Next Article in Journal
Physiological Doses of Oleic and Palmitic Acids Protect Human Endothelial Cells from Oxidative Stress
Next Article in Special Issue
A Combined Experimental and Computational Study on the Adsorption Sites of Zinc-Based MOFs for Efficient Ammonia Capture
Previous Article in Journal
Diindolylmethane Inhibits Cadmium-Induced Autophagic Cell Death via Regulation of Oxidative Stress in HEL299 Human Lung Fibroblasts
Previous Article in Special Issue
Photocatalytic Hydrogen Production by the Sensitization of Sn(IV)-Porphyrin Embedded in a Nafion Matrix Coated on TiO2
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 27
Issue 16
10.3390/molecules27165216
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

A Three-Dimensional Melamine Sponge Modified with MnOx Mixed Graphitic Carbon Nitride for Photothermal Catalysis of Formaldehyde

by
Rongyang Yin
,
Pengfei Sun
*,
Lujun Cheng
,
Tingting Liu
,
Baocheng Zhou
and
Xiaoping Dong
Department of Chemistry, Key Laboratory of Surface & Interface Science of Polymer Materials of Zhejiang Province, Zhejiang Sci-Tech University, 928 Second Avenue, Xiasha Higher Education Zone, Hangzhou 310018, China
*
Author to whom correspondence should be addressed.
Molecules 2022, 27(16), 5216; https://doi.org/10.3390/molecules27165216
Submission received: 20 July 2022 / Revised: 10 August 2022 / Accepted: 11 August 2022 / Published: 16 August 2022
(This article belongs to the Special Issue Catalytic Nanomaterials: Energy and Environment)
Browse Figures
Versions Notes

Abstract

:
Much attention has been paid to developing effective visible light catalytic technologies for VOC oxidation without requiring extra energy. In this paper, a series of sponge-based catalysts with rich three-dimensional porosity are synthesized by combining MnOx and graphitic carbon nitride (GCN) with commercial melamine sponges (MS) coated with polydopamine (PDA), demonstrating excellent photothermal catalytic performance for formaldehyde (HCHO). The three-dimensional porous framework of MS can provide a good surface for material modification and a reliable interface for gas-solid interaction. The grown layer of PDA framework not only increases the near-infrared wavelength absorption for improving the light-to-heat conversion of catalysts, but also brings excellent adhesion for the subsequent addition of MnOX and GCN. The efficient formaldehyde oxidation is attributed to the sufficient oxygen vacancies generated by co-loaded MnOX and GCN, which is conducive to the activation of more O2− in the oxidation process. As the surface temperature of catalyst rapidly increases to its maximum value at ca. 115 °C under visible light irradiation, the HCHO concentration drops from 160 ppm to 46 ppm within 20 min. The reaction mechanism is certified as a classical Mars-van Krevelen mechanism based on the photo-induced thermal catalysis process.

1. Introduction

HCHO has been extensively found in boards, paints, carpets, and wallpapers commonly used in interior decoration. According to the International Agency for Research on Cancer, formaldehyde can cause cancer in humans, especially nasopharyngeal cancer and leukemia [1,2]. With the general public’s need for health and concern for a more efficient use of resources, it is of great importance to develop efficient and clean indoor HCHO degradation methods. At present, HCHO treatment methods mainly include absorption [3], biological incineration [4] and catalytic oxidation [5]. Among them, the activated carbon adsorption method is the most widely used; however, this requires regularly replacing activated carbon and recovering activated carbon wastes, thus resulting in higher elution costs. In contrast, catalytic oxidation converts exhaust gas into harmless carbon dioxide and water, which is more suitable for HCHO purification. In catalytic oxidation, synergistic photothermal catalysis technology is considered as an efficient and low-carbon HCHO removal technology that integrates the advantages of both photocatalysis and thermocatalysis. Under illumination, the material with photothermal effect does not directly change the state of the internal electrons after absorbing photons, but converts light energy into lattice thermal vibration, thus increasing the material’s temperature. The catalysts can be activated using natural light sources without requiring additional energy.
Manganese oxide (MnOx), as a common transition metal oxide, has the above photothermal properties. Li Yuanzhi et al. reported MnOx nano-catalysts with various structures that have been proven to activate lattice oxygen with sunlight and efficiently remove various VOCs [6]. Wang Wenzhong also modified MnOx with cobalt oxide with significantly improved photothermal catalytic performance for the oxidation of VOCs, which was attributed to the changing lattice oxygen structure in MnOx [7]. Wang Zhongsen also synthesized two-dimensional nanosheets of MnOx by adding graphene oxide and polymeric carbon nitride, achieving excellent visible light oxidation efficiency of HCHO [2]. The photothermal effect of MnOx mainly originates from the non-radiative recombination of electron-hole pairs produced by the d-d transition of metal ions upon the absorption of photons. The surface temperature of MnOx increases even more efficiently after being modified by other photothermal materials such as black carbon or graphene, as black carbon-based materials are able to more sufficiently absorb the solar spectrum than metal oxide, ranging from ultraviolet light to the entire near-infrared band [8]. Thus, these materials endow MnOx with a stronger light-to-heat conversion ability, eventually inducing a thermal catalysis process with the Mars-van Krevelen (MvK) mechanism [9,10].
A three-dimensional porous composite MS/PDA/MnOx/GCN catalyst is synthesized by a simple method in this paper. A melamine sponge (MS) is used as a three-dimensional porous framework where a layer of polydopamine (PDA) is grown. Similar to carbon-based materials, black PDA has excellent light-to-heat conversion properties due to its strong ability to absorb near-infrared wavelengths [11]. Additionally, PDA exhibits excellent adhesion, which can firmly adhere subsequent MnOx nanosheets and graphitic carbon nitride (GCN) to further improve oxidation susceptibility and light-to-heat conversion. Compared with other photocatalysts without a fixed structure, this 3D skeleton structure exhibits better photoresponse performance. It provides a larger surface area for active phase loading and visible light absorption, which thus improves the removal efficiency of HCHO.
According to the experimental results, the synthesized catalyst exhibits a considerable HCHO photothermal catalytic removal efficiency with HCHO concentration dropping from 160 ppm to 46 ppm in 20 min. The morphology and surface elemental properties of the catalyst are also studied by SEM, HR-TEM, XRD, XPS, ESR, etc. Moreover, a surface reaction mechanism is proposed by using in situ DRIFTS and reactive oxygen species detection.

2. Experimental

2.1. Catalyst Synthesis

The flow chart of the synthesis process is shown in Figure 1: 50 mg dopamine hydrochloride was dispersed into 50 mL Tris-HCl solution (pH = 8.5) under agitation. Then, a blank melamine sponge (MS) with size = 2.5 cm3 was immersed into the solution and stirred magnetically for 6 h, which was named MS/PDA. After being washed with distilled water, the MS/PDA was further immersed in 50 mL 0.05 mol/L KMnO4 solution for 5 h at 60 °C and dried at 60 °C. The prepared sample was named MS/PDA/MnOx. Finally, the dried MS/PDA/MnOx was immersed into 0.2 g/L GCN suspension for 10 min by ultrasound. The obtained sample was washed by distilled water and dried at room temperature, which was named MS/PDA/MnOx/GCN. In order to investigate the influence of the loading sequence between GCN and MnOx on photothermal response performance, we also prepared the MS/PDA/GCN/MnOx catalyst by exchanging the synthesis order of the last two steps.

2.2. Characterization

The catalyst was characterized by scanning electron microscopy (SEM) using a field emission scanning electron microscope (Model SU-8100, Hitachi Co., Tokyo, Japan) equipped with an energy dispersive X-ray spectrometer (EDS). X-ray diffraction (XRD) was tested by a powder diffractometer with Cu Kα radiation (Model D/max RA, Rigaku Co., Tokyo, Japan). The chemical compositions and states were explored by X-ray photoelectron spectroscopy (XPS, Model AXIS UltraDLD, Kratos Co., Manchester, UK) using an Al Kα monochromatic source. Electron spin resonance (ESR) spectra were tested using an electron paramagnetic resonance spectrometer (Model ESP 300 E, Bruker Co., Ettlingen, Germany) equipped with a xenon lamp as a light source (420–600 nm). UV-vis-NIR diffuse-reflectance spectra (DRS) were analyzed on a HITACHI U-4100 spectrophotometer. The changes in the surface temperature of different catalysts were characterized by a thermal image (Model H21PRO, Hikvision Co., Hangzhou, China).

2.3. Photothermal Catalytic Performance

The performance of the catalyst was tested in a 0.5 L glass container containing a 0.2 g sponge sample, with observation glass in the middle. After the gas-phase reactor was preheated to ca. 40 °C, 2.0 μL HCHO (37%) solution was injected into the gas-phase reactor till completely evaporated. At this time, the initial concentration of HCHO was approximately ca. 160 ppm. A 300 W xenon lamp (Model HSX-F300, NBet Co., Beijing, China) was used as light source. The HCHO removal activity under light irradiation was indirectly evaluated by measuring the absorbance obtained by phenol reagent spectrophotometry (Model UV-2600, Shimadzu Co., Kyoto, Japan). During measurements, 5 mL gas was sampled with a syringe and injected into 5 mL 0.05 mol/L phenol reagent (MBTH hydrochloride hydrate) solution. Subsequently, 0.4 mL 1 wt.% NH4Fe(SO4)2 solution was added. After approximately 10 min, the absorbance of the above solution at 630 nm was measured. The changing surface temperature of the catalyst under light illuminations was also recorded by an infrared thermometer in the experimental process (Model H16, Hikvision Co., Hangzhou, China). A picture of the experimental set-up has been listed in the Supplementary Material.

2.4. Reaction Mechanism

The HCHO decomposition mechanism was clarified based on in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS) using a Bruker Co. Model TENSOR II spectrometer. The reaction spectra of HCHO on the surface of the catalyst were acquired by accumulating 32 scans at a 4 cm−1 resolution under the irradiation of a xenon lamp. To confirm the formation of oxidized OH radical and O2− radical during the reaction, the photoluminescence (PL) method with terephthalic acid (TA) oxidized by ·OH and blue tetrazolium (NBT) by O2− was employed. Both reaction products were detected by changing the absorbance using a fluoroanalyzer (Model Fluoromax-4, HORIBA Co., Kyoto, Japan).

3. Results and Discussion

3.1. Photothermal Catalytic Performance of Formaldehyde

The photothermal activity of different sponge loaded catalysts was evaluated by HCHO degradation (the concentration of HCHO was ca. 160 ppm) using 300 W xenon lamps. As displayed in Figure 2A, the HCHO concentration of four catalysts decreased to varying degrees. For MS/PDA, the poor removal efficiency of HCHO was obviously due to the lack of reactive oxygen species caused by the absence of loaded metal oxide. The catalysts MS/PDA/MnOx and MS/PDA/GCN/MnOx exhibited similar HCHO removal efficiency. The HCHO concentration declined from 160 ppm to 46 ppm within 20 min, implying that neither the oxidation susceptibility of subsequently loaded MnOx nor the photothermal synergistic performance of the catalyst was improved by adding GCN. However, the catalyst MS/PDA/MnOx/GCN revealed significantly improved HCHO removal performance compared with MS/PDA/GCN/MnOx, suggesting that the loading sequence of GCN had a great effect on the performance of the photothermal co-catalytic system.
Figure 2B shows the degradation of HCHO under different light sources. Obviously, the degradation efficiency of HCHO without any light irradiation was not ideal. Compared with the rapid decline in the degradation efficiency of HCHO under other conditions, NIR light played a key role in the HCHO removal though UV and visible light also contributed to the photodegradation of HCHO. Figure 2C also exhibits the change in the surface temperature of the catalyst MS/PDA/MnOx/GCN under the condition of different light sources. The surface temperature of the catalyst MS/PDA/MnOx/GCN filtered by NIR light did not obviously change compared with that with the presence of NIR light. The latter temperatures all significantly increased to ca. 115 °C. Thus, we believe the degradation of HCHO on the manganese-based catalyst was mainly affected by increased temperature, which induced the well-known Mars-van Krevelen process that decomposes CxHy utilizing·O2−, OH and other oxidation groups [10,12].
The UV-Vis-NIR DRS was also tested to evaluate the photo-thermal effect of four different catalysts. As shown in Figure S1, four catalysts all exhibited considerable NIR absorption (wavelength ranging from 400 to 800 nm) due to the loaded PDA. These were the efficient NIR-absorbing materials as reported in the literature [11,13]. For MS/PDA/MnOx/GCN, the highest NIR absorption was found. The NIR absorption of the catalyst MS/PDA/MnOx/GCN was found to be the highest because its outermost surface was further wrapped by GCN, which further increased NIR light absorption [14]. The changes in the surface temperature of the four catalysts were tested by thermal imaging, as exhibited in Figures S2 and S3. This was consistent with the UV-Vis-NIR DRS result that the catalyst MS/PDA/MnOx/GCN displayed the highest temperature.

3.2. Morphological Characteristics

As shown in Figure 3, the SEM image of the catalyst MS/PDA/MnOx/GCN exhibited uniformly attached MnOx on the 3D structure of MS. The EDX mapping also confirmed that the scanning of the Mn and O elements was in accordance with the MS skeleton. The XRD result is displayed in Figure 4. It can be observed from the figure that all the samples revealed an obvious peak at 2θ = ca. 22°, which was ascribed to the surface diffraction of the melamine sponge [11,13]. With the increase in surface load, the intensity of the diffraction peak became weaker. The characteristic peaks of Mn loaded samples at 2θ = 36.5° and 65.5° were ascribed to the (100) and (110) planes of an Akhtenskite MnOx phase (JCPDS NO.30-0820) [11,13], indicating that MnOx was effectively formed on the surface of the melamine sponge merely by using potassium permanganate. However, the loaded PDA and GCN were not identified by XRD diffraction patterns mainly due to the fact that the loading of these two substances always presented good dispersion, as exhibited by the SEM image.

3.3. Surface Properties

In order to further understand the different surface properties of the catalysts MS/PDA/MnOx, MS/PDA/MnOx/GCN and MS/PDA/GCN/MnOx, XPS analysis was carried out. As shown in Figure 5A, Mn 2p spectrum showed two characteristic peaks ascribed to Mn 2p 3/2 (641.9 eV) and Mn 2p 1/2 (653.4 eV) [15,16], which suggests the presence of MnO2. It should be noted that the splitting energy between these two characteristic peaks was 11.6 eV for MS/PDA/MnOx/GCN and 11.8 eV for MS/PDA/MnOx and MS/PDA/GCN/MnOx. The splitting energy of MS/PDA/MnOx/GCN decreased because of the enhanced π electron cloud density [16], which was probably originated from the reaction between the residual GCN on the external surface of MnOx and its functional groups.
The C 1s spectrum (Figure 5B) shows four peaks at 284.4, 286.2, 287.7 and 288.6 eV, respectively. The peak at 287.7 eV was ascribed to carbon in the melamine sponge conjugated system [11]. The peaks at 284.4 and 286.2 eV corresponded to sp2 graphite carbon in the PDA structure and C-O carbon in the benzene ring of the PDA molecules, respectively [11,17]. Additionally, the peak at 287.7 eV was ascribed to C=N to the GCN structure [18]. It was also observed that the order of GCN addition determined whether GCN reacted with PDA or MnOx. For MS/PDA/GCN/MnOx, PDA (peak at 284.4 eV) was found to be depleted compared with MS/PDA/MnOx/GCN and MS/PDA/MnOx. For the latter two catalysts, the PDA firstly reacted with manganese, resulting in a similar PDA structure. Especially for MS/PDA/MnOx/GCN, as GCN was loaded after MnOx, a tight bonding with MnOx as the splitting energy of Mn 2p shift was detected, as shown in Figure 5A.
The O 1s spectrum (Figure 5C) was divided into three peaks. The peak at 529.6 eV was ascribed to the lattice oxygen of Mn-O-Mn in MnOx [19], that at 531.3 eV was ascribed to surface chemisorbed oxygen species [20], and that at 532.8 eV was ascribed to hydroxyl groups such as Mn-OH or H-OH [21,22]. All of three Mn loaded catalysts exhibited chemisorbed oxygen species and lattice oxygen due to the predominant oxygen species formed on the surface MnOx. After the addition of GCN, the ionized oxygen species such as OH- emerged, indicating that the functional groups of GCN promoted the transformation of Mn-O to Mn-OH. As reported in the literature [23,24,25], GCN improves electrical conductivity and reduces the electron-transfer resistance of metal oxide and thus promotes the formation of Mn atoms and oxygen atoms into a covalent coordination bond or a hydrogen bond, such as Mn-OH.
Three fitted absorption bands can be observed in the N 1s spectrum in Figure S4. The peak around 398.6 eV resulted from N species in the C=N-C unit, while that at ca. 399.5 eV was assigned to the N-H groups in PDA and melamine sponge [11,26] and that around 400.2 eV to the N-(C)3 in GCN [2,27]. For MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN, the peak around 404.2 eV ascribed to π electron cloud density was caused by doped GCN [25].

3.4. Reaction Mechanism

The photo-thermal-induced ROS were tested to further explore the reaction mechanism on the catalyst surface. The PL detection method was employed to confirm the generation of hydroxide radical with p-Phthalic acid (TA) as indicator. As shown in Figure 6A, the oxidative product TAOH had a sole fluorescence response at 425 nm [28]. It can be clearly found that the PL strength on the three Mn supported catalysts was significantly improved as the irradiation time increased, indicating that hydroxide was produced during the reaction. The formation of ·O2− radical was also tested by nitro blue tetrazolium (NBT) as the indicator [29]. As shown in Figure 6B, the concentration of NBT over the catalysts MS/PDA/GCN/MnOx and MS/PDA/MnOx did not decrease significantly, meaning that O2 molecules were not activated on both catalysts. However, the generation of O2− radical on MS/PDA/MnOx/GCN was obvious. The result implies that the outermost layer of GCN provides favorable conditions for the adsorption and activation of O2 molecules on the reaction interface, which was also confirmed by the ESR result for oxygen vacancy determination. As shown in Figure 7, all samples showed a pair of steep peaks with a symmetric distribution in accordance with g = 2.002, an indication of electron trapping at oxygen vacancies [30]. It can be concluded from the ESR result of the catalyst MS/PDA/GCN that the addition of GCN provides a large number of oxygen vacancies for the catalyst system. Additionally, the catalysts MS/PDA/MnOx/GCN had more oxygen vacancies than MS/PDA/GCN/MnOx and MS/PDA/MnOx, as the loaded GCN on the outermost layer was partially retained. The formation of sufficient oxygen vacancies promoted the absorption and activation of O2 atoms [31], leading to the formation of more ·O2− radicals over MS/PDA/MnOx/GCN.
In situ DRIFTS measurements were also conducted to obtain insight into the HCHO degradation mechanism. As shown in Figure 8, several vibration peaks were identified at approximately 3634, 2363, 2335, 1712, 1550, 1425 and 1243 cm−1. It can be found that the peak at 1425 cm−1 represented the vibrations of dioxymethylene (DOM) [32,33]. Additionally, another group peak at 1712 and 1550 cm−1 represented formate (HCOO−) species [32,33]. These are the primary degradation products of HCHCO oxidation. With the extension of reaction time, their corresponding vibration peaks gradually increased, indicating the absorption and accumulation of HCHO. The shoulder peaks at 2363 and 2335 cm−1 corresponded to CO2 adsorption with a corresponding vibration peak at 1243 cm−1 (assigned to the CO32− oxidized from HCOO−) [9,34], implying the final mineralization of HCHO. There was also a very strong negative peak at 3634 cm−1, which was assigned to hydroxyl vibration peak, representing a large consumption of Mn-OH during HCHO oxidation [35,36].
Based on all the above, a plausible mechanism for HCHO oxidation over MS/PDA/MnOx/GCN is proposed as Figure 9. HCHO molecules were firstly adsorbed onto Mn-OH groups through hydrogen bonding [37,38], further utilizing adjacent Mn-O to form CO2 and H2O. Concurrently, O2 molecules absorbed onto conterminal oxygen vacancies to activate O2− and were involved in the formation of CO2 and the replenishment of Mn-O.

3.5. Reusability

The cyclic performance of catalysts is very important for photocatalytic materials, which can be used to estimate whether the catalyst is easy to deactivate. The deactivation of a catalyst always arises due to the loss of intrinsic (per-site) activity, or a decrease in the number of active sites, or increasingly restricted access to the active sites [39]. Based on the above in situ DRIFTS analysis and mechanism elaboration results, we can speculate that the most likely cause of deactivation over this catalyst was only due to the accumulation of residue at the active site. As shown in Figure 10, HCHO was purified by the MS/PDA/MnOx/GCN catalyst five times. The results showed that the purification effect of HCHO was basically the same as that purified for the first time. Although it would be wrong to repeat the experiment to measure the stability of the catalyst at 100% conversion without studying under kinetically controlled conditions [39], we could not measure stability at the 50% or 90% conversion rates because the high sensitivity of this catalyst could achieve a 100% conversion rate of HCHO in a very short time. However, it is worth noting that the MS/PDA/MnOx/GCN catalyst exhibited excellent reuse performance for at least five tests, which indicates the potential to be developed as a commercial catalyst against indoor HCHO removal.

4. Conclusions

To sum up, we designed an integral HCHO photocatalyst characterized by impressive light-to-heat conversion property and excellent reusability. The concentration of HCHO dropped from 160 ppm to 46 ppm within 20 min under the irradiation of visible light. The addition of GCN promoted the formation of oxygen vacancy, thus facilitating the activation of surface reactive oxygen species and maintaining the efficient oxidation of HCHO under a spontaneously rising surface temperature. The association of GCN with MnOx over common three-dimensional sponge materials offers great potential for commercial catalyst development aimed at indoor HCHO control without using noble metals, which also makes a significant contribution to the literature regarding catalysts designed to reduce environmental air pollution.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/molecules27165216/s1, Figure S1: UV–Vis-NIR DRS profiles of catalyst MS/PDA, MS/PDA/MnOx, MS/PDA/GCN/MnOx, and MS/PDA/MnOxGCN; Figure S2: Changes in surface temperature of catalyst MS/PDA, MS/PDA/MnOx, MS/PDA/GCN/MnOx, and MS/PDA/MnOxGCN over visible light irradiation; Figure S3: The thermal imagery of catalyst MS/PDA, MS/PDA/MnOx, MS/PDA/GCN/MnOx, and MS/PDA/MnOxGCN over visible light irradiation; Figure S4: N 1s XPS spectra of catalyst MS/PDA/MnOx, MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN; Figure S5: Photos of the experiment process.

Author Contributions

Conceptualization, X.D.; methodology, P.S. and L.C.; validation, P.S., L.C. and T.L.; formal analysis, P.S. and T.L.; investigation, R.Y.; writing—original draft preparation, R.Y.; writing—review and editing, P.S., B.Z. and X.D.; supervision, P.S., B.Z. and X.D. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Natural Science Founding of China (51908491), the National Key Research and Development Program of China (2017YFE0127400) and Science Fund of Zhejiang Sci-Tech University (21062255-Y).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

Sample Availability

Samples mentioned in paper are available from the authors.

References

  1. Cogliano, V.J.; Grosse, Y.; Baan, R.A.; Straif, K.; Secretan, M.B.; Ghissassi, F.E.; Working Group for Volume 88. Meeting report: Summary of IARC monographs on formaldehyde, 2-butoxyethanol, and 1-tert-butoxy-2-propanol. Environ. Health Perspect. 2005, 113, 1205–1208. [Google Scholar] [CrossRef] [PubMed]
  2. Wang, Z.; Yu, H.; Xiao, Y.; Zhang, L.; Guo, L.; Zhang, L.; Dong, X. Free-standing composite films of multiple 2D nanosheets: Synergetic photothermocatalysis/photocatalysis for efficient removal of formaldehyde under ambient condition. Chem. Eng. J. 2020, 394, 125014. [Google Scholar] [CrossRef]
  3. Zhang, W.; Huang, T.; Ren, Y.; Wang, Y.; Yu, R.; Wang, J.; Tu, Q. Preparation of chitosan crosslinked with metal-organic framework (MOF-199)@aminated graphene oxide aerogel for the adsorption of formaldehyde gas and methyl orange. Int. J. Biol. Macromol. 2021, 193, 2243–2251. [Google Scholar] [CrossRef] [PubMed]
  4. Rovina, K.; Vonnie, J.M.; Shaeera, S.N.; Yi, S.X.; Halid, N.F.A. Development of biodegradable hybrid polymer film for detection of formaldehyde in seafood products. Sens. Bio-Sens. Res. 2020, 27, 100310. [Google Scholar] [CrossRef]
  5. Cao, K.; Dai, X.; Wu, Z.; Weng, X. Unveiling the importance of reactant mass transfer in environmental catalysis: Taking catalytic chlorobenzene oxidation as an example. Chin. Chem. Lett. 2021, 32, 1206–1209. [Google Scholar] [CrossRef]
  6. Liu, F.; Zeng, M.; Li, Y.; Yang, Y.; Mao, M.; Zhao, X. UV-Vis-Infrared Light Driven Thermocatalytic Activity of Octahedral Layered Birnessite Nanoflowers Enhanced by a Novel Photoactivation. Adv. Funct. Mater. 2016, 26, 4518–4526. [Google Scholar] [CrossRef]
  7. Zheng, Y.; Wang, W.; Jiang, D.; Zhang, L.; Li, X.; Wang, Z. Ultrathin mesoporous Co3O4 nanosheets with excellent photo-/thermo-catalytic activity. J. Mater. Chem. A 2016, 4, 105–112. [Google Scholar] [CrossRef]
  8. Fu, L.; Wang, R.; Zhao, C.; Huo, J.; He, C.; Kim, K.-H.; Zhang, W. Construction of Cr-embedded graphyne electrocatalyst for highly selective reduction of CO2 to CH4: A DFT study. Chem. Eng. J. 2021, 414, 128857. [Google Scholar] [CrossRef]
  9. Tang, X.; Chen, J.; Li, Y.; Li, Y.; Xu, Y.; Shen, W. Complete oxidation of formaldehyde over Ag/MnOx-CeO2 catalysts. Chem. Eng. J. 2006, 118, 119–125. [Google Scholar] [CrossRef]
  10. Zhang, J.; Li, Y.; Wang, L.; Zhang, C.; He, H. Catalytic oxidation of formaldehyde over manganese oxides with different crystal structures. Catal. Sci. Technol. 2015, 5, 2305–2313. [Google Scholar] [CrossRef]
  11. Wang, Z.; Yu, H.; Xiao, Y.; Guo, L.; Zhang, L.; Dong, X. Polydopamine mediated modification of manganese oxide on melamine sponge for photothermocatalysis of gaseous formaldehyde. J. Hazard. Mater. 2021, 407, 124795. [Google Scholar] [CrossRef] [PubMed]
  12. Mao, C.; Vannice, M. Formaldehyde Oxidation over Ag Catalysts. J. Catal. 1995, 154, 230–244. [Google Scholar] [CrossRef]
  13. Sun, P.; Yu, H.; Liu, T.; Li, Y.; Wang, Z.; Xiao, Y.; Dong, X. Efficiently photothermal conversion in a MnOx-based monolithic photothermocatalyst for gaseous formaldehyde elimination. Chin. Chem. Lett. 2022, 33, 2564–2568. [Google Scholar] [CrossRef]
  14. Liang, Q.; Li, Z.; Huang, Z.-H.; Kang, F.; Yang, Q.-H. Holey Graphitic Carbon Nitride Nanosheets with Carbon Vacancies for Highly Improved Photocatalytic Hydrogen Production. Adv. Funct. Mater. 2015, 25, 6885–6892. [Google Scholar] [CrossRef]
  15. Sun, P.; Wang, W.; Dai, X.; Weng, X.; Wu, Z. Mechanism study on catalytic oxidation of chlorobenzene over MnxCe1−xO2/H-ZSM5 catalysts under dry and humid conditions. Appl. Catal. B Environ. 2016, 198, 389–397. [Google Scholar] [CrossRef]
  16. Lu, L.; Tian, H.; He, J.; Yang, Q. Graphene-MnO2 hybrid nanostructure as a new catalyst for formaldehyde oxidation. J. Phys. Chem. C 2016, 120, 23660–23668. [Google Scholar] [CrossRef]
  17. Li, L.; Chi, L.; Zhang, H.; Wu, S.; Wang, H.; Luo, Z.; Li, Y.; Li, Y. Fabrication of Ti-PDA nanoparticles with enhanced absorption and photocatalytic activities for hexavalent chromium Cr(VI) removal. Appl. Surf. Sci. 2022, 580, 152168. [Google Scholar] [CrossRef]
  18. Gao, P.; Zhou, W.; Zhang, J.; Yang, Z.; Yuan, X.; Wang, Z. The effect of acidified graphite carbon nitride on the removal of pollutants by coupling filtration and photocatalysis. Appl. Surf. Sci. 2021, 542, 148675. [Google Scholar] [CrossRef]
  19. Zhao, Q.; Chen, D.; Li, Y.; Zhang, G.; Zhang, F.; Fan, X. Rhodium complex immobilized on graphene oxide as an efficient and recyclable catalyst for hydrogenation of cyclohexene. Nanoscale 2013, 5, 882–885. [Google Scholar] [CrossRef]
  20. Sun, P.; Zhai, S.; Chen, J.; Yuan, J.; Wu, Z.; Weng, X. Development of a multi-active center catalyst in mediating the catalytic destruction of chloroaromatic pollutants: A combined experimental and theoretical study. Appl. Catal. B Environ. 2020, 272, 119015. [Google Scholar] [CrossRef]
  21. Li, L.; Yan, J.; Wang, T.; Zhao, Z.-J.; Zhang, J.; Gong, J.; Guan, N. Sub-10 nm rutile titanium dioxide nanoparticles for efficient visible-light-driven photocatalytic hydrogen production. Nat. Commun. 2015, 6, 5881. [Google Scholar] [CrossRef] [PubMed]
  22. Wang, M.; Zhang, P.; Li, J.; Jiang, C. The effects of Mn loading on the structure and ozone decomposition activity of MnOx supported on activated carbon. Chin. J. Catal. 2014, 35, 335–341. [Google Scholar] [CrossRef]
  23. Li, K.; Tong, Y.; Feng, D.; Chen, P. Electronic regulation of platinum species on metal nitrides realizes superior mass activity for hydrogen production. J. Colloid Interface Sci. 2022, 622, 410–418. [Google Scholar] [CrossRef] [PubMed]
  24. Simaioforidou, A.; Georgiou, Y.; Bourlinos, A.; Louloudi, M. Molecular Mn-catalysts grafted on graphitic carbon nitride (gCN): The behavior of gCN as support matrix in oxidation reactions. Polyhedron 2018, 153, 41–50. [Google Scholar] [CrossRef]
  25. Wang, Z.; Gu, Z.; Wang, F.; Hermawan, A.; Hirata, S.; Asakura, Y.; Hasegawa, T.; Zhu, J.; Inada, M.; Yin, S. An ultra-sensitive room temperature toluene sensor based on molten-salts modified carbon nitride. Adv. Powder Technol. 2021, 32, 4198–4209. [Google Scholar] [CrossRef]
  26. Peng, S.; Yang, X.; Strong, J.; Sarkar, B.; Jiang, Q.; Peng, F.; Liu, D.; Wang, H. MnO2-decorated N-doped carbon nanotube with boosted activity for low-temperature oxidation of formaldehyde. J. Hazard. Mater. 2020, 396, 122750. [Google Scholar] [CrossRef]
  27. Yao, C.; Wang, R.; Wang, Z.; Lei, H.; Dong, X.; He, C. Highly dispersive and stable Fe3+ active sites on 2D graphitic carbon nitride nanosheets for efficient visible-light photocatalytic nitrogen fixation. J. Mater. Chem. A 2019, 7, 27547–27559. [Google Scholar] [CrossRef]
  28. Lei, H.; Zhang, H.; Zou, Y.; Dong, X.; Jia, Y.; Wang, F. Synergetic photocatalysis/piezocatalysis of bismuth oxybromide for degradation of organic pollutants. J. Alloy Compd. 2019, 809, 151840. [Google Scholar] [CrossRef]
  29. Wang, Z.; Yu, H.; Zhang, L.; Guo, L.; Dong, X. Photothermal conversion of graphene/layered manganese oxide 2D/2D composites for room-temperature catalytic purification of gaseous formaldehyde. J. Taiwan Inst. Chem. Eng. 2020, 107, 119–128. [Google Scholar] [CrossRef]
  30. Han, Z.; Choi, C.; Hong, S.; Wu, T.S.; Soo, Y.L.; Jung, Y.; Qiu, J.; Sun, Z. Activated TiO2 with tuned vacancy for efficient electrochemical nitrogen reduction. Appl. Catal. B Environ. 2019, 257, 117896. [Google Scholar] [CrossRef]
  31. Ye, K.; Li, K.; Lu, Y.; Guo, Z.; Ni, N.; Liu, H.; Huang, Y.; Ji, H.; Wang, P. An overview of advanced methods for the characterization of oxygen vacancies in materials. TrAC Trends Anal. Chem. 2019, 116, 102–108. [Google Scholar] [CrossRef]
  32. Chen, M.; Wang, H.; Chen, X.; Wang, F.; Qin, X.; Zhang, C.; He, H. High-performance of Cu-TiO2 for photocatalytic oxidation of formaldehyde under visible light and the mechanism study. Chem. Eng. J. 2020, 390, 124481. [Google Scholar] [CrossRef]
  33. Wang, J.; Li, J.; Jiang, C.; Zhou, P.; Zhang, P.; Yu, J. The effect of manganese vacancy in birnessite-type MnO2 on room-temperature oxidation of formaldehyde in air. Appl. Catal. B Environ. 2017, 204, 147–155. [Google Scholar] [CrossRef]
  34. Miao, L.; Xie, Y.; Xia, Y.; Zou, N.; Wang, J. Facile photo-driven strategy for the regeneration of a hierarchical C@ MnO2 sponge for the removal of indoor toluene. Appl. Surf. Sci. 2019, 481, 404–413. [Google Scholar] [CrossRef]
  35. Fang, R.; Huang, H.; Ji, J.; He, M.; Feng, Q.; Zhan, Y.; Leung, D.Y. Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature. Chem. Eng. J. 2018, 334, 2050–2057. [Google Scholar] [CrossRef]
  36. Wang, J.; Zhang, G.; Zhang, P. Layered birnessite-type MnO2 with surface pits for enhanced catalytic formaldehyde oxidation activity. J. Mater. Chem. A 2017, 5, 5719–5725. [Google Scholar] [CrossRef]
  37. Zhang, C.; Liu, F.; Zhai, Y.; Ariga, H.; Yi, N.; Liu, Y.; Asakura, K.; Flytzani-Stephanopoulos, M.; He, H. Alkali-metal-promoted Pt/TiO2 opens a more efficient pathway to formaldehyde oxidation at ambient temperatures. Angew. Chem. Int. Ed. 2012, 51, 9628–9632. [Google Scholar] [CrossRef]
  38. Wang, Y.; Zhu, X.; Crocker, M.; Chen, B.; Shi, C. A comparative study of the catalytic oxidation of HCHO and CO over Mn0.75Co2.25O4 catalyst: The effect of moisture. Appl. Catal. B Environ. 2014, 160, 542–551. [Google Scholar] [CrossRef]
  39. Scott, S.L. A Matter of Life (Time) and Death; ACS: Washington, DC, USA, 2018; pp. 8597–8599. [Google Scholar]
Molecules 27 05216 g001 550
Figure 1. Schematic diagram of the sample preparation process.
Figure 1. Schematic diagram of the sample preparation process.
Molecules 27 05216 g001
Molecules 27 05216 g002 550
Figure 2. (A) Catalytic performance for HCHO degradation under the UV-Vis-NIR irradiation; (B) catalytic performance of catalyst MS/PDA/MnOx/GCN for HCHO degradation under irradiation with different wavelength ranges; (C) temperature change for catalyst MS/PDA/MnOx/GCN under irradiation with different wavelength ranges.
Figure 2. (A) Catalytic performance for HCHO degradation under the UV-Vis-NIR irradiation; (B) catalytic performance of catalyst MS/PDA/MnOx/GCN for HCHO degradation under irradiation with different wavelength ranges; (C) temperature change for catalyst MS/PDA/MnOx/GCN under irradiation with different wavelength ranges.
Molecules 27 05216 g002
Molecules 27 05216 g003 550
Figure 3. SEM image and EDX mapping of the catalyst MS/PDA/MnOx/GCN.
Figure 3. SEM image and EDX mapping of the catalyst MS/PDA/MnOx/GCN.
Molecules 27 05216 g003
Molecules 27 05216 g004 550
Figure 4. XRD profiles of the catalysts MS/PDA, MS/PDA/MnOx, MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN.
Figure 4. XRD profiles of the catalysts MS/PDA, MS/PDA/MnOx, MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN.
Molecules 27 05216 g004
Molecules 27 05216 g005 550
Figure 5. XPS spectra of the catalysts MS/PDA/MnOx, MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN: (A) Mn 2p; (B) C 1s; (C) O 1s.
Figure 5. XPS spectra of the catalysts MS/PDA/MnOx, MS/PDA/GCN/MnOx and MS/PDA/MnOx/GCN: (A) Mn 2p; (B) C 1s; (C) O 1s.
Molecules 27 05216 g005
Molecules 27 05216 g006 550
Figure 6. PL spectra of TA solution (A) and absorption spectra of NBT solution (B) with the catalysts MS/PDA/MnOx/GCN, MS/PDA/GCN/MnOx and MS/PDA/MnOx under xenon light irradiation.
Figure 6. PL spectra of TA solution (A) and absorption spectra of NBT solution (B) with the catalysts MS/PDA/MnOx/GCN, MS/PDA/GCN/MnOx and MS/PDA/MnOx under xenon light irradiation.
Molecules 27 05216 g006
Molecules 27 05216 g007 550
Figure 7. ESR test for the catalysts MS/PDA/GCN, MS/PDA/MnOx/GCN, MS/PDA/GCN/MnOx and MS/PDA/MnOx.
Figure 7. ESR test for the catalysts MS/PDA/GCN, MS/PDA/MnOx/GCN, MS/PDA/GCN/MnOx and MS/PDA/MnOx.
Molecules 27 05216 g007
Molecules 27 05216 g008 550
Figure 8. In situ DRIFTS of HCHO reaction on the catalyst MS/PDA/MnOx/GCN under xenon light irradiation.
Figure 8. In situ DRIFTS of HCHO reaction on the catalyst MS/PDA/MnOx/GCN under xenon light irradiation.
Molecules 27 05216 g008
Molecules 27 05216 g009 550
Figure 9. Probable degradation mechanism of HCHO over catalyst MS/PDA/MnOx/GCN.
Figure 9. Probable degradation mechanism of HCHO over catalyst MS/PDA/MnOx/GCN.
Molecules 27 05216 g009
Molecules 27 05216 g010 550
Figure 10. Cyclic performance test for HCHO removal.
Figure 10. Cyclic performance test for HCHO removal.
Molecules 27 05216 g010
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Yin, R.; Sun, P.; Cheng, L.; Liu, T.; Zhou, B.; Dong, X. A Three-Dimensional Melamine Sponge Modified with MnOx Mixed Graphitic Carbon Nitride for Photothermal Catalysis of Formaldehyde. Molecules 2022, 27, 5216. https://doi.org/10.3390/molecules27165216

AMA Style

Yin R, Sun P, Cheng L, Liu T, Zhou B, Dong X. A Three-Dimensional Melamine Sponge Modified with MnOx Mixed Graphitic Carbon Nitride for Photothermal Catalysis of Formaldehyde. Molecules. 2022; 27(16):5216. https://doi.org/10.3390/molecules27165216

Chicago/Turabian Style

Yin, Rongyang, Pengfei Sun, Lujun Cheng, Tingting Liu, Baocheng Zhou, and Xiaoping Dong. 2022. "A Three-Dimensional Melamine Sponge Modified with MnOx Mixed Graphitic Carbon Nitride for Photothermal Catalysis of Formaldehyde" Molecules 27, no. 16: 5216. https://doi.org/10.3390/molecules27165216