Next Article in Journal
Optothermal Raman Spectroscopy of Black Phosphorus on a Gold Substrate
Next Article in Special Issue
Electrospun Donor/Acceptor Nanofibers for Efficient Photocatalytic Hydrogen Evolution
Previous Article in Journal
Photoelectrochemical Response Enhancement for Metallofullerene-[12]Cycloparaphenylene Supramolecular Complexes
Previous Article in Special Issue
Highly Efficient Photothermal Reduction of CO2 on Pd2Cu Dispersed TiO2 Photocatalyst and Operando DRIFT Spectroscopic Analysis of Reactive Intermediates
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 9
10.3390/nano12091409
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation and Photocatalytic Properties of Anatase TiO2 with Hollow Hexagonal Frame Structure

by
Mengyuan Teng
,
Haixia Liu
*,
Bensheng Lin
,
Xiangzhu Zhou
and
Wei Zhou
*
Shandong Provincial Key Laboratory of Molecular Engineering, School of Chemistry and Chemical Engineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, China
*
Authors to whom correspondence should be addressed.
Nanomaterials 2022, 12(9), 1409; https://doi.org/10.3390/nano12091409
Submission received: 30 March 2022 / Revised: 13 April 2022 / Accepted: 15 April 2022 / Published: 20 April 2022
(This article belongs to the Special Issue Semiconductor-Based Nanomaterials for Photocatalytic Applications)
Browse Figures
Versions Notes

Abstract

:
Titanium dioxide (TiO2) has been widely used to solve energy and environmental pollution problems due to its excellent properties. In this study, the precursor (HTiOF3) with a spherical structure composed of hexagonal prisms was prepared via a simple solvothermal method using tetrabutyl titanate, hydrofluoric acid, glacial acetic acid and isopropanol as raw materials. Then, the calcination time and temperature of the precursor were controlled to prepare anatase TiO2 with different morphologies, and the photocatalytic performance of the prepared catalysts was studied. When the precursor was calcined at 600 °C for 7 h, the prepared TiO2 had a unique hexagonal framework structure and exhibited excellent photocatalytic performance. The degradation rate of the RhB solution was 98.58% at 40 min and the rate of hydrogen evolution was 2508.12 μmol g−1 h−1.

1. Introduction

TiO2 as an essential component of inorganic semiconductor catalysts has been attracting attention for a long time. It is considered to be an effective, environmentally benign and simple synthetic semiconductor photocatalytic material. It has been widely applied to many fields, such as photocatalysis, environmental pollution control and new energy conversion [1,2,3,4,5,6]. For most pragmatic applications of TiO2, it is of great importance to have exact control of the morphology, size, crystal phase and specific surface area because the properties of TiO2 strongly depend on these structural characteristics [7,8,9,10,11,12,13]. In particular, there are more and more researchers focusing their attention on the controllable synthesis of anatase TiO2, which shows a higher photoactivity than brookite or rutile [14].
In recent years, multifarious anatase TiO2 with different morphologies were reported, such as nanorods, nanoflowers and nanotubes [15,16,17]. Many researchers have put in a great deal of effort to explore the synthesis of various TiO2 nanostructures. However, most synthetic strategies have relied on the complex processes of experiments or the use of templating agents. For example, Klara Hernadi’s group [18] reported the synthesis of TiO2 hollow spheres via a hydrothermal and annealing route. However, there are carbon spheres as an aid to the template in this process. Lu et al. [19] prepared nanoporous TiO2 via a complicated route, which required two steps to prepare. Therefore, researchers are working on a simple and effective method to synthesize TiO2 nanostructures with unique morphology to improve the photocatalytic performance of the samples [20,21].
More and more effort has been devoted to developing various hollow titanium dioxide materials with different sizes, shapes and polymorphs due to the advantages of hollow nanostructures. However, these materials are all based on spherical structures. There have rarely been reports about single-crystal TiO2 materials with a hexagonal morphology. In addition, most of the hollow structures are completed through HF engraving or a basic framework of polymeric materials [22,23]. It is a big challenge for researchers to synthesize non-spherical hollow frame nanomaterials.
In this work, anatase TiO2 with a hollow hexagonal frame structure was synthesized using a template-free method. First, the precursor (HTiOF3) with a spherical structure composed of hexagonal prisms was synthesized using the hydrothermal method. The effect of changing the type of solvent on the precursor morphology was investigated. Then, the precursor was converted to TiO2 via calcination. TiO2 with different morphologies could be obtained by changing the calcination temperature or time, and the photocatalytic performance could be affected by the different morphologies. The results showed that the hollow hexagonal frame TiO2 had excellent photocatalytic activity and good stability.

2. Materials and Methods

2.1. Materials

The starting materials that were utilized were tetrabutyl titanate (TBT, chemical purity grade, Shanghai Macklin Biochemical Co., Ltd., Shanghai, China), titanium tetraisopropanolate (Shanghai Macklin Biochemical Co., Ltd., Shanghai, China), acetic acid and isopropanol (Tianjin Fuyu Fine Chemical Co., Ltd., Tianjin, China) and hydrofluoric (Shanghai Macklin Biochemical Co., Ltd., Shanghai, China). All chemicals were used as received without further purification. Distilled water was used throughout the experiment.

2.2. Synthetic Process

First, acetic acid (28 mL, 9.2 M) and isopropanol (21 mL, 4.9 M) were measured and mixed well under magnetic stirring. Then, hydrofluoric acid (1.6 mL, 0.7 M) was added to the mixed solution at room temperature. Tetrabutyl titanate (0.01 mol) was added dropwise to the above-mixed solution and stirred for 30 min to blend well. The stirred solution was transferred to a Teflon-lined stainless steel autoclave (100 mL) and reacted at 180 °C for 10 h. In order to remove unreacted precursor in the solution, the product was rinsed 3 times with deionized water (20 mL) and then rinsed with ethanol (20 mL) 3 times. The product was collected via centrifugation (5 min per cycle at 8000 rpm). Finally, the product was dried at 60 °C overnight. The dried precursor was calcined at 600 °C for 7 h (600 °C/7 h) with a heating rate of 2 °C/min to obtain hollow hexagonal frame TiO2. The precursor was calcined with the same heating rate for 2 h at 100 °C (100 °C/2 h), 300 °C (300 °C/2 h) and 600 °C (600 °C/2 h) to explore the effect of calcination temperature and time on the morphology and properties. The effect on the final morphology of the precursor was explored by changing a variable in the reaction conditions while other reaction conditions were unchanged (Table 1).

2.3. Characterization

X-ray diffraction (XRD) data were tested using a Bruker D8 Advanced X-ray powder diffractometer (Rigaku Corp, Tokyo, Japan) with Cu-Ka radiation (λ = 1.5418 Å). The morphologies of the as-prepared samples were analyzed using scanning electron microscopy (SEM, S-4800, Hitachi, Tokyo, Japan). The UV-vis diffuse reflectance spectra (DRS) were acquired on a UV-2550 spectrophotometer (Shimadzu, Tokyo, Japan). Photoluminescence (PL) spectra were measured at room temperature using a spectrophotometer (F97Pro, Lengguang, Shanghai, China). The N2 adsorption and desorption tests of samples were undertaken on an Autorsorb-iQ instrument (Qutachrome, Boynton Beach, FL, USA). The specific surface area was calculated using the Brunauer–Emmett–Teller (BET) method. Thermogravimetric analysis (TG) was performed in a nitrogen (N2) atmosphere using a thermogravimetric analyzer (Q50, Waters, Milford, MA, USA) at a heating rate of 5 °C min−1.

2.4. Photoelectrochemical Test

The transient photocurrent response and electrochemical impedance were measured using 0.5 M Na2SO4 aqueous electrolyte on a CHI 760E (Shanghai, China) electrochemical workstation in a standard three-electrode system. Then, 10 mg catalysts were dissolved in a mixed solution of 0.98 mL ethanol and 0.02 mL Nafion (5.0 wt%) and then given an ultrasonic treatment for 1 h. Next, a 5 μL mixed solution was loaded on a glassy carbon electrode and dried to obtain a working electrode. Pt was used as the counter electrode and Ag/AgCl as the reference electrode. A 300 W Xe lamp (PLS-SXE300 UV, Beijing Perfectlight Co., Ltd., Being, China) was utilized as the light source.

2.5. Measurement of Photocatalytic Activity

In this process, Rhodamine B (RhB) dye was used to evaluate the photocatalytic activity of all samples [24]. First, 0.1 g synthetic catalyst was added to 100 mL RhB (20 mg/L) aqueous solution. In order to obtain an equilibrium adsorption state, the mixture was magnetically stirred for 30 min in the dark before irradiation. A 300 W xenon lamp (PLS-SXE300UV, Beijing Perfectlight Co., Ltd., Beijing, China) was used as the light source. Then, 3 mL reaction solution was taken out every 10 min under simulated sunlight and the catalyst was filtered out. Finally, the RhB solution was determined using UV-vis spectroscopy. Under the same experimental conditions, 0.05 g, 0.15 g and 0.2 g of the catalyst were added to 100 mL of RhB solution for comparative experiments to study the effect of catalyst addition on the degradation efficiency.

2.6. Measurement of Photocatalytic H2 Evolution

The photocatalytic H2 evolution test was performed according to the method reported by Xia et al. [25]. First, 50 mg catalyst was dispersed in 40 mL water and 10 mL methanol. Then, 1 wt% of Pt provided by H2PtCl6·6H2O was added to the mixed solution as a co-catalyst. The reaction device was sealed and N2 was used to purge the solution for 30 min. Under the ultraviolet light source provided by a 300 W Xe lamp (PLS-SXE300 UV, Beijing Perfectlight Co., Ltd., Beijing, China), hydrogen was generated via irradiation. The entire reaction was kept at 15 °C. A gas chromatograph with N2 as the carrier gas was used to detect the hourly H2 production.

3. Results

The TiO2 precursor (S1) obtained through the solvothermal reaction at 180 °C for 10 h was characterized using XRD and SEM. The corresponding XRD patterns are displayed in Figure 1a. Unexpectedly, the peaks of as-prepared samples in the XRD patterns were not in accordance with the anatase TiO2 structure (JCPDS NO.21-1272). It can be seen from the figure that the sample had diffraction peaks at 2θ = 13.92°, 23.67°, 28.10° and 48.40°, which corresponded to the {002}, {100}, {004} and {200} planes of HTiOF3 [26], respectively, and it could be preliminarily determined that the TiO2 precursor was HTiOF3. According to the energy-dispersive spectrometer (EDS) spectrum (Figure 1d,g), the sample was identified as a titanate compound, which included Ti, F and O elements. It could be further verified that the TiO2 precursor was HTiOF3. Subsequently, the as-prepared hexagonal TiO2 precursor nanospheres were characterized via scanning electron microscopy. It can be seen in Figure 1b,c that the precursor exhibited a spherical structure assembled from many hexagonal prisms with smooth surfaces. The size of each hexagonal prism was approximately 2–3 μm.
In order to explore the effects of different reaction conditions on the morphology of the samples with hexagonal structures, a series of experiments were also carried out by adjusting different solvents (Table 1). The crucial role of HAc is to inhibit the hydrolysis and morphological control agents of TBT. HAc played a vital role in determining the morphology of the hexagonal structure of HTiOF3 [27]. This was well demonstrated in the S2 experiment. When only HAc was not added, sample S2 exhibited sheet-like structures, as shown in Figure 2a,b. Furthermore, when isopropanol was not used, only some bulky and irregularly shaped block structures were found, as shown in Figure 2c,d. When HF was not added, no significant morphology was observed in the prepared sample (this sample is not shown here). This indicated that the special morphology of the hexagonal TiO2 structure could not be formed in the case of lacking one of the reactants. In addition, when the titanium source was changed from tetrabutyl titanate to titanium isopropoxide, the sample’s morphology was still hexagonal microsphere structures (Figure 2e,f). It demonstrated that the type of titanium source did not affect the morphology of the as-prepared sample.
Furthermore, in order to obtain TiO2, the as-prepared precursor (HTiOF3) was calcined at different temperatures. As illustrated in Figure 3a, when the precursor was calcinated at 100 °C for 2 h, the hexagonal smooth surfaces gradually disappeared. The reason for this phenomenon was that HTiOF3 decomposed during the calcination process to generate HF gas and the overflow of the gas caused the surface to be uneven [26,28]. When the calcination temperature was raised to 300 °C, the end face of the hexagonal prism disappeared and six edges became apparent. All the side faces of the hexagonal prism were not broken and kept their original state (as shown in Figure 3b). Figure 3c is the SEM image of the precursor after calcination at 600 °C for 2 h. The samples gradually grew into hexagonal box structures. However, it was found that some material still existed in hexagonal boxes. The hexagonal frame structure was not obtained until the annealing reached 600 °C for 7 h. As shown in Figure 3d, the compounds in the hexagonal boxes wholly disappeared and the frame structure of TiO2 could be seen. The side face of the sample still maintained the previous complete appearance.
The corresponding XRD patterns for each sample are shown in Figure 3e. When the calcination temperature and the calcination time were 100 °C and 2 h, respectively, the precursor was not completely converted into TiO2 due to insufficient calcination. Therefore, it could be seen that the diffraction peak of the 100 °C/2 h sample corresponded to HTiOF3. No impurity peaks of other phases were found in the diffraction peaks of the other three samples. The characteristic peaks at 2θ values of 25.28°, 36.95°, 37.8°, 38.58°, 48.05°, 53.89°, 55.96°, 62.69°, 68.76°, 70.31° and 75.03° could be assigned to the (101), (103), (004), (112), (200), (105), (211), (204), (116), (220) and (215) crystal planes of anatase TiO2 (JCPDS No. 21-1272) [29]. In addition, with the increase in calcination temperature and calcination time, the diffraction peaks of the samples became sharper and sharper, which indicated that the crystallization degree was getting higher. Thus, it could be concluded that the formation of the hexagonal frame structure was not only related to the calcination temperature but also to the calcination time.
The TG and DTG curves of precursor (HTiOF3) are shown in Figure 4. It can be seen that there were four processes in the transformation from the HTiOF3 to TiO2. The first stage below 280 °C was a slight weight loss, which was mainly caused by the deintercalation of physically adsorbed water on the surface of the sample and the disappearance of evaporation of other chemicals. In the second stage of 280–400 °C, HTiOF3 was decomposed and converted into TiOF2, and some of the generated HF escaped. The third stage was 400–450 °C, where the decomposition of some titanium-containing impurities continued [30]. The fourth stage was 450–700 °C, in which TiOF2 was completely converted into TiO2. The result was consistent with the description of the SEM in Figure 3a,d.
Based on the above experimental exploration and characterization analysis, the formation mechanism of the obtained TiO2 with hexagonal frame structure was discussed. This process could basically be divided into the following stages: (I) hydrolysis of tetrabutyl titanate, (II) formation of spherical morphology composed of hexagonal structures, (III) Ostwald ripening and (IV) formation of TiO2 with hexagonal frame structures. First, the hydrolysis reaction of tetrabutyl titanate occurred and the nanoparticles mainly composed of the titanate compound were formed under solvothermal conditions. Subsequently, the nanoparticles aggregated into spherical structures assembled from hexagonal prisms. Next, the hexagonal prisms underwent Ostwald ripening and recrystallization growth due to annealing at a high temperature. Finally, the end face disappeared and the TiO2 with a hexagonal frame structure was obtained. It is worth noting that the side faces of the hexagonal prism were not broken and retained the complete morphology. The specific formation process of the hexagonal frame structure TiO2 is shown in Figure 5. The reaction equations for this process were as follows:
Ti(OR)4 + 4R-OH→Ti(OH)4 + 4R-OR
Ti(OH)4 + 3HF→HTiOF3 + 3H2O
2HTiOF3→TiO2 + 2HF + TiF4
For the purpose of studying the light absorption properties of four samples, the UV-vis diffuse reflectance spectra of four samples were investigated separately. It could be seen that all samples had no absorption in the visible light region, which was mainly caused by the large band gap [31]. With the increase in calcination temperature and calcination time, the light absorption intensity of the 600 °C/7 h sample was the highest. Compared with anatase TiO2, HTiOF3 had a higher UV absorption intensity. In addition, Figure 6b shows a tauc plot, which was obtained using a Kubelka–Munk transformation to determine the band gaps of TiO2 and HTiOF3 [32]. The band gap of 600 °C/7 h was 3.22 eV, which was smaller than other samples. It was shown that the difference in the morphology of TiO2 also caused a slight change in the band gap. The band gap of 100 °C/2 h was 3.3 eV. Although the UV absorption intensity of TiO2 was not as high as that of HTiOF3, the narrow band gap of TiO2 showed that it had better utilization of UV-vis light [33].
Samples with different morphologies have different specific surface areas and pore structures, which will affect photocatalytic performance. The N2 adsorption and desorption isotherms and pore size distribution curves are shown in Figure 7a. The isotherms of the four samples were all type IV isotherms, indicating a mesoporous structure [34]. It was shown that the samples had a mesoporous structure and pore diameters between 2 and 50 nm. The calculated values of the BET surface area and pore volume are listed in Table 2. It can be seen that 600 °C/7 h had a larger specific surface area and pore volume than other samples, which was mainly caused by its hollow morphology. The higher specific surface area can reduce the diffusion resistance and provide more active sites to promote the photocatalytic reaction, thereby the adsorption capacity of the photocatalyst for pollutants is improved [35].
The generation of photoluminescence is mainly caused by the recombination of photogenerated carriers, and the photoluminescence spectrum is used to reflect the separation efficiency of electrons and holes of the catalysts [36,37]. In general, the generation of fluorescence is caused by electron–hole recombination. The higher the fluorescence intensity, the more serious the electron–hole recombination of the semiconductor and the weaker the photocatalytic performance. As shown in Figure 7b, with the increase in calcination temperature and time, the fluorescence intensity of the sample gradually weakened. At room temperature, 600 °C/7 h had the lowest fluorescence intensity. It was speculated that this unique hollow structure is beneficial to the transport and separation of photon carriers.
Transient photocurrent response and EIS Nyquist plots were provided to characterize the electrochemical performance of the as-prepared samples under different calcination conditions. It can be seen in Figure 8a that the prepared TiO2 with the hexagonal frame structure had a high transient photocurrent intensity. The sizes of the arc radii of the EIS Nyquist plots (Figure 8b) were 600 °C/7 h < 600 °C/2 h < 300 °C/2 h < 100 °C/2 h. The smaller the arc radius, the larger the charge transfer resistance and the charge transfer is also limited [38]. Therefore, it could be concluded from the two electrochemical test results that when the calcination condition was 600 °C/7 h, the hexagonal frame structure TiO2 had excellent charge separation performance, thereby improving the photocatalytic performance. This also corresponded to the PL test as mentioned above.
The photocatalytic activity of the prepared samples was evaluated using photocatalytic degradation of RhB under UV-vis light (Figure 9a). After 40 min of light irradiation, the degradation efficiency of 600 °C/7 h reached 99%, while the degradation efficiencies of 100 °C/2 h, 300 °C/2 h and 600 °C/2 h were 33%, 28% and 92%, respectively. The Langmuir–Hinshelwood model is often used to illustrate the kinetics of heterogeneous photocatalytic processes. The specific equation is as follows:
C = C0e−kt
−ln(C/C0) = kt
where C0 (mg/L) is represented as the concentration of RhB aqueous solution at irradiation time t = 0 min. C (mg/L) is represented as the concentration of the RhB aqueous solution at irradiation time t (min). k (min−1) is represented as the first-order rate constant [39]. The rate constant k was calculated through a plot of linear fit between −ln(C/C0) against irradiation time (Figure 9b). The linear graph showed that the degradation process of RhB by TiO2 was in good agreement with the Langmuir–Hinshelwood first-order kinetic equation. It can be seen that the photocatalytic degradation rate constant of 600 °C/7 h was 0.106 min−1, which was higher than 100 °C/2 h (0.011 min−1), 300 °C/2 h (0.008 min−1) and 600 °C/2 h (0.06 min−1). The hollow structure enabled it to have a larger specific surface area compared with other samples. There were more reactive sites on its surface [40]. The rate constant can be improved by increasing the number of active sites during photocatalytic degradation [41,42]. It also promoted the adsorption of RhB dye on hollow hexagonal frame TiO2. In addition, the excellent photocatalytic activity was also related to high crystallinity. Compared with other morphologies of TiO2 prepared in previous studies, the TiO2 with hollow hexagonal morphology had more excellent photocatalytic degradation activity (Table S1). The radical trapping experiment of catalysts was carried out (Figure 9c). Compared with no scavenger added, it was clearly found that the photocatalytic degradation rate of RhB was decreased after adding BQ or TA, proving that ·OH and ·O2− played a major role in the photocatalytic activity. The recyclability and stability evaluation of 600 °C/7 h is shown in Figure 9d, and it can be seen that the catalyst still maintained a good degradation efficiency after four cycles, indicating that the hollow hexagonal frame TiO2 has excellent potential for application in the field of wastewater treatment.
In order to study the effects of different dosages of catalyst on the degradation of the RhB solution, different amounts of 600 °C/7 h sample (0.05 g, 0.10 g, 0.15 g and 0.20 g) were added to 100 mL of RhB under basic conditions. It can be seen from Figure S1 that when the amount of catalyst increased from 0.10 g to 0.20 g, the degradation rate decreased from 98.6% to 86.3% and the rate constant also changed from 0.106 min−1 to 0.049 min−1. When the high dosage of catalyst was added, part of the catalyst surface could not perform photon absorption and dye adsorption due to the shielding effect [43]. The worst degradation effect was obtained when 0.05 g catalyst was added, mainly because the number of active sites was insufficient, and it was difficult to adsorb more dye. Therefore, it was considered to be the optimal condition when the dosage of the catalyst was 0.10 g.
To further verify the excellent photocatalytic performance of the as-prepared hexagonal frame TiO2, a series of experiments on photocatalytic hydrogen evolution were carried out. With methanol as the sacrificial agent and chloroplatinic acid added, [PtCl6]2− in the solution was reduced to elemental Pt by photoelectrons generated by photoexcitation of TiO2 conduction band under UV-vis light irradiation [44]. With Pt-decorated TiO2 as a co-catalyst for hydrogen evolution, the rate of hydrogen evolution could be improved effectively. As shown in Figure 10a, the hydrogen yield of 100 °C/1 h within 6 h was 0. With the increase in calcination temperature and calcination time, the photocatalytic activity of the sample gradually increased. It can be seen from Figure 10b that 600 °C/7 h had the highest hydrogen yield at 2508.12 μmol g−1 h−1, which was significantly higher than the hydrogen yields of 100 °C/2 h (0 μmol g−1 h−1), 300 °C/2 h (148.07 μmol g−1 h−1) and 600 °C/2 h (2012.03 μmol g−1 h−1). This was also due to the high crystallinity and large specific surface area of 600 °C/7 h. All these reasons improved the photocatalytic hydrogen evolution performance. Under the same conditions, 600 °C/7 h was tested for four cycles of hydrogen production, and the cycle was repeated every 6 h. As shown in Figure 10c, the hydrogen production capacity of the sample changed little after four cycles. This showed that 600 °C/7 h had good stability. The samples after the hydrogen evolution reaction were analyzed using XRD (Figure 10d) and the diffraction peaks basically did not change, which further demonstrated the stability of the sample.
The photocatalytic mechanism is presented in Figure 11. It can be seen that when TiO2 is irradiated by light, electrons (e−) in the valence band (VB) are excited to the conduction band (CB), thereby generating photoinduced holes (h+) in the valence band. The generated carriers migrate to the catalyst surface under the action of the electric field. These carriers can react with oxygen and water on the surface of TiO2 to generate ·O2− and ·OH, thus realizing the degradation of RhB dyes. In the photocatalytic hydrogen evolution reaction, the cocatalyst Pt can capture the e− in the CB. The h+ reacts with water in the solution to form H+, which is reduced to H2 by e−. On the one hand, the hydrogen evolution cocatalyst Pt captures e− and delays the recombination with h+. On the other hand, methanol as a sacrificial agent can react with h+ and inhibit the recombination of photogenerated carriers [45]. Both of these reasons can improve the photocatalytic H2 evolution performance of the catalyst.

4. Conclusions

In conclusion, a template-free method was used to synthesize hollow hexagonal frame TiO2. The first step was to synthesize the precursor (HTiOF3) under the hydrothermal method and then calcine it at a certain temperature and time to obtain TiO2. By changing the type of solvent, the influencing factors of the precursor morphology were explored, and it was further demonstrated that the spherical structure composed of hexagonal prisms was obtained with certain conditions. In addition, the transformation process from the precursor to TiO2 was also studied by changing the calcination temperature and time. The highest photocatalytic activity was found in the hollow hexagonal frame TiO2, which was due to the larger specific surface area of the hollow structure. Through the photocurrent, EIS and PL measurements analysis, it was confirmed that the hexagonal frame TiO2 had a lower recombination rate of photogenerated electrons and holes. The excellent photocatalytic performance of TiO2 could be more intuitively shown by photocatalytic degradation of RhB solution and photocatalytic hydrogen evolution experiments.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/nano12091409/s1, Figure S1: (a) Photocatalytic degradation of RhB under UV light with different amounts of catalyst; (b) Linear fit between −ln (C/C0) and time of different amounts of catalyst, Table S1: Comparison of photocatalytic degradation of organic dyes catalyzed by TiO2 catalysts. References [46,47,48,49,50,51] are cited in the supplementary materials.

Author Contributions

Investigation, M.T. and H.L.; methodology, M.T., B.L. and H.L.; software, M.T. and B.L.; data curation, M.T. and X.Z.; formal analysis, M.T., X.Z. and H.L.; writing—original draft, M.T. and W.Z.; visualization, M.T., B.L. and H.L.; writing—review and editing, M.T., W.Z. and H.L.; conceptualization, H.L. and W.Z.; resources, H.L.; supervision, H.L.; project administration, H.L. and W.Z.; funding acquisition, H.L. and W.Z. All authors read and agreed to the published version of the manuscript.

Funding

This work was financially supported by the Natural Science Foundation of Shandong Province (ZR2020ME043), the National Natural Science Foundation of China (21871078, 52172206) and the Development Plan of Youth Innovation Team in Colleges and Universities of Shandong Province.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data supporting this study are available within the article.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Liu, Z.Y.; Zhang, X.T.; Nishimoto, S.; Murakami, T.; Fujishima, A. Efficient photocatalytic degradation of gaseous acetaldehyde by highly ordered TiO2 nanotube arrays. Environ. Sci. Technol. 2008, 42, 8547–8551. [Google Scholar] [CrossRef] [PubMed]
  2. Xiong, Z.G.; Dou, H.Q.; Pan, J.H.; Ma, J.Z.; Xu, C.; Zhao, X.S. Synthesis of mesoporous anatase TiO2 with a combined template method and photocatalysis. Crystengcomm 2010, 12, 3455–3457. [Google Scholar] [CrossRef]
  3. Hu, X.; Hu, X.J.; Peng, Q.Q.; Zhou, L.; Tan, X.F.; Jiang, L.H.; Tang, C.F.; Wang, H.; Liu, S.H.; Wang, Y.Q.; et al. Mechanisms underlying the photocatalytic degradation pathway of ciprofloxacin with heterogeneous TiO2. Chem. Eng. J. 2020, 380, 122366. [Google Scholar] [CrossRef]
  4. Wang, T.; Shen, D.Y.; Xu, T.; Jiang, R.L. Photocatalytic degradation properties of V-doped TiO2 to automobile exhaust. Sci. Total Environ. 2017, 586, 347–354. [Google Scholar] [CrossRef] [PubMed]
  5. Weng, Z.Y.; Guo, H.; Liu, X.M.; Wu, S.L.; Yeung, K.W.K.; Chu, P.K. Nanostructured TiO2 for energy conversion and storage. Rsc Adv. 2013, 3, 24758–24775. [Google Scholar] [CrossRef]
  6. Rawool, S.A.; Yadav, K.K.; Polshettiwar, V. Defective TiO2 for photocatalytic CO2 conversion to fuels and chemicals. Chem. Sci. 2021, 12, 4267–4299. [Google Scholar] [CrossRef]
  7. Jeon, J.P.; Kweon, D.H.; Jang, B.J.; Ju, M.J.; Baek, J.B. Enhancing the photocatalytic activity of TiO2 catalysts. Adv. Sustain. Syst. 2020, 4, 2000197. [Google Scholar] [CrossRef]
  8. Fang, W.Q.; Zhou, J.Z.; Liu, J.; Chen, Z.G.; Yang, C.; Sun, C.H.; Qian, G.R.; Zhou, J.; Qiao, S.Z.; Yang, H.G. Hierarchical structures of single-crystalline anatase TiO2 nanosheets dominated by (001) facets. Chem. Eur. J. 2011, 17, 1423–1427. [Google Scholar] [CrossRef] [Green Version]
  9. Yin, H.Y.; Wang, X.L.; Wang, L.; QLin, N.; Zhao, H.T. Self-doped TiO2 hierarchical hollow spheres with enhanced visible-light photocatalytic activity. J. Alloy. Compd. 2015, 640, 68–74. [Google Scholar] [CrossRef]
  10. Docampo, P.; Guldin, S.; Stefik, M.; Tiwana, P.; Orilall, M.C.; Hüttner, S.; Sai, H.; Wiesner, U.; Steiner, U.; Snaith, H.J. Control of solid-state dye-sensitized solar cell performance by block-copolymer-directed TiO2 synthesis. Adv. Funct. Mater. 2010, 20, 1787–1796. [Google Scholar] [CrossRef] [Green Version]
  11. Feng, Y.C.; Li, L.; Ge, M.; Guo, C.S.; Wang, J.F.; Liu, L. Improved catalytic capability of mesoporous TiO2 microspheres and photodecomposition of toluene. Acs Appl. Mater. Interfaces 2010, 2, 3134–3140. [Google Scholar] [CrossRef] [PubMed]
  12. Valero-Romero, M.J.; Santaclara, J.G.; Oar-Arteta, L.; Koppen, L.; Osadchii, D.Y.; Gascon, J.; Kapteijn, F. Photocatalytic properties of TiO2 and Fe-doped TiO2 prepared by metal organic framework-mediated synthesis. Chem. Eng. J. 2019, 36, 75–88. [Google Scholar] [CrossRef]
  13. Sofianou, M.V.; Psycharis, V.; Boukos, N.; Vaimakis, T.; Yu, J.G.; Dillert, R.; Bahnemann, D.; Trapalis, C. Tuning the photocatalytic selectivity of TiO2 anatase nanoplates by altering the exposed crystal facets content. Appl. Catal. B Environ. 2013, 142–143, 761–768. [Google Scholar] [CrossRef]
  14. Barbé, C.J.; Arendse, F.; Comte, P.; Jirousek, M.; Lenzmann, F.; Shklover, V.; Grätzel, M. Nanocrystalline titanium oxide electrodes for photovoltaic applications. J. Am. Ceram. Soc. 2010, 80, 3157–3171. [Google Scholar] [CrossRef]
  15. Nian, J.N.; Teng, H. Hydrothermal synthesis of single-crystalline anatase TiO2 nanorods with nanotubes as the precursor. J. Phys. Chem. B 2006, 110, 4193–4198. [Google Scholar] [CrossRef]
  16. Liu, M.; Piao, L.Y.; Lu, W.M.; Ju, S.T.; Zhao, L.; Zhou, C.L.; Li, H.L.; Wang, W.J. Flower-like TiO2 nanostructures with exposed {001} facets: Facile synthesis and enhanced photocatalysis. Nanoscale 2010, 2, 1115–1117. [Google Scholar] [CrossRef]
  17. Nguyen, N.T.; Yoo, J.E.; Altomare, M.; Schmuki, P. Suspended Pt nanoparticles over TiO2 nanotubes for enhanced photocatalytic H2 evolution. Chem. Commun. 2016, 50, 9653. [Google Scholar] [CrossRef] [Green Version]
  18. Réti, B.; Kiss, G.I.; Gyulavári, T.; Baan, K.; Magyari, K.; Hernadi, K. Carbon sphere templates for TiO2 hollow structures: Preparation, characterization and photocatalytic activity. Catal. Today 2017, 284, 160–168. [Google Scholar] [CrossRef] [Green Version]
  19. Kartini, I.; Meredith, P.; Zhao, X.S.; Costa, J.C.; Lu, G.Q. A two-step sol-gel method for synthesis of nanoporous TiO2. J. Nanosci. Nanotechnol. 2004, 4, 270. [Google Scholar] [CrossRef]
  20. Gong, X.Q.; Selloni, A. Reactivity of anatase TiO2 nanoparticles: The role of the minority (001) surface. J. Phys. Chem. B 2005, 109, 19560–19562. [Google Scholar] [CrossRef]
  21. Selloni, A. Crystal growth: Anatase shows its reactive side. Nat. Mater. 2008, 7, 613–615. [Google Scholar] [CrossRef] [PubMed]
  22. Pan, J.H.; Zhang, X.W.; Du, A.J.; Sun, D.D.; Leckie, J.O. Self-etching reconstruction of hierarchically mesoporous F-TiO2 hollow microspherical photocatalyst for concurrent membrane water purifications. J. Am. Chem. Soc. 2008, 130, 11256–11257. [Google Scholar] [CrossRef] [PubMed]
  23. Wang, H.Q.; Wu, Z.B.; Liu, Y. A Simple Two-Step Template Approach for Preparing Carbon-Doped Mesoporous TiO2 Hollow Microspheres. J. Phys. Chem. C 2009, 113, 13317–13324. [Google Scholar] [CrossRef]
  24. Cao, Q.; Li, Q.Q.; Pi, Z.C.; Zhang, J.; Sun, L.W.; Xu, J.Z.; Cao, Y.Y.; Cheng, J.Y.; Bian, Y. Metal–organic-framework-derived ball-flower-like porous Co3O4/Fe2O3 heterostructure with enhanced visible-light-driven photocatalytic activity. Nanomaterials 2022, 12, 904. [Google Scholar] [CrossRef]
  25. Xia, X.H.; Peng, S.; Bao, Y.W.; Wang, Y.; Lei, B.L.; Wang, Z.; Huang, Z.B.; Gao, Y. Control of interface between anatase TiO2 nanoparticles and rutile TiO2 nanorods for efficient photocatalytic H2 generation. J. Power Sources 2018, 376, 11–17. [Google Scholar] [CrossRef]
  26. Liu, P.; Wang, Y.; Zhang, H.M.; An, T.C.; Yang, H.G.; Tang, Z.Y.; Cai, W.P.; Zhao, H.J. Vapor-phase hydrothermal transformation of HTiOF3 intermediates into {001} faceted anatase single-crystalline nanosheets. Small 2012, 8, 3664–3673. [Google Scholar] [CrossRef]
  27. Bao, Y.P.; Lim, T.T.; Zhong, Z.Y.; Wang, R.; Hu, X. Acetic acid-assisted fabrication of hierarchical flower-like Bi2O3 for photocatalytic degradation of sulfamethoxazole and rhodamine B under solar irradiation. J. Colloid Interf. Sci. 2017, 505, 489–499. [Google Scholar] [CrossRef]
  28. Wu, T.X.; Wang, G.Z.; Zhu, X.G.; Liu, P.; Zhang, X.; Zhang, H.M.; Zhang, Y.X.; Zhao, H.J. Growth and in situ transformation of TiO2 and HTiOF3 crystals on chitosan-polyvinyl alcohol co-polymer substrates under vapor phase hydrothermal conditions. Nano Res. 2016, 9, 745–754. [Google Scholar] [CrossRef]
  29. Chen, M.; Ma, J.Z.; Zhang, B.; Wang, F.; Li, Y.B.; Zhang, C.B.; He, H. Facet-dependent performance of anatase TiO2 for photocatalytic oxidation of gaseous ammonia. Appl. Catal. B Environ. 2018, 223, 209–215. [Google Scholar] [CrossRef]
  30. Zheng, Y.; Hu, X.; Yang, P. Phase and morphology transformation from assembled hexagonal HTiOF3 prisms to {001} faceted TiO2 nanosheets. Crystengcomm 2018, 20, 4485–4491. [Google Scholar] [CrossRef]
  31. Hou, C.T.; Liu, H.Y.; Bakhtair, M.F. Preparation of Ag SPR-promoted TiO2-{001}/HTiOF3 photocatalyst with oxygen vacancies for highly efficient degradation of tetracycline hydrochloride. Mat. Sci. Semicon. Proc. 2021, 136, 106142. [Google Scholar] [CrossRef]
  32. Liu, Y.J.; Liu, H.X.; Zhou, H.M.; Li, T.D.; Zhang, L.N. A Z-scheme mechanism of N-ZnO/g-C3N4 for enhanced H2 evolution and photocatalytic degradation. Appl. Surf. Sci. 2019, 466, 133–140. [Google Scholar] [CrossRef]
  33. Shen, J.; Wang, R.; Liu, Q.Q.; Yang, X.F.; Tang, H.; Yang, J. Accelerating photocatalytic hydrogen evolution and pollutant degradation by coupling organic co-catalysts with TiO2. Chin. J. Catal. 2019, 40, 380–389. [Google Scholar] [CrossRef]
  34. Kaur, M.; Kaur, M.; Singh, D.; Oliveira, A.C.; Garg, V.K.; Sharma, V.K. Synthesis of CaFe2O4-NGO nanocomposite for effective removal of heavy metal ion and photocatalytic degradation of organic pollutants. Nanomaterials 2021, 11, 1471. [Google Scholar] [CrossRef]
  35. Wang, J.L.; Wang, X.Q.; Chen, Q.H.; Xu, H.L.; Dai, M.; Zhang, M.; Wang, W.Y.; Song, H. Microstructural modification of hollow TiO2 nanospheres and their photocatalytic performance. Appl. Surf. Sci. 2021, 535, 1484–1495. [Google Scholar] [CrossRef]
  36. Yu, J.C.; Yu, J.G.; Ho, W.; Jiang, Z.T.; Zhang, L.Z. Effects of F- doping on the photocatalytic activity and microstructures of nanocrystalline TiO2 powders. Chem. Mater. 2002, 14, 3808–3816. [Google Scholar] [CrossRef]
  37. Yu, J.G.; Zhao, X.J. Effect of surface treatment on the photocatalytic activity and hydrophilic property of the sol-gel derived TiO2 thin films. Mater. Res. Bull. 2001, 36, 97–107. [Google Scholar] [CrossRef]
  38. Pan, L.; Wang, S.B.; Xie, J.W.; Wang, L.; Zhang, X.W.; Zou, J.J. Constructing TiO2 p-n homojunction for photoelectrochemical and photocatalytic hydrogen generation. Nano Energy 2016, 28, 296–303. [Google Scholar] [CrossRef]
  39. Inbaraj, B.S.; Chen, B.Y.; Liao, C.W.; Chen, B.H. Green synthesis, characterization and evaluation of catalytic and antibacterial activities of chitosan, glycol chitosan and poly(γ-glutamic acid) capped gold nanoparticles. Int. J. Biol. Macromol. 2020, 161, 1484–1495. [Google Scholar] [CrossRef]
  40. Bai, S.; Liu, X.; Li, D.Q.; Chen, S.; Luo, R.X.; Chen, A.F. Synthesis of ZnO nanorods and its application in NO2 sensors. Sens. Actuat. B Chem. 2011, 153, 110–116. [Google Scholar] [CrossRef]
  41. Naeimi, A.; Sharifi, A.; Montazerghaem, L.; Abhari, A.R.; Mahmoodi, Z.; Bakr, Z.H.; Soldatov, A.V.; Ali, G.A.M. Transition metals doped WO3 photocatalyst towards high efficiency decolourization of azo dye. J. Mol. Struct. 2022, 1250, 131800. [Google Scholar] [CrossRef]
  42. Ethiraj, A.S.; Uttam, P.; Varunkumar, K.; Chong, K.F.; Ali, G.A.M. Photocatalytic performance of a novel semiconductor nanocatalyst: Copper doped nickel oxide for phenol degradation. Mater. Chem. Phys. 2020, 242, 122520. [Google Scholar] [CrossRef]
  43. Zyoud, A.; Zu’bi, A.; Helal, M.H.S.; Park, D.; Campet, G.; Hilal, H.S. Optimizing photo-mineralization of aqueous methyl orange by nano-ZnO catalyst under simulated natural conditions. J. Environ. Health Sci. Eng. 2015, 13, 46. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  44. Liu, M.J.; Xia, P.F.; Zhang, L.Y.; Cheng, B.; Yu, J.G. Enhanced photocatalytic H2-production activity of g-C3N4 nanosheets via optimal photodeposition of Pt as cocatalyst. Acs Sustain. Chem. Eng. 2018, 6, 10472–10480. [Google Scholar] [CrossRef]
  45. Yang, X.Y.; Liu, H.X.; Li, T.D.; Huang, B.B.; Hu, W.; Jiang, Z.Y.; Chen, J.B.; Niu, Q.F. Preparation of flower-like ZnO@ZnS core-shell structure enhances photocatalytic hydrogen production. Int. J. Hydrogen Energy 2020, 45, 26967–26978. [Google Scholar] [CrossRef]
  46. Ruqaishy, M.A.; Marzouqi, F.A.; Qi, K.Z.; Liu, S.Y.; Karthikeyan, S.; Kim, Y.; Al-Kindy, S.M.Z.; Kuvarega, A.T.; Selvaraj, R. Template-free preparation of TiO2 microspheres for the photocatalytic degradation of organic dyes. Korean J. Chem. Eng. 2018, 35, 2283–2289. [Google Scholar] [CrossRef]
  47. Wang, T.; Gao, Y.; Tang, T.; Bian, H.Q.; Zhang, Z.M.; Xu, J.H.; Xiao, H.; Chu, X. Preparation of ordered TiO2 nanofibers/nanotubes by magnetic field assisted electrospinning and the study of their photocatalytic properties. Ceram. Int. 2019, 45, 14404–14410. [Google Scholar] [CrossRef]
  48. Xu, X.J.; Fang, X.S.; Zhai, T.Y.; Zeng, H.B.; Liu, B.D.; Hu, X.Y.; Bando, Y.; Golberg, D. Tube-in-Tube TiO2 nanotubes with porous walls: Fabrication, formation mechanism, and photocatalytic properties. Small 2011, 7, 445–449. [Google Scholar] [CrossRef]
  49. Kanjana, N.; Maiaugree, W.; Poolcharuansin, P.; Laokul, P. Size controllable synthesis and photocatalytic performance of mesoporous TiO2 hollow spheres. J. Mater. Sci. Technol. 2020, 48, 105–113. [Google Scholar] [CrossRef]
  50. Du, Y.B.; Xu, X.Y.; Lin, L.; Ge, M.Y.; He, D.N. 3D hierarchical flower-like rutile TiO2 nanospheres-based versatile photocatalyst. J. Mater. Sci. 2018, 53, 385–395. [Google Scholar] [CrossRef]
  51. Chen, K.M.; Jiang, Z.; Qin, J.L.; Jiang, Y.; Li, R.; Tang, H.; Yang, X.F. Synthesis and improved photocatalytic activity of ultrathin TiO2 nanosheets with nearly 100% exposed (001) facets. Ceram. Int. 2014, 40, 16817–16823. [Google Scholar] [CrossRef]
Nanomaterials 12 01409 g001 550
Figure 1. (a) XRD patterns; (b,c) SEM micrographs of TiO2 precursor; (d–g) EDS images of TiO2 precursor: Ti (blue), O (yellow) and F (green).
Figure 1. (a) XRD patterns; (b,c) SEM micrographs of TiO2 precursor; (d–g) EDS images of TiO2 precursor: Ti (blue), O (yellow) and F (green).
Nanomaterials 12 01409 g001
Nanomaterials 12 01409 g002 550
Figure 2. SEM image of samples prepared under different reaction conditions: (a,b) S2; (c,d) S3; (e,f) S5.
Figure 2. SEM image of samples prepared under different reaction conditions: (a,b) S2; (c,d) S3; (e,f) S5.
Nanomaterials 12 01409 g002
Nanomaterials 12 01409 g003 550
Figure 3. SEM images of TiO2 synthesized with different calcined temperatures: (a) 100 °C/2 h; (b) 300 °C/2 h; (c) 600 °C/2 h; (d) 600 °C/7 h. (e) XRD patterns of TiO2 synthesized with different calcined conditions. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 3. SEM images of TiO2 synthesized with different calcined temperatures: (a) 100 °C/2 h; (b) 300 °C/2 h; (c) 600 °C/2 h; (d) 600 °C/7 h. (e) XRD patterns of TiO2 synthesized with different calcined conditions. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g003
Nanomaterials 12 01409 g004 550
Figure 4. The TG and DTG curves of the TiO2 precursor (HTiOF3).
Figure 4. The TG and DTG curves of the TiO2 precursor (HTiOF3).
Nanomaterials 12 01409 g004
Nanomaterials 12 01409 g005 550
Figure 5. The schematic diagram of TiO2 with a hexagonal frame structure. Note: 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 5. The schematic diagram of TiO2 with a hexagonal frame structure. Note: 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g005
Nanomaterials 12 01409 g006 550
Figure 6. (a) UV-vis absorption spectra of four samples and (b) tauc plot. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 6. (a) UV-vis absorption spectra of four samples and (b) tauc plot. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g006
Nanomaterials 12 01409 g007 550
Figure 7. (a) N2 adsorption and desorption isotherms and pore size distribution curves (inset) of all samples and (b) PL spectra for four samples at room temperature. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 7. (a) N2 adsorption and desorption isotherms and pore size distribution curves (inset) of all samples and (b) PL spectra for four samples at room temperature. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g007
Nanomaterials 12 01409 g008 550
Figure 8. (a) Transient photocurrent response tests of all samples and (b) EIS Nyquist plots of all samples. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 8. (a) Transient photocurrent response tests of all samples and (b) EIS Nyquist plots of all samples. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g008
Nanomaterials 12 01409 g009 550
Figure 9. (a) Photocatalytic degradation of RhB using four samples under UV-vis light, (b) linear fit between −ln (C/C0) and time among four samples, (c) trapping experiments of active species and (d) cyclic degradation curve of TiO2 with annealing 600 °C for 7 h. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 9. (a) Photocatalytic degradation of RhB using four samples under UV-vis light, (b) linear fit between −ln (C/C0) and time among four samples, (c) trapping experiments of active species and (d) cyclic degradation curve of TiO2 with annealing 600 °C for 7 h. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g009
Nanomaterials 12 01409 g010 550
Figure 10. (a) Photocatalytic H2 yield, (b) H2 evolution rate, (c) cycling test of photocatalytic H2 generation of TiO2 with annealing at 600 °C for 7 h and (d) XRD patterns of original and recycling samples of recycling samples. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Figure 10. (a) Photocatalytic H2 yield, (b) H2 evolution rate, (c) cycling test of photocatalytic H2 generation of TiO2 with annealing at 600 °C for 7 h and (d) XRD patterns of original and recycling samples of recycling samples. Note: 100 °C/2 h, the precursor calcined at 100 °C for 2 h; 300 °C/2 h, the precursor calcined at 300 °C for 2 h; 600 °C/2 h, the precursor calcined 600 °C for 2 h; 600 °C/7 h, the precursor calcined 600 °C for 7 h.
Nanomaterials 12 01409 g010
Nanomaterials 12 01409 g011 550
Figure 11. Photocatalytic mechanism of hexagonal frame TiO2 (e− represents an electron; h+ represents a hole).
Figure 11. Photocatalytic mechanism of hexagonal frame TiO2 (e− represents an electron; h+ represents a hole).
Nanomaterials 12 01409 g011
Table
Table 1. The composition of the solvent under different reaction conditions.
Table 1. The composition of the solvent under different reaction conditions.
Sample
Number		TBT (mol)Titanium Tetraisopropanolate (mol)HAc
(mL)		Isopropanol (mL)HF
(mL)
S10.1028211.6
S20.100211.6
S30.102801.6
S40.1028210
S500.0128211.6
Table
Table 2. BET surface area and pore volume of all samples.
Table 2. BET surface area and pore volume of all samples.
SampleBET Surface Area (m2/g)Pore Volume (cm3/g)
100 °C/2 h 123.20.152
300 °C/2 h 241.60.221
600 °C/2 h 348.70.253
600 °C/7 h 451.90.571
1 The precursor calcined at 100 °C for 2 h. 2 The precursor calcined at 300 °C for 2 h. 3 The precursor calcined at 600 °C for 2 h. 4 The precursor calcined at 600 °C for 7 h.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Teng, M.; Liu, H.; Lin, B.; Zhou, X.; Zhou, W. Preparation and Photocatalytic Properties of Anatase TiO2 with Hollow Hexagonal Frame Structure. Nanomaterials 2022, 12, 1409. https://doi.org/10.3390/nano12091409

AMA Style

Teng M, Liu H, Lin B, Zhou X, Zhou W. Preparation and Photocatalytic Properties of Anatase TiO2 with Hollow Hexagonal Frame Structure. Nanomaterials. 2022; 12(9):1409. https://doi.org/10.3390/nano12091409

Chicago/Turabian Style

Teng, Mengyuan, Haixia Liu, Bensheng Lin, Xiangzhu Zhou, and Wei Zhou. 2022. "Preparation and Photocatalytic Properties of Anatase TiO2 with Hollow Hexagonal Frame Structure" Nanomaterials 12, no. 9: 1409. https://doi.org/10.3390/nano12091409

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.