Article

Temperature Detectable Surface Coating with Carbon Nanotube/Epoxy Composites

1
Department of Civil and Environmental Engineering, Hanyang University, Seoul 04763, Korea
2
Department of Smart City Engineering, Hanyang University ERICA, Ansan 15588, Korea
3
Department of Civil and Environmental Engineering and Construction, The University of Nevada, Las Vegas, NV 89154, USA
4
Department of Civil and Environmental Engineering, Hanyang University ERICA, Ansan 15588, Korea
*
Authors to whom correspondence should be addressed.
Nanomaterials 2022, 12(14), 2369; https://doi.org/10.3390/nano12142369
Submission received: 5 June 2022 / Revised: 4 July 2022 / Accepted: 7 July 2022 / Published: 11 July 2022
(This article belongs to the Topic Advanced Nanomaterials for Sensing Applications)

Abstract

:
In the construction and machinery industry, heat is a major factor causing damage and destruction. The safety and efficiency of most machines and structures are greatly affected by temperature, and temperature management and control are essential. In this study, a carbon nanotube (CNT) based temperature sensing coating that can be applied to machines and structures having various structural types was fabricated, and characteristics analysis and temperature sensing performance were evaluated. The surface coating, which detects temperature through resistance change is made of a nanocomposite composed of carbon nanotubes (CNT) and epoxy (EP). We investigated the electrical properties by CNT concentration and temperature sensing performance of CNT/EP coating against static and cyclic temperatures. In addition, the applicability of the CNT/EP coating was investigated through a partially heating and cooling experiment. As a result of the experiment, the CNT/EP coating showed higher electrical conductivity as the CNT concentration increased. In addition, the CNT/EP coating exhibits high sensing performance in the high and sub−zero temperature ranges with a negative temperature coefficient of resistance. Therefore, the proposed CNT/EP coatings are promising for use as multi-functional coating materials for the detection of high and freezing temperatures.

1. Introduction

Temperature is a key parameter for most industries, and temperature sensors account for a large part of the overall sensor market [1]. In addition, according to industrial development, a temperature sensor is required with capable of responding to complex structures and various environments. However, in the case of conventional temperature sensor materials such as silicon diodes and platinum, heat loss occurs when there is not enough thermal energy, resulting in poor precision or slow response. It is also difficult to cope with large areas. In order to compensate for the shortcomings of the conventional temperature sensors, research on new materials or composites is being actively conducted.
Carbon nanotubes (CNT) are widely used as a functional filler, and carbon nanotube composites are utilized in various industrial fields. The structural morphology of CNT can be used as a composite mixed with different materials to impart electrical and thermal conductivity and/or mechanical properties [2,3,4]. In particular, the dispersion of these kinds of nanoparticles in polymeric systems allows to improve thermal stability, photooxidation resistance, and mechanical properties and simultaneously provides the means to make the resulting nanocomposite able to manifest functional properties [5,6].
The effect of temperature on CNT reinforced composites has been studied for different filler-resin composites. Gojny and Schulte [7] investigated the effect of multi-walled CNTs on the thermo-mechanical properties of multi-wall carbon nanotubes (MWCNTs)/epoxy composites and found that increasing concentrations of MWCNTs as well as functionalizing MWCNTs leads to an increase of the glass transition temperature with higher interfacial interaction between the CNT and the polymer matrix. For example, Jang and Yin [8,9] fabricated highly sensitive strain and fracture sensors by dispersing carbon nanotubes as well as ferromagnetic particles in polydimethylsiloxane (PDMS). In addition to sensing applications, other capabilities have been reported for a decade. Jang and Park [10] proposed carbon nanotube-reinforced composite materials for dual functions such as temperature sensing and de-icing. Yum and Jang [11] proposed multi-functional road coating materials with self-sensing consisting of CNTs and a polyurethane (PU) matrix, widely used materials for road marking, for future transportation systems.
Among the various polymer systems, commonly used epoxy resins belong to structurally suitable polymer systems [12,13,14]. These resins have excellent stiffness, strength, dimensional stability, chemical resistance, and durability, making them useful for a wide variety of industrial applications, particularly in the electronics, automotive, and aerospace industries [15,16]. Alamusi et al. [17] investigated the temperature dependence of CNT/epoxy resin composites resistance. Wenlong Wang et al. [18] investigated the correlation of the strain variation in CNT/epoxy resin composites with temperature using Raman spectroscopy.
In this study, a novel temperature-sensing coating composed of carbon nanotube and epoxy (EP) matrices applicable to various industrial fields was proposed. The CNT/EP coating material is manufactured by the solution casting method for high electrical conductivity. We then investigated the electrical conductivity of the CNT/EP coatings as a function of CNT concentration. The temperature sensing accuracy, sensing speed, and repeatability of the proposed CNT/EP coating were investigated through resistance measurement experiments for static and cyclic temperatures. In addition, applicability was evaluated by measuring the response of the CNT/EP coating to freezing and high temperature.

2. Experimental

2.1. Materials

Industrial-grade multi-walled carbon nanotubes were purchased from Nanolab, Inc. (Waltham, MA, USA). The CNTs have a diameter of 15 ± 5 nm, a length of 5–20 µm, and purity of higher than 85 wt.% including impurities such as iron and ceramic oxides. Epoxy was obtained from Easy Composites Ltd. (EpoxAcast 690, Staffordshire, UK) with a density of 1.12–1.18 g/cm3 and viscosity of 200–450 mPa∙s. The dispersant used acetone from Samchun pure chemical Co., Ltd. (Gyeonggi-do, Korea) with a purity of 99.7%.

2.2. Fabrication Procedure

Various fabrication methods according to matrix materials are being studied for the carbon nanotube-based composites [19,20]. In this study, the CNT/EP coating was fabricated based on the previous study [8,9,10,20]. The fabrication procedure of CNT/EP coatings was shown in Figure 1. 20 g of epoxy resin and 50 g of acetone were added to a 200 mL beaker and hand-mixed using a spatula. Then, various concentrations of CNTs (0–5 wt.%) were put into a beaker and mixed in the same way. An ultrasonicator (Q700CA, Qsonica LLC., Newtown, CT, USA) was applied to disperse CNTs in the solution. In this study, the ultrasonicator was operated in a pulsed mode with 90% amplitude for 30 min. Ice was placed around the beaker to prevent the evaporation of acetone. After dispersion, the sample was placed on a hot plate at 60 °C for 24 h to fully evaporate acetone. Then, 6 g of curing agent was added into the sample and was mixed evenly in a 3-roll mill (TR 50M, Trilos, San Ramon, CA, USA). After molding, the sample was placed into the vacuum chamber and operated for 30 min to remove air bubbles inside the sample. Finally, the CNT/EP coating was baked in hot oven at 60 °C.

2.3. Characterization

The resistance of the CNT/EP coatings was measured using a Keithley 2450 (Tektronix, Beaverton, OR, USA) for a high resistance above 109 Ω and Keithley 2700 (Tektronix, Beaverton, OR, USA) for normal resistance. The electrical resistance was evaluated from the current-voltage curves obtained by applying voltages between −10 V and +10 V. The specimens were prepared with a size of 50 mm × 30 mm × 1 mm. High-purity silver paint was applied to both ends of the specimens to minimize the contact resistance between the coating and the tip probe. The electrical conductivity (σ) of the specimens was calculated by
σ = L/RA
where R is the resistance of the coating (Ω), A is the area of the coating (m2) and L is the length of the coating (m).
For the microstructure of the CNT/EP coatings, the cross-section of the specimen was observed through a scanning electron microscope (MIRA3 FE-SEMs, TESCAN, Brno, Czech Republic) at 15 kV. For a high magnification measurement of more than 10,000 times, the CNT/EP coating cross-section was coated with platinum using sputter coating (QUORUM−Q150T S, Laughton, UK) for 10 min.
For resistance-temperature dependence in CNT/EP coatings, the change in resistance of CNT/EP coatings as a function of temperature was measured in an environmental chamber using a digital multimeter (Keithley 2700, Tektronix, Beaverton, OR, USA) with an externally connected data acquisition system, as shown in Figure 2a. The resistance of CNT/EP coatings was measured from −20 °C to 60 °C in 10 degree increments. Note that the samples remain constant at each temperature for 1 h for the steady-state temperature of the CNT/EP coatings. For cyclic piezoresistive response of CNT/EP coatings, the test exposed the samples repeatedly to sub-zero temperature ranges of −20 °C and +20 °C, where atmospheric phase changes can occur. The temperature change will cycle 50 times throughout the test with an hour dwell at each level.
For multi-sensing application, CNT/EP coating (5.0 wt.%) was painted on a polyethylene terephthalate (PET) substrate with a size of 150 mm × 150 mm × 10.0 mm. Total of 16 sensors were prepared using a silver paint and copper tape, as shown in Figure 2b. Heat source was applied to a side of PET substrate. The resistance of 16 sensors was collected using a digital multimeter.

3. Results and Discussion

3.1. Electrical Conductivity of CNT/EP Coating

Figure 3 showed the electrical characteristics of the CNT/EP coatings. Figure 3a showed the current–voltage curves. It can be seen that negative and positive voltage sections of the current–voltage curve are symmetrical and have linear relationships with each other. This indicates the good ohmic behavior of the CNT/EP coatings. Figure 3b showed the electrical conductivity for the CNT/EP coating as a function of CNT concentrations. Pure epoxy was non-conductive material with 1 × 10−14 S/m. A dramatic increase in electrical conductivity was observed when the concentration of CNTs increased from 0.25 wt.% to 1.0 wt.%. This behavior has been attributed to the occurrence of a percolation threshold [21,22,23,24]. In this study the percolation threshold, i.e., the minimum CNT concentration in the matrix after which no significant change in the electrical conductivity is observed, occurred at around 0.63 wt.% CNTs. Then, the electrical conductivity showed a slight increase even with an increase in the CNT concentrations. The observed increase in electrical conductivity of the CNT/EP coating is due to a well-dispersed CNT into the epoxy matrix as shown in Figure 3c. The effectiveness of electron transfer between the CNTs is very highly dependent on these CNTs’ spacing distance. CNT/EP Coating does not reach the improved percolation network formation of multi-wall carbon nanotubes but exhibits excellent electrical conductivity [25].
Figure 4 showed an SEM image of a cross-section of the CNT/EP coating with electrical conductivity. Densely packed CNT networks were clearly observed inside the sample. The electrical conductivity of the sample at the surface was about 1 × 10−14 S/m, whereas the electrical conductivity of the sample inside the surface was about 1 × 10−1 S/m. Because the major electron transport pathways are mostly internal of the sample, the charge flow in the CNT/EP coating can operate more reliably against surface damage.

3.2. Sensing Performance of CNT/EP Coating for Static and Cyclic Temperature

Figure 5 showed the effect of temperature on the resistance of the CNT/EP coatings. As shown in Figure 5a, the resistance of all CNT/EP coatings gradually decreased with the increasing temperature, demonstrating that CNT/EP coatings have a negative temperature coefficient of resistance (TCR). This phenomenon can be attributed to the thermal activation of charge carriers due to the increase in temperature, which overcomes the potential barrier between CNTs and reduces the resistance of the nanocomposite [26,27,28]. Figure 5b presented the normalized resistance relative to room temperature of the CNT/EP coatings. In this study, the resistance of all CNT/EP coatings varied linearly with temperature except for 0.63 wt.% CNT/EP coating due to its high sensitivity. Figure 5c showed the TCR of CNT/EP coatings. TCR can be calculated by:
TCR = R     R ref   R ref T     T ref
where, T is the coating temperature in degrees Celsius (°C), Tref is reference temperature (20 °C), R is the resistance at temperature T (Ω), and Rref is resistance at temperature Tref (Ω). It was observed that absolute TCR of CNT/EP coatings decreased with increasing CNT concentrations, and the difference was smaller at high concentrations [17,29]. In this study, TCR values of the CNT/EP coatings are around −0.07%/°C, which is slightly lower than that of the pure carbon sample −0.2%/°C [30,31,32]. Note that the behavior is similar value over the entire measured temperature range. In Table 1, we compared the TCR values obtained from the present study against other temperature sensors. This comparison confirms that the resistances of the CNT/EP coating were measured as functions of temperature [33,34,35,36,37,38].
Repeatability is one of the major factors required for long-term stable use of temperature sensors. Figure 6a showed the cyclic piezoresistive response of CNT/EP coatings at different temperatures. It was observed that a drift occurs for both CNT/EP coatings as increasing temperature cycles. A similar phenomenon was reported in previous literatures [39,40]. Some CNTs with weak adhesion may be separated due to the mismatch of the coefficient of thermal expansion during the temperature cycle iteration [41]. Figure 6b presented the drift factor of all CNT/EP coatings. A drift factor can be calculated by
Drift   factor = R n   R 0   R 0 × 100
where Rn is the resistance of nth sensing cycle (Ω), and R0 is the resistance of initial temperature cycle (Ω). Drift significantly reduced with increasing CNT concentrations. For example, the drift factor of the 5.00 wt.% coating is only 0.2% and showed constant repetition. This consistent resistance change demonstrates the long-term and repeatable use of CNT/EP coatings. Figure 6c showed the cyclic piezoresistive response of CNT/EP coating (5.0 wt.%) for 50 temperature cycles. The resistance of the CNT/EP coating was quickly varied with the cyclic temperature change. The proposed coating can clearly monitor the temperature with high stability.

3.3. Application of Temperature Sensing System

To demonstrate the feasibility of the temperature sensor, we placed CNT/EP coating on polyethylene terephthalate (PET) substrate to install a temperature sensor array for simulating temperature distribution. The heat source was applied to a corner of CNT/EP coatings to show heat distribution for the sensor array, as shown in Figure 7a and Figure 8a. Also, an infrared thermal camera was used to monitor heat distribution for CNT/EP coating (Figure 7b and Figure 8b). Before applying the heat source, each sensor maintained its initial resistance. After the heat source applies to a corner of CNT/EP coating, the resistance of sensors near the heat source dramatically changes with time, as shown in Figure 7c and Figure 8c. As a result of measuring resistance according to heat source, the resistance near the heat source part was significantly increased or reduced with time. The normalized resistance near the heat source part changed with the temperature, but there is little change in the other part. In particular, the resistance of sensors prominently changed in the heat source area, as shown in Figure 7d and Figure 8d. Temperature sensing can be possible through the resistance according to partial temperature change of the coating, which means that the CNT/EP coating can function as a temperature sensor and respond to various fields.

4. Conclusions

This study investigated the characteristics of CNT/EP coatings as a temperature sensor. Highly electrically conductive coatings have been successfully prepared by dispersing CNTs in an epoxy matrix. The addition of CNTs showed improved electrical conductivity. Static temperature sensing experiments confirmed that the proposed coating provided temperature sensing due to its negative temperature coefficient and can clearly monitor the temperature with high stability. Through the cyclic temperature experiment, it was confirmed that the drift of the CNT/EP coating occurred as the number of repetitions increased, which was alleviated as the CNT concentration increased. As a result, CNT/EP coatings with higher CNT concentrations are more suitable for temperature monitoring. In addition, the potential as a temperature sensor was confirmed through the partial temperature change experiment of the CNT/EP coating. Therefore, CNT/EP coating may enable potential applications to temperature sensors and sensor-integrated materials.

Author Contributions

Conceptualization, S.-H.J.; methodology, S.-H.J.; formal analysis, S.-H.J. and J.P.; investigation, S.-H.J.; writing—original draft preparation, S.-J.L.; writing—review and editing, S.-H.J. and J.P.; visualization, S.-J.L. and Y.-J.J.; supervision, S.-H.J.; project administration, S.-H.J.; funding acquisition, S.-H.J. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Technology Innovation Program (20014127, Development of a smart monitoring system integrating 3D printed battery-free antenna sensor technology with AI optimization) funded by the Ministry of Trade, Industry & Energy (MOTIE, Korea) and the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT) (NRF−2020R1C1C1005273).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

This work was supported by the Technology Innovation Program (20014127, Development of a smart monitoring system integrating 3D printed battery-free antenna sensor technology with AI optimization) funded By the Ministry of Trade, Industry & Energy (MOTIE, Korea) and the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT) (NRF−2020R1C1C1005273).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Webb, C. Infrared: Faster; smaller; cheaper. Control Instrum. 1997, 29, 44–45. [Google Scholar]
  2. Kong, L.; Chen, W. Carbon nanotube and graphene-based bioinspired electrochemical actuators. Adv. Mater. 2014, 26, 1025–1043. [Google Scholar] [CrossRef] [PubMed]
  3. Guadagno, L.; De Vivo, B.; Di Bartolomeo, A.; Lamberti, P.D.; Sorrentino, A.; Tucci, V.; Vertuccio, L.; Vittoria, V. Effect of functionalization on the thermo-mechanical and electrical behavior of multi-wall carbon nanotube/epoxy composites. Carbon 2011, 49, 1919–1930. [Google Scholar] [CrossRef]
  4. Bauhofer, W.; Kovacs, J.Z. A review and analysis of electrical percolation in carbon nanotube polymer composites. Compos. Sci. Technol. 2009, 69, 1486–1498. [Google Scholar] [CrossRef]
  5. Guadagno, L.; Vertuccio, L.; Naddeo, C.; Calabrese, E.; Barra, G.; Raimondo, M.; Sorrentino, A.; Binder, W.H.; Michael, P.; Rana, S. Reversible self-healing carbon-based nanocomposites for structural applications. Polymers 2019, 11, 903. [Google Scholar] [CrossRef] [Green Version]
  6. El Assami, Y.; Habti, M.D.; Raman, V. Stiffening offshore composite wind-blades bonding joints by carbon nanotubes reinforced resin–a new concept. J. Struct. Integr. Maint. 2020, 5, 87–103. [Google Scholar] [CrossRef]
  7. Florian, H.G.; Schulte, K. Functionalisation effect on the thermo-mechanical behaviour of multi-wall carbon nanotube/epoxy-composites. Compos. Sci. Technol. 2004, 64, 2303–2308. [Google Scholar]
  8. Jang, S.; Yin, H. Characterization and modeling of the effective electrical conductivity of a carbon nanotube/polymer composite containing chain-structured ferromagnetic particles. J. Compos. Mater. 2017, 51, 171–178. [Google Scholar] [CrossRef]
  9. Jang, S.; Yin, H. Effect of aligned ferromagnetic particles on strain sensitivity of multi-walled carbon nanotube/polydimethylsiloxane sensors. Appl. Phys. Lett. 2015, 106, 141903. [Google Scholar] [CrossRef] [Green Version]
  10. Jang, S.; Park, Y. Carbon nanotube-reinforced smart composites for sensing freezing temperature and deicing by self-heating. Nanomater. Nanotechnol. 2018, 8, 1847980418776473. [Google Scholar] [CrossRef] [Green Version]
  11. Yum, S.; Yin, H.; Jang, S. Toward multi-functional road surface design with the nanocomposite coating of carbon nanotube modified polyurethane: Lab-scale experiments. Nanomaterials 2020, 10, 1905. [Google Scholar] [CrossRef] [PubMed]
  12. Jang, S.; Kim, D.; Park, Y. Accelerated curing and enhanced material properties of conductive polymer nanocomposites by joule heating. Materials 2018, 11, 1775. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  13. Kim, J.-K.; May, Y.-W. Engineered Interfaces in Fiber Reinforced Composites; Elsevier: Amsterdam, The Netherlands, 1998. [Google Scholar]
  14. Vertuccioa, L.; Guadagnoa, L.; Spinellib, G.; Lambertib, P.; Zarrellic, M.; Russod, S.; Iannuzzod, G. Smart coatings of epoxy based CNTs designed to meet practical expectations in aeronautics. Compos. Part B Eng. 2018, 147, 42–46. [Google Scholar] [CrossRef]
  15. Ayesha, K.; Rafique, I.; Muhammad, B. Aerospace application of polymer nanocomposite with carbon nanotube, graphite, graphene oxide, and nanoclay. Polym.-Plast. Technol. Eng. 2017, 56, 1438–1456. [Google Scholar]
  16. Jin, F.; Li, X.; Park, S. Synthesis and application of epoxy resins: A review. J. Ind. Eng. Chem. 2015, 29, 1–11. [Google Scholar] [CrossRef]
  17. Li, Y.; Hu, N.; Wu, L.; Yuan, W.; Peng, X.; Gu, B.; Chang, C.; Liu, Y.; Ning, H.; Li, J.; et al. Temperature-dependent piezoresistivity in an MWCNT/epoxy nanocomposite temperature sensor with ultrahigh performance. Nanotechnology 2013, 24, 455501. [Google Scholar] [CrossRef]
  18. Wang, W.; Wang, C.; Yue, X.; Zhang, C.; Zhou, C.; Wu, W.; Zhu, H. Raman spectroscopy and resistance-temperature studies of functionalized multiwalled carbon nanotubes/epoxy resin composite film. Microelectron. Eng. 2019, 214, 50–54. [Google Scholar] [CrossRef]
  19. Demidenko, N.A.; Kuksin, A.V.; Molodykh, V.V.; Pyankov, E.S.; Ichkitidze, L.P.; Zaborova, V.A.; Tsymbal, A.A.; Tkachenko, S.A.; Shafaei, H.; Diachkova, E.; et al. Flexible Strain-Sensitive Silicone-CNT Sensor for Human Motion Detection. Bioengineering 2022, 9, 36. [Google Scholar] [CrossRef]
  20. Jang, S.; Yin, H. Effective electrical conductivity of carbon nanotube-polymer composites: A simplified model and its validation. Mater. Res. Express 2015, 2, 045602. [Google Scholar] [CrossRef]
  21. Krause, B.; Potschke, P.; Ilin, E.; Predtechenskiy, M. Melt mixed SWCNT-polypropylene composites with very low electrical percolation. Polymer 2016, 98, 45–50. [Google Scholar] [CrossRef]
  22. Lea, H.; Hecht, D.S.; Grüner, G. Percolation in transparent and conducting carbon nanotube networks. Nano Lett. 2004, 4, 2513–2517. [Google Scholar]
  23. Jang, S.; Li, L. Self-sensing carbon nanotube composites exposed to glass transition temperature. Materials 2020, 13, 259. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  24. Gong, S.; Wang, Y.; Xiao, Z.; Li, Z.; Wang, Z.X.; Lei, R.S.; Zhu, Z.H. Effect of temperature on the electrical property of epoxy composites with carbon nanotube. Compos. Sci. Technol. 2017, 149, 48–54. [Google Scholar] [CrossRef]
  25. Gerasimenko, A.Y.; Kuksin, A.V.; Shaman, Y.P.; Kitsyuk, E.P.; Fedorova, Y.O.; Sysa, A.V.; Pavlov, A.A.; Glukhova, O.E. Electrically conductive networks from hybrids of carbon nanotubes and graphene created by laser radiation. Nanomaterials 2022, 11, 1875. [Google Scholar] [CrossRef]
  26. Sanli, A.; Benchirouf, A.; Müller, C.; Kanoun, O. Piezoresistive performance characterization of strain sensitive multi-walled carbon nanotube-epoxy nanocomposites. Sens. Actuators Phys. 2017, 254, 61–68. [Google Scholar] [CrossRef]
  27. Mohiuddin, M.; van Hoa, S. Electrical resistance of CNT-PEEK composites under compression at different temperatures. Nanoscale Res. Lett. 2011, 6, 1–5. [Google Scholar] [CrossRef] [Green Version]
  28. Li, Q.; Xue, Q.Z.; Gao, X.L.; Zheng, Q.B. Temperature dependence of the electrical properties of the carbon nanotube/polymer composites. Express Polym. Lett. 2009, 3, 769–777. [Google Scholar] [CrossRef]
  29. Li, Q.; Luo, S.; Wang, Y.; Wang, Q. Carbon based polyimide nanocomposites thin film strain sensors fabricated by ink-jet printing method. Sens. Actuators A Phys. 2019, 300, 111664. [Google Scholar] [CrossRef]
  30. Itkis, M.E.; Borondics, F.; Yu, A.P.; Haddon, R.C. Bolometric infrared photoresponse of suspended single−walled carbon nanotube films. Science 2006, 312, 413–416. [Google Scholar] [CrossRef] [Green Version]
  31. Lu, R.T.; Li, Z.Z.; Xu, G.W.; Wu, J.Z. Suspending single−wall carbon nanotube thin film infrared bolometers on microchannels. Appl. Phys. Lett. 2009, 94, 163110. [Google Scholar] [CrossRef]
  32. Aliev, A.E. Bolometric detector on the basis of single-wall carbon nanotube/polymer composite. Infrared Phys. Technol. 2008, 51, 541–545. [Google Scholar] [CrossRef]
  33. Zhao, B.; Sivasankar, V.S.; Dasgupta, A.; Das, S. Ultrathin and ultrasensitive printed carbon nanotube-based temperature sensors capable of repeated uses on surfaces of widely varying curvatures and wettabilities. ACS Appl. Mater. Interfaces 2021, 13, 10257–10270. [Google Scholar] [CrossRef] [PubMed]
  34. Wu, L.; Qian, J.; Peng, J.; Wang, K.; Liu, Z.; Ma, T.; Zhou, Y.; Wang, G.; Ye, S. Screen-Printed Flexible Temperature Sensor Based on FG/CNT/PDMS Composite with Constant TCR. J. Mater. Sci. Mater. Electron. 2019, 30, 9593–9601. [Google Scholar] [CrossRef]
  35. Karimov, K.S.; Chani, M.T.S.; Khalid, F.A. Carbon nanotubes film based temperature sensors. Phys. E Low-Dimens. Syst. Nanostruct. 2011, 43, 1701–1703. [Google Scholar] [CrossRef]
  36. Dinh, T.; Phan, H.; Nguyen, T.; Qamar, A.; Foisal, A.R.M.; Viet, T.N.; Tran, C.; Zhu, Y.; Nguyen, N.; Dao, D.V. Environment-friendly carbon nanotube based flexible electronics for noninvasive and wearable healthcare. J. Mater. Chem. C 2016, 4, 10061–10068. [Google Scholar] [CrossRef]
  37. Cagatay, E.; Falco, A.; Abdellah, A.; Lugli, P. Carbon nanotube based temperature sensors fabricated by large-scale spray deposition. In Proceedings of the 2014 10th Conference on Ph. D. Research in Microelectronics and Electronics (PRIME), IEEE, Grenoble, France, 1–4 July 2014. [Google Scholar]
  38. Arai, F.; Ng, C.; Liu, P.; Dong, L.; Imaizumi, Y.; Maeda, K.; Maruyama, H.; Ichikawa, A.; Fukuda, T. Ultra-small site temperature sensing by carbon nanotube thermal probes. In Proceedings of the 4th IEEE Conference on Nanotechnology, IEEE, Munich, Germany, 16–19 August 2004; pp. 146–148. [Google Scholar]
  39. Blasdel, N.J.; Wujcik, E.K.; Carletta, J.E.; Lee, K.S.; Monty, C.N. Fabric nanocomposite resistance temperature detector. IEEE Sens. J. 2015, 15, 300–306. [Google Scholar] [CrossRef]
  40. De Volder, M.; Reynaerts, D.; Van Ho, C.; Tawfick, S.; Hart, A.J. A Temperature Sensor from a Self-Assembled Carbon Nanotube Microbridge. In Proceedings of the 9th IEEE Conference on Sensors 2010, Kona, HI, USA, 1–4 November 2010; pp. 2369–2372. [Google Scholar]
  41. Fung, C.K.M.; Wong, V.T.S.; Chan, R.H.M.; Li, W.J. Dielectrophoretic Batch Fabrication of Bundled Carbon Nanotube Thermal Sensors. IEEE Trans. Nanotechnol. 2004, 3, 395–403. [Google Scholar] [CrossRef]
Figure 1. Fabrication of CNT/EP coating.
Figure 1. Fabrication of CNT/EP coating.
Nanomaterials 12 02369 g001
Figure 2. Temperature sensing performance equipment and details: (a) static and cycle sensing test; (b) multi-sensing test.
Figure 2. Temperature sensing performance equipment and details: (a) static and cycle sensing test; (b) multi-sensing test.
Nanomaterials 12 02369 g002
Figure 3. Electrical characteristics of CNT/EP coating; (a) current−voltage curves; (b) electrical conductivity; (c) SEM image.
Figure 3. Electrical characteristics of CNT/EP coating; (a) current−voltage curves; (b) electrical conductivity; (c) SEM image.
Nanomaterials 12 02369 g003aNanomaterials 12 02369 g003b
Figure 4. SEM image of a cross-section of the CNT/EP coating with electrical conductivity.
Figure 4. SEM image of a cross-section of the CNT/EP coating with electrical conductivity.
Nanomaterials 12 02369 g004
Figure 5. Temperature sensing characteristics of CNT/EP coating; (a) electrical resistance; (b) normalized resistance; (c) TCR.
Figure 5. Temperature sensing characteristics of CNT/EP coating; (a) electrical resistance; (b) normalized resistance; (c) TCR.
Nanomaterials 12 02369 g005
Figure 6. Cyclic temperature sensing performance of the CNT/EP coatings; (a) normalized resistance (1.25 wt.%, 5.00 wt.%); (b) drift factor; (c) sensing performance (5.00 wt.%).
Figure 6. Cyclic temperature sensing performance of the CNT/EP coatings; (a) normalized resistance (1.25 wt.%, 5.00 wt.%); (b) drift factor; (c) sensing performance (5.00 wt.%).
Nanomaterials 12 02369 g006
Figure 7. Resistance of CNT/EP coating according to partially heating; (a) measured points and applied area; (b) infrared thermal image; (c) normalized resistance; (d) normalized resistance at t0, t1, t2.
Figure 7. Resistance of CNT/EP coating according to partially heating; (a) measured points and applied area; (b) infrared thermal image; (c) normalized resistance; (d) normalized resistance at t0, t1, t2.
Nanomaterials 12 02369 g007
Figure 8. Resistance of CNT/EP coating according to partially cooling; (a) measured points and applied area; (b) infrared thermal image; (c) normalized resistance; (d) normalized resistance at t0, t1, t2.
Figure 8. Resistance of CNT/EP coating according to partially cooling; (a) measured points and applied area; (b) infrared thermal image; (c) normalized resistance; (d) normalized resistance at t0, t1, t2.
Nanomaterials 12 02369 g008
Table 1. Comparison of the TCR between our case and other types of temperature sensors.
Table 1. Comparison of the TCR between our case and other types of temperature sensors.
ReferenceMaterial|TCR| (10−3/°C)Measured Temperature Range (°C)
In this paper
(Maximum)
CNT/epoxy0.7−20 to 60
[33]CNT-GO~605–50, 25–70
[34]CNT/PDMS; CNT/FG/PDMS; 1.5–2.8
~28
40–80
[35]MWCNT2.4–2.720–75
[36]CNT yarn (without solvent)~0.7525–80
[37]SWNT-CMC~30–100
[38]CNT deposited on ITO electrodes~0.425–90
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Lee, S.-J.; Jung, Y.-J.; Park, J.; Jang, S.-H. Temperature Detectable Surface Coating with Carbon Nanotube/Epoxy Composites. Nanomaterials 2022, 12, 2369. https://doi.org/10.3390/nano12142369

AMA Style

Lee S-J, Jung Y-J, Park J, Jang S-H. Temperature Detectable Surface Coating with Carbon Nanotube/Epoxy Composites. Nanomaterials. 2022; 12(14):2369. https://doi.org/10.3390/nano12142369

Chicago/Turabian Style

Lee, Seung-Jun, Yu-Jin Jung, JeeWoong Park, and Sung-Hwan Jang. 2022. "Temperature Detectable Surface Coating with Carbon Nanotube/Epoxy Composites" Nanomaterials 12, no. 14: 2369. https://doi.org/10.3390/nano12142369

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop