Next Article in Journal
Mechanical Characterization of Dental Prostheses Manufactured with PMMA–Graphene Composites
Previous Article in Journal
The Correlation between Shrinkage and Acoustic Emission Signals in Early Age Concrete
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 15
10.3390/ma15155390
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Constructing Heterogeneous Photocatalysts Based on Carbon Nitride Nanosheets and Graphene Quantum Dots for Highly Efficient Photocatalytic Hydrogen Generation

by
Yong Wang
1,†,
Chengxin Zeng
1,†,
Yichen Liu
1,
Dingyi Yang
1,
Yu Zhang
2,
Zewei Ren
1,
Qikun Li
1,
Jian Hao
3,
Wen Hu
1,*,
Yizhang Wu
4,* and
Rusen Yang
1,*
1
Academy of Advanced Interdisciplinary Research, School of Advanced Materials and Nanotechnology, Xidian University, Xi’an 710126, China
2
Department of Physics, Shaanxi University of Science and Technology, Xi’an 710021, China
3
State Key Laboratory of High-Efficiency Utilization of Coal and Green Chemical Engineering, Ningxia University, Yinchuan 750021, China
4
National Laboratory of Solid State Microstructures, Collaborative Innovation Center of Advanced Microstructures and Jiangsu Provincial Key Laboratory for Nanotechnology, Nanjing University, Nanjing 210093, China
*
Authors to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Materials 2022, 15(15), 5390; https://doi.org/10.3390/ma15155390
Submission received: 30 June 2022 / Revised: 24 July 2022 / Accepted: 3 August 2022 / Published: 5 August 2022
(This article belongs to the Special Issue Flexible Materials and Sensing Devices)
Browse Figures
Versions Notes

Abstract

:
Although graphitic carbon nitride nanosheets (CNs) with atomic thickness are considered as promising materials for hydrogen production, the wide band gap (3.06 eV) and rapid recombination of the photogenerated electron–hole pairs impede their applications. To address the above challenges, we synergized atomically thin CNs and graphene quantum dots (GQDs), which were fabricated as 2D/0D Van der Waals heterojunctions, for H2 generation in this study. The experimental characterizations indicated that the addition of GQDs to the π-conjugated system of CNs can expand the visible light absorption band. Additionally, the surface photovoltage spectroscopy (SPV) confirmed that introducing GQDs into CNs can facilitate the transport of photoinduced carriers in the melon chain, thus suppressing the recombination of charge carriers in body. As a result, the H2 production activity of the Van der Waals heterojunctions was 9.62 times higher than CNs. This study provides an effective strategy for designing metal-free Van der Waals hetero-structured photocatalysts with high photocatalytic activity.

1. Introduction

Since the TiO2 discovery as a photocatalyst for water splitting, different semiconductor materials with specific energy-band positions have been employed as photocatalytic materials for pollutant degradation, H2 production from water splitting, and carbon dioxide reduction [1,2,3,4,5,6,7,8,9]. Photocatalysts are considered to be an efficient technique to generate hydrogen energy, while also addressing environmental and energy issues. [4,5,10,11,12]. However, many of the semiconductor materials have a limited visible light-absorption range, due to the large band gaps caused by the usage of sunlight [13,14,15,16,17]. Additionally, the poor separation efficiency and rapid recombination of the photoinduced electron–hole pairs are other important factors limiting photocatalytic hydrogen production [18,19,20,21].
Two-dimensional semiconductor materials have a larger specific surface area, more reactive sites on the surface, and shorter photogenerated carrier-separation pathways than bulk materials [22,23,24,25]. As a result of their exceptional features, the 2D semiconductor materials have considerable application potential in the area of photocatalytic water splitting [26,27,28,29,30,31,32]. As a non-metallic photocatalyst, the atomically thin graphitic carbon-nitride nanosheets (CNs) are considered to be promising emerging photocatalysts because of their simple synthesis, high stability, and nontoxicity [6,24,27,28]. Although their conduction band and valence band position meet the requirements for overall water splitting, they can only respond to light of a wavelength below 419 nm owing to the large band gap of 3.06 eV, and therefore miss the most visible light [6,27,33,34,35]. Additionally, low photogenerated carrier separation efficiency and the quick recombination of photoinduced electron–hole pairs are still the key obstacles restricting the application of CNs.
To address these challenges, a composite of semiconductor photocatalytic materials and graphene systems can be used to broaden the absorption range of visible light and enhance the light absorption intensity of its materials [35,36,37,38,39,40,41,42,43]. Due to graphene’s metallic properties, the heterojunctions constructed are transformed into Schottky heterojunctions. However, as Schottky heterojunctions, the carriers are difficult to separate due to the large energy barrier at the interface, which further limits their practical application [44,45]. Therefore, determining the graphene materials that possess semiconductor properties is necessary.
Fortunately, graphene quantum dots (GQDs) as 0-dimensional nanomaterials have some special advantages, such as high dispersibility, a wide variety of active sites (edges, functional groups, dopants, etc.), and better tunability of the chemical and physical properties [46,47,48]. Therefore, the GQDs have garnered considerable interest in the sectors of the conversion and storage of energy, electrical/optical/chemical catalysis, among others. More importantly, GQDs have semiconductor properties due to their quantum confinement effect. Therefore, we constructed heterogeneous photocatalysts based on CNs and GQDs. The experimental characterization shows that the absorption edge of the sample is red-shifted, due to the introduction of the GQDs. When Pt is employed as a cocatalyst, the hydrogen production performance of the CNs/GQDs-3 reaches 4.99 mmol g−1 h−1, which is 9.62 times greater than that of the CNs. The creation of a CN heterojunction increases the usage of visible light and facilitates the separation of the photogenerated carriers, consequently considerably boosting the hydrogen production capacity of the catalyst.

2. Synthesis and Characterization

2.1. Preparation of CNs/GQDs Samples

Preparation of the CNs: First, 10 g of urea was put into a crucible that was covered with another crucible, then the crucibles were wrapped with tin foil and placed in a box furnace. At a heating rate of 0.5 °C min−1, the furnace temperature was raised to 550 °C in air, held for three hours; the bulk CN was obtained after cooling. Secondly, the bulk CN was ground into powders with a mortar, then 100 mg of the powder was placed in a large crucible and flattened. The crucible was put into a box furnace. At a heating rate of 5 °C min−1, the furnace temperature was raised to 520 °C in air, held for two hours, and the sample was then cooled to room temperature in the oven, and the graphitic carbon nitride nanosheets were obtained (CNs).
Preparation of the GQDs: A total of 2 g of the dried carbon block was weighed and then put into a reactor that containing 300 mL of 15 M concentrated nitric acid. Next, the solution from the previous step was maintained at 140 °C for 24 h for the reaction to occur and then raised to 180 °C to produce the dry powders. The product was dissolved in 1 L of distilled water and then the dispersion was centrifuged at 10,000 rpm for 30 min to obtain a supernatant. The large particles were filtered out of the supernatant, and the resulting dispersion was then freeze-dried to produce the gray GQDs powder.
Preparation of the CNs/GQDs samples: A total of 200 mL of distilled water was measured into a beaker and the pH was adjusted to four with hydrochloric acid. A total of 200 mg of CNs was added and stirred for 1 h to positively charge the surface of the CNs. The GQDs dispersion at a concentration of 1 mg/mL was added and mixed for 24 h to establish electrostatic adsorption between the GQDs and CNs. Then, the dispersion was centrifuged at 9000 rpm and repeated several times until the solution was neutral. The solution was then freeze-dried and the product was annealed in an argon atmosphere at 300 °C for 1 h. The samples were named CNs/GQDs-X (X = 1, 3, 5, X depending on the mass ratio of the GQDs to the CNs).

2.2. Characterization

The TEM was recorded on a JEM-2100F microscope (JEOL, Tokyo, Japan). The AFM and SKPM were measured by an atomic force microscope (OXFORD Cypher). The XRD data were measured by a D8+ Advance X-ray diffractometer (Bruker, Munich, Germany). The FTIR spectra were measured by a Nicolet+iS+50 Fourier Infrared spectrometer. The XPS measurements were recorded by a Thermo Scientific K-Alpha+ (ThermoFisher, Waltham, MA, USA). The UV-vis absorption data were performed on a Perkin Elmer Lambda UV-vis spectrophotometer. The PL spectra were measured by a 1J1-0015 spectrophotometer.

2.3. Electrochemical Measurements

The preparation of the working electrodes: A total of 5 mg of the CNs and CNs/GQDs-3 were dispersed in 5ml Alpha-terpineol, respectively. The dispersion was then sonicated for two hours to ensure a uniform slurry. Using a spatula to distribute the slurry uniformly over the 2.5 × 2.5 cm2 ITO glass electrodes. The electrodes were vacuum dried at 80 °C for 8 h to obtain the working electrodes. The tests were performed in a three-electrode system, utilizing a platinum sheet as the counter electrode, and using Ag/AgCl electrode as the reference electrode.

2.4. Photocatalytic Activity Measurement

A total of 25 mg of the sample was weighed and then distributed in 100 mL of deionized water which contained 10% TEOA. The H2PtCl6 with a mass fraction of 3% was added to the above dispersion as a co-catalyst. The dispersion was illuminated for 4 h with a 300 W xenon lamp (λ > 420 nm), and a data point was recorded every hour.
The apparent quantum efficiency (AQE) was measured using three LED lamps (420 nm, 550 nm, and 600 nm) and an optical power meter (Thorlabs), and was calculated based on the following equation:
AQE = N e N q × 100 % = 2 × M × N A × h × c S × P × t × λ
where Ne is the amount of reaction electrons; Np is the incident photons; M is the amount of H2 molecule; NA is Avogadro constant; h is the Planck constant; c is the speed of light; S is the irradiation area; P is the intensity of the irradiation; t is the photoreaction time; and λ is the wavelength of the monochromatic light.

3. Results

3.1. Morphological Characterization

The CNs were obtained by the deamination condensation of urea. The TEM result in Figure 1a shows that the CNs are flake-like and have a lateral dimension of about 1 μm. The thickness of the CNs ranges from 3 nm to 3.5 nm (Figure 1b). The graphene quantum dots (GQDs) were prepared by the oxidation-cutting method [46]. Figure 1c shows the morphology of the GQDs, which are about 5 nm in size (Figure S1, Supplementary Materials), uniformly distributed in the solution. After recombination, it can be observed from Figure 1d that the GQDs are adsorbed on the surface of the CNs, and the HRTEM image indicates that the GQDs have a lattice fringe spacing of 0.24 nm, which belongs to the (100) plane.

3.2. Microstructural and Optical Characterization

The XRD spectra are used to determine the microstructural changes in the samples (Figure 2a). The CNs displays two peaks located at around 13° and 27.6° due to the (100) reflection and (002) reflection, respectively. The peak intensities of the (002) and (100) planes increased with the increase in the recombination amount of the GQDs. It was reported that the CNs are layered nanosheets with a graphite-like phase, and the layers are connected by hydrogen bonds. However, when the GQDs adsorb to the CNs surface, they will adsorb to other CNs, which leads to the superposition of layered structures, which is also the reason for the increase in the (002) intensity of the interlayer peak. Thus, the bonding between the nanosheets is tighter, due to the existence of the electrostatic adsorption force. The number of layers is also increased after annealing (Figure S2, Supplementary Materials). The FTIR was measured to study the chemical bonds’ state. Figure 2b shows a peak at 809 cm−1 which was caused by the out-of-plane bending vibration of the heptazine rings. The C–N heterocycles stretching results in several peaks between 900 and 1800 cm−1. Meanwhile, the characteristic peaks between 3000–3400 cm−1 can be attributed to the N–H stretching vibrations. The FTIR characteristic peaks of the CNs are similar to a previous report [24]. The CNs/GQDs samples show the same peak positions as the CNs, and there is no new peak, indicating that the CNs/GQDs have the same chemical bonds as the CNs. The XPS C 1s spectra of the CNs, which were deconvoluted into two peaks, can be attributed to the C–C and N=C–N groups located at around 284.6 and 287.88 eV, respectively (Figure 2c). The CNs/GQDs sample show no obvious binding energy shifts, implying the same chemical states of the CNs and CNs/GQDs. Due to the large number of the C–C bonds in the GQDs, the peak area ratio of the C–C group to N=C–N group increased after the formation of the CNs/GQDs. The XPS N 1s spectra of CNs are shown in Figure 2d, with three species peaks located at 398.38, 399.25, and 400.54 eV, respectively. The signal situated at 398.38 eV is ascribed to the sp2-hybridized nitrogen C=N-C species. Meanwhile the other two peaks at 399.25 and 400.54 eV are caused by the NC3 and amino groups (NHx), respectively. The peak positions and the peak area ratio of the CNs/GQDs samples show almost no changes at all. The results of the XPS and FTIR indicate the same chemical states exist in both the CNs and CNs/GQDs.
The optical characteristics of the CNs and CNs/GQDs are characterized with UV-vis spectrum and PL spectrum. The CNs shows an absorption edge at 419 nm (Figure 2e). As a result, the CNs have trouble absorbing visible light in the 420–800 nm range. The absorption edges of the CNs/GQDs samples are red-shifted in comparison to CNs. It can be seen from Figure S3 (Supplementary Materials) that the band gap of CNs, CNs/GQDs-1, CNs/GQDs-3, and CNs/GQDs-5 are 3.073, 3.063, 3.058, and 3.055 eV, respectively, indicating that with the increase in the quantum dot loading, the band gap of the sample is also continuously decreasing. Figure 2f shows that the CNs have the highest emission peak at 438 nm (excited at 325 nm). The emission intensity of the CNs/GQDs decreased significantly with the increased GQDs, indicating the enhanced separation efficiency of the photoinduced electron–hole pairs.

3.3. Surface Potential Analysis

The Scanning Kelvin Probe Microscope (SKPM) was used to measure the surface potential of the CNs and CNs/GQDs in the dark and under visible light illumination to explore the photo-enhanced catalytic process. As shown in Figure 3a–c, the CNs have a ~28 mV surface potential in dark conditions, and it shows no significant change in the visible light irradiation. The negligible surface potential change indicates that the CNs respond poorly to visible light and the recombination of the photogenerated electron–hole pairs is significant. The CNs/GQDs-3 show a 57.37 mV surface potential in dark conditions, and it decreases by 16.53 mV under visible light illumination. Previous research has shown that a more negative surface-potential signal corresponds to a higher density of electrons [44,49]. The CNs/GQDs can thus promote the photogenerated carriers’ separation under illumination, and additional photogenerated electrons can participate in the reduction process.

3.4. Performance Characterization

The photoelectrochemical (PEC) properties were measured under visible light irradiation. As is shown in Figure 4a, the photocurrent response of the CNs/GQDs-3 is much larger than that of the CNs, and the EIS spectra in Figure 4b shows that the CNs/GQDs-3 sample shows a smaller arc radius compared with the CNs, indicating that the carriers are more easily transferred to the surface of the sample. The smaller impedance of CNs/GQDs-3 also contributes to the larger photocurrent response. To assess the photocatalytic activity of the samples, the H2 generation rate of CNs and CNs/GQDs were measured. Figure 4c shows that the H2 generation rate of CNs is 518.74 μmol g−1 h−1. The photocatalytic H2 evolution rate of CNs/GQDs-3 reaches 4.99 mmol g−1 h−1, which is 9.62 times greater than that of the CNs. Compared with the Pt-assisted g-C3N4-based photocatalysts that were reported so far, the CNs/GQDs samples show superior performance (Figure 4e; Table S1, Supplementary Materials). To study the wavelength dependent hydrogen generation for the CNs/GQDs-3, the hydrogen production rates at three wavelengths of 420, 550 and 600 nm were tested (Figure S4, Supplementary Materials). The AQE at 420 nm is 0.04%, which is the highest of the three wavelengths tested. To verify the stability of the photocatalyst, we tested the samples under visible light illumination for four cycles, taking a data point every hour. As shown in Figure 4d, after three cycles, the catalyst was not deactivated and still had good hydrogen evolution activity. After the test was completed, the sample was collected after the reaction and the XRD was performed, and the result shows that there was no change compared with the XRD before the reaction (Figure S5, Supplementary Materials), which indicates that the samples had good stability.

3.5. Mechanism Analysis

We determined the conduction band positions of the CNs and GQDs, using Mott–Schottky curves. Figure 5a shows the conduction band positions of the CNs and GQDs are −0.55 and −0.28 eV, considering the Ag/AgCl electrode, respectively. The ultraviolet photoelectron spectroscopy analysis results shows that the Fermi levels of the CNs and GQDs were 3.44 and 4.27 eV below the vacuum level, respectively (Figure 5b), indicating that the CNs had a higher Fermi-level position. Therefore, the electrons flow from the CNs to the GQDs during the photocatalytic process. The band gaps of the CNs and GQDs were 3.07 and 2.80 eV, respectively, as shown in Figure S6 (Supplementary Materials). Considering the energy band position analysis, the photocatalytic reaction mechanism of the CNs and the CNs/GQDs samples was proposed. In the absence of the GQDs loading, the photoexcited electron–holes recombined rapidly, which resulted in only a small number of electrons participating in the hydrogen production reaction. After the heterojunction formation, the electrons generated by illumination in the CN sample transferred to the GQDs due to the lower conduction band position of the metallic GQDs. The TEOA selectively adsorbed the holes, thus avoiding the recombination of the photogenerated electron–hole pairs. As a result, more of the electrons could participate in the hydrogen evolution reaction, and the hydrogen production rate of CNs/GQDs was significantly improved.

4. Conclusions

In summary, a unique CNs/GQDs Van der Waals heterojunction was successfully prepared, which was synthesized by the electrostatic self-assembly of the atomically thin CNs and 0D GQDs. The experimental characterizations indicate that the absorption range of the sample was red-shifted when the GQDs were introduced, and the CN/GQDs sample could absorb visible light for the photocatalytic reaction. Additionally, the SPV spectroscopy confirmed that introducing the GQDs in the CNs could promote the transport of photo-induced carriers in the melon chain, hence reducing recombination in the body. This is mainly because the heterojunctions constructed with the CNs are type II heterojunctions, due to the semiconducting properties of the GODs. Thanks to the introduction of 0D GQDs, the H2 evolution rate of CNs was enhanced.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ma15155390/s1. Figure S1: The TEM image of GQDs; Figure S2: The AFM image of the CNs/GQDs-3, and the curve is the corresponding height profile along the white line; Figure S3. The band gap patterns of CNs; CNs/GQDs-1; CNs/GQDs-3; and CNs/GQDs-5; Figure S4: Wavelength-dependent hydrogen generation for the CNs/GQDs-3 with 10 vol% of TEOA as a sacrificial donor; Figure S5. The XRD spectra of CNs/GQDs-3 after reaction; Figure S6: Plots of the transformed Kubelka–Munk function versus the light energy of (a) CNs; and (b) GQDs; Table S1. Hydrogen production capacity of CN-based catalysts.

Author Contributions

Conceptualization, Y.W. (Yong Wang), Z.R. and R.Y.; Data curation, Y.W. (Yong Wang), C.Z. and Y.W. (Yizhang Wu); Formal analysis, Y.W. (Yong Wang), C.Z., Y.L., D.Y., Y.Z., J.H. and W.H.; Funding acquisition, Y.W. (Yong Wang) and J.H.; Investigation, Q.L.; Methodology, Y.W. (Yong Wang), Y.Z. and Y.W. (Yizhang Wu); Project administration, R.Y.; Supervision, Y.W. (Yong Wang); Writing—original draft, Y.W. (Yong Wang), C.Z. and R.Y. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Natural Science Foundation of China (Grant No. 12104352 and 51973170), Fundamental Research Funds for the Central Universities (Grant No. XJS212208 and 2020BJ-56), and Foundation of State Key Laboratory of High-efficiency Utilization of Coal and Green Chemical Engineering (Grant No. 2022-K67), and the National Natural Science Foundation of Shaanxi Province under Grant No. 2019JCW-17 and 2020JCW-15.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Fujishima, A.; Honda, K. Electrochemical photolysis of water at a semiconductor electrode. Nat. Mater. 1972, 238, 37–38. [Google Scholar] [CrossRef] [PubMed]
  2. Linsebigler, A.; Lu, G.Q.; Yates, J.T., Jr. Photocatalysis on TiO2 surfaces: Principles, mechanisms, and selected results. Chem. Rev. 1995, 95, 735–738. [Google Scholar] [CrossRef]
  3. Liu, G.; Yang, H.G.; Pan, J.; Yang, Y.Q.; Lu, G.Q.; Cheng, H.M. Titanium dioxide crystals with tailored facets. Chem. Rev. 2014, 114, 9559–9612. [Google Scholar] [CrossRef] [PubMed]
  4. Zou, Z.G.; Ye, J.H.; Sayama, K.; Arakawa, H. Direct splitting of water under visible light irradiation with an oxide semiconductor photocatalyst. Nature 2001, 414, 625–627. [Google Scholar] [CrossRef]
  5. Ran, J.R.; Guo, W.W.; Wang, H.L.; Zhu, B.C.; Yu, J.G.; Qiao, S.Z. Metal-Free 2D/2D phosphorene/g-C3N4 van der waals heterojunction for highly enhanced visible-light photocatalytic H2 production. Adv. Mater. 2018, 30, 1800128. [Google Scholar] [CrossRef]
  6. Wang, L.; Zhao, X.; Lv, D.D.; Liu, C.W.; Lai, W.H.; Sun, C.Y.; Su, Z.M.; Xu, X.; Hao, W.C.; Dou, S.X.; et al. Promoted photocharge separation in 2D lateral epitaxial heterostructure for visible-light-driven CO2 photoreduction. Adv. Mater. 2020, 32, 2004311. [Google Scholar] [CrossRef]
  7. Shahabuddin, S.; Mehmood, S.; Ahmad, I.; Sridewi, N. Synthesis and characterization of 2D-WS2 incorporated polyaniline nanocomposites as photocatalyst for methylene blue degradation. Nanomaterials 2022, 12, 2090. [Google Scholar] [CrossRef]
  8. Borges, M.E.; Navarro, S.; Carmona, H.; Esparza, P. Natural volcanic material as a sustainable photocatalytic material for pollutant degradation under solar irradiation. Materials 2022, 15, 3996. [Google Scholar] [CrossRef] [PubMed]
  9. Krasnenko, V.; Rusevich, L.L.; Platonenko, A.; Mastrikov, Y.A.; Sokolov, M.; Kotomin, E.A. Water splitting on multifaceted SrTiO3 nanocrystals: Calculations of raman vibrational spectrum. Materials 2022, 15, 4233. [Google Scholar] [CrossRef] [PubMed]
  10. Kawai, T.; Sakata, T. Conversion of carbohydrate into hydrogen fuel by a photocatalytic process. Nature 1980, 286, 474–476. [Google Scholar] [CrossRef]
  11. Wang, Q.; Domen, K. Particulate photocatalysts for light-driven water splitting: Mechanisms, challenges, and design strategies. Chem. Rev. 2020, 120, 919–985. [Google Scholar] [CrossRef] [PubMed]
  12. Yao, T.T.; An, X.R.; Han, H.X.; Chen, J.Q.; Li, C. Photoelectrocatalytic materials for solar water splitting. Adv. Energy Mater. 2018, 8, 1800210. [Google Scholar] [CrossRef]
  13. Inoue, Y. Photocatalytic water splitting by RuO2-loaded metal oxides and nitrides with d0- and d10 -related electronic configurations. Energy Environ. Sci. 2009, 2, 364–386. [Google Scholar] [CrossRef]
  14. Wang, Z.; Inoue, Y.; Hisatomi, T.; Ishikawa, R.; Wang, Q.; Takata, T.; Chen, S.S.; Shibata, N.; Ikuhara, Y.; Domen, K. Overall water splitting by Ta3N5 nanorod single crystals grown on the edges of KTaO3 particles. Nat. Catal. 2018, 1, 756–763. [Google Scholar] [CrossRef]
  15. Shabalina, A.V.; Gotovtseva, E.Y.; Belik, Y.A.; Kuzmin, S.M.; Kharlamova, T.S.; Kulinich, S.A.; Vodyankina, O.V. Electrochemical study of semiconductor properties for bismuth silicate-based photocatalysts obtained via hydro/solvothermal approach. Materials 2022, 15, 4099. [Google Scholar] [CrossRef]
  16. Conte, F.; Rossetti, I.; Ramis, G.; Vaulot, C.; Hajjar-Garreau, S.; Bennici, S. Low metal loading (Au, Ag, Pt, Pd) photo-catalysts supported on TiO2 for renewable processes. Materials 2022, 15, 2915. [Google Scholar] [CrossRef]
  17. Irfan, M.; Shukrullah, S.; Naz, M.Y.; Ahmad, I.; Shoukat, B.; Legutko, S.; Alsaiari, M.A. Si/SiO2/Al2O3 supported growth of CNT forest for the production of La/ZnO/CNT photocatalyst for hydrogen production. Materials 2022, 15, 3226. [Google Scholar] [CrossRef]
  18. Tian, Z.L.; Zhang, P.F.; Qin, P.; Sun, D.; Zhang, S.N.; Guo, X.W.; Zhao, W.; Zhao, D.Y.; Huang, F.Q. Novel black BiVO4/TiO2-x photoanode with enhanced photon absorption and charge separation for efficient and stable solar water splitting. Adv. Energy Mater. 2019, 9, 1901287. [Google Scholar] [CrossRef]
  19. Mu, L.C.; Zhao, Y.; Li, A.L.; Wang, S.Y.; Wang, Z.L.; Yang, J.X.; Wang, Y.; Liu, T.F.; Chen, R.T.; Zhu, J.; et al. Enhancing charge separation on high symmetry SrTiO3 exposed with anisotropic facets for photocatalytic water splitting. Energy Environ. Sci. 2016, 9, 2463–2469. [Google Scholar] [CrossRef]
  20. Chen, X.J.; Wang, J.; Chai, Y.Q.; Zhang, Z.J.; Zhu, Y.F. Efficient photocatalytic overall water splitting induced by the giant internal electric field of a g-C3N4/rGO/PDIP Z-Scheme heterojunction. Adv. Mater. 2021, 33, 2007479. [Google Scholar] [CrossRef]
  21. Faraji, M.; Yousefi, M.; Yousefzadeh, S.; Zirak, M.; Naseri, N.; Jeon, T.H.; Choi, W.; Moshfegh, A.Z. Two-dimensional materials in semiconductor photoelectrocatalytic systems for water splitting. Energy Environ. Sci. 2019, 12, 59–95. [Google Scholar] [CrossRef]
  22. Tan, C.L.; Cao, X.H.; Wu, X.J.; He, Q.Y.; Yang, J.; Zhang, X.; Chen, J.Z.; Zhao, W.; Han, S.K.; Nam, G.H.; et al. Recent advances in ultrathin two-dimensional nanomaterials. Chem. Rev. 2017, 117, 6225–6331. [Google Scholar] [CrossRef] [PubMed]
  23. Liu, G.; Zhen, C.; Kang, Y.Y.; Wang, L.Z.; Cheng, H.M. Unique physicochemical properties of two-dimensional light absorbers facilitating photocatalysis. Chem. Soc. Rev. 2018, 47, 6410–6444. [Google Scholar] [CrossRef] [PubMed]
  24. Wang, Y.; Du, P.P.; Pan, H.Z.; Fu, L.; Zhang, Y.; Chen, J.; Du, Y.W.; Tang, N.J.; Liu, G. Increasing solar absorption of atomically thin 2D carbon nitride sheets for enhanced visible-light photocatalysis. Adv. Mater. 2019, 31, 1807540. [Google Scholar] [CrossRef]
  25. Peng, L.L.; Zhu, Y.; Chen, D.H.; Ruoff, R.S.; Yu, G.H. Two-dimensional materials for beyond-lithium-ion batteries. Adv. Energy Mater. 2016, 6, 1600025. [Google Scholar] [CrossRef]
  26. Zhang, M.W.; Wang, X.C. Two dimensional conjugated polymers with enhanced optical absorption and charge separation for photocatalytic hydrogen evolution. Energy Environ. Sci. 2014, 7, 1902–1906. [Google Scholar] [CrossRef]
  27. Niu, P.; Zhang, L.L.; Liu, G.; Cheng, H.M. Graphene-like carbon nitride nanosheets for improved photocatalytic activities. Adv. Funct. Mater. 2012, 22, 4763–4770. [Google Scholar] [CrossRef]
  28. Wang, Y.; Zhang, Y.; Di, M.Y.; Fu LPan, H.Z.; Zhang, K.Y.; Xu, Y.J.; Yan, S.C.; Zhang, C.F.; Du, Y.W.; Tang, N.J. Realization of ultrathin red 2D carbon nitride sheets to significantly boost the photoelectrochemical water splitting performance of TiO2 photoanodes. Chem. Eng. J. 2020, 396, 125267. [Google Scholar]
  29. Zhang, Y.; Wang, Y.; Di, M.Y.; Zhou, B.Y.; Xu, W.; Wu, N.D.; Wu, Y.Z.; Du, Y.W.; Zhong, W. Synergy of dopants and defects in ultrathin 2D carbon nitride sheets to significantly boost the photocatalytic hydrogen evolution. Chem. Eng. J. 2020, 385, 123938. [Google Scholar] [CrossRef]
  30. Xu, F.Y.; Meng, K.; Zhu, B.C.; Liu, H.B.; Xu, J.S.; Yu, J.G. Graphdiyne: A new photocatalytic CO2 reduction cocatalyst. Adv. Funct. Mater. 2019, 29, 1904256. [Google Scholar] [CrossRef]
  31. Li, X.D.; Sun, Y.F.; Xu, J.Q.; Shao, Y.J.; Wu, J.; Xu, X.L.; Pan, Y.; Ju, H.X.; Zhu, J.F.; Xie, Y. Selective visible-light-driven photocatalytic CO2 reduction to CH4 mediated by atomically thin CuIn5S8 layers. Nat. Energy 2019, 4, 690–699. [Google Scholar] [CrossRef]
  32. Zheng, Y.; Liu, J.; Liang, J.; Jaroniec, M.; Qiao, S.Z. Graphitic carbon nitride materials: Controllable synthesis and applications in fuel cells and photocatalysis. Energy Environ. Sci. 2012, 5, 6717–6731. [Google Scholar] [CrossRef]
  33. Wang, Y.; Xu, W.; Zhang, Y.; Wu, Y.Z.; Wang, Z.K.; Fu, L.; Bai, F.L.; Zhou, B.Y.; Wang, T.T.; Cheng, L.; et al. Introducing spin polarization into atomically thin 2D carbon nitride sheets for greatly extended visible-light photocatalytic water splitting. Nano Energy 2021, 83, 105783. [Google Scholar] [CrossRef]
  34. Wang, Y.; Guo, Y.L.; Wang, Z.K.; Fu, L.; Zhang, Y.; Xu, Y.J.; Yuan, S.J.; Pan, H.Z.; Du, Y.W.; Wang, J.L.; et al. Realization of strong room-temperature ferromagnetism in atomically thin 2D carbon nitride sheets by thermal annealing. ACS Nano 2021, 15, 12069–12076. [Google Scholar] [CrossRef]
  35. Wang, Y.; Zhang, Y.; Wang, Y.M.; Zeng, C.X.; Sun, M.; Yang, D.Y.; Cao, K.; Pan, H.Z.; Wu, Y.Z.; Liu, H.; et al. Constructing van der waals heterogeneous photocatalysts based on atomically thin carbon nitride sheets and graphdiyne for highly efficient photocatalytic conversion of CO2 into CO. ACS Appl. Mater. Interfaces 2021, 13, 40629–40637. [Google Scholar] [CrossRef]
  36. Pan, Z.M.; Zhang, G.G.; Wang, X.C. Polymeric carbon nitride/RGO/Fe2O3: All solid state z-scheme systems for photocatalytic overall water splitting. Angew. Chem. Int. Ed. 2019, 131, 7176–7180. [Google Scholar] [CrossRef]
  37. Xu, H.; Yi, J.; She, X.; Liu, Q.; Song, L.; Chen, S.M.; Yang, Y.C.; Song, Y.H.; Robert, V.; Lou, J.; et al. 2D heterostructure comprised of metallic 1T-MoS2/monolayer O-g-C3N4 towards efficient photocatalytic hydrogen evolution. Appl. Catal. B Environ. 2017, 220, 379–385. [Google Scholar] [CrossRef]
  38. Han, Y.Y.; Lu, X.L.; Tang, S.F.; Yin, X.P.; Wei, Z.W.; Lu, T.B. Water splitting: Metal-free 2D/2D heterojunction of graphitic carbon nitride/graphdiyne for improving the hole mobility of graphitic carbon nitride. Adv. Energy Mater. 2018, 8, 1870077. [Google Scholar] [CrossRef] [Green Version]
  39. Liu, J.; Yang, L.; Liu, N.; Han, Y.; Xing, Z.; Huang, H.; Lifshitz, Y.; Lee, S.T.; Zhong, J.; Kang, Z.H. Metal-free efficient photocatalyst for stable visible water splitting via a two-electron pathway. Science 2015, 46, 970–974. [Google Scholar] [CrossRef]
  40. Novoselov, K.S.; Mishchenko, A.; Carvalho, A.; Neto, A.C. 2D materials and van der waals heterostructures. Science 2016, 353, acc9439. [Google Scholar] [CrossRef] [Green Version]
  41. Wang, S.; Zhang, D.; Li, B.; Zhang, C.; Du, Z.G.; Yin, H.M.; Bi, X.F.; Yang, S.B. Ultrastable in-plane 1T–2H MoS2 heterostructures for enhanced hydrogen evolution reaction. Adv. Energy Mater. 2018, 8, 1801345. [Google Scholar]
  42. Si, Y.H.; Chen, W.M.; Shang, S.K.; Xia, Y.; Zeng, X.R.; Zhou, J.; Li, Y.Y. g-C3N4/Pt/BiVO4 nanocomposites for highly efficient visible-light photocatalytic removal of contaminants and hydrogen generation. Nanotechnology 2020, 31, 125706. [Google Scholar] [CrossRef] [PubMed]
  43. Yang, L.; Wang, X.; Wang, J.; Cui, G.M.; Liu, D.P. Graphite carbon nitride/boron-doped graphene hybrid for efficient hydrogen generation reaction. Nanotechnology 2018, 29, 345705. [Google Scholar] [CrossRef] [PubMed]
  44. Wang, Y.; Zeng, C.X.; Zhang, Y.; Su, R.; Yang, D.Y.; Wang, Z.K.; Wu, Y.Z.; Pan, H.Z.; Zhu, W.D.; Hu, W.; et al. Promoted photocarriers separation by straining in 2D/2D van der waals heterostructures for high-efficiency visible-light photocatalysis. Mater. Today Phys. 2022, 22, 100600. [Google Scholar] [CrossRef]
  45. You, B.; Tang, M.T.; Tsai, C.; Abild-Pedersen, F.; Zheng, X.L.; Li, H. Enhancing electrocatalytic water splitting by strain engineering. Adv. Mater. 2019, 31, 1807001. [Google Scholar] [CrossRef]
  46. Sun, Y.Y.; Zheng, Y.P.; Chen, J.; Zhang, W.L.; Tang, N.J.; Du, Y.W. Intrinsic magnetism of monolayer graphene oxide quantum dots. Appl. Phys. Lett. 2016, 108, 033105. [Google Scholar] [CrossRef]
  47. Cai, K.B.; Huang, H.Y.; Hsieh, M.L.; Chen, P.W.; Chiang, S.; Chang, S.H.; Shen, J.L.; Liu, W.R.; Yuan, C.T. Two-dimensional self-assembly of boric acid-functionalized graphene quantum dots: Tunable and superior optical properties for efficient eco-friendly luminescent solar concentrators. ACS Nano 2022, 16, 3994–4003. [Google Scholar] [CrossRef]
  48. Zahir, M.; Magri, P.; Luo, W.; Gaumet, J.J.; Pierrat, P. Recent advances on graphene quantum dots for electrochemical energy storage devices. Energy Environ. Mater. 2022, 5, 201–214. [Google Scholar] [CrossRef]
  49. Han, Q.T.; Bai, X.W.; Man, Z.; He, H.; Li, L.; Hu, J.; Alsaedi, A.; Hayat, T.; Yu, Z.; Zhang, W.; et al. Convincing synthesis of atomically thin, single-crystalline InVO4 sheets toward promoting highly selective and efficient solar conversion of CO2 into CO. J. Am. Chem. Soc. 2019, 141, 4209–4213. [Google Scholar] [CrossRef]
  50. Hong, J.D.; Wang, Y.S.; Wang, Y.B.; Zhang, W.; Xu, R. Noble-metal-free NiS/C3N4 for efficient photocatalytic hydrogen evolution from water. ChenSusChem 2013, 6, 2263–2268. [Google Scholar] [CrossRef]
  51. Yu, J.G.; Wang, S.H.; Cheng, B.; Lin, Z.; Huang, F. Noble Metal-free Ni(OH)2/g-C3N4 composite photocatalyst with enhanced visible-light photocatalytic H2-production activity. Catal. Sci. Technol. 2013, 3, 1782–1789. [Google Scholar] [CrossRef]
  52. Zhou, W.; Jia, T.; Zhang, D.Q.; Zheng, Z.K.; Hong, W.; Chen, X.D. The enhanced co-catalyst free photocatalytic hydrogen evolution and stability based on indenofluorene-containing donor-acceptor conjugated polymer dots/g-C3N4 nanosheets heterojunction. Appl. Catal. B Environ. 2013, 259, 118067. [Google Scholar] [CrossRef]
  53. Liu, C.Y.; Huang, H.W.; Ye, L.Q.; Yu, S.X.; Tian, N.; Du, X.; Zhang, T.R.; Zhang, Y.H. Intermediate-mediated strategy to horn-like hollow mesoporous ultrathin g-C3N4 tube with spatial anisotropic charge separation for superior photocatalytic H2 evolution. Nano Energy 2017, 41, 738–748. [Google Scholar] [CrossRef]
  54. Liu, Q.Q.; Shen, J.Y.; Yu, X.H.; Yang, X.F.; Liu, W.; Yang, J.; Tang, H.; Xu, H.; Li, H.M.; Li, Y.Y.; et al. Unveiling the origin of boosted photocatalytic hydrogen evolution in simultaneously (S, P, O)-codoped and exfoliated ultrathin g-C3N4 nanosheets. Appl. Catal. B Environ. 2017, 248, 84–94. [Google Scholar] [CrossRef]
  55. Tian, N.; Zhang, Y.H.; Li, X.W.; Xiao, K.; Du, X.; Dong, F.; Waterhouse, G.; Zhang, T.R.; Huang, H.W. Precursor-reforming protocol to 3D mesoporous g-C3N4 established by ultrathin self-doped nanosheets for superior hydrogen evolution. Nano Energy 2017, 38, 72–81. [Google Scholar] [CrossRef]
  56. Ma, L.T.; Fan, H.Q.; Fu, K.; Lei, S.H.; Hu, Q.Z.; Huang, H.T.; He, G.P. Protonation of graphitic carbon nitride (g-C3N4) for an electrostatically self-assembling carbon@g-C3N4 core−shell nanostructure toward high hydrogen evolution. ACS Sustain. Chem. Eng. 2017, 5, 7093–7103. [Google Scholar] [CrossRef]
  57. Yuan, J.L.; Liu, X.; Tang, Y.H.; Zeng, Y.X.; Wang, L.L.; Zhang, S.Q.; Cai, T.; Liu, Y.T.; Luo, S.L.; Pei, Y.; et al. Positioning cyanamide defects in g-C3N4: Engineering energy levels and active sites for superior photocatalytic hydrogen evolution. Appl. Catal. B Environ. 2018, 237, 24–31. [Google Scholar] [CrossRef]
  58. Yang, S.B.; Gong, Y.J.; Zhang, J.S.; Zhan, L.; Ma, L.L.; Fang, Z.Y.; Vajtai, R.; Wang, X.C.; Ajayan, P. Exfoliated graphitic carbon nitride nanosheets as efficient catalysts for hydrogen evolution under visible light. Adv. Mater. 2013, 25, 2452–2456. [Google Scholar] [CrossRef]
Materials 15 05390 g001 550
Figure 1. (a) TEM image of CNs; (b) The atomic force microscope image of CNs, and the white inset is the corresponding height profile along the white line; (c) TEM image of GQDs; and (d) High resolution transmission electron microscope (HRTEM) image of CNs/GQDs-3. The red circle and the inset are the location and magnification of GQDs, respectively.
Figure 1. (a) TEM image of CNs; (b) The atomic force microscope image of CNs, and the white inset is the corresponding height profile along the white line; (c) TEM image of GQDs; and (d) High resolution transmission electron microscope (HRTEM) image of CNs/GQDs-3. The red circle and the inset are the location and magnification of GQDs, respectively.
Materials 15 05390 g001
Materials 15 05390 g002 550
Figure 2. (a) The XRD images of CNs and CNs/GQDs; (b) The FTIR spectrum of CNs and CNs/GQDs; The XPS spectra of CNs and CNs/GQDs-3, (c) C 1 s track and (d) N 1s track; (e) The UV-vis spectrum of CNs and CNs/GQDs; and (f) The PL spectrum of CNs and CNs/GQDs.
Figure 2. (a) The XRD images of CNs and CNs/GQDs; (b) The FTIR spectrum of CNs and CNs/GQDs; The XPS spectra of CNs and CNs/GQDs-3, (c) C 1 s track and (d) N 1s track; (e) The UV-vis spectrum of CNs and CNs/GQDs; and (f) The PL spectrum of CNs and CNs/GQDs.
Materials 15 05390 g002
Materials 15 05390 g003 550
Figure 3. The surface potential of CNs in different conditions, (a) in the dark and (b) under illumination; (c) The surface potential curves along the white lines in (a,b). The surface potential of CNs/GQDs-3 (d) in the dark and (e) under illumination; (f) The surface potential along the white lines in (d,e).
Figure 3. The surface potential of CNs in different conditions, (a) in the dark and (b) under illumination; (c) The surface potential curves along the white lines in (a,b). The surface potential of CNs/GQDs-3 (d) in the dark and (e) under illumination; (f) The surface potential along the white lines in (d,e).
Materials 15 05390 g003
Materials 15 05390 g004 550
Figure 4. The photoelectrochemical (PEC) properties of CNs and CNs/GQDs-3. (a) Photocurrent and (b) electrochemical impedance spectroscopy (EIS) curves; (c) The H2 production rate of CNs and CNs/GQDs with Pt assistance (λ > 420 nm); (d) Cycling test curve of CNs/GQDs-3; (e) Hydrogen production capacity of CN-based catalysts [50,51,52,53,54,55,56,57,58].
Figure 4. The photoelectrochemical (PEC) properties of CNs and CNs/GQDs-3. (a) Photocurrent and (b) electrochemical impedance spectroscopy (EIS) curves; (c) The H2 production rate of CNs and CNs/GQDs with Pt assistance (λ > 420 nm); (d) Cycling test curve of CNs/GQDs-3; (e) Hydrogen production capacity of CN-based catalysts [50,51,52,53,54,55,56,57,58].
Materials 15 05390 g004
Materials 15 05390 g005 550
Figure 5. (a) Mott–Schottky curves of CNs and GQDs; (b) Ultraviolet photoelectron spectroscopy (UPS) of CNs and GQDs. The photocatalytic mechanism of (c) CNs and (d) CNs/GQDs.
Figure 5. (a) Mott–Schottky curves of CNs and GQDs; (b) Ultraviolet photoelectron spectroscopy (UPS) of CNs and GQDs. The photocatalytic mechanism of (c) CNs and (d) CNs/GQDs.
Materials 15 05390 g005
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Wang, Y.; Zeng, C.; Liu, Y.; Yang, D.; Zhang, Y.; Ren, Z.; Li, Q.; Hao, J.; Hu, W.; Wu, Y.; et al. Constructing Heterogeneous Photocatalysts Based on Carbon Nitride Nanosheets and Graphene Quantum Dots for Highly Efficient Photocatalytic Hydrogen Generation. Materials 2022, 15, 5390. https://doi.org/10.3390/ma15155390

AMA Style

Wang Y, Zeng C, Liu Y, Yang D, Zhang Y, Ren Z, Li Q, Hao J, Hu W, Wu Y, et al. Constructing Heterogeneous Photocatalysts Based on Carbon Nitride Nanosheets and Graphene Quantum Dots for Highly Efficient Photocatalytic Hydrogen Generation. Materials. 2022; 15(15):5390. https://doi.org/10.3390/ma15155390

Chicago/Turabian Style

Wang, Yong, Chengxin Zeng, Yichen Liu, Dingyi Yang, Yu Zhang, Zewei Ren, Qikun Li, Jian Hao, Wen Hu, Yizhang Wu, and et al. 2022. "Constructing Heterogeneous Photocatalysts Based on Carbon Nitride Nanosheets and Graphene Quantum Dots for Highly Efficient Photocatalytic Hydrogen Generation" Materials 15, no. 15: 5390. https://doi.org/10.3390/ma15155390

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop