Proceeding Paper

Facile Microwave-Assisted Preparation of Hetero-Structured CuCo2S4/CuCo2O4 Nanoparticles Using Organic Agent of Thiourea †

Department of Chemistry, Iran University of Science and Technology (IUST), 16846-13114 Tehran, Iran
*
Author to whom correspondence should be addressed.
Presented at the 24th International Electronic Conference on Synthetic Organic Chemistry, 15 November–15 December 2020; Available online: https://ecsoc-24.sciforum.net/.
Chem. Proc. 2021, 3(1), 60; https://doi.org/10.3390/ecsoc-24-08347
Published: 14 November 2020

Abstract

:
Ultra-fast one-put microwave assisted strategy was introduced for the synthesis of hetero-structured CuCo2S4/CuCo2O4 nanoparticles into a domestic microwave oven with the power of 900 W for 20 min. Thiourea as an organic agent was used as a sulfur source and driving agent to lead the solvent free combustion reaction to obtain this earth-abundant and low-cost mixed chalcogenide/oxide product. The structural and morphological specifications were studied in details using powder x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT−IR), scanning electron microscopy (SEM), and energy dispersion of x-ray spectrometry (EDX). The employed strategy relatively clarifies a new facile, rapid, and eco-friendly route to produce heterostructured nanocomposites for different functional purposes.

1. Introduction

Commonly, hetero-structured materials are defined as sandwich-like building blocks of two or more dissimilar layers with different features to create better functions than each component. One of the interesting heterostructures, is the growth of metal oxides in sulfide-based materials such as chalcogenides. Linnaeite compounds with a layered structure and general formula of AB2X4, where X is sulfur (S) or selenium (Se), A is divalent (Fe, Ni, Co, or Cu), and B is trivalent (Co, Ni), are promising candidates in the formation of the heterostructures’ materials. These materials attracted lots of attention after their discovery by the Linnaeite group of the Swedish Carl Linnaeus in 1845, which caused more efforts in identification of more layered transition metal sulfides and also oxides. CuCo2S4 as a member of the carrollite compounds category is a notable material because of having low-cost, nontoxic, abundant, and available constituents [1,2]. On the other hand, metal oxide materials are widely available materials with crystalline structures and different applications in various fields, e.g., electrical/optical industry, redox reactions, catalyst production, agricultural industry, drug delivery/medicine, etc. They have significant properties in terms of efficiency, reactivity, selectivity, and cycle repeatability so that their combination with other materials such as CuCo2S4 can be led to prepare new multifunctional materials.
Various chemical methods were reported to synthesize variety of hetero-structured nanomaterials. The introduction of a simple, inexpensive, high efficiency, and rapid technique is notable to reduce production costs [3,4,5]. Amongst different techniques such as sol-gel, hydrothermal/solvothermal, and precipitation/calcination methods, microwave assisted-method is considered as a facile and rapid strategy to produce nanomaterials. [2,3,4,5,6,7,8]. As a matter of fact, the synthesis of hetero-structured CuCo2S4/CuCo2O4 nanoparticles using the ultra-fast solvent free microwave-assisted procedure has not yet been reported. Thiourea was selected as a suitable sulfur source and also driving agent in process due to its availability, cheapness, and ease of use.

2. Experimental

2.1. Materials and Method

All chemicals were purchased from Merck Co. and used without further purification. Metal sources with stoichiometric ratio in the presence of thiourea were mixed with each other, put into a microwave oven, and treated by microwave irradiation with a power of 900 W for 20 min. The obtained black powder was rinsed with distilled water and absolute ethanol for several times, dried at 70 °C, and then characterized.

2.2. Characterizations

X-ray diffraction (XRD) pattern was recorded by a DRON-8 powder diffractometer using Cu Kα radiation (λ = 1.54060 Å). Fourier transform infrared (FT−IR) spectrum was obtained by a Shimadzu-8400S spectrometer in the range of 400–4000 cm−1 using KBr pellets. Scanning electron microscopy (SEM) images and energy-dispersive x-ray were taken on a VEGA\\TESCAN S360 with gold coating.

3. Result and Discussion

The observed strong peaks at around 500–700 cm−1 in the recorded FT-IR spectrum of the prepared product shown in Figure 1 can be related to the vibration frequencies of Co-O and Co-S and Cu-S bands of CuCo2S4/CuCo2O4 compound. The peaks at 3423 and 2360 cm−1 can be assigned to the vibrations of the adsorbed H2O and CO2 molecules.
Figure 2 exhibits XRD pattern of the prepared product. The appeared peaks at 16.8°, 31.19°, 35.50°, 38.76°, 41.58°, 47.17°, 50.23°, 54.91°, 59.24°, 62.21°, 64.02°, 65.13°, 68.70°, 71.13°, 75.10°, and 77.45°, which are in a good agreement with 111, 220, 311, 222, 004, 331, 422, 333, 440, 531, 620, 533, 622, 444, 711, 642, and 731 planes confirm the formation of cubic carrollite phase of CuCo2S4 (JCPDS card No. 75-1570). The diffraction lines at 2 Theta position of 31.36°, 36.95°, 38.94°, 45.06°, 56.02°, 59.60°, 65.70°, 69.00°, 77.55° are in a close accordance with 220, 311, 222, 400, 422, 511, 440, 531, and 533 are related to cubic planes CuCo2O4 (JCPDS card No. 1-1155), which was formed alongside carrollite phase [6].
The elemental EDX analysis shown in Figure 3 revealed the presence of Cu, Co, and S elements confirming the mentioned XRD data of the formation of layered building blocks of CuCo2S4/CuCo2O4.
SEM images (Figure 4) recorded the resulting product depicted as a spherical particulate morphology with an average particle size of about 40 nm. It was observed that these fine nanoparticles were gathered together and formed a bundle-like texture consisting of particles. It can provide a large surface with more available active sites and efficiently contacts for various targets [7].

4. Conclusions

In a summary, the hetero-structured CuCo2S4/CuCo2O4 nanoparticles were successfully synthesized by a rapid one-put microwave assisted strategy. This in situ treatment easily produced a suitable medium for the formation of heterostructure nanomaterial with a layered architecture. In fact, the microwave irradiation in the presence of proper chemicals created efficient interactions between reactants in solid state to reach this target. In addition, this procedure was carried out in a solid state without using any organic solvent, which can nominate it as an environment friendly method to prepare various nanomaterials.

Institutional Review Board Statement

This study did not involve humans or animals.

Informed Consent Statement

Not applicable.

Data Availability Statement

The necessary data has been given and this study does not report more data.

Acknowledgments

The financial support from IUST is gratefully acknowledged.

References

  1. Clark, A.H. Hypogene and supergene cobalt-copper sulfides, Carrizal Alto, Atacama, Chile. Am. Mineral. J. Earth Planet. Mater. 1974, 59, 302–306. [Google Scholar]
  2. Li, L.; Xu, J.; Ma, J.; Liu, Z.; Li, Y. A bimetallic sulfide CuCo2S4 with good synergistic effect was constructed to drive high performance photocatalytic hydrogen evolution. J. Colloid Interface Sci. 2019, 552, 17–26. [Google Scholar] [CrossRef] [PubMed]
  3. Zhu, Y.; Chen, X.; Zhou, W.; Xiang, K.; Hu, W.; Chen, H. Controllable preparation of highly uniform CuCo2S4 materials as battery electrode for energy storage with enhanced electrochemical performances. Electrochim. Acta 2017, 249, 64–71. [Google Scholar] [CrossRef]
  4. Fan, L.Q.; Pan, F.; Tu, Q.M.; Gu, Y.; Huang, J.L.; Huang, Y.F.; Wu, J.H. Synthesis of CuCo2S4 nanosheet arrays on Ni foam as binder-free electrode for asymmetric supercapacitor. Int. J. Hydrogen Energy 2018, 43, 23372–23381. [Google Scholar] [CrossRef]
  5. Wang, F.; Zheng, J.; Li, G.; Ma, J.; Yang, C.; Wang, Q. Microwave synthesis of mesoporous CuCo2S4 nanoparticles for supercapacitor applications. Mater. Chem. Phys. 2018, 215, 121–126. [Google Scholar] [CrossRef]
  6. Yang, Z.; Zhang, S.; Fu, Y.; Zheng, X.; Zheng, J. Shape-controlled synthesis of CuCo2S4 as highly-efficient electrocatalyst for nonenzymatic detection of H2O2. Electrochim. Acta 2017, 255, 23–30. [Google Scholar] [CrossRef]
  7. Zequine, C.; Bhoyate, S.; Wang, F.; Li, X.; Siam, K.; Kahol, P.K.; Gupta, R.K. Effect of solvent for tailoring the nanomorphology of multinary CuCo2S4 for overall water splitting and energy storage. J. Alloys Compd. 2019, 784, 1–7. [Google Scholar] [CrossRef]
  8. Miao, F.; Li, X.; Tao, B.; Chu, P.K. Heterostructured Co(OH)2 nanosheet-coated CuCo2S4 nanopencils on nickel foam for electrodes in high-performance supercapacitors. Ionics 2020, 26, 5241–5249. [Google Scholar] [CrossRef]
Figure 1. FT−IR spectrum of the synthesized nanoparticles.
Figure 1. FT−IR spectrum of the synthesized nanoparticles.
Chemproc 03 00060 g001
Figure 2. XRD pattern of the prepared CuCo2S4/CuCo2O4 nanoparticles.
Figure 2. XRD pattern of the prepared CuCo2S4/CuCo2O4 nanoparticles.
Chemproc 03 00060 g002
Figure 3. EDX analysis of the prepared product.
Figure 3. EDX analysis of the prepared product.
Chemproc 03 00060 g003
Figure 4. SEM images of resulting CuCo2S4/CuCo2O4 heterostructure.
Figure 4. SEM images of resulting CuCo2S4/CuCo2O4 heterostructure.
Chemproc 03 00060 g004
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Bahmani, M.; Imani, M.; Tadjarodi, A. Facile Microwave-Assisted Preparation of Hetero-Structured CuCo2S4/CuCo2O4 Nanoparticles Using Organic Agent of Thiourea. Chem. Proc. 2021, 3, 60. https://doi.org/10.3390/ecsoc-24-08347

AMA Style

Bahmani M, Imani M, Tadjarodi A. Facile Microwave-Assisted Preparation of Hetero-Structured CuCo2S4/CuCo2O4 Nanoparticles Using Organic Agent of Thiourea. Chemistry Proceedings. 2021; 3(1):60. https://doi.org/10.3390/ecsoc-24-08347

Chicago/Turabian Style

Bahmani, Mahdi, Mina Imani, and Azadeh Tadjarodi. 2021. "Facile Microwave-Assisted Preparation of Hetero-Structured CuCo2S4/CuCo2O4 Nanoparticles Using Organic Agent of Thiourea" Chemistry Proceedings 3, no. 1: 60. https://doi.org/10.3390/ecsoc-24-08347