Modeling and Experimental Study of Double-Row Bow-Type Micro-Displacement Amplifier for Direct-Drive Servo Valves
Next Article in Special Issue
Self-Aligned Hierarchical ZnO Nanorod/NiO Nanosheet Arrays for High Photon Extraction Efficiency of GaN-Based Photonic Emitter
Previous Article in Journal
A Comparative Study of Cavitation Characteristics of Nano-Fluid and Deionized Water in Micro-Channels
Previous Article in Special Issue
Silver Nanorings Fabricated by Glycerol-Based Cosolvent Polyol Method
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Micromachines
Volume 11
Issue 3
10.3390/mi11030311
micromachines-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of the Ammonium Tungsten Precursor Solution with the Modification of Glycerol on Wide Band Gap WO3 Thin Film and Its Electrochromic Properties

by
Jinxiang Liu
1,
Guanguang Zhang
1,
Kaiyue Guo
1,
Dong Guo
2,
Muyang Shi
1,
Honglong Ning
1,*,
Tian Qiu
3,
Junlong Chen
1,
Xiao Fu
1,
Rihui Yao
1,4,* and
Junbiao Peng
1
1
Institute of Polymer Optoelectronic Materials and Devices, State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou 510640, China
2
School of Medical Instrument & Food Engineering, University of Shanghai for Science and Technology, No.516 Jungong Road, Shanghai 200093, China
3
Department of Intelligent Manufacturing, Wuyi University, Jiangmen 529000, China
4
Guangdong Province Key Lab of Display Material and Technoloy, Sun Yat-sen University, Guangzhou 510275, China
*
Authors to whom correspondence should be addressed.
Micromachines 2020, 11(3), 311; https://doi.org/10.3390/mi11030311
Submission received: 11 February 2020 / Revised: 11 March 2020 / Accepted: 14 March 2020 / Published: 16 March 2020
(This article belongs to the Special Issue Wide Bandgap Based Devices: Design, Fabrication and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
Tungsten trioxide (WO3) is a wide band gap semiconductor material, which is commonly not only used, but also investigated as a significant electrochromic layer in electrochromic devices. WO3 films have been prepared by inorganic and sol-gel free ammonium tungstate ((NH4)2WO4), with the modification of glycerol using the spin coating technique. The surface tension, the contact angle and the dynamic viscosity of the precursor solutions demonstrated that the sample solution with a 25% volume fraction of glycerol was optimal, which was equipped to facilitate the growth of WO3 films. The thermal gravimetric and differential scanning calorimetry (TG-DSC) analysis represented that the optimal sample solution transformed into the WO3 range from 220 °C to 300 °C, and the transformation of the phase structure of WO3 was taken above 300 °C. Fourier transform infrared spectroscopy (FT-IR) spectra analysis indicated that the composition within the film was WO3 above the 300 °C annealing temperature, and the component content of WO3 was increased with the increase in the annealing temperature. The X-ray diffraction (XRD) pattern revealed that WO3 films were available for the formation of the cubic and monoclinic crystal structure at 400 °C, and were preferential for growing monoclinic WO3 when annealed at 500 °C. Atomic force microscope (AFM) images showed that WO3 films prepared using ammonium tungstate with modification of the glycerol possessed less rough surface roughness in comparison with the sol-gel-prepared films. An ultraviolet spectrophotometer (UV) demonstrated that the sample solution which had been annealed at 400 °C obtained a high electrochromic modulation ability roughly 40% at 700 nm wavelength, as well as the optical band gap (Eg) of the WO3 films ranged from 3.48 eV to 3.37 eV with the annealing temperature increasing.

1. Introduction

Currently, an increasing amount of attention has been concentrated on energy saving in buildings for the reason that the energy used for these is in excess of 30% of the consumption of the total energy in the word, as a matter of fact [1]. It is worth mentioning that it is the transition metal oxides that are the fascinating semiconducting materials which possess a variety of properties, applications and functions [2]. Tungsten trioxide (WO3), the most widely studied and used electrochromic material, has been studied for many years since having been found by Deb in the 1960s, thanks to its attractive characteristics of high coloring efficiency, good optical modulation ability and decent chemical stability in the field of electrochromism [3,4,5,6]. It is remarkable that WO3 with various crystalline structures by different synthesis methods is extensively appropriate for diverse device applications [7,8,9], such as the electrochromic smart window [10,11], rear-view automatic-dimming rearview mirror [12], gas sensor device [13,14,15], and military camouflage [16], etc. A large variety of techniques can be used to prepare WO3 thin films, such as chemical vapor deposition (CVD) [17], physical vapor deposition (PVD) [18] and wet chemical deposition methods base on solution [19,20,21]. In fact, the sol-gel technique that is used to prepare WO3 thin films is commonly considered feasible among wet chemical deposition methods due to a good few favorable and conspicuous advantages, such as large-area film formation, a repeatable process and inexpensive experimental facilities [22,23,24]. It is the formation of the gel network by polymerization that the principle of the sol-gel technique for preparing thin films depends on [3]. Nevertheless, it cannot be neglected that there is less satisfaction with thin films prepared by the sol-gel technique because of these following deficiencies, which would be limited in applications in electrochromism and thin film transistors, etc. Not only the stability of the precursor solution for the formation of gel structure is generally not adequate enough, and it would not gratify the industrial production as a significant parameter [25], but also the homogeneity throughout the sol-gel process would not be guaranteed effectively by producing a homogeneous precursor solution at room temperature [26]. Furthermore, there are practical limitations for the reason that thin films with microstructures and nanostructures prepared by the sol-gel technique are more fragile, so that they possibly cannot maintain well their structure in the course of the assembly process of electrochromic devices [27]. It is important to note that wrinkle cracks are observed on the surface of the thin films prepared by the sol-gel technique with the increase in the thickness of films [28,29].
To effectively solve this problem, WO3 thin films can be prepared by the spin coating technique using pure-inorganic ammonium tungstate precursor solution in this present study, which would not obtain the gel structure. In this work, WO3 thin films were successfully prepared using the above precursor solution by the spin coating technique. The glycerol, one kind of excellent solvent with high viscosity, has been utilized to magnify the adhesiveness of the pure-inorganic ammonium tungstate precursor solution, so as to sufficiently facilitate the growth of the WO3 films. The sample solution performance, the film surface morphology, components, crystallization, optical properties and the electrochromic properties, were investigated and discussed through different characterization methods.

2. Materials and Methods

Tungsten trioxide (WO3, <100 nm, 99.9% metals basis, Macklin Biochemical Co. Ltd, Shanghai, China) and ammonia hydroxide (NH3·H2O, AR, 26%, Guangzhou Chemical Reagent Factory, Guangzhou, China) were mixed in a beaker to prepare an ammonium tungstate ((NH4)2WO4) solution. Subsequently, five kinds of sample solution were prepared using glycerol (C3H8O3, AR, Richjoint, Shanghai, China) for modification. According to the different volume fraction of glycerol, the volume fractions of glycerol were 0%, 12.5%, 25%, 37.5% and 50%, respectively, and the concentration of ammonium tungstate solution was approximately 5.5 mol/L. The precursor solutions were uniformly obtained after being ultrasonically oscillated, which were not only transparent, but also sol-gel free. Eventually, all of the WO3 thin films were prepared, using the spin coating technique, onto indium tin oxide (ITO) plane glass substrates (2 × 2 cm2), with spin coating parameters (3500 revolutions per minute for 60 s).
The WO3 thin films were annealed at different temperatures in the air atmosphere: 200 °C, 250 °C, 300 °C, 350 °C, 400 °C, 450 °C and 500 °C, respectively.
The surface tension and the contact angle of the precursor solutions were measured by Attension Theta (Biolin Scientific, TL200, Gothenburg, Sweden). The dynamic viscosity measurements of the precursor solutions were implemented using a rotational rheometer (Thermo Fisher Scientific, HAAKE MARS 40, MA, USA). Thermal gravimetric analysis (TGA) and differential scanning calorimetry were characterized by a Differential Scanning Calorimeter (DSC, Differential Scanning Calorimeter, DSC214, NETZSCH Scientific Instruments Trading (Shanghai) Ltd., Selb, Germany). The thickness of all films was measured by a probe surface profiler (VeecoDektak150, Veeco, Somerset, NJ, USA). The crystalline structure of WO3 thin films was characterized by X-ray Diffraction using Cu Kα radiation (XRD, PANalytical Empyrean DY1577, PANalytical, Almelo, The Netherlands), and the XRD patterns were analyzed using the software Jade 6.0. As well as this, Fourier transform infrared spectroscopy (FT-IR) spectra of the solutions were recorded by an FT-IR spectrophotometer (SHIMADZU IR Prestige-21, SHIMADZU, Tokyo, Japan) with an ITO glass substrate acting as a blank. The surface morphology was observed by an atomic force microscopy (AFM, Being Nano-Instruments BY3000, Being Nano-Instruments, Beijing, China). The transmittance of the films at the initial state, colored state and bleached state were measured by an ultraviolet spectrophotometer (SHIMADZU UV2600, SHIMADZU, Tokyo, Japan), with air acting as a blank. The current of the electrochromic test and the relationship between the change of transmittance and the time were recorded by an electrochemical workstation (CH Instruments CHI600E, CH Instruments, Shanghai, China) and a micro-spectrometer (Morpho PG2000, Morpho, Shanghai, China), respectively.

3. Results and Discussion

The surface tension, the contact angle and the dynamic viscosity of all the precursor solutions are illustrated in Figure 1. Figure 1a shows that as the volume fraction of modified-ammonia tungstate glycerol increases, keeping the volume of the precursor solutions consistent, both of the surface tension and the contact angle decrease first, and then increase while obtaining a minimum in the sample solution with 25% volume fraction glycerol. As shown in Figure 1b, the dynamic viscosity of the solutions characterizes an increasing tendency with the increase in the volume of the glycerol. As defined, when the droplet has a tendency to spread out on the solid surface, not only the solid–liquid contact surface increases and the contact angle decreases, but also the surface tension decreases. In other words, the smaller the surface tension and the contact angle, the better the surface wettability of the solution on the substrate. Additionally, bigger dynamic viscosity could facilitate the growth of films. In comparison to dynamic viscosity, the surface tension and the contact angle exert a decisive part in selecting the optimal solution in this work. As a consequence, the ammonium tungstate solution with 25% volume fraction glycerol is used to grow WO3 thin films in this work.
Figure 2 shows the thermal gravimetric and differential scanning calorimetry (TG-DSC) curves of the sample solution with 25% volume fraction glycerol and the thickness of the films annealed at different temperatures. The sample solution successively loses weight from room temperature to approximately 300 °C, as shown in the TG curve. The drastic weight loss can be as a result of the water evaporation range from room temperature to 140 °C [30]. It was the pyrolysis of glycerol and the further evaporation of water that a continuous weight loss of the solution range from 140 °C to 220 °C results from [31]. It can be seen that there are multiple weak endothermic peaks and exothermic peaks, and the weight of the sample solution reduces in the temperature between 220 °C and 300 °C, which is presumably ascribed to the formation of WO3 from ammonium tungstate. The weight of the sample solution was not observed to change obviously above 300 °C. Besides, the thickness of the WO3 films decreases drastically between 200 °C and 300 °C, as shown in Figure 2b. The drastic drop of thickness probably results from the water evaporation and the pyrolysis of glycerol. The further change in thickness would be analyzed through the FT-IR and XRD. Furthermore, the slowly endothermic process between 300 °C and 460 °C could be observed, which is possibly attributed to the transformation of phase structure of WO3 from ammonium tungstate.
On the other hand, according to DSC analysis, it is concluded that the phase structure of WO3 was also transformed along with exothermic process above 460 °C. The further phase structure transformation of WO3 would be characterized and analyzed through XRD measurement.
The FT-IR spectra of the sample solution with a 25% volume fraction of glycerol are illustrated in Figure 3, which were annealed at 300 °C, 350 °C, 400 °C, 450 °C and 500 °C, respectively. It can be seen that there are a sharp peak at approximately 980 cm−1 and a weak peak at around 690 cm−1, which respectively correspond to the characteristic W=O stretching vibration and W–O–W stretching vibration [32,33], revealing the successful formation of WO3 from ammonium tungstate when WO3 films were annealed above 300 °C, which is consistent with the result of the TG-DSC analysis. In addition, the sharp peak shifts to a higher wavenumber, and becomes sharper from 300 °C to 350 °C in indication of that the W=O bond length shortens and the W=O bond vibrational steric resistance increases. It is indicated that the film structure becomes dense from loose, and the thickness of film deceases at 350 °C. Besides, the decrease in the film thickness in the temperature stage of 400–500 °C is also attributed to the densification of the film in the case of the stable content of WO3 in the film. As shown in Figure 3, both of the two peaks were intensified with the increase in the annealing temperature, which indicated that a mounting number of WO3 was generated, and the WO3 thin film was prone to be purer. According to FT-IR analysis, WO3 is the dominant composition within the films instead of glycerol as the annealing temperature increases.
Figure 4a–f presents the AFM 2D and 3D images (5000 nm × 5000 nm) of the WO3 thin films prepared using the sample solution with 25% volume fraction glycerol, which were annealed at different temperatures for an hour. Moreover, the surface roughness and the surface grain size of these films are illustrated in Figure 4g. As shown in Figure 4a,b, it is revealed that the WO3 thin film which was annealed at 200 °C is almost smooth and homogeneous. There are few surface grains on the WO3 thin films annealed at 200 °C for the reason that definite boundary would not be observed. According to the result of TG-DSC analysis, the film annealed at 200 °C did not transform into WO3 yet. With the increase in the annealing temperature, a slightly rough surface is commenced to emerge on the WO3 thin film, which can be observed in Figure 4c,d. There are a great many easily identifiable grains on the surface of the WO3 film in Figure 4e,f, which may be attributed to the crystallization of WO3 when the WO3 film was annealed at 500 °C. This can be confirmed through the result of XRD analysis. The average surface grain size of the WO3 thin films annealed at 200 °C, 350 °C and 500 °C are, respectively, 7.8 nm, 63.6 nm and 74.7 nm. The surface root mean square (RMS) roughness of the WO3 films annealed at 200 °C, 350 °C and 500 °C are 0.38 nm, 1.01 nm and 1.68 nm, respectively. It is worth mentioning that the WO3 films prepared in this work are less rough, with a surface roughness of less than 2 nm in comparison with the sol-gel-prepared WO3 films, although the surface roughness of WO3 films exists a slowly increasing tendency with annealing temperature [34,35,36]. In other words, the WO3 films with less roughness prepared in this work can reduce scattering of the incident light, and are beneficial to the transmission of incident light, so that they are more qualified for application in an electrochromic device [34].
X-ray Diffraction (XRD) is an effective experimental technique to characterize the crystalline structure and the grain size of material. The XRD patterns of the WO3 films prepared using the sample solution with 25% volume fraction glycerol onto ITO glass substrate, and annealed at different temperatures, are illustrated in Figure 5. The diffraction peaks were analyzed using Jade 6.0 and PDF#06-0416, PDF#41-0905 and PDF#30-1387. In the XRD of Figure 5, the diffraction peaks of the WO3 thin films annealed at 200 °C and 300 °C are matched well with Indium Oxide (In2O3), according to PDF#06-0416, indicating acquirement of the amorphous structure of the WO3 film [20,25,37]. It can be confirmed that there are some diffraction peaks of the WO3 film annealed at 400 °C, except for the diffraction peaks of ITO glass substrate in Figure 5. In other words, it is indicated that the crystalline temperature for the WO3 thin films is between 300 °C and 400 °C [2,38]. According to the broad diffraction peak located at approximately 24°, the formation of the WO3 cubic crystal structure is revealed, and monoclinic WO3 also exists at the same time [32]. It is suggested that the crystalline transformation in thin film, making the uplift of the film, results in the increase in thickness at 400 °C. Along with temperature being further increased, the WO3 film was confirmed to be preferential growth to monoclinic crystalline structure, rather than cubic crystalline structure when the WO3 film was annealed at 500 °C [16,39]. Furthermore, this can be in good agreement with the results of TG-DSC curves and AFM images.
Figure 6a–g display the optical transmittance spectra of the WO3 films at the initial state, colored state and bleached state in the wavelength range from 400 nm to 800 nm, which were prepared using the sample solution with 25% volume fraction glycerol, and annealed at different temperatures, and the optical transmittance modulation ability (∆T at 700 nm) curve of these films is illustrated in Figure 6h. The transmittance modulation ability (∆T) can be defined by the following formula at 700 nm wavelength:
∆T=|Tc − Tb|
In this formula, Tc and Tb are the optical transmittance of the WO3 films at a colored state and bleached state at the 700 nm wavelength, respectively. It is meant that the greater the ∆T, the better the optical transmittance modulation ability. As shown in Figure 6h, ∆T increased first from 200 °C to 300 °C, and subsequently decreased slightly at 350 °C. After ∆T achieved a maximum roughly 40% at 400 °C, it decreased again at 450 °C and 500 °C.
In the temperature stage of 200–300 °C, the precursor has not completely transformed. The quite thick film is attributed to a large quantity of amorphous carbon from the pyrolysis of glycerol. Besides, the amorphous carbon is the good binding receptor for Li+ [40,41], thereby there is a competitive relationship between amorphous carbon and WO3 in binding to Li+. As the annealing temperature increases, the thickness of the film decreases, suggesting that the amorphous carbon is gradually oxidized, and the content of amorphous carbon decreases. WO3 gradually plays a dominant role in the competition of binding to Li+ with the continuous formation of tungsten trioxide. As a consequence, the ∆T of the film gradually increases range from 200 °C to 300 °C.
When the annealing temperature rises above 350 °C, the composition of the film is basically WO3, and the effect of temperature on the mass of WO3 is negligible, according to the result of the TG curve in Figure 2. The ∆T of the film decreases slightly at 350 °C, which is attributed to the following possible reason: In the FT-IR of Figure 3, when the annealing temperature increases from 300 °C to 350 °C, the W=O absorption band shifts to a higher wavenumber and becomes sharper, which indicates that the W=O bond length shortens, as well as the W=O bond vibrational steric resistance increases. In addition, the mass of WO3 is basically constant, while the thickness of film decreases. It demonstrates that the film structure becomes dense from loose. The steric hindrance of Li+ into and out the thin film increases, and the binding sites may decrease at the same time, which is not conducive to electrochromism [42,43,44]. Therefore, there is a slight decrease in the ∆T at 350 °C.
The ∆T of the film at 400 °C is the best for the possible reasons as follows: Firstly, the crystalline WO3 film possesses a higher carrier mobility [37,45], WO3 is an n-type semiconductor [2] and electrons are the majority carrier, which is beneficial to electron injection in the electrochromic double injection of ions and electrons model [28,46]. Secondly, the crystallization degree of the film is not very high at 400 °C, and there are a lot of grain boundaries within the film in a mixed crystalline phase structure. Besides, different crystalline phases would produce a lot of crystallographic defects owing to the lattice constant mismatch. These grain boundaries and defects are essentially W–O-dangling bond, which are good ion binding sites, contributing to electrochromism. Hence, the ∆T of the film is the best at 400 °C.
However, with the further increase in annealing temperature, the crystal phase of the film is mainly monoclinic, and the diffraction peaks become sharper in Figure 5, which indicates that the crystallization degree of the film increases, suggesting that the grain boundaries in the film decrease and Li+ binding sites decrease. Moreover, the densification of the film is not conducive to the injection and extraction of Lithium ions [44,47]. In consequence, the ∆T of thin film decreases gradually in the temperature stage of 400–500 °C.
The optical properties of the WO3 films annealed at different temperatures are characterized in Figure 7. The optical band gap of these films can be calculated from the following formula [48,49]:
αhν = A(hν − Eg)n
In this formula, A is a content; α, the absorption coefficient, can be computed from the transmittance; the Planck constant (h) is 6.626 × 10−34 J s; ν, the photon frequency, can be converted from the wavelength; n is 2, because WO3 is an indirect band gap semiconductor; Eg, the optical band gap, is the value of the fitting line horizontal intercept of the curve of (αhν)1/2 versus the photon energy hν.
As shown in Figure 7b, the optical band gap (Eg) of the WO3 films are observed at the 3.48 eV, 3.45 eV, 3.47 eV and 3.37 eV ranges from 350 °C to 500 °C, respectively. The Eg of the WO3 films prepared in this work decreased first and then increased, and afterward decreased again with the increase in annealing temperature. The average bandgap of the WO3 films with a mixed crystalline structure, obtaining a minimum, is 3.37 eV at 500 °C [2].
Figure 8a,b illustrate the change of transmittance at 680 nm wavelength of the WO3 films prepared using the sample solution with 25% volume fraction glycerol and the change of transmittance at 680 nm wavelength under ±3.0 V voltages, respectively. Additionally, for sufficiently evaluating the electrochromic performance, coloration efficiency (CE) as an important parameter is defined by the following formula [50,51]:
CE = ΔOD/ΔQ = log[Tb/Tc]/(Q/A)
Q = ∫ I dt
In the formula, ΔOD is the optical density of the change between two optical states at 680 nm wavelength; Tb and Tc were defined above; the injecting and extracting charge density (Q) were calculated by integrating the current of a cycle of the electrochromic test; A is the electrochromic total area. The coloration efficiency (CE) value of sample was calculated to be 46.3 cm2·C−1 for WO3 thin films annealed at 400 °C in this work, as shown in Figure 8b. In general the CE value of sol-gel-prepared films ranges from 25 cm2·C−1 to 75 cm2·C−1, which shows that the CE value of sol-gel-free WO3 films as reliable as normal sol-gel WO3 films [37,52]. Further studies will be done about the electrical resistance and the electrochromic reliability.
It is worth comparing the performance in this work with other reported studies by other synthesis methods. The comparison of coloration efficiency and optical band gap between this work and other reported works would be demonstrated in Table 1. It is indicated that this work, using the sol-gel-free method, maintains a proper balance between optical band gap and coloration efficiency better than other works by synthesis methods in reference.

4. Conclusions

The WO3 thin films were successfully prepared on ITO glass substrate by spin coating technique using the glycerol-modified ammonium tungstate precursor solution. For better surface wetting, the sol-gel free ammonium tungstate solution with the 25% volume fraction of glycerol was selected to promote the growth of WO3 thin films. It is concluded that the ammonium tungstate transformed to WO3 range from 220 °C to 300 °C, and the crystalline structure of the WO3 films was observed when films were annealed above 300 °C.
Additionally, as the annealing temperature increases, the component content of WO3 within the film increased. The WO3 films prepared in this work were smoother and more homogeneous than the sol-gel-prepared films. The optical band gap of the WO3 films was variational from 3.48 eV to 3.37 eV with the increase in the annealing temperature above 350 °C. Furthermore, the coloration efficiency of the WO3 films attained 46.3 cm2·C−1.

Author Contributions

Conceptualization, J.L. and H.N.; methodology, R.Y. and D.G.; validation, M.S., X.F. and J.C.; resources, J.P. and R.Y.; data curation, G.Z., T.Q. and K.G.; writing—Original draft preparation, J.L. and G.Z.; writing—Review and editing, J.P. and H.N.; All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by Key-Area Research and Development Program of Guangdong Province (No.2019B010934001), National Natural Science Foundation of China (Grant No.51771074, 61804029 and 61574061), the Major Integrated Projects of National Natural Science Foundation of China (Grant No.U1601651), the Basic and Applied Basic Research Major Program of Guangdong Province (No.2019B030302007), the Guangdong Natural Science Foundation (No.2018A030310353), Science and Technology Project of Guangzhou (No.201904010344), the Fundamental Research Funds for the Central Universities (No.2019MS012), the Open Project of Guangdong Province Key Lab of Display Material and Technology (No.2017B030314031), 2019 Guangdong University Student Science and Technology Innovation Special Fund ("Climbing Plan" Special Fund) (No.pdjh2019a0028 and pdjh2019b0041), National College Students’ Innovation and Entrepreneurship Training Program (No.201910561005 and 201910561007), South China University of Technology 100 Step Ladder Climbing Plan Research Project (No.j2tw201902475, j2tw201902203 and j2tw202004095).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Thongpan, W.; Louloudakis, D.; Pooseekheaw, P.; Kumpika, T.; Kantarak, E.; Panthawan, A.; Tuantranont, A.; Thongsuwan, W.; Singjai, P. Electrochromic properties of tungsten oxide films prepared by sparking method using external electric field. Thin Solid Films 2019, 682, 135–141. [Google Scholar] [CrossRef]
  2. Mukherjee, R.; Sahay, P.P. Effect of precursors on the microstructural, optical, electrical and electrochromic properties of WO3 nanocrystalline thin films. J. Mater. Sci. Mater. Electron. 2015, 26, 6293–6305. [Google Scholar] [CrossRef]
  3. Mardare, C.C.; Hassel, A.W. Review on the versatility of tungsten oxide coatings. Phys. Status Solidi A 2019, 216, 1900047. [Google Scholar] [CrossRef] [Green Version]
  4. Bourdin, M.; Gaudon, M.; Weill, F.; Duttine, M.; Gayot, M.; Messaddeq, Y.; Cardinal, T. Nanoparticles (NPs) of WO3-x compounds by polyol route with enhanced photochromic properties. Nanomater.-Basel 2019, 9, 1555. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  5. Yu, H.; Guo, J.; Wang, C.; Zhang, J.; Liu, J.; Dong, G.; Zhong, X.; Diao, X. Essential role of oxygen vacancy in electrochromic performance and stability for WO3-y films induced by atmosphere annealing. Electrochim. Acta 2020, 332, 135504. [Google Scholar] [CrossRef]
  6. Pan, J.; Wang, Y.; Zheng, R.; Wang, M.; Wan, Z.; Jia, C.; Weng, X.; Xie, J.; Deng, L. Directly grown high-performance WO3 films by a novel one-step hydrothermal method with significantly improved stability for electrochromic applications. J. Mater. Chem. A 2019, 7, 13956–13967. [Google Scholar] [CrossRef]
  7. Wang, B.; Man, W.; Yu, H.; Li, Y.; Zheng, F. Fabrication of Mo-Doped WO₃ Nanorod Arrays on FTO Substrate with Enhanced Electrochromic Properties. Materials (Basel, Switzerland) 2018, 11, 1627. [Google Scholar] [CrossRef] [Green Version]
  8. Liang, Y.; Chang, C. Preparation of Orthorhombic WO3 Thin Films and Their Crystal Quality-Dependent Dye Photodegradation Ability. Coatings 2019, 9, 90. [Google Scholar] [CrossRef] [Green Version]
  9. Zheng, J.Y.; Haider, Z.; Van, T.K.; Pawar, A.U.; Kang, M.J.; Kim, C.W.; Kang, Y.S. Tuning of the crystal engineering and photoelectrochemical properties of crystalline tungsten oxide for optoelectronic device applications. CrystEngComm 2015, 17, 6070–6093. [Google Scholar] [CrossRef]
  10. Zhang, G.; Lu, K.; Zhang, X.; Yuan, W.; Shi, M.; Ning, H.; Tao, R.; Liu, X.; Yao, R.; Peng, J. Effects of annealing temperature on optical band gap of sol-gel tungsten trioxide films. Micromach.-Basel 2018, 9, 377. [Google Scholar] [CrossRef] [Green Version]
  11. Rozman, M.; Žener, B.; Matoh, L.; Godec, R.F.; Mourtzikou, A.; Stathatos, E.; Bren, U.; Lukšič, M. Flexible electrochromic tape using steel foil with WO3 thin film. Electrochim. Acta 2020, 330, 135329. [Google Scholar] [CrossRef]
  12. Yuan, J.; Wang, B.; Wang, H.; Chai, Y.; Jin, Y.; Qi, H.; Shao, J. Electrochromic behavior of WO3 thin films prepared by GLAD. Appl. Surf. Sci. 2018, 447, 471–478. [Google Scholar] [CrossRef]
  13. Wang, J.C.; Shi, W.; Sun, X.Q.; Wu, F.Y.; Li, Y.; Hou, Y. Enhanced Photo-Assisted Acetone Gas Sensor and Efficient Photocatalytic Degradation Using Fe-Doped Hexagonal and Monoclinic WO3 Phase-Junction. Nanomater.-Basel 2020, 10, 398. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  14. Liang, Y.; Chang, C. Improvement of Ethanol Gas-Sensing Responses of ZnO-WO3 Composite Nanorods through Annealing Induced Local Phase Transformation. Nanomater.-Basel 2019, 9, 669. [Google Scholar] [CrossRef] [Green Version]
  15. Leidinger, M.; Huotari, J.; Sauerwald, T.; Lappalainen, J.; Schütze, A. Selective detection of naphthalene with nanostructured WO3 gas sensors prepared by pulsed laser deposition. J. Sens. Sens. Syst. 2016, 5, 147–156. [Google Scholar] [CrossRef] [Green Version]
  16. Zhou, Q.; Chen, Y.; Li, X.; Qi, T.; Peng, Z.; Liu, G. Preparation and electrochromism of pyrochlore-type tungsten oxide film. Rare Metals 2018, 37, 604–612. [Google Scholar] [CrossRef]
  17. Kumar, A.; Singh, P.; Kulkarni, N.; Kaur, D. Structural and optical studies of nanocrystalline V2O5 thin films. Thin Solid Films 2008, 516, 912–918. [Google Scholar] [CrossRef]
  18. Kim, H.; Lee, H.; Maeng, W.J. Applications of atomic layer deposition to nanofabrication and emerging nanodevices. Thin Solid Films 2009, 517, 2563–2580. [Google Scholar] [CrossRef]
  19. De Andrade, J.R.; Cesarino, I.; Zhang, R.; Kanicki, J.; Pawlicka, A. Properties of electrodeposited WO3 thin films. Mol. Cryst. Liq. Cryst. 2014, 604, 71–83. [Google Scholar] [CrossRef]
  20. Pal, S.; Jacob, C. The influence of substrate temperature variation on tungsten oxide thin film growth in an HFCVD system. Appl. Surf. Sci. 2007, 253, 3317–3325. [Google Scholar] [CrossRef]
  21. Blackman, C.S.; Parkin, I.P. Atmospheric pressure chemical vapor deposition of crystalline monoclinic WO3 and WO3-x thin films from reaction of WCl6 with O-containing solvents and their photochromic and electrochromic properties. Chem. Mater. 2005, 17, 1583–1590. [Google Scholar] [CrossRef]
  22. Kangkun, N.; Kiama, N.; Saito, N.; Ponchio, C. Optical properties and photoelectrocatalytic activities improvement of WO3 thin film fabricated by fixed-potential deposition method. Optik 2019, 198, 163235. [Google Scholar] [CrossRef]
  23. Zhang, G.; Zhang, X.; Ning, H.; Chen, H.; Wu, Q.; Jiang, M.; Li, C.; Guo, D.; Wang, Y.; Yao, R.; et al. Tungsten doped stannic oxide transparent conductive thin film using preoxotungstic acid dopant. Superlattices Microstruct 2019, 130, 277–284. [Google Scholar] [CrossRef]
  24. Fardindoost, S.; Iraji Zad, A.; Rahimi, F.; Ghasempour, R. Pd doped WO3 films prepared by sol-gel process for hydrogen sensing. Int. J. Hydrog. Energy 2010, 35, 854–860. [Google Scholar] [CrossRef]
  25. Avellaneda, C.O.; Bueno, P.R.; Faria, R.C.; Bulhões, L.O.S. Electrochromic properties of lithium doped WO3 films prepared by the sol-gel process. Electrochim. Acta 2001, 46, 1977–1981. [Google Scholar] [CrossRef]
  26. Danks, A.E.; Hall, S.R.; Schnepp, Z. The evolution of ’sol-gel’ chemistry as a technique for materials synthesis. Mater. Horiz. 2016, 3, 91–112. [Google Scholar] [CrossRef] [Green Version]
  27. Xie, Z.; Liu, Q.; Zhang, Q.; Lu, B.; Zhai, J.; Diao, X. Fast-switching quasi-solid state electrochromic full device based on mesoporous WO3 and NiO thin films. Sol. Energy Mater. Sol. Cells 2019, 200, 110017. [Google Scholar] [CrossRef]
  28. Wen-Cheun Au, B.; Chan, K.; Knipp, D. Effect of film thickness on electrochromic performance of sol-gel deposited tungsten oxide (WO3). Opt Mater. 2019, 94, 387–392. [Google Scholar] [CrossRef]
  29. Sonavane, A.C.; Inamdar, A.I.; Shinde, P.S.; Deshmukh, H.P.; Patil, R.S.; Patil, P.S. Efficient electrochromic nickel oxide thin films by electrodeposition. J. Alloys Compd. 2010, 489, 667–673. [Google Scholar] [CrossRef]
  30. Jin, L.H.; Bai, Y.; Li, C.S.; Wang, Y.; Feng, J.Q.; Lei, L.; Zhao, G.Y.; Zhang, P.X. Growth of tungsten oxide nanostructures by chemical solution deposition. Appl. Surf. Sci. 2018, 440, 725–729. [Google Scholar] [CrossRef]
  31. Zhao, B.; Zhang, X.; Dong, G.; Wang, H.; Yan, H. Efficient electrochromic device based on sol-gel prepared WO3 films. Ionics 2015, 21, 2879–2887. [Google Scholar] [CrossRef]
  32. Vidmar, T.; Topič, M.; Dzik, P.; Opara Krašovec, U. Inkjet printing of sol-gel derived tungsten oxide inks. Sol. Energy Mater. Sol. Cells 2014, 125, 87–95. [Google Scholar] [CrossRef]
  33. García-García, F.J.; Mosa, J.; González-Elipe, A.R.; Aparicio, M. Sodium ion storage performance of magnetron sputtered WO3 thin films. Electrochim. Acta 2019, 321, 134669. [Google Scholar] [CrossRef]
  34. Leitzke, D.W.; Cholant, C.M.; Landarin, D.M.; Lucio, C.S.; Krüger, L.U.; Gündel, A.; Flores, W.H.; Rodrigues, M.P.; Balboni, R.D.C.; Pawlicka, A.; et al. Electrochemical properties of WO3 sol-gel thin films on indium tin oxide/poly(ethylene terephthalate) substrate. Thin Solid Films 2019, 683, 8–15. [Google Scholar] [CrossRef]
  35. Djaoued, Y.; Ashrit, P.V.; Badilescu, S.; Bruning, R. Synthesis and characterization of macroporous tungsten oxide films for electrochromic application. J. Sol-Gel Sci. Technol. 2003, 28, 235–244. [Google Scholar] [CrossRef]
  36. Caruso, T.; Castriota, M.; Policicchio, A.; Fasanella, A.; De Santo, M.P.; Ciuchi, F.; Desiderio, G.; La Rosa, S.; Rudolf, P.; Agostino, R.G.; et al. Thermally induced evolution of sol-gel grown WO3 films on ITO/glass substrates. Appl. Surf. Sci. 2014, 297, 195–204. [Google Scholar] [CrossRef]
  37. Ge, C.; Wang, M.; Hussain, S.; Xu, Z.; Liu, G.; Qiao, G. Electron transport and electrochromic properties of sol-gel WO3 thin films: Effect of crystallinity. Thin Solid Films 2018, 653, 119–125. [Google Scholar] [CrossRef]
  38. Mukherjee, R.; Sahay, P.P. Structural, morphological, optical and electrical properties of spray-deposited Sb-doped WO3 nanocrystalline thin films prepared using ammonium tungstate precursor. J. Mater. Sci. Mater. Electron. 2015, 26, 2697–2708. [Google Scholar] [CrossRef]
  39. Yang, H.; Yu, J.; Jeong, R.H.; Boo, J. Enhanced electrochromic properties of nanorod based WO3 thin films with inverse opal structure. Thin Solid Films 2018, 660, 596–600. [Google Scholar] [CrossRef]
  40. Xia, T.; Zhang, W.; Wang, Z.; Zhang, Y.; Song, X.; Murowchick, J.; Battaglia, V.; Liu, G.; Chen, X. Amorphous carbon-coated TiO2 nanocrystals for improved lithium-ion battery and photocatalytic performance. Nano Energy 2014, 6, 109–118. [Google Scholar] [CrossRef] [Green Version]
  41. Wang, Z.; Tian, W.; Liu, X.; Yang, R.; Li, X. Synthesis and electrochemical performances of amorphous carbon-coated Sn-Sb particles as anode material for lithium-ion batteries. J. Solid State Chem. 2007, 180, 3360–3365. [Google Scholar] [CrossRef]
  42. Madhavi, V.; Kondaiah, P.; Hussain, O.M.; Uthanna, S. Structural, optical and electrochromic properties of RF magnetron sputtered WO3 thin films. Phys. B: Condens. Matter 2014, 454, 141–147. [Google Scholar] [CrossRef]
  43. Kim, H.; Choi, D.; Kim, K.; Chu, W.; Chun, D.; Lee, C.S. Effect of particle size and amorphous phase on the electrochromic properties of kinetically deposited WO3 films. Sol. Energy Mater. Sol. Cells 2018, 177, 44–50. [Google Scholar] [CrossRef]
  44. Koo, B.; Ahn, H. Fast-switching electrochromic properties of mesoporous WO3 films with oxygen vacancy defects. Nanoscale 2017, 9, 17788–17793. [Google Scholar] [CrossRef]
  45. Darmawi, S.; Burkhardt, S.; Leichtweiss, T.; Weber, D.A.; Wenzel, S.; Janek, J.; Elm, M.T.; Klar, P.J. Correlation of electrochromic properties and oxidation states in nanocrystalline tungsten trioxide. Phys. Chem. Chem. Phys. 2015, 17, 15903–15911. [Google Scholar] [CrossRef] [Green Version]
  46. Kharade, R.R.; Mane, S.R.; Mane, R.M.; Patil, P.S.; Bhosale, P.N. Synthesis and characterization of chemically grown electrochromic tungsten oxide. J. Sol-Gel Sci. Technol. 2010, 56, 177–183. [Google Scholar] [CrossRef]
  47. Muthu Karuppasamy, K.; Subrahmanyam, A. The electrochromic and photocatalytic properties of electron beam evaporated vanadium-doped tungsten oxide thin films. Sol. Energy Mater. Sol. Cells 2008, 92, 1322–1326. [Google Scholar] [CrossRef]
  48. Hoseinzadeh, S.; Ghasemiasl, R.; Bahari, A.; Ramezani, A.H. Effect of post-annealing on the electrochromic properties of layer-by-layer arrangement FTO-WO3-Ag-WO3-Ag. J. Electron. Mater. 2018, 47, 3552–3559. [Google Scholar] [CrossRef]
  49. Najafi-Ashtiani, H.; Bahari, A. Optical, structural and electrochromic behavior studies on nanocomposite thin film of aniline, o-toluidine and WO3. Opt. Mater. 2016, 58, 210–218. [Google Scholar] [CrossRef]
  50. Najafi-Ashtiani, H.; Bahari, A.; Gholipour, S. Investigation of coloration efficiency for tungsten oxide-silver nanocomposite thin films with different surface morphologies. J. Mater. Sci. Mater. Electron. 2018, 29, 5820–5829. [Google Scholar] [CrossRef]
  51. Hoseinzadeh, S.; Ghasemiasl, R.; Bahari, A.; Ramezani, A.H. The injection of Ag nanoparticles on surface of WO3 thin film: Enhanced electrochromic coloration efficiency and switching response. J. Mater. Sci. Mater. Electron. 2017, 28, 14855–14863. [Google Scholar] [CrossRef]
  52. Zhi, M.; Huang, W.; Shi, Q.; Wang, M.; Wang, Q. Sol-gel fabrication of WO3/RGO nanocomposite film with enhanced electrochromic performance. RSC Adv. 2016, 6, 67488–67494. [Google Scholar] [CrossRef]
Micromachines 11 00311 g001 550
Figure 1. The surface tension and the contact angle and the dynamic viscosity of the all sample precursor solutions. (a) The surface tension and the contact angle. (b) The dynamic viscosity.
Figure 1. The surface tension and the contact angle and the dynamic viscosity of the all sample precursor solutions. (a) The surface tension and the contact angle. (b) The dynamic viscosity.
Micromachines 11 00311 g001
Micromachines 11 00311 g002 550
Figure 2. (a) The thermal gravimetric and differential scanning calorimetry (TG-DSC) curves of the sample solution with 25% volume fraction glycerol. The endothermic process and exothermic process are appointed as “endo” and “exo”, respectively. (b) The thickness of the WO3 films annealed at different temperatures.
Figure 2. (a) The thermal gravimetric and differential scanning calorimetry (TG-DSC) curves of the sample solution with 25% volume fraction glycerol. The endothermic process and exothermic process are appointed as “endo” and “exo”, respectively. (b) The thickness of the WO3 films annealed at different temperatures.
Micromachines 11 00311 g002
Micromachines 11 00311 g003 550
Figure 3. Fourier transform infrared (FT-IR) spectra of WO3 films prepared using the sample solution with 25% volume fraction glycerol.
Figure 3. Fourier transform infrared (FT-IR) spectra of WO3 films prepared using the sample solution with 25% volume fraction glycerol.
Micromachines 11 00311 g003
Micromachines 11 00311 g004 550
Figure 4. The atomic force microscope (AFM) 2D and 3D images of the WO3 thin films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures: (a,b) 200 °C, (c,d) 350 °C, (e,f) 500 °C, respectively. (g) The surface roughness and the surface grain size of these films.
Figure 4. The atomic force microscope (AFM) 2D and 3D images of the WO3 thin films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures: (a,b) 200 °C, (c,d) 350 °C, (e,f) 500 °C, respectively. (g) The surface roughness and the surface grain size of these films.
Micromachines 11 00311 g004
Micromachines 11 00311 g005 550
Figure 5. The X-ray Diffraction (XRD) patterns of the WO3 films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures: 200 °C, 300 °C, 400 °C and 500 °C, respectively.
Figure 5. The X-ray Diffraction (XRD) patterns of the WO3 films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures: 200 °C, 300 °C, 400 °C and 500 °C, respectively.
Micromachines 11 00311 g005
Micromachines 11 00311 g006 550
Figure 6. The optical transmittance spectra of the WO3 films annealed at different temperatures at the initial state, colored state and bleached state: (a) 200 °C, (b) 250 °C, (c) 300 °C, (d) 350 °C, (e) 400 °C, (f) 450 °C, (g) 500 °C, respectively. (h) The optical transmittance modulation ability (ΔT at 700 nm wavelength) with ±3.0 V voltages.
Figure 6. The optical transmittance spectra of the WO3 films annealed at different temperatures at the initial state, colored state and bleached state: (a) 200 °C, (b) 250 °C, (c) 300 °C, (d) 350 °C, (e) 400 °C, (f) 450 °C, (g) 500 °C, respectively. (h) The optical transmittance modulation ability (ΔT at 700 nm wavelength) with ±3.0 V voltages.
Micromachines 11 00311 g006
Micromachines 11 00311 g007 550
Figure 7. (a) The transmittance of WO3 films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures. The transmittance of air is specified as 100%. (b) The curve of (αhν)1/2 versus hν for WO3 films.
Figure 7. (a) The transmittance of WO3 films prepared using the sample solution with 25% volume fraction glycerol annealed at different temperatures. The transmittance of air is specified as 100%. (b) The curve of (αhν)1/2 versus hν for WO3 films.
Micromachines 11 00311 g007
Micromachines 11 00311 g008 550
Figure 8. (a) Change curve of transmittance at 680 nm of WO3 films prepared using the sample solution with 25% volume fraction glycerol. (b) Variation of the optical density (OD) versus charge density for WO3 film. The applied voltage was range from −3.0 V to +3.0 V.
Figure 8. (a) Change curve of transmittance at 680 nm of WO3 films prepared using the sample solution with 25% volume fraction glycerol. (b) Variation of the optical density (OD) versus charge density for WO3 film. The applied voltage was range from −3.0 V to +3.0 V.
Micromachines 11 00311 g008
Table
Table 1. The comparison of optical band gap and coloration efficiency between this work and the reported works by synthesis methods.
Table 1. The comparison of optical band gap and coloration efficiency between this work and the reported works by synthesis methods.
Result fromSynthesis MethodCrystallinityOptical Band Gap(eV)Coloration Efficiency (cm2/C)
[5]DC magnetron sputteringAmorphous3.5140.5
[37]Sol-gelAmorphous3.3145.3
[37]Sol-gelCrystalline3.1027.4
[52]Sol-gelCrystalline3.0146.7
This workSol-gel freeCrystalline3.3746.3

Share and Cite

MDPI and ACS Style

Liu, J.; Zhang, G.; Guo, K.; Guo, D.; Shi, M.; Ning, H.; Qiu, T.; Chen, J.; Fu, X.; Yao, R.; et al. Effect of the Ammonium Tungsten Precursor Solution with the Modification of Glycerol on Wide Band Gap WO3 Thin Film and Its Electrochromic Properties. Micromachines 2020, 11, 311. https://doi.org/10.3390/mi11030311

AMA Style

Liu J, Zhang G, Guo K, Guo D, Shi M, Ning H, Qiu T, Chen J, Fu X, Yao R, et al. Effect of the Ammonium Tungsten Precursor Solution with the Modification of Glycerol on Wide Band Gap WO3 Thin Film and Its Electrochromic Properties. Micromachines. 2020; 11(3):311. https://doi.org/10.3390/mi11030311

Chicago/Turabian Style

Liu, Jinxiang, Guanguang Zhang, Kaiyue Guo, Dong Guo, Muyang Shi, Honglong Ning, Tian Qiu, Junlong Chen, Xiao Fu, Rihui Yao, and et al. 2020. "Effect of the Ammonium Tungsten Precursor Solution with the Modification of Glycerol on Wide Band Gap WO3 Thin Film and Its Electrochromic Properties" Micromachines 11, no. 3: 311. https://doi.org/10.3390/mi11030311

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.