Properties of Biocomposites Produced with Thermoplastic Starch and Digestate: Physicochemical and Mechanical Characteristics
Previous Article in Journal
Growing Interface with Phase Separation and Spontaneous Convection during Hydrodynamically Stable Displacement
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 14
Issue 20
10.3390/ma14206091
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

KCl Extracted from Chlorine Bypass Dust as Activator for Plain Concrete

by
Hong-Beom Choi
1,
Jin-Man Kim
2,*,
Sun-Mi Choi
3 and
Sung-Su Kim
4
1
Construction Test & Certification Department, Korea Institute of Civil Engineering and Building Technology, Goyang-si 10223, Korea
2
Department of Architectural Engineering, Kongju National University, Cheonan City 31080, Korea
3
Eco-Friendly Concrete Research Center, Kongju National University, Cheonan City 31080, Korea
4
Department of Environmental Energy Engineering, Kyonggi University, Suwon 16227, Korea
*
Author to whom correspondence should be addressed.
Materials 2021, 14(20), 6091; https://doi.org/10.3390/ma14206091
Submission received: 29 August 2021 / Revised: 27 September 2021 / Accepted: 1 October 2021 / Published: 15 October 2021
(This article belongs to the Topic Geopolymers: Synthesis, Characterization and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
This study demonstrated the use of KCl separated from chlorine bypass dust (CBD) as an activator for plain concrete. The separated KCl was mixed with either ground granulated blast-furnace slag (BFS) alone, or a mixture of BFS and cement. The mixed paste of separated KCl and BFS set within 24 h, and exhibited a compressive strength of 22.6 MPa after 28 d. The separated KCl, cement, and BFS mixture exhibited a more rapid setting and a higher initial activity. Further, the compressive strength at 28 d was 57.7 MPa, which was 26.2% higher than that of the mixture without the activator. Water curing of samples with added separated KCl led to the generation of hydrocalumite, or Friedel’s salt. However, this hydrocalumite was decomposed while being cured under autoclave conditions at 180 °C. Overall, KCl was an effective activator for composite materials containing cement, and resulted in superior properties compared to mineral admixtures without an activator.

1. Introduction

Advances in concrete-based construction technologies have facilitated rapid industrial development and the construction of cutting-edge residential infrastructures. Concrete is an essential construction material and has cement as its main ingredient. Cement generates carbon dioxide during high-temperature sintering due to chemical decomposition, which leads to the emission of approximately 0.8 tons of carbon dioxide per ton of cement during production [1,2]. Consequently, the carbon dioxide emissions from the cement industry account for 8% of global carbon dioxide emissions [3]. Due to environmental concerns regarding these substantial greenhouse gas (GHG) emissions, as well as the depletion of cement raw material reserves, recent research has focused on reducing the proportion of cement in concrete.
Industrial by-products with hydraulic or pozzolanic reactivity have been widely investigated as substitutes that might allow for the reduction of cement usage, ground granulated blast furnace slag (BFS) and fly ash (FA) being two representative cementitious materials [4,5]. These industrial by-products are also activated by alkali components, where the addition of an alkali activator can lead to enhanced reactions by forcibly destroying the thin film on the surface of industrial by-product particles [6,7]. There are various studies on the properties of mixtures that use strong alkali activators, such as Ca(OH)2, NaOH, and KOH, instead of Portland cement [8,9,10,11,12]. Further, enhanced strength has been achieved by adding alkali activators to the cementitious mixtures even when using industrial by-products [13,14,15,16,17]. A number of studies of additive materials have been reported in which the addition of polyvinyl alcohol (PVA) fibers and nano-SiO2 improves both the quality and the development direction of existing alkali-activated mortar [18,19,20]. However, alkali-activated cement relies on costly alkali activators, and is thus less favorable in terms of performance and economic efficiency compared to mixtures based on Portland cement. Because these issues must be addressed to encourage the practical use of alkali-activated cement, research on the development of cheaper activators will be needed.
Cement processing provides the optimal environmental solution for the safe treatment of plastic wastes. However, plastics with a high chlorine content, such as polyvinyl chloride (PVC), will increase the chlorine content of the clinker when it burns in a cement kiln. Thus, the clinker should be discharged regularly to reduce the high chlorine content. The waste generated from the chlorine discharging process is referred to as chlorine bypass dust (CBD) [21,22]. CBD mainly comprises K, Cl, and Ca, and its landfill disposal is costly. A previous study reported that K and Cl ions in the form of KCl (potassium chloride) and Ca in the form of Ca(OH)2 exist in CBD [23,24].
We prepared a pure KCl solution from CBD, by dissolution with tap water and filter separation. Reports on the use of reagent-grade KCl have demonstrated that it can accelerate the setting time and initial compressive strength of cement by increasing the initial hydration heat [25]. Because KCl has high alkalinity, it can be used as an alkali activator for cementitious materials like NaOH and KOH. We hypothesized that if the separated KCl were well prepared, it could show the almost same performance as reagent KCl.
This study therefore aimed to investigate the hydration characteristics of KCl separated from CBD in cementitious materials, such as ground granulated blast furnace slag and fly ash. The properties of cement-free mortar and cement-containing mortar were analyzed. The reaction characteristics between the by-products and KCl were analyzed, and the resulting strength was compared with samples prepared using other alkali activators, such as NaOH and KOH. Because a high Cl content can lead to the corrosion of the steel reinforcements in reinforced concrete, this research can be applied to plain concrete structures without steel reinforcement, such as soil solidification agents. This research can also be applied very limitedly to reinforced concrete.

2. Materials and Methods

2.1. Experimental Design

This study investigated several binders, replacement ratios, alkali activator types, and alkali activator dosages (Table 1). Ordinary Portland Cement (OPC) was used as a reference binder, and was compared to BFS and FA as representative latent hydraulic industrial by-products. The replacement ratios of BFS and FA were 0%, 50%, and 100%. The replacement ratios 0% and 50% were set using the activity measurement method per ASTM C989:2018 (Standard Specification for Ground Granulated Blast-Furnace Slag and Mortar) and the 100% replacement ratio was selected for the purpose of zero cement testing [26]. The effects of the various alkali activators, namely NaOH, KOH, and liquid separated KCl, were evaluated according to the presence or absence of cement. The content of each alkali activator was 10% of the mass of BFS and FA. The concentration of the liquid-separated KCl was determined based on precipitation and drying. The cement-free and cement-containing mortar samples (Table 2) were subjected to water curing and autoclave curing at 180 °C. The mix proportions were calculated based on a water-to-binder ratio of 40% and air content of 5%. The setting time of the paste was measured, and the flow and compressive strength of the mortar were evaluated over an aging period of 28 d.

2.2. Materials

Although the high content of KCl and Ca(OH)2 in CBD is highly soluble in water, they have different solubilities. To get the pure KCl, we mixed CBD with tap water and reacted with CO2 in a carbonation chamber. Ca(OH)2 was converted into solid calcium carbonate(CaCO3) easily. The solid materials, including solid calcium carbonate, were separated from the solution using a glass microfiber filter. From this process, it was possible to get the pure KCl solution.
OPC was obtained from company H in Danyang-gun of the Republic of Korea, BFS (type 3) was obtained from company S in Dangjin-si of the Republic of Korea, and FA (type 2) was obtained from power generation company E in Donghae-si of the Republic of Korea. The fineness of the OPC, BFS, and FA powders was 382, 436, and 305 m2/kg, respectively, and was measured by ASTM C204:2018 (Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus) [27]. The chemical compositions of the binders and the CBD are given in Table 3. A polycarboxylate-based superplasticizer from s company in Asan-si of the Republic of Korea was used, and a superplasticizer diluted at a concentration of 20% was used in the test. Reagent-grade NaOH with a purity of >98% from company D in Ansan-si of the Republic of Korea and KOH with a purity of >85% from company D in Ansan-si of the Republic of Korea were also used as activators to serve as a comparison with the KCl separated from the CBD. The raw CBD contained CaO as well as Ca ions, while the extracted KCl mostly contained KCl minerals (Figure 1). In CBD, KCl is separated into highly soluble components, but the pH was raised using NaOH to prevent dissolution of Ca and other components. Selective separation of KCl was achieved by mixing the CBD with water at a solid-water ratio of 400 g/L at 20 °C using an INTLLAB MS-500 magnetic stirrer (INTLLAB, Weihai, China) running at 300 rpm for 10 min. The solution and solids were separated using a grade C glass microfiber (GF/C) filter with diameter 4.7 cm, pore size 1.2 µm, CAT no. 1822-047, Whatman. Separation was performed by gravity filtration. The pH of the solution was 12.7, the KCl purity was >95%, and the KCl concentration was 193 g/L. These measurements were used to calculate the solid. The main ions in the solution were K and Cl ions (>95%), while some Ca ions were also included.

2.3. Methodology

The setting time of the sample pastes was determined three time at a temperature of 20 ± 2 °C and a relative humidity of 60 ± 5% in accordance with the ASTM C191:2019 (Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle) [28]. The amount of water required to obtain a normal consistency in the fixed state was determined based on the content of each alkali activator. The alkali activator was dissolved in the sample paste and the flow of mortar was determined three times using a specified flow table based on ASTM C1437:2020—the standard test method for flow of hydraulic cement mortar [29]. The table was dropped into the paste 25 times for 15 s, and the diameter was measured.
The compressive strength of the molded mortar samples was measured five times in accordance with the ASTM C109:2020 (Standard Test Method for Compressive Strength of Hydraulic Cement Mortar) [30]. The samples used for the evaluation of compressive strength and hydration were aged 3, 7, and 28 days under water curing (3D-W, 7D-W, 28D-W, respectively) and autoclave curing (Autoclave). In particular, the water-cured samples were held at a constant temperature of 20 ± 1 °C and humidity of 60 ± 5% for 24 h, demolded, and subjected to water curing in a water tank at 20 °C. The autoclave cured samples were also held at a constant temperature of 20 ± 1 °C and a humidity of 60 ± 5% for 24 h, and subsequently cured at 180 °C and 10 atm for 8 h. The composition of the hydrates after aging for 28 d was determined two times for both sets of cured samples using a MiniFlex600 X-ray diffraction (XRD, Rigaku, Tokyo, Japan) device with a step size of 0.020° in the range between 5° and 60° 2-theta at a scanning speed of 6°/min. Cu K (λ = 1.5056 Å) was used as the Radiation source, the X-ray generator was 600 W, and the monochromator was not used. Samples used for the X-ray diffraction were kept under 45 µm by grinding.

3. Results

3.1. Mortar Flow

The flow of the cement-free and cement-containing mortar samples with NaOH, KOH, and the cement-derived KCl as activators is illustrated in Figure 2. Each activator was added to the mixing water and used in the dissolved state. Therefore, the liquid phase increased as a sum of the mixing water and activators. The fluidity of the mortar was not affected by the activators, and all the mixtures fell within the 185 ± 15 mm range due to the use of a superplasticizer. FA was found to satisfy the target fluidity even with a small amount of superplasticizer due to its spherical particles and low fineness. On the other hand, as BFS has a rough granular shape and a relatively high fineness because of its process of manufacture by grinding, a large amount of superplasticizer was used to achieve the target fluidity. There was no difference in fluidity, despite the increases in the amount of liquid phase that could affect the flow of mortar due to the replacement of mixing water and binder with the added activators. This was attributed to an increase in the viscosity of the mixing water due to the solid to liquid dissolution of the activator.

3.2. Paste Setting Time

The setting times of the cement-free and cement-containing mortar pastes with KCl separated from the activators CBD, NaOH, and KOH were evaluated at an activator content of 10% compared to the mass of mineral admixture (Figure 3). These samples were also used in the mortar test. Among the 100% mineral admixtures, the BFS mixtures with NaOH and KOH exhibited a final setting time of less than 3 h, which was faster than the 100% OPC sample. However, the mixture with KCl exhibited a final setting time of 15 h 37 min. The FA mixture with NaOH did not set within 24 h, while the FA mixtures with KOH and KCl set within 8 h 53 min and 17 h 17 min, respectively. The addition of KCl to both non-cement mixtures (100% BFS or FA) led to a setting time of >10 h due to the properties of the activator. However, it was encouraging that KCl led to the same level of acceleration in FA, while KOH and NaOH exhibited a significantly lower acceleration effect in FA, despite their high acceleration effect in BFSs with high hydration activity due to their latent hydraulic properties. In particular, the non-cement mixture containing NaOH in FA did not set within 16 h. These findings demonstrated that KCl had a superior effect as an alkali activator.
The use of NaOH and KOH in the 50% OPC and 50% mineral admixture binders led to rapid setting within ~1 h, regardless of the binder composition. The addition of KCl to the FA mixture led to a final setting time of 5 h 37 min, which was slightly longer than that of 100% OPC. However, the addition of KCl to the BFS mixture led to faster setting (4 h 10 min) than 100% OPC. This indicated that KCl also accelerated setting by stimulating the cement alite and interstitial minerals due to the high alkalinity (pH > 12) and salinity, despite the minimal initial stimulation due to the relatively low pH compared to NaOH and KOH. This confirmed that KCl can be used as an activator for mixtures of OPC and mineral admixture.

3.3. Compressive Strength of Mortar

The compressive strength of the 100% OPC mortar sample without an activator and that of the 100% BFS mortar samples with NaOH, KOH, and cement-derived KCl as activators were evaluated according to curing conditions and age (Figure 4). Further, the strength development rate of each sample compared to the strength of the OPC 100% sample was calculated as the hydration activity index. The samples with 100% FA were excluded from further investigation because they could not develop an early-stage strength of 1 MPa or higher before 28 d, despite the use of alkali activators. This lack of early-stage strength was attributed to a lack of hydration reaction activation within the samples by the alkali activators. A large amount of the FA particles was inert because the Fe2O3 content was over 11% and the 45-µm sieve residue was less than 40% according to ASTM C618:2019 due to the fineness of 305 m2/kg.
The 100% BFS mortar samples developed to different strengths depending on activator type. In particular, NaOH and KOH activators led to compressive strengths of >30 MPa after aging for 28 d. Although this was lower than the compressive strength of 100% OPC at 28 d (46 MPa), the non-cement mixtures based on the latent hydraulic binder exhibited a hydration activity index of >65%, which demonstrated the high possibility of using the binder alone. The samples subjected to autoclave curing exhibited higher hydration activity indices than the water-cured samples. In particular, the 100% BFSs sample with NaOH as an activator exhibited a high hydration activity index of >130% after autoclave-curing compared to OPC. Therefore, BFS is expected to achieve higher performance than OPC when used in precast concrete product manufacturing based on hydrothermal synthesis. However, the 100% BFS sample with cement-derived KCl as an activator did not exhibit an equivalent performance to the NaOH- and KOH- activated samples. Although strength development in a non-cement sample was achieved using the KCl activator, the strength was only half that of OPC. This corresponded to the setting behavior (Figure 3), where the strength development contribution of KCl via alkali stimulation was low compared to NaOH and KOH.
The compressive strength of the 100% OPC mortar sample without an activator was compared to that of the 50% mineral admixture (BFS or FA) and 50% OPC mortar samples with alkali activators, and the hydration activity indices were calculated (Figure 5). The 100% FA samples did not develop an early-stage strength of 1 MPa before 28 d, but the 50% OPC and 50% FA mixture strengthened sufficiently. In particular, the 50% FA and 50% OPC sample without an activator exhibited a hydration activity index of >50% compared to OPC at all ages, where the activity reached 60% as the age increased. This is judged to be because OPC served as an active material and contributed to the pozzolan reaction by stimulating the FA surface, where the effect increased with age. Further, it appeared that FA partially contributed to strength development due to its high amorphous Si content, thereby generating tobermorite via hydrothermal synthesis during autoclave curing. Therefore, the strength ratios of the water-cured FA samples at 28 d of age compared to the BFS samples were only 69%, 69%, 51%, and 67% for no activator, NaOH, KOH, and KCl, respectively, but increased to 81%, 110%, 75%, and 88%, respectively, under autoclave curing.
The samples comprising 100% mineral admixture did not exhibit reactivity due to their latent hydraulic properties in the absence of an activator. However, mixing of the mineral admixture with OPC led to strength development due to stimulation by CH generation during OPC hydration. Thus, the samples without an added activator also exhibited a hydration activity index of >50%. The 50% BFS and 50% OPC sample exhibited a hydration activity index of more than 100% compared to OPC at 28 days of age. However, the 50% BFS and 50% OPC samples with NaOH and KOH as activators exhibited lower strengths because OPC theoretically generates approximately 20% Ca(OH)2 with sufficient hydration reaction with water, and the addition of the activator adversely affected strength development due to excessive alkali [31]. Further, the minerals that were generated by the hydration of OPC at a high pH, such as ettringite, were unstable despite the strength contribution of NaOH and KOH via the stimulation of mineral admixture reactivity [32,33]. The 50% BFS and 50% OPC samples with KCl as an activator exhibited the opposite trend to the 100% BFS sample, and achieved a higher strength than those of the samples activated with NaOH and KOH, as well as the 100% OPC sample. In particular, the hydration activity index of the 50% BFS and 50% OPC sample activated with KCl exceeded 100% at all ages and reached 127% at 28 d. This demonstrated that KCl did not affect the instability of the minerals in OPC because the pH was not as high as NaOH and KOH. Cl participated in a rapid hardening reaction with OPC, where the subsequent hydration reaction of alkali C3A also affected BFS and FA [34,35,36]. The amounts of NaOH and KOH added in this study were excessive, while KCl was used at a level that can develop appropriate performance for the mixtures of OPC and mineral admixture. Therefore, further research on this is required to determine the optimal activator dosage for strength development.
The 50% mineral admixture (BFS or FA) and 50% OPC mortar samples with no added activator were compared to the samples with added activators to evaluate the strength intensification rate for each activator according to age and curing condition (Figure 6). The samples activated using NaOH and KOH exhibited a significant reduction in strength at all ages, while those with KCl showed improved strength. In particular, the 50% BFS and 50% OPC sample with a KCl activator exhibited a compressive strength of 34.6 MPa after 3 d, which was >90% higher than the compressive strength of the sample without an activator (18.2 MPa). This compressive strength was even higher than that of the 100% OPC sample (30.3 MPa). These findings confirmed that the use of KCl had a beneficial effect on the strength intensification rates of the samples with BFS and FA at all ages. This effect was maximized in the early stages because the addition of KCl to the 50% BFS and 50% OPC mixture facilitated a faster setting rate than the 100% OPC mixture. Fast setting time indicates that a large number of hydrates were produced throughout the sample in the initial stage, which would have filled the pores in the sample and caused high strength to be expressed. It is judged that KCl promotes the generation of hydrates that should be expressed in the long term, resulting in high initial strength. This increase in strength was attributed to accelerated hydration in the early stages, which even affected the strength at 28 d.
The compressive strength of the FA samples was generally lower than the strengths of the BFS samples. In this study, the mineral admixtures were used at the same weight ratio under the same conditions. However, ASTM C989:2018 (Standard Specification for Ground Granulated Blast-Furnace Slag and Mortar) and ASTM C618:2019 (Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete) suggest mixing proportions of BFS and FA to OPC of 50% and 25%, respectively, for the measurement of the hydration activity index [37]. Overall, the use of proper mixing proportions and their effects were not negligible. Therefore, the recommended mixing proportions of mineral admixtures will be considered in future studies. Impact evaluation for the use of cement-derived KCl as an activator should also be further investigated.

3.4. Mineral Composition

Mineral analysis was conducted for the 50% BFS and 50% OPC (Figure 7) and 50% FA and 50% OPC samples (Figure 8). Among the BFS mixtures, the water-cured sample activated with KCl contained hydrocalumite, which was not observed in the samples that used the other activators. Hydrocalumite is known as Friedel’s salt [38]. The presence of Friedel’s salt can compromise the strength of a 100% OPC sample, but this adverse effect is minimized by the presence of the mineral admixture [39]. In addition, a previous study reported that the generation of Friedel’s salt in a mixture of OPC with a substantial proportion of BFS led to enhanced strength due to the filling of pores [40]. Thus, the increased strength due to the use of KCl in this study was also likely attributed the generation of Friedel’s salt. The Friedel’s salt-based hydrate production itself did not appear to occupy the pores significantly compared to the overall hydrate, but the triggering reaction of Friedel’s salt might have influenced the promotion of amorphous products such as the C–H–S system. The hydrate generated by this facilitation reaction filled the voids of the test sample and contributed to the increase in strength. Water curing led to the formation of hydrocalumite, while autoclave curing did not. This indicated that autoclave curing at 180 °C led to the decomposition of CaClOH that constitutes hydrocalumite at ~100 °C [41]. Thus, the loss of strength due to autoclave curing of the BFS mixtures was related to the decomposition of hydrocalumite and amorphous minerals. Friedel’s salt-based hydrate was decomposed in all test samples, but it seems that the BFS mixture, where a relatively substantial number of Friedel’s salt-based hydrates are present, was significantly affected. In the case of the FA mixture, the production of tobermorite under high-temperature and high-pressure conditions seems to have had a greater influence on the intensity than the decomposition of the product.
The FA mixtures activated with KCl also produced hydrocalumite under water curing, but not autoclave curing. In addition to the decomposition of hydrocalumite, tobermorite and katoite were formed during autoclave curing and contributed to strength development with low density compared to C–S–H generated at room temperature, and had a high volume stability. The positive pore-filling effect of the minerals generated in the FA mixtures was larger than the negative effect of the decomposition of minerals such as hydrocalumite. Thus, the compressive strength increased overall.

4. Conclusions

This study provides basic insights into the use of cement-derived KCl as an activator for plain mortar and concrete. Reagent-grade KOH and NaOH were used as alkali activators for comparison, and the basic characteristics of mortar comprising only mineral admixture or mineral admixture with OPC as a binder were analyzed. The conclusions of this study are as follows:
  • The setting of the mortar paste due to the addition of KCl was slightly slower than pastes containing the strong alkali activators. However, setting within 24 h was achieved when the mineral admixture was used alone, and the setting of the mineral admixture and OPC mixtures was accelerated.
  • The fluidity of the mortar was maintained or decreased slightly with the addition of KCl and the alkali activators due to increased mortar viscosity.
  • Analysis of compressive strength demonstrated that the 100% mineral admixture samples activated with KCl were not as strong as the samples activated with NaOH and KOH. However, the activity index values of the 50% BFS and 50% OPC sample activated with KCl was 100% or more at all ages, and especially 127% at 28 d and 135% under autoclave condition.
  • Water curing of the samples with KCl led to the formation of hydrocalumite, or Friedel’s salt. However, hydrocalumite decomposed during autoclave curing at 180 °C.
  • The addition of KCl accelerated setting, improved the early stage hydration activity of the mineral admixtures and OPC mixtures, and increased the strength by >20% compared to the mixtures without an activator at 28 d.
Overall, these findings demonstrated that KCl has higher applicability in mixtures of cement and mineral admixtures than in mineral admixtures alone. The optimal application conditions of KCl as an activator for plain concrete products should be further investigated based on the analysis of its properties in low-cement mixtures at different proportions, and in the presence of hydrocalumite based on a controlled accelerated curing temperature.

Author Contributions

Conceptualization, J.-M.K.; methodology, J.-M.K. and H.-B.C.; software, H.-B.C.; validation, J.-M.K. and S.-S.K.; formal analysis, H.-B.C. and S.C.; investigation, J.-M.K.; resources, J.-M.K. and S.-S.K.; data curation, H.-B.C. and S.-M.C.; writing—original draft preparation, J.-M.K. and H.-B.C.; writing—review and editing, J.-M.K. and H.-B.C. and S.C.; visualization, H.-B.C.; supervision, J.-M.K.; project administration, J.-M.K.; funding acquisition, J.-M.K. All authors have read and agreed to the published version of the manuscript.

Funding

Not applicable.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

This work was supported by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) and the Ministry of Trade, Industry & Energy (MOTIE) of the Republic of Korea (No. 20182010202100) and This work was also supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIP) (No. NRF-2020R1A2C2013161).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Kim, Y.S.; Yu, G.M.; Mun, K.J. Strength Characteristics of Solidified Soil with Hardening Agents made of Industrial By-Products. J. Korean Geo-Environ. Soc. 2012, 13, 19–26. [Google Scholar]
  2. Flower, D.J.M.; Sanjayan, J.G. Greenhouse gas emissions due to concrete manufacture. Int. J. Life Cycle Assess. 2007, 12, 282–288. [Google Scholar] [CrossRef]
  3. Olivier, J.G.J.; Janssens-Maenhout, G.; Muntean, M.; Peters, J. Trends in Global CO2 Emission: 2013/2014/2015 Report; PBL Netherlands Environmental Assessment Agency and European Commission Joint Research Centre: Ispra, Italy; Hague, The Netherlands, 2015. [Google Scholar]
  4. Nazari, A.; Shadi, R. Splitting tensile strength of concrete using ground granulated blast furnace slag and SiO2 nano particles as binder. Energy Build. 2011, 43, 864–872. [Google Scholar] [CrossRef]
  5. Felekoglu, B.; Türkel, S.; Kalyoncu, H. Optimization of fineness to maximize the strength activity of high-calcium ground fly ash-Portland cement composites. Constr. Build. Mater. 2009, 23, 2053–2061. [Google Scholar] [CrossRef]
  6. Bezjak, A. On the Determination of Rat Constants for Hydration Processes in Cement pastes. Cem. Concr. Res. 1981, 10, 553–563. [Google Scholar] [CrossRef]
  7. Fernandez-Jimenez, A. Determination of Kinetic Equations of Alkaline Activation of Blast Furnace Slag by Means of Calorimetric Data. J. Therm. Anal. Calorim. 1998, 52, 945–955. [Google Scholar] [CrossRef]
  8. Bernal, S.A.; de Gutiérrez, R.M.; Provis, J.L. Engineering and durability properties of concretes based on alkali-activated granulated blast furnace slag/metakaolin blends. Constr. Build. Mater. 2012, 33, 99–108. [Google Scholar] [CrossRef]
  9. Collins, F.; Sanjayan, J.G. Microcracking and strength development of alkali activated slag concrete. Cem. Concr. Compos. 2001, 23, 345–352. [Google Scholar] [CrossRef]
  10. Wardhono, A.; Law, D.W.; Molyneaux, T.C.K. Long term performance of alkali activated slag concrete. J. Adv. Concr. Technol. 2015, 13, 187–192. [Google Scholar] [CrossRef] [Green Version]
  11. El-Feky, M.S.; Kohail, M.; El-Tair, A.M.; Serag, M.I. Effect of microwave curing as compared with conventional regimes on the performance of alkali activated slag pastes. Constr. Build. Mater. 2020, 233, 117268. [Google Scholar] [CrossRef]
  12. Hamed, N.; El-Feky, M.S.; Kohail, M.; Nasr, E.-S.-A.R. Effect of nano-clay deagglomeration on mechanical properties of concrete. Constr. Build Mater. 2019, 205, 245–256. [Google Scholar] [CrossRef]
  13. Amer, I.; Kohail, M.; El-Feky, M.S.; Rashad, A.; Khalaf, M.A. Evaluation of Using Cement in Alkali-Activated Slag Concrete. Int. J. Sci. Technol. Res. 2020, 9, 245–248. [Google Scholar]
  14. Angulo-Ramírez, D.E.; de Gutiérrez, R.M.; Puertas, F. Alkali-activated Portland blast-furnace slag cement: Mechanical properties and hydration. Constr. Build. Mater. 2017, 140, 119–128. [Google Scholar] [CrossRef]
  15. Al-Kutti, W.; Nasir, M.; Johari, M.A.M.; Islam, A.B.M.S.; Manda, A.A.; Blaisi, N.I. An overview and experimental study on hybrid binders containing date palm ash, fly ash, OPC and activator composites. Constr. Build. Mater. 2018, 159, 567–577. [Google Scholar] [CrossRef]
  16. Puertas, F.; Palacios, M.; Vázquez, T. Carbonation process of alkali-activated slag mortars. J. Mater. Sci. 2006, 41, 3071–3082. [Google Scholar] [CrossRef]
  17. Yang, K.H.; Song, J.K.; Ashour, A.F.; Lee, E.T. Properties of cementless mortars activated by sodium silicate. Constr. Build Mater. 2008, 22, 1981–1989. [Google Scholar] [CrossRef] [Green Version]
  18. Gao, Z.; Zhang, P.; Guo, J.; Wang, W. Bonding behavior of concrete matrix and alkali-activated mortar incorporating nano-SiO2 and polyvinyl alcohol fiber: Theoretical analysis and prediction model. Ceram. Int. 2021, 47, 31638–31649. [Google Scholar] [CrossRef]
  19. Zhang, P.; Wang, K.; Wang, J.; Guo, J.; Hu, S.; Ling, L. Mechanical properties and prediction of fracture parameters of geopolymer/alkali-activated mortar modified with PVA fiber and nano-SiO2. Ceram. Int. 2020, 46, 20027–20037. [Google Scholar] [CrossRef]
  20. Zhang, P.; Gao, Z.; Wang, J.; Wang, K. Numerical modeling of rebar-matrix bond behaviors of nano-SiO2 and PVA fiber reinforced geopolymer composites. Ceram. Int. 2021, 47, 11727–11737. [Google Scholar] [CrossRef]
  21. Rha, C.Y.; Seong, J.W.; Kim, C.E. The preparation and characterization of blended cement used by-pass dust. J. Korean Ceram. Soc. 1999, 36, 618–624. [Google Scholar]
  22. Han, M.C.; Lee, D.J. Physical and Chemical Properties of Chlorine Bypass System-Dust from Cement Manufacturing. J. Korean Recycl. Constr. Resour. Inst. 2019, 7, 310–315. [Google Scholar] [CrossRef]
  23. Lee, Y.H.; Han, D.H.; Lee, S.M.; Eom, H.K.; Kim, S.S. A Study on the Cation Extraction and Separation in Cement Industrial By-products for Applications to the Carbonation Process. Appl. Chem. Eng. 2019, 30, 34–38. [Google Scholar] [CrossRef]
  24. Jang, Y.H.; Lee, Y.H.; Kim, J.Y.; Park, I.G.; Lee, J.Y.; Park, B.H.; Lee, S.M.; Kim, S.S. A study on the optimization of Ion Exchange Resin operating condition for removal of KCl from CKD extract. J. Korean Appl. Sci. Technol. 2019, 36, 1088–1095. [Google Scholar] [CrossRef]
  25. Lee, E.H.; Jeong, C.I.; Park, S.K.; Lee, H.H. The Influence of KCl on the Hydration Property of OPC. J. Korean Ceram. Soc. 2002, 39, 943–947. [Google Scholar] [CrossRef]
  26. Standard Specification for Ground Granulated Blast-Furnace Slag and Mortar; ASTM C989:2018; ASTM International: West Conshohocken, PA, USA, 2018.
  27. Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus; ASTM C204:2018; ASTM International: West Conshohocken, PA, USA, 2018.
  28. Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle; ASTM C191:2019; ASTM International: West Conshohocken, PA, USA, 2019.
  29. Standard Test Method for Flow of Hydraulic Cement Mortar; ASTM C1437:2020; ASTM International: West Conshohocken, PA, USA, 2020.
  30. Standard Test Method for Compressive Strength of Hydraulic Cement Mortars; ASTM C109:2020; ASTM International: West Conshohocken, PA, USA, 2020.
  31. Carde, C.; François, R.; Torrenti, J.M. Leaching of both calcium hydroxide and C-S-H from cement paste: Modeling the mechanical behavior. Cem. Concr. Res. 1996, 26, 1257–1268. [Google Scholar] [CrossRef]
  32. Bizzozero, J.; Gosselin, C.; Scrivener, K.L. Expansion mechanisms in calcium aluminate and sulfoaluminate systems with calcium sulfate. Cem. Concr. Res. 2014, 56, 190–202. [Google Scholar] [CrossRef]
  33. Alahrache, S.; Winnefeld, F.; Champenois, J.B.; Hesselbarth, F.; Lothenbach, B. Chemical activation of hybrid binders based on siliceous fly ash and Portland cement. Cem. Concr. Res. 2016, 66, 10–23. [Google Scholar] [CrossRef]
  34. Yokoyama, S.; Nakano, T.; Tsuchida, Y.; Maki, I. Influence of Chlorine on Clinker Formation from Incinerated Ash of Urban Composite Waste. Cem. Sci. Concr. Technol. 1999, 53, 140–145. [Google Scholar] [CrossRef]
  35. Sutou, K.; Harada, H.; Ueno, U. Chlorine By-pass System for stable Kiln Operation and the Recycling of waste. Int. Cem. Rev. 1999, 634, 28–35. [Google Scholar] [CrossRef]
  36. Miyahara, S.; Nakamura, A.; Sakai, E.; Daimon, M. Hydration of cement with KCl. Cem. Sci. Concr. Technol. 1999, 53, 58–62. [Google Scholar]
  37. Standard Specification for Coal Fly ash and Raw or Calcined Natural Pozzolan for Use in Concrete; ASTM C618:2019; ASTM International: West Conshohocken, PA, USA, 2019.
  38. Bothe, J.V., Jr.; Brown, P.W. PhreeqC modeling of Friedel’s salt equilibria at 23 ± 1 °C. Cem. Concr. Res. 2004, 34, 1057–1063. [Google Scholar] [CrossRef]
  39. Qiao, C.; Suraneni, P.; Weiss, J. Flexural strength reduction of cement pastes exposed to CaCl2 solutions. Cem. Concr. Compos. 2018, 86, 297–305. [Google Scholar] [CrossRef]
  40. Kim, T.W.; Kim, I.T.; Seo, K.Y.; Park, H.J. Strength and pore characteristics of OPC-slag Cement paste mixed with polyaluminum chloride. Constr. Build. Mater. 2019, 223, 616–628. [Google Scholar] [CrossRef]
  41. Galan, I.; Perron, L.; Glasser, F.P. Impact of chloride-rich environments on cement paste mineralogy. Cem. Concr. Res. 2015, 68, 174–183. [Google Scholar] [CrossRef]
Materials 14 06091 g001 550
Figure 1. Mineral composition of CBD and KCl.
Figure 1. Mineral composition of CBD and KCl.
Materials 14 06091 g001
Materials 14 06091 g002 550
Figure 2. Flow of samples with KCl separated from CBD, NaOH and KOH as activators.
Figure 2. Flow of samples with KCl separated from CBD, NaOH and KOH as activators.
Materials 14 06091 g002
Materials 14 06091 g003a 550Materials 14 06091 g003b 550
Figure 3. Setting of the cement-containing and non-cement mortar with KCl separated from CBD, NaOH, and KOH as activators, namely, (a) 100% FA, (b) 100% BFS, (c) 50% FA and 50% OPC, and (d) 50% BFS and 50% OPC.
Figure 3. Setting of the cement-containing and non-cement mortar with KCl separated from CBD, NaOH, and KOH as activators, namely, (a) 100% FA, (b) 100% BFS, (c) 50% FA and 50% OPC, and (d) 50% BFS and 50% OPC.
Materials 14 06091 g003aMaterials 14 06091 g003b
Materials 14 06091 g004 550
Figure 4. Compressive strength and activity index of the 100% BFS mortar sample with KCl separated from CBD, NaOH, and KOH as activators.
Figure 4. Compressive strength and activity index of the 100% BFS mortar sample with KCl separated from CBD, NaOH, and KOH as activators.
Materials 14 06091 g004
Materials 14 06091 g005 550
Figure 5. Compressive strength and activity index of the 50% mineral admixture (BFS or FA) and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Figure 5. Compressive strength and activity index of the 50% mineral admixture (BFS or FA) and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Materials 14 06091 g005
Materials 14 06091 g006 550
Figure 6. Compressive strength intensification rate of the KCl separated from CBD, NaOH, and KOH activators in the 50% mineral admixture (BFS or FA) and 50% OPC mortar samples.
Figure 6. Compressive strength intensification rate of the KCl separated from CBD, NaOH, and KOH activators in the 50% mineral admixture (BFS or FA) and 50% OPC mortar samples.
Materials 14 06091 g006
Materials 14 06091 g007 550
Figure 7. Mineral analysis of the 50% BFS and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Figure 7. Mineral analysis of the 50% BFS and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Materials 14 06091 g007
Materials 14 06091 g008 550
Figure 8. Mineral analysis of the 50% FA and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Figure 8. Mineral analysis of the 50% FA and 50% OPC mortar samples with KCl separated from CBD, NaOH, and KOH as activators.
Materials 14 06091 g008
Table
Table 1. Binders, replacement ratios, alkali activator types, and alkali activator dosages used in this experimental design.
Table 1. Binders, replacement ratios, alkali activator types, and alkali activator dosages used in this experimental design.
Binder TypeMineral Admixture
Replacement Ratio (wt%)		Alkali Activator TypeAlkali Activator Dosage (wt%)
OPC
BFS
FA		0
50
100		None
NaOH
KOH
KCl (by-product)		10% to mineral admixture
Table
Table 2. Mixtures used to prepare cement-containing and non-cement mortar samples.
Table 2. Mixtures used to prepare cement-containing and non-cement mortar samples.
MixtureW/B
(%)		Air
(%)		Water (kg/m3)Binder (kg/m3)Sand (kg/m3)Alkaline Activator (kg/m3)Total (kg/m3)
OPCBFSFANaOHKOHKCl
NoneOPC100405206515--1545---2265
BFS50204255255-1532---2247
FA50201251-2511505---2208
NaOHBFS50204255255-153226--2273
BFS100203-507-152051--2280
FA50201251-251150525--2233
FA100196--489146849--2202
KOHBFS50204255255-1532-26-2273
BFS100203-507-1520-51-2280
FA50201251-2511505-25-2233
FA100196--4891468-49-2202
KClBFS50204255255-1532--262273
BFS100203-507-1520--512280
FA50201251-2511505--252233
FA100196--4891468--492202
Table
Table 3. Chemical composition of the binders and the CBD used in this experiment.
Table 3. Chemical composition of the binders and the CBD used in this experiment.
CaOSiO2Al2O3Fe2O3MgOSO3K2OClOtherTotal
OPC65.8417.443.843.273.203.251.440.051.67100
BFS48.1330.5112.930.552.702.580.600.011.99100
FA6.9149.7021.6611.132.450.871.530.195.56100
CBD44.47.743.231.920.5513.689.8715.72.91100
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Choi, H.-B.; Kim, J.-M.; Choi, S.-M.; Kim, S.-S. KCl Extracted from Chlorine Bypass Dust as Activator for Plain Concrete. Materials 2021, 14, 6091. https://doi.org/10.3390/ma14206091

AMA Style

Choi H-B, Kim J-M, Choi S-M, Kim S-S. KCl Extracted from Chlorine Bypass Dust as Activator for Plain Concrete. Materials. 2021; 14(20):6091. https://doi.org/10.3390/ma14206091

Chicago/Turabian Style

Choi, Hong-Beom, Jin-Man Kim, Sun-Mi Choi, and Sung-Su Kim. 2021. "KCl Extracted from Chlorine Bypass Dust as Activator for Plain Concrete" Materials 14, no. 20: 6091. https://doi.org/10.3390/ma14206091

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.