Characterization of a Macro- and Micro-Textured Titanium Grade 5 Alloy Surface Obtained by Etching Only without Sandblasting
Next Article in Special Issue
Facile Synthesis of g-C3N4/TiO2/Hectorite Z-Scheme Composite and Its Visible Photocatalytic Degradation of Rhodamine B
Previous Article in Journal
The Influence of Solvent on the Crystal Packing of Ethacridinium Phthalate Solvates
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 13
Issue 22
10.3390/ma13225072
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Cost-Effective Production of TiO2 with 90-Fold Enhanced Photocatalytic Activity Via Facile Sequential Calcination and Ball Milling Post-Treatment Strategy

by
Anantha-Iyengar Gopalan
1,†,
Jun-Cheol Lee
2,†,
Gopalan Saianand
3,
Kwang-Pill Lee
1,
Woo-Young Chun
4,
Yao-long Hou
5,
Venkatramanan Kannan
6,
Sung-Sik Park
5 and
Wha-Jung Kim
1,*
1
School of Architecture and Civil Engineering, Daegyeong Regional Infrastructure Technology Development Center, Kyungpook National University, Daegu 41566, Korea
2
Department of Architecture, Seowon University, Cheongju 28674, Korea
3
Global Centre for Environmental Remediation (GCER), Faculty of Science, The University of Newcastle, Callaghan 2308, NSW, Australia
4
Real-scale Fire Testing; Research Center, Korea Conformity Laboratories, 33-72, Eonjang 1-Gil, Samcheok-si, Gangwon-do 25913, Korea
5
Department of Civil Engineering, Kyungpook National University, 80 Daehakro, Buk-gu, Daegu 41566, Korea
6
Department of Physics, SCSVMV Deemed University, Kanchipuram 631561, India
*
Author to whom correspondence should be addressed.
†
Authors contributed equally to this work.
Materials 2020, 13(22), 5072; https://doi.org/10.3390/ma13225072
Submission received: 6 October 2020 / Revised: 28 October 2020 / Accepted: 6 November 2020 / Published: 10 November 2020
(This article belongs to the Special Issue Advanced Photocatalytic Materials for Water Treatment)
Browse Figures
Review Reports Versions Notes

Abstract

:
Titanium dioxide (TiO2), the golden standard among the photocatalysts, exhibits a varying level of photocatalytic activities (PCA) amongst the synthetically prepared and commercially available products. For commercial applications, superior photoactivity and cost-effectiveness are the two main factors to be reckoned with. This study presents the development of simple, cost-effective post-treatment processes for a less costly TiO2 to significantly enhance the PCA to the level of expensive commercial TiO2 having demonstrated superior photoactivities. We have utilized sequential calcination and ball milling (BM) post-treatment processes on a less-costlier KA100 TiO2 and demonstrated multi-fold (nearly 90 times) enhancement in PCA. The post-treated KA100 samples along with reference commercial samples (P25, NP400, and ST01) were well-characterized by appropriate instrumentation and evaluated for the PCA considering acetaldehyde photodegradation as the model reaction. Lattice parameters, phase composition, crystallite size, surface functionalities, titanium, and oxygen electronic environments were evaluated. Among post-treated KA100, the sample that is subjected to sequential 700 °C calcination and BM (KA7-BM) processes exhibited 90-fold PCA enhancement over pristine KA100 and the PCA-like commercial NP400 (pure anatase-based TiO2). Based on our results, we attribute the superior PCA for KA7-BM due to the smaller crystallite size, the co-existence of mixed anatase-srilankite-rutile phases, and the consequent multiphase heterojunction formation, higher surface area, lattice disorder/strain generation, and surface oxygen environment. The present work demonstrates a feasible potential for the developed post-treatment strategy towards commercial prospects.

1. Introduction

Titanium dioxide (TiO2) photocatalysis is predominantly being utilized as a pivotal solution to mitigate issues related to energy scarcity and environmental protection [1,2,3,4,5,6,7]. The increasing photocatalytic application prospects of TiO2 create demand for its mass production and thus a large number of companies produce varieties of TiO2 products [8,9,10]. However, there exist wide variations in the photocatalytic activities (PCA) as well as the cost per kilogram (Kg) among the commercial products [11]. The photocatalytic efficiency of various TiO2 is compared with relevance to a particular model photoreaction, for example, gaseous acetaldehyde (AD) degradation or dye degradation in solution, etc. [12]. One should keep in mind that PCA of TiO2 depends on a large number of factors that include crystalline phase structure, phase composition, particle size, surface area, porosity, bandgap, morphology, and surface-bound hydroxyl species [12,13]. These factors vary among the commercial TiO2 products leading to differences in the PCA. There is a controversy in the literature on deciding the combination of the above-mentioned factors that determine the PCA of the particular commercial TiO2 [14,15]. Among the commercial TiO2 products, Degussa P25 TiO2 has been mostly considered as the research standard because it has substantially higher PCA than most of the other available samples of TiO2 [16]. For the photocatalytic application purposes and also mitigating the inherent problems associated with pristine TiO2, post-treatment processes of commercial TiO2 have been utilized to enhance the PCA of TiO2. The associated total costs (the price of the TiO2 and the post-treatment) will ultimately widen the potential utilities in real-life applications (Scheme 1). Hence, it is challenging to design a simple and cost-effective post-treatment strategy towards enhancing PCA of a commercially low-cost TiO2 to the level of P25 TiO2 or relatively inexpensive TiO2.
Considerable research activities are being focused on the enhancement of photocatalytic properties of TiO2 that mostly involve pre-synthetic or in-situ modification strategies [17]. Reports on post–modification properties of TiO2 are scarce, especially with relevance to modification of commercial TiO2. One must note that the smaller particle size of TiO2 can result in larger surface area and higher photocatalytic activity. Towards this direction, the grinding process of the powder, like dry/wet ball milling (BM), was employed to obtain smaller particle size and narrower size distribution [18,19]. On the other hand, it is to be noted that phase, crystallite size, and crystallinity of TiO2 play an important role in the enhancement of photocatalytic activity, and these modifications were attempted by the calcination process. The effect of calcination temperature on a phase transition of TiO2 from anatase to rutile was studied in temperatures ranging from 350 to 750 °C [20]. A phase mixture of anatase and brookite was found at a calcination temperature of 200 °C, a mixture of three phases (anatase, rutile, and brookite) was found at 600 °C, and a complete transformation into rutile phase was noticed at 800 °C [21]. The increase in crystallite size and crystallinity of TiO2 was identified by increasing the calcination temperature. However, an explanation of the effect of the changes in crystallite size and phase transformation of TiO2 on the photocatalytic activity has not been detailed or correlated. Recently, a hydrothermal post-treatment was adopted to enhance the photocatalytic activity of TiO2 [22]. Taking photo-decolorization of Rhodamine B dye as the model reaction, a nearly 10 times increase in photoactivity was reported for the hydrothermal-treated TiO2 with water as solvent as compared with that of the untreated ones. The enhancement in photoactivity was ascribed due to the formation of desirable anatase phase, porous structure, large surface area, small particle size, and hydrophilic surface. Literature reveals that new and cost-effective post-treatment of TiO2 is highly warranted, especially on commercial products, towards realizing significant enhancement in the photocatalytic activities. In this work, we have chosen KA100 TiO2 with a price of 4$/Kg and post-treated with a combination of calcination and BM processes to enhance the PCA of KA100 to the level closer to commercially available expensive TiO2 samples such as P25 (~54$/Kg), ST01 (~75$/Kg), and NP400 (~54$/Kg). The post-treatment conditions for KA100 which generate enhanced PCA with P25 or other listed commercial samples have been optimized and the reasons for the enhanced PCA are explained based on the modification of properties derived through post-treatment and the enhancement in the PCA for acetaldehyde (AD) degradation.

2. Materials and Methods

2.1. Chemicals

The commercial TiO2 samples, ST01 (Ishihara Sangyo, Yokkaichi, Japan), P25 (Degussa, Frankfurt, Germany), NP400 (Bentech Frontier, Yongbong-ro Buk-gu, Korea), and KA100 (Cosmo chemicals, Seoul, Korea), were purchased and used.

2.2. Calcination and Ball Milling

KA100 was calcined at different temperatures and the samples were designated based on the temperature of calcination. The calcined sample was subjected to wet BM using a ball milling machine (IBMT-38-4, As One, Osaka, Japan). A typical procedure is outlined. The alumina milling jar (having 1000 mL volume) was filled with 40 g of a calcined sample, 40 g of distilled water, and alumina balls (having a diameter of 10 mm). The rotational speed of the motor in the BM machine was 650 rpm and the BM duration was 3 h. After three hours of BM, the sample was washed with distilled water and dried at 100 °C for 2 h.

2.3. Characterization

The crystal structure, phase composition, and crystallinity of the samples were examined by an X-ray diffraction (XRD) analyzer (D/Max-2500, Rigaku, Tokyo, Japan) [23]. The scanning angle 2θ was varied from 5° to 80° with a step of 0.02°. The operating voltage, applied current, and Cu Kα radiation were 45 kV, 40 mA, and 1.5418 Å, respectively. For crystallinity determination, CaF2 was used as the standard and the procedure is relayed elsewhere [24,25]. X-ray photoelectron spectrum (XPS) was recorded with an X-ray Photoelectron Spectroscopy (NEXSA, ThermoFisher, Waltham, MA, USA) using an Al-Kα monochromator source (1486.6 eV) [26,27,28]. Raman spectra were recorded in the range 100 to 2700 cm−1 using a Raman spectrometer (inVia reflex, Renishaw, Wotton-under-Edge, UK), equipped with a 536 nm laser [29]. The band gaps of the samples were determined by Ultraviolet-visible diffuse reflectance spectroscopy (S-3100, Seoul, Scinco, Korea) in the wavelength region 200 to 700 nm.

2.4. Photocatalytic Decomposition of Acetaldehyde (AD)

The photocatalytic AD degradation experiment was designed and carried out by the gas bag A method standardized by the Korea Photocatalyst Association. Typically, about 1.0 g of the photocatalyst was dispersed into 0.5 g of water to obtain a stable slurry. The photocatalytic slurry was applied on the surface of a pre-cleaned circular glass plate (90 mm of diameter) and dried at 100 °C for 2 h. The Tedlar bag (3 L volume) with the coated glass plate was placed in a stainless-steel box. The diluted AD gas with air having an initial AD concentration of 100 ppm was inducted within the Tedlar bag set-up. The sample was irradiated with a UV lamp (Sankyo Denki, Kanagawa, Japan, UV wavelength from 310 to 400 nm, 15 W) fixed in the stainless-steel box. The ultraviolet intensity of the lamp was 1.0 mW/cm2 on the sample surface. The concentration of AD gas was monitored with the gas analyzer (Gas sampling pump kit, GV-100 s, Gastec Corporation, Kanagawa, Japan) every 30 min over 2 h.

3. Results and Discussion

3.1. Influence of Calcination and BM Processes on Microstructural and Electronic Properties

Figure 1 presents the XRD patterns of pristine KA100, calcined KA100 at different temperatures, few calcined + BM, and reference TiO2 (P25, NP400, and ST01) samples. XRD patterns were consistent with data of the TiO2 comprising of a mixture of anatase (A) (major weight proportion, ~97%) and rutile (R) (minor weight proportion, ~3%) (Table 1). Particularly, the KA7-BM showed a higher R phase proportion (3.30%). To note, the R% increased from 2.78% to 3.30% when the KA7 was subsequently subjected to BM. It is inferred that the mechanical force/energy involved in BM could transform A to R phase. It must be noted that NP400 and ST01 samples were pure A samples, whilst P25 comprises of 77.90% A and 22.10% R phases. Generally, TiO2 exhibits higher photocatalytic activities because of the synergistic effects from the two phases, band alignments, and the probable heterojunction/interfacial electron transfer [10,23,30]. TiO2 with a mixture of A and R compositions has been reported to exhibit lower rates for the recombination of photo-generated electrons and holes, and R contributes significantly to better light absorption [10]. The literature suggests that a mass ratio of 3:7 (R to A) is the best for achieving high photocatalytic activities [31]. However, other reports detail that even a lesser proportion of R can also yield improved photoactivities, and the parameters like crystallite size, surface area, and optical absorption will determine the PCA in such cases [18]. Also, a mixture of A and brookite (B), as well as R and B, can result in fast photodegradation rates of organic molecules [32]. In the present case, non-calcined, calcined, and calcined + ball milled KA100 samples did not show even a trace of the B phase.
Most commonly, the particle size is determined using X-ray diffraction measurements and by the help of the Scherrer equation [33]. However, keeping note that Scherrer equation is related to a sharp peak of X-ray diffraction and there are limitations based on the use of non-monochromatic X-ray source, dependence on the instrument as well as the relationship between signal, sample to criterion noise, and influences by peak broadening, considerations are given to improve the reliability of size determinations by other methods [34]. Modification through the Williamson-Hall (W-H) method was developed by considering the contributions of additive effects of different angular dependencies of the size and strain/disorder functions for reflections [35]. To note, the W-H method for crystallite size and strain analysis is still underutilized as compared to the Scherrer method and this may be because there are several limitations of the W-H approach and few further modifications of the W-H approach were suggested [36]. The Rietveld method (R-M) has been introduced considering a whole-pattern fitting approach instead of single-peak analysis [37]. The main advantage of the R-M is that it can effectively minimize or eliminate the inaccuracies arising from preferred orientation, particle statistics, micro-absorption, peaks overlapping, and detection of amorphous phase and trace phases [38]. Based on the R-M and refinements, the amorphous and the nanocrystalline alloys such as Fe–B–Nb alloy structure [39] and Ni-Mo alloys [40] were analyzed [41]. However, one can notice at least two important preconditions for quantitative crystallite size analysis such as: (1) the quantified phase is the crystalline phase, and (2) the crystal structure is known [42]. Particularly, if amorphous material is involved, quantitative results could not be achieved directly and with precision. Keeping all these advancements happening for the determination of crystallite size, one can notice through the literature that the Scherrer equation is almost universally used for the determination of crystallite size, of course, despite its limitations, and reliability of meaningful size information derived from such calculations. In this work, it is reasonable to consider the formation of the amorphous state of any of the TiO2 phases (anatase, rutile, brookite, or any other) upon post-treatment of TiO2 samples. Hence, the Scherrer method was used in this work for obtaining a comparative analysis of the crystal structural parameters among the samples.
The crystallite size was calculated using the Scherrer formula which suggested that the crystallite size of KA100 increases marginally from 60 nm (for non-calcined) to 65 nm (for the calcinations temperature of 1000 °C) with calcination treatment. The KA7-BM sample had the smallest size amongst the investigated KA100 samples. The decrease in particle size after BM has been reported and the extent of decrease depends on the energy of the BM [20]. A drastic increase in PCA of close to one hundred times that of the untreated sample was witnessed for the BM processed samples. The crystallite size of the ST01, NP400, and P25 is much smaller (6, 17, 20 nm, respectively) than the calcined KA100 and BM processed samples. The lattice parameters of crystalline KA100 did not change either by calcination or by B, signifying that these post-treatments did not influence the crystal structure. The A crystallinity was estimated by the full width at half maximum (FWHM) at the 101 main peaks with reference to CaF2 as the standard (Table 1 and Table 2). Whilst the KA4 is 100% crystalline, the value decreased to 72.0% for KA7. However, the crystallinity increased to 89.2% upon subsequent BM. The amorphous and metastable srilankite (S) (TiO2-II phase, orthorhombic) formation could be possible upon calcination at 700 °C [32,43]. This could be the reason for the decreased crystallinity at 700 °C. However, subsequent BM (mechanical activation) could induce transformations of amorphous S to crystalline S and R phase formation. The increased crystallinity and R proportion for KA7-BM are evident from Table 1 and Table 2. The decrease in particle size upon BM of KA7 could be correlated to the phase transformations (A to S to R) as detailed above [44]. It is therefore envisaged that subsequent BM processing of KA7 caused the deconstruction and then reconstruction of the crystal grains [45]. Thus, KA7-BM is expected to possess a multiphase microstructure [43]. Specific surface area and pore size of the selected samples were obtained from the N2 adsorption-desorption isotherms and presented (Table 1 and Table 2). KA7-BM showed a nearly 10% increase in surface area as compared to KA7 (Table 1 and Table 2). The larger surface area of the KA7-BM is correlated to the smaller crystallite size as compared to KA7.
The optical bandgap of different samples was investigated by diffuse reflectance measurements and the derived Tauc plots (Figure 2). It was noticed that the KA100 samples comprising of A-R phases have an energy bandgap between 3.06 and 3.03 eV. Keeping in mind that the bandgap of a semiconductor can be influenced by several factors such as doping, synthetic parameters, lattice mismatch [46], crystallite size [47], annealing/calcination temperature [48], and phase composition, and also based on the recent reports that inform “the bandgap determination through extrapolation of Tauc segment to the hv (X) axis is not appropriate for samples containing more than one prominent optical absorbing center/or phase” [49,50], the bandgap was also determined the by extrapolation of the linear part of the dependence to the baseline (Figure 2). The optical band as determined by the Tauc plot and baseline extrapolation method is referred to as BG-T and BG-BE, respectively. Apparently, the bandgap was not altered much by the post-treatment processes for KA100 (Table 1 and Table 2).
The peak positions of Raman bands corresponding to A phase in non-calcined KA100 are compared to other post-treated KA100 samples (Figure 3, Table 3). The Raman bands at 142.02 cm−1 (Eg), 195.5 cm−1 (Eg), 394.6 cm−1 (B1g), 516.3 cm−1 (A1g + B1g), and 638.5 cm−1 (Eg) correspond to the Raman allowed modes of A TiO2. However, the Raman band at 105 cm−1, which is a unique feature of R-TiO2, is not observed or it has very minimum intensity. The Raman B1g mode showed red (lower wavenumber) shifting upon a post (heat)-treatment, whilst A1g + B1g and Eg bands showed blue (higher wavenumber) shifts (Figure 3). Factors such as crystallite size, the composition of mixed phases (A to R), the nature and magnitude of the defects in the crystal structure, and stoichiometry deviation can influence these Raman bands either alone or in conjunction. Raman spectrum of post-treated KA100 samples informs that post-treatment of KA100 could have caused one or more of the above-mentioned modifications.
The Ti 2p XPS spectra of KA4, KA7, and KA8 samples exhibited Ti 2p3/2 and Ti 2p1/2 doublets and a satellite peak, which are characteristic peaks associated with the Ti4+ valence state on lattice oxygen of TiO2 [51] (Table 2 and Figure 4). The appearance of Ti 2p3/2 and Ti 2p1/2 peaks (with a separation close to the standard value of 5.6 to 5.7 eV), along with a well-known charge transfer shake-up satellite peak (~13.2 eV higher than the main peak) are characteristics of TiO2 (Table 2). The Ti2p XPS spectrum of KA7-BM shows additional shoulders around 463 and 457 eV that could be assigned to the presence of Ti3+ valence state and associated with oxygen vacancy as the defect in TiO2 crystal lattice [52]. Besides, the Ti2p XPS spectrum of KA7 + BM shows the satellite/shake-up peak at a larger distance (13.50 eV) from the main Ti 2p peak (Table 2). Because the position of the shake-up satellite peak is correlated to the excitation of a valence electron to a previously unoccupied state by the outgoing Ti 2p photoelectron, it is envisaged that the charge transfer characteristics of KA7 + BM can be different from the other samples, possibly due to the lattice disorder and the subtle deviations in the electronic structure. The calcined KA100 samples exhibit a O1s peak at 529.78 eV (Figure 4) that is assigned to oxygen bound to tetravalent Ti ions. The observed difference in the O1s peak position KA7 + BM (529.68 eV) correlates with the probable lattice disorder as inferred from the Ti 2p electronic environments (Figure 3). Besides, the presence of a shoulder at ~533 eV suggests that the BM processed TiO2 surface is partially covered with hydroxide OH groups [53].

3.2. Photocatalytic Degradation of AD

Figure 5a–c depicts the changes in the AD concentration over time due to the photodegradation by the various TiO2 samples under investigation. Typically, non-calcined KA100 decomposes 50% of AD after 2 h, whilst 100% of degradation was evident for KA100 at a similar period (Figure 4a). Interestingly, KA7 + BM degrades AD at a faster rate, and 100% AD decomposition was witnessed by 30 min ahead of KA7 (Figure 5b). P25 and ST01 exhibited much faster AD photodegradation, requiring nearly 60 min for 100% decomposition. However, the PCA of KA7 + BM is similar to NP400 (Figure 5a–c). More quantitative evaluation and comparison of PCA of the studied samples were done by deriving the first-order rate constant of the AD photodegradation (kAD). The values of kAD were determined from the slope of the plots, logarithmic concentration of AD at a time (lnC) versus time (Figure 6a–c). Figure 5d presents the kAD of the non-calcined and calcined samples. The KA7 + BM showed the highest kAD among the studied samples. Figure 5e compares the kAD values between KA7, KA7 + BM, and pristine commercial TiO2 samples (P25, ST01, and NP400). One must note that KA7 has slightly higher kAD than KA8. Due to the higher kAD of KA7 and lower calcination temperature requirement, KA7 was considered for further BM treatment. Hence, the comparison chart included only the kAD values of KA7 and KA7 + BM. The comparison reveals that the PCA of KA7 is increased ~60 times as compared to KA100 and a ~90 times increase was witnessed by the subsequent BM process. The simple BM process of KA7 caused a 45% increase in the kAD of KA7. Interestingly, the photocatalytic performance of KA100 (less expensive, 4$/Kg) could be improved like NP400 (more costly, 54$/kg) by simple post-treatment processes (calcination at 700 °C and subsequent BM). Thus, nearly 13 times less expensive KA100 could be transformed to show the PCA similar to NP400, and nearly 67% enhancement as that of PCA of much costlier ST01 and P25. We strongly believe that further tuning the BM parameters such as power (the energy involved), time, etc., of the KA100 post-treatment process could result in PCA similar to P25 and STO1. On perusal of Figure 5e, it is evident that KA7-BM exhibited the superior PCA amongst the post-treated KA100 samples. Literature suggests that improved photoactivity for TiO2 could arise through various factors such as mixed-phase existence, high surface area, high crystallinity, presence of surface defects, and hydrophobic–hydrophilic transformation [54,55]. A comparative photocatalytic activity study has been performed earlier between two commercial TiO2 powders (Cristal Global, Millennium PC500, and Evonik, P25), taking AD degradation in the gas phase as the model photoreaction [12]. It has been notified that the quantum efficiency of P25 is superior to PC500 based on the higher available surface area. However, the better PCA for PC500 as compared to P25 is attributed to the presence of surface OH groups and alternative reaction pathways even with a lower amount of photogenerated holes. In the present work, the superior photocatalytic performance of KA7-BM (90-fold enhancement over KA100) is attributed to synergistic factors that operate because of the smaller crystallite size, co-existence of A-S-R phases, and the consequent multiphase heterojunction formation, higher surface area, lattice disorder/strain generation, and surface oxygen environment. The outcome of the research paves the way for the development of a simple post-treatment strategy to enhance photocatalytic performance on a cost-effective basis and the consequent commercial prospects for large-scale production of cheaper TiO2 with enhanced photocatalytic performances.

4. Conclusions

In summary, we have successfully prepared a facile and low-cost version of TiO2 through a unique post-treatment strategy involving sequential calcination and ball milling pulverization. The influence of calcined, non-calcined, and calcined and ball-milled samples were analyzed for their microstructural and electronic properties, and the photocatalytic performances were compared with reference commercial samples of TiO2. The experimental results suggest that the as-developed cost-effective TiO2 sample (KA7) possessed excellent photocatalytic activities (90-fold enhancement) for the degradation of acetaldehyde compared to pristine KA100 and were less expensive than their commercial counterparts (P25, NP400, and ST01).

Author Contributions

A.-I.G. and J.-C.L., Conceptualization, Validation, Writing—Original draft and review editing; G.S., Data Curation, Validation, Writing—Review editing; K.-P.L., Writing—Review editing; W.-Y.C., Y.-l.H., V.K., and S.-S.P., Data Curation, Writing—Review editing; W.-J.K., Funding acquisition, Supervision, and Writing—Review editing. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (No. NRF-2018R1A2B2003832).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Li, L.; Yan, J.; Wang, T.; Zhao, Z.-J.; Zhang, J.; Gong, J.; Guan, N. Sub-10 nm rutile titanium dioxide nanoparticles for efficient visible-light-driven photocatalytic hydrogen production. Nat. Commun. 2015, 6, 5881. [Google Scholar] [CrossRef] [PubMed]
  2. Nakata, K.; Fujishima, A. TiO2 photocatalysis: Design and applications. J. Photochem. Photobiol. C Photochem. Rev. 2012, 13, 169–189. [Google Scholar] [CrossRef]
  3. Gopalan, A.-I.; Lee, J.-C.; Saianand, G.; Lee, K.-P.; Sonar, P.; Dharmarajan, R.; Hou, Y.-l.; Ann, K.-Y.; Kannan, V.; Kim, W.-J. Recent Progress in the Abatement of Hazardous Pollutants Using Photocatalytic TiO2-Based Building Materials. Nanomaterials 2020, 10, 1854. [Google Scholar] [CrossRef] [PubMed]
  4. Lang, X.; Saianand, G.; Fu, W.; Ramakrishna, S. Photocatalytic water splitting utilizing electrospun semiconductors for solar hydrogen generation: Fabrication, Modification and Performance. Bull. Chem. Soc. Jpn. 2020. [Google Scholar] [CrossRef]
  5. Nasr, M.; Eid, C.; Habchi, R.; Miele, P.; Bechelany, M. Recent Progress on Titanium Dioxide Nanomaterials for Photocatalytic Applications. ChemSusChem 2018, 11, 3023–3047. [Google Scholar] [CrossRef]
  6. Bahrami, B.; Mabrouk, S.; Adhikari, N.; Elbohy, H.; Gurung, A.; Reza, K.M.; Pathak, R.; Chowdhury, A.H.; Saianand, G.; Yue, W.; et al. Nanoscale control of grain boundary potential barrier, dopant density and filled trap state density for higher efficiency perovskite solar cells. InfoMat 2020, 2, 409–423. [Google Scholar] [CrossRef] [Green Version]
  7. Saianand, G.; Sonar, P.; Wilson, G.J.; Gopalan, A.-I.; Roy, V.A.L.; Unni, G.E.; Mamun Reza, K.; Bahrami, B.; Venkatramanan, K.; Qiao, Q. Current advancements on charge selective contact interfacial layers and electrodes in flexible hybrid perovskite photovoltaics. J. Energy Chem. 2020, 54, 151–173. [Google Scholar] [CrossRef]
  8. Lee, H.-G.; Sai-Anand, G.; Komathi, S.; Gopalan, A.-I.; Kang, S.-W.; Lee, K.-P. Efficient visible-light-driven photocatalytic degradation of nitrophenol by using graphene-encapsulated TiO2 nanowires. J. Hazard. Mater. 2015, 283, 400–409. [Google Scholar] [CrossRef]
  9. Lee, H.-G.; Gopalan, A.-I.; Sai-Anand, G.; Kang, S.-W.; Lee, K.-P. New Heterojunction Titanium Dioxide Nanowire as Photocatalyst. J. Nanosci. Nanotechnol. 2015, 15, 7421–7425. [Google Scholar] [CrossRef]
  10. Lee, J.-C.; Gopalan, A.-I.; Saianand, G.; Lee, K.-P.; Kim, W.-J. Manganese and Graphene Included Titanium Dioxide Composite Nanowires: Fabrication, Characterization and Enhanced Photocatalytic Activities. Nanomaterials 2020, 10, 456. [Google Scholar] [CrossRef] [Green Version]
  11. Montes-Navajas, P.; Serra, M.; Corma, A.; Garcia, H. Contrasting photocatalytic activity of commercial TiO2 samples for hydrogen generation. Catal. Today 2014, 225, 52–54. [Google Scholar] [CrossRef]
  12. Verbruggen, S.W.; Masschaele, K.; Moortgat, E.; Korany, T.E.; Hauchecorne, B.; Martens, J.A.; Lenaerts, S. Factors driving the activity of commercial titanium dioxide powders towards gas phase photocatalytic oxidation of acetaldehyde. Catal. Sci. Technol. 2012, 2, 2311–2318. [Google Scholar] [CrossRef]
  13. Chalastara, K.; Guo, F.; Elouatik, S.; Demopoulos, G.P. Tunable Composition Aqueous-Synthesized Mixed-Phase TiO2 Nanocrystals for Photo-Assisted Water Decontamination: Comparison of Anatase, Brookite and Rutile Photocatalysts. Catalysts 2020, 10, 407. [Google Scholar] [CrossRef] [Green Version]
  14. Ju, M.-G.; Sun, G.; Wang, J.; Meng, Q.; Liang, W. Origin of High Photocatalytic Properties in the Mixed-Phase TiO2: A First-Principles Theoretical Study. Acs Appl. Mater. Interfaces 2014, 6, 12885–12892. [Google Scholar] [CrossRef]
  15. Jiang, X.; Manawan, M.; Feng, T.; Qian, R.; Zhao, T.; Zhou, G.; Kong, F.; Wang, Q.; Dai, S.; Pan, J.H. Anatase and rutile in evonik aeroxide P25: Heterojunctioned or individual nanoparticles? Catal. Today 2018, 300, 12–17. [Google Scholar] [CrossRef]
  16. Ohtani, B.; Prieto-Mahaney, O.O.; Li, D.; Abe, R. What is Degussa (Evonik) P25? Crystalline composition analysis, reconstruction from isolated pure particles and photocatalytic activity test. J. Photochem. Photobiol. A Chem. 2010, 216, 179–182. [Google Scholar] [CrossRef] [Green Version]
  17. He, H.Y.; Chen, P. Recent advances in property enhancement of nano TiO2 in photodegradation of organic pollutants. Chem. Eng. Commun. 2012, 199, 1543–1574. [Google Scholar] [CrossRef]
  18. Jung, H.J.; Nam, K.; Sung, H.-G.; Hyun, H.S.; Sohn, Y.; Shin, W.G. Preparation of TiO2-Decorated Boron Particles by Wet Ball Milling and their Photoelectrochemical Hydrogen and Oxygen Evolution Reactions. Materials 2016, 9, 1012. [Google Scholar] [CrossRef] [Green Version]
  19. Jung, H.J.; Sohn, Y.; Sung, H.G.; Hyun, H.S.; Shin, W.G. Physicochemical properties of ball milled boron particles: Dry vs. wet ball milling process. Powder Technol. 2015, 269, 548–553. [Google Scholar] [CrossRef]
  20. Ali, M.E.M.; Assirey, E.A.; Abdel-Moniem, S.M.; Ibrahim, H.S. Low temperature-calcined TiO2 for visible light assisted decontamination of 4-nitrophenol and hexavalent chromium from wastewater. Sci. Rep. 2019, 9, 19354. [Google Scholar] [CrossRef]
  21. Mutuma, B.K.; Shao, G.N.; Kim, W.D.; Kim, H.T. Sol–gel synthesis of mesoporous anatase–brookite and anatase–brookite–rutile TiO2 nanoparticles and their photocatalytic properties. J. Colloid Interface Sci. 2015, 442, 1–7. [Google Scholar] [CrossRef] [PubMed]
  22. Sun, Q.; Li, K.; Wu, S.; Han, B.; Sui, L.; Dong, L. Remarkable improvement of TiO2 for dye photocatalytic degradation by a facile post-treatment. New J. Chem. 2020, 44, 1942–1952. [Google Scholar] [CrossRef]
  23. Lee, H.-G.; Gopalan, A.-I.; Sai-Anand, G.; Lee, B.-C.; Kang, S.-W.; Lee, K.-P. Facile synthesis of functionalized graphene-palladium nanoparticle incorporated multicomponent TiO2 composite nanofibers. Mater. Chem. Phys. 2015, 154, 125–136. [Google Scholar] [CrossRef]
  24. Toyoda, M.; Nanbu, Y.; Nakazawa, Y.; Hirano, M.; Inagaki, M. Effect of crystallinity of anatase on photoactivity for methyleneblue decomposition in water. Appl. Catal. B Environ. 2004, 49, 227–232. [Google Scholar] [CrossRef]
  25. Inagaki, M.; Nakazawa, Y.; Hirano, M.; Kobayashi, Y.; Toyoda, M. Preparation of stable anatase-type TiO2 and its photocatalytic performance. Int. J. Inorg. Mater. 2001, 3, 809–811. [Google Scholar] [CrossRef]
  26. Sai-Anand, G.; Dubey, A.; Gopalan, A.-I.; Venkatesan, S.; Ruban, S.; Reza, K.M.; Choi, J.; Lakhi, K.S.; Xu, B.; Qiao, Q.; et al. Additive assisted morphological optimization of photoactive layer in polymer solar cells. Sol. Energy Mater. Sol. Cells 2018, 182, 246–254. [Google Scholar] [CrossRef]
  27. Gopalan, S.-A.; Gopalan, A.-I.; Vinu, A.; Lee, K.-P.; Kang, S.-W. A new optical-electrical integrated buffer layer design based on gold nanoparticles tethered thiol containing sulfonated polyaniline towards enhancement of solar cell performance. Sol. Energy Mater. Sol. Cells 2018, 174, 112–123. [Google Scholar] [CrossRef]
  28. Anand, G.S.; Gopalan, A.I.; Kang, S.-W.; Lee, K.-P. Development of a surface plasmon assisted label-free calorimetric method for sensitive detection of mercury based on functionalized gold nanorods. J. Anal. At. Spectrom. 2013, 28, 488–498. [Google Scholar] [CrossRef]
  29. Saianand, G.; Gopalan, A.-I.; Lee, J.-C.; Sathish, C.; Gopalakrishnan, K.; Unni, G.E.; Shanbhag, D.; Dasireddy, V.D.B.C.; Yi, J.; Xi, S.; et al. Mixed Copper/Copper-Oxide Anchored Mesoporous Fullerene Nanohybrids as Superior Electrocatalysts toward Oxygen Reduction Reaction. Small 2020, 16, 1903937. [Google Scholar] [CrossRef]
  30. Lee, J.-C.; Gopalan, A.-I.; Sai-Anand, G.; Lee, K.-P.; Kim, W.-J. Preparation of Visible Light Photocatalytic Graphene Embedded Rutile Titanium(IV) Oxide Composite Nanowires and Enhanced NOx Removal. Catalysts 2019, 9, 170. [Google Scholar] [CrossRef] [Green Version]
  31. Kim, S.-J.; Lee, E.G.; Park, S.D.; Jeon, C.J.; Cho, Y.H.; Rhee, C.K.; Kim, W.W. Photocatalytic Effects of Rutile Phase TiO2 Ultrafine Powder with High Specific Surface Area Obtained by a Homogeneous Precipitation Process at Low Temperatures. J. Sol. Gel Sci. Technol. 2001, 22, 63–74. [Google Scholar] [CrossRef]
  32. Saitow, K.-i.; Wakamiya, T. 130-fold enhancement of TiO2 photocatalytic activities by ball milling. Appl. Phys. Lett. 2013, 103, 031916. [Google Scholar] [CrossRef]
  33. Holzwarth, U.; Gibson, N. The Scherrer equation versus the ‘Debye-Scherrer equation’. Nat. Nanotechnol. 2011, 6, 534. [Google Scholar] [CrossRef] [PubMed]
  34. Hargreaves, J.S.J. Some considerations related to the use of the Scherrer equation in powder X-ray diffraction as applied to heterogeneous catalysts. Catal. Struct. React. 2016, 2, 33–37. [Google Scholar] [CrossRef] [Green Version]
  35. Williamson, G.K.; Hall, W.H. X-ray line broadening from filed aluminium and wolfram. Acta Metall. 1953, 1, 22–31. [Google Scholar] [CrossRef]
  36. Kibasomba, P.M.; Dhlamini, S.; Maaza, M.; Liu, C.-P.; Rashad, M.M.; Rayan, D.A.; Mwakikunga, B.W. Strain and grain size of TiO2 nanoparticles from TEM, Raman spectroscopy and XRD: The revisiting of the Williamson-Hall plot method. Results Phys. 2018, 9, 628–635. [Google Scholar] [CrossRef]
  37. Rietveld, H.M. A profile refinement method for nuclear and magnetic structures. J. Appl. Crystallogr. 1969, 2, 65–71. [Google Scholar] [CrossRef]
  38. Zhao, P.; Lu, L.; Liu, X.; De la Torre, A.G.; Cheng, X. Error Analysis and Correction for Quantitative Phase Analysis Based on Rietveld-Internal Standard Method: Whether the Minor Phases Can Be Ignored? Crystals 2018, 8, 110. [Google Scholar] [CrossRef] [Green Version]
  39. Karolus, M. Applications of Rietveld refinement in Fe–B–Nb alloy structure studies. J. Mater. Process. Technol. 2006, 175, 246–250. [Google Scholar] [CrossRef]
  40. Karolus, M.; Łągiewka, E. Crystallite size and lattice strain in nanocrystalline Ni–Mo alloys studied by Rietveld refinement. J. Alloy. Compd. 2004, 367, 235–238. [Google Scholar] [CrossRef]
  41. Bish, D.L.; Howard, S.A. Quantitative phase analysis using the Rietveld method. J. Appl. Crystallogr. 1988, 21, 86–91. [Google Scholar] [CrossRef]
  42. Snellings, R.; Salze, A.; Scrivener, K.L. Use of X-ray diffraction to quantify amorphous supplementary cementitious materials in anhydrous and hydrated blended cements. Cem. Concr. Res. 2014, 64, 89–98. [Google Scholar] [CrossRef]
  43. Verma, R.; Gangwar, J.; Srivastava, A.K. Multiphase TiO2 nanostructures: A review of efficient synthesis, growth mechanism, probing capabilities, and applications in bio-safety and health. Rsc Adv. 2017, 7, 44199–44224. [Google Scholar] [CrossRef] [Green Version]
  44. Rezaee, M.; Mousavi Khoie, S.M. Mechanically induced polymorphic phase transformation in nanocrystalline TiO2 powder. J. Alloys Compd. 2010, 507, 484–488. [Google Scholar] [CrossRef]
  45. Ismail, A.A.; Bahnemann, D.W. Mesoporous titania photocatalysts: Preparation, characterization and reaction mechanisms. J. Mater. Chem. 2011, 21, 11686–11707. [Google Scholar] [CrossRef] [Green Version]
  46. Ngo, T.S.; Le, D.D.; Song, J.-H.; Hong, S.-K. Growth and characterization of gallium oxide films grown with nitrogen by plasma-assisted molecular-beam epitaxy. Thin Solid Film. 2019, 682, 93–98. [Google Scholar] [CrossRef]
  47. Takeya, J.; Yamagishi, M.; Tominari, Y.; Hirahara, R.; Nakazawa, Y.; Nishikawa, T.; Kawase, T.; Shimoda, T.; Ogawa, S. Very high-mobility organic single-crystal transistors with in-crystal conduction channels. Appl. Phys. Lett. 2007, 90, 102120. [Google Scholar] [CrossRef]
  48. Rex, J.P.; Yam, F.K.; Lim, H.S. The influence of deposition temperature on the structural, morphological and optical properties of micro-size structures of beta-Ga2O3. Results Phys. 2019, 14, 102475. [Google Scholar] [CrossRef]
  49. Jubu, P.R.; Yam, F.K.; Igba, V.M.; Beh, K.P. Tauc-plot scale and extrapolation effect on bandgap estimation from UV–vis–NIR data—A case study of β-Ga2O3. J. Solid State Chem. 2020, 290, 121576. [Google Scholar] [CrossRef]
  50. Makuła, P.; Pacia, M.; Macyk, W. How To Correctly Determine the Band Gap Energy of Modified Semiconductor Photocatalysts Based on UV–Vis Spectra. J. Phys. Chem. Lett. 2018, 9, 6814–6817. [Google Scholar] [CrossRef] [Green Version]
  51. Bharti, B.; Kumar, S.; Lee, H.-N.; Kumar, R. Formation of oxygen vacancies and Ti3+ state in TiO2 thin film and enhanced optical properties by air plasma treatment. Sci. Rep. 2016, 6, 32355. [Google Scholar] [CrossRef] [PubMed]
  52. Wang, X.; Li, Y.; Liu, X.; Gao, S.; Huang, B.; Dai, Y. Preparation of Ti3+ self-doped TiO2 nanoparticles and their visible light photocatalytic activity. Chin. J. Catal. 2015, 36, 389–399. [Google Scholar] [CrossRef]
  53. Iwabuchi, A.; Choo, C.-k.; Tanaka, K. Titania Nanoparticles Prepared with Pulsed Laser Ablation of Rutile Single Crystals in Water. J. Phys. Chem. B 2004, 108, 10863–10871. [Google Scholar] [CrossRef]
  54. Vildozo, D.; Portela, R.; Ferronato, C.; Chovelon, J.-M. Photocatalytic oxidation of 2-propanol/toluene binary mixtures at indoor air concentration levels. Appl. Catal. B Environ. 2011, 107, 347–354. [Google Scholar] [CrossRef]
  55. Wu, M.; Zheng, A.; Deng, F.; Su, B.-L. Significant photocatalytic activity enhancement of titania inverse opals by anionic impurities removal in dye molecule degradation. Appl. Catal. B Environ. 2013, 138–139, 219–228. [Google Scholar] [CrossRef]
Materials 13 05072 sch001 550
Scheme 1. Cost vs. photoactivity comparison of various investigated TiO2 samples.
Scheme 1. Cost vs. photoactivity comparison of various investigated TiO2 samples.
Materials 13 05072 sch001
Materials 13 05072 g001 550
Figure 1. X-ray diffraction (XRD) patterns of (a) commercial and non-calcined TiO2 samples and (b) post-treated (calcined, calcined + ball milling (BM)) KA100 TiO2.
Figure 1. X-ray diffraction (XRD) patterns of (a) commercial and non-calcined TiO2 samples and (b) post-treated (calcined, calcined + ball milling (BM)) KA100 TiO2.
Materials 13 05072 g001
Materials 13 05072 g002 550
Figure 2. Tauc plots derived from the UV-Visible diffuse reflectance spectrum of the respective samples showing bandgap determined through baseline extrapolation.
Figure 2. Tauc plots derived from the UV-Visible diffuse reflectance spectrum of the respective samples showing bandgap determined through baseline extrapolation.
Materials 13 05072 g002
Materials 13 05072 g003 550
Figure 3. Raman spectrum of calcined and ball milled KA100.
Figure 3. Raman spectrum of calcined and ball milled KA100.
Materials 13 05072 g003
Materials 13 05072 g004 550
Figure 4. X-ray photoelectron spectroscopy spectra for core level of (a) Ti 2p and (b) O1s spectra.
Figure 4. X-ray photoelectron spectroscopy spectra for core level of (a) Ti 2p and (b) O1s spectra.
Materials 13 05072 g004
Materials 13 05072 g005 550
Figure 5. Photodegradation of acetaldehyde (AD) using photocatalysts: (a) various calcined KA100 (b) calcined + ball-milled KA100 and (c) commercial (P25, ST01, and NP400) TiO2 samples, (d) rate constant variations amongst post-treated KA100 (X-axis shows the calcinations temperature) and (e) bar diagram showing the comparison of the rate constant between post-treated KA100 and commercial samples.
Figure 5. Photodegradation of acetaldehyde (AD) using photocatalysts: (a) various calcined KA100 (b) calcined + ball-milled KA100 and (c) commercial (P25, ST01, and NP400) TiO2 samples, (d) rate constant variations amongst post-treated KA100 (X-axis shows the calcinations temperature) and (e) bar diagram showing the comparison of the rate constant between post-treated KA100 and commercial samples.
Materials 13 05072 g005
Materials 13 05072 g006 550
Figure 6. First-order rate constant determination for the photocatalytic acetaldehyde decomposition using the logarithm of the concentration of acetaldehyde at time t (referred to as C) versus time. (a) KA100 and various calcined samples, (b) KA100 calcined + ball milling post treated samples and (c) reference commercial TiO2 samples.
Figure 6. First-order rate constant determination for the photocatalytic acetaldehyde decomposition using the logarithm of the concentration of acetaldehyde at time t (referred to as C) versus time. (a) KA100 and various calcined samples, (b) KA100 calcined + ball milling post treated samples and (c) reference commercial TiO2 samples.
Materials 13 05072 g006
Table
Table 1. Summary of the parameters derived from XRD patterns.
Table 1. Summary of the parameters derived from XRD patterns.
Sample Designation/AcronymsAnatase (%)Rutile (%)Crystallinity (%)
Non-calcined/KA97.222.78-
400 °C/KA497.102.90100
600 °C/KA697.302.70-
700 °C/KA797.282.7872.0
800 °C/KA897.242.76-
900 °C/KA997.232.77-
1000 °C/KA1096.823.18-
700 °C, KA7-BM96.703.3089.2
800 °C, KA7-BM97.102.90-
ST01100.00--
P2577.9022.10-
NP400100.00--
Table
Table 2. Summary of key textural parameters, optical bandgap, and electronic states of Ti 2p.
Table 2. Summary of key textural parameters, optical bandgap, and electronic states of Ti 2p.
Sample DetailsTextural ParametersDRSTi 2p Environment (Peaks) (eV)
DesignationSurface Area (m2/g)Pore Diameter (nm)Optical Bandgap BG-T (BG-BE)2p3/2, 2p1/2Peak SeparationsSatellite Peaks (nm)Distance from the Main Peak
Non-calcined/KA--3.05 (3.12)----
400 °C/KA48.22874.43.05 (3.12)458.58, 464.38471.785.8013.20
600 °C/KA6--3.06 (3.10)----
700 °C/KA78.57771.33.05 (3.10)458.58, 464.18471.895.6013.21
800 °C/KA87.80078.53.04 (3.11)458.58, 464.48471.78
-		5.90
-		13.20
-
900 °C/KA9--3.05 (3.10)----
1000 °C/KA10--3.04 (3.12)----
700 °C, KA7-BM9.33665.63.03 (3.10)458.68, 464.38472.185.7013.50
800 °C, KA7-BM 1--3.03 (3.10)----
ST01-223.43.03 (3.11)----
P25-70.042.93 (2.97) -
NP400-83.333.06 (3.10) -
1 BM—Ball milling, ST01, P25, and NP400 are commercial TiO2 samples.
Table
Table 3. Raman spectra of non-calcined, calcined, and ball milled KA100 samples of TiO2.
Table 3. Raman spectra of non-calcined, calcined, and ball milled KA100 samples of TiO2.
Peak Position (cm−1)
Sample DesignationPeak 1Peak 2Peak 3Peak 4Peak 5
Non-calcined142.02195.51394.61516.33638.4
400 °C142.11195.42396.18515.16639.7
700 °C142.11195.42395.08516.25638.63
800 °C142.11195.42395.08516.25638.63
700 °C, BM142.11195.42395.08515.16637.57
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Gopalan, A.-I.; Lee, J.-C.; Saianand, G.; Lee, K.-P.; Chun, W.-Y.; Hou, Y.-l.; Kannan, V.; Park, S.-S.; Kim, W.-J. Cost-Effective Production of TiO2 with 90-Fold Enhanced Photocatalytic Activity Via Facile Sequential Calcination and Ball Milling Post-Treatment Strategy. Materials 2020, 13, 5072. https://doi.org/10.3390/ma13225072

AMA Style

Gopalan A-I, Lee J-C, Saianand G, Lee K-P, Chun W-Y, Hou Y-l, Kannan V, Park S-S, Kim W-J. Cost-Effective Production of TiO2 with 90-Fold Enhanced Photocatalytic Activity Via Facile Sequential Calcination and Ball Milling Post-Treatment Strategy. Materials. 2020; 13(22):5072. https://doi.org/10.3390/ma13225072

Chicago/Turabian Style

Gopalan, Anantha-Iyengar, Jun-Cheol Lee, Gopalan Saianand, Kwang-Pill Lee, Woo-Young Chun, Yao-long Hou, Venkatramanan Kannan, Sung-Sik Park, and Wha-Jung Kim. 2020. "Cost-Effective Production of TiO2 with 90-Fold Enhanced Photocatalytic Activity Via Facile Sequential Calcination and Ball Milling Post-Treatment Strategy" Materials 13, no. 22: 5072. https://doi.org/10.3390/ma13225072

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop