Next Article in Journal
Inter- vs. Intra-Molecular Hydrogen Bond in Complexes of Nitrophthalic Acids with Pyridine
Next Article in Special Issue
Functional Surface Coatings on Orthodontic Appliances: Reviews of Friction Reduction, Antibacterial Properties, and Corrosion Resistance
Previous Article in Journal
Enzymes and Enzyme Inhibitors—Applications in Medicine and Diagnosis
Previous Article in Special Issue
An Experimental Anodized and Low-Pressure Oxygen Plasma-Treated Titanium Dental Implant Surface—Preliminary Report
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 24
Issue 6
10.3390/ijms24065244
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Extensive Investigation on the Effect of Niobium Insertion on the Physical and Biological Properties of 45S5 Bioactive Glass for Dental Implant

by
Imen Hammami
1,
Sílvia Rodrigues Gavinho
1,
Ana Sofia Pádua
2,
Maria do Carmo Lança
3,
João Paulo Borges
3,
Jorge Carvalho Silva
2,
Isabel Sá-Nogueira
4,5,
Suresh Kumar Jakka
1,* and
Manuel Pedro Fernandes Graça
1,*
1
I3N and Physics Department, University of Aveiro, 3810-193 Aveiro, Portugal
2
Physics Department and CENIMAT-I3N, NOVA School of Science and Technology, 2829-516 Caparica, Portugal
3
Materials Science Department and CENIMAT-I3N, NOVA School of Science and Technology, 2829-516 Caparica, Portugal
4
UCIBIO, Applied Molecular Biosciences Unit, Department of Life Sciences, NOVA School of Science and Technology, NOVA University Lisbon, 2819-516 Caparica, Portugal
5
Associate Laboratory i4HB—Institute for Health and Bioeconomy, NOVA School of Science and Technology, NOVA University Lisbon, 2819-516 Caparica, Portugal
*
Authors to whom correspondence should be addressed.
Int. J. Mol. Sci. 2023, 24(6), 5244; https://doi.org/10.3390/ijms24065244
Submission received: 31 December 2022 / Revised: 1 March 2023 / Accepted: 8 March 2023 / Published: 9 March 2023
(This article belongs to the Special Issue Recent Process Design and Development Strategies for Dental Materials)
Browse Figures
Review Reports Versions Notes

Abstract

:
Dental implants have emerged as one of the most consistent and predictable treatments in the oral surgery field. However, the placement of the implant is sometimes associated with bacterial infection leading to its loss. In this work, we intend to solve this problem through the development of a biomaterial for implant coatings based on 45S5 Bioglass® modified with different amounts of niobium pentoxide (Nb2O5). The structural feature of the glasses, assessed by XRD and FTIR, did not change in spite of Nb2O5 incorporation. The Raman spectra reveal the Nb2O5 incorporation related to the appearance of NbO4 and NbO6 structural units. Since the electrical characteristics of these biomaterials influence their osseointegration ability, AC and DC electrical conductivity were studied by impedance spectroscopy, in the frequency range of 102–106 Hz and temperature range of 200–400 K. The cytotoxicity of glasses was evaluated using the osteosarcoma Saos-2 cells line. The in vitro bioactivity studies and the antibacterial tests against Gram-positive and Gram-negative bacteria revealed that the samples loaded with 2 mol% Nb2O5 had the highest bioactivity and greatest antibacterial effect. Overall, the results showed that the modified 45S5 bioactive glasses can be used as an antibacterial coating material for implants, with high bioactivity, being also non-cytotoxic to mammalian cells.

1. Introduction

The loss of one or more teeth has become a common problem resulting from trauma, bone or dental pathology, cancer, or simply ageing. According to statistics reported by the American Association of Oral and Maxillofacial Surgeons [1], 69% of adults aged between 35 and 44 have lost at least one permanent tooth due to an accident, gum disease, a failed root canal, or tooth decay. In addition, by the age of 74, approximately 26% of those persons have lost all their permanent teeth. Therefore, the demand for dental implants has increased rapidly. The statistics in 2010 revealed more than 300,000 dental implants placed per year [2]. The clinical success of dental implants is related to their ability to ensure rapid osteointegration and prevent the development of peri-implantitis [3]. These conditions are essential to ensure the long-term success of the implant. Peri-implantitis disease is an inflammatory condition that affects the tissues around dental implants. Just like a natural tooth, bacteria can grow at the implant neck and over time irritate gums, which remain in a chronic inflamed state and can lead to bone loss around the implant(s). Initially, the implant(s) remain clinically stable, without any sign of mobility being evidenced. In the absence of effective treatment, bone lysis continues, ultimately leading to implant loss. Therefore, peri-implantitis is considered a secondary implant failure.
To mitigate bacterial contamination, various measures have been used such as careful disinfection and rigorous aseptic surgical protocols [4]. Infection, which can also occur after surgery, is characterized by bacterial colonization and biofilm formation on implant surfaces. The biofilm is considered the primary etiologic reason for the inflammation of peri-implant tissues [5]. Peri-implantitis-associated biofilms are caused by a plethora of microbial species including anaerobes and facultative aerobes, and Staphylococcus aureus plays a predominant role in the development of this pathology [6]. To ensure the long-term success of the dental implant, the selection of the biomaterial to be used is a critical factor. Research on the development of new biomaterials or the manipulation of the structure and composition of existing biomaterials has been carried out to improve the properties of biomedical devices [7,8,9].
Typically, biomaterials for medical prostheses are made of metallic materials, mainly stainless steel and titanium alloys [10,11,12]. However, metal prostheses show dramatic failure due to their higher mechanical properties than those of bone tissue, resulting in necrosis and stress shielding of the tissue in contact. It is known that the long-term use of these materials can lead to an excessive release of metal ions which can promote local inflammation, pain, and even clinical failure [13,14,15]. Besides this issue, the formation of the biofilm problem can also lead to implant failure. Thus, an optimal implant should be able to prevent bacterial adhesion and enhance osteointegration [16,17]. To address these challenges, new progress in biomaterial science has led to the development of bioactive materials for implant coatings [4,18,19].
It has been reported that modifying the surface topography of an implant, by depositing a bioactive coating, improves the mechanical interlocking of the bone with the implant and increases the processes of proliferation and adhesion of osteoblasts [20,21,22]. Among the bioactive materials, silicate-based bioglasses containing calcium and phosphorus are mainly used in dental and orthopaedic surgery [23,24]. The first bioactive glasses were discovered in 1969 by L.L. Hench, called 45S5 Bioglass®, with the weight composition of 45% SiO2, 24.5% Na2O, 24.5% CaO, and 6% P2O5 [25]. This bioactive glass promotes the nucleation of calcium phosphate hydroxyapatite (HA) and carbonate (HAC) during ion exchanges that occur through contact/reaction with physiological fluids [26,27,28]. The formation of HAC on the surface of bioactive glasses promotes osteoinduction, osteoconduction, osseointegration, and angiogenesis [29,30,31]. A further benefit of using bioglass is the ability to alter its composition by incorporating extra ions that can improve its functionality without being toxic [32,33].
Several reports have shown that metallic ions (including magnesium, zinc, copper, silver, etc.) could be employed to generate antibacterial activity [34,35,36,37]. However, the information concerning their long-term effects on human health is limited. Loading these ions into bioactive systems is an effective strategy to control their release over a long period [38,39]. Moreover, bioactive materials can optimize the response of the biological system by interacting with the adjacent tissues, inducing reactions that promote their development and regeneration [40]. The presence of niobium (Nb) species in biomaterials has been reported to improve their bioactive and mechanical properties [41,42]. Some investigations reported that niobium ions promote the differentiation and mineralization of osteogenic cells [41,43]. The insertion of niobium in metallic alloys and ceramic matrices has shown superior corrosion resistance and low cytotoxicity [44,45]. Although niobium-containing bioactive glasses have recently attracted great interest, the effect of their incorporation on the physical and biological response of the 45S5 bioactive glasses is, according to our knowledge, very low.
For this purpose, 45S5 bioactive glasses containing Nb2O5 were prepared by a melt-quenching technique. X-ray diffraction, IR, and Raman spectroscopies were used to evaluate the influence of Nb2O5 on the structure of 45S5 Bioglass®. The electrical characteristics of the glasses were studied due to their potential to be electrically charged/polarized, therefore optimizing the osseointegration. Cytotoxicity tests using human osteosarcoma Saos-2 cells were used to assess the biocompatibility of the 45S5 bioactive glasses modified by the Nb insertion. The in vitro investigation of bioactivity was conducted by immersing samples (pellets made of powdered bioactive glass) in simulated body fluid (SBF), which is a solution with the same ionic strength and mineral content as the blood plasma. The changes in bioglasses, in terms of dissolution and precipitation of the protective layer containing calcium phosphates, were evaluated using scanning electron microscopy (SEM) with energy-dispersive X-ray analysis (EDX). The antibacterial activity of the bioglasses was evaluated from their ability to inhibit the growth of the S. aureus bacteria, which is commonly associated with implant infections, as well as other bacteria involved in the formation of the pathogenic biofilm.

2. Results

2.1. Structural Characterization

The XRD patterns, illustrated in Figure 1, consist of typical broad bands, without traces of crystalline phases, which confirm the amorphous character of the glasses. These results match well with the ones reported in the literature for 45S5 glasses [3,46]. The insertion of niobium, up to 8% mole of Nb2O5, did not promote the formation of any crystalline phase but enlarged the band at smaller angles. This phenomenon was already observed in phosphate glasses with niobium [47].
Figure 2 depicts the features revealed by the FTIR spectra of the glasses. The Si-O-Si stretching modes are ascribed to the bands detected at around 1010 cm−1 and 721 cm−1 [46,48,49,50,51,52,53,54]. The presence of the non-bridging oxygen ions is shown by the appearance of a band at 912 cm−1 that is attributed to the Si-ONBO stretching mode [46,51,53,54,55]. The presence of a shoulder at 596 cm−1 is attributed to the bending vibration of the P-O molecule [46,50,53,54,55,56]. The band that appeared at around 497 cm−1 is associated with the Si-O-Si bending mode [46,48,49,50,51,52,53,54].
Figure 3 shows the Raman spectra of the bioactive glasses prepared. For a more detailed analysis, the Raman spectra of BGNb1, BGNb2, BGNb4, and BGNb8 were deconvolved by a Gaussian fitting (Figure 4).
The whole range of Raman spectra can be separated into two regions: low wavenumber (500–900 cm−1) and high wavenumber (>900 cm−1). In the low-frequency region, a broad band at about 630 cm−1 is observed for BGNb0 which can be associated with the rocking motion of bridging oxygen in structural units that contain non-bridging oxygen ions (NBO) [57,58,59]. With the insertion of Nb2O5 in the glass network, it is noted that the band is shifted towards a higher frequency. By fitting and deconvoluting this peak (Figure 4), two bands can be differentiated, one located at 630–680 cm−1 and the other at 710–750 cm−1, and attributed to the vibrational mode of the Si-O-Si bond and the vibration of Nb-O, respectively, in NbO6 octahedra, with a low degree of distortion [60,61,62]. Moreover, an additional broad peak at 780–890 cm−1 is observed for the modified bioglass. The deconvoluted Raman spectra (Figure 4), show that this peak could be distinguished as three different bands located at 782–804 cm−1, 806–829 cm−1, and 857–886 cm−1, which are assigned to vibrations of NbO6 octahedrons with different degrees of distortion, to the vibration of NbO4 units, and to the symmetric stretching of Q0 units in the silicate network (SiO44−), respectively [63,64,65]. The vibrational bands of NbO6 units increased with increasing Nb2O5 concentration up to 2 mol%, whereas the NbO4 vibrational band decreased. A shoulder is observed for the BGNb0 sample at around 857 cm−1, corresponding to symmetric stretching of Q0 Si units [54,65]. At the high-frequency region, a vibration band can be observed at around 945 cm−1 and a shoulder at 1050 cm−1. From the result obtained by a deconvolution process (Figure 4), five vibrational modes located at 900–923 cm−1, 938–944 cm−1, 967–975 cm−1, 997–1023 cm−1, and 1051–1078 cm−1 can be distinguished, which correspond to symmetric stretching of Q1 Si, Q2 Si, Q0 P, and Q1 P units, and asymmetric stretching of bridging oxygen in all Q species, respectively [54,57,65].
The sum of the area of Raman vibration bands associated with non-bridging oxygen ions is plotted in Figure 5 as a function of Nb2O5 concentration. An increase in the number of NBOs for the bioglass with Nb2O5 content up to 2 mol% can be observed, indicating the existence of an optimal amount of Nb2O5 that can be added to the base bioglass.

2.2. Thermal Analysis

The differential thermal analysis (DTA) spectra of BGNb2 and BGNb8 are shown in Figure 6. The thermograms of both samples demonstrate the presence of a glass transition temperature, Tg, followed by an exothermic peak, Tc, ascribed to structural alteration associated with the formation of crystalline phases, and an endothermic peak, Tm, attributed to the melting point of bioglass. The Tg values were determined from the thermograms using the tangent method on the measured DTA curve, above and below the glass transition region. The value presented in Table 1 is the mean value of the abscissas of the tangents’ interceptions. The uncertainty in these measurements is 2%. In a prior study, a comparable thermal response was observed for the 45S5 bioglass [3]. The critical temperatures of the bioglasses modified by Nb2O5 are reported in Table 1.

2.3. Electrical Characterization

Figure 7 depicts the DC conductivity versus 1000/T on a logarithmic scale. It is visible that the conductivity rises with the increase in the temperature, which should be related to the increased mobility of the charge carriers. For temperatures above 300 K, approximately, this variation becomes linear, indicating that the Arrhenius formalism may be used to evaluate the activation energy associated with this thermally activated process. The calculated activation energy at the high-temperature region (inset in Figure 7) for all samples is registered in Table 2. The activation energy (Ea (DC)) decreases with the increase in Nb2O5 concentration, reaching a minimum value at the value of 2 mol%. After, a reversing trend is observed. This behavior is similar to the one observed for the NBO ions amount (Figure 5). On the contrary, an opposite trend was observed for the DC conductivity (σDC), which shows a maximum value for the sample with 2 mol% of Nb2O5.
The dielectric properties of the samples were analyzed using the modulus formalism, (M* = 1/ε*), to minimize the effect of electrode polarization and conductivity. Figure 8 shows the presence of one dielectric relaxation which is shifted to higher frequencies with increasing the temperature. It should be noted that other formalisms, such as permittivity or impedance, did not exhibit this dielectric relaxation behavior. Therefore, the observed relaxation behavior should be associated with an intrinsic characteristic related to dipole formation between the network modifier ions and the non-bridging oxygen ions.
The AC conductivity (Figure 9) showed the same feature, in resonance with DC conductivity, where the variation increases linearly in the high-temperature region. The results obtained for AC conductivity are registered in Table 2 and show an agreement with DC conductivity results. The bioglass with 2 mol% Nb2O5 content exhibits the highest AC conductivity. The activation energy value decreases with increasing frequency for all bioglass samples. This can be explained due to the increase in the applied frequency which enhances the electronic jumps between the localized states [66,67].

2.4. In Vitro Evaluation of the Biocompatibility

The human osteosarcoma Saos-2 cells were used to evaluate the cytotoxicity of the bioactive glasses prepared. Two sets of samples were tested, which we call the non-passivated and the passivated ones. The difference between the two sets is that the non-passivated is the filtered solution of the pristine bioglass powders that were in contact with the McCoy 5A medium for 24 h. The passivated solution was achieved by changing the medium after 24 h to a new medium, which was kept in contact with the powders for a new 24 h period. The filtered solution was then called the passivated sample. Figure 10 displays the results obtained for the passivated and non-passivated samples. All samples showed an improvement in cell viability when the concentration decreased from 100 mg/mL to 6.75 mg/ mL, as expected. Moreover, it can be seen that the passivated samples exhibit higher cell viability compared to the non-passivated samples. The passivated samples, which better simulate physiological conditions [68], revealed cell viability higher than 80%, except for the BGNb0 and BGNb1 samples that showed toxicity at the 100 mg/mL concentration and BGNb0 at 50 mg/mL, respectively.

2.5. Antibacterial Activity

Figure 11 depicts the antibacterial activity of the bioglasses modified by Nb2O5 insertion evaluated by the observed inhibition halo against the Gram-positive Staphylococcus aureus and Streptococcus mutans and the Gram-negative Escherichia coli bacteria. By the rise of the inhibition halo, we can conclude that the samples have antibacterial activity. An increase in the inhibition halo with increasing the content of Nb2O5 up to 2 mol% is noted. A decrease in the antibacterial effect was observed with increasing the Nb2O5 from 2 to 8 mol%.

2.6. In Vitro Degradation and Bioactivity Assay

The in vitro bioactivity, i.e., the ability to induce an apatite-like layer formation, of the bioglasses prepared, was investigated using an immersion test in simulated body fluid (SBF). Figure 12 shows the SEM micrographs and the EDS data of the surface of bioglass pellets after immersion in SBF.
The SEM micrographs confirmed the bioactivity of the glasses. The surface morphologies of pellets show the presence of spherical (cauliflower-like) particles characteristic of an apatitic layer formation. With the increase in the immersion time in SBF, this layer becomes thicker. It can be seen that for the samples with an immersion time of 28 days, the size of the particles decreases with increasing the percentage of niobium beyond 2 mol%, and in the case of the sample with the highest load percentage, BGNb8, only small amounts of apatite particles start to appear. The EDS graphs (Figure 12(d1–d5)) confirm the change in the amount of the chemical elements with the soaking time in SBF. The amount of Na and Si atoms tends to decrease with the immersion time, while the amount of P and Ca tends to increase.
The variation of Si and Na atomic percentage and the Ca/P ratio, determined using the data from EDS analysis on the surface of the bioglass samples before and after immersion in SBF solution, are illustrated in Figure 13. An abrupt drop in the atomic percentage of the elements is evident during the initial 2 days of immersion in all samples while no significant change is observed afterward. The samples with lower percentages of niobium, BGNb1, and BGNb2, show a faster decrease in Na and Si percentage in the first 2 d compared to the other glasses, and the value of the Ca/P ratio decreases reaching a value of 1.60–1.80, comparable to that of hydroxyapatite (Ca/P = 1.67) [69,70,71]. The decrease in the atomic percentage of Na and Si in the sample modified with 8 mol% of Nb2O5 is not significant, in contrast with the other samples, and the Ca/P ratio is considered high.
Figure 14 depicts the variation of pH of the bioactive glass samples after soaking in SBF for different periods, from 12 h up to 28 days. For all samples, the pH initially increases compared to the initial pH of the SBF solution, 7.4, and then, after 2 days of sample immersion, it starts to decrease.

3. Discussion

The results obtained by XRD and FTIR do not reciprocate any type of modification in the structure of the glass matrix with the insertion of Nb2O5. However, Raman spectra clearly showed the appearance of NbO4 and NbO6 structural groups, located at 800–810 cm−1 and 827–862 cm−1, for the glasses modified with Nb2O5 (Figure 3 and Figure 4). As the concentration of Nb2O5 is raised up to 2 mol%, the quantity of NbO6 units, related to niobium ions acting as modifiers in the glass matrix, increases progressively. Exceeding the 2 mol% of Nb2O5, there is a fractional conversion of NbO6 units into NbO4 units, which contributes to the formation of the glass network. Similar behavior was already found in other glasses containing niobium [72,73,74]. The presence of NbO6 units is predicted to act as a network modifier through the depolymerization of Si-O-Si bonds. These octahedrons can form a chain structure with different degrees of distortion by sharing their vertices with at least two silicon octahedrons. With the increasing NbO6 concentration, a higher concentration of NBO is expected [59,72]. The BGNb2 sample exhibits a high concentration of NbO6 structural groups (Figure 4), and thus a high concentration of NBO as justified in Figure 5.
The presence of NbO6 and NbO4 plays a critical role in the thermal response of the bioglass. From Figure 7 and Table 1, it can be observed that the Tg increases with the insertion of a high concentration of niobium, which indicates that an increase in network connectivity occurs due to the presence of a high concentration of NbO4, the network former, leading to a decrease in the amount of NBO ions. For the BGNb2 sample, a slight decrease in the characteristic temperatures is observed compared to the bioglass base, which is attributed to the increase in the amount of NBO ions and the weakness in the glass network, facilitating the ion mobility. Similar behaviors were reported in the literature for niobium glass systems [75,76].
The existence of NBO ions could affect the electrical properties of the prepared glasses. It is known that in the bioactive glass system, the conductivity is mainly related to the energy transported by Na+ and Ca+ ions moving through the glass network [3,77]. For the glasses modified with Nb2O5, the presence of NbO6 units leads to the degradation of the bioglass network by the formation of more NBO ions. Such structural alterations may have a significant impact on Na+ and Ca+ mobility. The mobility of such network modifier ions increases with the rise in NBO ions. One can notice in Table 2 that the sample with 2 mol% content of Nb2O5 exhibits the highest DC conductivity and therefore the lowest activation energy since the decrease in activation energy suggests an increase in the charge carrier’s mobility. The same happens to the AC conductivity, the increase in the conductivity with samples loaded with Nb2O5 up to 2 mol% should be essentially related to the increase in Na+ ions’ mobility.
From the biomedical applications point of view, it is critical to evaluate the cytotoxicity of the bioactive glasses given their intended use as implant coating materials. The evaluation of the bioactive glasses’ cytotoxicity against the human osteosarcoma Saos-2 cells, represented in Figure 10, shows low cell viability at high extract concentration, especially in the case of the samples with no or low content of Nb2O5. It was found that increasing the content of Nb2O5 inserted into the bioactive glass network can increase the biocompatibility of materials, which is consistent with the results of previous studies [75,78,79]. The non-passivated samples show lower cell viability compared to the passivated samples, which could be explained by the high rate of ion-exchange reactions that take place during the first 24 h of material–cell culture medium interactions leading to an increase in local pH [52]. Based on the results of passivated samples, which better mimic physiological circumstances, all modified bioactive glasses by niobium insertion can be used in a biomedical application where the extracellular fluid is exposed to bioactive glasses in circumstances corresponding to the 100 mg/mL extract production. The exceptions are the glasses with Nb2O5 content lower than 2 mol%, which show cell viability less than 80% at that concentration.
An important factor in reducing the risk of implant infection is preventing bacterial colonization. The 45S5 glass particles promote a considerable antibacterial effect against certain oral bacteria mainly due to the change in pH and the osmotic pressure effect [80,81]. The increase in pH to a more alkaline range creates an unfriendly environment for bacteria, resulting in morphological alterations. Additionally, variations in ion concentration in the bacterial environment result in a reduction in pressure across the bacterial cell membrane, which causes bacteria to shrink and therefore damages the cell membrane [81,82]. The antibacterial test results obtained using the agar diffusion method demonstrate the antibacterial properties against Gram-positive and Gram-negative bacteria (Figure 11). The inhibition halo tends to increase with increasing the Nb2O5 concentration up to 2mol%, which can be due to the high ionic strength of Nb5+ ions preventing bacteria from growing by creating a hyperosmotic environment [72,74]. Additionally, the presence of a disintegrated glass network due to the high concentration of NbO6 units in those glasses offers a suitable environment for the leaching of alkali metals ions, Na+, and Ca2+, which could lead to an increase in pH and thus promote the death of bacteria. Beyond 2 mol% of Nb2O5 insertion, the antibacterial activity of the samples decreased, which could be related to the conversion of certain NbO6 structural units into NbO4 units, as proved by the Raman analysis.
To assess the in vitro bioactivity of the synthesized bioactive glasses in a biological medium, the SBF immersion test was chosen. This method serves a better understanding of the physicochemical reactions taking place on bioglass in physiological fluids. When evaluating bioglass in vitro, it is critical to take into account changes in the surface chemistry, mainly the formation of an apatitic layer, since it has a significant impact on osteoblast cell adhesion and proliferation [83]. The formation of an apatitic layer is purely physicochemical and does not involve cells. This was observed in the SEM images of bioglasses after the immersion in SBF which is a cell-free solution (Figure 12). The apatite particles are formed on the surface of the bioglass, and with increasing immersing time the particles tend to aggregate, and a dense layer is formed. However, the size of the formed apatite seems to be smaller for the samples with the highest concentration of Nb2O5 (above 2 mol%) compared to the other samples. To better understand the effect of niobium on the formation of the hydroxyapatite (HA) layer on the bioglass surface, we refer to the mechanism proposed by L. Hench for the original Bioglass® which is adaptable to the majority of bioactive materials [25]. Similarly to the 45S5 bioactive glass, the SiO4 tetrahedron serves as the main structural unit of the bioactive glasses containing niobium, which may form bonds with other SiO4 tetrahedrons through Si-O-Si bonding, also known as bridging oxygen (BO) ions. Network modifiers alter the structure of the glass by converting BO into NBO, resulting in a drop in the glass network connectivity and thus a rise in the dissolution rate and consequently the release of ions. In fact, when the glass comes into contact with SBF, the alkali and alkaline earth ions (Na+ and Ca2+) present on the surface of the glass are exchanged with the H+ and H3O+ ions of the medium. This leads to an increase in the pH of the medium as the H+ ions are replaced by cations. The rise in pH values promotes the breaking, in the glass network, of the Si-O-Si bonds leading to a faster dissolution of the glass and the formation of silanol units (Si(OH)4). These silanol units then condense on the surface of the glass, forming a hydrated silica layer which promotes the nucleation of the carbonated hydroxyapatite. From the results obtained (Figure 13b), a faster drop can be seen in the atomic percentage of Na on the bioglass surface in the first days of SBF immersion. The presence of niobium acting as a network modifier, at high concentrations in the samples with a low percentage of Nb2O5 (≤2 mol%), creates a higher number of NBO ions and therefore promotes a faster release of the Na+ ions. For the samples with Nb2O5 > 2 mol%, the amount of NbO4 units increases, reducing the amount of NBO ions, and therefore the mobility or release of the network modifiers, namely the Na ions, becomes more difficult leading to a reduction in the glass dissolution rate. The same trend is observed for Si, which exhibits faster release from the bioglass with Nb2O5 concentration below 4 mol%, as indicated in Figure 13a by the faster decrease in the atomic percentage of this element. This proves the enhanced surface reactivity for the bioglasses with niobium load up to 2 mol%. The SEM micrographs in Figure 12 show that after 24 h of SBF immersion, the amount and the size of spheroidal apatite particles are more pronounced in the sample BGNb2, suggesting the existence of an optimal composition for the apatite formation. With longer soaking times in SBF, the concentration of the ions stabilizes and the Ca/P ratio decreases, reaching a value between 1.6 and 1.8 for the sample with niobium content up to 2 mol%, close to that of the HA of the human bones [69,70]. For the samples with higher niobium amount, the value of the Ca/P ratio is above 2, higher than the ideal value of 1.67. This higher value of Ca/P suggests that those samples are less bioactive [84,85], meaning that the apatite structure does not develop easily on the glass surface when exposed to SBF. After 28 days of soaking in SBF, the apatite particles grow and become denser, which indicates the formation of a dense layer of crystalline HA on the bioglass surface, while the growth was reduced for the samples with niobium content of 4 mol% and only the beginning of the formation of small apatite particles was observed for the sample with 8 mol% of niobium loads.
The variation in the pH is indicated in Figure 14. The increase in the pH in the first 48 h was due to the high release of the alkaline metal ions from the bioglass surface, and then it decreases due to the formation of silanol. The incorporation of 2 mol % of niobium into the bioglass resulted in a higher value of pH, which can be explained by the highest degradation rate of this sample and this is consistent with the condition of the creation of an HA-like layer on the surface of the bioactive glass with higher crystallinity [59,72].

4. Materials and Methods

4.1. Bioglass Preparation

A series of 45S5 bioactive glasses (45% SiO2, 24.5% Na2O, 24.5% CaO, and 6% P2O5 (wt%)) modified by the insertion of different amounts of Nb2O5, from 0 to 8 mol% (designed by BGNb0, BGNb1…BGNb8) was prepared using the melt-quenching technique. In brief, high-purity grade SiO2, P2O5, CaCO3, Na2CO3, and Nb2O5 (>99.99%) were mixed and ground in a planetary ball mill at 300 rpm for 1 h to homogenize, before undergoing calcination at 800 °C for 8 h. The powder was then placed in platinum crucibles and melted at 1300 °C for 1 h. The melt was quenched between the casting plates to obtain bulk glass samples.

4.2. Structural Characterization

Malvern Panalytical Aeris powder diffractometer (CuKα radiation, λ = 1.54056 Å) was used to collect the X-ray diffraction (XRD) patterns at room temperature. The acquisition was performed using a scan step of 0.02° in 1 s in a 2θ angle range of 10–70°.
The FTIR spectra were performed on FT Perkin-Elmer Spectrum BX Spectrometer in the ATR crystal (Golden Gate Diamond ATR Accessory), in the range of 400 and 1300 cm−1. The measurements were obtained from bioglass powder dispersed in KBr pellets. During acquisition, the room temperature and humidity were kept at approximately 23 °C and 35%, respectively.
Raman spectra were recorded at room temperature using a Horiba Jobin Yvon HR 800 spectrometer with an Ar+ laser (λ = 532 nm). Spectra were collected in a back-scattering geometry between 200 and 1500 cm−1 with a 50x lens focused on the sample.

4.3. Thermal Analysis

The thermal properties of the glasses were investigated using a simultaneous differential thermal analysis (DTA)/thermogravimetric (TG) measurement. A Hitachi STA 7300 system was employed, under Nitrogen N50 (99.999%) flowing at 200 mL/min and heating at 10 °C/min.

4.4. Electrical Characterization

Bulk glass samples were used for the electrical measurements. The samples were polished until parallel surfaces with a thickness of about 1 mm were obtained and then painted with silver conductive paste to form the electrodes. The direct current conductivity (σDC) of the samples was measured with a Keithley 617 electrometer, capable of measuring currents down to 10−14 A. This measurement was performed in a temperature range between 200 and 400 K where a voltage of 100 V was applied across the bulk glass. The AC electrical conductivity (σAC) and impedance measurements were also performed in the temperature range of 200 to 400 K, using a precision impedance meter, Agilent 4294, operating in a broad frequency window from 100 Hz to 1 MHz and in the Cp–Rp configuration. The temperature of the samples was regulated by an Oxford Research IT-C4 and monitored using a platinum sensor in both DC and AC measurements.
The complex electric permittivity ε* was calculated with the following equation [86,87]:
ε* = ε’ − j ε’’ = Cp (d/ε0 A) − j d (ω Rp ε0 A)
At the high-temperature range, the activation energy (Ea) of the DC and AC conductivities was determined by fitting the data to the Arrhenius model [88,89,90,91].
σ = σ0 exp(−EA/(kB T)),
where σ0 is a pre-exponential factor, EA is the activation energy, KB is the Boltzmann constant, and T the temperature.

4.5. In Vitro Evaluation of the Biocompatibility

In accordance with International Standard “ISO 10993-5 Biological evaluation of medical devices—Part 5: Tests for in vitro cytotoxicity” [92], the cytotoxicity of the bioglasses was assessed at various concentrations against the human osteosarcoma cell line (Saos-2 cells, ATCC® HTB-85™). Extracts were produced by placing the bioglass powder in contact with a culture medium, McCoy 5A medium (Merck KGaA, Darmstadt, Germany) at a concentration of 100 mg/mL. For non-passivated extract, the medium in contact with the powder was kept in an incubator for 24 h at 37 °C then filtered with a 0.22 µm millipore filter and stored at 37 °C. For the passivated extract, a new McCoy 5A medium was added to the same bioglass powder and then placed in the incubator for another 24 h at 37 °C. The 96-well plates were seeded with a Saos-2 cell line at a density of 30,000 cells/cm2 and placed in an incubator with 5% CO2 atmosphere for 24 h at 37 °C. After, the culture medium was removed and on the same plate, negative controls (C-) (viable cells), positive controls (C+) (in which the toxic compound dimethyl sulphoxide was added), non-passivated and passivated extracts with appropriate dilutions (50 mg/mL, 25 mg/mL, 12.5 mg/mL, and 6.75 mg/mL) were placed in an incubator for 48 h. The resazurin cell viability indicator was used to assess cell populations [93]. Using a Biotek ELX800 microplate reader, the optical absorbances of each well were measured at 570 and 600 nm. To confirm the assay’s reproducibility, two biological replicates, with six statistical replicates each, were carried out in this test for each sample.

4.6. Antibacterial Activity

The bacterial strains Escherichia coli K12 DSM498, Staphylococcus aureus COL MRSA (methicillin-resistant strain), and Streptococcus mutans DSM20523, were used as models to assess the antibacterial activity of the glasses, as previously described [46]. The method of agar diffusion assay plates, using the two-layer bioassay, was performed with TSB medium with the molten seeded overlay containing approximately 108 CFU/mL of the appropriate indicator bacteria. Bioglass pellets with a diameter of 6 mm were placed in the center of the plates, left for 4 h at room temperature, and then incubated for 24 h at 37 °C. In the case of S. mutans the plates were placed in a 5% CO2 incubator.
Images of the pellets were taken, and the diameter of the inhibition halo was measured with ImageJ software; each pellet was measured 30 times in several orientations [94]. The results of the eight independent assays for each bacterium were statistically analyzed with an unpaired t-test, comparing the bioactive glass base composition with each of the different samples using GraphPad Prism 8.0 software.

4.7. In Vitro Bioactivity Assay

The bioactivity evaluation of the bioglasses was conducted by immersing samples (pellets made of powdered bioglass) in simulated body fluid SBF, according to ISO 23317:2017 Standards. The samples were placed in different flasks, soaked in SBF, and remained inside an incubator at 37 °C with continuous oscillating support for 12, 24, 48, 96 h, 14, and 28 days. The SBF solutions were refreshed every 48 h to mimic the biological environment.
To calculate the volume of SBF used for each sample, we used the following formula:
Vs = 100 mm × Sa
where Vs is the volume of SBF in mm3, and Sa is the surface area of the pellet in mm2.
After soaking, the pellets were collected and gently rinsed with deionized water and then dried at room temperature.
This assay aimed to determine the change in ion concentration and the formation of an apatite-like layer on the bioglass surface over 28 days with the presence of a different concentration of Nb2O5. For that, TESCAN Vega 3 scanning electron microscopy (SEM) (TESCAN ORSAY HOLDING, a.s., Brno-Kohoutovice, Czech Republic) equipped with energy-dispersive X-ray spectroscopy (EDS) (Bruker EDS) was performed on the glass surface to determine the morphological and compositional changes resulting from the reaction in SBF.

5. Conclusions

Bioactive 45S5 glasses modified by the insertion of different amounts of niobium pentoxide, Nb2O5, were successfully synthesized using the melt-quenching technique. XRD and FTIR results show that there was no alteration in the glass matrix with the addition of Nb. The characterization using Raman spectroscopy showed the appearance of additional bands for the bioactive glass containing niobium attributed to the distortion of NbO6 units and the vibration of NbO4. The fractional conversion of the network modifier units of NbO6 into the NbO4 network former affects the electrical properties of the sample and causes a decrease in the bioactivity and antibacterial effect. The sample with 2 mol% of Nb2O5 content presented the highest percentage of NbO6 units and showed a higher dissolution rate and maximal growth of the HA layer on its surface in the in vitro immersion tests in SBF. Moreover, the evaluation of the antibacterial activity against E. coli, S. aureus, and S. mutans revealed that glass loaded with 2 mol% of Nb2O5 had the greatest antibacterial effect. We can conclude that the 45S5 bioactive glass modified by the insertion of 2 mol% of Nb2O5 is more suitable for biomedical applications and can be employed as a coating material for a dental implant without being harmful to osteoblasts cells.

Author Contributions

Conceptualization, I.H., S.R.G., A.S.P., I.S.-N. and M.P.F.G.; methodology, I.H., S.R.G., A.S.P., I.S.-N. and M.P.F.G.; software, I.H.; validation, I.H. and M.P.F.G.; formal analysis, I.H.; investigation, I.H., S.R.G., A.S.P., S.K.J., I.S.-N. and M.P.F.G.; resources, J.C.S., J.P.B., I.S.-N. and M.P.F.G.; data curation, I.H.; writing—original draft preparation, I.H.; writing—review and editing, M.P.F.G., I.S.-N., J.C.S., J.P.B., S.K.J. and M.d.C.L.; visualization, I.H. and M.P.F.G.; supervision, M.P.F.G., J.C.S. and J.P.B. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by FEDER funds through the COMPETE 2020 Program and National Funds through FCT—Portuguese Foundation for Science and Technology under the project LISBOA-01-0247-FEDER-039985/POCI-01-0247-FEDER-039985, LA/P/0037/2020, UIDP/50025/2020, and UIDB/50025/2020 of the Associate Laboratory Institute of Nanostructures, Nanomodelling and Nanofabrication—i3N, UIDP/04378/2020 and UIDB/04378/2020 of the Research Unit on Applied Molecular Biosciences—UCIBIO, and LA/P/0140/2020 of the Associate Laboratory Institute for Health and Bioeconomy—i4HB. S.R. Gavinho and A. Sofia Pádua acknowledges FCT—Portuguese Foundation for Science and Technology for the PhD grant (SFRH/BD/148233/2019 and UI/DB/151287/2021, respectively). S.K. Jakka acknowledges FCT—Fundaçao para a Ciência e a Tecnologia, Portugal, I.P., in the scope of the framework contract foreseen in the numbers 4, 5, and 6 of article 23 of the Decree Law 57/2016 of 29 August, changed by Law 57/2017 of 19 July.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Gaviria, L.; Salcido, J.P.; Guda, T.; Ong, J.L. Current trends in dental implants. J. Korean Assoc. Oral Maxillofac. Surg. 2014, 40, 50. [Google Scholar] [CrossRef] [PubMed]
  2. Gupta, A.; Dhanraj, M.; Sivagami, G. Status of surface treatment in endosseous implant: A literary overview. Indian J. Dental Res. 2010, 21, 433. [Google Scholar] [CrossRef]
  3. Gavinho, S.R.; Graça, M.P.F.; Prezas, P.R.; Kumar, J.S.; Melo, B.M.G.; Sales, A.J.M.; Almeida, A.F.; Valente, M.A. Structural, thermal, morphological and dielectric investigations on 45S5 glass and glass-ceramics. J. Non-Cryst. Solids 2021, 562, 120780. [Google Scholar] [CrossRef]
  4. Zhao, L.; Wang, H.; Huo, K.; Cui, L.; Zhang, W.; Ni, H.; Zhang, Y.; Wu, Z.; Chu, P.K. Antibacterial nano-structured titania coating incorporated with silver nanoparticles. Biomaterials 2011, 32, 5706–5716. [Google Scholar] [CrossRef]
  5. Wang, Z.; Shen, Y.; Haapasalo, M. Dent. Mater. with antibiofilm properties. Dent. Mater. 2014, 30, e1–e16. [Google Scholar] [CrossRef]
  6. Charalampakis, G.; Leonhardt, Å.; Rabe, P.; Dahlén, G. Clinical and microbiological characteristics of peri-implantitis cases: A retrospective multicentre study. Clin. Oral Implants Res. 2012, 23, 1045–1054. [Google Scholar] [CrossRef] [PubMed]
  7. Tibbitt, M.W.; Rodell, C.B.; Burdick, J.A.; Anseth, K.S. Progress in material design for biomedical applications. Proc. Natl. Acad. Sci. USA 2015, 112, 14444–14451. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  8. Festas, A.J.; Ramos, A.; Davim, J.P. Medical devices biomaterials—A review. Proc. Instit. Mech. Eng. Part L 2020, 234, 218–228. [Google Scholar] [CrossRef]
  9. Chen, F.-M.; Liu, X. Advancing biomaterials of human origin for tissue engineering. Prog. Polym. Sci. 2016, 53, 86–168. [Google Scholar] [CrossRef] [Green Version]
  10. Becerikli, M.; Jaurich, H.; Wallner, C.; Wagner, J.M.; Dadras, M.; Jettkant, B.; Pöhl, F.; Seifert, M.; Jung, O.; Mitevski, B. P2000-A high-nitrogen austenitic steel for application in bone surgery. PLoS ONE 2019, 14, e0214384. [Google Scholar] [CrossRef]
  11. Ramakrishna, S.; Ramalingam, M.; Kumar, T.S.; Soboyejo, W.O. Biomaterials: A nano Approach; CRC Press: Boca Raton, FL, USA, 2016. [Google Scholar]
  12. Singh, N.; Hameed, P.; Ummethala, R.; Manivasagam, G.; Prashanth, K.G.; Eckert, J. Selective laser manufacturing of Ti-based alloys and composites: Impact of process parameters, application trends, and future prospects. Mater. Today Adv. 2020, 8, 100097. [Google Scholar] [CrossRef]
  13. Boccaccini, A.R.; Brauer, D.S.; Hupa, L. Bioactive Glasses: Fundamentals, Technology and Applications; Royal Society of Chemistry: London, UK, 2016. [Google Scholar]
  14. Ylänen, H. Bioactive Glasses: Materials, Properties and Applications; Woodhead Publishing: Sawston, UK, 2017. [Google Scholar]
  15. Shukla, A.A.; Etzel, M.R.; Gadam, S. Process Scale Bioseparations for the Biopharmaceutical Industry; CRC Press: Boca Raton, FL, USA, 2006. [Google Scholar]
  16. Zhang, B.G.; Myers, D.E.; Wallace, G.G.; Brandt, M.; Choong, P.F. Bioactive coatings for orthopaedic implants—Recent trends in development of implant coatings. Int. J. Mol. Sci. 2014, 15, 11878–11921. [Google Scholar] [CrossRef] [Green Version]
  17. Davidson, D.J.; Spratt, D.; Liddle, A.D. Implant materials and prosthetic joint infection: The battle with the biofilm. EFORT Open Rev. 2019, 4, 633–639. [Google Scholar] [CrossRef] [PubMed]
  18. Trisi, P.; Marcato, C.; Todisco, M. Bone-to-implant apposition with machined and MTX microtextured implant surfaces in human sinus grafts. Int. J. Period. Restor. Dent. 2003, 23, 426–437. [Google Scholar]
  19. Bornstein, M.M.; Lussi, A.; Schmid, B.; Belser, U.C.; Buser, D. Early loading of nonsubmerged titanium implants with a sandblasted and acid-etched (SLA) surface: 3-year results of a prospective study in partially edentulous patients. Int. J. Oral Maxillofac. Implants 2003, 18, 659–666. [Google Scholar]
  20. Al Mugeiren, O.M.; Baseer, M.A. Dental implant bioactive surface modifiers: An update. J. Int. Soc. Prevent. Commun. Dent. 2019, 9, 1. [Google Scholar] [CrossRef]
  21. Damiati, L.; Eales, M.G.; Nobbs, A.H.; Su, B.; Tsimbouri, P.M.; Salmeron-Sanchez, M.; Dalby, M.J. Impact of surface topography and coating on osteogenesis and bacterial attachment on titanium implants. J. Tissue Eng. 2018, 9, 2041731418790694. [Google Scholar] [CrossRef] [PubMed]
  22. Priyadarshini, B.; Rama, M.; Chetan; Vijayalakshmi, U. Bioactive coating as a surface modification technique for biocompatible metallic implants: A review. J. Asian Ceramic Soc. 2019, 7, 397–406. [Google Scholar] [CrossRef] [Green Version]
  23. Islam, M.T.; Felfel, R.M.; Abou Neel, E.A.; Grant, D.M.; Ahmed, I.; Hossain, K.M.Z. Bioactive calcium phosphate–based glasses and ceramics and their biomedical applications: A review. J. Tissue Eng. 2017, 8, 2041731417719170. [Google Scholar] [CrossRef] [Green Version]
  24. Alamri, A.; Salloot, Z.; Alshaia, A.; Ibrahim, M.S. The effect of bioactive glass-enhanced orthodontic bonding resins on prevention of demineralization: A systematic review. Molecules 2020, 25, 2495. [Google Scholar] [CrossRef]
  25. Hench, L.L. The story of Bioglass®. J. Mater. Sci. Mater. Med. 2006, 17, 967–978. [Google Scholar] [CrossRef]
  26. Hench, L.L. (Ed.) An Introduction to Bioceramics, 2nd ed.; Imperial College Press: London, UK, 2013; ISBN 978-1-908977-15-1. [Google Scholar]
  27. Boccaccini, A.R. (Ed.) Tissue Engineering Using Ceramics and Polymers, 2nd ed.; Elsevier: Amsterdam, The Netherlands, 2014; ISBN 978-0-85709-716-3. [Google Scholar]
  28. Zheng, K.; Sui, B.; Ilyas, K.; Boccaccini, A.R. Porous bioactive glass micro-and nanospheres with controlled morphology: Developments, properties and emerging biomedical applications. Mater. Horiz. 2021, 8, 300–335. [Google Scholar] [CrossRef]
  29. Xynos, I.D.; Edgar, A.J.; Buttery, L.D.; Hench, L.L.; Polak, J.M. Ionic products of bioactive glass dissolution increase proliferation of human osteoblasts and induce insulin-like growth factor II mRNA expression and protein synthesis. Biochem. Biophys. Res. Commun. 2000, 276, 461–465. [Google Scholar] [CrossRef]
  30. Vollenweider, M.; Brunner, T.J.; Knecht, S.; Grass, R.N.; Zehnder, M.; Imfeld, T.; Stark, W.J. Remineralization of human dentin using ultrafine bioactive glass particles. Acta Biomater. 2007, 3, 936–943. [Google Scholar] [CrossRef]
  31. Rahaman, M.N.; Liu, X.; Bal, B.S.; Day, D.E.; Bi, L.; Bonewald, L.F. Bioactive glass in bone tissue engineering. Biomater. Sci. Process. Prop. Appl. II 2012, 237, 73–82. [Google Scholar]
  32. Pantulap, U.; Arango-Ospina, M.; Boccaccini, A.R. Bioactive glasses incorporating less-common ions to improve biological and physical properties. J. Mater. Sci. Mater. Med. 2022, 33, 1–41. [Google Scholar] [CrossRef] [PubMed]
  33. Joy-anne, N.O.; Akande, O.; Ecker, M. Incorporation of Novel Elements in Bioactive Glass Compositions to Enhance Implant Performance. In Current Concepts in Dental Implantology-From Science to Clinical Research; IntechOpen: London, UK, 2021. [Google Scholar]
  34. Leung, Y.H.; Ng, A.M.; Xu, X.; Shen, Z.; Gethings, L.A.; Wong, M.T.; Chan, C.M.; Guo, M.Y.; Ng, Y.H.; Djurišić, A.B. Mechanisms of antibacterial activity of MgO: Non-ROS mediated toxicity of MgO nanoparticles towards Escherichia coli. Small 2014, 10, 1171–1183. [Google Scholar] [CrossRef]
  35. Tian, T.; Wu, C.; Chang, J. Preparation and in vitro osteogenic, angiogenic and antibacterial properties of cuprorivaite (CaCuSi 4 O 10, Cup) bioceramics. RSC Adv. 2016, 6, 45840–45849. [Google Scholar] [CrossRef]
  36. Palanikumar, L.; Ramasamy, S.N.; Balachandran, C. Size-dependent antimicrobial response of zinc oxide nanoparticles. IET Nanobiotechnol. 2014, 8, 111–117. [Google Scholar] [CrossRef]
  37. Oliveira, R.L.; Barbosa, L.; Hurtado, C.R.; Ramos, L. de P.; Montanheiro, T.L.; Oliveira, L.D.; Tada, D.B.; Triches, E. de S. Bioglass-based scaffolds coated with silver nanoparticles: Synthesis, processing and antimicrobial activity. J. Biomed. Mater. Res. Part A 2020, 108, 2447–2459. [Google Scholar] [CrossRef] [PubMed]
  38. Mourino, V.; Cattalini, J.P.; Boccaccini, A.R. Metallic ions as therapeutic agents in tissue engineering scaffolds: An overview of their biological applications and strategies for new developments. J. R. Soc. Interface 2012, 9, 401–419. [Google Scholar] [CrossRef] [Green Version]
  39. Hoppe, A.; Güldal, N.S.; Boccaccini, A.R. A review of the biological response to ionic dissolution products from bioactive glasses and glass-ceramics. Biomaterials 2011, 32, 2757–2774. [Google Scholar] [CrossRef] [PubMed]
  40. Nour, S.; Baheiraei, N.; Imani, R.; Rabiee, N.; Khodaei, M.; Alizadeh, A.; Moazzeni, S.M. Bioactive materials: A comprehensive review on interactions with biological microenvironment based on the immune response. J. Bionic Eng. 2019, 16, 563–581. [Google Scholar] [CrossRef]
  41. Fernandes, G.V.D.O.; Alves, G.; Linhares, A.B.R.; Prado da Silva, M.H.; Granjeiro, J.M. Evaluation of cytocompatibility of bioglass-niobium granules with human primary osteoblasts: A multiparametric approach. In Proceedings of the Key Engineering Materials; Trans. Tech. Publ.: Stafa-Zurich, Switzerland, 2012; Volume 493, pp. 37–42. [Google Scholar]
  42. Holloway, E.M.; Wu, J.H.; Czerwinski, M.; Sweet, C.W.; Wu, A.; Tsai, Y.-H.; Huang, S.; Stoddard, A.E.; Capeling, M.M.; Glass, I. Differentiation of human intestinal organoids with endogenous vascular endothelial cells. Dev. Cell 2020, 54, 516–528. [Google Scholar] [CrossRef]
  43. Denry, I.L.; Holloway, J.A.; Nakkula, R.J.; Walters, J.D. Effect of niobium content on the microstructure and thermal properties of fluorapatite glass-ceramics. J. Biomed. Mater. Res. Part B 2005, 75, 18–24. [Google Scholar] [CrossRef] [PubMed]
  44. Takahashi, K.; Shiraishi, N.; Ishiko-Uzuka, R.; Anada, T.; Suzuki, O.; Masumoto, H.; Sasaki, K. Biomechanical evaluation of Ti-Nb-Sn alloy implants with a low Young’s modulus. Int. J. Mol. Sci. 2015, 16, 5779–5788. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  45. Prado da Silva, M.H.; Ramirez, C.M.; Granjeiro, J.M.; Rossi, A.M. In vitro assessment of new niobium phosphate glasses and glass ceramics. In Proceedings of the Key Engineering Materials; Trans. Tech. Publ.: Stafa-Zurich, Switzerland, 2008; Volume 361, pp. 229–232. [Google Scholar]
  46. Gavinho, S.R.; Pádua, A.S.; Sá-Nogueira, I.; Silva, J.C.; Borges, J.P.; Costa, L.C.; Graça, M.P.F. Biocompatibility, Bioactivity, and Antibacterial Behaviour of Cerium-Containing Bioglass®. Nanomaterials 2022, 12, 4479. [Google Scholar] [CrossRef]
  47. Senapati, A.; Barik, S.K.; Venkata Krishnan, R.; Chakraborty, S.; Jena, H. Studies on synthesis, structural and thermal properties of sodium niobium phosphate glasses for nuclear waste immobilization applications. J. Ther. Anal. Calorim. 2022, 148, 1–15. [Google Scholar] [CrossRef]
  48. Gupta, N.; Santhiya, D.; Murugavel, S.; Kumar, A.; Aditya, A.; Ganguli, M.; Gupta, S. Effects of transition metal ion dopants (Ag, Cu and Fe) on the structural, mechanical and antibacterial properties of bioactive glass. Colloids Surf. A Physicochem. Eng. Asp. 2018, 538, 393–403. [Google Scholar] [CrossRef]
  49. Miola, M.; Verné, E.; Ciraldo, F.E.; Cordero-Arias, L.; Boccaccini, A.R. Electrophoretic deposition of chitosan/45S5 bioactive glass composite coatings doped with Zn and Sr. Front. Bioeng. Biotechnol. 2015, 3, 159. [Google Scholar] [CrossRef] [Green Version]
  50. Ibrahim, N.F.; Mohamad, H.; Noor, S.N.F.M. Characterization on melt-derived bioactive glass powder from SiO2-CaO-Na2O-P2O5 system. J. Non-Cryst. Solids 2017, 462, 23–31. [Google Scholar] [CrossRef]
  51. Ibrahim, N.F.; Mohamad, H.; Noor, S.N.F.M.; Ahmad, N. Melt-derived bioactive glass based on SiO2-CaO-Na2O-P2O5 system fabricated at lower melting temperature. J. Alloys Compd. 2018, 732, 603–612. [Google Scholar] [CrossRef]
  52. El-Rashidy, A.A.; Roether, J.A.; Harhaus, L.; Kneser, U.; Boccaccini, A.R. Regenerating bone with bioactive glass scaffolds: A review of in vivo studies in bone defect models. Acta Biomater. 2017, 62, 1–28. [Google Scholar] [CrossRef] [PubMed]
  53. Boccaccini, A.R.; Chen, Q.; Lefebvre, L.; Gremillard, L.; Chevalier, J. Sintering, crystallisation and biodegradation behaviour of Bioglass®-derived glass–ceramics. Farad. Discuss. 2007, 136, 27–44. [Google Scholar] [CrossRef]
  54. Dziadek, M.; Zagrajczuk, B.; Jelen, P.; Olejniczak, Z.; Cholewa-Kowalska, K. Structural variations of bioactive glasses obtained by different synthesis routes. Ceram. Int. 2016, 42, 14700–14709. [Google Scholar] [CrossRef]
  55. Akhtach, S.; Tabia, Z.; El Mabrouk, K.; Bricha, M.; Belkhou, R. A comprehensive study on copper incorporated bio-glass matrix for its potential antimicrobial applications. Ceram. Int. 2021, 47, 424–433. [Google Scholar] [CrossRef]
  56. Dunne, C.F.; Twomey, B.; Stanton, K.T. Effect of a blast coating process on the macro-and microstructure of Grade 5 titanium foam. Mater. Lett. 2015, 147, 75–78. [Google Scholar] [CrossRef]
  57. Aguiar, H.; Serra, J.; González, P.; León, B. Structural study of sol–gel silicate glasses by IR and Raman spectroscopies. J. Non-Cryst. Solids 2009, 355, 475–480. [Google Scholar] [CrossRef]
  58. Aguiar, H.; Solla, E.L.; Serra, J.; González, P.; León, B.; Almeida, N.; Cachinho, S.; Davim, E.J.C.; Correia, R.; Oliveira, J.M. Orthophosphate nanostructures in SiO2–P2O5–CaO–Na2O–MgO bioactive glasses. J. Non-Cryst. Solids 2008, 354, 4075–4080. [Google Scholar] [CrossRef]
  59. Lopes, J.H.; Magalhães, A.; Mazali, I.O.; Bertran, C.A. Effect of niobium oxide on the structure and properties of melt-derived bioactive glasses. J. Am. Ceram. Soc. 2014, 97, 3843–3852. [Google Scholar] [CrossRef]
  60. Aronne, A.; Sigaev, V.N.; Champagnon, B.; Fanelli, E.; Califano, V.; Usmanova, L.Z.; Pernice, P. The origin of nanostructuring in potassium niobiosilicate glasses by Raman and FTIR spectroscopy. J. Non-Cryst. Solids 2005, 351, 3610–3618. [Google Scholar] [CrossRef]
  61. Santos, L.F.; Wondraczek, L.; Deubener, J.; Almeida, R.M. Vibrational spectroscopy study of niobium germanosilicate glasses. J. Non-Cryst. Solids 2007, 353, 1875–1881. [Google Scholar] [CrossRef]
  62. Fukumi, K.; Sakka, S. Coordination state of Nb5+ ions in silicate and gallate glasses as studied by Raman spectroscopy. J. Mater. Sci. 1988, 23, 2819–2823. [Google Scholar] [CrossRef]
  63. Sene, F.F.; Martinelli, J.R.; Gomes, L. Synthesis and characterization of niobium phosphate glasses containing barium and potassium. J. Non-Cryst. Solids 2004, 348, 30–37. [Google Scholar] [CrossRef]
  64. Graça, M.P.F.; da Silva, M.F.; Valente, M.A. NaNbO3 crystals dispersed in a B2O3 glass matrix–Structural characteristics versus electrical and dielectrical properties. Solid State Sci. 2009, 11, 570–577. [Google Scholar] [CrossRef]
  65. Araujo, M.S.; Silva, A.C.; Bartolomé, J.F.; Mello-Castanho, S. Structural and thermal behavior of 45S5 Bioglass®-based compositions containing alumina and strontium. J. Am. Ceram. Soc. 2020, 103, 3620–3630. [Google Scholar] [CrossRef]
  66. Langar, A.; Sdiri, N.; Elhouichet, H.; Ferid, M. Structure and electrical characterization of ZnO-Ag phosphate glasses. Results Phys. 2017, 7, 1022–1029. [Google Scholar] [CrossRef]
  67. Farid, A.M.; Bekheet, A.E. AC conductivity and dielectric properties of Sb2S3 films. Vacuum 2000, 59, 932–939. [Google Scholar] [CrossRef]
  68. Hohenbild, F.; Arango-Ospina, M.; Moghaddam, A.; Boccaccini, A.R.; Westhauser, F. Preconditioning of bioactive glasses before introduction to static cell culture: What is really necessary? Methods Protoc. 2020, 3, 38. [Google Scholar] [CrossRef]
  69. Beaufils, S.; Rouillon, T.; Millet, P.; Le Bideau, J.; Weiss, P.; Chopart, J.-P.; Daltin, A.-L. Synthesis of calcium-deficient hydroxyapatite nanowires and nanotubes performed by template-assisted electrodeposition. Mater. Sci. Eng. C 2019, 98, 333–346. [Google Scholar] [CrossRef]
  70. Legeros, R.Z. Apatites in biological systems. Prog. Cryst. Growth Charact. 1981, 4, 1–45. [Google Scholar] [CrossRef]
  71. Silva, C.C.; Graça, M.P.F.; Valente, M.A.; Sombra, A.S.B. Crystallite size study of nanocrystalline hydroxyapatite and ceramic system with titanium oxide obtained by dry ball milling. J. Mater. Sci. 2007, 42, 3851–3855. [Google Scholar] [CrossRef]
  72. Madhavi, B.; Reddy, A.S.S.; Prasad, P.S.; Prasad, A.; Devi, P.P.K.; Kumar, V.R.; Veeraiah, N. The impact of Nb2O5 on in-vitro bioactivity and antibacterial activity of CaF2–CaO–B2O3–P2O5–SrO glass system. Ceram. Int. 2021, 47, 28328–28337. [Google Scholar] [CrossRef]
  73. Chu, C.M.; Wu, J.J.; Yung, S.W.; Chin, T.S.; Zhang, T.; Wu, F.B. Optical and structural properties of Sr–Nb–phosphate glasses. J. Non-Cryst. Solids 2011, 357, 939–945. [Google Scholar] [CrossRef]
  74. Maeda, H.; Lee, S.; Miyajima, T.; Obata, A.; Ueda, K.; Narushima, T.; Kasuga, T. Structure and physicochemical properties of CaO–P2O5–Nb2O5–Na2O glasses. J. Non-Cryst. Solids 2016, 432, 60–64. [Google Scholar] [CrossRef]
  75. de Siqueira, L.; Campos, T.M.; Camargo, S.E.; Thim, G.P.; Triches, E.S. Structural, crystallization and cytocompatibility evaluation of the 45S5 bioglass-derived glass-ceramic containing niobium. J. Non-Cryst. Solids 2021, 555, 120629. [Google Scholar] [CrossRef]
  76. Sanghi, S.; Rani, S.; Agarwal, A.; Bhatnagar, V. Influence of Nb2O5 on the structure, optical and electrical properties of alkaline borate glasses. Mater. Chem. Phys. 2010, 120, 381–386. [Google Scholar] [CrossRef]
  77. Obata, A.; Nakamura, S.; Moriyoshi, Y.; Yamashita, K. Electrical polarization of bioactive glass and assessment of their in vitro apatite deposition. J. Biomed. Mater. Res. Part A 2003, 67, 413–420. [Google Scholar] [CrossRef]
  78. Altmann, A.S.P.; Collares, F.M.; Leitune, V.C.B.; Arthur, R.A.; Takimi, A.S.; Samuel, S.M.W. In vitro antibacterial and remineralizing effect of adhesive containing triazine and niobium pentoxide phosphate inverted glass. Clin. Oral Investig. 2017, 21, 93–103. [Google Scholar] [CrossRef]
  79. Obata, A.; Takahashi, Y.; Miyajima, T.; Ueda, K.; Narushima, T.; Kasuga, T. Effects of niobium ions released from calcium phosphate invert glasses containing Nb2O5 on osteoblast-like cell functions. ACS Appl. Mater. Interfaces 2012, 4, 5684–5690. [Google Scholar] [CrossRef]
  80. Allan, I.; Newman, H.; Wilson, M. Antibacterial activity of particulate Bioglass® against supra-and subgingival bacteria. Biomaterials 2001, 22, 1683–1687. [Google Scholar] [CrossRef]
  81. Drago, L.; Toscano, M.; Bottagisio, M. Recent evidence on bioactive glass antimicrobial and antibiofilm activity: A mini-review. Materials 2018, 11, 326. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  82. Hu, S.; Chang, J.; Liu, M.; Ning, C. Study on antibacterial effect of 45S5 Bioglass®. J. Mater. Sci. Mater. Med. 2009, 20, 281–286. [Google Scholar] [CrossRef]
  83. Dorozhkin, S.V.; Epple, M. Biological and medical significance of calcium phosphates. Angew. Chem. Int. Ed. 2002, 41, 3130–3146. [Google Scholar] [CrossRef]
  84. Chien, C.-S.; Liao, T.-Y.; Hong, T.-F.; Kuo, T.-Y.; Chang, C.-H.; Yeh, M.-L.; Lee, T.-M. Surface microstructure and bioactivity of hydroxyapatite and fluorapatite coatings deposited on Ti-6Al-4V substrates using Nd-YAG laser. J. Med. Biol. Eng 2014, 34, 109–115. [Google Scholar] [CrossRef]
  85. Bano, S.; Romero, A.R.; Grant, D.M.; Nommeots-Nomm, A.; Scotchford, C.; Ahmed, I.; Hussain, T. In-vitro cell interaction and apatite forming ability in simulated body fluid of ICIE16 and 13–93 bioactive glass coatings deposited by an emerging suspension high velocity oxy fuel (SHVOF) thermal spray. Surf. Coat. Technol. 2021, 407, 126764. [Google Scholar] [CrossRef]
  86. El-Mallawany, R.A. Tellurite Glasses Handbook: Physical Properties and Data; CRC Press: Boca Raton, FL, USA, 2014. [Google Scholar]
  87. Feroci, M. Investigation of the role of electrogenerated N-heterocyclic carbene in the Staudinger synthesis in ionic liquid. Int. J. Org. Chem. 2011, 1, 191. [Google Scholar] [CrossRef] [Green Version]
  88. Graça, M.P.F.; Ferreira da Silva, M.G.; Valente, M.A. Preparation, structure, morphology, and dc and ac conductivity of the 88SiO2-6Li2O-6Nb2O5 (% mole) sol-gel derived glass-ceramics. J. Sol-Gel Sci. Technol. 2007, 42, 1–8. [Google Scholar] [CrossRef]
  89. Macdonald, J. Emphasizing solid materials and systems. In Impedance Spectroscopy; John Wiley & Sons Inc.: New York, NY, USA, 1987. [Google Scholar]
  90. Graça, M.P.F.; da Silva, M.F.; Sombra, A.S.B.; Valente, M.A. Electric and dielectric properties of a SiO2–Na2O–Nb2O5 glass subject to a controlled heat-treatment process. Phys. B Condens. Matter 2007, 396, 62–69. [Google Scholar] [CrossRef]
  91. Graça, M.P.F.; da Silva, M.F.; Sombra, A.S.B.; Valente, M.A. Electrical characterization of SiO2: LiNbO3 glass and glass–ceramics using dc conductivity, TSDC measurements and dielectric spectroscopy. J. Non-Cryst. Solids 2007, 353, 4390–4394. [Google Scholar] [CrossRef]
  92. ISO 10993-5:2009; Biological Evaluation of Medical Devices—Part 5: Tests for In Vitro Cytotoxicity. International Organization for Standardization: Geneva, Switzerland, 2009.
  93. Vieira, T.; Silva, J.C.; do Rego, A.B.; Borges, J.P.; Henriques, C. Electrospun biodegradable chitosan based-poly (urethane urea) scaffolds for soft tissue engineering. Mater. Sci. Eng. C 2019, 103, 109819. [Google Scholar] [CrossRef] [PubMed]
  94. Schneider, C.A.; Rasband, W.S.; Eliceiri, K.W. NIH Image to ImageJ: 25 years of image analysis. Nat. Methods 2012, 9, 671–675. [Google Scholar] [CrossRef] [PubMed]
Ijms 24 05244 g001 550
Figure 1. XRD patterns of 45S5 bioglass samples modified by the insertion of 0 and 8 mol% of Nb2O5.
Figure 1. XRD patterns of 45S5 bioglass samples modified by the insertion of 0 and 8 mol% of Nb2O5.
Ijms 24 05244 g001
Ijms 24 05244 g002 550
Figure 2. FTIR spectra of bioactive glasses modified by Nb2O5 insertion.
Figure 2. FTIR spectra of bioactive glasses modified by Nb2O5 insertion.
Ijms 24 05244 g002
Ijms 24 05244 g003 550
Figure 3. Raman spectra of bioactive glasses modified by Nb2O5 insertion.
Figure 3. Raman spectra of bioactive glasses modified by Nb2O5 insertion.
Ijms 24 05244 g003
Ijms 24 05244 g004 550
Figure 4. Deconvoluted Raman spectra of (a) BGNb1; (b) BGNb2; (c) BGNb4; and (d) BGNb8.
Figure 4. Deconvoluted Raman spectra of (a) BGNb1; (b) BGNb2; (c) BGNb4; and (d) BGNb8.
Ijms 24 05244 g004
Ijms 24 05244 g005 550
Figure 5. Sum of the areas of the bands associated with NBOs vibrations.
Figure 5. Sum of the areas of the bands associated with NBOs vibrations.
Ijms 24 05244 g005
Ijms 24 05244 g006 550
Figure 6. DTA spectra of (a) BGNb2; (b) BGNb8.
Figure 6. DTA spectra of (a) BGNb2; (b) BGNb8.
Ijms 24 05244 g006
Ijms 24 05244 g007 550
Figure 7. DC conductivity versus 1000/T (inset: a magnification of the high-temperature measurement zone is shown in the inset; the lines reflect the Arrhenius fit).
Figure 7. DC conductivity versus 1000/T (inset: a magnification of the high-temperature measurement zone is shown in the inset; the lines reflect the Arrhenius fit).
Ijms 24 05244 g007
Ijms 24 05244 g008 550
Figure 8. The imaginary part of the dielectric modulus (M″) versus frequency for BGNb2 glass, between 200 K and 400 K.
Figure 8. The imaginary part of the dielectric modulus (M″) versus frequency for BGNb2 glass, between 200 K and 400 K.
Ijms 24 05244 g008
Ijms 24 05244 g009 550
Figure 9. AC conductivity versus 1000/T at (a) 1 kHz; (b) 10 kHz (inset: magnification of the high-temperature measurement zone; the lines reflect the Arrhenius fit).
Figure 9. AC conductivity versus 1000/T at (a) 1 kHz; (b) 10 kHz (inset: magnification of the high-temperature measurement zone; the lines reflect the Arrhenius fit).
Ijms 24 05244 g009
Ijms 24 05244 g010 550
Figure 10. Relative viability of (a) non-passivated and (b) passivated bioactive glass samples modified by Nb2O5 insertion, in culture with Saos-2 cells.
Figure 10. Relative viability of (a) non-passivated and (b) passivated bioactive glass samples modified by Nb2O5 insertion, in culture with Saos-2 cells.
Ijms 24 05244 g010
Ijms 24 05244 g011 550
Figure 11. Antibacterial activity of the bioglass samples against E. coli, S. aureus, and S. mutans based on inhibition halo. Results are reported as mean ± SD. The asterisks indicate significance in an unpaired t-test; * p ≤ 0.05; ** p ≤ 0.01; *** p ≤ 0.001; **** p ≤ 0.0001.
Figure 11. Antibacterial activity of the bioglass samples against E. coli, S. aureus, and S. mutans based on inhibition halo. Results are reported as mean ± SD. The asterisks indicate significance in an unpaired t-test; * p ≤ 0.05; ** p ≤ 0.01; *** p ≤ 0.001; **** p ≤ 0.0001.
Ijms 24 05244 g011
Ijms 24 05244 g012 550
Figure 12. SEM micrographs of five groups of bioactive glass samples modified by the insertion of different percentages of Nb2O5 after immersion in SBF for (a1–a5) 24 h; (b1–b5) 14 d; (c1–c5) 28 d; (d1–d5) plots of the EDS analysis for all immersion times. (The magnification of SEM images is 10 kX).
Figure 12. SEM micrographs of five groups of bioactive glass samples modified by the insertion of different percentages of Nb2O5 after immersion in SBF for (a1–a5) 24 h; (b1–b5) 14 d; (c1–c5) 28 d; (d1–d5) plots of the EDS analysis for all immersion times. (The magnification of SEM images is 10 kX).
Ijms 24 05244 g012
Ijms 24 05244 g013 550
Figure 13. The variation of elemental concentration of (a) Si; (b) Na; (c) Ca/P ratio on the surface of bioactive glasses after immersion in SBF as a function of immersion time.
Figure 13. The variation of elemental concentration of (a) Si; (b) Na; (c) Ca/P ratio on the surface of bioactive glasses after immersion in SBF as a function of immersion time.
Ijms 24 05244 g013
Ijms 24 05244 g014 550
Figure 14. Variation of pH of the SBF solution with the immersion time.
Figure 14. Variation of pH of the SBF solution with the immersion time.
Ijms 24 05244 g014
Table
Table 1. The characteristic temperatures for BGNb0, BGNb2, and BGNb8.
Table 1. The characteristic temperatures for BGNb0, BGNb2, and BGNb8.
SampleTg (°C)Tc (°C)Tm (°C)
BGNb0 [3]5527281175
BGNb25506841077
BGNb85918111110
Table
Table 2. The DC conductivity (σDC), DC activation energy Ea (DC), AC conductivity (σAC), and AC activation energy Ea (AC), for all bioglass samples.
Table 2. The DC conductivity (σDC), DC activation energy Ea (DC), AC conductivity (σAC), and AC activation energy Ea (AC), for all bioglass samples.
SampleσDC (×10−9)
[S/m]
(At 300 K)		Ea (DC)
[kJ/mol]		σAC (×10−7)
[S/m]
(At 350 K, 1 kHz)		Ea (AC)
[kJ/mol]
(At 1 kHz)		σAC (×10−7)
[S/m]
(At 350 K, 10 kHz)		Ea (AC)
[kJ/mol]
(At 10 kHz)
BGNb00.91 ± 0.0175.42 ± 0.081.50 ± 0.0149.39 ± 0.984.91 ± 0.0537.95 ± 0.97
BGNb10.78 ± 0.0476.79 ± 0.061.84 ± 0.0450.21 ± 0.965.65 ± 0.1138.49 ± 0.79
BGNb21.52 ± 0.1069.35 ± 0.202.36 ± 0.0348.61 ± 0.876.54 ± 0.1337.83 ± 0.61
BGNb40.51 ± 0.0276.47 ± 0.151.17 ± 0.0147.55 ± 0.863.69 ± 0.0636.37 ± 0.66
BGNb80.19 ± 0.0179.47 ± 0.161.23 ± 0.0244.25 ± 0.924.60 ± 0.2134.11 ± 0.69
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Hammami, I.; Gavinho, S.R.; Pádua, A.S.; Lança, M.d.C.; Borges, J.P.; Silva, J.C.; Sá-Nogueira, I.; Jakka, S.K.; Graça, M.P.F. Extensive Investigation on the Effect of Niobium Insertion on the Physical and Biological Properties of 45S5 Bioactive Glass for Dental Implant. Int. J. Mol. Sci. 2023, 24, 5244. https://doi.org/10.3390/ijms24065244

AMA Style

Hammami I, Gavinho SR, Pádua AS, Lança MdC, Borges JP, Silva JC, Sá-Nogueira I, Jakka SK, Graça MPF. Extensive Investigation on the Effect of Niobium Insertion on the Physical and Biological Properties of 45S5 Bioactive Glass for Dental Implant. International Journal of Molecular Sciences. 2023; 24(6):5244. https://doi.org/10.3390/ijms24065244

Chicago/Turabian Style

Hammami, Imen, Sílvia Rodrigues Gavinho, Ana Sofia Pádua, Maria do Carmo Lança, João Paulo Borges, Jorge Carvalho Silva, Isabel Sá-Nogueira, Suresh Kumar Jakka, and Manuel Pedro Fernandes Graça. 2023. "Extensive Investigation on the Effect of Niobium Insertion on the Physical and Biological Properties of 45S5 Bioactive Glass for Dental Implant" International Journal of Molecular Sciences 24, no. 6: 5244. https://doi.org/10.3390/ijms24065244

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop