Tunable Luminescence and Energy Transfer of Sr3B2O6:Ce3+, Sm3+ Phosphors with Potential Anti-Counterfeiting Applications
Previous Article in Journal
Energy-Resolved Ultrafast Spectroscopic Investigation on the Spin-Coupled Electronic States in Multiferroic Hexagonal HoMnO3
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 15
10.3390/ma15155187
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Ag Nanocluster-Enhanced Scintillation Properties of Borophosphate Glasses Doped with CsPbBr3 Quantum Dots

by
Ying Du
1,2,
Lu Deng
1 and
Danping Chen
1,*
1
Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China
2
Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China
*
Author to whom correspondence should be addressed.
Materials 2022, 15(15), 5187; https://doi.org/10.3390/ma15155187
Submission received: 26 June 2022 / Revised: 14 July 2022 / Accepted: 23 July 2022 / Published: 26 July 2022
(This article belongs to the Special Issue Optical Properties of Transparent Ceramics)
Browse Figures
Versions Notes

Abstract

:
A novel and effective method to improve scintillation properties of glass-ceramics, such as intensity enhancement and decay-time shortening, is reported in this work. Compared with crystal scintillators, glass scintillators always have the problems of low efficiency and long decay; how to solve them has always been a scientific puzzle in the field of scintillation glass-ceramics. The plasma enhancement effect can be predicted to solve the above problems. Ag+ ions were diffused into glasses by ion exchange, and then Ag nanoparticles and CsPbBr3 quantum dots were formed by heat treatment. The structure of the CsPbBr3 perovskite consists of a series of shared corner PbBr6 octahedra with Cs ions occupying the cuboctahedral cavities. By using Ag and the plasma resonance effect, the photoluminescence intensity of CsPbBr3 quantum dot glasses was enhanced by 3 times, its radioluminescence intensity increased by 6.25 times, and its decay time was reduced by a factor of more than one. Moreover, the mechanism of photoluminescence and radioluminescence enhanced by Ag and plasma was discussed based on the experimental results and finite-difference time-domain method. We concluded that the increase in radioluminescence intensity was related to plasma enhancements and the energy exchange between Ag nanoclusters and CsPbBr3 quantum dots. Doping Ag is a valid means to improve the scintillation luminescence of CsPbBr3 quantum dot glasses, which can be applied in the field of scintillation.

1. Introduction

Scintillation materials can absorb ionizing radiation and emit photons in the visible or ultraviolet range. They are widely used in radiation detection applications, including medical diagnosis, safety inspection, industrial detection, basic scientific research, and radiation dosimetry [1,2,3,4,5]. A good scintillator should have a high light yield, fast decay time, high density, and low cost. Scintillation glasses have received considerable attention because they have low production costs and good optical uniformity. They can be prepared in large sizes and various shapes, such as being drawn into optical fibers [6,7,8,9]. The radioluminescence properties of Ce3+, Tb3+, Pr3+, Eu2+, and Yb2+ in various glasses have been extensively studied [10,11,12,13,14]. Except for Ce3+, the fluorescence lifetimes of the other ions are too long to be used as fast scintillation materials. Thus, Ce3+, which has the advantages of a nanosecond decay time, high light yield, and radiation resistance, has attracted the most attention and has been researched extensively. However, because of the charge migration quenching effect problem, low-density scintillation glasses doped with Ce3+ have high luminescence efficiency, while high-density glasses have low luminescence efficiency [15]. Hence, finding new scintillation luminescence centers to replace Ce3+ has become a critical issue. Cesium lead halide, CsPbX3 (X = Cl, Br, I), quantum dots (QDs) have attracted considerable attention because of their remarkable optoelectronic properties. In addition, some theoretical studies on CsPbX3 QDs by using first-principles calculations have also accomplished a great many achievements and laid the background for future experimental works. These theoretical studies have helped, directed, predicted and supported on important optics, luminescence properties, and structural features of CsPbX3 QDs [16,17]. However, their poor stability limits their practical applications [18,19]. Because a glass matrix can effectively prevent the degradation of metal halide perovskites, the stability of QDs embedded in glasses is significantly improved while still exhibiting good optical properties. Particularly, the luminescence of CsPbBr3 QDs in borophosphate glass at a temperature range of about 300 K to 500 K is stable in previous study [20]. To date, CsPbX3 perovskite QDs have been synthesized in low melting point phosphate oxyfluoride and borophosphate glasses [20,21], but the scintillation luminescence intensity of CsPbX3 QD-doped glasses is very low. This is because the size of the QDs is too small, and there are several defects on their surface. These defects act as recombination centers of electron-hole pairs generated by high-energy rays, thereby terminating energy transfer from electron-hole pairs to QDs. Therefore, improving the scintillation luminescence intensity of CsPbX3 QDs in glasses and reducing their fluorescence lifetimes are serious challenges for developing new scintillation glass-ceramics.
Luminescence properties of some materials can be enhanced by local surface plasmon effects caused by precious metal nanoparticles (NPs) [22,23]. Thus, it is imperative to introduce plasmonic nanostructures into glasses containing CsPbX3 QDs to improve their luminescence. Besides, macro-scale metal materials and their corresponding large-sized NPs will not produce fluorescent emission, but when the number of atoms or ions that make up the particles is reduced to a certain extent, nanoclusters (NCs) with discrete energy level structures and luminescence properties will be formed. These NCs do not have a complete lattice structure. Moreover, it is worth noting that the luminescence properties of NCs are closely related to their size distribution. As the number of atoms or ions that make up NCs increases (that is, the size of NCs increases), their excitation and emission spectra are redshifted, implying that NCs have size-dependent tunable luminescence properties [24,25,26]. One of the conditions for achieving resonance energy transfer is that the emission spectrum of the sensitizer and the excitation spectrum of the activator effectively overlap. Hence, how to flexibly and effectively regulate the emission band of metal NCs to achieve high-efficiency energy transfer for the activator is of great significance. Ag NPs can be introduced into glass in different ways. Compared with other methods, ion exchange has the advantages of low-cost, large-scale production, uniform particle distribution, and increased doping [27]. Xu et al. [28] had reported that the presence of these Ag-species resulted in enhanced photoluminescence total intensity by 5 times for the CsPbBr3 QD-doped glasses. Zhang et al. [29] had found that the 0.1 molar ratio Ag2O-doped CsPbBr3 quantum dot glasses sample had a photoluminescence intensity 2.37 times than the undoped sample. However, there is no report on the enhancement of scintillation luminescence of CsPbBr3 quantum dot glasses by Ag nanoclusters in the known literature. In this study, colorless and transparent borophosphate glasses were successfully prepared by melt-quenching. Appropriate ion exchange and heat-treatment processes were used to form Ag NPs and CsPbBr3 QDs with uniform particle sizes inside the glasses. Then, the photoluminescence and radioluminescence properties were measured and analyzed. Finally, the influence of the Ag NP content in glasses on the luminescence performance of CsPbBr3 QDs was simulated using the finite-difference time-domain (FDTD) method. Compared to other studies, the superiority, critical improvement, and novelty of the work lies in Ag plasma-enhanced scintillation luminescence of CsPbBr3 quantum dot glasses and reduced their fluorescence decay.

2. Experimental Procedures

2.1. Glass Composition and Preparation

As shown in Figure 1, borophosphate glasses with a composition of 15P2O5-5Na2O-5K2O-10ZnO-10Al2O3-40B2O3-7Cs2O-3PbBr2-5NaBr (PG, the composition is expressed in mol.%) were prepared using the melt-quenching method. These glasses were proven to have excellent chemical stability and used for three-dimensional direct lithography of stable perovskite nanocrystals [21,30]. Starting materials were NaPO3, KPO3, ZnO, Al2O3, Al(PO3)3, H3BO3, Cs2CO3, PbBr2, and NaBr powders (analytical purity). They were thoroughly mixed in appropriate proportions and placed in covered corundum crucibles in 30 g batches. The melting conditions were 900 °C for 20 min, after which the glass melts were poured into a preheated stainless-steel plate. Each glass was annealed at 300 °C for 2 h in a muffle furnace to release the inner stress and then slowly cooled to room temperature. All obtained glass samples were cut and polished to a regular size of 10 × 10 × 2 mm3 for subsequent experiments.
Processed PG glasses were immersed in AgNO3:NaNO3 molten salts with different molar concentrations and heated at 360 °C for 4 h in a muffle furnace. The AgNO3 concentrations used were 0.25, 0.5, 1.0, 1.5, and 3.0 mol.%. After ion exchange, glass samples were washed with absolute ethanol and deionized water to remove residual nitrate from their surfaces. The obtained glass samples were denoted as IXP-0.25 Ag, IXP-0.5 Ag, IXP-1.0 Ag, IXP-1.5 Ag, and IXP-3.0 Ag. According to previous work [20], the PG glass transition temperature Tg was about 411 °C and the crystallization peak temperature Tp was about 555 °C. Generally, the heat-treatment temperature of glass-ceramic is selected between the Tg and the Tp. Thus, the samples were then heated at 430 °C for 3 h in a muffle furnace to promote the formation of CsPbBr3 QDs and Ag NPs. Finally, the obtained glass-ceramics samples are denoted as HTP-0.25 Ag, HTP-0.5 Ag, HTP-1.0 Ag, HTP-1.5 Ag, and HTP-3.0 Ag. For comparison, a PG glass was directly heated at 430 °C for 3 h, and the obtained glass sample was denoted as HTP-0 Ag.

2.2. Characterization of Glass Samples

X-ray diffraction (XRD) patterns of glass samples were recorded on a Ultima IV X-ray diffractometer of Rigaku (Tokyo, Japan) using Cu Kα radiation, and the test range was 10–90° in steps of 10 °/min. X-ray photoelectron spectroscopy (XPS) spectra of glass samples were obtained using a K-Alpha X-ray photoelectron spectrometer of Thermal Fisher (Walthamm, MA, USA) and the bulk samples were polished on both sides. Before testing, the surface contaminants of glass samples were ultrasonically cleaned with ethanol, and these glasses were tested after drying. The microstructures of glass samples were observed using a JEOL 2100F transmission electron microscope (TEM) of JEOL (Tokyo, Japan) operated at an accelerating voltage of 200 kV and the glass samples were ground into powders, then placed in ethanol and sonicated for half an hour. Elemental distribution on glass sample surfaces was measured using a JXA-8230 electron probe microanalyzer (EPMA) of Japan and the bulk samples were polished on both sides and processed into flakes with a size of 10 × 10 × 1 mm3. The surface of glasses was cleaned and then carbonized. The Raman spectra of samples were tested using an InVia model Raman microscope of Thermo Fisher from (Walthamm, MA, USA), which excitation light source was a 785 nm argon-ion laser, the test range was 100–1000 cm−1, and the grating resolution was 1800 bars/mm. Absorption spectra were recorded using a Lambda 950 UV-Vis-NIR spectrophotometer of Perkin-Elmer from (Walthamm, MA, USA). Excitation and emission spectra and fluorescence lifetimes of glass samples were obtained using a FLS920 spectrophotometer of Edinburgh Instruments (Livingston, UK). Photoluminescence quantum yields (PLQYs), defined as the ratio of emitted photons to absorbed photons, were determined using a spectrofluorometer equipped with an 8 cm integrating sphere and a Xe lamp as the excitation source. X-ray-excited radioluminescence spectra were measured using an X-ray tube (Mo anode, 100 kV, 1 mA) with the SBP-300 fluorescence spectrometer of Zolix (Beijing, China).

3. Results and Discussion

The purpose of the study is to improve the scintillation performance of CsPbBr3-QD-doped glasses. The research structure of the work including sample preparation, structure characterization, property measuring, and mechanism investigation is shown in Figure 2.

3.1. XRD Patterns of PG and CsPbBr3 QD-Doped Glasses Containing Ag NPs

The XRD patterns of the PG glass and CsPbBr3 QD-doped glasses containing Ag NPs are shown in Figure 3. PG glass exhibits a typical amorphous structure, whereas distinct diffraction peaks gradually appear in CsPbBr3 QD-doped glasses containing Ag NPs. These main diffraction peaks were consistent with the (110), (200), (211), and (220) crystal planes of the cubic CsPbBr3 crystal (PDF #54-0752). Therefore, it can be inferred that CsPbBr3 crystals were successfully precipitated in the glasses after heat treatment. The XRD results also revealed that the addition of a small amount of Ag was favorable for the crystallization of CsPbBr3 QDs. However, as the concentration of AgNO3 was increased, the intensity of the diffraction peaks decreased, implying that the crystal quality of CsPbBr3 decreased. In addition, with the increase in AgNO3 concentration, the diffraction peaks of CsPbBr3 QD-doped glasses containing Ag NPs shifted to higher angles, indicating a decrease in interplanar spacing of crystal lattices. This may be caused by the partial replacement of Cs+ by Ag+ ions.

3.2. XPS Spectra of PG and CsPbBr3 QD-Doped Glasses Containing Ag NPs

The XPS spectra of the HTP-0 Ag, HTP-0.25 Ag, HTP-1.0 Ag, and HTP-3.0 Ag glasses are shown in Figure 4. The binding energy was calibrated by assuming C1s binding energy of 284.6 eV. Figure 4b–d show that CsPbBr3 QD-doped glasses containing Ag NPs have two prominent peaks near 367 and 373 eV, corresponding to the Ag 3d5/2 and Ag 3d3/2, respectively. According to the relevant literature, the approximately binding energy of 367–368 eV is attributed Ag 3d5/2 core shell of Ag+. The binding energy of 373–374 eV is attributed Ag 3d3/2 of metallic Ag [31,32]. Since the XPS binding energy of Ag NPs is slightly higher than that of Ag+ ions [33,34], both of them may be present. Compared with the y-axis of Figure 4b–d, the intensity of the two signal peaks increased with AgNO3 concentration, which indicates that the Ag NPs and Ag+ ion content in the glasses increased. Moreover, the binding energy of Ag 3d of CsPbBr3 QD-doped glass also increased with the AgNO3 concentration, implying that the proportion of Ag NPs increased.

3.3. TEM and EPMA Images of CsPbBr3 QD-Doped Glasses Containing Ag NPs

The microstructure of CsPbBr3 QD-doped glasses containing Ag NPs was further characterized to confirm the successful precipitation of Ag NPs and CsPbBr3 QDs in the glasses. The TEM image of the HTP-1.0 glass (Figure 5a) demonstrates that numerous nanoparticles are evenly distributed in the glass matrix. Moreover, the high-resolution transmission electron microscopy (HRTEM, Figure 5b,c) confirms their single-crystal and highly crystalline nature with distinctly resolved lattice fringes. Meanwhile, a typical interplanar spacing of the (200) plane of an individual CsPbBr3 particle is 2.91 Å, while that of the (100) plane of Ag is 2.5 Å. In addition, as shown in Figure 5b, some CsPbBr3 QDs are surrounded by Ag NPs, which intuitively proves that the localized plasmonic effect generated by Ag NPs has an effect on CsPbBr3 QDs. Overall, the presence of both CsPbBr3 QDs and Ag NPs in glasses was revealed by TEM images. The selected area electron diffraction (SAED) patterns (Figure 5d,e) correspond to the diffraction images of the (111) plane of the CsPbBr3 crystal and the (100) plane of the Ag crystal.
Furthermore, the elemental maps of Cs, Pb, Br, and Ag on the surface of the HTP-1.0 Ag are shown in Figure 6a–d. Figure 6a–c shows that the distributions of Cs, Pb, and Br are relatively uniform in the same surface area, which indicates that these elements are uniformly dispersed in the glass. It further confirms that the CsPbBr3 QDs are uniformly distributed in the glass. Due to Br volatility, its content in the same area is far lower than that of Cs and Pb. However, as shown in Figure 6d, the content of Ag decreased in some areas, which indicates that after a long period of ion exchange, Ag+ ions diffused inside the glass. The depths of the Ag+ ions in HTP-0.5 Ag, HTP-1.0 Ag, and HTP-3.0 Ag were also measured (Figure 6e–g). The depth of Ag+ ions entering glasses was approximately ten to tens of micrometers from the glass surface, and the higher the concentration of AgNO3, the deeper the ions penetrated the glasses and the greater the content of Ag+ ions. The EPMA test results showed that the Ag element was on the surface and inside of glasses after ion exchange, and then, after heat treatment, Ag NCs would be formed on the surface and inside of glasses. Such overall crystallization glass-ceramics are beneficial for commercial applications.

3.4. Raman Spectra of CsPbBr3 QD-Doped Glasses Containing Ag NPs

The Raman spectra of CsPbBr3 QD-doped glasses containing Ag NPs under a 785 nm laser excitation are shown in Figure 7a. The peak at 126 cm−1 gradually evolved for CsPbBr3 QD-doped glasses containing Ag NPs, corresponding to the second-order phonon mode of the [PbBr6]4− octahedron [35,36]. This is another confirmation of the CsPbBr3 QD formation. Moreover, with an increase in the AgNO3 concentration, the vibration peak intensity of the [PbBr6]4− octahedron tends to first increase and then decrease. When the concentration of AgNO3 is 1.0 mol.%, the peak at 126 cm−1 was the strongest. Compared with the HTP-0 Ag (without ion exchange), the peak intensity at 126 cm−1 of HTP-1.0 Ag increased by ca. 10 times. This may be due to the interaction between the surface plasmon resonance absorption effect of Ag NPs and CsPbBr3 QDs. Surface plasmons are ideal carriers for enhancing Raman scattering. Moreover, the energy of the light electric field is localized by Ag NPs within a very small area near the surface. Because the intensity of the Raman signal is proportional to the fourth power of the local electric field amplitude [37,38], the Raman signal peaks of CsPbBr3 crystals around Ag NPs are significantly enhanced. In the past, it was difficult to test the Raman peak of [PbBr6]4− in CsPbBr3 QD-doped glasses. After adding Ag, the Raman peak intensity of [PbBr6]4− could be significantly enhanced, which also reflected that Ag mainly entered around the quantum dots rather than around the glass phase, because the Raman peak intensity of the glass phase was not enhanced.

3.5. Photoluminescence Properties of CsPbBr3 QD-Doped Glasses Containing Ag NPs

The absorption spectra of PG and CsPbBr3 QD-doped glasses containing Ag NPs are shown in Figure 8a. The PG and HTP-0 Ag glasses are highly transparent in the visible range. The small absorption shoulder peaks of HTP-0 Ag near 515 nm were induced by CsPbBr3 QDs. In addition, CsPbBr3 QD-doped glasses containing Ag NPs exhibited no characteristic absorption peaks of Ag NPs. This may be because the absorption of QDs in CsPbBr3 QD-doped glass is too strong, resulting in the masking of the plasmonic absorption resonance peaks. Therefore, the absorption spectrum of HTB-1.0 Ag was measured (Figure S1). It shows the characteristic absorption peaks of Ag NPs in the 400–500 nm range. Compared with HTP-0 Ag, the absorption intensity of CsPbBr3 QD glasses containing Ag NPs significantly increased in the 500–550 nm range. This may be because the absorption ranges of Ag NPs and CsPbBr3 QDs coincide, and the surface plasmon resonance effect caused by Ag NPs significantly enhances the absorption of CsPbBr3 QDs surrounding the Ag NPs. In addition, according to the XRD results, the significant increase in the absorption intensity of CsPbBr3 QD glasses containing Ag NPs in the range of 500–550 nm may be also related to the substitution of Cs+ with Ag+ ions.
The fluorescence spectra of PG and CsPbBr3 QD-doped glasses containing Ag NPs under an excitation of 420 nm are shown in Figure 8b. All the CsPbBr3 QD-doped glasses containing Ag NPs exhibited a narrow-band emission of CsPbBr3 QD exciton recombination near 520 nm, which further proves the successful crystallization of CsPbBr3 particles. As the concentration of AgNO3 increased, the PL intensity of CsPbBr3 QD-doped glasses containing Ag NPs first increased and then decreased. When the concentration of AgNO3 was 1.0 mol.%, the PL intensity was the strongest. Compared to HTP-0 Ag, the photoluminescence intensity of HTP-1.0 Ag located at approximately 520 nm increased by approximately three times. This phenomenon can be explained by the strong coupling between the local surface plasmon resonance absorption of Ag NPs and the excitation light of 420 nm, which enhances the photoluminescence of CsPbBr3 QDs. It is well known that the intensity of plasmon resonance peaks depends on the concentration of the metal NPs in the glass matrix. With an increase in the Ag NP content in the glasses, the distance between the Ag nanostructures decreased and their interaction increased, which produced a local electric field and contributed to the photoluminescence enhancement. However, with a further increase in the Ag NP content, the PL intensity of the CsPbBr3 QDs decreased. This may be due to the following two reasons: (i) excessive Ag NPs inhibit the growth of CsPbBr3 QDs, and (ii) the plasmon absorption of excessive Ag NPs becomes a non-radiative relaxation pathway for photogenerated charge carriers. In addition, with the increase in AgNO3 concentration, the absorption cut-off wavelengths and the emission center wavelengths of CsPbBr3 QD glasses containing Ag NPs were first redshifted and then blueshifted. This is because adding a small amount of Ag can act as a nucleating agent to facilitate the crystallization of CsPbBr3 crystals. The increase in the size of the QDs causes a redshift in the absorption and emission spectra. However, as the concentration of AgNO3 was further increased, the absorption and emission spectra of CsPbBr3 QD glasses containing Ag NPs showed a blue shift, which implies that the grain size of CsPbBr3 decreased. There are two possible reasons for this. First, the mixed alkali effect caused by the addition of Ag+ inhibits the migration of Cs+ ions, making it difficult for CsPbBr3 QDs to grow. Second, a large number of Ag NPs enter the glasses, and too many crystal nucleating agents form too many crystallites, suppressing the growth of CsPbBr3 crystal grains. To further explore the photoluminescence properties of CsPbBr3 QD glasses containing Ag NPs, the fluorescence spectra of IXP-1.0 Ag under different heat-treatment times are shown in Figure 8c. The photoluminescence intensity of IXP-1.0 Ag 4 h increases approximately 2.2 times compared to that of the HTP-1.0 Ag. This indicates that the photoluminescence performance of CsPbBr3 QD-doped glasses containing Ag NPs can also be improved by precisely adjusting the heat-treatment process.
The PLQYs of the CsPbBr3 QD-doped glasses containing Ag NPs are shown in Figure 8d. As the concentration of AgNO3 increased, the PQLYs of the CsPbBr3 QD-doped glasses first increased and then decreased. HTP-1.0 Ag had a relatively high PLQY value. This can be attributed to changes in the size and quality of the CsPbBr3 crystals. Compared to HTP-0 Ag, the increase in the PLQY value of HTP-1.0 Ag is not positively related to the increase in its photoluminescence intensity. This is because CsPbBr3 QD-doped glasses containing Ag NPs have a stronger absorption of excitation light (Figure 8a).
The fluorescence decay curves of the CsPbBr3 QD-doped glasses containing Ag NPs are shown in Figure 8e. Owing to their non-single exponential features, the PL decay curves can be described by the following double exponential function:
τ = A1 exp(−t/τ1) + A2 exp(−t/τ2)
The calculated average lifetimes of CsPbBr3 QD glasses containing Ag NPs are 24.90, 18.95, 14.95, 13.62, 12.25 and 8.99 ns, for HTP-0 Ag, HTP-0.25 Ag, HTP-0.5 Ag, HTP-1.0 Ag, HTP-1.5 Ag, and HTP-3.0 Ag glass samples, respectively. Compared with HTP-0 Ag, the fluorescence decay of CsPbBr3 QD-doped glasses containing Ag NPs was faster. As the Ag content increased, the fluorescence lifetime of the CsPbBr3 QD-doped glasses containing Ag NPs gradually decreased. This also confirms that the plasma effect increases the ability of the electrons to transition from a lower to a higher energy level. The rapid increase in the number of electrons at the upper energy level causes them to become unstable and the decay time becomes shorter. In other words, the plasma effect increases the PL intensity because it accelerates the number of cycles of electrons at the upper and lower energy levels.
The influence of the Ag NP content on the photoluminescence properties of CsPbBr3 QDs in glasses was simulated using the FTDT method. A model was established based on the size and distribution of Ag and CsPbBr3 nanoparticles (Figure 5b). A rectangular parallelepiped was used to simulate a glass substrate, spheres were used to simulate Ag and CsPbBr3 nanoparticles, and a plane wave was used to simulate the excitation light. Perfectly matched layer boundary conditions were used to eliminate the influence of reflected light at the boundary to achieve the purpose of simulating an infinite space. An electric field monitor (E monitor), set above the model structure, was used to obtain the electric field distribution of the structure. An emitted light intensity monitor (T monitor) set above the model structure was used to obtain the emitted light intensity of the structure. The electric field intensity distributions of 0, 2, 3, 4, 5, and 6 Ag NPs around CsPbBr3 QDs in the established glass model under excitation light are shown in Figure 9a–f. As shown in Figure 9a, since there are no Ag NPs around the CsPbBr3 QDs in the glass model, only the electric field intensity distributions between CsPbBr3 QDs is exhibited, and its electric field intensity is very weak under excitation light. As there are more and more Ag NPs around CsPbBr3 QDs in the glass model, the electric field intensity between Ag NPs and CsPbBr3 QDs first increases and then decreases, as shown in Figure 9b–f. Moreover, the electric field intensity in Figure 9c is strongest. This phenomenon can be explained as the intensity of the plasmon resonance peak is related to the concentration of Ag NPs. In addition, the emitted light intensity of the CsPbBr3 QD-doped glass model containing different numbers of Ag NPs is shown in Figure 9g. With the increase in Ag NPs in the glass model, the emitted light intensity first increased and then decreased. Compared with the CsPbBr3 QD glass model without Ag NPs in Figure 9a, when there are three Ag NPs around CsPbBr3 QDs, the emitted light intensity increases by approximately three times. This result is consistent with the change in the electric field between Ag NPs in Figure 9a–f and the experimental results in Figure 8b.

3.6. Scintillation Properties of CsPbBr3 QD-Doped Glasses Containing Ag NPs

The X-ray excitation scintillation spectra of the CsPbBr3 QD-doped glasses containing Ag NPs are shown in Figure 10a. Under X-ray excitation, the PG glass had almost no radioluminescence emission. CsPbBr3 QD-doped glasses containing Ag NPs had a narrow-band emission near 540 nm, and with an increase in the content of Ag NPs, their scintillation intensity first increased and then decreased. HTP-1.0 Ag had the strongest radioluminescence. These results are consistent with previous photoluminescence results. The radioluminescence and photoluminescence intensity comparison graph of CsPbBr3 QD-doped glasses containing Ag NPs is shown in Figure 10b. Compared with HTP-0 Ag, the photoluminescence intensity of HTP-1.0 Ag glass increases by approximately 3 times, while its radioluminescence intensity increases by approximately 6.25 times. This may be because Ag NCs are composed of Ag+ ions, and Ag NPs emit light under ultraviolet short-wavelength excitation. This can enhance the radioluminescence of CsPbBr3 QDs in glass through energy transfer. To support this conjecture, the excitation spectra of HTP-0 Ag and CsPbBr3 QD-doped glasses containing Ag NPs were measured and analyzed (Figure S2). Unfortunately, the energy transfer between Ag NCs and CsPbBr3 QDs was not observed in their excitation spectra and the corresponding emission spectra in Figure 8b. This is because the absorption of CsPbBr3 QDs is much stronger than that of Ag NCs. Therefore, the excitation and emission spectra of the HTB-1.0 Ag glass were measured (Figure S3a,b). Under ultraviolet short-wavelength excitation, HTB-1.0 Ag exhibits broadband luminescence in the ultraviolet-visible band, which is attributed to the luminescence of Ag NCs. The Ag NCs in the glass is formed by agglomeration and assembly of Ag NPs and Ag+ ions. At present, the geometry and energy level structure of Ag NCs that can produce radiation transitions in glass matrices of different components have not been fully clarified. It is generally believed that the clusters with radioluminescence properties may be Ag2+, Ag32+, Ag42+, etc. [39,40,41]. The PL and radioluminescence properties of CsPbBr3 QD-doped glasses containing Ag NPs are summarized in Table 1. Obviously, the plasma effect caused by the injection of Ag NPs can enhance the scintillation luminescence intensity of CsPbBr3 QD-doped glasses and reduce their fluorescence lifetimes.

4. Conclusions

Scintillation glasses and glass-ceramics generally have the problems of low light yield and long decay time, which is the dilemma and bottleneck in scintillation glasses research at present. To solve these problems, Ag+ ions were first diffused into glasses by ion exchange, and then Ag NCs and CsPbBr3 QDs were formed in transparent glass-ceramics by heat treatment. Compared with CsPbBr3 QD glass, the photoluminescence intensity of Ag+-doped CsPbBr3 QD glass was enhanced by 3 times, its radioluminescence intensity increased by 6.25 times, and its decay time was reduced by a factor of more than one via the above process. Moreover, the mechanism of photoluminescence and radioluminescence enhanced by Ag and plasma was discussed based on the experimental results and finite-difference time-domain method. Ag NCs not only greatly enhanced the light yield of CsPbBr3 QD-doped glass but also effectively shortened their fluorescence decay time, thereby considerably improving the scintillation property of CsPbBr3 QD-doped glass. This work provides a new path for the development of new scintillation glass-ceramic materials. With further optimization of glass composition and the concomitant increase in density, CsPbBr3 QD-doped glasses containing Ag NCs can be used in fast scintillation devices such as colliders for scientific experimental research in high-energy physics and nuclear physics.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ma15155187/s1, Figure S1: Absorption spectrum of HTB-1.0 Ag. Figure S2: Excitation spectra of PG and CsPbBr3 QD-doped glasses containing Ag NPs. Figure S3: (a) Excitation and (b) emission spectra of HTB-1.0 Ag

Author Contributions

Data curation, L.D.; Formal analysis, Y.D.; Investigation, Y.D.; Methodology, L.D.; Software, L.D.; Writing – original draft, Y.D.; Funding acquisition, D.C.; Project administration, D.C.; Writing – review & editing, D.C. All authors have read and agreed to the published version of the manuscript.

Funding

This study was supported by the National Natural Science Foundation of China (No. 51872308).

Institutional Review Board Statement

Not application.

Informed Consent Statement

Not applicable.

Data Availability Statement

The study did not report any data.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Heo, J.H.; Shin, D.H.; Park, J.K.; Kim, D.H.; Lee, S.J.; Im, S.H. High-Performance Next-Generation Perovskite Nanocrystal Scintillator for Nondestructive X-Ray Imaging. Adv. Mater. 2018, 30, 1801743. [Google Scholar] [CrossRef] [PubMed]
  2. Zhang, Y.H.; Sun, R.J.; Qi, X.Y.; Fu, K.F.; Chen, Q.S.; Ding, Y.C.; Xu, L.J.; Liu, L.M.; Han, Y.; Malko, A.V.; et al. Metal Halide Perovskite Nanosheet for X-ray High-Resolution Scintillation Imaging Screens. ACS Nano 2019, 13, 2520–2525. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Moretti, F.; Patton, G.; Belsky, A.; Fasoli, M.; Vedda, A.; Trevisani, M.; Bettinelli, M.; Dujardin, C. Radioluminescence Sensitization in Scintillators and Phosphors: Trap Engineering and Modeling. J. Phys. Chem. C 2014, 118, 9670–9676. [Google Scholar] [CrossRef]
  4. Chen, Q.S.; Wu, J.; Ou, X.Y.; Huang, B.L.; Almutlaq, J.; Zhumekenov, A.A.; Guan, X.W.; Han, S.Y.; Liang, L.L.; Yi, Z.G.; et al. All-inorganic perovskite nanocrystal scintillators. Nature 2018, 561, 88–93. [Google Scholar] [CrossRef]
  5. Ma, W.B.; Jiang, T.M.; Yang, Z.; Zhang, H.; Su, Y.R.; Chen, Z.; Chen, X.Y.; Ma, Y.G.; Zhu, W.J.; Yu, X.; et al. Highly Resolved and Robust Dynamic X-Ray Imaging Using Perovskite Glass-Ceramic Scintillator with Reduced Light Scattering. Adv. Sci. 2021, 8, 2003728. [Google Scholar] [CrossRef] [PubMed]
  6. Qi, R.D.; Xu, Q.C.; Wu, N.; Cui, K.Y.; Zhang, W.; Huang, Y.D. Non-suspended optomechanical crystal cavities using As2S3 chalcogenide glass. Photonics Res. 2021, 9, 05000893. [Google Scholar] [CrossRef]
  7. Isokawa, Y.; Nakauchi, D.; Okada, G.; Kawaguchi, N.; Yanagida, T. Radiation induced luminescence properties of Ce-doped Y2O3-Al2O3-SiO2 glass prepared using floating zone furnace. J. Alloys Compd. 2019, 782, 859–864. [Google Scholar] [CrossRef]
  8. Wang, Y.T.; Fu, S.N.; Kong, J.; Komarov, A.; Klimczak, M.; Buczyński, R.; Tang, X.H.; Tang, M.; Qin, Y.W.; Zhao, L.M. Nonlinear Fourier transform enabled eigenvalue spectrum investigation for fiber laser radiation. Photonics Res. 2021, 9, 08001531. [Google Scholar] [CrossRef]
  9. Juárez-Hernández, M.; Mejía, E.B. Spectral analysis of short-wavelength emission by up-conversion in a Tm3+: ZBLAN dual-diode-pumped optical fiber. Chin. Opt. Lett. 2020, 18, 071901. [Google Scholar] [CrossRef]
  10. Zaman, F.; Rooh, G.; Srisittipokakun, N.; Kim, H.J.; Kaewnuam, E.; Meejitpaisan, P.; Kaewkhao, J. Scintillation and luminescence characteristics of Ce3+ doped in Li2O-Gd2O3-BaO-B2O3 scintillating glasses. Radiat. Phys. Chem. 2017, 130, 158–163. [Google Scholar] [CrossRef]
  11. Shen, C.; Yan, Q.Q.; Xu, Y.S.; Yang, G.; Wang, S.F.; Xing, Z.W.; Chenw, G.R. Luminescence Behaviors of Ce3+ Ions in Chalcohalide Glasses. J. Am. Ceram. Soc. 2010, 93, 614–617. [Google Scholar] [CrossRef]
  12. Chen, Q.; Valiev, D.; Stepanov, S.; Ding, J.; Liu, L.; Li, C.; Lin, H.; Zhou, Y.; Zeng, F. Influence of the Tb3+ concentration on the luminescent properties of high silica glass. Opt. Mater. 2018, 86, 606–610. [Google Scholar] [CrossRef]
  13. Sun, Y.; Koshimizu, M.; Kishimoto, S.; Asai, K. Synthesis and characterization of Pr3+-doped glass scintillators prepared by the sol-gel method. J. Sol-Gel Sci. Technol. 2012, 62, 313–318. [Google Scholar] [CrossRef]
  14. Patton, G.; Moretti, F.; Belsky, A.; al Saghir, K.; Chenu, S.; Matzen, G.; Allix, M.; Dujardin, C. Light yield sensitization by X-ray irradiation of the BaAl4O7: Eu2+ ceramic scintillator obtained by full crystallization of glass. Phys. Chem. Chem. Phys. 2014, 16, 24824–24829. [Google Scholar] [CrossRef] [PubMed]
  15. Liu, L.W.; Shao, C.Y.; Zhang, Y.; Liao, X.L.; Yang, Q.H.; Hu, L.L.; Chen, D.P. Scintillation properties and X-ray irradiation hardness of Ce3+-doped Gd2O3-based scintillation glass. J. Lumin. 2016, 176, 1–5. [Google Scholar] [CrossRef]
  16. Oliveira, M.I.A.; Rivelino, R.; Mota, F.d.; Gueorguiev, G.K. Optical Properties and Quasiparticle Band Gaps of Transition-Metal Atoms Encapsulated by Silicon Cages. J. Phys. Chem. C 2014, 118, 5501–5509. [Google Scholar] [CrossRef] [Green Version]
  17. Freitas, R.R.Q.; de Brito Mota, F.; Rivelino, R.; de Castilho, C.M.C.; Kakanakova-Georgieva, A.; Gueorguiev, G.K. Spin-orbit-induced gap modification in buckled honeycomb XBi and XBi3; (X = B, Al, Ga, and In) sheets. J. Phys. Condens. Matter 2015, 27, 485306. [Google Scholar] [CrossRef] [Green Version]
  18. Quan, C.J.; Xing, X.; Huang, S.H.; Jin, M.F.F.; Shi, T.C.; Zhang, Z.Y.; Xiang, W.D.; Wang, Z.S.; Leng, Y.X. Nonlinear optical properties of CsPbClxBr(3−x) nanocrystals embedded glass. Photonics Res. 2021, 9, 1767–1774. [Google Scholar] [CrossRef]
  19. He, Q.Y.; Mei, E.; Wang, Z.; Liang, X.J.; Chen, S.Q.; Xiang, W.D. Ultrastable Gd3+ doped CsPbCl1.5Br1.5 nanocrystals blue glass for regulated and low thresholds amplified spontaneous emission. Photonics Res. 2021, 9, 1916–1923. [Google Scholar] [CrossRef]
  20. Du, Y.; Wang, X.; Shen, D.Y.; Yuan, J.; Wang, Y.J.; Yan, S.S.; Han, S.; Tao, Y.T.; Chen, D.P. Precipitation of CsPbBr3 quantum dots in borophosphate glasses inducted by heat-treatment and UV-NIR ultrafast lasers. Chem. Eng. J. 2020, 401, 126132. [Google Scholar] [CrossRef]
  21. Wang, Y.J.; Zhang, R.L.; Yue, Y.; Yan, S.S.; Zhang, L.Y.; Chen, D.P. Room temperature synthesis of CsPbX3 (X = Cl, Br, I) perovskite quantum dots by water-induced surface crystallization of glass. J. Alloys Compd. 2020, 818, 152872. [Google Scholar] [CrossRef]
  22. Lu, M.; Zhang, X.Y.; Bai, X.; Wu, H.; Shen, X.Y.; Zhang, Y.; Zhang, W.; Zheng, W.T.; Song, H.W.; Yu, W.W.; et al. Spontaneous Silver Doping and Surface Passivation of CsPbl3 Perovskite Active Layer Enable Light-Emitting Devices with an External Quantum Efficiency of 11.2%. ACS Energy Lett. 2018, 3, 1571–1577. [Google Scholar] [CrossRef] [PubMed]
  23. Chang, C.C.; Sharma, Y.D.; Kim, Y.S.; Bur, J.A.; Shenoi, R.V.; Krishna, S.; Huang, D.H.; Lin, S.Y. A Surface Plasmon Enhanced Infrared Photodetector Based on InAs Quantum Dots. Nano Lett. 2010, 10, 1704–1709. [Google Scholar] [CrossRef] [PubMed]
  24. Diez, I.; Ras, R.H. Fluorescent silver nanoclusters. Nanoscale 2011, 3, 1963–1970. [Google Scholar] [CrossRef]
  25. Kuznetsov, A.S.; Tikhomirov, V.K.; Shestakov, M.V.; Moshchalkov, V.V. Ag Nanocluster Functionalized Glasses for Efficient Photonic Conversion in Light Sources, Solar Cells and Flexible Screen Monitors. Nanoscale 2013, 5, 10065–10075. [Google Scholar] [CrossRef]
  26. Gonella, F. Silver doping of glasses. Ceram. Int. 2015, 41, 6693–6701. [Google Scholar] [CrossRef]
  27. Li, L.J.; Yang, Y.; Zhou, D.C.; Xu, X.H.; Qiu, J.B. The influence of Ag species on spectroscopic features of Tb3+-activated sodium-aluminosilicate glasses via Ag+-Na+ ion exchange. J. Non-Cryst. Solids 2014, 385, 95–99. [Google Scholar] [CrossRef]
  28. Xu, Z.S.; Liu, X.F.; Qiu, J.R.; Cheng, C. Enhanced luminescence of CsPbBr3 perovskite quantum-dot-doped borosilicate glasses with Ag nanoparticles. Opt. Lett. 2019, 44, 5626–5629. [Google Scholar] [CrossRef]
  29. Zhang, K.; Zhou, D.C.; Qiu, J.B.; Long, Z.W.; Zhu, R.; Wang, Q.; Lai, J.A.; Wu, H.; Zhu, C.C. Silver nanoparticles enhanced luminescence and stability of CsPbBr3 perovskite quantum dots in borosilicate glass. J. Am. Ceram. Soc. 2020, 103, 2463–2470. [Google Scholar] [CrossRef]
  30. Sun, K.; Tan, D.Z.; Fang, X.Y.; Xia, X.T.; Lin, D.J.; Song, J.; Lin, Y.H.; Liu, Z.J.; Gu, M.; Yue, Y.Z.; et al. Three-dimensional direct lithography of stable perovskite nanocrystals in glass. Science 2022, 375, 307–310. [Google Scholar] [CrossRef]
  31. Mohapatra, S. Tunable surface plasmon resonance of silver nanoclusters in ion exchanged soda lime glass. J. Alloy. Compd. 2014, 598, 11–15. [Google Scholar] [CrossRef]
  32. Fang, Y.Z.; Meng, S.H.; Hou, J.S.; Liu, Y.F.; Guo, Y.Y.; Zhao, G.Y.; Zou, J.; Hu, L.L. Experimental study of growth of silver nanoparticles embedded in Bi2O3-SiO2-B2O3 glass. J. Alloy. Compd. 2019, 809, 151725. [Google Scholar] [CrossRef]
  33. Mathpal, M.C.; Kumar, P.; Kumar, S.; Tripathi, A.K.; Singh, M.K.; Prakash, J.; Agarwal, A. Opacity and plasmonic properties of Ag embedded glass based metamaterials. RSC Adv. 2015, 5, 12555–12562. [Google Scholar] [CrossRef]
  34. Wang, P.W. Formation of silver colloids in silver ion-exchanged soda-lime glasses during annealing. Appl. Surf. Sci. 1997, 120, 291–298. [Google Scholar] [CrossRef]
  35. Fan, H.Y.; Gao, G.J.; Wang, G.N.; Hu, L.L. Infrared, Raman and XPS spectroscopic studies of Bi2O3-B2O3-GeO2 glasses. Solid State Sci. 2010, 12, 541–545. [Google Scholar] [CrossRef]
  36. Zhang, L.; Zeng, Q.X.; Wang, K. Pressure-Induced Structural and Optical Properties of Inorganic Halide Perovskite CsPbBr3. J. Phys. Chem. Lett. 2017, 8, 3752–3758. [Google Scholar] [CrossRef] [PubMed]
  37. Schmid, T.; Opilik, L.; Blum, C.; Zenobi, R. Nanoscale Chemical Imaging Using Tip-Enhanced Raman Spectroscopy: A Critical Review, Angew. Chem. Int. Ed. 2013, 52, 5940–5954. [Google Scholar] [CrossRef] [PubMed]
  38. Zrimsek, A.B.; Chiang, N.H.; Mattei, M.; Zaleski, S.; McAnally, M.O.; Chapman, C.T.; Henry, A.I.; Schatz, G.C.; van Duyne, R.P. Single-Molecule Chemistry with Surface- and Tip-Enhanced Raman Spectroscopy. Chem. Rev. 2017, 117, 7583–7613. [Google Scholar] [CrossRef]
  39. Shestakov, M.V.; Cuong, N.T.; Tikhomirov, V.K.; Nguyen, M.T.; Chibotaru, L.F.; Moshchalkov, V.V. Quantum Chemistry Modeling of Luminescence Kinetics of Ag Nanoclusters Dispersed in Glass Host. J. Phys. Chem. C 2013, 117, 7796–7800. [Google Scholar] [CrossRef]
  40. Ma, R.H.; Zhao, J.J.; Chen, X.T.; Qiao, X.S.; Fan, X.P.; Du, J.C.; Zhang, X.H. Stabilization of ultra-small [Ag2]2+ and [Agm]n+ nano-clusters through negatively charged tetrahedrons in oxyfluoride glass networks: To largely enhance the luminescence quantum yields. Phys. Chem. Chem. Phys. 2017, 19, 22638–22645. [Google Scholar] [CrossRef]
  41. Li, Y.D.; Chen, F.W.; Liu, C.; Han, J.J.; Zhao, X.J. UV-Visible spectral conversion of silver ion-exchanged aluminosilicate glasses. J. Non-Cryst. Solids 2017, 471, 82–90. [Google Scholar] [CrossRef]
Materials 15 05187 g001 550
Figure 1. Schematic diagram of the preparation of PG glass and CsPbBr3 QD-doped glasses containing Ag NPs.
Figure 1. Schematic diagram of the preparation of PG glass and CsPbBr3 QD-doped glasses containing Ag NPs.
Materials 15 05187 g001
Materials 15 05187 g002 550
Figure 2. The program of research structure.
Figure 2. The program of research structure.
Materials 15 05187 g002
Materials 15 05187 g003 550
Figure 3. XRD patterns of PG and CsPbBr3 QD-doped glasses containing Ag NPs.
Figure 3. XRD patterns of PG and CsPbBr3 QD-doped glasses containing Ag NPs.
Materials 15 05187 g003
Materials 15 05187 g004 550
Figure 4. (a–d) Ag 3d XPS spectra of PG and CsPbBr3 QD-doped glasses containing Ag NPs.
Figure 4. (a–d) Ag 3d XPS spectra of PG and CsPbBr3 QD-doped glasses containing Ag NPs.
Materials 15 05187 g004
Materials 15 05187 g005 550
Figure 5. (a) TEM image, (b,c) HRTEM images, (d,e) SAED patterns.
Figure 5. (a) TEM image, (b,c) HRTEM images, (d,e) SAED patterns.
Materials 15 05187 g005
Materials 15 05187 g006 550
Figure 6. (a–d) the elemental maps of Cs, Pb, Br and Ag of HTP-1.0 Ag and (e–g) the depths of Ag+ ions in HTP-0.5 Ag, HTP-1.0 Ag and HTP-3.0 Ag glass samples.
Figure 6. (a–d) the elemental maps of Cs, Pb, Br and Ag of HTP-1.0 Ag and (e–g) the depths of Ag+ ions in HTP-0.5 Ag, HTP-1.0 Ag and HTP-3.0 Ag glass samples.
Materials 15 05187 g006
Materials 15 05187 g007 550
Figure 7. (a) Raman spectra of CsPbBr3 QD-doped glasses containing Ag NPs and (b) comparison spectra of Raman peak between HTP-0 Ag and HTP-1.0 Ag.
Figure 7. (a) Raman spectra of CsPbBr3 QD-doped glasses containing Ag NPs and (b) comparison spectra of Raman peak between HTP-0 Ag and HTP-1.0 Ag.
Materials 15 05187 g007
Materials 15 05187 g008a 550Materials 15 05187 g008b 550
Figure 8. (a) Absorption, (b,c) emission spectra, (d) PLQYs and (e) fluorescence decay curves of CsPbBr3 QD-doped glasses containing Ag NPs.
Figure 8. (a) Absorption, (b,c) emission spectra, (d) PLQYs and (e) fluorescence decay curves of CsPbBr3 QD-doped glasses containing Ag NPs.
Materials 15 05187 g008aMaterials 15 05187 g008b
Materials 15 05187 g009 550
Figure 9. (a–f) Electric field intensity distribution of different numbers of Ag NPs in CsPbBr3 QD-doped glasses under excitation light calculated by using the FDTD method and (g) emitted light intensity of CsPbBr3 QD-doped glasses model containing different numbers of Ag NPs.
Figure 9. (a–f) Electric field intensity distribution of different numbers of Ag NPs in CsPbBr3 QD-doped glasses under excitation light calculated by using the FDTD method and (g) emitted light intensity of CsPbBr3 QD-doped glasses model containing different numbers of Ag NPs.
Materials 15 05187 g009
Materials 15 05187 g010 550
Figure 10. (a) X-ray excitation scintillation spectra of CsPbBr3 QD-doped glasses containing Ag NPs and (b) their radioluminescence and photoluminescence intensity comparison graph.
Figure 10. (a) X-ray excitation scintillation spectra of CsPbBr3 QD-doped glasses containing Ag NPs and (b) their radioluminescence and photoluminescence intensity comparison graph.
Materials 15 05187 g010
Table
Table 1. Scintillation performances of CsPbBr3 QD-doped glasses containing Ag NPs.
Table 1. Scintillation performances of CsPbBr3 QD-doped glasses containing Ag NPs.
Glass SamplePhotoluminescence Center Wavelength (nm)Photoluminescence Peak Intensity (a.u.)Radioluminescence Center Wavelength (nm)Radioluminescence Peak Intensity (a.u.)Fluorescence Lifetime (ns)PLQY
(%)		Density (g/cm3)
HTP-0 Ag5200.345380.1624.9027.22.75
HTP-0.25 Ag5210.385400.2618.9528.32.82
HTP-0.5 Ag5250.655430.4514.9537.92.91
HTP-1.0 Ag5261547113.6243.03.03
HTP-1.5 Ag5230.545420.3912.2532.83.12
HTP-3.0 Ag5220.425410.348.9926.83.24
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Du, Y.; Deng, L.; Chen, D. Ag Nanocluster-Enhanced Scintillation Properties of Borophosphate Glasses Doped with CsPbBr3 Quantum Dots. Materials 2022, 15, 5187. https://doi.org/10.3390/ma15155187

AMA Style

Du Y, Deng L, Chen D. Ag Nanocluster-Enhanced Scintillation Properties of Borophosphate Glasses Doped with CsPbBr3 Quantum Dots. Materials. 2022; 15(15):5187. https://doi.org/10.3390/ma15155187

Chicago/Turabian Style

Du, Ying, Lu Deng, and Danping Chen. 2022. "Ag Nanocluster-Enhanced Scintillation Properties of Borophosphate Glasses Doped with CsPbBr3 Quantum Dots" Materials 15, no. 15: 5187. https://doi.org/10.3390/ma15155187

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop