Next Article in Journal
Special Issue “Advanced Materials for Water Remediation”
Next Article in Special Issue
Polarization-Dependent Scattering of Nanogratings in Femtosecond Laser Photowritten Waveguides in Fused Silica
Previous Article in Journal
Study on Remote Field Eddy Current Testing Technology for Crack-like Defects in Long Truss Structure of Aircraft
Previous Article in Special Issue
Picosecond Bessel Beam Fabricated Pure, Gold-Coated Silver Nanostructures for Trace-Level Sensing of Multiple Explosives and Hazardous Molecules
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 15
10.3390/ma15155092
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Regular Periodic Surface Structures on Indium Tin Oxide Film Efficiently Fabricated by Femtosecond Laser Direct Writing with a Cylindrical Lens

by
Long Chen
1,†,
Jian Yang
1,†,
Qilin Jiang
1,
Kaiqiang Cao
1,
Jukun Liu
2,*,
Tianqing Jia
1,*,
Zhenrong Sun
1 and
Hongxing Xu
1
1
State Key Laboratory of Precision Spectroscopy, School of Physics and Electronic Science, East China Normal University, Shanghai 200062, China
2
College of Science, Shanghai Institute of Technology, Shanghai 201418, China
*
Authors to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Materials 2022, 15(15), 5092; https://doi.org/10.3390/ma15155092
Submission received: 1 June 2022 / Revised: 18 July 2022 / Accepted: 19 July 2022 / Published: 22 July 2022
(This article belongs to the Special Issue Fundamentals and Applications of Laser Micro/Nanostructuring and Synthesis of Micro/Nanomaterials)
Browse Figures
Review Reports Versions Notes

Abstract

:
Regular laser-induced periodic surface structures (LIPSS) were efficiently fabricated on indium tin oxide (ITO) films by femtosecond laser direct writing with a cylindrical lens. It was found that randomly distributed nanoparticles and high spatial frequency LIPSSs (HSFL) formed on the surface after a small number of cumulative incident laser pulses per spot, and regular low spatial frequency LIPSSs (LSFL) appeared when more laser pulses accumulated. The mechanism of the transition was studied by real-time absorptance measurement and theoretical simulation. Results show that the interference between incident laser and surface plasmon polaritons (SPPs) excited by random surface scatterers facilitates the formation of prototype LSFLs, which in turn enhances light absorption and SPP excitation following laser pulses. The effects of scanning velocity and laser fluence on LSFL quality were discussed in detail. Moreover, large-area extremely regular LSFL with a diameter of 30 mm were efficiently fabricated on an ITO film by femtosecond laser direct writing with the cylindrical lens. The fabricated LSFLs on the ITO film demonstrate vivid structural color. During LSFL processing, the decrease of ITO film thickness leads to the increase of near-infrared optical transmittance.

1. Introduction

Ultrafast laser has become an effective tool for micro/nano-processing [1,2,3,4,5]. Versatile methods are offered for cutting, drilling and modification of different kinds of materials [6,7,8]. In the large variety of subfields related to ultrafast laser micro/nano-processing, laser-induced periodic surface structures (LIPSS) have received considerable attention over the past decades [9,10]. The formation of LIPSSs is a universal phenomenon observed on semiconductors, dielectrics, metals and thin films [2,5,11,12,13,14,15,16,17,18]. According to the relationship between incident laser wavelength λ and the period of induced surface structures Λ, LIPSS can be classified as high spatial frequency LIPSS (HSFL, Λ < 0.5λ) and low spatial frequency LIPSS (LSFL, 0.5λ < Λ < λ) [5,18,19,20,21,22,23,24,25,26]. LIPSSs exhibit great potential for applications in many fields, such as structural colors [18,27,28,29], color-based anti-counterfeiting [30], superhydrophobicity [31,32] and birefringence [33,34,35,36].
Indium-tin oxide (ITO) films have a wide bandgap of 3.5–4.3 eV. As a semiconductor, ITO has high carrier concentration, low electrical resistivity and high optical transparency at visible wavelengths [37,38], and is widely used as a transparent electrode in organic light emitting devices (OLED), liquid crystal displays, thin film solar cells, etc. [39,40,41,42,43,44]. However, the transmittance of untreated ITO film in the infrared band is low, which will significantly reduce the light absorption efficiency of thin-film solar cells [45,46] and limit the application of ITO film as a transparent electrode in the infrared band.
Nanostructures fabricated on the ITO film can effectively modulate its electric and optical properties, especially surface resistance and optical transmittance [10,16,41,47,48,49,50,51], and can be used for application in film solar cells and OLED devices. Reinhardt et al. enhanced the robustness of an ITO film in a severe environment (i.e., strong acid) by fabricating LIPSS with a nanosecond laser, and the incorporation of silicon into ITO is considered to be the reason for the robustness of this sub-pattern against acidic environments [52]. Liu et al. reported that LIPSSs were processed on ITO film by picosecond laser, which ensured low resistance and improved IR transmittance [53]. At present, the efficient fabrication of large-area regular nanostructures on ITO films has attracted great attention.
In this paper, regular LSFLs on ITO thin films were efficiently fabricated by femtosecond laser direct writing with a cylindrical lens. It was found that the number of cumulative laser pulses per spot played a crucial role in LSFL formation. Unlike semiconductor and metal surfaces, such as silicon and copper, randomly distributed nanoparticles and HSFL parallel to the incident laser polarization appeared on the surface with only a few incident laser pulses. With more incident laser pulses accumulated, surface geometry turned into regular LSFLs. Through real-time absorptance measurement and theoretical simulation, it was found that the formation of regular LSFLs was caused by the interference between incident light and surface plasmon polaritons (SPPs) excited by random surface scatterers. Large-area extremely regular LSFLs were efficiently fabricated on an ITO film with a diameter of 30 mm by a femtosecond laser focused with a cylindrical lens. The linear focusing of the cylindrical lens greatly improves the processing efficiency, and the LIPSSs fabricated are extremely regular. The fabricated LSFLs on the ITO film demonstrate great potential in structural color. During LSFL processing, the decrease in ITO film thickness leads to an increase in near-infrared optical transmittance.

2. Materials and Methods

2.1. Laser Direct Writing Setup and Sample Characterization

Figure 1a shows the experimental setup for laser direct writing. A commercial femtosecond laser (Light Conversion Ltd., Vilnius, Lithuania) was used in the experiment, which produced laser pulses of wavelength 1030 nm, pulse width 250 fs and pulse energy 1 mJ with a repetition rate of 1 kHz. The laser power and polarization were adjusted through a combination of a half-wave plate and a Glan prism. A mechanical shutter was used to control the laser irradiation time. The femtosecond laser was incident vertically on the sample through a cylindrical lens with a focal length of 50 mm. The focal spot was 15 µm wide along the minor axis (1/e2 intensity) and 4.0 mm long along the major axis. Compared with a common circular lens with the same focal length (focal spot diameter of 15 μm), the fabrication efficiency is 266 times higher. Moreover, the LIPSSs produced with a cylindrical lens are also more regular [29,36]. An electronically controlled half-wave plate was used to continuously rotate the direction of laser polarization. A colinear monitoring system consisting of a white light source, a dichroic mirror and a charge-coupled device (CCD) were built to monitor the femtosecond laser direct writing in real-time. Figure 1b shows the schematic of the laser polarization, focal spot and scanning direction.
A glass substrate with a diameter of 30 mm coated with ITO film of thickness 175 ± 10 nm (MTI-group, Jiangsu, China) was used in the experiments. The sample was mounted on an x/y/z/θ translation stage. After femtosecond laser direct writing, the samples were cleaned in an ultrasonic bath with deionized water, isopropanol and, finally, acetone [16]. The surface morphology was examined using a scanning electron microscope (SEM, Sigma 300, ZEISS, Oberkochen, Germany) and an optical confocal microscope (Smartproof 5, ZEISS, Oberkochen, Germany). The resolution of the optical confocal microscope was 5 nm on the Z axis and 100 nm on the X/Y axis. Semi-quantitative measurement of the chemical composition was performed using energy-dispersive X-ray spectroscopy (EDS) (SEM, Sigma 300, ZEISS, Oberkochen, Germany). The EDS instrument was an accessory of the SEM and had an information depth of 600 nm. The transmittance spectra of the ITO film were measured using an ultravioletivisible-NIR spectrophotometer (LAMBDA 950, PerkinElmer, Waltham, MA, USA).

2.2. Real-Time Absorptance Measurement Setup

The laser was focused onto the surface of the sample at an inclination angle of 70° (the angle between the incident laser and the sample surface). The laser fluence and polarization were adjusted through a combination of a half-wave plate and a Glan prism. Two energy meters were placed on the reflected and transmitted light path to measure the reflected and transmitted energy of each laser pulse in real-time. The absorptance A could be calculated as
A = 1 − R − T ,
where R is reflectance and T is transmittance. The reflectance and transmittance could be calculated by taking the ratio between the measured and the incident pulse energies.
The transmitted and reflected lasers were focused on the energy meter through a quartz lens with a focal length of 50 mm and a diameter of 75 mm in order to collect all the laser energy scattered and diffracted by the sample structure. The lens had a collection angle of 70° (the corresponding collection angle of the reflected light was in the range of 35−105°). The scattered light beyond the collection angle was also measured using an energy meter, but its energy was too small and below the energy meter measurement range. Therefore, most of the scattered light has been included in the measurement of absorption.
The real-time reflectance measurement should be carried out at an appropriate angle. For a normal incident laser, the detector cannot directly receive the reflected light in real-time. Therefore, an incident angle of 70° was set for the absorption measurement, and the detector could receive the reflected light well.
It is known that the LIPSS periods vary with the incident angle [54,55,56]. However, the incident angle of 70° was very close to 90°, and the periods of the LIPSSs were only 50 nm different from those when using a normal incident laser [56]. The periods of the two cases were very close, and the LSFL formation processes were basically the same. Therefore, it is feasible to use an incident angle of 70° to replace normal incidence in the absorption measurement during LIPSS formation.

2.3. Structural Color Measurement Setup

Figure 2 shows a schematic diagram of the measurement setup to characterize the structural color of the samples from different viewing angles [18,29]. A wide spectral light source (a tungsten halogen lamp with a spectral range of 400–2200 nm) illuminated vertically on the sample surface, and structural colors were measured at different viewing angles using a CCD moving in the Y-Z plane (perpendicular to the LIPSS direction). The angle between the CCD and the Z axis was defined as the observation angle α. The diffraction equation reveals the relationship between the diffraction wavelength λ and the observation angle α:
n λ = d sin α ,
where the integer n is the diffraction order and d is the period of LIPSS.

3. Results and Discussion

3.1. Formation of LSFL on ITO Film

The formation process of regular LSFLs on the ITO film is shown in Figure 3, in which the laser scanning velocity decreased from 12 to 3 mm/s with the pulse fluence fixed at 0.66 J/cm2. Large differences can be observed across different scanning velocities. When the scanning velocity was 12 mm/s, the average number of cumulative pulses per spot was only 1.2. As shown in Figure 3a, slight ablation appeared on the ITO film with some randomly distributed nanoparticles. Due to the high scanning velocity, loosely spaced burnt regions were formed. When the scanning velocity decreased to 6 mm/s, the number of cumulative pulses increased to 2.4 on average. The original random nanoparticles evolved into many short and irregular HSFLs parallel to the laser polarization (Figure 3b). Figure 3c shows the 2D Fourier transform (FT) images of the SEM image of Figure 3b. Figure 3g,h are the corresponding FT spectrums for kx = 0 μm−1 and ky = 0 μm−1 in Figure 3c, respectively. As shown in Figure 3g, the peak of the FT spectrum was 3.0 ± 1 μm−1, which indicated that the HSFL period was 330 ± 100 nm. Meanwhile, some fuzzy prototype LSFLs perpendicular to the laser polarization were formed. As shown in Figure 3h, the peak of the FT spectrum was 1.5 ± 0.4 μm−1, which indicated that the LSFL period was 660 ± 150 nm. The LSFL produced was very irregular and had a wide range of periodic fluctuations.
It was reported that HSFLs parallel to the laser polarization were formed on the LSFL ridge of the metal surface, which was attributed to the cavitation instability in the molten surface layer [57,58,59].
When the scanning velocity further decreased to 4 mm/s, the LSFL perpendicular to the laser polarization direction became clearer and more regular (Figure 3d). Only short HSFLs appeared on the stripes of the LSFL. However, since the number of accumulated pulses per spot was still less than 4, the LSFLs were rather curved and irregular. Finally, when the scanning velocity decreased to 3 mm/s, very regular LSFLs formed on the surface as shown in Figure 3e. Figure 3f depicts the 2D Fourier transform (FT) image of the LSFLs and Figure 3i is the corresponding FT spectrum for ky = 0 μm−1. As shown in Figure 3f, the peak of the FT spectrum was 1.075 ± 0.008 μm−1, which indicated that the LSFL period was 930 ± 5 nm.
Since the scanning velocity directly determines the number of cumulative laser pulses per spot, it is helpful to examine the optical response of the ITO film for each consecutive laser pulse. Figure 4 shows the measured reflectance, transmittance and absorptance of the ITO film irradiated by 20 consecutive laser pulses with the pulse fluence fixed at 0.66 J/cm2. For the first laser pulse radiation, the reflectance and transmittance of the ITO film were 20% and 62% respectively, corresponding to a very low absorptance value of only 18%. The absorptance was enhanced rapidly to 32% of the radiation by the 5th laser pulse. However, the absorptance began to decrease with further laser pulse radiation. It was only 15% of the radiation by the 20th laser pulse, which indicated that most of the ITO film had been ablated off.
Under femtosecond laser irradiation, ITO was rapidly excited to form a surface plasma layer, and the properties of the material changed from dielectric to metallic. After the initial laser pulse irradiation, periodic ablation stripes covering random defects were formed on the ITO film, as shown in Figure 3a [18]. These ablation stripes and random defects would lead to the uneven absorption of subsequent laser pulses on ITO film, resulting in an irregular distribution of nanoparticles and HSFLs. These surface patterns served as scattering sites for the following laser pulses, and surface plasmon polarizations (SPPs) could be excited on the surface [5,18,19,25,60], which is studied in detail in Section 3.2 and the corresponding descriptions. The interference between the incident laser and SPPs led to the periodic distribution of energy and electronic temperature. The electrons then transferred the energy to the crystal lattice through electro-phonon coupling, which caused the ablation of the material and the formation of prototype LSFLs [5,11,25,60]. The appearance of LSFLs due to SPPs further enhanced light absorption and SPP excitation for subsequent laser pulse irradiation, causing the enhanced absorption for following pulses (Figure 4b). This led to an absolute advantage of periodic light absorption compared with the original non-uniform absorption [19], forming a self-enhancing process. Therefore, for a lower scanning velocity, more pulses accumulated on a single spot and the LSFL became straighter and more regular.

3.2. Theoretical Simulation of Light Field Distribution

To further validate the LSFL formation mechanism we proposed, COMSOL Multiphysics software was used to calculate the electric field distribution by solving Maxwell’s equations. Figure 5 presents the schematic of the simulation setup [61,62]. The simulation domain was 15 × 10 × 0.875 μm3 in volume, where four layers of air (0.5 μm), the ITO film in the excited states (0.075 μm), ground states (0.1 μm) and the glass layer (0.2 μm) were enclosed. The dielectric permittivity of ITO in the ground states is 3.6159 + 0.0085i, which is taken from reference [63]. The dielectric permittivity of ITO in the excited states is calculated to be −4.45 + 0.35i according to the Drude model, in which the carrier density is calculated from the Boltzmann’s transport equation [25,64]. The details are shown in the Supplementary Materials.
Figure 3a,b show that random defects and irregular HSFLs formed on the ITO film with high scanning velocity. The sizes of the HSFLs are 500 × 100 nm2, with orientation parallel to the laser polarization. The depths of the HSFLs were measured to be in the range of several tens to hundreds of nanometers [65,66,67]. In order to simplify the simulation, the ablated regions were represented by rectangular grooves with sizes of 500 × 100 × 75 nm3. The selection of other sizes such as 600 × 120 × 60 nm3 will not have a great influence on the simulation results. The positions and numbers of these rectangular grooves are randomly distributed according to the experimental results. However, the orientation changes after being irradiated by a series of laser pulses.
Plane waves irradiated the sample in the normal direction. The boundary conditions in the X directions were periodic boundary (PBC) conditions, while in other directions scattering boundary conditions (SBC) were implemented [61,62].
We first simulated the light field distribution on the upper surface irradiated by the initial laser pulse, in which HSFsL parallel to the laser polarization were formed. As shown in Figure 6a, the magnified image of the black square region shows nanogrooves with orientations parallel to the laser polarization. Some periodic distribution of the light field occurred on the surface as a result of the interference between the incident light and SPPs excited by the HSFL nanostructures. The 2D FT image in Figure 6d shows that periodicity parallel to the laser polarization was stronger than that in the vertical direction. These light intensity distributions would lead to prototype LSFLs perpendicular to the laser polarization. In order to further analyze the evolution of light intensity distribution caused by the formation of the prototype LSFLs, the grooves were placed separately at different angles from the polarization direction, as shown in Figure 6b. The 2DFT image in Figure 6e shows that periodicity parallel to the laser polarization was obviously reduced and became lower than that in the vertical direction. The FT spectrum in kx direction was 1.43 ± 0.35 μm−1, corresponding to a period of 700 ± 160 nm. The ripple-distributed light intensity was significantly enhanced, in agreement with the discussion in the previous section that the formation of LSFL will further enhance SPP excitation. With the groove directions completely perpendicular to the polarization direction as shown in Figure 6c, the light intensity distribution was very regular with a period of 930 ± 15 nm (Figure 6f), and the periodicity parallel to the laser polarization almost completely disappeared.

3.3. Effects of Scanning Velocity and Laser Fluence on LSFL Quality

The scanning velocity and laser fluence have a great influence on the LSFL quality, so a detailed study of the effects of these two parameters is necessary for the fabrication of desirable LSFLs. Figure 7 and Figure 8 show the SEM images and ripple depth of LSFLs fabricated at different scanning velocities from 4 to 1 mm/s. As shown in Figure 7a, when the laser scanning velocity was 4 mm/s, the number of cumulative laser pulses per spot was only 3.5 on average. The LSFLs formed on the surface show fuzzy and irregular shapes with an average depth of 12 nm. When the scanning velocity was reduced to 3 mm/s, very regular LSFLs appeared as shown in Figure 7b with the FT spectrum peak at 1.075 ± 0.008 μm−1 corresponding to a LIPSS period of 930 ± 5 nm. Figure 7e shows the depth profile along the red line in Figure 7b. The depth of each ripple fluctuated in a very small range, which shows that the LSFLs are very regular. The average depth reached a maximum value of 48 nm. Further decrease in the scanning velocity results in the LSFLs being ablated off (Figure 7c,d). When the scanning velocity was reduced to 1 mm/s, the LSFLs almost disappeared. Very thin and shallow ripples (10 nm) appeared on the surface of the glass substrate.
The main components of the ITO film are indium, tin and oxygen. Therefore, the weight percentage of indium ions can be used to characterize the removal of the ITO film. Figure 9a–h shows the SEM images of the geometry and the distribution of the indium ion content for the LSFL fabricated under scanning velocities from 4 to 1 mm/s with the pulse fluence fixed at 0.66 J/cm2. When the scanning velocity was 4 mm/s, as shown in Figure 9e, the indium ion content was relatively high, reaching 39.3%, indicating that the main component of the surface was ITO. When the scanning velocity was reduced to 3 mm/s, very regular LSFLs formed and the indium ions were evenly distributed in the vertical direction (Figure 9b,f). Figure 9k shows the distribution of indium ions along the red line in (b) and the indium ion content distribution was very regular. The whole ITO film was gradually ablated off with further decreases in the scanning velocity. With a scanning velocity of 1 mm/s, the indium ion content on the surface was reduced to merely 2.42% as shown in Figure 9h,j.
Figure 10 and Figure 11 show the SEM images and ripple depth of the LSFLs fabricated on the ITO film for different pulse fluences at a fixed scanning velocity of 3 mm/s. As shown in Figure 10a, when the laser fluence was 0.55 J/cm2, sprototype LSFLs formed on the ITO film surface. Due to the low laser fluence, the ITO film in the gap regions was not completely removed and the formed LSFLs were very irregular. There were some HSFL patterns parallel to the laser polarization direction. The average depth measured by a confocal microscope was 24 nm, as shown in Figure 11. When the laser fluence increased to 0.66 J/cm2, very regular LSFLs with a period of 930 ± 5 nm were formed. Figure 11 shows that the depth reached a maximum value of 48 nm at this pulse fluence. With further increasea in the pulse fluence, LSFLa began to be ablated off. When the pulse fluence increased to 0.89 J/cm2, LSFL almost disappeared, and the depth of the ripples was only 9 nm.
In order to better study the formation process of LSFLa, we studied different types of micro/nanostructures depending on the laser fluence and scanning velocity, as shown in Figure 12. When the scanning velocity was in the range of 3–4 mm/s and the laser fluence was in the range of 0.64–0.79 J/cm2, regular LSFLs covered the entire ablation area. When the laser fluence exceeded 1.3 J/cm2, LSFLs were ablated off. When the laser fluence was lower than 0.3 J/cm2, loosely spaced burnt regions were formed on the ITO film.
The formation of LSFLs on ITO films with different thicknesses (such as 50 nm, 175 nm and 600 nm) was also studied. LSFLs can be prepared on all these ITO films with different thicknesses, but the quality varies greatly. For ITO films with a thickness of 50 nm, they were easily completely ablated before regular LSFLs formed. While for ITO films with a thickness of 600 nm, the laser fluence required for processing LSFLs was higher than 1.0 J/cm2 at a scanning velocity of 3 mm/s. The heat accumulation during laser processing was very serious, which resulted in irregular LSFLs [5,52,53,68]. ITO film with a thickness of 175 nm was suitable for processing LSFLs with extreme regularity.

4. Large-Area LSFL Fabrication and Applications

4.1. Fabrication of Large-Area LSFL

Based on the study of the LSFL formation mechanism and effects of the fabrication parameters, large-area extremely regular LSFLs with a diameter of 30 mm were prepared efficiently on the ITO thin film by femtosecond laser direct writing with a cylindrical lens [29]. The laser fluence was 0.66 J/cm2 and scanning velocity was 3.0 mm/s, indicating that the interval between adjacent scanning lines was 1.5 mm and the number of cumulative pulses per spot was about five. As shown in Figure 13a, the LSFLs were extremely straight and regular with a period of 930 nm. Figure 13b shows the optical image of the LSFLs prepared. Different colors due to diffraction can be clearly observed. Note that large-area LSFLs on the ITO film with a diameter of 30 mm can be fabricated very efficiently within 4 min using cylindrical lens focusing.

4.2. Structural Color Patterning

Various patterns of LSFLs were fabricated by placing masks of different shapes on the ITO sample and the measurement setup shown in Figure 2 was used to characterize the structural color from different viewing angles [29]. Due to the diffraction of the uniform LSFLs, different structural colors could be displayed on the CCD by observing from different angles, as shown in Figure 14a–i. Figure 14j shows the diffraction spectra of the pattern composed of extremely regular LSFLs with peaks at 470, 540 and 660 nm, where the full widths at half-maximum (FWHM) are 32.7, 30.6 and 35.2 nm, respectively. Each diffraction spectrum has only one peak, and the FWHM values are all less than 36 nm. Therefore, all the structural colors were very bright and pure because the fabricated LSFLs were extremely straight and regular.

4.3. Increasing Near-Infrared Optical Transmittance

Figure 15 shows light transmittance spectra of ITO films with LSFLs in the wavelength range of 300–2000 nm. The transmittance only changed slightly with laser fluences in the wavelength range of 300–1000 nm. In the near-infrared region of 1200–1900 nm, the average transmittance of the original ITO film was 37.96% in Table 1. With femtosecond laser direct writing of LSFLs, the transmittance in the near-infrared region increased. When the pulse fluence was 0.66 J/cm2, very regular LSFLs formed, and the average transmittance increased to 71.3%. When the fluence further increased to 0.89 J/cm2, the ITO film was almost completely removed, and the transmittance increased to 91.0%. The near-infrared optical properties of the ITO film can be tuned by femtosecond laser writing of LSFLs at different fabrication parameters. The increase in transmittance was mainly caused by the decrease in ITO film thickness. LSFL processing is accompanied by material removal and a corresponding increase in transmittance.

5. Conclusions

In this paper, regular LSFLs were efficiently prepared on ITO films by femtosecond laser direct writing with a cylindrical lens. It was found that a small number of cumulative laser pulses per spot led to the formation of randomly distributed nanoparticles and HSFLs parallel to the incident laser polarization, while more accumulated pulses induced regular LSFLs perpendicular to the laser polarization. The transition mechanism was studied by real-time absorptance measurement and theoretical simulations. The results demonstrate that the interference between incident laser and SPPs excited by random surface scatterers facilitates prototype LSFL formation, which in turn enhances light absorption and SPP excitation for the following laser pulses. The effects of scanning velocity and laser fluence on LSFL quality were studied in detail. Large-area extremely regular LSFLs on ITO film with a diameter of 30 mm were efficiently fabricated by femtosecond laser direct writing with a cylindrical lens. The fabricated LSFLs on the ITO film demonstrated vivid structural color. During LSFL processing, a decrease in ITO film thickness leads to an increase in near-infrared optical transmittance.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ma15155092/s1, Supplementary Materials presents how the permittivity values used in the simulation were obtained.

Author Contributions

Experiment inquiry, investigation, data curation and writing—original draft, L.C. and J.Y.; Formal analysis, J.Y., Q.J., J.L. and T.J.; Data curation and writing—review & editing., Q.J., K.C., Z.S. and H.X.; Writing—review & editing, J.L. and T.J., Z.S. and H.X. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Natural Science Foundation of China (12074123), the Ministry of Science and Technology of China (Grant No. 2021 YFA1401100) and the Foundation of ‘Manufacturing beyond limits’ of Shanghai.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Bulgakova, N.M.; Bulgakov, A.V. Pulsed laser ablation of solids: Transition from normal vaporization to phase explosion. Appl. Phys. A 2001, 73, 199–208. [Google Scholar] [CrossRef]
  2. Jia, T.Q.; Chen, H.X.; Huang, M.; Zhao, F.L.; Qiu, J.R.; Li, R.X.; Xu, Z.Z.; He, X.K.; Zhang, J.; Kuroda, H. Formation of nanogratings on the surface of a ZnSe crystal irradiated by femtosecond laser pulses. Phys. Rev. B 2005, 72, 125429. [Google Scholar] [CrossRef]
  3. Jia, T.Q.; Chen, H.X.; Huang, M.; Zhao, F.L.; Li, X.X.; Xu, S.Z.; Sun, H.Y.; Feng, D.H.; Li, C.B.; Wang, X.F. Ultraviolet-infrared femtosecond laser-induced damage in fused silica and CaF2 crystals. Phys. Rev. B 2006, 73, 54105. [Google Scholar] [CrossRef]
  4. Zhou, R.; Lin, S.D.; Ding, Y.; Yang, H.; Keng, K.O.Y.; Hong, M.H. Enhancement of laser ablation via interacting spatial double-pulse effect. Opto-Electron. Adv. 2018, 1, 180014. [Google Scholar] [CrossRef] [Green Version]
  5. Zhang, Y.C.; Jiang, Q.L.; Long, M.Q.; Han, R.Z.; Cao, K.Q.; Zhang, S.A.; Feng, D.H.; Jia, T.Q.; Sun, Z.R.; Qiu, J.R.; et al. Femtosecond laser-induced periodic structures: Mechanisms, techniques, and applications. Opto-Electron. Sci. 2022, 1, 220005. [Google Scholar] [CrossRef]
  6. Sugioka, K.; Cheng, Y. Ultrafast lasers—reliable tools for advanced materials processing. Light. Sci. Appl. 2014, 3, e149. [Google Scholar] [CrossRef]
  7. Liu, X.Q.; Bai, B.F.; Chen, Q.D.; Sun, H.B. Etching-assisted femtosecond laser modification of hard materials. Opto-Electron. Adv. 2019, 2, 9190021. [Google Scholar] [CrossRef] [Green Version]
  8. Xie, X.Z.; Zhou, C.X.; Wei, X.; Hu, W.; Ren, Q.L. Laser machining of transparent brittle materials: From machining strategies to applications. Opto-Electron. Adv. 2019, 2, 180017. [Google Scholar] [CrossRef]
  9. Sipe, J.E.; Young, J.F.; Preston, J.S.; Van Driel, H.M. Laser-induced periodic surface structure. I. Theory. Phys. Rev. B 1983, 27, 1141. [Google Scholar] [CrossRef]
  10. Cheng, C.W.; Lee, I.M.; Chen, J.S. Femtosecond laser-induced nanoperiodic structures and simultaneous crystallization in amorphous indium-tin-oxide thin films. Appl. Surf. Sci. 2014, 316, 9–14. [Google Scholar] [CrossRef]
  11. Bonse, J.; Rosenfeld, A.; Krüger, J. On the role of surface plasmon polaritons in the formation of laser-induced periodic surface structures upon irradiation of silicon by femtosecond-laser pulses. J. Appl. Phys. 2009, 106, 104910. [Google Scholar] [CrossRef]
  12. Sakabe, S.; Hashida, M.; Tokita, S.; Namba, S.; Okamuro, K. Mechanism for self-formation of periodic grating structures on a metal surface by a femtosecond laser pulse. Phys. Rev. B 2009, 79, 33409. [Google Scholar] [CrossRef] [Green Version]
  13. Rohloff, M.; Das, S.K.; Höhm, S.; Grunwald, R.; Rosenfeld, A.; Krüger, J.; Bonse, J. Formation of laser-induced periodic surface structures on fused silica upon multiple cross-polarized double-femtosecond-laser-pulse irradiation sequences. J. Appl. Phys. 2011, 110, 14910. [Google Scholar] [CrossRef]
  14. Bonse, J.; Krüger, J.; Höhm, S.; Rosenfeld, A. Femtosecond laser-induced periodic surface structures. J. Laser Appl. 2012, 24, 42006. [Google Scholar] [CrossRef]
  15. Taweesup, K.; Yamamoto, I.; Chikyow, T.; Lothongkum, G.; Tsukagoshi, K.; Ohishi, T.; Tungasmita, S.; Visuttipitukul, P.; Ito, K.; Takahashi, M. Improvement of the effective work function and transmittance of thick indium tin oxide/ultrathin ruthenium doped indium oxide bilayers as transparent conductive oxide. Thin Solid Films 2016, 598, 126–130. [Google Scholar] [CrossRef] [Green Version]
  16. Solodar, A.; Cerkauskaite, A.; Drevinskas, R.; Kazansky, P.G.; Abdulhalim, I. Ultrafast laser induced nanostructured ITO for liquid crystal alignment and higher transparency electrodes. Appl. Phys. Lett. 2018, 113, 81603. [Google Scholar] [CrossRef]
  17. Zhang, D.S.; Sugioka, K. Hierarchical microstructures with high spatial frequency laser induced periodic surface structures possessing different orientations created by femtosecond laser ablation of silicon in liquids. Opto-Electron. Adv. 2019, 2, 190002. [Google Scholar] [CrossRef] [Green Version]
  18. Zhang, Y.C.; Jiang, Q.L.; Cao, K.Q.; Chen, T.Q.; Cheng, K.; Zhang, S.A.; Feng, D.H.; Jia, T.Q.; Sun, Z.R.; Qiu, J.R. Extremely regular periodic surface structures in a large area efficiently induced on silicon by temporally shaped femtosecond laser. Photonics Res. 2021, 9, 839–847. [Google Scholar] [CrossRef]
  19. Huang, M.; Zhao, F.L.; Cheng, Y.; Xu, N.S.; Xu, Z.Z. Origin of laser-induced near-subwavelength ripples: Interference between surface plasmons and incident laser. ACS Nano 2009, 3, 4062–4070. [Google Scholar] [CrossRef]
  20. Le Harzic, R.; Dörr, D.; Sauer, D.; Neumeier, M.; Epple, M.; Zimmermann, H.; Stracke, F. Large-area, uniform, high-spatial-frequency ripples generated on silicon using a nanojoule-femtosecond laser at high repetition rate. Opt. Lett. 2011, 36, 229–231. [Google Scholar] [CrossRef]
  21. Liang, F.; Vallée, R.; Chin, S.L. Mechanism of nanograting formation on the surface of fused silica. Opt. Express 2012, 20, 4389–4396. [Google Scholar] [CrossRef] [PubMed]
  22. Murphy, R.D.; Torralva, B.; Adams, D.P.; Yalisove, S.M. Pump-probe imaging of laser-induced periodic surface structures after ultrafast irradiation of Si. Appl. Phys. Lett. 2013, 103, 141104. [Google Scholar] [CrossRef]
  23. Garcia Lechuga, M.; Puerto, D.; Fuentes Edfuf, Y.; Solis, J.; Siegel, J. Ultrafast moving-spot microscopy: Birth and growth of laser-induced periodic surface structures. ACS Photonics 2016, 3, 1961–1967. [Google Scholar] [CrossRef] [Green Version]
  24. Wang, L.; Xu, B.B.; Cao, X.W.; Li, Q.K.; Tian, W.J.; Chen, Q.D.; Juodkazis, S.; Sun, H.B. Competition between subwavelength and deep-subwavelength structures ablated by ultrashort laser pulses. Optica 2017, 4, 637–642. [Google Scholar] [CrossRef]
  25. Liu, J.K.; Jia, X.; Wu, W.S.; Cheng, K.; Feng, D.H.; Zhang, S.A.; Sun, Z.R.; Jia, T.Q. Ultrafast imaging on the formation of periodic ripples on a Si surface with a prefabricated nanogroove induced by a single femtosecond laser pulse. Opt. Express 2018, 26, 6302–6315. [Google Scholar] [CrossRef]
  26. Liu, J.K.; Zhao, H.; Cheng, K.; Ju, J.Q.; Feng, D.H.; Zhang, S.A.; Sun, Z.R.; Jia, T.Q. Ultrafast dynamics of the thin surface plasma layer and the periodic ripples formation on GaP crystal irradiated by a single femtosecond laser pulse. Opt. Express 2019, 27, 37859–37876. [Google Scholar] [CrossRef]
  27. Liu, Y.; Li, S.Y.; Niu, S.C.; Cao, X.W.; Han, Z.W.; Ren, L.Q. Bio-inspired micro-nano structured surface with structural color and anisotropic wettability on Cu substrate. Appl. Surf. Sci. 2016, 379, 230–237. [Google Scholar] [CrossRef]
  28. Wu, H.; Jiao, Y.L.; Zhang, C.C.; Chen, C.; Yang, L.; Li, J.W.; Ni, J.C.; Zhang, Y.C.; Li, C.Z.; Zhang, Y.Y.; et al. Large area metal micro-/nano-groove arrays with both structural color and anisotropic wetting fabricated by one-step focused laser interference lithography. Nanoscale 2019, 11, 4803–4810. [Google Scholar] [CrossRef]
  29. Chen, L.; Cao, K.Q.; Li, Y.L.; Liu, J.K.; Zhang, S.A.; Feng, D.H.; Sun, Z.R.; Jia, T.Q. Large-area straight, regular periodic surface structures produced on fused silica by the interference of two femtosecond laser beams through cylindrical lens. Opto-Electron. Adv. 2021, 4, 200036. [Google Scholar] [CrossRef]
  30. Dusser, B.; Sagan, Z.; Soder, H.; Faure, N.; Colombier, J.P.; Jourlin, M.; Audouard, E. Controlled nanostructrures formation by ultra fast laser pulses for color marking. Opt. Express 2010, 18, 2913–2924. [Google Scholar] [CrossRef] [Green Version]
  31. Giannuzzi, G.; Gaudiuso, C.; Di Mundo, R.; Mirenghi, L.; Fraggelakis, F.; Kling, R.; Lugarà, P.M.; Ancona, A. Short and long term surface chemistry and wetting behaviour of stainless steel with 1D and 2D periodic structures induced by bursts of femtosecond laser pulses. Appl. Surf. Sci. 2019, 494, 1055–1065. [Google Scholar] [CrossRef]
  32. Jalil, S.A.; Akram, M.; Bhat, J.A.; Hayes, J.J.; Singh, S.C.; ElKabbash, M.; Guo, C. Creating superhydrophobic and antibacterial surfaces on gold by femtosecond laser pulses. Appl. Surf. Sci. 2020, 506, 144952. [Google Scholar] [CrossRef]
  33. Drevinskas, R.; Beresna, M.; Gecevičius, M.; Khenkin, M.; Kazanskii, A.G.; Matulaitienė, I.; Niaura, G.; Konkov, O.I.; Terukov, E.I.; Svirko, Y.P. Giant birefringence and dichroism induced by ultrafast laser pulses in hydrogenated amorphous silicon. Appl. Phys. Lett. 2015, 106, 171106. [Google Scholar] [CrossRef]
  34. Drevinskas, R.; Gecevičius, M.; Beresna, M.; Bellouard, Y.; Kazansky, P.G. Tailored surface birefringence by femtosecond laser assisted wet etching. Opt. Express 2015, 23, 1428–1437. [Google Scholar] [CrossRef]
  35. Cerkauskaite, A.; Drevinskas, R.; Solodar, A.; Abdulhalim, I.; Kazansky, P.G. Form-birefringence in ITO thin films engineered by ultrafast laser nanostructuring. ACS Photonics 2017, 4, 2944–2951. [Google Scholar] [CrossRef]
  36. Chen, L.; Cao, K.Q.; Liu, J.K.; Jia, T.Q.; Li, Y.L.; Zhang, S.A.; Feng, D.H.; Sun, Z.R.; Qiu, J.R. Surface birefringence of regular periodic surface structures produced on glass coated with an indium tin oxide film using a low-fluence femtosecond laser through a cylindrical lens. Opt. Express 2020, 28, 30094–30106. [Google Scholar] [CrossRef]
  37. Kim, H.; Horwitz, J.S.; Kushto, G.; Pique, A.; Kafafi, Z.H.; Gilmore, C.M.; Chrisey, D.B. Effect of film thickness on the properties of indium tin oxide thin films. J. Appl. Phys. 2000, 88, 6021–6025. [Google Scholar] [CrossRef]
  38. Park, J.O.; Lee, J.H.; Kim, J.J.; Cho, S.H.; Cho, Y.K. Crystallization of indium tin oxide thin films prepared by RF-magnetron sputtering without external heating. Thin Solid Films 2005, 474, 127–132. [Google Scholar] [CrossRef]
  39. Chopra, K.L.; Paulson, P.D.; Dutta, V. Thin-film solar cells: An overview. Prog. Photovolt. 2004, 12, 69–92. [Google Scholar] [CrossRef]
  40. Li, Z.H.; Cho, E.S.; Kwon, S.J. A new laser direct etching method of indium tin oxide electrode for application to alternative current plasma display panel. Appl. Surf. Sci. 2009, 255, 9843–9846. [Google Scholar] [CrossRef]
  41. Shin, H.; Sim, B.; Lee, M. Laser-driven high-resolution patterning of indium tin oxide thin film for electronic device. Opt. Lasers Eng. 2010, 48, 816–820. [Google Scholar] [CrossRef]
  42. Risch, A.; Hellmann, R. Picosecond Laser Patterning of ITO Thin Films. Phys. Procedia 2011, 12, 133–140. [Google Scholar] [CrossRef] [Green Version]
  43. Rowell, M.W.; McGehee, M.D. Transparent electrode requirements for thin film solar cell modules. Energy Environ. Sci. 2011, 4, 131–134. [Google Scholar] [CrossRef]
  44. Lee, J.; Kim, S.; Lee, M. Micro-scale patterning of indium tin oxide film by spatially modulated pulsed Nd:YAG laser beam. Appl. Surf. Sci. 2012, 258, 9107–9111. [Google Scholar] [CrossRef]
  45. Vinodkumar, R.; Lethy, K.J.; Beena, D.; Detty, A.P.; Navas, I.; Nayar, U.V.; Mahadevan Pillai, V.P.; Ganesan, V.; Reddy, V.R. Effect of ITO buffer layers on the structural, optical and electrical properties of ZnO multilayer thin films prepared by pulsed laser deposition technique. Sol. Energy Mater. Sol. Cells 2010, 94, 68–74. [Google Scholar] [CrossRef]
  46. Sun, K.W.; Zhou, W.C.; Tang, X.F.; Huang, Z.B.; Lou, F.; Zhu, D.M. Effect of the heat treatment on the infrared emissivity of indium tin oxide (ITO) films. Appl. Surf. Sci. 2011, 257, 9639–9642. [Google Scholar] [CrossRef]
  47. Cheng, C.W.; Shen, W.C.; Lin, C.Y.; Lee, Y.J.; Chen, J.S. Fabrication of micro/nano crystalline ITO structures by femtosecond laser pulses. Appl. Phys. A 2010, 101, 243–248. [Google Scholar] [CrossRef]
  48. Afshar, M.; Straub, M.; Voellm, H.; Feili, D.; Koenig, K.; Seidel, H. Sub-100 nm structuring of indium-tin-oxide thin films by sub-15 femtosecond pulsed near-infrared laser light. Opt. Lett. 2012, 37, 563–565. [Google Scholar] [CrossRef]
  49. Krause, S.; Miclea, P.T.; Steudel, F.; Schweizer, S.; Seifert, G. Precise microstructuring of indium-tin oxide thin films on glass by selective femtosecond laser ablation. EPJ Photovolt. 2013, 4, 40601. [Google Scholar] [CrossRef]
  50. Cheng, C.W.; Lee, I.M.; Chen, J.S. Femtosecond laser processing of indium-tin-oxide thin films. Opt. Lasers Eng. 2015, 69, 1–6. [Google Scholar] [CrossRef]
  51. McDonnell, C.; Milne, D.; Prieto, C.; Chan, H.; Rostohar, D.; O’Connor, G.M. Laser patterning of very thin indium tin oxide thin films on PET substrates. Appl. Surf. Sci. 2015, 359, 567–575. [Google Scholar] [CrossRef]
  52. Reinhardt, H.M.; Maier, P.; Kim, H.C.; Rhinow, D.; Hampp, N. Nanostructured Transparent Conductive Electrodes for Applications in Harsh Environments Fabricated via Nanosecond Laser-Induced Periodic Surface Structures (LIPSS) in Indium–Tin Oxide Films on Glass. Adv. Mater. Interfaces 2019, 6, 1900401. [Google Scholar] [CrossRef]
  53. Liu, P.; Wang, W.J.; Pan, A.F.; Xiang, Y.; Wang, D.P. Periodic surface structures on the surface of indium tin oxide film obtained using picosecond laser. Opt. Laser Technol. 2018, 106, 259–264. [Google Scholar] [CrossRef]
  54. Wu, Q.H.; Ma, Y.R.; Fang, R.C.; Liao, Y.; Yu, Q.X.; Chen, X.L.; Wang, K. Femtosecond laser-induced periodic surface structure on diamond film. Appl. Phys. Lett. 2003, 82, 1703–1705. [Google Scholar] [CrossRef]
  55. Tan, B.; Venkatakrishnan, K. A femtosecond laser-induced periodical surface structure on crystalline silicon. J. Micromech. Microeng. 2006, 16, 1080–1085. [Google Scholar] [CrossRef]
  56. Schwarz, S.; Rung, S.; Esen, C.; Hellmann, R. Homogeneous low spatial frequency LIPSS on dielectric materials generated by beam-shaped femtosecond pulsed laser irradiation. J. Laser Micro Nanoeng. 2018, 13, 90–94. [Google Scholar]
  57. Ionin, A.A.; Kudryashov, S.I.; Ligachev, A.E.; Makarov, S.V.; Seleznev, L.V.; Sinitsyn, D.V. Nanoscale cavitation instability of the surface melt along the grooves of one-dimensional nanorelief gratings on an aluminum surface. JETP Lett. 2011, 94, 266–269. [Google Scholar] [CrossRef]
  58. Ionin, A.A.; Kudryashov, S.I.; Makarov, S.V.; Seleznev, L.V.; Sinitsyn, D.V.; Ligachev, A.E.; Golosov, E.V.; Kolobov, Y.R. Sub-100 nanometer transverse gratings written by femtosecond laser pulses on a titanium surface. Laser Phys. Lett. 2013, 10, 56004. [Google Scholar] [CrossRef]
  59. Skolski, J.Z.P.; Römer, G.R.B.E.; Vincenc Obona, J.; Huis in ’t Veld, A.J. Modeling laser-induced periodic surface structures: Finite-difference time-domain feedback simulations. J. Appl. Phys. 2014, 115, 103102. [Google Scholar] [CrossRef]
  60. Cheng, K.; Liu, J.K.; Cao, K.Q.; Chen, L.; Zhang, Y.C.; Jiang, Q.L.; Feng, D.H.; Zhang, S.A.; Sun, Z.R.; Jia, T.Q. Ultrafast dynamics of single-pulse femtosecond laser-induced periodic ripples on the surface of a gold film. Phys. Rev. B 2018, 98, 184106. [Google Scholar] [CrossRef]
  61. Kluczyk, K.; David, C.; Jacak, J.; Jacak, W. On modeling of plasmon-induced enhancement of the efficiency of solar cells modified by metallic nano-particles. Nanomaterials 2018, 9, 3. [Google Scholar] [CrossRef] [Green Version]
  62. Xia, Y.J.; Zhao, H.; Zheng, C.J.; Zhang, S.A.; Feng, D.H.; Sun, Z.R.; Jia, T.Q. Selective excitation on tip-enhanced Raman spectroscopy by pulse shaping femtosecond laser. Plasmonics 2019, 14, 523–531. [Google Scholar] [CrossRef] [Green Version]
  63. Moerland, R.J.; Hoogenboom, J.P. Subnanometer-accuracy optical distance ruler based on fluorescence quenching by transparent conductors. Optica 2016, 3, 12–116. [Google Scholar] [CrossRef]
  64. Ederth, J.; Johnsson, P.; Niklasson, G.A.; Hoel, A.; Hultåker, A.; Heszler, P.; Granqvist, C.G.; Van Doorn, A.R.; Jongerius, M.J.; Burgard, D. Electrical and optical properties of thin films consisting of tin-doped indium oxide nanoparticles. Phys. Rev. B 2003, 68, 155410. [Google Scholar] [CrossRef]
  65. Miyazaki, K.; Miyaji, G. Nanograting formation through surface plasmon fields induced by femtosecond laser pulses. J. Appl. Phys. 2013, 114, 153108. [Google Scholar] [CrossRef] [Green Version]
  66. Wang, L.; Chen, Q.D.; Cao, X.W.; Buividas, R.; Wang, X.; Juodkazis, S.; Sun, H.B. Plasmonic nano-printing: Large-area nanoscale energy deposition for efficient surface texturing. Light Sci. Appl. 2017, 6, e17112. [Google Scholar] [CrossRef]
  67. Li, Z.X.; Wu, Q.; Jiang, X.D.; Zhou, X.; Liu, Y.Y.; Hu, X.Y.; Zhang, J.M.; Yao, J.H.; Xu, J.J. Formation mechanism of high spatial frequency laser-induced periodic surface structures and experimental support. Appl. Surf. Sci. 2022, 580, 152107. [Google Scholar] [CrossRef]
  68. Zhang, F.Z.; Chen, L.; Zhang, Y.C.; Jiang, Q.L.; Feng, D.H.; Zhang, S.A.; Jia, T.Q.; Sun, Z.R.; Xu, H.X. High-Performance Birefringence of Periodic Nanostructures in FTO Thin Film Fabricated by IR-UV Femtosecond Laser. Front. Phys. 2022, 10, 208. [Google Scholar] [CrossRef]
Materials 15 05092 g001 550
Figure 1. (a) Schematic of the laser direct writing setup. HWP is a half-wave plate, GP is a Glan prism and WL is a white light source. (b) Schematic of the laser polarization, focal spot and scanning direction.
Figure 1. (a) Schematic of the laser direct writing setup. HWP is a half-wave plate, GP is a Glan prism and WL is a white light source. (b) Schematic of the laser polarization, focal spot and scanning direction.
Materials 15 05092 g001
Materials 15 05092 g002 550
Figure 2. Schematic of the setup for structural color measurement.
Figure 2. Schematic of the setup for structural color measurement.
Materials 15 05092 g002
Materials 15 05092 g003 550
Figure 3. SEM images of micro/nanostructures on the ITO film after laser irradiation for scanning velocity of (a) 12, (b) 6, (d) 4 and (e) 3 mm/s with pulse fluence fixed at 0.66 J/cm2. The scale bars are 10 μm in (a) and (d) and 2 μm in (b) and (e). The insets in (a) and (d) are the enlarged SEM images for the red square areas. (c) and (f) are the 2D Fourier transform (FT) images of the LSFL in (b) and (e), respectively. (g) and (h) are the corresponding FT spectrums for kx = 0 μm−1 and ky = 0 μm−1 in (c), respectively. (i) is the corresponding FT spectrum for ky = 0 μm−1 in (f). (j) is the confocal optical microscope image of (e).
Figure 3. SEM images of micro/nanostructures on the ITO film after laser irradiation for scanning velocity of (a) 12, (b) 6, (d) 4 and (e) 3 mm/s with pulse fluence fixed at 0.66 J/cm2. The scale bars are 10 μm in (a) and (d) and 2 μm in (b) and (e). The insets in (a) and (d) are the enlarged SEM images for the red square areas. (c) and (f) are the 2D Fourier transform (FT) images of the LSFL in (b) and (e), respectively. (g) and (h) are the corresponding FT spectrums for kx = 0 μm−1 and ky = 0 μm−1 in (c), respectively. (i) is the corresponding FT spectrum for ky = 0 μm−1 in (f). (j) is the confocal optical microscope image of (e).
Materials 15 05092 g003
Materials 15 05092 g004 550
Figure 4. Measured (a) reflectance, transmittance and (b) absorptance of the ITO film for each consecutive femtosecond laser pulse. The pulse fluence was fixed at 0.66 J/cm2.
Figure 4. Measured (a) reflectance, transmittance and (b) absorptance of the ITO film for each consecutive femtosecond laser pulse. The pulse fluence was fixed at 0.66 J/cm2.
Materials 15 05092 g004
Materials 15 05092 g005 550
Figure 5. Schematic of the simulation setup with COMSOL Multiphysics software. The arrow E shows the laser polarization.
Figure 5. Schematic of the simulation setup with COMSOL Multiphysics software. The arrow E shows the laser polarization.
Materials 15 05092 g005
Materials 15 05092 g006 550
Figure 6. Surface light intensity distribution for different nanogroove orientations. Nanogrooves are (a) parallel to laser polarization (initial horizontal HSFLs), (b) mostly and (c) completely perpendicular to laser polarization (prototype LSFLs). (d–f) are the 2D FT images of the light field distributions in the red boxes of (a–c). The arrow E shows the laser polarization in (a). The color bars in (a–c) indicate the normalized light intensity.
Figure 6. Surface light intensity distribution for different nanogroove orientations. Nanogrooves are (a) parallel to laser polarization (initial horizontal HSFLs), (b) mostly and (c) completely perpendicular to laser polarization (prototype LSFLs). (d–f) are the 2D FT images of the light field distributions in the red boxes of (a–c). The arrow E shows the laser polarization in (a). The color bars in (a–c) indicate the normalized light intensity.
Materials 15 05092 g006
Materials 15 05092 g007 550
Figure 7. SEM images of LSFLs on the ITO film after laser irradiation under scanning velocities of (a) 4, (b) 3, (c) 2 and (d) 1 mm/s with a fixed pulse fluence of 0.66 J/cm2. The scale bars are all 2 μm. The FT of (b) is highlighted in the inset. (e) shows the depth profile along the red line in (b).
Figure 7. SEM images of LSFLs on the ITO film after laser irradiation under scanning velocities of (a) 4, (b) 3, (c) 2 and (d) 1 mm/s with a fixed pulse fluence of 0.66 J/cm2. The scale bars are all 2 μm. The FT of (b) is highlighted in the inset. (e) shows the depth profile along the red line in (b).
Materials 15 05092 g007
Materials 15 05092 g008 550
Figure 8. LSFL depth versus scanning velocity at a constant laser fluence of 0.66 J/cm2.
Figure 8. LSFL depth versus scanning velocity at a constant laser fluence of 0.66 J/cm2.
Materials 15 05092 g008
Materials 15 05092 g009 550
Figure 9. SEM images of LSFLs on the ITO film after laser irradiation under scanning velocities of (a) 4, (b) 3, (c) 2 and (d) 1 mm/s with fixed pulse fluence of 0.66 J/cm2. (e–h) Distributions of indium ion content measured by EDS corresponding to (a–d) respectively. The scale bars are all 2 μm. (i) and (j) are the sum spectra of (a,d), respectively. (k) is the distribution of the indium content along the red line in (b).
Figure 9. SEM images of LSFLs on the ITO film after laser irradiation under scanning velocities of (a) 4, (b) 3, (c) 2 and (d) 1 mm/s with fixed pulse fluence of 0.66 J/cm2. (e–h) Distributions of indium ion content measured by EDS corresponding to (a–d) respectively. The scale bars are all 2 μm. (i) and (j) are the sum spectra of (a,d), respectively. (k) is the distribution of the indium content along the red line in (b).
Materials 15 05092 g009
Materials 15 05092 g010 550
Figure 10. SEM images of LSFLa on the ITO film after laser irradiation under pulse fluences of (a) 0.55, (b) 0.66, (c) 0.75 and (d) 0.89 J/cm2 with a fixed scanning velocity of 3 mm/s. The scale bars are all 2 μm. The FT image of (b) is highlighted in the inset. The double arrow in (a) indicates the laser polarization direction.
Figure 10. SEM images of LSFLa on the ITO film after laser irradiation under pulse fluences of (a) 0.55, (b) 0.66, (c) 0.75 and (d) 0.89 J/cm2 with a fixed scanning velocity of 3 mm/s. The scale bars are all 2 μm. The FT image of (b) is highlighted in the inset. The double arrow in (a) indicates the laser polarization direction.
Materials 15 05092 g010
Materials 15 05092 g011 550
Figure 11. LSFL depth versus the pulse fluence at a constant scanning velocity of 3 mm/s.
Figure 11. LSFL depth versus the pulse fluence at a constant scanning velocity of 3 mm/s.
Materials 15 05092 g011
Materials 15 05092 g012 550
Figure 12. Different types of micro/nanostructures depending on the laser fluence and scanning velocity.
Figure 12. Different types of micro/nanostructures depending on the laser fluence and scanning velocity.
Materials 15 05092 g012
Materials 15 05092 g013 550
Figure 13. (a) SEM image of large-area regular LSFL. The scale bar is 10 μm and the inset is the 2DFT of the SEM image. (b) Optical image of the large-area LSFL.
Figure 13. (a) SEM image of large-area regular LSFL. The scale bar is 10 μm and the inset is the 2DFT of the SEM image. (b) Optical image of the large-area LSFL.
Materials 15 05092 g013
Materials 15 05092 g014 550
Figure 14. (a–i) Optical images, and (j) the diffraction spectra of different patterns composed of extremely regular LSFLs.
Figure 14. (a–i) Optical images, and (j) the diffraction spectra of different patterns composed of extremely regular LSFLs.
Materials 15 05092 g014
Materials 15 05092 g015 550
Figure 15. Light transmittance spectra of ITO films with LSFLs fabricated by femtosecond laser direct writing with different pulse fluences. The scanning velocity was fixed at 3.0 mm/s.
Figure 15. Light transmittance spectra of ITO films with LSFLs fabricated by femtosecond laser direct writing with different pulse fluences. The scanning velocity was fixed at 3.0 mm/s.
Materials 15 05092 g015
Table
Table 1. The average transmittance in the near-infrared band from 1200 to 1900 nm for LSFL fabricated by femtosecond laser direct writing with different pulse fluences (0~0.89 J/cm2).
Table 1. The average transmittance in the near-infrared band from 1200 to 1900 nm for LSFL fabricated by femtosecond laser direct writing with different pulse fluences (0~0.89 J/cm2).
Fluences (J/cm2)00.320.410.660.750.820.89
Light transmittance (%)37.9656.8365.3071.3276.9181.3290.96
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Chen, L.; Yang, J.; Jiang, Q.; Cao, K.; Liu, J.; Jia, T.; Sun, Z.; Xu, H. Regular Periodic Surface Structures on Indium Tin Oxide Film Efficiently Fabricated by Femtosecond Laser Direct Writing with a Cylindrical Lens. Materials 2022, 15, 5092. https://doi.org/10.3390/ma15155092

AMA Style

Chen L, Yang J, Jiang Q, Cao K, Liu J, Jia T, Sun Z, Xu H. Regular Periodic Surface Structures on Indium Tin Oxide Film Efficiently Fabricated by Femtosecond Laser Direct Writing with a Cylindrical Lens. Materials. 2022; 15(15):5092. https://doi.org/10.3390/ma15155092

Chicago/Turabian Style

Chen, Long, Jian Yang, Qilin Jiang, Kaiqiang Cao, Jukun Liu, Tianqing Jia, Zhenrong Sun, and Hongxing Xu. 2022. "Regular Periodic Surface Structures on Indium Tin Oxide Film Efficiently Fabricated by Femtosecond Laser Direct Writing with a Cylindrical Lens" Materials 15, no. 15: 5092. https://doi.org/10.3390/ma15155092

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop