Next Article in Journal
Editorial for the Special Issue “Nanoscale Ferroic Materials—Ferroelectric, Piezoelectric, Magnetic, and Multiferroic Materials”
Next Article in Special Issue
Radical-Scavenging Activatable and Robust Polymeric Binder Based on Poly(acrylic acid) Cross-Linked with Tannic Acid for Silicon Anode of Lithium Storage System
Previous Article in Journal
Mechanochemical Synthesis of Nickel Mono- and Diselenide: Characterization and Electrical and Optical Properties
Previous Article in Special Issue
Synergetic Effect of Li-Ion Concentration and Triple Doping on Ionic Conductivity of Li7La3Zr2O12 Solid Electrolyte
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 17
10.3390/nano12172950
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Tackling Structural Complexity in Li2S-P2S5 Solid-State Electrolytes Using Machine Learning Potentials

by
Carsten G. Staacke
1,†,
Tabea Huss
1,†,
Johannes T. Margraf
1,
Karsten Reuter
1 and
Christoph Scheurer
1,2,*
1
Fritz-Haber-Institut der Max-Planck-Gesellschaft, Faradayweg 4-6, 14195 Berlin, Germany
2
Forschungszentrum Jülich GmbH, Institute of Energy and Climate Research, Fundamental Electrochemistry (IEK-9), Wilhelm-Johnen-Straße, 52428 Jülich, Germany
*
Author to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Nanomaterials 2022, 12(17), 2950; https://doi.org/10.3390/nano12172950
Submission received: 12 July 2022 / Revised: 17 August 2022 / Accepted: 18 August 2022 / Published: 26 August 2022
(This article belongs to the Special Issue Nanomaterials for Lithium‐Ion Batteries)
Browse Figures
Review Reports Versions Notes

Abstract

:
The lithium thiophosphate (LPS) material class provides promising candidates for solid-state electrolytes (SSEs) in lithium ion batteries due to high lithium ion conductivities, non-critical elements, and low material cost. LPS materials are characterized by complex thiophosphate microchemistry and structural disorder influencing the material performance. To overcome the length and time scale restrictions of ab initio calculations to industrially applicable LPS materials, we develop a near-universal machine-learning interatomic potential for the LPS material class. The trained Gaussian Approximation Potential (GAP) can likewise describe crystal and glassy materials and different P-S connectivities P m S n . We apply the GAP surrogate model to probe lithium ion conductivity and the influence of thiophosphate subunits on the latter. The materials studied are crystals (modifications of Li 3 PS 4 and Li 7 P 3 S 11 ), and glasses of the xLi 2 S–(100 – x)P 2 S 5 type (x = 67, 70 and 75). The obtained material properties are well aligned with experimental findings and we underscore the role of anion dynamics on lithium ion conductivity in glassy LPS. The GAP surrogate approach allows for a variety of extensions and transferability to other SSEs.

1. Introduction

While lithium-ion batteries with liquid electrolytes entered the market in 1991, all-solid-state lithium-ion batteries (ASS-LIBs), although investigated for decades, are still not widely in use [1,2,3,4,5,6]. ASS-LIBs promise several advantages in comparison to liquid electrolyte batteries: higher power density, minimized safety and fire hazards, longer cycle lifetimes, more comprehensive temperature ranges, and enhanced energy density by potential usage of Li metal anodes [1,7,8]. Solid electrolytes of the Li 2 S-P 2 S 5 material class have gained substantial attention due to their favorable properties [6,9]. First, they possess high conductivities of up to 10 − 2 Scm − 1 , which ranks them among the most conductive solid electrolytes such as Li 10 GeP 2 S 12 or Li 1.3 Al 0.3 Ti 1.7 (PO 4 ) 3 [10,11]. Secondly, they are composed of the earth-abundant elements sulfur and phosphorous enabling sustainable applications at large scales.
However, this material class’s potential is hampered by the poor understanding of the relevant structure-property relations. This manifests itself in huge deviations in Li-ion conductivity between theory and experiment. As such, β -Li 3 PS 4 serves as an illustrating example. Experimental studies report a lithium ion conductivity of approximately 10 − 7 Scm − 1 , making the material unsuitable for industrial battery applications [12]. In contrast, an ab initio study predicts a conductivity of 10 − 1 Scm − 1 ; a six orders of magnitude deviation from experiment that would make the material the new record holder in solid-state lithium ion conduction [13]. Such huge discrepancies often arise from computational limitations that constrain tractable system sizes and sampling times. In the LPS case, high-resolution TEM images for instance revealed the presence of crystalline nanoparticles in otherwise amorphous regions, highlighting that conductivity calculations of ideal crystals are too short-sighted for this materials class [14]. The problem is further accentuated by the complex chemical structure of LPS [15,16]. A large structural variability at the molecular level, more precisely different thiophosphate poly-anions, are found in all crystalline and amorphous materials [6,17]. For a detailed description of the lithium ion conductivity in LPS we thus need to tackle these challenges: structural complexity of LPS glass compounds, chemical reactivity of thiophosphates, and the influence of anion composition on the lithium ion conductivity.
Here we tackle these challenges by replacing the computationally demanding direct first-principles calculations with a surrogate machine-learning (ML) model. Once trained, this Gaussian Approximation Potential (GAP) model allows for an upscaling of both time and length scale: molecular dynamics (MD) simulations covering up to several nanoseconds and system sizes of several thousand atoms become feasible. Furthermore, the flexibility offered by the ML approach allows one to implement a GAP model that is more versatile and can better represent the crucial complex chemistry than a classical force field [18]. We present a data-efficient iterative training approach to extend an earlier ML force field to yield a near-universal description of the LPS material class [19,20].
In the first part of this work we present our data-efficient training protocol and evaluate the GAP model on (a) its predictive accuracy for lithium ion conductivity and (b) its ability to reproduce two known phase transitions in crystalline Li 3 PS 4 . The second part focuses on the influence of anion composition on the lithium ion conductivity of different LPS glass compounds.

2. Methods

Computational Details

Reference density-functional theory (DFT) calculations are performed with the PBE functional, default ’light’ integration grids and a ’tier 1’ basis set of numerical atomic orbitals, as implemented in FHI-aims [21,22]. The Brillouin zone is sampled with a 1 × 1 × 1 k-grid. Initial training configurations are generated with ab initio molecular dynamics (MD) using the Γ -point approximation for the k-grid. GAP-based MD and Nudged-Elastic-Band (NEB) simulations are performed using the LAMMPS [23] code and the corresponding interface to QUIP [24,25]. For training set construction and data analysis, the atomic simulation environment ASE, SciPy and scikit-learn are used [26,27,28].

3. Results

3.1. Lithium Ion Mobility

We obtain the reactive GAP model used to describe the LPS class by fitting to DFT training data computed with the FHI-aims full-potential package [22]. The underlying approach is based on three consecutive steps: defining the anion lattice, sampling of Li-sites, and fine-tuning the materials density. In the first place, only the dominant anion species (e.g., PS 4 3 − and P 2 S 7 4 − ) are taken into consideration and utilized in a ratio that represents the desired stoichiometry correctly. For a data-efficient sampling of lithium sites, we sample Li-ion distributions on stable and meta-stable Li sites in a quasi-Monte Carlo like fashion. The materials density is obtained by an iterative compression scheme. Convergence, a detailed step-by-step description of the underlying algorithm, and numerical error assessments of the training procedure are given in Sections A–C in the Supplementary Materials. The benefit of this approach is that it allows the free tuning of stoichiometries and polyanion ratios. In contrast to previous work on crystalline Li 7 P 3 S 11 we use a purely short-ranged GAP. In Ref. [19] we combined a GAP model with an electrostatic baseline in order to study the role of long-range electrostatics in machine-learned interatomic potentials for complex battery materials. We previously showed that neglecting long-range electrostatics is unproblematic for describing lithium ion transport in isotropic bulk-like systems [19].
As a first validation of our GAP model, we turn to the Li-ion conductivity of crystalline LPS materials ( α , β , γ Li 3 PS 4 and Li 7 P 3 S 11 ) at finite temperature, predicted from MD simulations via the Nernst-Einstein equation (see section F in the Supplementary Materials for details). Using the GAP model we evaluate the ionic conductivity from the mean-square-displacement (MSD) sampled during 2 ns MD simulations for every crystalline compound at various temperatures between 400 and 800 K. Room temperature (RT) conductivities are extrapolated from a linear fit. Note that for crystalline Li 7 P 3 S 11 we required longer simulation times of up to 13 ns to reach converged conductivities, i.e., time scales that would essentially be prohibitive for direct ab initio MD. While Li-ion conductivity in LPS is usually dominated by diffusion of defects (Li + vacancies), Li 7 P 3 S 11 exhibits a more collective Li + motion yielding the observed high conductivity [19,29,30]. As seen in Figure 1, a broad range of Li-ion conductivities are exhibited in LPS.
While high RT conductivities of up to 3.6 × 10 − 3 Scm − 1 are found for α -Li 3 PS 4 and Li 7 P 3 S 11 , β and γ -Li 3 PS 4 exhibit poor RT conductivities of 10 − 5 to 10 − 7 Scm − 1 . These crystalline RT conductivities are in good agreement with experimental literature, although the extrapolated RT conductivity of β -Li 3 PS 4 is somewhat overestimated [30]. For ensemble averaging, we generated 20 structurally uncorrelated glass geometries for each specific temperature and stoichiometry. Hence, each data point in Figure 1 is an average over 20 MD calculations [31]. We consider three different stoichiometries in the analysis that cover the range from fully tetrahedral (Li 3 PS 4 ) via mixed (Li 7 P 3 S 11 ) to fully bridged tetrahedral (Li 4 P 2 S 7 ) thiophosphate moieties. These three dominant anion subunits are depicted below. As apparent from Figure 1, the ion conductivity over the whole temperature range and the extrapolated RT conductivities increase with growing Li 2 S content of the glass material, almost tripling conductivity from Li 4 P 2 S 7 (Li 2 S = 67 mol%) to Li 3 PS 4 (Li 2 S = 75 mol%). Hence, for an increasing Li 2 S content an increase RT conductivity is observed. These findings are again in good agreement with experimental studies.

3.2. Li 3 PS 4 Phase Transition

As a final validation step, we test the GAP’s predictive power on the known phase transitions in Li 3 PS 4 . As we show in Figure S8 in the Supplementary Materials, the Arrhenius curves of β and γ -Li 3 PS 4 exhibit a change of slope at roughly 700 K. Above 700 K, conductivities of β and γ -Li 3 PS 4 even match those of α -Li 3 PS 4 . This change of slope is caused by the phase transition to α -Li 3 PS 4 , involving a rotation of 25 % of the PS 4 3 − tetrahedra by 180 ∘ for both structures [18].
We can probe the phase transition quantitatively by studying the radial distribution functions (RDFs) of the sulfur sublattice as a function of simulation temperature (Figure 2). The β - and γ -phase share a HCP (hexagonal close-packed) sulfur sublattice, which is transformed to a BCC (body centered cubic) lattice in the α -phase [18]. For both sublattices, the S-S RDF displays a distinct peak at 3.4 Å, attributed to the intramolecular S-S distance. In the HCP sublattice, a second distinct peak at 4.3 Å is observed. The latter is missing in the BCC structure. Both β - and γ -phase show the characteristic double-peak in the low-temperature RDF, while the second peak vanishes for temperatures above 650 K. This same phase transition has also been observed in experimental studies and ab initio simulations [32,33]. Conceptually, these three phases can be distinguished by their different arrangement of PS 4 3 − . These are either all pointing in the same direction ( γ ), are arranged in a zig-zag fashion in one ( α ) or two directions ( β ) in space. A visualization can be found in Figure S6 in the Supplementary Materials [32]. The here obtained temperature between 600 and 700 K for the phase transition again matches fairly well with the experimentally reported 746 K [33].

3.3. The Role of Anion Composition in Li 2 S-P 2 S 5 Glasses

Concluding that we can correctly describe the lithium ion dynamics and structural changes in crystalline Li 3 PS 4 we now turn to the influence of anion composition on the lithium ion conductivity in LPS glasses. As shown above, the RT conductivity generally increases with Li 2 S content of the glass material. The increasing Li-ion conductivity is partly attributable to the lithium mass percentage increase at equal densities. This larger concentration of charge carriers yields higher conductivities for similar diffusion coefficients, accounting for an increase in conductivity of ∼30%. As this is much less than the above described rough tripling of the conductivity, we suspect the different anion compositions in the sulfur sub-lattice to be another, dominant factor.
Existing data on the origin of ion conductivity suppression by the anion lattice is quite ambiguous. For example, experimental studies report a strong conductivity suppression by P 2 S 6 4 − , attributed to meso-scale precipitation of the non-conducting Li 2 P 2 S 6 phase [34,35]. On the contrary, density of state calculations report that P 2 S 7 4 − should suppress ion conduction at the atomic scale [36]. The charge transfer along the covalent bond between the P and the bridging S lowers the positive partial charge of the P centers, which supposedly attracts Li + ions to the P 2 S 7 4 − anions more strongly than the other thiophosphate anions. These are just two illustrative examples discussed as possible origins of ion conductivity suppression by the anion lattice.
First, we analyse the anion composition at different temperatures for all three stoichiometries. Violin plots depicting the building block distributions at different temperatures within the structure ensembles are displayed in Figure 3. For the Li 3 PS 4 glass, the simple PS 4 3 − o r t h o -thiophosphate is as intuitively expected the predominant species over the whole temperature range. H y p o -thiodiphosphate P 2 S 6 4 − occurs only in small concentrations ≤10 at.% and shows no strong temperature dependence. Up to 25 at.% of p y r o -thiodiphosphate P 2 S 7 4 − occur at the lower temperature but gradually disappear between 600 and 700 K. These anion ratios are in agreement with experimental ratios found for Li 3 PS 4 [37]. In both, the Li 7 P 3 S 11 and Li 4 P 2 S 7 glasses, the P 2 S 6 4 − content instead increases between 400 and 700 K, even though the increase is not too pronounced in comparison to the width of the distribution in the ensemble. The found P 2 S 6 4 − contents in Li 7 P 3 S 11 and Li 4 P 2 S 7 are slightly higher compared to experimental data [17].
Next, we analyze the number of Li-positions occupied during MD simulations at finite temperatures, by calculating the isosurface of the probability density distribution of Li-positions (exemplary visualizations see Figure S9 in the Supplementary Materials). When referencing the volume enclosed by the isosurface to the total volume of the simulation cell, we identify the relative accessible volume for all Li-ions for a given stoichiometry. As shown in the left panel of Figure 4 for the Li 7 P 3 S 11 and Li 4 P 2 S 7 glasses, the same relative volume is accessed by Li, while Li 3 PS 4 exhibits a 10 % higher accessible Li-volume at all temperatures. This is intuitive as P 2 S n 4 − moieties have a larger surface/volume of the anion, allowing for a smaller number of Li-sites in the material compared to smaller PS 4 3 − anions.
In order to explore the effect of the anion lattice motion on the Li-ion conductivity we either constrain the sulfur positions, or the phosphorous positions, and compare the Li ion conductivity obtained within MD simulations with these two frozen lattices to the unconstrained Li-ion conductivity. As seen in the right panel of Figure 4, the Li-ion conductivity decreases for all three glass stoichioemetries for both frozen lattices. However, while in the case of frozen phosphorus we observe only a slight decrease in conductivity, freezing the sulfur degrees of freedom reduces the conductivity by approximately two orders of magnitude. We observe the largest decrease of the conductivity for the stoichiometry consisting of the highest PS 4 3 − (Li 3 PS 4 ) content, and the smallest change for the lowest PS 4 3 − content (Li 4 P 2 S 7 ). This suggests that the motion of sulfur throughout the Li-ion conduction plays a significant role.
Smith and Siegel showed that in glassy Li 3 PS 4 , lithium migration occurs via a mechanism that combines a concerted motion of lithium ions with re-orientations of PS 4 3 − anions [38]. This effect, known as the ’paddlewheel’ mechanism, can directly attribute the increasing Li-ion conductivity with increasing PS 4 3 − content. So far, the paddlewheel effect has only been shown in Li 3 PS 4 , but our results confirm this effect occurs as long as PS 4 3 − is present. Hence, the conductivity of Li 4 P 2 S 6 and Li 4 P 2 S 7 decrease as well when the sulfur lattice is frozen, but the effect is not as pronounced as in Li 3 PS 4 . As the Li-ion conductivity of all three stoichiometries is almost identical when the sulfur lattice is frozen, this actually suggests that the higher accessible volume of Li in Li 3 PS 4 arises from re-orientations of PS 4 3 − anions. Hence, both effects can not be decoupled, but rather the re-orientation of PS 4 3 − anions generates new Li sites. Together with the increased overall Li content, this thus fully rationalizes why the Li-ion conductivity increases with higher Li 2 S content.

4. Conclusions

All of the herein described effects, collective Li-ion motion of crystalline Li 7 P 3 S 11 , phase transitions of crystalline Li 3 PS 4 , and the conductivity/anion-composition relation in glassy LPS, could not be studied before by a single interatomic potential, preventing the relative identification of trends and common origins. While not only this can now be achieved by our machine learning surrogate model, the general structure of the training protocol furthermore allows for a variety of extensions, including additional selection criteria [20,39], using an electrostatic baseline in the model [40], doping with transition metals, and modeling of solid/solid interfaces [41,42]. We correspondingly see much prospects in the use of ML potentials to further elucidate atomic scale processes in complex battery materials.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/nano12172950/s1, Figure S1: Anion Voronoi Tesselation, Figure S2: Glass sampling approach, Figures S3 and S4: Sampling of P-P distances, Figures S5 and S6: Force parity plot, Figures S7–S10: Radial distribution functions, Figure S11: Li 3 PS 4 crystal configuration, Figure S12: Density dependence of the conductivity, Figure S13: Computational Arrhenius plots, Figure S14: Li accessible volume. Table S1: Technical Hyperparameters for the GAP, Table S2: Coordination-resolved force RMSEs, Table S3: Lithium ion conductivity. References [43,44,45,46,47,48,49] are cited in the Supplementary Materials.

Author Contributions

The project has been conceptualized by C.G.S. and K.R. C.G.S. developed the general fitting procedure, T.H. refined the iterative training scheme. C.S. and J.T.M. guided the formal analysis. The manuscript was jointly written and edited by all authors. All authors have read and agreed to the published version of the manuscript.

Funding

Open access funded by Max Planck Society. We acknowledge funding from the German Research Foundation (DFG) through its Cluster of Excellence e-conversion EXC 2089/1.

Data Availability Statement

Data and codes can be found under Ref. [31].

Conflicts of Interest

The authors declare no conflict of interest.

Abbreviations

The following abbreviations are used in this manuscript:
LPSLithium thiophosphate
SSESolid-state electrolytes
GAPGaussian Approximation Potential
ASS-LIBAll-solid-state lithium-ion batteries
NEBNudged-Elastic-Band
MLMachine Learning
MDMolecular Dynamics
DFTDensity-functional theory
MSDMean-square-displacement
RDFRadial distribution function
HCPHexagonal close-packed

References

  1. Janek, J.; Zeier, W.G. A solid future for battery development. Nat. Energy 2016, 1, 16141. [Google Scholar] [CrossRef]
  2. Zheng, F.; Kotobuki, M.; Song, S.; Lai, M.O.; Lu, L. Review on solid electrolytes for all-solid-state lithium-ion batteries. J. Power Sources 2018, 389, 198–213. [Google Scholar] [CrossRef]
  3. Luntz, A.C.; Voss, J.; Reuter, K. Interfacial challenges in solid-state Li ion batteries. J. Phys. Chem. Lett. 2015, 6, 4599–4604. [Google Scholar] [CrossRef] [PubMed]
  4. Oudenhoven, J.F.; Baggetto, L.; Notten, P.H. All-solid-state lithium-ion microbatteries: A review of various three-dimensional concepts. Adv. Energy Mater. 2011, 1, 10–33. [Google Scholar] [CrossRef]
  5. Shoji, M.; Cheng, E.J.; Kimura, T.; Kanamura, K. Recent progress for all solid state battery using sulfide and oxide solid electrolytes. J. Phys. D Appl. Phys. 2019, 52, 103001. [Google Scholar] [CrossRef]
  6. Kudu, Ö.U.; Famprikis, T.; Fleutot, B.; Braida, M.D.; Le Mercier, T.; Islam, M.S.; Masquelier, C. A review of structural properties and synthesis methods of solid electrolyte materials in the Li2S-P2S5 binary system. J. Power Sources 2018, 407, 31–43. [Google Scholar] [CrossRef]
  7. Robinson, A.L.; Janek, J. Solid-state batteries enter EV fray. MRS Bull. 2014, 39, 1046–1047. [Google Scholar] [CrossRef]
  8. Kim, K.J.; Balaish, M.; Wadaguchi, M.; Kong, L.; Rupp, J.L. Solid-state Li–metal batteries: Challenges and horizons of oxide and sulfide solid electrolytes and their interfaces. Adv. Energy Mater. 2021, 11, 2002689. [Google Scholar] [CrossRef]
  9. Guo, H.; Wang, Q.; Urban, A.; Artrith, N. Artificial Intelligence-Aided Mapping of the Structure–Composition–Conductivity Relationships of Glass–Ceramic Lithium Thiophosphate Electrolytes. Chem. Mater. 2022, 34, 6702–6712. [Google Scholar] [CrossRef]
  10. Kamaya, N.; Homma, K.; Yamakawa, Y.; Hirayama, M.; Kanno, R.; Yonemura, M.; Kamiyama, T.; Kato, Y.; Hama, S.; Kawamoto, K.; et al. A lithium superionic conductor. Nat. Mater. 2011, 10, 682–686. [Google Scholar] [CrossRef]
  11. Aono, H.; Sugimoto, E.; Sadaoka, Y.; Imanaka, N.; Adachi, G.-y. Ionic Conductivity of Solid Electrolytes Based on Lithium Titanium Phosphate. J. Electrochem. Soc. 1990, 137, 1023–1027. [Google Scholar] [CrossRef]
  12. Tachez, M.; Malugain, J.; Mercire, R.; Robert, G. Ionic conductivity of and phase transition in lithium thiophosphate Li3PS4. Solid State Ion. 1984, 14, 181–185. [Google Scholar] [CrossRef]
  13. Yang, Y.; Wu, Q.; Cui, Y.; Chen, Y.; Shi, S.; Wang, R.Z.; Yan, H. Elastic Properties, Defect Thermodynamics, Electrochemical Window, Phase Stability, and Li+ Mobility of Li3PS4: Insights from First-Principles Calculations. ACS Appl. Mater. Interfaces 2016, 8, 25229–25242. [Google Scholar] [CrossRef] [PubMed]
  14. Tsukasaki, H.; Mori, S.; Morimoto, H.; Hayashi, A.; Tatsumisago, M. Direct observation of a non-crystalline state of Li2S–P2S5 solid electrolytes. Sci. Rep. 2017, 7, 4142. [Google Scholar] [CrossRef]
  15. Liu, Z.; Fu, W.; Payzant, E.A.; Yu, X.; Wu, Z.; Dudney, N.J.; Kiggans, J.; Hong, K.; Rondinone, A.J.; Liang, C. Anomalous High Ionic Conductivity of Nanoporous β-Li3PS4. J. Am. Chem. Soc. 2013, 135, 975–978. [Google Scholar] [CrossRef]
  16. Wenzel, S.; Weber, D.A.; Leichtweiss, T.; Busche, M.R.; Sann, J.; Janek, J. Interphase formation and degradation of charge transfer kinetics between a lithium metal anode and highly crystalline Li7P3S11 solid electrolyte. Solid State Ion. 2016, 286, 24–33. [Google Scholar] [CrossRef]
  17. Dietrich, C.; Weber, D.A.; Sedlmaier, S.J.; Indris, S.; Culver, S.P.; Walter, D.; Janek, J.; Zeier, W.G. Lithium ion conductivity in Li2S-P2S5 glasses–building units and local structure evolution during the crystallization of superionic conductors Li3PS4, Li7P3S11 and Li4P2S7. J. Mater. Chem. A 2017, 5, 18111–18119. [Google Scholar] [CrossRef]
  18. Kim, J.S.; Jung, W.D.; Choi, S.; Son, J.W.; Kim, B.K.; Lee, J.H.; Kim, H. Thermally Induced S-Sublattice Transition of Li3PS4 for Fast Lithium-Ion Conduction. J. Phys. Chem. Lett. 2018, 9, 5592–5597. [Google Scholar] [CrossRef]
  19. Staacke, C.G.; Heenen, H.H.; Scheurer, C.; Csányi, G.; Reuter, K.; Margraf, J.T. On the Role of Long-Range Electrostatics in Machine-Learned Interatomic Potentials for Complex Battery Materials. ACS Appl. Energy Mater. 2021, 4, 12562–12569. [Google Scholar] [CrossRef]
  20. Timmermann, J.; Lee, Y.; Staacke, C.G.; Margraf, J.T.; Scheurer, C.; Reuter, K. Data-efficient iterative training of Gaussian approximation potentials: Application to surface structure determination of rutile IrO2 and RuO2. J. Chem. Phys. 2021, 155, 244107. [Google Scholar] [CrossRef]
  21. Perdew, J.P.; Burke, K.; Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 1996, 77, 3865. [Google Scholar] [CrossRef] [PubMed]
  22. Blum, V.; Gehrke, R.; Hanke, F.; Havu, P.; Havu, V.; Ren, X.; Reuter, K.; Scheffler, M. Ab initio molecular simulations with numeric atom-centered orbitals. Comput. Phys. Commun. 2009, 180, 2175–2196. [Google Scholar] [CrossRef]
  23. Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 1995, 117, 1–19. [Google Scholar] [CrossRef]
  24. Bartók, A.P.; Payne, M.C.; Kondor, R.; Csányi, G. Gaussian approximation potentials: The accuracy of quantum mechanics, without the electrons. Phys. Rev. Lett. 2010, 104, 136403. [Google Scholar] [CrossRef] [PubMed]
  25. Bartók, A.P.; Kondor, R.; Csányi, G. On representing chemical environments. Phys. Rev. B 2013, 87, 184115. [Google Scholar] [CrossRef]
  26. Larsen, A.H.; Mortensen, J.J.; Blomqvist, J.; Castelli, I.E.; Christensen, R.; Dułak, M.; Friis, J.; Groves, M.N.; Hammer, B.; Hargus, C.; et al. The atomic simulation environment—A Python library for working with atoms. J. Phys. Condens. Matter 2017, 29, 273002. [Google Scholar] [CrossRef]
  27. Virtanen, P.; Gommers, R.; Oliphant, T.E.; Haberland, M.; Reddy, T.; Cournapeau, D.; Burovski, E.; Peterson, P.; Weckesser, W.; Bright, J.; et al. SciPy 1.0: Fundamental Algorithms for Scientific Computing in Python. Nat. Methods 2020, 17, 261–272. [Google Scholar] [CrossRef]
  28. Pedregosa, F.; Varoquaux, G.; Gramfort, A.; Michel, V.; Thirion, B.; Grisel, O.; Blondel, M.; Prettenhofer, P.; Weiss, R.; Dubourg, V.; et al. Scikit-learn: Machine Learning in Python. J. Mach. Learn. Res. 2011, 12, 2825–2830. [Google Scholar] [CrossRef]
  29. Wang, Y.; Richards, W.D.; Ong, S.P.; Miara, L.J.; Kim, J.C.; Mo, Y.; Ceder, G. Design principles for solid-state lithium superionic conductors. Nat. Mater. 2015, 14, 1026–1031. [Google Scholar] [CrossRef]
  30. Chu, I.H.; Nguyen, H.; Hy, S.; Lin, Y.C.; Wang, Z.; Xu, Z.; Deng, Z.; Meng, Y.S.; Ong, S.P. Insights into the performance limits of the Li7P3S11 superionic conductor: A combined first-principles and experimental study. ACS Appl. Mater. Interfaces 2016, 8, 7843–7853. [Google Scholar] [CrossRef]
  31. Scheurer, C. Model Structures for Glass Phases of the Solid-State Electrolyte LPS. 2022. Available online: https://edmond.mpdl.mpg.de/dataset.xhtml?persistentId=doi:10.17617/3.VZHSXS (accessed on 17 August 2022). [CrossRef]
  32. Homma, K.; Yonemura, M.; Kobayashi, T.; Nagao, M.; Hirayama, M.; Kanno, R. Crystal structure and phase transitions of the lithium ionic conductor Li3PS4. Solid State Ion. 2011, 182, 53–58. [Google Scholar] [CrossRef]
  33. Phuc, N.H.H.; Totani, M.; Morikawa, K.; Muto, H.; Matsuda, A. Preparation of Li3PS4 solid electrolyte using ethyl acetate as synthetic medium. Solid State Ion. 2016, 288, 240–243. [Google Scholar] [CrossRef]
  34. Busche, M.R.; Weber, D.A.; Schneider, Y.; Dietrich, C.; Wenzel, S.; Leichtweiss, T.; Schröder, D.; Zhang, W.; Weigand, H.; Walter, D.; et al. In Situ Monitoring of Fast Li-Ion Conductor Li7P3S11 Crystallization Inside a Hot-Press Setup. Chem. Mater. 2016, 28, 6152–6165. [Google Scholar] [CrossRef]
  35. Hayashi, A.; Minami, K.; Ujiie, S.; Tatsumisago, M. Preparation and ionic conductivity of Li7P3S11-z glass-ceramic electrolytes. J. Non-Cryst. Solids 2010, 356, 2670–2673. [Google Scholar] [CrossRef]
  36. Ohara, K.; Mitsui, A.; Mori, M.; Onodera, Y.; Shiotani, S.; Koyama, Y.; Orikasa, Y.; Murakami, M.; Shimoda, K.; Mori, K.; et al. Structural and electronic features of binary Li2S-P2S5 glasses. Sci. Rep. 2016, 6, 21302. [Google Scholar] [CrossRef]
  37. Dietrich, C.; Weber, D.A.; Culver, S.; Senyshyn, A.; Sedlmaier, S.J.; Indris, S.; Janek, J.; Zeier, W.G. Synthesis, Structural Characterization, and Lithium Ion Conductivity of the Lithium Thiophosphate Li2P2S6. Inorg. Chem. 2017, 56, 6681–6687. [Google Scholar] [CrossRef]
  38. Smith, J.G.; Siegel, D.J. Low-temperature paddlewheel effect in glassy solid electrolytes. Nat. Comm. 2020, 11, 1483. [Google Scholar] [CrossRef]
  39. Timmermann, J.; Kraushofer, F.; Resch, N.; Li, P.; Wang, Y.; Mao, Z.; Riva, M.; Lee, Y.; Staacke, C.; Schmid, M.; et al. IrO2 Surface Complexions Identified through Machine Learning and Surface Investigations. Phys. Rev. Lett. 2020, 125, 206101. [Google Scholar] [CrossRef]
  40. Staacke, C.G.; Wengert, S.; Kunkel, C.; Csányi, G.; Reuter, K.; Margraf, J.T. Kernel charge equilibration: Efficient and accurate prediction of molecular dipole moments with a machine-learning enhanced electron density model. Mach. Learn. Sci. Technol. 2022, 3, 015032. [Google Scholar] [CrossRef]
  41. Stegmaier, S.; Schierholz, R.; Povstugar, I.; Barthel, J.; Rittmeyer, S.P.; Yu, S.; Wengert, S.; Rostami, S.; Hans, K.; Reuter, K.; et al. Nano-Scale Complexions Facilitate Li Dendrite-Free Operation in LATP Solid-State Electrolyte. Adv. Energy Mater 2021, 11, 2100707. [Google Scholar] [CrossRef]
  42. Türk, H.; Schmidt, F.P.; Götsch, T.; Girgsdies, F.; Hammud, A.; Ivanov, D.; Vinke, I.C.; de Haart, L.; Eichel, R.A.; Reuter, K.; et al. Complexions at the Electrolyte/Electrode Interface in Solid Oxide Cells. Adv. Mater. Interfaces 2021, 8, 2100967. [Google Scholar] [CrossRef]
  43. Mehrer, H. Diffusion in Solids: Fundamentals, Methods, Materials, Diffusion-Controlled Processes; Springer Science & Business Media: Cham, Switzerland, 2007; Volume 155. [Google Scholar]
  44. Frenkel, D.; Smit, B. Understanding Molecular Simulation: From Algorithms to Applications; Elsevier: Alpharetta, GA, USA, 2001; Volume 1. [Google Scholar]
  45. Seino, Y.; Ota, T.; Takada, K.; Hayashi, A.; Tatsumisago, M. A sulphide lithium super ion conductor is superior to liquid ion conductors for use in rechargeable batteries. Energy Environ. Sci. 2014, 2, 627–631. [Google Scholar] [CrossRef]
  46. De Klerk, N.; van der Maas, E.; Wagemaker, M. Analysis of Diffusion in Solid-State Electrolytes through MD Simulations, Improvement of the Li-Ion Conductivity in β-Li3PS4 as an Example. ACS Appl. Energy Mater. 2018, 2, 3230–3242. [Google Scholar] [CrossRef] [PubMed]
  47. Baba, T.; Kawamura, Y. Structure and ionic conductivity of Li2S–P2S5 glass electrolytes simulated with first-principles molecular dynamics. Front. Energy Res. 2016, 4, 22. [Google Scholar] [CrossRef]
  48. Shiotani, S.; Ohara, K.; Tsukasaki, H.; Mori, S.; Kanno, R. Pair distribution function analysis of sulfide glassy electrolytes for all-solid-state batteries: Understanding the improvement of ionic conductivity under annealing condition. Sci. Rep. 2017, 7, 6972. [Google Scholar] [CrossRef]
  49. Seino, Y.; Nakagawa, M.; Senga, M.; Higuchi, H.; Takada, K.; Sasaki, T. Analysis of the structure and degree of crystallisation of 70Li2S–30P2S5 glass ceramic. J. Mater. Chem. A 2015, 3, 2756–2761. [Google Scholar] [CrossRef]
Nanomaterials 12 02950 g001 550
Figure 1. (A) Computational Arrhenius plots for Li 7 P 3 S 11 (red solid line) and α , β and γ phase of Li 3 PS 4 (blue solid lines), as well as the glasses of Li 4 P 2 S 6 (orange dashed line), Li 7 P 3 S 11 (red dashed line), and Li 3 PS 4 (blue dashed line). (B) Reference conductivity data from literature. A tabulated form including references can be found in Table S3 in the Supplementary Materials. Solid lines refer to nominal crystalline materials, dashed lines to glasses/ceramics.
Figure 1. (A) Computational Arrhenius plots for Li 7 P 3 S 11 (red solid line) and α , β and γ phase of Li 3 PS 4 (blue solid lines), as well as the glasses of Li 4 P 2 S 6 (orange dashed line), Li 7 P 3 S 11 (red dashed line), and Li 3 PS 4 (blue dashed line). (B) Reference conductivity data from literature. A tabulated form including references can be found in Table S3 in the Supplementary Materials. Solid lines refer to nominal crystalline materials, dashed lines to glasses/ceramics.
Nanomaterials 12 02950 g001
Nanomaterials 12 02950 g002 550
Figure 2. S-S radial distribution functions (RDFs) for MD snapshots of α -Li 3 PS 4 (left panel), β -Li 3 PS 4 (middle panel), and γ -Li 3 PS 4 (right panel) at different temperatures. The disappearance of the peak at 4.3 Å, occurring for β and γ at 700K, corresponds to the phase transition to the α -phase.
Figure 2. S-S radial distribution functions (RDFs) for MD snapshots of α -Li 3 PS 4 (left panel), β -Li 3 PS 4 (middle panel), and γ -Li 3 PS 4 (right panel) at different temperatures. The disappearance of the peak at 4.3 Å, occurring for β and γ at 700K, corresponds to the phase transition to the α -phase.
Nanomaterials 12 02950 g002
Nanomaterials 12 02950 g003 550
Figure 3. Top: Dominant anions in the Li 2 S–P 2 S 5 material class. Bottom: Anion compositions for different MD temperatures, displayed for Li 3 PS 4 (left panel), Li 7 P 3 S 11 (middle panel), and Li 4 P 2 S 7 (right panel) glasses.
Figure 3. Top: Dominant anions in the Li 2 S–P 2 S 5 material class. Bottom: Anion compositions for different MD temperatures, displayed for Li 3 PS 4 (left panel), Li 7 P 3 S 11 (middle panel), and Li 4 P 2 S 7 (right panel) glasses.
Nanomaterials 12 02950 g003
Nanomaterials 12 02950 g004 550
Figure 4. (Left panel) Accessible volume of lithium during MD simulations at various temperatures: Li 3 PS 4 (blue dashed line), Li 7 P 3 S 11 (red dashed line), and Li 4 P 2 S 7 (orange dashed line). (Right panel) Li ion conductivity with frozen sulfur lattice (diamonds with dotted lines), with frozen phosphor lattice (diamonds with solid line) and without constraints on the sulfur lattice (dots with dashed line): Li 3 PS 4 (blue lines), Li 7 P 3 S 11 (red lines), and Li 4 P 2 S 7 (orange lines).
Figure 4. (Left panel) Accessible volume of lithium during MD simulations at various temperatures: Li 3 PS 4 (blue dashed line), Li 7 P 3 S 11 (red dashed line), and Li 4 P 2 S 7 (orange dashed line). (Right panel) Li ion conductivity with frozen sulfur lattice (diamonds with dotted lines), with frozen phosphor lattice (diamonds with solid line) and without constraints on the sulfur lattice (dots with dashed line): Li 3 PS 4 (blue lines), Li 7 P 3 S 11 (red lines), and Li 4 P 2 S 7 (orange lines).
Nanomaterials 12 02950 g004
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Staacke, C.G.; Huss, T.; Margraf, J.T.; Reuter, K.; Scheurer, C. Tackling Structural Complexity in Li2S-P2S5 Solid-State Electrolytes Using Machine Learning Potentials. Nanomaterials 2022, 12, 2950. https://doi.org/10.3390/nano12172950

AMA Style

Staacke CG, Huss T, Margraf JT, Reuter K, Scheurer C. Tackling Structural Complexity in Li2S-P2S5 Solid-State Electrolytes Using Machine Learning Potentials. Nanomaterials. 2022; 12(17):2950. https://doi.org/10.3390/nano12172950

Chicago/Turabian Style

Staacke, Carsten G., Tabea Huss, Johannes T. Margraf, Karsten Reuter, and Christoph Scheurer. 2022. "Tackling Structural Complexity in Li2S-P2S5 Solid-State Electrolytes Using Machine Learning Potentials" Nanomaterials 12, no. 17: 2950. https://doi.org/10.3390/nano12172950

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop