Next Article in Journal
Tracking Bacterial Nanocellulose in Animal Tissues by Fluorescence Microscopy
Next Article in Special Issue
Amphiphilic Cationic Peptide-Coated PHA Nanosphere as an Efficient Vector for Multiple-Drug Delivery
Previous Article in Journal
Superhydrophilic Nanotextured Surfaces for Dental Implants: Influence of Early Saliva Contamination and Wet Storage
Previous Article in Special Issue
Antibacterial Activity of Electrospun Polyacrylonitrile Copper Nanoparticle Nanofibers on Antibiotic Resistant Pathogens and Methicillin Resistant Staphylococcus aureus (MRSA)
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 15
10.3390/nano12152604
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Tailoring of Optical Properties of Methacrylate Resins Enriched by HPHT Microdiamond Particles

by
Ewelina Kowalewska
1,2,
Mateusz Ficek
1,
Krzysztof Formela
3,
Artur Zieliński
3,
Srinivasu Kunuku
1,
Miroslaw Sawczak
4 and
Robert Bogdanowicz
1,*
1
Faculty of Electronics, Telecommunications and Informatics, Gdańsk University of Technology, 11/12 G, Narutowicza St., 80-233 Gdansk, Poland
2
Academic Centre for Materials and Nanotechnology, AGH University of Science and Technology, 30 A, Mickiewicza Ave., 30-059 Krakow, Poland
3
Faculty of Chemistry, Gdańsk University of Technology, 11/12 G, Narutowicza St., 80-233 Gdansk, Poland
4
Centre for Plasma and Laser Engineering, The Szewalski Institute of Fluid Flow Machinery, Polish Academy of Science, 14 Fiszera St., 80-231 Gdansk, Poland
*
Author to whom correspondence should be addressed.
Nanomaterials 2022, 12(15), 2604; https://doi.org/10.3390/nano12152604
Submission received: 31 May 2022 / Revised: 14 July 2022 / Accepted: 21 July 2022 / Published: 28 July 2022
(This article belongs to the Special Issue Synthesis, Properties and Applications of Polymeric Nanomaterials)
Browse Figures
Versions Notes

Abstract

:
Diamond particles have great potential to enhance the mechanical, optical, and thermal properties of diamond–polymer composites. However, the improved properties of diamond–polymer composites depend on the size, dispersibility, and concentration of diamond particles. In the present study, diamond–polymer composites were prepared by adding the microdiamond particles (MDPs) with different concentrations (0.2–1 wt.%) into polymers (acrylate resins) and then subjected to a photocuring process. The surface morphology and topography of the MDPs–polymer composites demonstrated a uniform high-density distribution of MDPs for one wt.% MPDs. Thermogravimetric analysis was employed to investigate the thermal stability of the MDPs–polymer composites. The addition of MDPs has significantly influenced the polymers’ thermal degradation. Absorption and emission spectra of thin layers were recorded through UV/Vis spectrophotometry and spectrofluorimetry. The obtained results revealed a significant increase in the fluorescence intensity of MDPs–polymer composites (at 1 wt.% of MDPs, a 1.5×, 2×, and 5× increase in fluorescence was observed for MDPs–green, MDPs–amber daylight, and MDPs–red resin, respectively) compared with the reference polymer resins. The obtained results of this work show the new pathways in producing effective and active 3D-printed optical elements.

1. Introduction

Nanodiamonds (NDs) are allotropes of nanocarbons that are promising for numerous applications. NDs are widely used in electronics, energy storage, and coating manufacturing due to their unique physicochemical properties, such as high chemical stability, superior hardness, and thermal conductivity [1,2]. In addition, NDs’ chemical stability and biocompatibility properties are highly desirable in medical fields, including imaging, diagnosis, and targeted drug delivery [3,4,5,6,7]. ND powders can be obtained by various methods, including dynamic synthesis; high-pressure, high-temperature synthesis (HPHT); and chemical vapor deposition (CVD). NDs synthesized via the detonation method are frequently mentioned as helpful in preparing ND composites [8,9] by improving their mechanical properties [8,9]. Monocrystalline diamond powders produced by the HPHT method show high optical transparency for potential optoelectronic applications [10,11]. Moreover, structural defects and impurities responsible for the fluorescence of diamonds can be introduced deliberately or unintentionally during the material synthesis. Without expensive high-energy particle irradiation, HPHT diamonds exhibit synthesis-induced defects, such as nitrogen atoms, leading to form color centers for fluorescent emission [12,13,14].
Composites based on ND-incorporated polymer matrices have attracted significant attention due to their improved toughness, strength, transparency, and heat-resistance [15,16,17]. The large active surface area of small carbon nanostructures creates large interfacial areas in composites, and such regions exhibit better physical properties than pure polymers because of the increased interaction with nanoparticles [18]. Recent developments have been focused on the homogeneous distribution of NDs in the polymer matrices by surface functionalization of NDs, resulting in enhanced mechanical properties demonstrated for ND–polymer composites [5]. The most prominent polymers used in the synthesis of ND–polymer composites are poly(methyl methacrylate) (PMMA) [19,20], polyurethane [21], polypropylene [22], and epoxy [23,24]. An increased Young’s modulus and higher glass transition temperature have been observed in composites containing only 0.25 wt.% NDs in a polyurethane-based matrix [17]. ND–polymer composites have also exhibited potential in transparent UV filter coating applications [18,25]. Methacrylate oligomer composites were synthesized by 3D printing [26,27,28]. The obtained ND–polymer resins showed that the addition of NDs significantly reduced the contact angle of the resins, reduced sorption, and improved the mechanical properties.
Zhang et al. reported an enhanced Young’s modulus and yielding stress of 85% and 15%, respectively, for a diamond nanothread (DNT)-incorporated PMMA matrix [29]. The DNT reinforcement mechanism is mainly based on mechanical interlocking and interfacial interactions, which are affected by the DNT’s morphology. Takada et al. reported on acrylic denture base resins modified with NDs (0.014–1 wt.%) [30], and the results showed that a small amount of NDs could impart desirable thermal and esthetic properties to denture base resins. In addition, the ND denture base composites demonstrated antibacterial properties [19,28]. A recent review by Kausar described many approaches to synthesizing ND–polymer composites and the impact of the NDs on the morphological, mechanical, or thermal properties [31]. Octadecylamine-functionalized ND–poly(l-lactic acid) composites have exhibited great potential for bone tissue engineering and regenerative medicine due to their excellent mechanical properties, intrinsic fluorescence, and biodegradability [32]. However, according to the best of our knowledge, less attention has been paid to improving the optical properties of polymers by incorporating diamond particles into the polymer matrix. Therefore, the present study intended to synthesize microdiamond particles (MDPs)–polymer composites with acrylate-based resins and investigate their thermal stability and optical properties. Furthermore, the effect of MDPs was evaluated in terms of the morphology and optical properties.

2. Materials and Methods

2.1. Materials

Monocrystalline diamond powder MSY 0–0.25 with a median grain diameter of 125 nm was purchased from Pureon AG (Lengwil, Switzerland). Diamond particles were produced by milling the monocrystalline diamond films synthesized by the HPHT process. Acetone was obtained from Sigma-Aldrich, Poznań, Poland. The acrylate-based resins (green daylight resin 3D firm, red daylight resin 3D firm, and amber daylight resin 3D hard) were purchased from Photocentric Ltd. (Peterborough, UK), and the properties of the resins are listed in Table 1. The resins are chemically composed of acrylate oligomers, acrylate monomers, methacrylate monomers, methacrylate oligomers, and photoinitiators.

2.2. Fabrication of Composites

MDPs–acrylate composites were prepared by adding 1% of MDPs added to the acetone and then subjected to ultrasonication for 15 min to obtain the proper dispersion of the MDPs throughout the acetone. The MDPs solution was then added to polymer resin in weight proportions of 1:1, 1:2, 1:3, 1:4, and 1:5, and these MDPs–acrylate composites were subjected to homogenization for one minute, at 1000 rpm, with a homogenizer (CAT × 120). This process led to obtaining MDPs–acrylate with different MDP concentrations: 0.2, 0.25, 0.33, 0.5, and 1 wt.%. The samples were placed in a vacuum oven for 12 h, at room temperature, to eliminate air bubbles (Figure 1). Thin layers of MDPs–acrylate composites (up to 245 µm) were prepared by pouring the liquid samples between two sodium glass slides and two horizontally located coverslips. Due to the presence of the photoinitiators, the abovementioned processing steps were carried out with minimal exposure to visible light. Subsequently, the samples underwent photocuring for 12 h.
Shenderova et al. described that it was difficult to attain the required dispersion of NDs by direct mechanical mixing of the NDs into the PDMS matrix, which results in the formation of large (fractions of a millimeter) agglomerates of NDs in the ND–PDMS composite. An intermediate solvent was employed to resolve this issue; the solvent served as a dispersion medium for the nanoparticles before mixing with the polymer matrix [33]. Therefore, in this present study, acetone was used as an intermediate solvent to reduce the agglomeration of the MDPs. The entire process was repeated for each kind of acrylate resin. To evaluate the effect of the added acetone, one set of samples was prepared by adding the MDPs directly to the polymer resin, and pure resins were utilized as reference material.

2.3. Measurements

The morphology and topography of the MDPs–polymer composites were observed by employing a Scanning Electron Microscope (SEM) (Phenom XL, Waltham, MA, USA) with a backscattered electron detector, operating with the accelerating voltage of 10 kV. AFM topography images were obtained by using a NTEGRA (NT-MD, Moscow, Russia) system with NSG30 probes (TipsNano, Tallinn, Estonia), having geometric parameters of 125 × 48 × 4 μm with a tip curvature radius equal to 10 nm. The measurements were carried out in atmospheric conditions, with a moving sample, in semi-contact mode, and the set point was set to half the value of the free oscillation amplitude. Thermogravimetric analysis (TGA) of the MDPs–polymer composites was carried out with a TG 209 F3 apparatus from the Netzsch Group (Selb, Germany). The TGA process was performed for six samples at one time (approx. 10 mg weight), with the samples placed on a ceramic dish. The measurements were performed under a nitrogen atmosphere over a temperature range from 30 to 800 °C, with a heating rate of 10 °C/min.
Absorption spectra were obtained by using a double-beam UV-9000 Metash Spectrophotometer (Shanghai, China). The signal was registered over the 300–1000 nm range, with a 5 nm step. Two sodium glasses with the same thickness as the investigated samples were used as a reference beam. The transmittance of the samples was calculated through Beer’s law. The fluorescence spectra were recorded by utilizing a custom-built setup, using a 532 nm CW Nd:YAG SHG laser (Millenia, Spectra Physics, Milpitas, CA, USA) as an excitation source. The samples were excited by laser from the front surface, at 45 degrees. The fluorescence signal was collected by using a quartz lens and focused on the entrance of an optical fiber. A bandpass filter (OG570, Schott, NY, USA) was used in the detection path to block the laser radiation. The fluorescence signal was analyzed by using a 0.3 m monochromator (SR303i, Andor, Belfast, Great Britain) equipped with 600 groove/mm grating and recorded with an iCCD detector (DH740, Andor, Belfast, UK).

3. Results and Discussion

3.1. Topology and Thermal Behavior

The surface morphology of the MDPs–polymer composites was observed by using the SEM, and the obtained SEM images are shown in Figure 2. Figure 2a shows the surface morphology of the reference sample (MDPs 0 wt.%) derived from the polymer that depicts the river lines kind of surface feature with a smooth surface [34]. Initially, 0.2 wt.% of MDPs was added to the polymer, and the resulting surface morphology revealed an unevenly dispersed micron size MDPs agglomerates on the polymer’s lines kind of surface (Figure 2b). Next, the MDPs’ filler concentration was increased to 0.25% (Figure 2c), 0.33% (Figure 2d), and 0.50% (Figure 2e), and the obtained surface morphology images demonstrate that the uniform distribution of MDPs in the polymer matrix has been increased with the concentration of MDPs. The increase in MDPs’ concentration from 0.2 to 0.25 wt.% has not shown a significant rise in MDPs’ distribution in the polymer matrix (Figure 2c). However, the river-lines pattern of the polymer surface has been partially covered with MDPs for the MDP-filler concentration of 0.33 wt.% (Figure 2d). The distribution of MDPs has been increased and clearly shows the river-lines pattern of the polymer surface MDP agglomerates for the MDP-filler concentration of 0.50% (Figure 2e). Figure 2f shows the SEM morphology of 1% of MDPs added to the polymer composite, revealing a high density of MDP agglomerates with sizes up to 2 µm. Therefore, an MDP concentration up to 0.50% added to the polymer significantly improved a uniform distribution of MDPs throughout the polymer. A further increase in the concentration of MDPs added to polymer led to the formation of high-density MDP aggregates on the MDPs–polymer surface. The MPD aggregates that appeared on the polymer composite’s surface were formed during the hardening process. MDPs and MDP aggregates are marked in red circles in the SEM images of MDPs–polymer composites (Figure 2a–f). The distribution of MDPs in the polymer matrix is consistent with other publications [35].
MDPs–polymer composites were prepared with and without acetone for the MDP filler concentration of 1% to investigate the role of acetone in mixing or distributing the MDPs in the polymer. The surface morphology of the MDPs–polymer composite with the MDPs concentration of 1% in acetone depicts a uniform distribution of MDPs with sizes ~1–3 µm (Figure 2f). In contrast, the MDPs–polymer composite containing the MDP concentration of 1% and without the addition of acetone leads to the formation of large MDP agglomerates with sizes of 10 µm (Figure not shown). It has been reported that direct mixing of MDPs into the polymer resulted in the formation of large aggregates due to a lack of dispersion, and an intermediate medium is required to achieve appropriate dispersion of MDPs throughout the polymer matrix [33]. Therefore, in the present study, acetone was used as an intermediate medium to disperse the MDPs and to form a homogeneous arrangement of MDPs in the resin matrix. In addition, the surface morphology of the MDPs–polymer composite changed with the concentration of MDPs [36,37]. Therefore, the solvent was determined to be necessary to obtain homogeneous samples, and further measurements were conducted only on the acetone-based materials.
The topography and amplitude of different MDPs–polymer composites are shown in Figure 3. Figure 3a,b shows the reference (without MDPs) resin sample’s AFM topography and amplitude image. The topography image reveals the polymer surface without any MDPs particles and river-lines kind of surface feature, which is similar than the SEM morphology of the polymer surface (Figure 2a). The topography images of MDPs–red resin (Figure 3c), MDPs–green resin (Figure 3e), and MDPs–amber resin (Figure 3g) composites revealed the presence of MDP agglomerates of 1 µm in size, irrespective of the concentration of MDPs. In addition, the MDPs are densely covered on lines of polymer surface for the filler concentration of 0.5 and 1 wt.%. MDPs and MDP aggregates were marked in red circles in the AFM topography images of MDPs–polymer composites (Figure 3).
Moreover, MDPs clusters were found in a cross-section (Figure not shown) and the surface of the MDPs–polymer composites at a height of 200–350 nm. Additional amplitude imaging with the use of AFM enabled the imaging of nanostructures and their locations concerning the roughness of the surface of the base material, which is visible at smaller scales. The corresponding AFM amplitude images are labeled as Figure 3b for the reference sample, Figure 3d for MDPs–red resin, Figure 3f for MDPs–green resin, and Figure 3h for MDPs–amber resin composites. These images illustrate the momentary changes in the probe oscillations, allowing for more precise assessment of the locations of topography changes without the possibility of directly estimating the height. The tendency to agglomerate in the areas of primary surface unevenness is visible, especially in the case of higher MDP concentrations.
The upper part of Figure 4a shows the TGA curves of the MDPs–green resin samples, while their derivatives (DTG curves) are illustrated in the lower half. A significant loss in weight was observed for MDPs–green resin composites at temperatures between 350 and 550 °C, and it is attributed to the degradation of the polymer matrix. The degradation temperature (TD) ranged from 364.4 to 375.2 °C (Table 2). The lowest TD value was obtained for the reference polymer sample, while MDPs samples have illustrated the TD ~ 500 to 800 °C [see the supporting information Figure S1a]. A small increase in TD was observed along with the increasing MDPs-filling concentration, which is related to the interaction of the MDPs with the polymer matrix and obvious higher thermal stability observed for the MDPs–polymer composite compared to the polymeric matrix. The difference between the TD value of the reference sample and MDPs–green resin with 1 wt.% of ND was around 4 °C, which is similar to PMMA:MDPs composites (TD~6 °C) [34].
In addition, the degradation of the different MDPs–polymer composites (1 wt.% of MDPs), such as MDPs–green, MDPs–red, and MDPs–amber daylight resins, was studied. The obtained TGA and DTG curves of these samples are shown in Figure 4b. The upper part of Figure 4b shows the TGA curves of the MDPs–polymer resins, which depict the degradation of the polymer from 350 to 450 °C. The TD values of the MDPs–green and MDPs–red resins are 373.5 and 373.0 °C, respectively, while a lower TD value of 368 °C characterized the MDPs–amber daylight resin composite. According to the manufacturer’s specifications, amber resin is characterized by higher hardness and lower flexibility than the green and red polymers due to its slightly different chemical composition. Consequently, its interfacial interactions with the MDP filler lead to the maximum decomposition rate.
To better understand the thermal stability of the materials studied in the present study, the obtained results were compared with observations described by different research groups working in the field of polymer/diamond composites (Table 3). The comparative study in Table 3 shows no simple correlation between a higher concentration of MDP filler and improvement of the thermal stability of MDPs–polymer composites. It should be highlighted that many factors might affect the thermal stability of MDPs–polymer composites, such as the MDPs’ reinforcement filler content or characteristics (purity, surface area, particle size, etc.), polymer matrix composition (kind of polymer, its molecular weight or crosslink density), interfacial interactions in the matrix-filler system, and thermal stability measurements’ conditions.

3.2. Optical Properties

The UV–Vis spectra of the MDPs–polymer composites are presented in Figure 5. The transmittance curves of different amounts of MDP filler added to MDPs–red resin (Figure 5a), MDPs–amber resin (Figure 5b), and MDPs–green resin (Figure 5c) composites demonstrate that the transmittance decreased with the increasing MDPs concentration. The influence of MDPs on the UV–Vis transmittance of the MDPs–polymer composites was confirmed [42,43,44]. The decrease in transmittance with the increase in the concentration of MDPs particles is caused by the different refractive indexes of the MDPs particles and the polymer matrix [45]. In addition, the scattering and reflection of incident light from the widely dispersed MDPs on the river-lines structure of the polymer surface (Figure 2 and Figure 3) are also factors for the decrease in transmittance for MDPs–polymer composites. However, in the case of amber daylight resin, the transmission value is relatively constant at 90% throughout the low-energy part of the spectrum (Figure 5d). As a result, the MDPs–polymer composites exhibited lower transmittance values at lower wavelengths.
Nevertheless, the transmittance increased with the wavelength. The observed high absorbance at lower wavelengths is mainly related to Rayleigh light scattering, which increases proportionally with the decrease in wavelength to 1/λ4. In addition, the MDPs–polymer composites exhibited strong absorption in the UV range (up to 380 nm) due to the presence of sodium glass. It was not possible to detect the signal in the higher-energy region. However, previous studies suggest the existence of the additional absorption band even below 300 nm [18]. In addition, the spectral characteristics of MDPs–polymer composites also depend on the size of the MDPs used in the preparation. Larionova et al. reported that the diameter of the diamond particles influences the color of the nanodiamond suspensions [46].
The fluorescence spectra of the MDPs–polymer composites with different MDP concentrations are shown in Figure 6a for MDPs–red resin, Figure 6b for MDPs–amber resin, and Figure 6c for MDPs–green resin composites. All of the MDPs–polymer composites show a wide fluorescent band at around 588 nm and a small band at 700 nm, which is not observed in the case of the reference resin sample. The fluorescence spectra of the reference resin samples depict broad and relatively weak fluorescence, while the fluorescence signal increases significantly with the addition of MDPs to the polymers. The fluorescence of MDPs samples revealed the typical NV emission [see the supporting information Figure S1b], which is the origin for enhanced fluorescence from MDPs added polymers. It can be observed that the amber daylight resin demonstrated high emission intensity ranging from 560 to about 700 nm (Figure 6b). The MDPs–polymer composites showed an enhancement in fluorescence of the polymer at 588 nm. The fluorescence intensity increased monotonically with the MDPs concentration, and MDPs–polymer composites with the highest concentration of MDPs (1 wt.%) illustrated 4.5 times higher fluorescence intensity than the reference composite (Figure 6b). Therefore, the obtained results indicate that the fluorescence of MDPs arise from synthesis-induced defects such as NV centers. Moreover, the fluorescence of the MDPs is not quenched by the polymer and is responsible for a significant contribution to the emission signal of the MDPs–polymer composite. The addition of 1% of MDPs to the pure green resin resulted in a 1.5× increase in the intensity of the composite (Figure 6c).
No significant fluorescence enhancement was observed for the MDPs–polymer composites with less than 1% MDPs. The MDPs–red composites demonstrated a slightly different emission spectrum than the other samples (Figure 6a,d). The main fluorescent band was shifted toward longer wavelengths and occurred around 600 nm, and for the addition of 1 wt.% MDPs, the fluorescence increased two times compared to the reference sample (Figure 6a,d). The differences in emission spectra shapes are related to the individual resin compositions, but the most interesting effect is the fluorescence enhancement observed for the MDPs–resin composites. Surface-enhanced fluorescence was initially observed for fluorophores under a strong electromagnetic field near metal nanoparticles. This effect is strongly observed in the resonance absorption of plasmonic metal nanoparticles. In this case, the fluorescence enhancement can be explained by the increased absorption and scattering cross-section of plasmonic nanoparticles and decreased fluorescence lifetime of the fluorophore that allows the excited state to return to the ground state at a higher frequency. Recent studies of core/shell-type nanoparticles show that the refractive index of the nanoparticle surrounding (core) has a critical role in fluorescence enhancement, and a significant fluorescence enhancement factor can be achieved by utilizing shells having a higher refractive index [47]. It can be assumed that, in the case of polymeric materials such as epoxy resin, local changes in the polymer structure caused by the presence of nanoparticles will also affect the intensity of fluorescence enhancement [48,49]. The effect of surface-enhanced fluorescence can be observed not only in the case of plasmonic metal nanoparticles but also in the case of non-metallic nanomaterials, such as ZnO nanoparticles and crosslinked polymer nanoparticles [50,51]. The results show that adding the most commonly used NV–NDs or HPHT–MDPs could be successfully applied in fluorescence studies and advanced optical elements.

4. Conclusions

MDPs–polymer composites synthesized by the photocuring method were prepared by adding different concentrations (1%, 0.5%, 0.33%, 0.25%, and 0.2%) of MDPs to three kinds of acrylate resins. SEM morphological studies of the MDPs–resin composites confirmed the presence of MDPs in the polymer matrix, and the distribution density increased with the MDPs concentration. In addition, the AFM topography images of the MDPs–polymer composites are consistent with the SEM images. The density of the MDP agglomerates was also shown to increase with the increasing MDP filler concentration. Acetone was used as an intermediate solvent to prevent aggregation and to improve the dispersibility of the MDPs. TGA studies demonstrated that the stability of MDPs–polymer composites could be maintained up to around 360 °C, and it was found that low concentrations of MDPs have little influence on the degradation temperatures. Moreover, the fluorescence of the MDPs is not completely quenched by the polymer matrix. Importantly, no straightforward correlation was found between an increased concentration of MDP filler and the improved thermal stability of the prepared composites.
UV/Vis spectrophotometry made it possible to determine the ranges of wavelengths with reduced light transmission due to limited MDPs dispersion. Furthermore, intrinsic structural defects in the MDPs showed an influence on the MDPs–polymer composite’s absorption and emission spectra. The obtained results demonstrate the significant potential of the application of polymer–diamond composites in 3D-printed optical elements. An undoubted advantage of the materials described above is the uncomplicated synthesis process, which does not require expensive equipment. It was also proved that a significant increase in the fluorescence of the composites is achievable even at low concentrations of ND (<1%). Moreover, the HPHT–MDPs showed significant fluorescence from nitrogen-vacancy centers; this factor influences the emission properties of MDPs-based polymer composites. Subsequent work should focus on techniques to prevent the agglomeration of the nanodiamonds and improve their dispersion throughout the polymer matrix, which may affect higher optical transmittance of the composites.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/nano12152604/s1, Figure S1: (a) TG curve of MDPs measured in air, which revealing the significant material loss between 500 °C–800 °C. (b) Photoluminescence spectrum of MDPs used as filler in the NDs-polymer matrix depicting the typical NV luminescence.

Author Contributions

Formal analysis, investigation, visualization, and writing—original draft preparation, E.K.; conceptualization, investigation, visualization, and data curation, M.F.; investigation, data curation, and writing—original draft preparation, K.F.; investigation, data curation, and writing—original draft preparation, A.Z.; formal analysis and writing—original draft preparation, S.K.; investigation, data curation, and writing—original draft preparation, M.S.; conceptualization, writing—review and editing, supervision, project administration, and funding acquisition, R.B. All authors have read and agreed to the published version of the manuscript.

Funding

This research work was supported by the “TEAM-NET” project carried out within the POIR.04.04.00-00-1644/18 program of the Foundation for Polish Science co-financed by the European Union under the European Regional Development Fund.

Data Availability Statement

Data underlying the results presented in this paper are not publicly available at this time but may be obtained from the authors upon reasonable request.

Acknowledgments

The authors thank Foundation for Polish Science and the European Union (European Regional Development Fund) for providing funding to conduct this research.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Janik, M.; Głowacki, J.M.; Sawczak, M.; Wcisło, A.; Niedziałkowski, P.; Jurak, K.; Ficek, M.; Bogdanowicz, R. Poly-L-Lysine-functionalized fluorescent diamond particles: pH triggered fluorescence enhancement via surface charge modulation. MRS Bullet. 2022, 47. [Google Scholar] [CrossRef]
  2. Karami, P.; Salkhi Khasraghi, S.; Hashemi, M.; Rabiei, S.; Shojaei, A. Polymer/nanodiamond composites—A comprehensive review from synthesis and fabrication to properties and applications. Adv. Colloid Interface Sci. 2019, 269, 122–151. [Google Scholar] [CrossRef] [PubMed]
  3. Zhang, P.; Yang, J.; Li, W.; Wang, W.; Liu, C.; Griffith, M.; Liu, W. Cationic polymer brush grafted-nanodiamond via atom transfer radical polymerization for enhanced gene delivery and bioimaging. J. Mater. Chem. 2011, 21, 7755–7764. [Google Scholar] [CrossRef]
  4. Taylor, A.C.; González, C.H.; Miller, B.S.; Edgington, R.J.; Ferretti, P.; Jackman, R.B. Surface functionalisation of nanodiamonds for human neural stem cell adhesion and proliferation. Sci. Rep. 2017, 7, 7307. [Google Scholar] [CrossRef] [PubMed]
  5. Jariwala, D.H.; Patel, D.; Wairkar, S. Surface functionalization of nanodiamonds for biomedical applications. Mater. Sci. Eng. C 2020, 113, 110996. [Google Scholar] [CrossRef] [PubMed]
  6. Białobrzeska, W.; Głowacki, M.J.; Janik, M.; Ficek, M.; Pyrchla, K.; Sawczak, M.; Bogdanowicz, R.; Malinowska, N.; Żołędowska, S.; Nidzworski, D. Quantitative fluorescent determination of DNA—Ochratoxin a interactions supported by nitrogen-vacancy rich nanodiamonds. J. Mol. Liq. 2021, 342, 117338. [Google Scholar] [CrossRef]
  7. Głowacki, M.J.; Ficek, M.; Sawczak, M.; Wcisło, A.; Bogdanowicz, R. Fluorescence of nanodiamond cocktails: pH-induced effects through interactions with comestible liquids. Food Chem. 2022, 381, 132206. [Google Scholar] [CrossRef] [PubMed]
  8. Mochalin, V.N.; Shenderova, O.; Ho, D.; Gogotsi, Y. The properties and applications of nanodiamonds. Nat. Nanotechnol. 2012, 7, 11–23. [Google Scholar] [CrossRef]
  9. Dong, J.; Jiang, R.; Huang, H.; Chen, J.; Tian, J.; Deng, F.; Dai, Y.; Wen, Y.; Zhang, X.; Wei, Y. Facile preparation of fluorescent nanodiamond based polymer nanoparticles via ring-opening polymerization and their biological imaging. Mater. Sci. Eng. C 2020, 106, 110297. [Google Scholar] [CrossRef] [PubMed]
  10. Ficek, M.; Głowacki, M.J.; Gajewski, K.; Kunicki, P.; Gacka, E.; Sycz, K.; Mrózek, M.; Wojciechowski, A.M.; Gotszalk, T.P.; Gawlik, W.; et al. Integration of fluorescent, NV-Rich nanodiamond particles with AFM cantilevers by focused ion beam for hybrid optical and micromechanical devices. Coatings 2021, 11, 1332. [Google Scholar] [CrossRef]
  11. Wojciechowski, A.M.; Nakonieczna, P.; Mrózek, M.; Sycz, K.; Kruk, A.; Ficek, M.; Głowacki, M.; Bogdanowicz, R.; Gawlik, W. Optical magnetometry based on nanodiamonds with nitrogen-vacancy color centers. Materials 2019, 12, 2951. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Qin, J.-X.; Yang, X.-G.; Lv, C.-F.; Li, Y.-Z.; Liu, K.-K.; Zang, J.-H.; Yang, X.; Dong, L.; Shan, C.-X. Nanodiamonds: Synthesis, properties, and applications in nanomedicine. Mater. Des. 2021, 210, 110091. [Google Scholar] [CrossRef]
  13. Kumar, R.; Singh, D.K.; Kumar, P.; Trinh, C.T.; Lee, K.G.; Kumar, R.; Dhakate, S.R. High ensemble concentration of photo-stable NV centers in type Ib nanodiamonds by thermal assisted migration of native vacancies. Diam. Relat. Mater. 2021, 114, 108337. [Google Scholar] [CrossRef]
  14. Boudou, J.P.; Tisler, J.; Reuter, R.; Thorel, A.; Curmi, P.A.; Jelezko, F.; Wrachtrup, J. Fluorescent nanodiamonds derived from HPHT with a size of less than 10 Nm. Diam. Relat. Mater. 2013, 37, 80–86. [Google Scholar] [CrossRef]
  15. Jee, A.Y.; Lee, M. Thermal and mechanical properties of Alkyl-functionalized nanodiamond composites. Curr. Appl. Phys. 2011, 11, 1183–1187. [Google Scholar] [CrossRef]
  16. Zhao, Y.Q.; Lau, K.T.; Kim, J.K.; Xu, C.L.; Zhao, D.D.; Li, H.L. Nanodiamond/Poly (Lactic Acid) Nanocomposites: Effect of nanodiamond on structure and properties of poly (lactic acid). Compos. Part B Eng. 2010, 41, 646–653. [Google Scholar] [CrossRef]
  17. Bershtein, V.; Karabanova, L.; Sukhanova, T.; Yakushev, P.; Egorova, L.; Lutsyk, E.; Svyatyna, A.; Vylegzhanina, M. Peculiar dynamics and elastic properties of hybrid semi-interpenetrating polymer network–3-D diamond nanocomposites. Polymer 2008, 49, 836–842. [Google Scholar] [CrossRef]
  18. Mochalin, V.N.; Gogotsi, Y. Nanodiamond-polymer composites. Diam. Relat. Mater. 2015, 58, 161–171. [Google Scholar] [CrossRef]
  19. Mangal, U.; Kim, J.-Y.; Seo, J.-Y.; Kwon, J.-S.; Choi, S. Novel Poly (Methyl Methacrylate) containing and fungal resistance. Materials 2019, 12, 3438. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  20. Protopapa, P.; Kontonasaki, E.; Bikiaris, D.; Paraskevopoulos, K.M.; Koidis, P. Reinforcement of a PMMA resin for fixed interim prostheses with nanodiamonds. Dent. Mater. J. 2011, 30, 222–231. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  21. Alishiri, M.; Shojaei, A.; Abdekhodaie, M.J. Biodegradable polyurethane Acrylate/HEMA-Grafted nanodiamond composites with bone regenerative potential applications: Structure, mechanical properties and biocompatibility. RSC Adv. 2016, 6, 8743–8755. [Google Scholar] [CrossRef]
  22. Lebedev, O.V.; Bogdanova, O.I.; Goncharuk, G.P.; Ozerin, A.N. Tribological and percolation properties of polypropylene/nanodiamond soot composites. Polym. Polym. Compos. 2020, 28, 369–377. [Google Scholar] [CrossRef]
  23. Neitzel, I.; Mochalin, V.; Knoke, I.; Palmese, G.R.; Gogotsi, Y. Mechanical properties of epoxy composites with high contents of nanodiamond. Compos. Sci. Technol. 2011, 71, 710–716. [Google Scholar] [CrossRef]
  24. Neitzel, I.; Mochalin, V.; Bares, J.A.; Carpick, R.W.; Erdemir, A.; Gogotsi, Y. Tribological properties of nanodiamond-epoxy composites. Tribol. Lett. 2012, 47, 195–202. [Google Scholar] [CrossRef]
  25. Behler, K.D.; Stravato, A.; Mochalin, V.; Korneva, G.; Yushin, G.; Gogotsi, Y. Nanodiamond-polymer composite fibers and coatings. ACS Nano 2009, 3, 363–369. [Google Scholar] [CrossRef] [PubMed]
  26. Mangal, U.; Seo, J.Y.; Yu, J.; Kwon, J.S.; Choi, S.H. Incorporating aminated nanodiamonds to improve the mechanical properties of 3d-Printed resin-based biomedical appliances. Nanomaterials 2020, 10, 827. [Google Scholar] [CrossRef] [PubMed]
  27. Ely, E.D.; Lonne, Q.; Lantada, A.D.; Mejía-Ospino, E.; Durán, H.A.E.; Hernández, R.C.; Ramírez-Caballero, G.; Endrino, J.L. Physical and chemical properties characterization of 3d-printed substrates loaded with copper-nickel nanowires. Polymers 2020, 12, 2680. [Google Scholar] [CrossRef]
  28. Mangal, U.; Min, Y.J.; Seo, J.Y.; Kim, D.E.; Cha, J.Y.; Lee, K.J.; Kwon, J.S.; Choi, S.H. Changes in tribological and antibacterial properties of poly(methyl methacrylate)-based 3D-printed intra-oral appliances by incorporating nanodiamonds. J. Mech. Behav. Biomed. Mater. 2020, 110, 103992. [Google Scholar] [CrossRef]
  29. Zhang, Y.; Rhee, K.Y.; Hui, D.; Park, S.-J. A Critical review of nanodiamond based nanocomposites: Synthesis, properties and applications. Compos. Part B Eng. 2018, 143, 19–27. [Google Scholar] [CrossRef]
  30. Takada, T.; Fukuchi, M.; Nezu, T.; Nagano-Takebe, F.; Endo, K. Evaluation of thermal conductivity and esthetic quality of denture base resin composites with acrylic polymer and nanodiamonds. J. Appl. Polym. Sci. 2021, 138, 51436. [Google Scholar] [CrossRef]
  31. Kausar, A. Nanodiamond Integrating Poly(Methyl Methacrylate) nanocomposites intending for technological innovations. Mater. Res. Innov. 2021, 25, 310–319. [Google Scholar] [CrossRef]
  32. Zhang, Q.; Mochalin, V.N.; Neitzel, I.; Knoke, I.Y.; Han, J.; Klug, C.A.; Zhou, J.G.; Lelkes, P.I.; Gogotsi, Y. Fluorescent PLLA-nanodiamond composites for bone tissue engineering. Biomaterials 2010, 32, 87–94. [Google Scholar] [CrossRef]
  33. Shenderova, O.; Tyler, T.; Cunningham, G.; Ray, M.; Walsh, J.; Casulli, M.; Hens, S.; McGuire, G.; Kuznetsov, V.; Lipa, S. Nanodiamond and Onion-like carbon polymer nanocomposites. Diam. Relat. Mater. 2007, 16, 1213–1217. [Google Scholar] [CrossRef]
  34. Sipaut, C.S.; Ahmad, N.; Adnan, R.; Rahman, I.A.; Bakar, M.A.; Ismail, J.; Chee, C.K. Properties and morphology of bulk epoxy composites filled with modified fumed silica-epoxy nanocomposites. J. Appl. Sci. 2007, 7, 27–34. [Google Scholar] [CrossRef] [Green Version]
  35. Hui, Y.Y.; Chen, O.Y.; Azuma, T.; Chang, B.-M.; Hsieh, F.-J.; Chang, H.-C. All-Optical thermometry with nitrogen-vacancy centers in nanodiamond-embedded polymer films. J. Phys. Chem. C 2019, 123, 15366–15374. [Google Scholar] [CrossRef]
  36. Morimune-Moriya, S.; Nishino, T. Strong, tough, transparent and highly heat-resistant acrylic glass based on nanodiamond. Polymer 2021, 222, 123661. [Google Scholar] [CrossRef]
  37. Tiainen, T.; Lobanova, M.; Karjalainen, E.; Tenhu, H.; Hietala, S. Stimuli-responsive nanodiamond–polyelectrolyte composite films. Polymers 2020, 12, 507. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  38. Zhang, Y.; Choi, J.R.; Park, S.J. Thermal conductivity and thermo-physical properties of nanodiamond-attached exfoliated hexagonal boron nitride/epoxy nanocomposites for microelectronics. Compos. Part A Appl. Sci. Manuf. 2017, 101, 227–236. [Google Scholar] [CrossRef]
  39. Špitalský, Z.; Kromka, A.; Matějka, L.; Černoch, P.; Kováová, J.; Kotek, J.; Šlouf, M. Effect of nanodiamond particles on properties of epoxy composites. Adv. Compos. Lett. 2008, 17, 29–34. [Google Scholar] [CrossRef] [Green Version]
  40. Li, W.; Yu, X.; Naito, K.; Ding, H.; Qu, X.; Zhang, Q. Surface functionalization and disaggregation of nanodiamonds via in situ copolymerization. J. Nanosci. Nanotechnol. 2017, 17, 8883–8889. [Google Scholar] [CrossRef]
  41. Hsin, Y.L.; Chu, H.Y.; Jeng, Y.R.; Huang, Y.H.; Wang, M.H.; Chang, C.K. In Situ De-agglomeration and surface functionalization of detonation nanodiamond, with the polymer used as an additive in lubricant oil. J. Mater. Chem. 2011, 21, 13213–13222. [Google Scholar] [CrossRef]
  42. Vanyukov, V.V.; Mikheev, G.M.; Mogileva, T.N.; Puzyr, A.P.; Bondar, V.S.; Svirko, Y.P. Concentration dependence of the optical limiting and nonlinear light scattering in aqueous suspensions of detonation nanodiamond clusters. Opt. Mater. 2014, 37, 218–222. [Google Scholar] [CrossRef]
  43. Shenderova, O.; Grichko, V.; Hens, S.; Walch, J. Detonation nanodiamonds as UV radiation filter. Diam. Relat. Mater. 2007, 16, 2003–2008. [Google Scholar] [CrossRef]
  44. Ficek, M.; Sobaszek, M.; Gnyba, M.; Ryl, J.; Gołuński, Ł.; Smietana, M.; Jasiński, J.; Caban, P.; Bogdanowicz, R. Optical and electrical properties of boron doped diamond thin conductive films deposited on fused silica glass substrates. Appl. Surf. Sci. 2016, 387, 846–856. [Google Scholar] [CrossRef]
  45. Zhou, R.-J.; Burkhart, T. Optical properties of particle-filled polycarbonate, polystyrene, and poly(methyl methacrylate) composites. J. Appl. Polym. Sci. 2010, 115, 1866–1872. [Google Scholar] [CrossRef]
  46. Larionova, I.; Kuznetsov, V.; Frolov, A.; Shenderova, O.; Moseenkov, S.; Mazov, I. Properties of Individual Fractions of Detonation Nanodiamond. Diam. Relat. Mater. 2006, 15, 1804–1808. [Google Scholar] [CrossRef]
  47. Sun, S.; Rasskazov, I.L.; Carney, P.S.; Zhang, T.; Moroz, A. Critical role of shell in enhanced fluorescence of metal-dielectric core-shell nanoparticles. J. Phys. Chem. C 2020, 124, 13365–13373. [Google Scholar] [CrossRef]
  48. Reineck, P.; Lau, D.W.M.; Wilson, E.R.; Nunn, N.; Shenderova, O.A.; Gibson, B.C. Visible to Near-IR fluorescence from single-digit detonation nanodiamonds: Excitation wavelength and PH dependence. Sci. Rep. 2018, 8, 2478. [Google Scholar] [CrossRef] [Green Version]
  49. Tsukahara, R.; Fujiwara, M.; Sera, Y.; Nishimura, Y.; Sugai, Y.; Jentgens, C.; Teki, Y.; Hashimoto, H.; Shikata, S. Removing non-size-dependent electron spin decoherence of nanodiamond quantum sensors by aerobic oxidation. ACS Appl. Nano Mater. 2019, 2, 3701–3710. [Google Scholar] [CrossRef] [Green Version]
  50. Nirala, N.R.; Shtenberg, G. Amplified fluorescence by Zno nanoparticles vs. quantum dots for bovine mastitis acute phase response evaluation in milk. Nanomaterials 2020, 10, 549. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  51. Li, Q.; Kamra, T.; Ye, L. Nanoparticle-enhanced fluorescence emission for non-separation assays of carbohydrates using a boronic acid-alizarin complex. Chem. Commun. 2016, 52, 3701–3704. [Google Scholar] [CrossRef] [PubMed] [Green Version]
Nanomaterials 12 02604 g001 550
Figure 1. Schematic of the preparation of MDPs–polymer composites: dispersion of acetone and MDPs solution (a), homogenization of the obtained solution with polymer resin (b), air-bubble removal with vacuum (c), and photocuring of prepared samples (d).
Figure 1. Schematic of the preparation of MDPs–polymer composites: dispersion of acetone and MDPs solution (a), homogenization of the obtained solution with polymer resin (b), air-bubble removal with vacuum (c), and photocuring of prepared samples (d).
Nanomaterials 12 02604 g001
Nanomaterials 12 02604 g002 550
Figure 2. SEM images of the MDP composites based on green daylight resin with (a) 0 wt.% (green polymer), (b) 0.2 wt.%, (c) 0.25 wt.%, (d) 0.33 wt.%, (e) 0.5 wt.%, and (f) 1 wt.% of MDPs content (0 wt.% belongs to the pure polymer without MDPs). MDPs and MDP aggregates are marked with red circles.
Figure 2. SEM images of the MDP composites based on green daylight resin with (a) 0 wt.% (green polymer), (b) 0.2 wt.%, (c) 0.25 wt.%, (d) 0.33 wt.%, (e) 0.5 wt.%, and (f) 1 wt.% of MDPs content (0 wt.% belongs to the pure polymer without MDPs). MDPs and MDP aggregates are marked with red circles.
Nanomaterials 12 02604 g002
Nanomaterials 12 02604 g003 550
Figure 3. AFM topography and amplitude images of the pure polymer sample (a,b), MDPs–red resin composite with 1 wt% MDPs (c,d), MDPs–green resin composite with 1 wt% MDPs (e,f), and MDPs–amber resin with 0.5 wt% MDPs (g,h).
Figure 3. AFM topography and amplitude images of the pure polymer sample (a,b), MDPs–red resin composite with 1 wt% MDPs (c,d), MDPs–green resin composite with 1 wt% MDPs (e,f), and MDPs–amber resin with 0.5 wt% MDPs (g,h).
Nanomaterials 12 02604 g003
Nanomaterials 12 02604 g004 550
Figure 4. TG and DTG curves of MDPs–polymer composites with (a) green resin and (b) all samples with 1 wt.% (0 wt.% in Figure 4a belongs to the pure polymer without MDPs).
Figure 4. TG and DTG curves of MDPs–polymer composites with (a) green resin and (b) all samples with 1 wt.% (0 wt.% in Figure 4a belongs to the pure polymer without MDPs).
Nanomaterials 12 02604 g004
Nanomaterials 12 02604 g005 550
Figure 5. UV–Vis spectra of MDPs–polymer composites with amber resin (a), red resin (b), green resin (c), and comparison of the samples’ transmittance at 532 nm (d) (0 wt.% in above figures belongs to the pure polymer without MDPs).
Figure 5. UV–Vis spectra of MDPs–polymer composites with amber resin (a), red resin (b), green resin (c), and comparison of the samples’ transmittance at 532 nm (d) (0 wt.% in above figures belongs to the pure polymer without MDPs).
Nanomaterials 12 02604 g005
Nanomaterials 12 02604 g006 550
Figure 6. Fluorescence enhancement of MDPs–polymer composites with amber resin (a), red resin (b), and green resin (c). Graph (d) shows normalized fluorescence and absorption signal for composites with 1 wt.% ND (0 wt.% in above figures belongs to the pure polymer without MDPs).
Figure 6. Fluorescence enhancement of MDPs–polymer composites with amber resin (a), red resin (b), and green resin (c). Graph (d) shows normalized fluorescence and absorption signal for composites with 1 wt.% ND (0 wt.% in above figures belongs to the pure polymer without MDPs).
Nanomaterials 12 02604 g006
Table
Table 1. Mechanical properties of the resins according to the manufacturer.
Table 1. Mechanical properties of the resins according to the manufacturer.
Resin TypeHardnessTensile StrengthElongation at BreakViscosity (25 °C)Volumetric Shrinkage
Green Daylight Resin 3D firm65 Shore D26 MPa14.9%560 cps5.9%
Red Daylight Resin 3D firm65 Shore D26 MPa14.9%560 cps5.9%
Amber Daylight Resin 3D hard77 Shore D42 MPa8.7%230 cps6.6%
Table
Table 2. TGA results of MDPs–polymer composites: TD—degradation temperature at which mass loss reaches 5%, Tmax—temperature corresponding to a maximum rate of decomposition, mr—weight percentage of the residue at 800 °C.
Table 2. TGA results of MDPs–polymer composites: TD—degradation temperature at which mass loss reaches 5%, Tmax—temperature corresponding to a maximum rate of decomposition, mr—weight percentage of the residue at 800 °C.
Resin TypeND Content (wt.%)TD (°C)Tmax (°C)mr (%)
Green0369.4426.412.1
Green0.2375.2429.912.2
Green0.25371.7427.513.4
Green0.33372.2430.112.7
Green0.5364.4426.313.0
Green1373.5426.014.1
Red1373.0426.313.0
Amber1368.0430.015.0
Average calculated for all studied samples370.9 ± 3.5427.8 ± 1.913.2 ± 1.0
Average calculated for samples with 1 wt.% ND371.5 ± 3.0427.4 ± 2.214.0 ± 1.0
Table
Table 3. Comparison of TGA for polymer/diamonds composites.
Table 3. Comparison of TGA for polymer/diamonds composites.
Sample CompositionTGA ConditionsTD
(°C)/MDPs Concentration 		ObservationsReferences
MDPs–acrylate composites
MDPs content: 0.2–1.0 wt.% 		30–800 °C (10 °C/min)
N2 		369.4 (0)
375.2 (0.2)
371.7 (0.25)
372.2 (0.33)
364.4 (0.5)
373.5 (1.0)
373.0 (1.0)
368.0 (1.0)		The overall trend is that a higher content of MDPs improved the thermal stability. However, in selected samples, deviations from this trend were observed. This may be related to chemical reactions between the MDPs and PMMA during synthesis that will affect the curing kinetics and consequently the performance properties of the studied materials.This work
Poly (methyl methacrylate)/nanodiamond nanocomposites
ND content: 0.1–1.0 wt.%		50–450 °C
(10 °C/min)
N2		287 (0)
288 (0.1)
289 (0.5)
293 (1.0)		The thermal stability increased proportionally to the ND content.
A higher content of ND resulted in a higher T-5%.		[36]
Nanodiamond-attached exfoliated hexagonal boron nitride/epoxy nanocomposites
Filler content: 10–50 phr		30–900 °C (10 °C/min)
N2		PDT (polymer decomposition temperature)
378.3 (0)
389.2 (10)
401.8 (20)
398.2 (30)
392.3 (40)
391.2 (50)		For a sample with 10 phr of NDs, an increase of the decomposition temperature by 10.9 °C was observed. Moreover, as could be expected, the char residue for the sample with 10 phr of ND is much higher than it is for unadulterated epoxy resin.
Similar trends were also observed in the other composites, which contained 20, 30, 40, and 50 phr of the EBN and NDEBN.		[38]
Epoxy/nanodiamond composites
ND content: 0.1–1.0 wt.%		No information about temperature measurement range,
(10 °C/min)
Air and N2		Air N2
295 (0)
342 (0)
316 (0.1)
344 (0.1)
326 (0.5)
338 (0.5)
310 (1.0)
343 (1.0)		Interestingly, the sample with 0.5 wt.% of NDs decreased in thermal stability (in nitrogen) compared to the reference material. A similar tendency was observed in our present work.[39]
Aminated nanodiamonds (A-NDs) as nanofillers in biological-grade acrylate-based 3D-printed materials
ND content: 0.1 wt.%		100–800 °C (10 °C/min)
N2		In the reference sample, 40% weight loss was recorded at 405 °C, while in the ND- and
A-ND-incorporated nanocomposites, the same was observed at 420 and 426 °C, respectively.		The weight loss axis is presented only to 40%; therefore, it is difficult to comment on the presented results.
The authors mentioned that the addition of ND increased the thermal stability of the polymer matrix.
A very high level of residue for the reference sample indicated the presence of other fillers in the material.		[26]
ND-grafted poly(styrene)
(ND-PS) and ND-grafted poly(methyl methacrylate) (ND-PMMA)		30–1000 °C (10 °C/min)
N2		The authors presented only TGA curves. There is no additional information with a summary of thermal degradation parameters.Chemical grafting of polymers to the surface of the NDs resulted in deterioration of thermal stability of the studied systems, which is related to the obvious lower thermal stability of polymers compared to the ND filler.
TGA//DTG method is a useful tool for determining the grafting degree.
For the studied systems,
the grafting ratio of the PMMA was 10.56%, while for PS, it was 6.21%.		[40]
Various kinds of polymer chains (e.g., polystyrene, polymethyl methacrylate, and polyglycidyl methacrylate) were chemically grafted onto the deagglomerated nanodiamond by the wet-stirred-media-milling process25–500 °C (10 °C/min)
N2		The authors presented only TGA curves. There is no additional information with a summary of thermal degradation parameters.Chemical grafting of polymers to the surface of the NDs resulted in deterioration of thermal stability of the studied systems, which is related to the obvious lower thermal stability of polymers compared to the ND filler.
The grafting degrees for the studied systems were as follows:
~24% for PS,
~31% for PMMA,
~34% for PGMA.		[41]
PMMA + nanodiamonds
ND content: 1–2 wt.%		30–1000 °C (20 °C/min)
N2		The authors presented only TGA curves. There is no additional information with a summary of thermal degradation parameters.The authors pointed out that a noticeable effect can be observed after high polymer weight loss. The results demonstrate that, even at relatively low dispersity and agglomeration of NDs in PMMA, the thermal degradation temperature can be increased.[33]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Kowalewska, E.; Ficek, M.; Formela, K.; Zieliński, A.; Kunuku, S.; Sawczak, M.; Bogdanowicz, R. Tailoring of Optical Properties of Methacrylate Resins Enriched by HPHT Microdiamond Particles. Nanomaterials 2022, 12, 2604. https://doi.org/10.3390/nano12152604

AMA Style

Kowalewska E, Ficek M, Formela K, Zieliński A, Kunuku S, Sawczak M, Bogdanowicz R. Tailoring of Optical Properties of Methacrylate Resins Enriched by HPHT Microdiamond Particles. Nanomaterials. 2022; 12(15):2604. https://doi.org/10.3390/nano12152604

Chicago/Turabian Style

Kowalewska, Ewelina, Mateusz Ficek, Krzysztof Formela, Artur Zieliński, Srinivasu Kunuku, Miroslaw Sawczak, and Robert Bogdanowicz. 2022. "Tailoring of Optical Properties of Methacrylate Resins Enriched by HPHT Microdiamond Particles" Nanomaterials 12, no. 15: 2604. https://doi.org/10.3390/nano12152604

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop