO-3, (d) LSACO-4, and (e) LSACO-5.
Figure 7. SEM images of the surface morphology of calcined LSACO coatings on alumina substrate: (a) LSACO-1, (b) LSACO-2, (c) LSACO-3, (d) LSACO-4, and (e) LSACO-5.
Catalysts 09 00381 g007
Catalysts 09 00381 g008 550
Figure 8. Light-off curves for CO oxidation recorded on the sputtered perovskite coatings and on Pt film. Reactive mixture: CO/O2 = 3000 ppm/3%. Overall flow = 3.6 L/h.
Figure 8. Light-off curves for CO oxidation recorded on the sputtered perovskite coatings and on Pt film. Reactive mixture: CO/O2 = 3000 ppm/3%. Overall flow = 3.6 L/h.
Catalysts 09 00381 g008
Catalysts 09 00381 g009 550
Figure 9. Two successive LO recorded on (a) LSACO-4 and (b) LSACO-5. Reactive mixture: CO/O2 = 3000 ppm/3%. Overall flow = 3.6 L/h.
Figure 9. Two successive LO recorded on (a) LSACO-4 and (b) LSACO-5. Reactive mixture: CO/O2 = 3000 ppm/3%. Overall flow = 3.6 L/h.
Catalysts 09 00381 g009
Catalysts 09 00381 g010 550
Figure 10. Ag3d XPS spectrum of LSAC-5.
Figure 10. Ag3d XPS spectrum of LSAC-5.
Catalysts 09 00381 g010
Catalysts 09 00381 g011 550
Figure 11. Variation of CO and NO conversion as a function of temperature on LSACO-4. Reactive mixture: CO/O2/NO/C3H8/H2O: 950 ppm/8%/270 ppm/1000 ppm/10%. Overall flow: 3.6 L/h.
Figure 11. Variation of CO and NO conversion as a function of temperature on LSACO-4. Reactive mixture: CO/O2/NO/C3H8/H2O: 950 ppm/8%/270 ppm/1000 ppm/10%. Overall flow: 3.6 L/h.
Catalysts 09 00381 g011
Table
Table 1. Sputtering parameters used for LaCoO3 coating.
Table 1. Sputtering parameters used for LaCoO3 coating.
TargetIntensity (A)Pulse Frequency (kHz)Dead Time (Toff µs)Ar Flow Rate (sccm) *O2 Flow Rate (sccm) *Total Pressure (Pa)Draw Distance (mm)Sputtering Time (h)
La150550201.5453
Co0.2 to 0.4
* sccm = Standard Cubic Centimeter per Minutes.
Table
Table 2. Sputtering parameters used for LSACO coatings.
Table 2. Sputtering parameters used for LSACO coatings.
CoatingILa (A) Pulse (kHz)/Toff (µs)ISr (A) Pulse (kHz)/Toff (µs)IAg (A) Pulse (kHz)/Toff (µs)ICo (A) Pulse (kHz)/Toff (µs)
LSACO-11.2 50/51.2 350/1.40.008 00.35 50/5
LSACO-20.8 50/51.1 350/1.40.009 00.35 50/5
LSACO-30.75 50/51.1 350/1.40.01 00.35 50/5
LSACO-40.6 50/51.1 350/1.40.013 00.35 50/5
LSACO-50.6 50/51.1 350/1.40.013 00.4 50/5
Table
Table 3. Chemical composition determined by EDS of the as-prepared La1-x-ySrxAgyCoO3-α (LSCAO) perovskite coatings.
Table 3. Chemical composition determined by EDS of the as-prepared La1-x-ySrxAgyCoO3-α (LSCAO) perovskite coatings.
CoatingsLa (at%)Sr (at%)Ag (at%)Co (at%)Chemical Formula
LSACO-129 ± 0.2914 ± 0.147 ± 0.0750 ± 0.5La0.58Sr0.28Ag0.14Co1O3
LSACO-229 ± 0.2911 ± 0.1111 ± 0.1149 ± 0.5La0.56Sr0.23Ag0.21Co0.94O3
LSACO-332 ± 0.329 ± 0.111 ± 0.1148 ± 0.5La0.61Sr0.18Ag0.21Co0.92O3
LSACO-420 ± 0.207 ± 0.125 ± 0.2548 ± 0.5La0.39Sr0.13Ag0.49Co0.93O3
LSACO-521 ± 0.219 ± 0.128 ± 0.2842 ± 0.4La0.40Sr0.20Ag0.48Co0.70O3
Table
Table 4. Surface composition determined by XPS of LSACO-4 and LSACO-5 after catalytic tests.
Table 4. Surface composition determined by XPS of LSACO-4 and LSACO-5 after catalytic tests.
SampleLa at%Sr at%Ag at%Co at%
LSACO-447 111230
LSACO-551131026

Share and Cite

MDPI and ACS Style

Arab Pour Yazdi, M.; Lizarraga, L.; Vernoux, P.; Billard, A.; Briois, P. Catalytic Properties of Double Substituted Lanthanum Cobaltite Nanostructured Coatings Prepared by Reactive Magnetron Sputtering. Catalysts 2019, 9, 381. https://doi.org/10.3390/catal9040381

AMA Style

Arab Pour Yazdi M, Lizarraga L, Vernoux P, Billard A, Briois P. Catalytic Properties of Double Substituted Lanthanum Cobaltite Nanostructured Coatings Prepared by Reactive Magnetron Sputtering. Catalysts. 2019; 9(4):381. https://doi.org/10.3390/catal9040381

Chicago/Turabian Style

Arab Pour Yazdi, Mohammad, Leonardo Lizarraga, Philippe Vernoux, Alain Billard, and Pascal Briois. 2019. "Catalytic Properties of Double Substituted Lanthanum Cobaltite Nanostructured Coatings Prepared by Reactive Magnetron Sputtering" Catalysts 9, no. 4: 381. https://doi.org/10.3390/catal9040381

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.