Comparison of Microstructure, Texture, and Mechanical Properties of TZ61 and AZ61 Mg Alloys Processed by Differential Speed Rolling
Previous Article in Journal
Thermo-Electro-Mechanical Simulation of Electro-Active Composites
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 3
10.3390/ma15030778
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mayenite Synthesis from Hydroxide Precursors: Structure Formation and Active Sites on Its Surface

by
Aleksandr V. Kapishnikov
1,2,*,
Roman M. Kenzhin
1,2,
Anton P. Koskin
2,
Alexander M. Volodin
2 and
Pavel V. Geydt
1,*
1
Laboratory of Functional Diagnostics of Low-Dimensional Structures for Nanoelectronics, Department of Physics, Novosibirsk State University, Pirogova Str., 2, 630090 Novosibirsk, Russia
2
Federal Research Center Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, Prospekt Lavrentieva, 5, 630090 Novosibirsk, Russia
*
Authors to whom correspondence should be addressed.
Materials 2022, 15(3), 778; https://doi.org/10.3390/ma15030778
Submission received: 29 October 2021 / Revised: 12 January 2022 / Accepted: 17 January 2022 / Published: 20 January 2022
Browse Figures
Versions Notes

Abstract

:
We studied the formation process of a mayenite structure from hydroxide precursors in different gas media. According to X-ray diffraction data, this method allows a well-crystallized mayenite (Ca12Al14O33 or C12A7) phase to be obtained at low (500–900 °C) temperatures with an insignificant impurity of CaO. It was shown that the lattice parameters for C12A7 obtained in an inert atmosphere (Ar) were lower when compared with similar samples in the air. These results can be explained by the different levels of oxygen nonstoichiometry in the resulting phase. We noted that sintering and crystallization of mayenite proceeds at lower temperatures in Ar than in the air medium. We found the presence of donor and acceptor active sites on the surface of mayenite, which was detected by the spin probe method. The specific (per unit surface) concentration of such sites (2.5 × 1016 m−2 and 1.5 × 1015 m−2 for donor and acceptor sites, respectively) is comparable to that of γ-Al2O3, which is traditionally used as catalyst support. This allows it to be used in adsorption and catalytic technologies, taking into account its high specific surface area (~30–50 m2/g at a low synthesis temperature).

1. Introduction

Recently, a significant number of works were dedicated to the study of the properties of calcium aluminates with a mayenite structure (Ca12Al14O33 or 12CaO·7Al2O3, also abbreviated as C12A7). This is due to the possible wide range of variations in the functional properties of this material, caused by changing the composition of its anionic sublattice, which occurs with the retention of its cationic framework. The unique chemical and electrophysical properties of these materials were discovered almost two decades ago [1,2] and later studied in detail in numerous works of the H. Hosono group [3,4,5,6,7,8,9,10]. These compounds contain a stable cationic framework [Ca24Al28O64]4+ and a sufficiently mobile anionic sublattice 4X−. The chemical and electrical properties of the obtained materials can be varied over a very wide range by simply replacing the X− anions. The composition of the unit cell of such a compound can be described by the formula:
1 unit cell = [Ca24Al28O64]4+ • 4X−,
where X− = H−, O2−, O− , O2−, OH−, Cl−, F−, e−.
The materials containing unstable (active) forms of anions, e.g., H−, O−, O2−, and especially, e−, are prominent in this series. Thus, X− = O− can act as suppliers for materials with reactive radical O− anions for chemical and catalytic oxidation reactions [5,11,12], while electrides (X− = e− [2]) can be used in emission devices [13,14,15] and memory elements [16,17], acting as electron donors in organic synthesis reactions [18], or as electron donor support materials for heterogeneous catalysts based on noble metals [7,9,10]. A wide range of possible applications has stimulated the development of synthesis methods focused on the fabrication of these materials in desired forms (1D, 2D, 3D) with the required functional properties. Particularly, the key parameters for the use of mayenite in catalytic and adsorption technologies are the specific surface area (SSA) of the material and the presence of various types of active sites on its surface. At the same time, emission devices require a low work function for the ceramic composite materials that can be used in them. Whereas the ReRAM memory elements require a significant difference in concentration of carriers; they are mobile and have a high cyclic stability of the crystal lattice for active layer materials.
Previously, we proposed a simple method for the synthesis of pure-phase mayenite with a sufficiently high SSA by sintering of the hydroxide precursors [19,20]. A similar approach to the synthesis of mayenite was used in a recently published work by another research group [21]. It should be noted that acceptor and donor sites on the surface of oxide systems studied using the spin probe method play an important role in many catalytic reactions on acid catalysts [22,23], and are also responsible for the stabilization of active forms of supported noble metals [24,25,26,27]. In this regard, the study of such sites for mayenite samples synthesized under various conditions is of particular interest. Despite the fairly widespread use of inorganic electrides with a mayenite structure as effective support materials for catalysts [7,9,11], a detailed characterization of the active sites of mayenite (e.g., their types and concentrations) has not yet been reported in the literature. The aim of the present work was to conduct a comparative study of the evolution of the C12A7 structure and active sites on its surface during the calcination of this material in a wide temperature range and different gas atmosphere.

2. Materials and Methods

The synthesis of mayenite was carried out using a method similar that described in works [19,20]. The starting materials for the synthesis were aluminum hydroxide (Pural SB-1, pseudo-boehmite, >99.9%, Condea, Brunsbüttel, Germany) and calcium carbonate (extra purity, >99.97%, Reachim, Penza, Russia). The first stage of the synthesis was the preparation of CaO by decomposing CaCO3 in a muffle in the air at 950 °C for 6 h. Next, CaO was added to a suspension of aluminum hydroxide (100 g/L) in distilled water at room temperature and continuously stirred. The final component ratio corresponded to the stoichiometry of mayenite (12CaO·7Al2O3). The mixture was thoroughly stirred in distilled water for 10 h, filtered, and dried at 110 °C. Then, it was calcined in a muffle furnace in the air at 250 °C for 6 h. The obtained C12A7-250 sample was used as a starting material for further synthesis. Then, the obtained samples were calcined in the air and an Ar flow (16.67 sccm). The initial sample C12A7-250 was heated in all cases at a rate of 3 °C/min. The temperature was maintained for 6 h, and then the sample was cooled down to room temperature at the same rate of 3 °C/min. The samples obtained by calcining in the air are hereinafter referred to as C12A7-T, where T is the calcination temperature. The designation C12A7-T-Ar will be used for the samples calcined in Ar atmosphere.
The phase composition of the samples was studied by X-ray powder diffraction on an ARL X’tra (ThermoFisher, Ecublens, Switzerland) diffractometer with Cu Kα radiation (the X-ray wavelength λ = 1.5418 Å). The data were recorded in the 2θ range 15–50° with a resolution of the Bragg reflection angle 2θ = 0.02°. The calculation and refinement of the unit cell parameters were carried out according to the positions of 3–4 separate peaks by the least-squares method using the POLYCRYSTAL software package [28]. An approximation of the reflections was conducted using the Cauchy–Lorentz functions. The coherent scattering region (CSR or crystallite) sizes D were determined according to the Selyakov–Scherrer formula: D = 0.9λ/(β·cosθ), where β is the broadening of diffraction reflection peaks. The semi-quantitative estimation of the fractions of the crystalline and nanocrystalline (dispersive) components of mayenite was based on an integral intensity analysis, similar to the method described in [29,30]. After subtracting the background intensity, the peaks of mayenite were analyzed as a superposition of two reflections from the crystalline and dispersive phases. The fraction of the crystalline component Wcr was estimated by the formula: Wcr = Icr/(Icr + In), where Icr and In are integral intensities of the diffraction peaks of the crystalline and dispersive phases, respectively.
The concentration of various types of active sites on the sample surface was experimentally determined using spin probe methods. The probe adsorption and spectrum recording procedures were described in detail in our earlier publications [22,24,31]. The Electron Paramagnetic Resonance (EPR) spectra were recorded at room temperature using an ERS-221 spectrometer (Center of Scientific Instruments Engineering, Leipzig, German Democratic Republic) operating in the X-band. The concentrations of the paramagnetic species were determined by numerical double integration with baseline compensation. A dark-colored, crystalline powder 2,2-diphenyl-1-picrylhydrazyl (DPPH) primary standard for quantitative EPR spectrometry was used for calibration of the spectrometer prior to the study. To determine the concentration of donor sites on the surface of the studied systems, we used radical anions emerging during the adsorption of acceptor molecules, such as 1,3,5-trinitrobenzene (TNB) spin probes [24,31]. To determine the concentration of acceptor (acid) sites, we used the radicals emerging during the adsorption of anthracene [22]. Before the adsorption of the probe molecules, the samples were activated in the air at 500 °C for 3 h.
Specific surface areas were determined on the basis of the Brunauer–Emmett–Teller (BET) theory. The data for this method were obtained by low-temperature argon adsorption using an Accelerated Surface Area and Porosimetry system ASAP-2400 (Micromeritics Instrument Corp., Norcross, GA, USA).

3. Results

3.1. X-ray Diffraction Analysis of the Evolution of C12A7 Samples after Heating in Air and An Ar Flow

According to the X-ray phase analysis, the initial sample C12A7-250 appeared to be a mixture of amorphous calcium and aluminum hydroxides. Due to the difficulty in determining the positions of the peaks, it can only be argued that the sample contained the Ca3Al2(OH)12, Ca(OH)2, and AlO(OH) phases. The samples obtained upon further calcination in Ar and air contained several impurities with the primary Ca12Al14O33 phase (JCPDS № 9-413). The formation of mayenite in Ar (Figure 1a) and air (Figure 1b) proceeded in a similar way. Traces of CaO (JCPDS № 37-1497) were also present in the phase composition of samples, apart from the C12A7 at synthesis temperatures ranging from 500 °C to 900 °C. A significant broadening is also observed at the bottom of the reflections from the mayenite phase (Figure 2). This effect can be caused by a bimodal distribution of the particle size and associated with the contribution from nanocrystalline mayenite with a CSR of about 10 nm. The partial decomposition of C12A7 to the Ca3Al2O6 (C3A, JCPDS № 38-1429) and CaAl2O4 (CA, JCPDS № 23-1036) phases occurred at 1100 °C in both atmospheres, according to Figure 1. This decomposition process, similar for both media, was mentioned in previous work by Eufinger et al. [32]. An insignificant difference was observed, i.e., the admixture of the CaAl4O7 (CA2, JCPDS № 23-1037) phase appeared in the phase composition during the heating above 900 °C in air (Figure 1b). Remarkably, when the temperature increased to 1250 °C, calcium aluminate phases reacted and formed the C12A7 phase again. At 1380 °C in Ar, the formation of well-crystallized mayenite with a small admixture of C3A was observed.
The comparison of the initial (500 °C) and final (1380 °C) states of the material is specially presented in Figure 2 to designate the phase purity of the heated material after two distinct heating conditions.
The structural state of C12A7 appeared to be different for the samples synthesized in air and in Ar. Table 1 presents the calculated C12A7 lattice parameters for different synthesis conditions. For mayenite obtained in an Ar medium at low temperatures (500–900 °C), our experimental values were close to the values for C12A7:O2− that were previously reported by other groups [33,34]. The increased value of the lattice parameter at 500 °C can be associated with a high proportion of the C12A7:OH− states in the structure. When the temperature rises to 700–900 °C, the dehydration and substitution of OH− groups by O2− anions occurs, which can reduce the lattice parameter. The increased value of the lattice parameter at 1100 °C can be associated with the decomposition reaction of mayenite at this temperature, which can affect the state of its unit cell. With a further increase in temperature, the lattice parameter becomes close to the value for electron-injected C12A7:e− that was mentioned in previous works [35,36]. Remarkably, in the case of heating in the air, the values of the lattice parameters were higher than in the Ar medium. A similar value for the parameter of 12.070 Å was mentioned in [37], even though it was acquired by the theoretical DFT method. The nature of the change in the parameters with increasing temperature is similar to calcination in Ar, except that the radical states of oxygen-like O− and O2− are formed in the framework in an oxygen-containing medium [5,38]. In [39], the values of possible lattice parameters were shown depending on oxygen stoichiometry. In accordance with “ab initio” calculations, the formation of the superstoichiometric state in Ca12Al14O32+δ is possible in the air at 25–750 °C [39]. Our experimental dataset (Table 1) can be associated with the lattice parameters for the stoichiometric parameter δ in the range of 4–6 (a = 12.02−12.04 Å). This provides evidence for the dominance of O2− clathrate forms in the mayenite structure obtained in the air medium.
The genesis of the microstructure during both heating in the air and an Ar atmosphere is similar, with minor differences (see Table 2). Calcination at 500 °C resulted in obtaining quietly dispersive systems with high SSA values. The increasing synthesis temperature facilitated the sintering of nanocrystalline mayenite and decreased SSA in the temperature range of 500–900 °C for both Ar and air media. This was also verified by the value of the fraction of the dispersive phase, which sharply decreased for the corresponding temperatures in both gas media. This sintering process was accompanied by lowering the CSR values, which can be explained by the formation of new, well-crystallized, small particles from the dispersive fraction. According to the data presented in Table 2, the sintering of nanocrystalline mayenite particles occurs in an Ar atmosphere at a lower temperature than in the air. A subsequent increase in calcination temperature promotes the formation of a well-crystallized mayenite phase. The decomposition process at 1100 °C does not significantly affect crystallite sizes. Most likely, this process occurs in smaller C12A7 particles while the larger particles persist.

3.2. Evolution of Active Sites on the Surface of C12A7 Samples after Heating in Air and an Ar Flow

Active sites on the surface of solids are caused by the presence of various types of coordinatively unsaturated structures. They significantly determine the result of the interaction of the surface with molecules of the external medium in gas or liquid phases. The most important role is played by active sites when using materials in catalytic and adsorption technologies. Spin probe methods based on the use of EPR spectroscopy detects and determines the concentration of various types of active sites on the surface of dispersed oxide systems with acidic and basic properties [22,23,24,25,31]. Thus, effective spin probes for the study of catalysts with basic properties are radical anions of aromatic nitro compounds emerging during their adsorption on donor surface sites [24,25,31], while radical cations emerge from the adsorption of donor molecules of aromatic compounds on the acceptor sites of the surface [22,23]. In the final part of the present work, we studied such sites on the surface of C12A7 samples previously characterized by the XRD method. We used γ-Al2O3 and CaO, individual components that are often used as precursors for the synthesis of mayenite, as reference samples in these experiments.
Figure 3 shows the EPR spectra emerging from the adsorption of 1,3,5-trinitrobenzene (TNB) molecules on the donor sites of the surface of the studied samples. These are the spectra of TNB radical anions stabilized at donor surface sites [24,25,31]. They represent a three-component signal due to a hyperfine interaction with nitrogen atoms. The sites responsible for the formation of these radical anions are present on mayenite, and their spectra are similar to those observed for γ-Al2O3. Slightly different hyperfine coupling Azz values (31 G for γ-Al2O3, 30 G for C12A7 and 25 G for CaO) for these samples correlate well, with an increase in the strength of the main sites in this series.
Donor sites on the surface of oxide materials play an important role in the stabilization of the deposited noble metals [24,25,26,27] and determine the activity of such materials in catalytic oxidation reactions. In this regard, it was of interest to compare the concentrations of the donor sites detected by the spin probe method for C12A7-T materials and γ-Al2O3, i.e., a traditional support for various catalysts. Figure 4 shows the results of this comparison. As can be seen from the data presented in Table 2, the SSA values for these samples are different. For this reason, the data in Figure 4 are referred to as the unit area of the samples.
It is observed that the heating of C12A7 samples in the temperature range from 500 °C to 700 °C has practically no effect on the specific surface concentration of the detected donor sites and is more than twice that of γ-Al2O3. This decrease, together with an increase in temperature up to 1100 °C may be due to the reversible decomposition of the mayenite phase and the formation of C3A and CA phases (See Figure 1) with other surface properties.
The presence and strength of the electron-acceptor sites on the surface of oxide systems are associated with their acidic properties. In many cases, their concentration can determine the efficiency of the catalytic reactions due to the acidic properties of the catalyst [22,23]. In the present work, we used radical cations emerging after the adsorption of anthracene as spin probes to estimate the concentration of the acceptor sites.
Figure 5a shows a typical EPR spectrum that appears after the adsorption of anthracene molecules on the studied samples. It is a singlet line (g = 2.0036, Hp-p = 7.2 G), which appeared to be the same for the γ-Al2O3 and C12A7 samples. However, the concentration of these radicals differs, which was determined by the concentration of acceptor sites on the surface of the studied materials. For CaO, the formation of these radicals was not observed due to the lack of acidic properties.
Figure 5b shows a comparison of the specific (per unit surface) concentration of these radicals for the studied samples. It is clearly seen that the concentration of acceptor sites on the surface of the C12A7 and γ-Al2O3 samples are similar up to a calcination temperature of 900 °C. This decrease in concentration for samples calcined at 1100 °C, as in the case of TNB radical anions, is most likely related to a decrease in the fraction of the mayenite phase in the studied material due to its decomposition.
From the presented results, it can be concluded that the specific concentrations of acceptor sites on the surface of all studied C12A7 samples are similar to those of γ-Al2O3. At the same time, the specific concentration of donor sites on mayenite is almost twice as high as γ-Al2O3. Mayenite is most likely more effective as a support for catalysts in comparison with γ-Al2O3, for which the presence of donor sites plays an important role. Specifically, these donor sites can consist of noble metal oxidation catalysts [24,25,26,27].

4. Conclusions

Solid-state transformations of hydroxide precursors Ca(OH)2 and Al(OH)3, followed by the controlled heating of the obtained mayenite ceramic material in different gas media, was studied in this work. The XRD analysis showed that this method allows predominantly C12A7 to be obtained, but it also contains some admixtures such as CaO for low temperatures (500–900 °C) or C3A, CA, and CA2 for high (1100–1380 °C) temperatures. The lattice parameters for mayenite obtained in Ar are lower than for similar samples in the air. Our results were caused by different levels of oxygen non-stoichiometry in the obtained mayenite. The sintering and crystallization of mayenite in Ar proceeds at lower temperatures than in the air medium. We detected the donor and acceptor active sites on the surface of mayenite by the spin probe method. The specific (per unit surface) concentration of such sites is comparable to that of γ-Al2O3, which is traditionally used as a catalyst support. Thus, we highlight the capability of using mayenite in adsorption and catalytic technologies, taking into account its high specific surface area ~30–50 m2/g already at a low synthesis temperature. The obtained phases can be used in various deposition techniques to produce various desired structures, which are proposed for further applications in catalysis, ceramics, memory elements and electron-emitting devices.

Author Contributions

Investigation, A.V.K., R.M.K. and A.P.K.; Methodology, A.M.V.; Project administration, P.V.G.; Writing—original draft, A.V.K. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Ministry of Science and Higher Education of Russian Federation by the grant FSUS-2020-0029.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding authors.

Acknowledgments

The authors are thankful to A.O. Geydt for help with translation. The authors acknowledge the Center of Collective Use “VTAN” of NSU for the usage of the XRD equipment.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Hayashi, K.; Matsuishi, S.; Kamiya, T.; Hirano, M.; Hosono, H. Light-induced conversion of an insulating refractory oxide into a persistent electronic conductor. Nature 2002, 419, 462–465. [Google Scholar] [CrossRef] [PubMed]
  2. Matsuishi, S.; Toda, Y.; Miyakawa, M.; Hayashi, K.; Kamiya, T.; Hirano, M.; Tanaka, I.; Hosono, H. High-density electron anions in a nanoporous single crystal: [Ca24Al28O64]4+(4e−). Science 2003, 301, 626–629. [Google Scholar] [CrossRef] [PubMed]
  3. Miyakawa, M.; Hayashi, K.; Hirano, M.; Toda, Y.; Kamiya, T.; Hosono, H. Fabrication of Highly Conductive 12CaO·7Al2O3 Thin Films Encaging Hydride Ions by Proton Implantation. Adv. Mater. 2003, 15, 1100–1103. [Google Scholar] [CrossRef]
  4. Kim, S.W.; Matsuishi, S.; Miyakawa, M.; Hayashi, K.; Hirano, M.; Hosono, H. Fabrication of room temperature-stable 12CaO·7Al2O3 electride: A review. J. Mater. Sci. Mater. Electron. 2007, 18, S5–S14. [Google Scholar] [CrossRef]
  5. Hosono, H.; Hayashi, K.; Kajihara, K.; Sushko, P.V.; Shluger, A.L. Oxygen ion conduction in 12CaO·7Al2O3: O2− conduction mechanism and possibility of O− fast conduction. Solid State Ion. 2009, 180, 550–555. [Google Scholar] [CrossRef]
  6. Kim, S.W.; Shimoyama, T.; Hosono, H. Solvated Electrons in High-Temperature Melts and Glasses of the Room-Temperature Stable Electride [Ca24Al28O64] 4+·4e−. Science 2011, 333, 71–74. [Google Scholar] [CrossRef] [PubMed]
  7. Kitano, M.; Inoue, Y.; Yamazaki, Y.; Hayashi, F.; Kanbara, S.; Matsuishi, S.; Yokoyama, T.; Kim, S.W.; Hara, M.; Hosono, H. Ammonia synthesis using a stable electride as an electron donor and reversible hydrogen store. Nat. Chem. 2012, 4, 934–940. [Google Scholar] [CrossRef]
  8. Kim, S.W.; Hosono, H. Synthesis and properties of 12CaO·7Al2O3 electride: Review of single crystal and thin film growth. Philos. Mag. Lett. 2012, 92, 2596–2628. [Google Scholar] [CrossRef]
  9. Sharif, M.J.; Kitano, M.; Inoue, Y.; Niwa, Y.; Abe, H.; Yokoyama, T.; Hara, M.; Hosono, H. Electron Donation Enhanced CO Oxidation over Ru-Loaded 12CaO·7Al2O3 Electride Catalyst. J. Phys. Chem. C 2015, 119, 11725–11731. [Google Scholar] [CrossRef]
  10. Hara, M.; Kitano, M.; Hosono, H. Ru-Loaded C12A7:e− Electride as a Catalyst for Ammonia Synthesis. ACS Catal. 2017, 7, 2313–2324. [Google Scholar] [CrossRef]
  11. Yang, S.W.; Kondo, J.N.; Hayashi, F.; Hirano, M.; Domen, K.; Hosono, H. Partial oxidation of methane to syngas over promoted C12A7. Appl. Catal. A-Gen 2004, 277, 239–246. [Google Scholar] [CrossRef]
  12. Dong, T.; Li, J.; Huang, F.; Wang, L.; Tu, J.; Torimoto, Y.; Sadakata, M.; Li, Q.X. One-step synthesis of phenol by O− and OH− emission material. Chem. Commun. 2005, 21, 2724–2726. [Google Scholar] [CrossRef]
  13. Chen, X.; Sanmartin, J.R. Bare-tether cathodic contact through thermionic emission by low-work-function materials. Phys. Plasmas 2012, 19, 073508. [Google Scholar] [CrossRef] [Green Version]
  14. Toshihiro, T.; Hayashi, K. Thermionic Electron Emission from a Mayenite Electride-Metallic Titanium Composite Cathode. Appl. Phys. Express 2013, 6, 015802. [Google Scholar]
  15. Feizi, E.; Ray, A.K. 12CaO·7Al2O3 Ceramic: A Review of the Electronic and Optoelectronic Applications in Display Devices. J. Display Technol. 2016, 12, 451–459. [Google Scholar] [CrossRef] [Green Version]
  16. Adachi, Y.; Kim, S.-W.; Kamiya, T.; Hosono, H. Bistable resistance switching in surface-oxidized C12A7: e− single-crystal. Mater. Sci. Eng. B 2009, 161, 76–79. [Google Scholar] [CrossRef]
  17. Hosono, H.; Hayashi, K.; Kamiya, T.; Atou, T.; Susaki, T. New functionalities in abundant element oxides: Ubiquitous element strategy. Sci. Technol. Adv. Mater. 2011, 12, 034303. [Google Scholar] [CrossRef] [Green Version]
  18. Buchammagari, H.; Toda, Y.; Hirano, M.; Hirano, H.; Takeuchi, D.; Osakada, K. Room Temperature-Stable Electride as a Synthetic Organic Reagent: Application to Pinacol Coupling Reaction in Aqueous Media. Org. Lett. 2007, 9, 4287–4289. [Google Scholar] [CrossRef]
  19. Volodin, A.M.; Zaikovskii, V.I.; Kenzhin, R.M.; Bedilo, A.F.; Mishakov, I.V.; Vedyagin, A.A. Synthesis of Nanocrystalline Calcium Aluminate C12A7 under Carbon Nanoreactor Conditions. Mater. Lett. 2017, 189, 210–212. [Google Scholar] [CrossRef]
  20. Yakovlev, I.V.; Volodin, A.M.; Papulovskiy, E.S.; Andreev, A.S.; Lapina, O.B. Structure of Carbon-Coated C12A7 Electride via Solid-State NMR and DFT Calculations. J. Phys. Chem. C 2017, 121, 22268–22273. [Google Scholar] [CrossRef]
  21. Berent, K.; Komarek, S.; Lach, R.; Pyda, W. The Effect of Calcination Temperature on the Structure and Performance of Nanocrystalline Mayenite Powders. Materials 2019, 12, 3476. [Google Scholar] [CrossRef] [Green Version]
  22. Zotov, R.A.; Molchanov, V.V.; Volodin, A.M.; Bedilo, A.F. Characterization of the Active Sites on the Surface of Al2O3 Ethanol Dehydration Catalysts by EPR using Spin Probes. J. Catal. 2011, 278, 71–77. [Google Scholar] [CrossRef]
  23. Bedilo, A.F.; Ivanova, A.S.; Pahomov, N.A.; Volodin, A.M. Development of an ESR Technique for Testing Sulfated Zirconia Catalysts. J. Molec. Catal. A 2000, 158, 409–412. [Google Scholar] [CrossRef]
  24. Vedyagin, A.A.; Volodin, A.M.; Stoyanovskii, V.O.; Mishakov, I.V.; Medvedev, D.A.; Noskov, A.S. Characterization of active sites of Pd/Al2O3 model catalysts with low Pd content by luminescence, EPR and ethane hydrogenolysis. Appl. Catal. B 2011, 103, 397–403. [Google Scholar] [CrossRef]
  25. Vedyagin, A.A.; Volodin, A.M.; Kenzhin, R.M.; Chesnokov, V.V.; Mishakov, I.V. CO Oxidation over Pd/ZrO2 Catalysts: Role of Support′s Donor Sites. Molecules 2016, 21, 1289. [Google Scholar] [CrossRef] [PubMed]
  26. Vedyagin, A.A.; Volodin, A.M.; Kenzhin, R.M.; Stoyanovskii, V.O.; Rogov, V.A.; Kriventsov, V.V.; Mishakov, I.V. The role of chemisorbed water in formation and stabilization of active sites on Pd/Alumina oxidation catalysts. Catal. Today 2018, 307, 102–110. [Google Scholar] [CrossRef]
  27. Vedyagin, A.A.; Shubin, Y.V.; Kenzhin, R.M.; Plyusnin, P.E.; Stoyanovskii, V.O.; Volodin, A.M. Prospect of Using Nanoalloys of Partly Miscible Rhodium and Palladium in Three-Way Catalysis. Top.Catal. 2019, 62, 305–314. [Google Scholar] [CrossRef]
  28. Tsybulya, S.V.; Cherepanova, S.V.; Solovʹeva, L.P. Polycrystal Software Package for IBM/PC. Struct. Chem. 1996, 37, 332–334. [Google Scholar] [CrossRef]
  29. Abrosimova, G.E.; Aronin, A.S.; Kholstinina, N.N. On the determination of the volume fraction of the crystalline phase in amorphous-crystalline alloys. Phys. Solid State 2010, 52, 445–451. [Google Scholar] [CrossRef]
  30. Huang, S. Structure and Structure Analysis of Amorphous Materials; Claredon: Oxford, UK, 1984. [Google Scholar]
  31. Medvedev, D.A.; Rybinskaya, A.A.; Kenzhin, R.M.; Volodin, A.M.; Bedilo, A.F. Characterization of electron donor sites on Al2O3 surface. Phys. Chem. Chem. Phys. 2012, 14, 2587–2598. [Google Scholar] [CrossRef]
  32. Eufinger, J.; Schmidt, A.; Lerch, M.; Janek, J. Novel anion conductors—Conductivity, thermodynamic stability and hydration of anion-substituted mayenite-type cage compounds C12A7:X (X = O, OH, Cl, F, CN, S, N). Phys. Chem. Chem. Phys. 2015, 17, 6844–6857. [Google Scholar] [CrossRef] [Green Version]
  33. Matovic, B.; Prekajski, M.; Pantic, J.; Brauniger, T.; Rosic, M.; Zagorac, D.; Milivojevic, D. Synthesis and densification of single-phase mayenite (C12A7). J. Eur. Ceramic. Soc. 2016, 36, 4237–4241. [Google Scholar] [CrossRef]
  34. Boysen, H.; Lerch, M.; Stys, A.; Senyshin, A. Structure and oxygen mobility in mayenite (Ca12Al14O33): A high-temperature neutron powder diffraction study. ActaCrystalogr. B 2007, 63, 675–682. [Google Scholar] [CrossRef] [PubMed]
  35. Salasin, J.R.; Schwerzler, S.E.A.; Mukherjee, R.; Keffer, D.J.; Sickafus, K.E.; Rawn, C.J. Direct Formation and Structural Characterization of Electride C12A7. Materials 2019, 12, 84. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  36. Matsuishi, S.; Nomura, T.; Hirano, M.; Kodama, K.; Shamoto, S.I.; Hosono, H. Direct synthesis of powdery inorganic electride [Ca24Al28O64]4+(e−)4 and determination of oxygen stoichiometry. Chem. Mater. 2009, 21, 2589–2591. [Google Scholar] [CrossRef]
  37. Huang, J.; Valenzano, L.; Sant, G. Framework and Channel Modifications in Mayenite (12CaO·7Al2O3) Nanocages by Cationic Doping. Chem. Mater. 2015, 27, 4731–4741. [Google Scholar] [CrossRef]
  38. Hayashi, K.; Hirano, M.; Matsuishi, S.; Hosono, H. Microporous crystal 12CaO·7Al2O3 encaging abundant O− radicals. J. Am. Chem. Soc. 2002, 124, 738–739. [Google Scholar] [CrossRef]
  39. Yu, Z.; Okoronkwo, M.U.; Sant, G.; Misture, S.T.; Wang, B. Understanding Oxygen Nonstoichiometry in Mayenite: From Electride to Oxygen Radical Clathrate. J. Phys. Chem. C 2019, 123, 11982–11992. [Google Scholar] [CrossRef]
Materials 15 00778 g001 550
Figure 1. Diffraction patterns of samples obtained in inert Ar atmosphere (a) and in air (b) at different temperatures.
Figure 1. Diffraction patterns of samples obtained in inert Ar atmosphere (a) and in air (b) at different temperatures.
Materials 15 00778 g001
Materials 15 00778 g002 550
Figure 2. Comparison of diffraction patterns for samples obtained at 500 °C and 1380 °C in Ar atmosphere.
Figure 2. Comparison of diffraction patterns for samples obtained at 500 °C and 1380 °C in Ar atmosphere.
Materials 15 00778 g002
Materials 15 00778 g003 550
Figure 3. EPR spectra of radical anions on the surface of γ-Al2O3, C12A7-500, and CaO samples activated at 500 °C, appearing after the adsorption of 1,3,5-trinitrobenzene.
Figure 3. EPR spectra of radical anions on the surface of γ-Al2O3, C12A7-500, and CaO samples activated at 500 °C, appearing after the adsorption of 1,3,5-trinitrobenzene.
Materials 15 00778 g003
Materials 15 00778 g004 550
Figure 4. The concentration of TNB-radical anions per unit surface of the samples.
Figure 4. The concentration of TNB-radical anions per unit surface of the samples.
Materials 15 00778 g004
Materials 15 00778 g005 550
Figure 5. (a) Typical EPR spectrum of radicals appearing after the adsorption of anthracene on γ-Al2O3 and C12A7 samples. (b) The concentration of radicals arising from the adsorption of anthracene molecules on acceptor sites. The given concentration values are referred to as the unit surface of the samples.
Figure 5. (a) Typical EPR spectrum of radicals appearing after the adsorption of anthracene on γ-Al2O3 and C12A7 samples. (b) The concentration of radicals arising from the adsorption of anthracene molecules on acceptor sites. The given concentration values are referred to as the unit surface of the samples.
Materials 15 00778 g005
Table
Table 1. Lattice parameters for C12A7 synthesized at different temperatures in Ar and air media.
Table 1. Lattice parameters for C12A7 synthesized at different temperatures in Ar and air media.
T, °Ca, ÅRef.
ArAir
50011.995 ± 0.00312.041 ± 0.007This work
70011.981 ± 0.00312.038 ± 0.004This work
90011.982 ± 0.00212.022 ± 0.001This work
110011.998 ± 0.00312.025 ± 0.003This work
125011.998 ± 0.00312.033 ± 0.004This work
138011.999 ± 0.001-This work
1200-11.989[33]
1350-11.979[34]
130011.993-[35]
130011.999-[36]
Table
Table 2. Crystallite sizes of crystalline C12A7 (D), fractions of crystalline (Wcr) and nanocrystalline (Wn) C12A7, and SSA for samples obtained in Ar and air at different temperatures.
Table 2. Crystallite sizes of crystalline C12A7 (D), fractions of crystalline (Wcr) and nanocrystalline (Wn) C12A7, and SSA for samples obtained in Ar and air at different temperatures.
T, °CD, nmWcr, %Wn, %SSA, m2/g
ArAirArAirArAirArAir
5009677232077806163
7005371655335475445
9007057-70-302638
11009285--1412
125010090--12
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Kapishnikov, A.V.; Kenzhin, R.M.; Koskin, A.P.; Volodin, A.M.; Geydt, P.V. Mayenite Synthesis from Hydroxide Precursors: Structure Formation and Active Sites on Its Surface. Materials 2022, 15, 778. https://doi.org/10.3390/ma15030778

AMA Style

Kapishnikov AV, Kenzhin RM, Koskin AP, Volodin AM, Geydt PV. Mayenite Synthesis from Hydroxide Precursors: Structure Formation and Active Sites on Its Surface. Materials. 2022; 15(3):778. https://doi.org/10.3390/ma15030778

Chicago/Turabian Style

Kapishnikov, Aleksandr V., Roman M. Kenzhin, Anton P. Koskin, Alexander M. Volodin, and Pavel V. Geydt. 2022. "Mayenite Synthesis from Hydroxide Precursors: Structure Formation and Active Sites on Its Surface" Materials 15, no. 3: 778. https://doi.org/10.3390/ma15030778

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.