Jellyfish Collagen: A Biocompatible Collagen Source for 3D Scaffold Fabrication and Enhanced Chondrogenicity
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Marine Drugs
Volume 19
Issue 9
10.3390/md19090502
marinedrugs-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Changes in the Molecular Characteristics of Bovine and Marine Collagen in the Presence of Proteolytic Enzymes as a Stage Used in Scaffold Formation

by
Marfa N. Egorikhina
1,*,
Ludmila L. Semenycheva
2,
Victoria O. Chasova
2,
Irina I. Bronnikova
1,
Yulia P. Rubtsova
1,
Evgeniy A. Zakharychev
2 and
Diana Ya. Aleynik
1
1
Federal State Budgetary Educational Institution of Higher Education, Privolzhsky Research Medical University, the Ministry of Health of the Russian Federation (FSBEI HE PRMU MOH), Minin and Pozharsky Square 10/1, 603950 Nizhny Novgorod, Russia
2
Faculty of Chemistry, Lobachevsky State University of Nizhny Novgorod, pr. Gagarina 23, 603950 Nizhny Novgorod, Russia
*
Author to whom correspondence should be addressed.
Mar. Drugs 2021, 19(9), 502; https://doi.org/10.3390/md19090502
Submission received: 19 July 2021 / Revised: 25 August 2021 / Accepted: 31 August 2021 / Published: 2 September 2021
(This article belongs to the Special Issue Regenerative Potential of Marine Natural Compounds)
Browse Figures
Versions Notes

Abstract

:
Biopolymers, in particular collagen and fibrinogen, are the leading materials for use in tissue engineering. When developing technology for scaffold formation, it is important to understand the properties of the source materials as well as the mechanisms that determine the formation of the scaffold structures. Both factors influence the properties of scaffolds to a great extent. Our present work aimed to identify the features of the molecular characteristics of collagens of different species origin and the changes they undergo during the enzymatic hydrolysis used for the process of scaffold formation. For this study, we used the methods of gel-penetrating chromatography, dynamic light scattering, reading IR spectra, and scanning electron microscopy. It was found that cod collagen (CC) and bovine collagen (BC) have different initial molecular weight parameters, and that, during hydrolysis, the majority of either type of protein is hydrolyzed by the proteolytic enzymes within the first minute. The differently sourced collagen samples were also hydrolyzed with the formation of two low molecular fractions: Mw ~ 10 kDa and ~20 kDa. In the case of CC, the microstructure of the final scaffolds contained denser, closely spaced fibrillar areas, while the BC-sourced scaffolds had narrow, short fibrils composed of unbound fibers of hydrolyzed collagen in their structure.

Graphical Abstract

1. Introduction

The issue of restoring the integrity and functional adequacy of damaged or lost tissues is one of the most pressing challenges in modern medicine. At present, it is inextricably linked with the task of creating new materials for regenerative medicine. Such new biomimetic materials require certain universal properties (lack of toxicity, biocompatibility, low immunogenicity, etc.), as well as the ability to simulate the individual properties that determine the original tissue-specific features of the material being repaired (biodegradation rate, porosity, mechanical integrity, elasticity, etc.) while providing low-cost, minimally labor-intensive solutions. One of the main properties required of materials for tissue engineering and of the scaffolds based on them is good regenerative potential. This is provided by the biological activity of the material and its structural properties.
The biological activity that can be attained, and the structure of the material or scaffold that can be generated, strongly depend on the components from which they have been formed. Therefore, it is extremely important to be aware of the required properties of the material being developed as early as at the stage of selecting its constituents. Collagen is a recognized leader among components for creating biomaterials, scaffolds, and tissue-engineered constructs. It is known for its intense biological activity, which is preserved during the formation of various materials, scaffolds, inks for bioprinters, etc. [1,2,3,4]. The unique properties of this protein make it possible to create biomimetic constructs similar in structure to natural extracellular matrices [5,6,7]. The resulting materials/scaffolds have a porosity and microfiber structure that enables them to provide a large surface area for cell attachment and appropriate conditions for maintaining their viability, migration, and proliferation [8,9,10]. This protein blends perfectly with other materials, providing the possibility for creating hybrid or polycomposite scaffolds with improved properties compared to monocomposite constructs [11,12,13]. In particular, the combination of collagen and fibrin makes it possible to obtain hybrid scaffolds with mechanical characteristics that differ from those made purely of collagen or fibrin [14,15]. For example, the creation of collagen-based scaffold materials is carried out by introducing fragments of synthetic polymers into their composition, which contribute to the formation of the necessary spatial–geometric structures [16,17,18,19]. It is known, for example, that scaffolds based on collagen and acrylates possess improved mechanical properties and cytocompatibility [20,21,22,23,24,25]. It should also be taken into account that collagen is a thermally unstable polymer; at temperatures above 30–40 °C, its denaturation with the formation of gelatin begins [26,27,28,29]. Comparative data on the properties of hybrid materials based on collagen and gelatin proves the perspective of their use in combination or replacement of collagen with gelatin in scaffold-based technologies [30,31,32].
Early on, various types of collagen were isolated and described. They were shown to differ in their amino acid sequences and degree of modification—the extent of hydroxylation or glycosylation [33,34]. However, only in recent years have works begun to appear in which collagens belonging to the same type have been shown to demonstrate different properties depending on the species of animal from whose tissues they have been isolated [35,36,37,38]. A.M. Carvalho et al. [39] set forth a comparative study of type I collagen isolated from bovine skin, cod skin, and rat tails. The authors proved that, depending on their origin, the collagen samples varied in their amino acid composition, exhibited distinctive features in infrared spectra, and had dissimilar denaturation temperatures. The α-chains of the cod collagen had higher electrophoretic mobility compared with those of the mammalian collagens, which was due to their having a lower molecular weight. According to M. Gauza-Włodarczyk [40], certain differences were also established between fish collagen and cattle collagen when comparing their thermal properties. It is notable that analysis, using a bioinformatic analysis, of collagen from five sources of various origins revealed their differences, these being most pronounced between phylogenetically distant species, for example, between pigs and fish [41]. That is, the nature of the substrate from which the biopolymer is isolated largely determines its properties. Few data have appeared in the literature attesting that the nature of the collagen used can determine the properties of scaffolds. Therefore, A. Sorushanova et al. [42] showed that the properties of collagen sponges correlated with the origin of the collagen (from pig skin or bovine skin). Bovine collagen sponges had a larger pore diameter compared to sponges derived from pig collagen using the same technology. The bovine collagen sponges were more resistant to enzymatic denaturation and had a higher absorption capacity and elastic modulus. Another work has established that sheep collagen scaffolds have significantly higher ultimate strain and stress resistance and strength compared to scaffolds derived from cattle or pig collagen. They also appear to be more resistant to collagenase degradation compared to the cattle collagen samples, which, themselves, show a higher resistance than pig collagen scaffolds [43].
In our early works, it was established that hybrid hydrogel scaffolds formed from either cod collagen (CC) or bovine collagen (BC) in combination with fibrinogen (Fg) under the same conditions varied in their structural and mechanical properties [44]. Thus, it was shown that scaffolds made using BC had a denser structure compared to scaffolds made using CC. Differences in the elastic properties were also revealed. In particular, the compressive stress at a deformation value of 50% for the scaffold samples made using BC was 1.6 times higher than that for scaffold samples made with CC. It was also established that scaffolds made with CC and BC both had good biocompatibility and provided conditions that enabled stem cells to be maintained in a viable state, additionally sustaining their three-dimensional growth [44].
The technology for the formation of these scaffolds is based on enzymatic hydrolysis of the proteins [45]. The use of proteolytic enzymes, in the presence of which the spatial structure of scaffolds are formed from fragments of the protein hydrolysates, is not unique and is in widespread use in work with biopolymers [19,46,47,48,49]. Despite this, many of the processes and mechanisms involved in the formation of these structures (especially when it comes to composite or hybrid materials) remain unexplored.
This work aims to identify the features of the molecular characteristics of collagens of different species origin (bovine and marine) and the changes they undergo during enzymatic hydrolysis by pancreatin and thrombin during scaffold formation, as well as the features of the supramolecular structures in the composition of the hybrid hydrogel scaffolds resulting from their combination with fibrinogen.

2. Results and Discussion

2.1. Characteristics of Native Collagen—CC and BC

As evidenced by data in the literature, the characteristics of native collagen isolated from the tissues of various animal species differ significantly in several parameters: molecular weight characteristics, amino acid ratios and sequences, as well as in their physicochemical properties [50,51,52,53]. Taking into account the purpose of this study, in comparable conditions, we investigated native collagen of the first type from cod skin isolated according to the author’s method [54] and bovine collagen-reagent by Sigma-Aldrich Company, isolated from calf skin [55]. Cod collagen and bovine collagen were isolated under comparable conditions by extraction with a solution of acetic acid [54,56]. The retention of the native protein structure for both cod collagen and bovine collagen is proved by the data of their molecular weight parameters. They are presented in Table 1.
The main collagen fraction is high molecular weight for both cod collagen and bovine collagen. However, the Mw of the original native bovine collagen is several times higher than that of cod collagen. The Mw of cod collagen has a value of ~300 kDa, corresponds to the literature data, and obviously represents a helix of three α-chains, each of which has a molecular mass of ~100 kDa [33,34]. Bovine collagen is identified as an associate of 2–3 collagen macromolecules with MW of ~300 kDa, the formation of which is possible, according to the literature data, in concentrated aqueous collagen solutions due to intermolecular bonds [57,58]. The polydispersity coefficients in the case of bovine collagen are higher than in the case of cod collagen (Table 1, lines 1, 4). Moreover, in native collagen of both cod and bovine collagen, small amounts of low-molecular-weight fraction with Mw of ~17–20 kDa and traces of a polymer with Mw of ~9–10 kDa appear. Apparently, these are products of partial hydrolysis of native collagen. Close values of hydrolysates according to Mw values when analyzed by the GPC method draw attention to themselves (Table 1). The MWD curves, according to the GPC data of cod collagen (Figure 1a) and bovine collagen (Figure 1b), have an identical form. According to the goal of this study, it is important that both initial proteins are dissolved in aqueous 0.5–1.0 M acetic acid. Such solutions are the starting point for experiments.
The high degree of similarity of the proteins is also evidenced by the IR spectra of the CC and BC films (Figure 2)—they are practically the same. They have absorption bands characteristic of proteins, corresponding to oscillations in the following ranges: 1600–1700 cm−1—NH- and C=O-bonds; 1510–1570 cm−1—plane bending vibrations of NH-bonds; 1200–1350 cm−1—bending vibrations of C-N and NH-bonds; 1720–1730 cm−1—stretch vibrations of the carboxyl group, C=O.

2.2. Characteristics of the CC and BC Hydrolysis Products

A comparative analysis of the molecular weight characteristics of the CC and BC hydrolysis products formed in the presence of the proteolytic enzymes pancreatin and thrombin was carried out at room temperature. The results indicate similarities and differences for the hydrolysis process occurring under comparable conditions for the specified substrates. The majority of the high molecular BC and CC macromolecules at room temperature are destroyed within the first minute in the presence of both thrombin and pancreatin. However, there are differences in the amounts of the low molecular fractions and the behavior of the initial CC and BC during the process of hydrolysis (data on hydrolysis in the presence of thrombin are shown in Table 2).
It may be recalled that in the process of enzymatic hydrolysis of collagen, both by denaturation via the destruction of the triple-stranded structure and by the destruction of individual chains to low-molecular-weight peptides and oligomeric peptides can occur [59]. The CC and BC hydrolysates consist of several fractions, two of them with close Mw values and a polydispersity coefficient close to 1.0: most of them have Mw ~ 9–10 kDa (80–90%), while smaller proportions have Mw ~ 17–20 kDa (less than 10%).
The CC digest solution contains no initial polymer with Mw ~ 300 kDa but does contain macromolecules with Mw ~ 100 kDa [60]. This Mw corresponds to the length of one α-chain; apparently, these are the products of the CC denaturation [33,34]. In the case of BC hydrolysis, ≤10% of the initial high-molecular-weight fraction remains during enzymic hydrolysis in all samples even after prolonged contact with the enzyme for 3 days (Table 2, line 4), while no denaturation products are left. Figure 3 shows the MWD curve dynamics of the enzymatic hydrolysis products of CC and BC over 3 days, from which it is obvious that there is a general tendency for the reduction of collagen macromolecules to low molecular fractions with Mw ~ 9–10 kDa and ~17–20 kDa for both types of collagen, with each of the two different proteolytic enzymes. The hydrolysis products of CC and BC are shown schematically in Figure 4.
Note, particularly, that CC and BC hydrolysates (Figure 3), as well as the fibrinogen hydrolysate [61], have fractions with practically the same Mw values, namely ~9–10 kDa and ~17–20 kDa. This is crucial to define the scaffold formation process. Apparently, due to the fact that proteolytic enzymes hydrolyze the peptide bond formed by the amino acid residues of arginine and lysine [62,63,64], the Mw of the hydrolysates have similar values. It has been suggested [61] that the formation of a hybrid scaffold upon hydrolysis of a mixture of Fg and collagen by thrombin occurs through the fusion of the collagen hydrolysate fibers during the aggregation of the fibrin monomer into the network structure of its polymer [65], thus forming the spatial structure of the scaffold. In the process of enzymatic hydrolysis, the intrinsic viscosity of the collagen solution according to the Mark–Houwink equation (Equation (1)) changes for bovine collagen and cod collagen from 1.03 and 2.35 values up to 0.09 values (the Mw was calculated for the hydrolyzate with Mw ~ 10 kDa, the predominant content of which takes place in both cases). This leads to an increase in the mobility of collagen macromolecules in solution and the formation of the spatial organization of the copolymer.
[ η ] = K M α
where K and α are the individual constants of the polymer (for collagen, the values of K = 1.34 × 10−4, α = 0.71) [66,67].
The data obtained in this work are consistent with this hypothesis.
A schematic representation of the enzymatic hydrolysis of collagen is shown in Figure 5.

2.3. The Role of Collagen Hydrolysates in the Formation of the Spatial Structure of Scaffolds

In order to clarify the picture of the supramolecular design of scaffolds, joint hydrolysis by thrombin of a 1:1 ratio of Fg and collagen at a high protein concentration (about 1%) was carried out. After 10 min, a coagulate had formed in the solution (Figure 6a) that was analogous to a hybrid scaffold obtained from collagen and fibrinogen (Figure 6b).
It has previously been noted that a water-insoluble fibrin-polymer can be dissolved in dilute solutions of urea or acetic acid [65]. We were able to dissolve hybrid hydrogel scaffolds, based on both CC and BC combined with Fg and obtained according to Section 3.3, in 3% acetic acid over a period of 5 days. Analysis of these solutions using both GPC and dynamic light scattering indicated the destruction of the high molecular structure. According to the GPC data, four fractions were present in the solutions (Figure 7). The two low molecular fractions had Mw values of ~10 kDa and ~20 kDa (Mw/Mn ~ 1.0). The high molecular fraction had Mw values less than 150 kDa with Mw/Mn = 1.2–1.3 for CC, while that derived from BC was less than 240 kDa with Mw/Mn = 1.4–1.6 (Table 3). The contents of the first three fractions for BC and CC are comparable. The high molecular fraction of the scaffold hydrolysate with BC is of greater importance in comparison with that for CC, the value of the polydispersity coefficient and its content being much higher. The rather high polydispersity of the high molecular fractions, especially in the case of BC, indicates their heterogeneity in terms of Mw. The latter suggests that this is an incompletely hydrolyzed high molecular polymer.
The particle size distribution curves for the scattering intensity of acetic acid solutions of scaffolds with CC (a) and BC (b) (Figure 8) are very similar to each other. The method allows us to specify three groups of macro coils of sizes up to ~50 nm, ~50–150 nm, and ~250–500 nm. Accordingly, the first group can be attributed to individual macromolecules, which were recorded using GPC, with Mw up to 150 kDa. The other two groups are associations of macromolecules peculiar to such concentrated aqueous solutions of polar monomers [57] that include natural proteins.

2.4. Features of the Supramolecular Structure of Structure-Forming Biopolymers and Scaffolds Produced from Them

Scanning electron microscopy was used to analyze the supramolecular structures of CC and BC scaffolds formed in association with Fg. Figure 9 shows samples of films of the initial CC (a), BC (b), Fg (c), and the structure of the flocculants based on Fg with CC (d). The photographs show that both types of collagen have a fibrillar structure, represented by lengthwise stretched fibers. In the process of preparation and formation of collagen films (in the process of water evaporation, a discrepancy between the rate of water evaporation, the density of the material for research, etc.), the samples of different morphology were obtained. However, threadlike structural homogeneity of both cod collagen and bovine collagen draws attention to itself. Native Fg, unlike collagen, does not have a fibrillar structure and is present in the form of plates with uneven edges. The picture of the structure of the coagulate obtained by the combined hydrolysis of CC and Fg is in marked contrast (Figure 9d). It is characterized by developed reticular microarchitectonics with a system of heterogeneous pores. The unity of the structure is noteworthy. It is impossible to distinguish the Fg or collagen fibers, indicating the formation of uniform structural elements from fibrin and collagen hydrolysates as a result of the enzymatic hydrolysis.
At the next stage, we studied the structure of hybrid hydrogel scaffolds based on Fg with CC (Figure 10a,c) and BC (Figure 10b,d) obtained through the enzymatic hydrolysis reaction, as well as of solutions of these scaffolds in 3% acetic acid (Figure 10e,f), respectively, for CC and BC). The surface structure of the scaffolds (Figure 10a,b) was characterized by the presence of closely spaced fibers and resembled the fibrillar structure of native collagen (Figure 9a,b). However, it should be noted that the surface structure of the CC and BC scaffolds was not identical. The fibers of scaffolds with CC were stretched lengthwise and tangled with each other longitudinally. The fibers of the BC scaffolds were also oriented lengthwise. However, unlike the fibers of the CC scaffolds, the fibers of the BC scaffolds were “branched” and tangled in both the longitudinal and transverse directions. It should be noted that during the scaffold formation, all components and production environments were identical, except for the type of collagen. Thus, differences in the collagen, or rather in the products of its hydrolysis, must have determined the differences in the structural characteristics of the scaffolds. This was despite the amount of fibrinogen in the composite for preparing the scaffolds being 22 times higher than the amount of collagen. Thus, even with such an unequal ratio, collagen plays an essential role in the formation of the structural elements of such scaffolds. This is consistent with our earlier data, which showed differences in scaffold densities and their elastic properties [44]. Differences in internal architectonics were also discussed, so we shall now focus on discussing the features of the internal structure of the scaffolds compared with the structure of the coagulate obtained by the combined hydrolysis of Fg and collagen.
The structure of the hybrid scaffolds (Figure 10c,d) was different from the structure of the coagulate (Figure 9d). Thus, when comparing the structural elements, it can be noted that the membranes between the pores in the scaffolds are thicker and that pores of a much larger size can be observed. These differences could be due to three factors. The first is the different ratio of concentrations of the main structure-forming proteins in the scaffolds and coagulate. In the coagulate, the ratio of Fg and collagen was 1:1, while in the scaffolds, it was 22:1, respectively. The second is the difference in the composites. The coagulate composite consisted of a solution of “pure” Fg and “pure” collagen. The composite for the formation of scaffolds also contained “pure” collagen, but the fibrinogen was in the form of blood plasma cryoprecipitate. It is known that blood plasma cryoprecipitate contains not only fibrinogen but also other proteins, for example, factor XIII, fibronectin, fibrinolysis inhibitors, and cell adhesion molecules [68,69]. According to the literature, these proteins can also take part in the formation of the scaffold structure by forming bonds with the fibrin matrix [70,71,72]. The third factor is the PEGylation of the protein. For the methodology used to produce the hybrid scaffolds studied here, the proteins present in blood plasma cryoprecipitate, including the fibrinogen, are exposed to PEG, which, according to the literature, can lead to cross-linking of the protein molecules [73,74]. However, despite these factors and the revealed differences, the general picture is that the hybrid hydrogel scaffold and the structure of the coagulate had much in common. Thus, the internal architectonics of the scaffolds (Figure 10c,d) was represented by a three-dimensional structure with a heterogeneous pore system and was similar to the three-dimensional structure of the coagulate obtained by the combined hydrolysis of Fg and collagen (Figure 9d). It was impossible to distinguish individual fibrin or collagen fibers in the study using scanning electron microscopy of the dehydrated sections of scaffold samples, as in the case of the coagulates. Thus, we can conclude that the formation of the structural elements of hybrid scaffolds based on Fg and collagen as a result of enzymatic hydrolysis is principally due to the interaction of the hydrolysates of the main structure-forming proteins. They determine the presence of a three-dimensional structure with heterogeneous porosity. At the same time, differences regarding the fiber thicknesses, their interlacing, the size of the walls between the pores, the sizes of the pores, etc., can be due to various factors, including the origin of the collagen and the characteristics of its hydrolysates. The latter is confirmed by the results of the study of the polymer structures and the freeze-dried solutions of scaffolds in 3% acetic acid. The images for scaffolds with CC (Figure 10e) and scaffolds with BC (Figure 10f) show differences in their microstructure. Both samples, with either cod or bovine collagen, have fragments of interconnected fibers, although these are less extensive than in the initial collagen. However, the sample with CC presents only located fibrillar areas, while the sample with BC showed narrow, short fibrils in its structure. Most likely, these fibrils are composed of the unbound fibers of high molecular BC that were found to be present in hydrolysates using the GPC method (Table 1 and Table 3, Figure 3 and Figure 7). They have Mw greater than those of CC and are distinguished by their different structure.

3. Materials and Methods

3.1. Enzymatic Hydrolysis of Collagen of Various Origins

Pancreatin (Hubei Maxpharm Industries Co, LTD, Wuhan, China) of proteolytic activity 2 U/mg, and thrombin (Renam NPO, Moscow, Russia) of proteolytic activity 2 U/mg, were used as the enzymes for the hydrolysis of both the bovine and cod collagen at 25 °C, in aqueous solution at pH ~ 7.0. For the hydrolysis, a 1% solution of each type of high molecular collagen (HMC) was prepared. Then 1M NaOH was added to the 1% HMC solution to neutralize any acid, with the solution subsequently brought to the required volume with distilled water.
The hydrolysis was carried out by adding the relevant enzyme to the resulting mixture at a mass ratio of collagen: enzyme of 102:1. Samples (1 mL) were taken from the reaction medium at regular intervals after the addition of the enzyme. For these, the hydrolysis was interrupted by adding a 4% acetic acid solution (1 mL) to the samples [2,44].

3.2. Combined Hydrolysis of CC and Fg by Thrombin

Enzymatic hydrolysis was carried out using thrombin (Renam NPO, (Russia)) at a protein:thrombin ratio of 103:1 at 25 °C, in aqueous solution at pH ~ 7.0. For hydrolysis, a 1% aqueous solution of the relevant protein was prepared. Then, 1 mL samples were taken at certain intervals after the addition of the enzyme. The hydrolysis was interrupted by adding a 4% acetic acid solution (1 mL) to the samples.

3.3. Formation of Hybrid Hydrogel Scaffolds Based on Fg and Collagen

Human blood plasma cryoprecipitate obtained from the GBUZ NO blood center (Nizhny Novgorod, Russia) was used as a source of fibrinogen. The protein was PEGylated (PEG-NHS; Sigma-Aldrich, Darmstadt, Germany). Then a solution of 2% collagen was added—either CC isolated from cod skin [54] or BA—bovine collagen (Sigma-Aldrich, Germany). Phosphate buffer (PBS) was added to the resulting mixture at a 7:1 ratio. To polymerize the mixture, a solution of human thrombin (80 U/mL; Sigma-Aldrich, Germany) in 1% CaCL2 solution was introduced into it. Studies with the scaffolds were carried out 24 h after their formation. For this, the newly formed scaffolds were flushed with 5 mL of PBS and incubated in a CO2 incubator [45,75].

3.4. Freeze Drying

Samples of aqueous solutions for analysis on an electron microscope were placed in a container, frozen with liquid nitrogen, connected to a vacuum unit, and with a decrease in pressure of 0.5–1.0 mbar the water was sublimated into a trap while maintaining a negative temperature of the mixture for at least 4 h.

3.5. Scaffold Dissolution

Scaffolds were dissolved at room temperature in 15 mL of a 3% aqueous solution of acetic acid for 3 days.

3.6. Reading IR Spectra of CC and BC (See Article in “Inorganic”)

An IRPrestige-21 (Shimadzu, Kyoto, Japan) spectrophotometer was used to record the absorption spectra. Range of wave numbers: 500–550 cm−1. Accuracy: ±0.05 cm−1. Reflecting KBr plates were used to prepare the films.

3.7. Determination of the Molecular Weight Characteristics of Proteins Using Gel-Penetrating Chromatography (GPC)

To identify the molecular weight characteristics of the proteins in aqueous solution, a high-performance liquid chromatograph—Shimadzu CTO20A/20AC (Shimadzu, Kyoto, Japan)—with an LC-Solutions-GPC software module was used. Columns—Tosoh Bioscience TSKgel G3000SWxl—with a pore diameter of 5 μm were used for the separation. We used an ELSD-LT II low-temperature light-scattering detector. The flow rate was 0.8 mL/min, with the eluent being a 0.5 M acetic acid solution. Calibration was performed using narrow disperse dextran samples (molecular mass range: 1000–410,000 Da). Before measurements, the solution was filtered through a polyethersulfone filter with a pore size of 0.45 μm.

3.8. Scanning Electron Microscopy

To determine the structural characteristics of the collagen, fibrinogen, and scaffolds, a JSM-IT300 scanning electron microscope (JEOL Ltd., Tokyo, Japan) was used. The diameter of the electron probe was 5 nm, and the operating voltage was 20 kV. In order to avoid charging the samples, detectors of low-energy secondary electrons and backscattered electrons were used in low vacuum mode.

3.9. Dynamic Light Scattering Method

The average hydrodynamic weight diameters of the scaffold particles with CC and BC in acetic acid solution were determined using dynamic light scattering (DLS) in the polymodal analysis mode of the correlation function. The measurements were carried out at 25 ± 0.1 °C at an angle of 90° over a range from 0.1 to 5000 nm in 1 cm polystyrene cuvettes using a NanoBrook Omni spectrometer (Brookhaven Instruments, NY, Holtsville, NY, USA). The accumulation time of the correlation function was 180 s. The hydrodynamic weight diameter was calculated as the average of 10 parallel measurements. Before measurements were recorded, the cuvette was dedusted three times by rinsing with distilled water filtered through a polyethersulfone filter with a pore size of 0.2 μm.
The samples for measurement were also filtered through a polyethersulfone filter with a pore size of 0.2 μm.

4. Conclusions

Based on the studies described, it can be stated that the CC and BC materials used have different initial molecular weight parameters. In the process of hydrolysis, during the first minute under standard conditions, the majority of each of the two types of protein (>80%) was hydrolyzed by the proteolytic enzymes pancreatin or thrombin (collagen:pancreatin ratio = 10:1). In the subsequent period of monitoring of the molecular weight parameters, the values for the BC samples underwent little further change. In the case of CC, the hydrolysis process continued until there had been a complete disappearance of the high molecular fraction. It was shown that all the collagen samples, regardless of the nature of the initial substrate, were hydrolyzed with the formation of two low molecular fractions, either of Mw ~ 10 kDa or ~20 kDa, with the main part of the hydrolysate (more than 80%) falling within the fraction with an Mw of less than 10 kDa, and this tendency could be observed throughout the entire process. It was found that the concentration of the enzyme had practically no effect on the molecular weight parameters of the final products of the protein degradation. Based on the scanning electron microscopy results, it can be concluded that there are differences in the microstructure of the scaffolds containing collagen from the different sources. Thus, the nature of the collagen source determines its molecular weight characteristics as well as those of its hydrolysates. The latter, in turn, mediate the formation of the structural elements and directly impact the microarchitectonics of the scaffolds formed during enzymatic hydrolysis. We anticipate that the data from our study will, in the future, make it possible both to predict the structural characteristics of scaffolds at the production stage and to offer the opportunity to modulate their properties. Of course, this requires further wide-ranging studies.

Author Contributions

Conceptualization, M.N.E. and L.L.S.; methodology, M.N.E., L.L.S., V.O.C., Y.P.R., E.A.Z. and D.Y.A.; software, V.O.C., E.A.Z., I.I.B. and Y.P.R.; validation, V.O.C., I.I.B., Y.P.R., E.A.Z. and D.Y.A.; formal analysis, M.N.E., L.L.S., V.O.C. and E.A.Z.; investigation, M.N.E., L.L.S., V.O.C., Y.P.R. and E.A.Z.; resources, M.N.E., L.L.S. and D.Y.A.; data curation, M.N.E. and L.L.S.; writing—original draft preparation, M.N.E., L.L.S., V.O.C., I.I.B., Y.P.R. and E.A.Z.; writing—review and editing, M.N.E., L.L.S. and D.Y.A.; visualization, M.N.E., V.O.C. and E.A.Z.; supervision, M.N.E., L.L.S., V.O.C. and E.A.Z.; project administration, M.N.E. and L.L.S.; funding acquisition, M.N.E. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Ministry of Health of the Russian Federation. State task No. 121022500010-6 (RC 208.090.01).

Institutional Review Board Statement

The study was conducted according to the guidelines of the Declaration of Helsinki. The study protocol was approved by the Local ethical committee of the FSBEI HE PRMU MOH (Nizhny Novgorod, Russia) (approved by the local ethics committee on 10 March 2021, protocol No.5).

Informed Consent Statement

Each person included in the study provided voluntary informed consent.

Data Availability Statement

All data supporting the conclusions of this article are included in this article.

Acknowledgments

The study was carried out on the equipment of the Center for Collective Use “New materials and resource-saving technologies” (Research Institute of Chemistry, N.I. Loba-chevsky State University of Nizhny Novgorod).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Silvipriya, K.; Kumar, K.; Bhat, A.; Kumar, B.; John, A.; Lakshmanan, P. Collagen: Animal Sources and Biomedical Application. J. Appl. Pharm. Sci. 2015, 5, 123–127. [Google Scholar] [CrossRef] [Green Version]
  2. George, J.; Mahija, J.S.R. Collagen and its therapeutical applications in regenerative medicine collagen and its therapeutical applications in regenerative medicine. Int. J. Sci. Res. Dev. 2018, 6, 268–277. [Google Scholar]
  3. Diamantides, N.; Wang, L.; Pruiksma, T.; Siemiatkoski, J.; Dugopolski, C.; Shortkroff, S.; Kennedy, S.; Bonassar, L.J. Correlating rheological properties and printability of collagen bioinks: The effects of riboflavin photocrosslinking and pH. Biofabrication 2017, 9, 034102. [Google Scholar] [CrossRef] [PubMed]
  4. Muthukumar, T.; Sreekumar, G.; Sastry, T.; Chamundeeswari, M. Collagen as a Potential Biomaterial in Biomedical Applications. Rev. Adv. Mater. Sci. 2018, 53, 29–39. [Google Scholar] [CrossRef]
  5. Suzuki, A.; Kodama, Y.; Miwa, K.; Kishimoto, K.; Hoshikawa, E.; Haga, K.; Sato, T.; Mizuno, J.; Izumi, K. Manufacturing mi-cropatterned collagen scaffolds with chemical-crosslinking for development of biomimetic tissue-engineered oral mucosa. Sci. Rep. 2020, 10, 1–14. [Google Scholar] [CrossRef]
  6. Parisi, C.; Salvatore, L.; Veschini, L.; Serra, M.P.; Hobbs, C.; Madaghiele, M.; Sannino, A.; Di Silvio, L. Biomimetic gradient scaffold of collagen–hydroxyapatite for osteochondral regeneration. J. Tissue Eng. 2020, 11. [Google Scholar] [CrossRef] [Green Version]
  7. Jang, C.H.; Ahn, S.H.; Yang, G.-H.; Kim, G.H. A MSCs-laden polycaprolactone/collagen scaffold for bone tissue regeneration. RSC Adv. 2016, 6, 6259–6265. [Google Scholar] [CrossRef]
  8. Dong, C.; Lv, Y. Application of Collagen Scaffold in Tissue Engineering: Recent Advances and New Perspectives. Polymers 2016, 8, 42. [Google Scholar] [CrossRef] [Green Version]
  9. Lausch, A.J.; Chong, L.C.; Uludag, H.; Sone, E.D. Multiphasic collagen scaffolds for engineered tissue interfaces. Adv. Funct. Mater. 2018, 28, 1–9. [Google Scholar] [CrossRef]
  10. Kourgiantaki, A.; Tzeranis, D.; Karali, K.; Georgelou, K.; Bampoula, E.; Psilodimitrakopoulos, S.; Yannas, I.V.; Stratakis, E.; Sidiropoulou, K.; Charalampopoulos, I.; et al. Neural stem cell delivery via porous collagen scaffolds promotes neuronal differentiation and locomotion recovery in spinal cord injury. NPJ Regen. Med. 2020, 5, 1–14. [Google Scholar] [CrossRef] [PubMed]
  11. Davidenko, N.; Schuster, C.F.; Bax, D.V.; Farndale, R.W.; Hamaia, S.; Best, S.M.; Cameron, R.E. Evaluation of cell binding to collagen and gelatin: A study of the effect of 2D and 3D architecture and surface chemistry. J. Mater. Sci. Mater. Med. 2016, 27, 148. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Kalirajan, C.; Palanisamy, T. Bioengineered Hybrid Collagen Scaffold Tethered with Silver-Catechin Nanocomposite Modulates Angiogenesis and TGF-β Toward Scarless Healing in Chronic Deep Second Degree Infected Burns. Adv. Health Mater. 2020, 9, e2000247. [Google Scholar] [CrossRef] [PubMed]
  13. Ureña-Saborio, H.; Alfaro-Viquez, E.; Esquivel-Alvarado, D.; Esquivel, M.; Madrigal-Carballo, S. Collagen/chitosan hybrid 3D-scaffolds as potential biomaterials for tissue engineering. Int. J. Nano Biomater. 2018, 7, 163–175. [Google Scholar] [CrossRef]
  14. Rowe, S.L.; Stegemann, J.P. Interpenetrating Collagen-Fibrin Composite Matrices with Varying Protein Contents and Ratios. Biomacromolecules 2006, 7, 2942–2948. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  15. Brougham, C.M.; Levingstone, T.J.; Jockenhoevel, S.; Flanagan, T.C.; O’Brien, F.J. Incorporation of fibrin into a collagen-glycosaminoglycan matrix results in a scaffold with improved mechanical properties and enhanced capacity to resist cell-mediated contraction. Acta Biomater. 2015, 26, 205–214. [Google Scholar] [CrossRef] [Green Version]
  16. Schweizer, T.A.; Shambat, S.M.; Haunreiter, V.D.; Mestres, C.A.; Weber, A.; Maisano, F.; Zinkernagel, A.S.; Hasse, B. Polyester Vascular Graft Material and Risk for Intracavitary Thoracic Vascular Graft Infection1. Emerg. Infect. Dis. 2020, 26, 2448–2452. [Google Scholar] [CrossRef] [PubMed]
  17. Kocen, R.; Gasik, M.; Gantar, A.; Novak, S. Viscoelastic behaviour of hydrogel-based composites for tissue engineering under mechanical load. Biomed. Mater. 2017, 12, 025004. [Google Scholar] [CrossRef]
  18. Zhang, D.; Wu, X.; Chen, J.; Lin, K. The development of collagen based composite scaffolds for bone regeneration. Bioact. Mater. 2017, 3, 129–138. [Google Scholar] [CrossRef]
  19. Al Kayal, T.; Losi, P.; Pierozzi, S.; Soldani, G. A New Method for Fibrin-Based Electrospun/Sprayed Scaffold Fabrication. Sci. Rep. 2020, 10, 1–4. [Google Scholar] [CrossRef] [Green Version]
  20. Sousa, R.O.; Martins, E.; Carvalho, D.N.; Alves, A.L.; Oliveira, C.; Duarte, A.R.C.; Silva, T.H.; Reis, R.L. Collagen from Atlantic cod (Gadus morhua) skins extracted using CO2 acidified water with potential application in healthcare. J. Poly. Res. 2020, 27, 73. [Google Scholar] [CrossRef] [Green Version]
  21. Castilho, M.; Hochleitner, G.; Wilson, W.; Van Rietbergen, B.; Dalton, P.D.; Groll, J.; Malda, J.; Ito, K. Mechanical behavior of a soft hydrogel reinforced with three-dimensional printed microfibre scaffolds. Sci. Rep. 2018, 8, 1–10. [Google Scholar] [CrossRef]
  22. Jiang, H.-J.; Xu, J.; Qiu, Z.-Y.; Ma, X.-L.; Zhang, Z.-Q.; Tan, X.-X.; Cui, Y.; Cui, F.-Z. Mechanical Properties and Cytocompatibility Improvement of Vertebroplasty PMMA Bone Cements by Incorporating Mineralized Collagen. Materials 2015, 8, 2616–2634. [Google Scholar] [CrossRef]
  23. Vedhanayagam, M.; Ananda, S.; Nair, B.U.; Sreeram, K.J. Polymethyl methacrylate (PMMA) grafted collagen scaffold re-inforced by PdO-TiO2 nanocomposites. Mater. Sci. Eng. C-Mater. Biol. Appl. 2019, 108, 110378. [Google Scholar] [CrossRef]
  24. Carrion, B.; Souzanchi, M.F.; Wang, V.T.; Tiruchinapally, G.; Shikanov, A.; Putnam, A.J.; Coleman, R.M. The synergistic effects of matrix stiffness and composition on the response of chondroprogenitor cells in a 3D precondensation microenvironment. Adv. Healthcare Mater. 2015, 5, 1192–1202. [Google Scholar] [CrossRef]
  25. Semenycheva, L.L.; Chasova, V.O.; Fukina, D.G.; Koryagin, A.V.; Valetova, N.B.; Suleimanov, E.V. Synthesis of polymethyl methacrylate—Collagen graft copolymer using a photocatalyst—Complex oxide RbTe1.5W0.5O6. All materials. Encyclop. Ref. 2021, 7, 15–23. [Google Scholar]
  26. Bello, A.B.; Kim, D.; Kim, D.; Park, H.; Lee, S.H. Engineering and functionalization of gelatin biomaterials: From cell culture to medical applications. Tissue Eng.-Part B 2019, 26, 164–180. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Cruz-López, H.; Rodríguez-Morales, S.; Enríquez-Paredes, L.M.; Villarreal-Gómez, L.J.; Olivera-Castillo, L.; Cortes-Santiago, Y.; López, L.M. Comparison of collagen characteristic from the skin and swim bladder of Gulf corvina (Cynoscion othonopterus). Tissue Cell 2021, 72, 101593. [Google Scholar] [CrossRef]
  28. Sun, B.; Li, C.; Mao, Y.; Qiao, Z.; Jia, R.; Huang, T.; Xu, D.; Yang, W. Distinctive characteristics of collagen and gelatin extracted from Dosidicus gigas skin. Int. J. Food Sci. Technol. 2021, 56, 3443–3454. [Google Scholar] [CrossRef]
  29. Veeruraj, A.; Arumugam, M.; Balasubramanian, T. Isolation and characterization of thermostable collagen from the marine eel-fish (Evenchelys macrura). Proc. Biochem. 2013, 48, 1592–1602. [Google Scholar] [CrossRef]
  30. Sharifi, E.; Azami, M.; Kajbafzadeh, A.M.; Moztarzadeh, F.; Faridi-Majidi, R.; Shamousi, A.; Karimi, R.; Ai, J. Preparation of a biomimetic composite scaffold from gelatin/collagen andbioactive glass fibers for bone tissue engineering. Mater. Sci. Eng. 2016, 59, 533–541. [Google Scholar] [CrossRef]
  31. Cao, J.; Wang, P.; Liu, Y.; Zhu, C.; Fan, D. Double crosslinked HLC-CCS hydrogel tissue engineering scaffold for skin wound healing. Int. J. Biol. Macromol. 2020, 155, 625–635. [Google Scholar] [CrossRef]
  32. Shah, B.M.; Palakurthi, S.S.; Khare, T.; Khare, S.; Palakurthi, S. Natural proteins and polysaccharides in the development of micro/nano delivery systems for the treatment of inflammatory bowel disease. Int. J. Biol. Macromol. 2020, 165, 722–737. [Google Scholar] [CrossRef]
  33. Gelse, K.; Pöschl, E.; Aigner, T. Collagens—Structure, function, and biosynthesis. Adv. Drug Deliv. Rev. 2003, 55, 1531–1546. [Google Scholar] [CrossRef] [Green Version]
  34. Copes, F.; Pien, N.; Van Vlierberghe, S.; Boccafoschi, F.; Mantovani, D. Collagen-Based Tissue Engineering Strategies for Vascular Medicine. Front. Bioeng. Biotechnol. 2019, 7, 166. [Google Scholar] [CrossRef] [Green Version]
  35. Davison-Kotler, E.; Marshall, W.S.; García-Gareta, E. Sources of collagen for biomaterials in skin wound healing. Bioengineering 2019, 6, 56. [Google Scholar] [CrossRef] [Green Version]
  36. Oliveira, V.D.M.; Assis, C.R.D.; Costa, B.D.A.M.; Neri, R.C.D.A.; Monte, F.T.D.; Freitas, H.M.S.D.C.V.; França, R.C.P.; Santos, J.F.; Bezerra, R.D.S.; Porto, A.L.F. Physical, Biochemical, Densitometric and spectroscopic techniques for characterization collagen from alternative sources: A review based on the sustainable valorization of aquatic by-products. J. Mol. Struct. 2020, 1224, 129023. [Google Scholar] [CrossRef]
  37. Semenycheva, L.L.; Valetova, N.B.; Chasova, V.O.; Podguzkova, M.V.; Zakharycheva, N.S.; Egorikhina, M.; Astanina, M.V.; Kuznetsova, Y.L. Molecular Weight Parameters of Collagen from Different Feedstock and Dynamics of Their Change upon Enzymatic Hydrolysis by Pancreatin. Polym. Sci. Ser. D 2020, 13, 235–239. [Google Scholar] [CrossRef]
  38. Gojkovic, Z.; Marova, I.; Matouskova, P.; Obruca, S.; Miloslav, P. Use of Ultrasonic Spectroscopy and Viscosimetry for the Characterization of Chicken Skin Collagen in Comparison with Collagens from other Animal Tissues. Prep. Biochem. Biotechnol. 2014, 44, 761–771. [Google Scholar] [CrossRef]
  39. Carvalho, A.M.; Marques, A.P.; Silva, T.H.; Reis, R.L. Evaluation of the potential of collagen from codfish skin as a bio-material for biomedical applications. Mar. Drugs 2018, 16, 495. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  40. Gauza-Włodarczyk, M.; Kubisz, L.; Mielcarek, S.; Włodarczyk, D. Comparison of thermal properties of fish collagen and bovine collagen in the temperature range 298–670 K. Mater. Sci. Eng. C 2017, 80, 468–471. [Google Scholar] [CrossRef]
  41. Nuñez, S.M.; Guzmán, F.; Valencia, P.; Almonacid, S.; Cárdenas, C. Collagen as a source of bioactive peptides: A bioinformatics approach. Electron. J. Biotechnol. 2020, 48, 101–108. [Google Scholar] [CrossRef]
  42. Sorushanova, A.; Skoufos, I.; Tzora, A.; Mullen, A.M.; Zeugolis, D.I. The influence of animal species, gender and tissue on the structural, biophysical, biochemical and biological properties of collagen sponges. J. Mater. Sci. Mater. Med. 2021, 32, 1–12. [Google Scholar] [CrossRef]
  43. Ghodbane, S.A.; Dunn, M. Physical and mechanical properties of cross-linked type I collagen scaffolds derived from bovine, porcine, and ovine tendons. J. Biomed. Mater. Res. Part A 2016, 104, 2685–2692. [Google Scholar] [CrossRef] [Green Version]
  44. Egorikhina, M.N.; Aleynik, D.Y.; Rubtsova, Y.P.; Levin, G.Y.; Charykova, I.N.; Semenycheva, L.L.; Bugrova, M.L.; Zakharychev, E.A. Hydrogel scaffolds based on blood plasma cryoprecipitate and collagen derived from various sources: Structural, mechanical and biological characteristics. Bioact. Mater. 2019, 4, 334–345. [Google Scholar] [CrossRef]
  45. Egorikhina, M.N.; Levin, G.Y.; Charykova, I.N.; Alejnik, D.Y.; Sosnina, L.N. Method for Creating a Bioresorbable Cellular Scaffold Based on Fibrin of Blood Plasma. Patent 2653434 RU; Int. Cl. C12N 5/00, 8 May 2018. [Google Scholar]
  46. Arulmolia, J.; Wrightb, H.J.; Phanc, D.T.T.; Shethb, U.; Quea, R.A.; Bottend, G.A.; Keatinga, M. Combination scaffolds of salmon fibrin, hyaluronic acid, and laminin for human neural stem cell and vascular tissue engineering. Acta Biomater. 2016, 46, 122–138. [Google Scholar] [CrossRef] [Green Version]
  47. Sproul, E.P.; Hannan, R.T.; Brown, A.C. Controlling Fibrin Network Morphology, Polymerization, and Degradation Dynamics in Fibrin Gels for Promoting. Tissue Repair. 2018, 1758, 85–99. [Google Scholar] [CrossRef]
  48. Solovieva, E.V.; Fedotov, A.Y.; E Mamonov, V.; Komlev, V.S.; A Panteleyev, A. Fibrinogen-modified sodium alginate as a scaffold material for skin tissue engineering. Biomed. Mater. 2017, 13, 025007. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  49. León-López, A.; Morales-Peñaloza, A.; Martínez-Juárez, V.M.; Vargas-Torres, A.; Zeugolis, D.I.; Aguirre-Álvarez, G. Hydrolyzed collagen-sources and applications. Molecules 2019, 24, 4031. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  50. Raja, H.; Mohd, R.N.; Yaakob, M.C.; Amin, I.; Noorfaizan, A. Chemical and functional properties of bovine and porcine skin gelatin. Int. Food Res. J. 2011, 18, 813–817. [Google Scholar]
  51. Sotelo, C.G.; Comesaña, M.B.; Ariza, P.R.; Ricardo, I. Characterization of collagen from different discarded fish species of the west coast of the iberian peninsula characterization of collagen from different discarded fish species. J. Aquat. Food Prod. Technol. 2016, 25, 388–399. [Google Scholar] [CrossRef] [Green Version]
  52. Meyer, M. Processing of collagen based biomaterials and the resulting materials properties. Biomed. Eng. Online 2019, 18, 1–74. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  53. Buckley, M. Species identification of bovine, ovine and porcine type 1 collagen; comparing peptide mass fingerprinting and LC-based proteomics methods. Int. J. Mol. Sci. 2016, 17, 445. [Google Scholar] [CrossRef] [Green Version]
  54. Semenycheva, L.L.; Kuznetsova, J.L.; Valetova, N.B.; Geras’kina, E.V.; Tarankova, O.A. Method for Producing of Acetic Dispersion of High Molecular Fish Collagen. Patent RF No. RU 2567171 C1, 10 November 2015. [Google Scholar]
  55. Available online: https://www.sigmaaldrich.com/RU/ru/product/sigma/c9791 (accessed on 25 August 2021).
  56. Komsa-Penkova, R.; Koynova, R.; Kostov, G.; Tenchov, B.G. Thermal stability of calf skin collagen type I in salt solutions. Biochim. Biophys. Acta (BBA)-Protein Struct. Mol. Enzym. 1996, 1297, 171–181. [Google Scholar] [CrossRef]
  57. Shtykova, E.V.; Bogacheva, E.N.; Dadinova, L.A.; Jeffries, C.M.; Fedorova, N.V.; Golovko, A.O.; Baratova, L.A.; Batishchev, O. Small-angle X-Ray analysis of macromolecular structure: The structure of protein NS2 (NEP) in solution. Crystallogr. Rep. 2017, 62, 894–902. [Google Scholar] [CrossRef]
  58. Sartuqui, J.; Elía, N.D.; Gravina, A.N.; Messina, P.V. Analyzing the hydrodynamic and crowding evolution of aqueous hydroxyapatite-gelatin networks: Digging deeper into bone scaffold design variables. Biopolymers 2015, 103, 393–405. [Google Scholar] [CrossRef] [PubMed]
  59. Rosenblum, G.; Steen, P.V.D.; Cohen, S.; Bitler, A.; Brand, D.; Opdenakker, G.; Sagi, I. Direct Visualization of Protease Action on Collagen Triple Helical Structure. PLoS ONE 2010, 5, e11043. [Google Scholar] [CrossRef] [Green Version]
  60. Semenycheva, L.L.; Egorikhina, M.; Chasova, V.O.; Valetova, N.B.; Podguzkova, M.V.; Astanina, M.V.; Kuznetsova, Y.L. Enzymatic hydrolysis of collagen by pancreatin and thrombin as a step in the formation of scaffolds. Russ. Chem. Bull. 2020, 69, 164–168. [Google Scholar] [CrossRef]
  61. Semenycheva, L.L.; Egorikhina, M.N.; Chasova, V.O.; Valetova, N.B.; Kuznetsova, Y.L.; Mitin, A.V. Enzymatic Hydrolysis of Marine Collagen and Fibrinogen Proteins in the Presence of Thrombin. Mar. Drugs 2020, 18, 208. [Google Scholar] [CrossRef] [Green Version]
  62. Bender, M.; Bergeron, R.; Komiyama, M. Bioorganic Chemistry of Enzymatic Catalysis; Mir: Moscow, Russian, 1987; p. 352. [Google Scholar]
  63. Klein, T.; Eckhard, U.; Dufour, A.; Solis, N.; Overall, C.M. Proteolytic cleavage—Mechanisms, function, and “omic” approaches for a near-ubiquitous posttranslational modification. Chem. Rev. 2018, 118, 1137–1168. [Google Scholar] [CrossRef] [PubMed]
  64. Simpson, R.J. Fragmentation of Protein Using Trypsin. Cold Spring Harb. Protoc. 2006, 282, 2612–2626. [Google Scholar] [CrossRef]
  65. Momot, A.P.; Taranenko, I.A. Method for Determination of Fibrin Monomer Self-Assembly Time. Patent RF No. 2,366,955, 10 September 2009. [Google Scholar]
  66. Tumurova, T.B.; Shalbuev, D.V. Study of the effect of the fermented milk composition on the degree of destruction of the collagen macrostructure. In Proceedings of the XIV International Scientific and Practical Conference “Leather and fur in the XXI century: Technology, Quality, Ecology, Education”, Ulan-Ude, Russia, 5–8 September 2018; pp. 12–17. [Google Scholar]
  67. Masuelli, M.A. Mark-Houwink parameters for aqueous-soluble polymers and biopolymers at various temperatures. J. Polym. Biopolym. Phys. Chem. 2014, 2, 37–43. [Google Scholar]
  68. Sparrow, R.L.; Simpson, R.; Greening, D. A Protocol for the Preparation of Cryoprecipitate and Cryo-depleted Plasma for Proteomic Studies. In Serum/Plasma Proteomics; Humana Press: New York, NY, USA, 2017; Volume 1619, pp. 23–30. [Google Scholar] [CrossRef]
  69. Nascimento, B.; Goodnough, L.T.; Levy, J.H. Cryoprecipitate therapy. Br. J. Anaesth. 2014, 113, 922–934. [Google Scholar] [CrossRef] [Green Version]
  70. Ramanathan, A.; Karuri, N. Fibronectin alters the rate of formation and structure of the fibrin matrix. Biochem. Biophys. Res. Commun. 2014, 443, 395–399. [Google Scholar] [CrossRef]
  71. Falvo, M.R.; Gorkun, O.V.; Lord, S.T. The molecular origins of the mechanical properties of fibrin. Biophys. Chem. 2010, 152, 15–20. [Google Scholar] [CrossRef] [Green Version]
  72. Collet, J.P.; Shuman, H.; Ledger, R.E.; Lee, S.; Weisel, J.W. The elasticity of an individual fibrin fiber in a clot. Proc. Natl. Acad. Sci. USA 2005, 102, 9133–9137. [Google Scholar] [CrossRef] [Green Version]
  73. Bryant, S.J.; Durand, K.L.; Anseth, K.S. Manipulations in hydrogel chemistry control photoencapsulated chondrocyte behavior and their extracellular matrix production. J. Biomed. Mater. Res. Part A 2003, 67, 1430–1436. [Google Scholar] [CrossRef]
  74. Lee, S.; Tong, X.; Yang, F. Effects of the poly(ethylene glycol) hydrogel crosslinking mechanism on protein release. Biomater. Sci. 2015, 4, 405–411. [Google Scholar] [CrossRef] [Green Version]
  75. Egorikhina, M.N.; Rubtsova, Y.P.; Charykova, I.N.; Bugrova, M.L.; Bronnikova, I.I.; Mukhina, P.A.; Sosnina, L.N.; Aleynik, D.Y. Biopolymer Hydrogel Scaffold as An Artificial Cell Niche for Mesenchymal Stem Cells. Polymers 2020, 12, 2550. [Google Scholar] [CrossRef]
Marinedrugs 19 00502 g001 550
Figure 1. MWD curve of the initial samples of CC (a) and BC (b).
Figure 1. MWD curve of the initial samples of CC (a) and BC (b).
Marinedrugs 19 00502 g001
Marinedrugs 19 00502 g002 550
Figure 2. IR spectra of CC and BC films.
Figure 2. IR spectra of CC and BC films.
Marinedrugs 19 00502 g002
Marinedrugs 19 00502 g003a 550Marinedrugs 19 00502 g003b 550
Figure 3. MWD curves of CC hydrolysates with pancreatin (a) and thrombin (b), BC with pancreatin (c), and thrombin (d) for 3 days.
Figure 3. MWD curves of CC hydrolysates with pancreatin (a) and thrombin (b), BC with pancreatin (c), and thrombin (d) for 3 days.
Marinedrugs 19 00502 g003aMarinedrugs 19 00502 g003b
Marinedrugs 19 00502 g004 550
Figure 4. Collagen hydrolysis scheme in the presence of enzymes.
Figure 4. Collagen hydrolysis scheme in the presence of enzymes.
Marinedrugs 19 00502 g004
Marinedrugs 19 00502 g005 550
Figure 5. Scheme showing collagen hydrolysate formation—scaffold fragments.
Figure 5. Scheme showing collagen hydrolysate formation—scaffold fragments.
Marinedrugs 19 00502 g005
Marinedrugs 19 00502 g006 550
Figure 6. Photographs of a coagulate from a hydrolysate of a CC and Fg mixture (a) and of a CC and Fg scaffold (b).
Figure 6. Photographs of a coagulate from a hydrolysate of a CC and Fg mixture (a) and of a CC and Fg scaffold (b).
Marinedrugs 19 00502 g006
Marinedrugs 19 00502 g007 550
Figure 7. MWD curves of polymer fractions of hybrid scaffold hydrolysates based on fibrinogen with collagen: CC (a) and BC (b).
Figure 7. MWD curves of polymer fractions of hybrid scaffold hydrolysates based on fibrinogen with collagen: CC (a) and BC (b).
Marinedrugs 19 00502 g007
Marinedrugs 19 00502 g008 550
Figure 8. Particle size distribution curves for the scattering intensity of solutions of scaffolds with CC (a) and BC (b) in acetic acid solution.
Figure 8. Particle size distribution curves for the scattering intensity of solutions of scaffolds with CC (a) and BC (b) in acetic acid solution.
Marinedrugs 19 00502 g008
Marinedrugs 19 00502 g009 550
Figure 9. Microstructure of native CC (a), BC (b) and fibrinogen (c) lyophilisate film samples; structure of the coagulate based on Fg and CC (d)—lyophilisate, cross section.
Figure 9. Microstructure of native CC (a), BC (b) and fibrinogen (c) lyophilisate film samples; structure of the coagulate based on Fg and CC (d)—lyophilisate, cross section.
Marinedrugs 19 00502 g009
Marinedrugs 19 00502 g010 550
Figure 10. Microstructure of hybrid scaffold samples based on collagen and Fg: microarchitectonics of the scaffold surface (a,b), the internal architectonics of scaffolds seen in cross section—dehydrated under low vacuum conditions (c,d); the structure of scaffolds dissolved in 3% acetic acid—lyophilisates (e,f).
Figure 10. Microstructure of hybrid scaffold samples based on collagen and Fg: microarchitectonics of the scaffold surface (a,b), the internal architectonics of scaffolds seen in cross section—dehydrated under low vacuum conditions (c,d); the structure of scaffolds dissolved in 3% acetic acid—lyophilisates (e,f).
Marinedrugs 19 00502 g010
Table
Table 1. Molecular weight parameters * of the high molecular collagen (HMC).
Table 1. Molecular weight parameters * of the high molecular collagen (HMC).
Item No. Nature of CollagenMw × 10−3,
kDa		Mw/MnContent of HMC in the Dry Residue of Collagen, %
1CC250–3001.2–1.395–97
217–201.1–1.23–5
39–101.1–1.2trace amounts
4BC600–9501.2–1.692–93
517–201.1–1.27–8
69–101.1–1.2trace amounts
Note: Mw—average molecular weight, Mw/Mn—coefficient of polydispersion. * Results obtained for a series of samples.
Table
Table 2. Molecular weight parameters of the initial and thrombin hydrolyzed CC and BC samples.
Table 2. Molecular weight parameters of the initial and thrombin hydrolyzed CC and BC samples.
Item No. SampleParameter Values during Hydrolysis
InitialMin3 Days
160
Mw, kDaMw, kDa Mw, kDaMw, kDa
ValueFraction, %ValueFraction, %ValueFraction, %ValueFraction, %
1CC30096125–127151241612116
217–18417–18217–18217–188
3--9–10839–10829–1076
4BC 9509399079808˃10310
5177–8175171–2173
6--9–10889–1090–919–1087
Note: collagen:thrombin ratio = 102:1.
Table
Table 3. Molecular weight parameters of scaffold hydrolysates based on fibrinogen and collagens of different origins.
Table 3. Molecular weight parameters of scaffold hydrolysates based on fibrinogen and collagens of different origins.
Item No.Scaffold Based onMw × 10−3, kDaMw/MnContent, %
1CC120–1501.2–1.315
201.012
101.058
oligomers1.215
2BC200–2401.4–1.630
201.014
101.046
oligomers1.210
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Egorikhina, M.N.; Semenycheva, L.L.; Chasova, V.O.; Bronnikova, I.I.; Rubtsova, Y.P.; Zakharychev, E.A.; Aleynik, D.Y. Changes in the Molecular Characteristics of Bovine and Marine Collagen in the Presence of Proteolytic Enzymes as a Stage Used in Scaffold Formation. Mar. Drugs 2021, 19, 502. https://doi.org/10.3390/md19090502

AMA Style

Egorikhina MN, Semenycheva LL, Chasova VO, Bronnikova II, Rubtsova YP, Zakharychev EA, Aleynik DY. Changes in the Molecular Characteristics of Bovine and Marine Collagen in the Presence of Proteolytic Enzymes as a Stage Used in Scaffold Formation. Marine Drugs. 2021; 19(9):502. https://doi.org/10.3390/md19090502

Chicago/Turabian Style

Egorikhina, Marfa N., Ludmila L. Semenycheva, Victoria O. Chasova, Irina I. Bronnikova, Yulia P. Rubtsova, Evgeniy A. Zakharychev, and Diana Ya. Aleynik. 2021. "Changes in the Molecular Characteristics of Bovine and Marine Collagen in the Presence of Proteolytic Enzymes as a Stage Used in Scaffold Formation" Marine Drugs 19, no. 9: 502. https://doi.org/10.3390/md19090502

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.