A Novel Method to Prepare Transparent, Flexible and Thermally Conductive Polyethylene/Boron Nitride Films
Next Article in Special Issue
Enhanced Spontaneous Emission of CsPbI3 Perovskite Nanocrystals Using a Hyperbolic Metamaterial Modified by Dielectric Nanoantenna
Previous Article in Journal
Recent Progress in Two-Dimensional MoTe2 Hetero-Phase Homojunctions
Previous Article in Special Issue
On the Shape-Selected, Ligand-Free Preparation of Hybrid Perovskite (CH3NH3PbBr3) Microcrystals and Their Suitability as Model-System for Single-Crystal Studies of Optoelectronic Properties
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 1
10.3390/nano12010112
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Efficient and Stable Perovskite Solar Cells Based on Inorganic Hole Transport Materials

by
Helen Hejin Park
Advanced Materials Division, Korea Research Institute of Chemical Technology (KRICT), Daejeon 34114, Korea
Nanomaterials 2022, 12(1), 112; https://doi.org/10.3390/nano12010112
Submission received: 15 December 2021 / Revised: 27 December 2021 / Accepted: 27 December 2021 / Published: 30 December 2021
(This article belongs to the Special Issue Applications of Metal Halide Perovskites in Optoelectronic Devices)
Browse Figures
Versions Notes

Abstract

:
Although power conversion efficiencies of organic-inorganic lead halide perovskite solar cells (PSCs) are approaching those of single-crystal silicon solar cells, the working device stability due to internal and external factors, such as light, temperature, and moisture, is still a key issue to address. The current world-record efficiency of PSCs is based on organic hole transport materials, which are usually susceptible to degradation from heat and diffusion of dopants. A simple solution would be to replace the generally used organic hole transport layers (HTLs) with a more stable inorganic material. This review article summarizes recent contributions of inorganic hole transport materials to PSC development, focusing on aspects of device performance and long-term stability. Future research directions of inorganic HTLs in the progress of PSC research and challenges still remaining will also be discussed.

1. Introduction

Photovoltaic (PV) technology research has been mainly focused on high efficiencies with low-cost materials and fabrication processes, but the high stability of working devices is also crucial for commercialization. Perovskite solar cells (PSCs) have impressively increased their unit-cell efficiency from 3.8% to 25.5% within about a decade [1], approaching single-crystal silicon solar cell efficiency values. Organometallic halide perovskites are based on the chemical formula of AMX3, where A is organic or metal cations, such as formamidinium ((NH2)2CH+ (FA+)), methylammonium (CH3NH3+ (MA+)), or Cs+, M is metal ions such as Pb2+ or Sn2+, and X is halogen ions, such as I−, Br−, or Cl−. Organometallic halide perovskites exhibit features of an ideal light absorber material, including high absorption coefficients (~10−4 cm−1), long carrier diffusion lengths (>1 μm), ambipolar charge transport capabilities, and low exciton binding energy (20–50 meV) [2].
Despite the remarkable growth in efficiency enhancement, compared to silicon solar cells, the working device stability still needs improvement. Degradation in PSCs can occur from both internal and external factors. Internal degradation factors include ion migration in the perovskite, lattice relaxation at interfaces, and diffusion of HTL dopants, while external degradation factors include exposure to light, heat, bias, moisture, and oxygen [3].
Perovskite solar cell device structures normally consist of the perovskite layer in between an HTL and electron transport layer (ETL), with a transparent conducting oxide (TCO), such as fluorine-doped tin oxide (FTO) or indium tin oxide (ITO), on top of a glass substrate and a metal, such as silver (Ag), gold (Au), or aluminum (Al), as the top contact [4]. Depending on the sequence of the transport layer type, the device structure is called n-i-p for the n-type ETL on the bottom (on top of the TCO) and the p-type HTL on top of the light-absorbing perovskite layer (below the top metal contact), and p-i-n for the HTL on the bottom and ETL on top of the light-absorbing layer.
The conventional HTL is based on organic materials, which are susceptible to elevated temperatures, and diffusion of HTL dopants into the perovskite layer can also cause degradation of PSC devices. Conventional n-i-p structures usually use poly[bis(4-phenyl)(2,5,6-trimethylphenyl)amine] (PTAA) and 2,2′,7,7′-tetrakis-(N,N-di-4-methoxyphenylamino)-9,9′-spirobifluorene (spiro-OMeTAD) as the HTL [5,6], whereas conventional p-i-n structures normally use poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) and PTAA [7,8,9]. Both spiro-OMeTAD and PTAA normally have dopants, such as lithium bis(trifluoromethanesulfonyl)imide and 4-tert-butylpyridine, to improve the conductivity of the HTLs. However, such dopants easily migrate out of the HTL diffusing into the perovskite layer, which leads to degrading the PSCs. PEDOT: PSS-based PSCs are known to suffer from stability issues due to the hygroscopic and acidic characteristics of PEDOT:PSS.
Suitable HTL materials should (i) possess suitable band alignment with the light absorber layer for effective transfer of the photoexcited holes from the perovskite to the HTL, (ii) have high carrier mobility to enhance the fill factor by reducing series resistance, (iii) exhibit a wide optical bandgap so that there will be no contribution as a second light absorber layer, (iv) possess high transparency to minimize optical losses, (v) show adequate hydrophobic nature to tolerate long-term exposure to humidity, (vi) have low materials and fabrication costs, (vii) be environmentally friendly, and (viii) show good stability against light and heat [10,11,12].
While much effort has been made to modify the perovskite layer to enhance device stability [13,14,15,16], another straightforward approach to enhance the working stability of PSCs would be to replace these organic HTLs with inorganic materials. In this review, the recent progress of inorganic HTLs in PSCs is summarized based on device performance and stability in Section 2. Inorganic HTL materials covered include nickel oxide (NiOx), copper thiocyanate (CuSCN), Cu-based delafossite materials, such as CuAlO2, CuCrO2, CuGaO2, and CuFeO2, copper oxide (CuOx), copper iodide (CuI), copper sulfide (CuS), cobalt oxide (CoOx), chromium oxide (CrOx), molybdenum oxide (MoOx), vanadium oxide (VOx). Section 2 will also discuss the long-term stability of the inorganic HTL-based PSCs. Progress in the photovoltaic performance and device stability are summarized in Table 1 and Table 2, respectively. Conclusions along with future directions will be discussed in Section 3.

2. Device Performance and Stability of Inorganic Hole Transport Materials-Based PSCs

2.1. Nickel Oxide

Nickel oxide has already been used in dye-sensitized solar cells (DSSCs) and organic photovoltaics (OPV) as the p-type HTL before being applied in PSCs [62,63]. NiOx exhibits high transparency from its wide bandgap (3.6 eV), deep valence band (−5.2 to −5.4 eV), and high carrier mobility (0.1 cm2/Vs) while having suitable stability against light, heat, and moisture, making it a suitable HTL candidate for PSCs [64]. NiOx has been applied to PSCs in both n-i-p and p-i-n structures. There are more considerations required when applying NiOx on top of the perovskite layer in n-i-p structures, as sputtering, water, or polar organic solvents can damage the underlying perovskite layer. NiOx was applied in n-i-p structured PSCs by dc magnetron sputtering [17]. The efficiency was only 7.3%, but the unencapsulated device remained stable for 60 days in a 25 °C ambient atmosphere with 28 ± 2% relative humidity without light soaking. Chlorobenzene-dispersed NiOx HTL can also be directly deposited on the perovskite films without decomposing the perovskite, resulting in efficiencies over 9% [18].
For p-i-n configurations, power conversion efficiencies (PCEs) of 17.3% [19] and 17.6% [20] were achieved by pulsed laser deposition, by controlling the deposition time and oxygen partial pressure, and by solution processing, respectively. Vertical recrystallization of the perovskite layer and co-doping the NiOx with lithium (Li) and magnesium (Mg) resulted in a PCE over 20%, and the device stability maintained over 85% of its initial PCE under maximum power point tracking (MPPT) conditions for over 500 h, as shown in Figure 1 [21]. Li-doping increases the p-type conductivity, whereas Mg-doping adjusts the valence band energy level. Previous reports demonstrate NiOx-based PSCs maintaining 85% of its initial PCE at 60% humidity and 60 °C for 500 h for encapsulated devices (Figure 2) [60], and 100% of its initial PCE under 1 SUN at 40% humidity and 35 °C for 1000 h under MPPT conditions for devices without encapsulation (Figure 3) [61].
Application of NiOx by atmospheric pressure spatial atomic layer deposition (s-ALD) system, a more rapid method than conventional ALD [65,66], in p-i-n structured PSCs has been demonstrated. Employing high-quality and high-uniformity NiOx HTLs in PSCs resulted in PCEs over 17% with negligible hysteresis and fill factors over 80% [22,67]. Perovskite films with improved efficient collection of charge carriers and intrinsic electronic quality were enabled from the high uniformity of NiOx, resulting in PSC devices with reduced interfacial trapping and improved open-circuit voltage (VOC). NiO has also been applied to p-i-n PSCs using plasma-enhanced ALD (PEALD), resulting in PSCs over 17% [24]. For p-i-n structured PSCs, atomic layer deposition (ALD) of NiO employed in PSCs resulted in efficiencies of over 18% [23]. The ALD NiO-based PSCs maintained over 99% of their initial PCE at room temperature conditions and 87% at 85 °C under 1 SUN, MPPT, as shown in Figure 4.
Researchers have found various methods to dope NiOx to improve conductivity, and thus, the PSC device performance. Copper-doped NiOx (Cu:NiOx) resulted in efficiencies over 17.8% using a low-temperature combustion process, outperforming the conventional sol-gel-derived high-temperature Cu:NiOx PCE of 15.5% [25]. Despite the reduced process temperature Cu:NiOx prepared by this combustion process has a tendency to be better than the conventional high-temperature sol-gel process in terms of optical transparency, crystallinity, and electrical conductivity. Yue et al. further improved Cu:NiOx-based PSCs by doping the methylammonium lead halide perovskite with chlorine to improve the open-circuit voltage, modifying the aluminum cathode with zirconium acetylacetonate (Zracac), and employing fluorine-doped tin oxide (FTO), which resulted in a PCE of 20.5% [26]. Doping of NiOx with lithium (Li) and magnesium (Mg) in PSC has also been demonstrated, resulting in PCEs of 18% [28] and 18.5% [30], respectively. Li-doped NiO surface by a hot-casting method enabled highly crystalline MAPbI3, resulting in hysteresis-free, efficient, and photostable PSCs. Limitations of poor fill factor and short-circuit current density in sputtered NiOx-based PSCs can be overcome through introducing Mg at a low oxygen partial pressure deposition condition. Doping NiOx with Li and Mg have also demonstrated devices with PCEs of above 20.7% with suitable stability for 500 h in a light soaking and thermal aging test [21], and 19.2% with retaining >80% of the initial PCE after light soaking for 1000 h or thermal exposure at 85 °C for 500 h [27]. Doping NiOx with cesium (Cs) exhibits higher conductivity and higher working function, resulting in improved PCE from 16.0% to 19.4% when applied in PSCs [29]. Doping with cobalt (Co) improved PSC devices from efficiencies of 16.0% to 17.8% due to less charge accumulation and open-circuit voltage loss from the improved hole mobility and reduction in interfacial resistance [31]. Thus, NiOx can be doped by various elements, such as Cu, Li, Mg, Cs, and Co, to improve the conductivity and enhance the efficiency of the PSC by reducing interfacial resistance at the HTL/perovskite interface.

2.2. Copper Thiocyanate

Copper thiocyanate (CuSCN) has a wide bandgap of 3.9 eV and appropriate valence band energy level of −5.3 eV with carrier mobility of 10−2–10−1 cm2/Vs and superior thermal stability compared to spiro-OMeTAD, making it a suitable HTL candidate for PSCs [68]. Furthermore, it is solution processable with a low cost, showing potential in commercialization. CuSCN has been applied to PSCs in mostly n-i-p configurations. Madhavan et al. demonstrated PCE values of 16.6% from a thick CuSCN layer of 500 nm fabricated by doctor blading, whereas spin-coated CuSCN films of 30 nm resulted in PSCs of 15.4% [32]. Jung et al. demonstrated CuSCN-based PSCs with a PCE of 18.0% using a formamidinium-based lead halide perovskite, (FAPbI3)0.85(MAPbBr3)0.15, which is more tolerant to thermal stress than MAPbI3 [33]. CuSCN-based PSCs retained 60% of the initial PCE in air at 125 °C with 40% relative humidity for 2 h, while spiro-OMeTAD-based PSCs retained only 25% of their initial PCE under the same conditions.
Highly conformal CuSCN layers were formed through a fast solvent removal method, facilitating rapid carrier extraction and collection, resulting in a PCE of 20.4% [34]. Applying a reduced graphene oxide (RGO) layer before the top Au contact further enhances the stability by reducing potential-induced degradation from the reaction of Au and SCN− anions at the CuSCN/Au contact. These PSCs showed excellent thermal stability under long-term heating. Over 95% of the initial PCE is maintained under 1 SUN, 60 °C, in nitrogen (N2) atmosphere with MPPT conditions after 1000 h surpassing the light stability of devices based on spiro-OMeTAD, as shown in Figure 5. Light and heat stability of CuSCN-based PSCs can be greatly enhanced by the insertion of an RGO layer in between CuSCN and Au to block anion diffusion.

2.3. Copper Iodide

Copper iodide (CuI) is a p-type semiconductor with a valence band energy level of −5.2 eV, a large bandgap of 3.1 eV, and hole mobility of 0.5–2 cm2/Vs [69]. Due to its hydrophobicity, CuI shows suitable ambient stability compared to PEDOT:PSS. CuI has already been widely used in OPV and DSSCs as an HTL and is a promising alternative in terms of low-cost and large-scale industrial commercialization [70]. CuI has been applied to PSCs in both p-i-n and n-i-p configurations, with PCEs of 7.5% [35] and 16.8% [36], respectively. CuI in the n-i-p structured device was successfully applied in a planar structured device and displayed significantly reduced hysteresis compared to the conventional devices based on spiro-OMeTAD. CuI in a p-i-n structured device maintained 93% of its initial PCE after storage in 25% humidity at room temperature without illumination for 300 h, showing better air stability than the reference PSC based on PEDOT:PSS, as shown in Figure 6 [36]. Ramachandran et al. reported a two-step electrodeposition method of preparing CuSCN on top of CuI on ITO with a carbon back electrode, resulting in a PCE of 20.4% [37].

2.4. Copper Oxide

Copper oxides, such as cuprous oxide (Cu2O) and cupric oxide (CuO), are p-type semiconductors composed of environmentally friendly and abundant elements with low cost and suitable heat and ambient stability [71]. CuO has a bandgap of 1.3 eV and a valence band energy level of approximately −5.4 eV, while Cu2O has a bandgap of 2.1 eV, valence band energy level of −5.3 to −5.4 eV, and high carrier mobility of ~100 cm2/Vs [72]. Solution-processed CuOx has been applied to p-i-n PSC devices, exhibiting high transparency in the visible region and a smooth surface, resulting in a PCE of 17.1% [38]. Approximately 90% of the initial PCE was maintained after storage in air without encapsulation for 300 h, showing enhanced air stability compared to the conventional PSC device based on PEDOT:PSS, as shown in Figure 7. Efficiencies were further improved to 17.4% by applying solution-processed CuOx, which exhibit high optical transmittance, high work function, and excellent hole-extracting ability [40]. Conventional PEDOT:PSS-based PSC devices resulted in 12.0% efficiency. The high work function of CuOx enables ohmic contact at the perovskite/CuOx interface, which reduces open-circuit voltage loss.
Further improvements in CuOx-based PSCs were made by Rao et al. by Cl doping of the perovskite layer based on a modified one-step fast deposition-crystallization method leading to a PCE of 19.0% [39]. Cl-doping MAPbI3 perovskite films remarkably improves the perovskite hole mobility and film morphology, greatly increasing the device recombination resistance and reducing the intrinsic defects. Quantum dot (QD) Cu2O dispersed in a nonpolar solvent has been spin-coated on top of the perovskite layer in a mesoporous n-i-p structure, resulting in a PCE of 18.9% [41]. Surface modification of Cu2O allows direct deposition on the perovskite film without decomposing the perovskite, resulting in a significantly higher PCE compared to the unmodified Cu2O, which resulted in a PCE of 11.9%. The dopant-free method and hydrophobic surface of Cu2O enable excellent long-term stability maintaining over 90% of the initial PCE for over 1 month when stored in air without encapsulation with a relative humidity of 30%, as shown in Figure 8. Kim et al. reported a one-step deposition of Cu2O-CuSCN to produce a nanocomposite HTL composed of Cu2O nanoparticles (20 nm in size) dispersed in a CuSCN solution with diethyl sulfide [42]. High mobility of Cu2O placed at the perovskite/CuSCN interface improved the hole extraction rate and reduced interfacial reaction, improving the PSC efficiencies from 17.7 to 19.2%, and encapsulated devices sustained its PCE over 90% under severe conditions of 85% relative humidity and 85 °C for 720 h, as shown in Figure 9.

2.5. Delafossites

Delafossite materials are based on the chemical formula of ABO2, where A is Cu, Pt, Pd, or Ag, and B is Al, Ga, Cr, In, Sc, Fe, Y, La, etc. Some common Cu-based delafossite materials are CuAlO2, CuCrO2, and CuGaO2. CuAlO2 has a bandgap of 3.75–3.86 eV, valence band of −5.0 to −5.3 eV, and hole mobility of 3.6 cm2/Vs [73,74]. p-Type CuAlO2 has been reported to exhibit decent thermal, chemical, and ambient stability and optical transparency and contains non-toxic and cheap, easily accessible elements. Inserting CuAlO2 deposited by direct current (DC) magnetron sputtering on top of ITO and below PEDOT:PSS in a p-i-n configuration resulted in a higher PCE of 14.5% compared to the PCE of the reference device (11.1%) [43]. By inserting 15 nm of CuAlO2, the stability of the device improved by maintaining 80% of its initial PCE after storage in ambient conditions for 240 h, whereas the reference device only retained 35% of its initial PCE.
CuCrO2 has a bandgap of 2.9–3.1 eV while maintaining high transmittance in the wavelength region above 400 nm, valence band energy level of −5.3 eV, and carrier mobility of 0.1–1 cm2/Vs with suitable light stability [75]. CuCrO2 spin-coated on top of the perovskite layer in an n-i-p structure resulted in a PCE of 16.7%, and retained around 88% of its initial PCE after 500 h under 1 SUN, MPPT in a nitrogen atmosphere at room temperature, as shown in Figure 10 [12]. In a p-i-n structure, applying CuCrO2 nanocrystals as the HTL resulted in an efficiency of 19% [44] and retained ~95% of its initial PCE after continuous 1 SUN illumination in argon atmosphere for 1000 h, as shown in Figure 11. Here, CuCrO2 nanocrystals function as an HTL as well as a UV-blocking underlayer to improve photostability. CuCrO2 has also been doped with Mg, with improved conductivity from 1 to 220 S cm−1, resulting in a PCE of 13.1% [45]. The PCE was further improved by Zhang et al. to 14.1% [46].
CuGaO2 has a bandgap of 3.6 eV, a valence band energy level of ~−5.3 eV, and hole mobility of 10−2–10−1 cm2/Vs [76,77,78]. CuGaO2 has suitable heat and ambient stability compared to spiro-OMeTAD. CuGaO2 spin-coated on top of the perovskite layer in an n-i-p configuration resulted in a PCE of 18.5% and retained over 90% of its initial PCE after storage in ambient air at 25 °C and 30–55% relative humidity for 30 days without encapsulation, which is superior to the spiro-OMeTAD-based PSCs, as shown in Figure 12 [47]. A mesoporous CuGaO2 coated on top of NiOx on FTO resulted in a PCE of 20%, which is superior to that of the planar cell (16.7%) [48], and maintained over 80% of its original PCE after 1000 h in a nitrogen atmosphere at 85 °C of unencapsulated devices, as shown in Figure 13.
CuFeO2 is also a cost-effective and highly light, moisture, and thermally stable material for an HTL candidate. PSCs with CuFeO2 exhibit suitable thermal, moisture, and photostability compared to PSCs based on spiro-OMeTAD [49]. Unencapsulated devices with CuFeO2 retained about 85% of their initial PCE under 1 SUN at MPPT for over 1000 h in nitrogen, whereas spiro-OMeTAD devices dropped to 10%, as shown in Figure 14. Thermal and humidity stability tests show that CuFeO2-based devices retained 80% of their initial PCE after exposure to 70 °C for 120 h and retained over 90% of their initial PCE after exposure to 80 ± 5% relative humidity for 300 h. Among the delafossite-based PSCs, devices with CuCrO2 and CuGaO2 reported high efficiencies above 19%. PSCs with CuCrO2 show suitable light stability, while CuGaO2-based devices show suitable heat and ambient stability compared to spiro-OMeTAD-based devices.

2.6. Copper Sulfide

Copper sulfide (CuS) is a p-type semiconductor, which has also been used in the fields of gas sensors, catalysis, and nonlinear optical materials [79,80]. CuS has been investigated to replace PEDOT:PSS in OPV, exhibiting decent performance compared to devices based on PEDOT:PSS [81]. CuS nanoparticles were coated on top of ITO in a p-i-n configuration PSCs, which resulted in a PCE of 16.2% [50], and maintained over 90% of its initial PCE in air without encapsulation for 260 h, shown in Figure 15. CuS nanoparticles can modify the surface of ITO by tuning the surface work function, reducing the interfacial carrier injection barrier, and enabling the hole extraction efficiency between the ITO and perovskite layers, but not ruin the transmittance and surface roughness of ITO.

2.7. Cobalt Oxide

Cobalt oxide (CoOx) has a favorable valence band energy level of −5.3 eV. Co3O4 applied by screen printing to an n-i-p configuration of a ZrO2 scaffold resulted in a PCE of 13.3% for carbon-based PSCs [52]. CoOx spin-coated on top of ITO in a p-i-n configuration resulted in a PCE of 14.5% [51]. Shalan et al. reported that according to photoluminescence decays of perovskite deposited on various HTLs, CoOx had a faster hole-extracting time of 2.8 ns compared to PEDOT:PSS (17.5 ns) and NiOx (22.8 ns). CoOx-based PSC retained 90% of its initial PCE after storage in a nitrogen atmosphere for 1000 h. Lithium cobalt oxide (LiCoO2) prepared by radio frequency (RF) magnetron sputtering in a p-i-n structured device resulted in a PCE of 19.1%, with high efficiency stable up to 90 °C, and 60% of the initial PCE was retained after continuous thermal stress at 100 °C for 5 days in an inert atmosphere, showing higher stability than the PEDOT:PSS-based device (Figure 16) [53]. UV-ozone-treated LiCoO2 exhibits a super-hydrophilic surface that can be wetted easily by the perovskite precursor solution and made wetting of a large-area substrate of 10 cm × 10 cm possible.

2.8. Chromium Oxide

Chromium oxide (CrOx) has also been investigated to replace organic HTLs in PSCs. Cu doping of CrOx can suppress the surface hydroxylation and hexavalent chromium ions, which are harmful to the interface stability of PSCs. Cu-doped CrOx in p-i-n PSC devices resulted in a PCE of 17.7%, and maintained over 70% of its original PCE after 190 h in 30% humidity 20 °C without encapsulation, as shown in Figure 17, whereas undoped CrOx-based PSCs resulted in a PCE of 14.8% and maintained less than 10% of its initial PCE [54]. PSCs with Cu-doped CrOx shows superior ambient stability than PSCs with undoped CrOx.

2.9. Molybdenum Oxide

Molybdenum oxide (MoO3) is an n-type semiconductor with a deep conduction band energy level, making it an appropriate HTL. Due to its suitable energy alignment properties, MoO3 has already been used in OPV [82]. Thermally evaporated MoOx on ITO in a p-i-n configuration resulted in a PCE of 13.1% [55]. UV-ozone treatment of MoOx was required to increase the wettability of the perovskite formation process. Titanium-doped MoO2 nanoparticles by a scalable solvothermal cracking process applied to an n-i-p PSC configuration resulted in a PCE of 15.8% [56]. Titanium-doping in MoO2 nanoparticles produces stronger Mo-O bonding and thus, enhances the stability against humidity. Xie et al. reported that reduced graphene oxide (RGO) doping is an effective method to make MoOx a promising HTL [57]. Conductive MoOx:RGO can facilitate perovskite crystallization and reduce the VOC loss, resulting in a PCE of 18.2% and VOC of 1.12 V.

2.10. Vanadium Oxide

Vanadium oxide (VO2) is also an n-type semiconductor with a deep conduction band energy level, making it an appropriate HTL [82,83]. VOx on top of the perovskite layer using a ZrO2 scaffold resulted in a PCE of 15.8% [58]. VOx was applied by post-treatment of the perovskite/carbon interface to facilitate the charge transfer from the high work function of VOx while not sacrificing the conductivity of carbon. A low-temperature solution-processed Cs-doped VOx was applied on top of ITO in a p-i-n structure resulted in a PCE of 14.5% [59], and maintained 94% of its initial PCE value after 720 h in the air (50–70% humidity) without encapsulation, showing suitable ambient stability, as shown in Figure 18. Introducing Cs to VOx improved the electrical conductivity and can change the phase separation pattern and microstructural film morphology. The enlarged surface roughness resulted in enhanced interfacial adhesion between the HTL and perovskite layer.

3. Conclusions

In summary, the recent progress of inorganic HTL-based PSCs and the roles of the inorganic HTLs on device performance and stability against heat, humidity, bias, and light are discussed. The efficiencies of inorganic HTL-based PSCs reported so far are over 20% for Cu:NiOx, Li,Mg:NiOx, CuSCN, CuI-CuSCN, and CuGaO2, which is lower but still approaching the efficiencies for organic HTL-based PSCs. Superior device stability of inorganic HTL-based PSCs to organic HTL-based PSCs has been reported, showing the potential of inorganic HTLs to replace organic HTLs in PSC devices. Further investigation on increasing the PCEs of inorganic HTL-based PSCs and a better understanding of the degradation and working mechanisms are still required.
The general criteria for selecting potential HTL candidates are also discussed. The valence band energy levels should be close to that of the perovskite layer to facilitate efficient carrier transport and appropriate conduction band energy levels to impede recombination at the HTL/perovskite interface. The carrier mobility should be high to reduce resistance and loss during transport, while the transparency should be high enough to reduce input solar radiation loss. In a p-i-n structure, the nucleation and wettability of the perovskite solution on the HTL surface become important. In an n-i-p structure, the stability of the HTL becomes important because of its contact with humidity and oxygen.
Although this review focused on single-junction unit-cell perovskite solar cells, large-area coating methods and tandem configurations, which consist of wide-bandgap perovskite solar cells on top of lower bandgap materials, such as silicon, Cu(In,Ga)Se2, and tin-related materials [15,84,85,86,87,88], need to be considered for commercialization [89]. Thus, inorganic HTL incorporated into tandem perovskite solar cells and coating methods for large-area devices are future directions to be taken. There may be temperature or fabrication limitations of the inorganic HTL in these tandem configurations, depending on the bottom cell. Especially, flexible tandem solar cells will have a limit on the processing temperatures of the layers. Obtaining highly uniform pinhole-free films of the inorganic HTL over a large area will also be important to consider for commercialization.

Funding

This work was supported financially by the Korea Research Institute of Chemical Technology (KRICT), Republic of Korea (SS2122-20), from the Korea Institute of Energy Technology Evaluation and Planning (KETEP), and the Ministry of Trade Industry and Energy (MOTIE), Republic of Korea (no. 20203040010320), and from the National Research Council of Science and Technology (NST), the Republic of Korea (no. CAP-18-05-KAERI).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data sharing not applicable.

Conflicts of Interest

The author declares no conflict of interest.

References

  1. National Renewable Energy Lab. Photovoltaic Research. Available online: http://www.nrel.gov/pv/ (accessed on 15 December 2021).
  2. Hwang, T.; Lee, B.; Kim, J.; Lee, S.; Gil, B.; Yun, A.J.; Park, B. From Nanostructural Evolution to Dynamic Interplay of Constituents: Perspectives for Perovskite Solar Cells. Adv. Mater. 2018, 30, 1–22. [Google Scholar] [CrossRef] [PubMed]
  3. Jung, H.J.; Kim, D.; Kim, S.; Park, J.; Dravid, V.P.; Shin, B. Stability of Halide Perovskite Solar Cell Devices: In Situ Observation of Oxygen Diffusion under Biasing. Adv. Mater. 2018, 30, 1–10. [Google Scholar] [CrossRef]
  4. Zuo, C.; Bolink, H.; Han, H.; Huang, J.; Cahen, D.; Ding, L. Advances in Perovskite Solar Cells. Adv. Sci. 2016, 3, 1500324. [Google Scholar] [CrossRef]
  5. Rombach, F.M.; Haque, S.A.; Macdonald, T.J. Lessons learned from spiro-OMeTAD and PTAA in perovskite solar cells. Energy Environ. Sci. 2021, 14, 5161. [Google Scholar] [CrossRef]
  6. Jiang, Q.; Zhao, Y.; Zhang, X.; Yang, X.; Chen, Y.; Chu, Z.; Ye, Q.; Li, X.; Yin, Z.; You, J. Surface passivation of perovskite film for efficient solar cells. Nat. Photonics 2019, 13, 460–466. [Google Scholar] [CrossRef]
  7. Perrin, L.; Lemercier, T.; Planès, E.; Berson, S.; Flandin, L. Perovskite Inverted Solar Cells: Impact of Hole Transport Layer and Anti-Solvent Ejection Time. In Proceedings of the IEEE 48th Photovoltaic Specialists Conference (PVSC), Fort Lauderdale, FL, USA, 20–25 June 2021; pp. 1324–1327. [Google Scholar] [CrossRef]
  8. Lemercier, T.; Perrin, L.; Planès, E.; Berson, S.; Flandin, L. A Comparison of the Structure and Properties of Opaque and Semi-Transparent NIP/PIN-Type Scalable Perovskite Solar Cells. Energies 2020, 13, 3794. [Google Scholar] [CrossRef]
  9. Wang, M.; Wang, H.; Li, W.; Hu, X.; Sun, K.; Zang, Z. Defect passivation using ultrathin PTAA layers for efficient and stable perovskite solar cells with a high fill factor and eliminated hysteresis. J. Mater. Chem. A 2019, 7, 26421. [Google Scholar] [CrossRef]
  10. Kung, P.-K.; Li, M.-H.; Lin, P.-Y.; Chiang, Y.-H.; Chan, C.-R.; Guo, T.-F.; Chen, P. A Review of Inorganic Hole Transport Materials for Perovskite Solar Cells. Adv. Mater. Interfaces 2018, 5, 1800882. [Google Scholar] [CrossRef]
  11. Gil, B.; Yun, A.J.; Lee, Y.; Kim, J.; Lee, B.; Park, B. Recent Progress in Inorganic Hole Transport Materials for Efficient and Stable Perovskite Solar Cells. Electron. Mater. Lett. 2019, 15, 505–524. [Google Scholar] [CrossRef]
  12. Akin, S.; Liu, Y.; Dar, M.I.; Zakeeruddin, S.M.; Gratzel, M.; Turand, S.; Sonmezoglu, S. Hydrothermally processed CuCrO2 nanoparticles as an inorganic hole transporting material for lowcost perovskite solar cells with superior stability. J. Mater. Chem. A 2018, 6, 20327. [Google Scholar] [CrossRef]
  13. Kim, J.; Yun, A.J.; Gil, B.; Lee, Y.; Park, B. Triamine-Based Aromatic Cation as a Novel Stabilizer for Efficient Perovskite Solar Cells. Adv. Funct. Mater. 2019, 29, 1–7. [Google Scholar] [CrossRef] [Green Version]
  14. Yun, A.J.; Kim, J.; Gil, B.; Woo, H.; Park, K.; Cho, J.; Park, B. Incorporation of Lithium Fluoride Restraining Thermal Degradation and Photodegradation of Organometal Halide Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2020, 12, 50418–50425. [Google Scholar] [CrossRef]
  15. Kim, D.; Jung, H.J.; Park, I.J.; Larson, B.W.; Dunfield, S.P.; Xiao, C.; Kim, J.; Tong, J.; Boonmongkolras, P.; Ji, S.G.; et al. Efficient, stable silicon tandem cells enabled by anion-engineered wide-bandgap perovskites. Science 2020, 368, 155–160. [Google Scholar] [CrossRef]
  16. Hwang, T.; Cho, D.; Kim, J.; Kim, J.; Lee, S.; Lee, B.; Kim, K.H.; Hong, S.; Kim, C.; Park, B. Investigation of chlorine-mediated microstructural evolution of CH3NH3PbI3(Cl) grains for high optoelectronic responses. Nano Energy 2016, 25, 91–99. [Google Scholar] [CrossRef]
  17. Nejand, B.A.; Ahmadi, V.; Shahverdi, H.R. New Physical Deposition Approach for Low Cost Inorganic Hole Transport Layer in Normal Architecture of Durable Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2015, 7, 21807–21818. [Google Scholar] [CrossRef] [PubMed]
  18. Liu, Z.; Zhu, A.; Cai, F.; Tao, L.; Zhou, Y.; Zhao, Z.; Chen, Q.; Cheng, Y.-B.; Zhou, H. Nickel oxide nanoparticles for efficient hole transport in p-i-n and n-i-p perovskite solar cells. J. Mater. Chem. A 2017, 5, 6597–6605. [Google Scholar] [CrossRef]
  19. Park, J.H.; Seo, J.; Park, S.; Shin, S.S.; Kim, Y.C.; Jeon, N.J.; Shin, H.-W.; Ahn, T.K.; Noh, J.H.; Yoon, S.C.; et al. Efficient CH3NH3PbI3 Perovskite Solar Cells Employing Nanostructured p-Type NiO Electrode Formed by a Pulsed Laser Deposition. Adv. Mater. 2015, 27, 4013–4019. [Google Scholar] [CrossRef]
  20. Zhang, H.; Cheng, J.; Lin, F.; He, H.; Mao, J.; Wong, K.S.; Jen, A.K.-Y.; Choy, W.C.H. Pinhole-Free and Surface-Nanostructured NiOx Film by Room-Temperature Solution Process for High-Performance Flexible Perovskite Solar Cells with Good Stability and Reproducibility. ACS Nano 2016, 10, 1503–1511. [Google Scholar] [CrossRef] [PubMed]
  21. Xie, F.; Chen, C.-C.; Wu, Y.; Li, X.; Cai, M.; Liu, X.; Yang, X.; Han, L. Vertical recrystallization for highly efficient and stable formamidinium-based inverted-structure perovskite solar cells. Energy Environ. Sci. 2017, 10, 1942. [Google Scholar] [CrossRef]
  22. Zhao, B.; Lee, L.C.; Yang, L.; Pearson, A.J.; Lu, H.; She, X.-J.; Cui, L.; Zhang, K.H.L.; Hoye, R.L.Z.; Karani, A.; et al. In Situ Atmospheric Deposition of Ultrasmooth Nickel Oxide for Efficient Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2018, 10, 41849–41854. [Google Scholar] [CrossRef] [PubMed]
  23. Seo, S.; Jeong, S.; Bae, C.; Park, N.-G.; Shin, H. Perovskite Solar Cells with Inorganic Electron- and HoleTransport Layers Exhibiting Long-Term (≈500 h) Stability at 85 °C under Continuous 1 Sun Illumination in Ambient Air. Adv. Mater. 2018, 30, 1801010. [Google Scholar] [CrossRef] [PubMed]
  24. Koushik, D.; Jost, M.; Ducinskas, A.; Burgess, C.; Zardetto, V.; Weijtens, C.; Verheijen, M.A.; Kessels, W.M.M.; Albrecht, S.; Creatore, M. Plasma-assisted atomic layer deposition of nickel oxide as hole transport layer for hybrid perovskite solar cells. J. Mater. Chem. C 2019, 7, 12532. [Google Scholar] [CrossRef] [Green Version]
  25. Jung, J.W.; Chueh, C.-C.; Jen, A.K.-Y. A Low-Temperature, Solution-Processable, Cu-Doped Nickel Oxide Hole-Transporting Layer via the Combustion Method for High-Performance Thin-Film Perovskite Solar Cells. Adv. Mater. 2015, 27, 7874–7880. [Google Scholar] [CrossRef] [PubMed]
  26. Yue, S.; Liu, K.; Xu, R.; Li, M.; Azam, M.; Ren, K.; Liu, J.; Sun, Y.; Wang, Z.; Cao, D.; et al. Efficacious engineering on charge extraction for realizing highly efficient perovskite solar cells. Energy Environ. Sci. 2017, 10, 2570. [Google Scholar] [CrossRef]
  27. Wu, Y.; Xie, F.; Chen, H.; Yang, X.; Su, H.; Cai, M.; Zhou, Z.; Noda, T.; Han, L. Thermally Stable MAPbI3 Perovskite Solar Cells with Efficiency of 19.19% and Area over 1 cm2 achieved by Additive Engineering. Adv. Mater. 2017, 29, 1701073. [Google Scholar] [CrossRef]
  28. Nie, W.; Tsai, H.; Blancon, J.-C.; Liu, F.; Stoumpos, C.C.; Traore, B.; Kepenekian, M.; Durand, O.; Katan, C.; Tretiak, S.; et al. Critical Role of Interface and Crystallinity on the Performance and Photostability of Perovskite Solar Cell on Nickel Oxide. Adv. Mater. 2018, 30, 1703879. [Google Scholar] [CrossRef] [PubMed]
  29. Chen, W.; Liu, F.-Z.; Feng, X.-Y.; Djurišic, A.B.; Chan, W.K.; He, Z.-B. Cesium Doped NiOx as an Efficient Hole Extraction Layer for Inverted Planar Perovskite Solar Cell. Adv. Energy Mater. 2017, 7, 1700722. [Google Scholar] [CrossRef]
  30. Li, G.; Jiang, Y.; Deng, S.; Tam, A.; Xu, P.; Wong, M.; Kwok, H.-S. Overcoming the Limitations of Sputtered Nickel Oxide for High-Efficiency and Large-Area Perovskite Solar Cells. Adv. Sci. 2017, 4, 1700463. [Google Scholar] [CrossRef]
  31. Lee, P.-H.; Li, B.-T.; Lee, C.-F.; Huang, Z.-H.; Huang, Y.-C.; Su, W.-F. High-efficiency perovskite solar cell using cobalt doped nickel oxide hole transport layer fabricated by NIR process. Sol. Energy Mater. Sol. Cells 2020, 208, 110352. [Google Scholar] [CrossRef]
  32. Madhavan, V.E.; Zimmermann, I.; Roldán-Carmona, C.; Grancini, G.; Buffiere, M.; Belaidi, A.; Nazeeruddin, M.K. Copper Thiocyanate Inorganic HoleTransporting Material for High-Efficiency Perovskite Solar Cells. ACS Energy Lett. 2016, 1, 1112–1117. [Google Scholar] [CrossRef]
  33. Jung, M.; Kim, Y.C.; Jeon, N.J.; Yang, W.S.; Seo, J.; Noh, J.H.; Seok, S.I. Thermal Stability of CuSCN Hole Conductor-Based Perovskite Solar Cells. ChemSusChem 2016, 9, 1–6. [Google Scholar] [CrossRef]
  34. Arora, N.; Dar, M.I.; Hinderhofer, A.; Pellet, N.; Schreiber, F.; Zakeeruddin, S.M.; Grätzel, M. Perovskite solar cells with CuSCN hole extraction layers yield stabilized efficiencies greater than 20%. Science 2017, 358, 768–771. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  35. Sepalage, G.A.; Meyer, S.; Pascoe, A.; Scully, A.D.; Huang, F.; Bach, U.; Cheng, Y.-B.; Spiccia, L. Copper(I) Iodide as Hole-Conductor in Planar Perovskite Solar Cells: Probing the Origin of J–V Hysteresis. Adv. Funct. Mater. 2015, 25, 5650–5661. [Google Scholar] [CrossRef]
  36. Sun, W.; Ye, S.; Rao, H.; Li, Y.; Liu, Z.; Xiao, L.; Chen, Z.; Bian, Z.; Huang, C. Room-temperature and solution-processed copper iodide as the hole transport layer for inverted planar perovskite solar cells. Nanoscale 2016, 8, 15954. [Google Scholar] [CrossRef]
  37. Ramachandran, K.; Jeganathan, C.; Karuppuchamy, S. Electrodeposition of nanostructured bilayer CuI@CuSCN as hole transport material for highly efficient inverted perovskite solar cells. J. Alloys Compd. 2021, 881, 160530. [Google Scholar] [CrossRef]
  38. Sun, W.; Li, Y.; Ye, S.; Rao, H.; Yan, W.; Peng, H.; Li, Y.; Liu, Z.; Wang, S.; Chen, Z.; et al. High-performance inverted planar heterojunction perovskite solar cells based on a solutionprocessed CuOx hole transport layer. Nanoscale 2016, 8, 10806. [Google Scholar] [CrossRef]
  39. Rao, H.; Ye, S.; Sun, W.; Yan, W.; Li, Y.; Peng, H.; Liu, Z.; Bian, Z.; Li, Y.; Huang, C. A 19.0% efficiency achieved in CuOx-based inverted CH3NH3PbI3xClx solar cells by an effective Cl doping method. Nano Energy 2016, 27, 51–57. [Google Scholar]
  40. Yu, Z.-K.; Fu, W.-F.; Liu, W.-Q.; Zhang, Z.-Q.; Liu, Y.-J.; Yan, J.-L.; Ye, T.; Yang, W.-T.; Li, H.-Y.; Chen, H.-Z. Solution-processed CuOx as an efficient hole-extraction layer for inverted planar heterojunction perovskite solar cells. Chin. Chem. Lett. 2017, 28, 13–18. [Google Scholar] [CrossRef] [Green Version]
  41. Liu, C.; Zhou, X.; Chen, S.; Zhao, X.; Dai, S.; Xu, B. Hydrophobic Cu2O Quantum Dots Enabled by Surfactant Modification as Top Hole-Transport Materials for Efficient Perovskite Solar Cells. Adv. Sci. 2019, 6, 1801169. [Google Scholar] [CrossRef] [Green Version]
  42. Kim, J.; Lee, Y.; Gil, B.; Yun, A.J.; Kim, J.; Woo, H.; Park, K.; Park, B. A Cu2O−CuSCN Nanocomposite as a Hole-Transport Material of Perovskite Solar Cells for Enhanced Carrier Transport and Suppressed Interfacial Degradation. ACS Appl. Energy Mater. 2020, 3, 7572–7579. [Google Scholar] [CrossRef]
  43. Igbari, F.; Li, M.; Hu, Y.; Wang, Z.-K.; Liao, L.-S. A room-temperature CuAlO2 hole interfacial layer for efficient and stable planar perovskite solar cells. J. Mater. Chem. A 2016, 4, 1326. [Google Scholar] [CrossRef]
  44. Zhang, H.; Wang, H.; Zhu, H.; Chueh, C.-C.; Chen, W.; Yang, S.; Jen, A.K.-Y. Low-Temperature Solution-Processed CuCrO2 Hole-Transporting Layer for Efficient and Photostable Perovskite Solar Cells. Adv. Energy Mater. 2018, 8, 1702762. [Google Scholar] [CrossRef]
  45. Jeong, S.; Seo, S.; Shin, H. p-Type CuCrO2 particulate films as the hole transporting layer for CH3NH3PbI3 perovskite solar cells. RSC Adv. 2018, 8, 27956. [Google Scholar] [CrossRef] [Green Version]
  46. Zhang, B.; Thampy, S.; Dunlap-Shohl, W.A.; Xu, W.; Zheng, Y.; Cao, F.-Y.; Cheng, Y.-J.; Malko, A.V.; Mitzi, D.B.; Hsu, J.W.P. Mg Doped CuCrO2 as Efficient Hole Transport Layers for Organic and Perovskite Solar Cells. Nanomaterials 2019, 9, 1311. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  47. Zhang, H.; Wang, H.; Chen, W.; Jen, A.K.-Y. CuGaO2: A Promising Inorganic Hole-Transporting Material for Highly Efficient and Stable Perovskite Solar Cells. Adv. Mater. 2017, 29, 1604984. [Google Scholar] [CrossRef]
  48. Chen, Y.; Yang, Z.; Wang, S.; Zheng, X.; Wu, Y.; Yuan, N.; Zhang, W.-H.; Liu, S. Design of an Inorganic Mesoporous Hole-Transporting Layer for Highly Efficient and Stable Inverted Perovskite Solar Cells. Adv. Mater. 2018, 30, 1805660. [Google Scholar] [CrossRef]
  49. Akin, S.; Sadegh, F.; Turan, S.; Sonmezoglu, S. Inorganic CuFeO2 Delafossite Nanoparticles as Effective Hole Transport Materials for Highly Efficient and Long-Term Stable Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2019, 11, 45142–45149. [Google Scholar] [CrossRef]
  50. Rao, H.; Sun, W.; Ye, S.; Yan, W.; Li, Y.; Peng, H.; Liu, Z.; Bian, Z.; Huang, C. Solution-Processed CuS NPs as an Inorganic Hole-Selective Contact Material for Inverted Planar Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2016, 8, 7800–7805. [Google Scholar] [CrossRef]
  51. Shalan, A.E.; Oshikiri, T.; Narra, S.; Elshanawany, M.M.; Ueno, K.; Wu, H.-P.; Nakamura, K.; Shi, X.; Diau, E.W.-G.; Misawa, H. Cobalt Oxide (CoOx) as an Efficient Hole-Extracting Layer for High Performance Inverted Planar Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2016, 8, 33592–33600. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  52. Bashir, A.; Shukla, S.; Lew, J.H.; Shukla, S.; Bruno, A.; Gupta, D.; Baikie, T.; Patidar, R.; Akhter, Z.; Priyadarshi, A.; et al. Spinel Co3O4 nanomaterials for efficient and stable large area carbon-based printed perovskite solar cells. Nanoscale 2018, 10, 2341. [Google Scholar] [CrossRef]
  53. Chiang, C.-H.; Chen, C.-C.; Nazeeruddin, M.K.; Wu, C.-G. A newly developed lithium cobalt oxide super hydrophilic film for large area, thermally stable and highly efficient inverted perovskite solar cells. J. Mater. Chem. A 2018, 6, 13751. [Google Scholar] [CrossRef]
  54. Qin, P.; He, Q.; Yang, G.; Yu, X.; Xiong, L.; Fang, G. Metal ions diffusion at heterojunction chromium Oxide/CH3NH3PbI3 interface on the stability of perovskite solar cells. Surf. Interfaces 2018, 10, 93–99. [Google Scholar] [CrossRef]
  55. Tseng, Z.-L.; Chen, L.-C.; Chiang, C.-H.; Chang, S.-H.; Chen, C.-C.; Wu, C.-G. Efficient inverted-type perovskite solar cells using UV-ozone treated MoOx and WOx as hole transporting layers. Sol. Energy 2016, 139, 484–488. [Google Scholar] [CrossRef]
  56. Im, K.; Heo, J.H.; Im, S.H.; Kim, J. Scalable synthesis of Ti-doped MoO2 nanoparticle-hole-transportingmaterial with high moisture stability for CH3NH3PbI3 perovskite solar cells. Chem. Eng. J. 2017, 330, 698–705. [Google Scholar] [CrossRef]
  57. Xie, B.; Zhang, Y.; Li, Y.; Chen, W.; Hu, X.; Zhang, S. Solution preparation of molybdenum oxide on graphene: A hole transport layer for efficient perovskite solar cells with a 1.12 V high open-circuit voltage. J. Mater. Sci. Mater. Electron. 2020, 31, 6248–6254. [Google Scholar] [CrossRef]
  58. Li, D.; Tong, C.; Ji, W.; Fu, Z.; Wan, Z.; Huang, Q.; Ming, Y.; Mei, A.; Hu, Y.; Rong, Y.; et al. Vanadium Oxide Post-Treatment for Enhanced Photovoltage of Printable Perovskite Solar Cells. ACS Sustain. Chem. Eng. 2019, 7, 2619–2625. [Google Scholar] [CrossRef]
  59. Yao, X.; Qi, J.; Xu, W.; Jiang, X.; Gong, X.; Cao, Y. Cesium-Doped Vanadium Oxide as the Hole Extraction Layer for Efficient Perovskite Solar Cells. ACS Omega 2018, 3, 1117–1125. [Google Scholar] [CrossRef]
  60. Zhou, Y.; Yin, X.; Luo, Q.; Zhao, X.; Zhou, D.; Han, J.; Hao, F.; Tai, M.; Li, J.; Liu, P.; et al. Efficiently Improving the Stability of Inverted Perovskite Solar Cells by Employing Polyethylenimine-Modified Carbon Nanotubes as Electrodes. ACS Appl. Mater. Interfaces 2018, 10, 31384–31393. [Google Scholar] [CrossRef]
  61. Bush, K.A.; Palmstrom, A.F.; Yu, Z.J.; Boccard, M.; Cheacharoen, R.; Mailoa, J.P.; McMeekin, D.P.; Hoye, R.L.Z.; Bailie, C.D.; Leijtens, T.; et al. 23.6%-efficient monolithic perovskite/silicon tandem solar cells with improved stability. Nat. Energy 2017, 2, 17009. [Google Scholar] [CrossRef]
  62. Li, L.; Gibson, E.A.; Qin, P.; Boschloo, G.; Gorlov, M.; Hagfeldt, A.; Sun, L. Double-Layered NiO Photocathodes for p-Type DSSCs with Record IPCE. Adv. Mater. 2010, 22, 1759–1762. [Google Scholar] [CrossRef]
  63. Manders, J.R.; Tsang, S.-W.; Hartel, M.J.; Lai, T.-H.; Chen, S.; Amb, C.M.; Reynolds, J.R.; So, F. Solution-Processed Nickel Oxide Hole Transport Layers in High Efficiency Polymer Photovoltaic Cells. Adv. Funct. Mater. 2013, 23, 2993–3001. [Google Scholar] [CrossRef]
  64. Liu, S.; Liu, R.; Chen, Y.; Ho, S.; Kim, J.H.; So, F. Nickel Oxide Hole Injection/Transport Layers for Efficient Solution-Processed Organic Light-Emitting Diodes. Chem. Mater. 2014, 26, 4528–4534. [Google Scholar] [CrossRef]
  65. Park, H.H.; Jayaraman, A.; Heasley, R.; Yang, C.; Hartle, L.; Mankad, R.; Haight, R.; Mitzi, D.B.; Gunawan, O.; Gordon, R.G. Atomic layer deposition of Al-incorporated Zn(O,S) thin films with tunable electrical properties. Appl. Phys. Lett. 2014, 105, 202101. [Google Scholar] [CrossRef]
  66. Park, H.H.; Heasley, R.; Gordon, R.G. Atomic layer deposition of Zn(O,S) thin films with tunable electrical properties by oxygen annealing. Appl. Phys. Lett. 2013, 102, 132110. [Google Scholar] [CrossRef]
  67. Park, H.H. Inorganic Materials by Atomic Layer Deposition for Perovskite Solar Cells. Nanomaterials 2021, 11, 88. [Google Scholar] [CrossRef]
  68. Kim, J.; Lee, Y.; Yun, A.J.; Gil, B.; Park, B. Interfacial Modification and Defect Passivation by the Cross-Linking Interlayer for Efficient and Stable CuSCN-Based Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2019, 11, 46818–46824. [Google Scholar] [CrossRef] [PubMed]
  69. Inudo, S.; Miyake, M.; Hirato, T. Electrical properties of CuI films prepared by spin coating. Phys. Status Solidi A 2013, 210, 2395–2398. [Google Scholar] [CrossRef] [Green Version]
  70. Perera, V.P.S.; Tennakone, K. Recombination processes in dye-sensitized solid-state solar cells with CuI as the hole collector. Sol. Energy Mater. Sol. Cells 2003, 79, 249–255. [Google Scholar] [CrossRef]
  71. Eom, T.; Kim, S.; Agbenyeke, R.E.; Jung, H.; Shin, S.M.; Lee, Y.K.; Kim, C.G.; Chung, T.-M.; Jeon, N.J.; Park, H.H.; et al. Copper Oxide Buffer Layers by Pulsed-Chemical Vapor Deposition for Semitransparent Perovskite Solar Cells. Adv. Mater. Interfaces 2020, 8, 2001482. [Google Scholar] [CrossRef]
  72. Zuo, C.; Ding, L. Solution-Processed Cu2O and CuO as Hole Transport Materials for Efficient Perovskite Solar Cells. Small 2015, 11, 5528–5532. [Google Scholar] [CrossRef]
  73. Nie, X.; Wei, S.-H.; Zhang, S.B. Bipolar Doping and Band-Gap Anomalies in Delafossite Transparent Conductive Oxides. Phys. Rev. Lett. 2002, 88, 066405. [Google Scholar] [CrossRef]
  74. Gillen, R.; Robertson, J. Band structure calculations of CuAlO2, CuGaO2, CuInO2, and CuCrO2 by screened exchange. Phys. Rev. B 2011, 84, 035125. [Google Scholar] [CrossRef] [Green Version]
  75. Gil, B.; Kim, J.; Yun, A.J.; Park, K.; Cho, J.; Park, M.; Park, B. CuCrO2 Nanoparticles Incorporated into PTAA as a Hole Transport Layer for 85 °C and Light Stabilities in Perovskite Solar Cells. Nanomaterials 2020, 10, 1669. [Google Scholar] [CrossRef]
  76. Yu, M.; Draskovic, T.I.; Wu, Y. Understanding the Crystallization Mechanism of Delafossite CuGaO2 for Controlled Hydrothermal Synthesis of Nanoparticles and Nanoplates. Inorg. Chem. 2014, 53, 5845–5851. [Google Scholar] [CrossRef]
  77. Xu, Z.; Xiong, D.; Wang, H.; Zhang, W.; Zeng, X.; Ming, L.; Chen, W.; Xu, X.; Cui, J.; Wang, M.; et al. Remarkable photocurrent of p-type dye-sensitized solar cell achieved by size controlled CuGaO2 nanoplates. J. Mater. Chem. A 2014, 2, 2968. [Google Scholar] [CrossRef]
  78. Yu, M.; Draskovic, T.I.; Wu, Y. Cu(I)-based delafossite compounds as photocathodes in p-type dye-sensitized solar cells. Phys. Chem. Chem. Phys. 2014, 16, 5026. [Google Scholar] [CrossRef] [PubMed]
  79. Galdikas, A.; Mironas, A.; Strazdiene, V.; Setkus, A.; Ancutiene, I.; Janickis, V. Room-temperature-functioning ammonia sensor based on solid-state CuS films. Sens. Actuators B 2000, 67, 76–83. [Google Scholar] [CrossRef]
  80. Sakamoto, T.; Sunamura, H.; Kawaura, H.; Hasegawa, T.; Nakayama, T.; Aono, M. Nanometer-scale switches using copper sulfide. Appl. Phys. Lett. 2003, 82, 3032. [Google Scholar] [CrossRef]
  81. Li, J.; Jiu, T.; Tao, G.-H.; Wang, G.; Sun, C.; Li, P.; Fang, J.; He, L. Manipulating surface ligands of Copper Sulfide nanocrystals: Synthesis, characterization, and application to organic solar cells. J. Colloid Interface Sci. 2014, 419, 142–147. [Google Scholar] [CrossRef]
  82. Meyer, J.; Hamwi, S.; Kröger, M.; Kowalsky, W.; Riedl, T.; Kahn, A. Transition Metal Oxides for Organic Electronics: Energetics, Device Physics and Applications. Adv. Mater. 2012, 24, 5408–5427. [Google Scholar] [CrossRef]
  83. Park, H.H.; Larrabee, T.J.; Ruppalt, L.B.; Culbertson, J.C.; Prokes, S.M. Tunable Electrical Properties of Vanadium Oxide by HydrogenPlasma-Treated Atomic Layer Deposition. ACS Omega 2017, 2, 1259–1264. [Google Scholar] [CrossRef]
  84. Hwang, S.; Larina, L.; Lee, H.; Kim, S.; Choi, K.S.; Jeon, C.; Ahn, B.T.; Shin, B. Wet Pretreatment-Induced Modification of Cu(In,Ga)Se2/Cd-Free ZnTiO Buffer Interface. ACS Appl. Mater. Interfaces 2018, 10, 20920–20928. [Google Scholar] [CrossRef] [PubMed]
  85. Park, H.H.; Heasley, R.; Sun, L.; Steinmann, V.; Jaramillo, R.; Hartman, K.; Chakraborty, R.; Sinsermsuksakul, P.; Chua, D.; Buonassisi, T.; et al. Co-optimization of SnS absorber and Zn(O,S) buffer materials for improved solar cells. Prog. Photovolt. Res. Appl. 2015, 23, 901–908. [Google Scholar] [CrossRef] [Green Version]
  86. Park, H.H.; Kim, J.; Kim, G.; Jung, H.; Kim, S.; Moon, C.S.; Lee, S.J.; Shin, S.S.; Hao, X.; Yun, J.S.; et al. Transparent Electrodes Consisting of a Surface-Treated Buffer Layer Based on Tungsten Oxide for Semitransparent Perovskite Solar Cells and Four-Terminal Tandem Applications. Small Methods 2020, 4, 2000074. [Google Scholar] [CrossRef]
  87. Jung, H.; Kim, G.; Jang, G.S.; Lim, J.; Kim, M.; Moon, C.S.; Hao, X.; Jeon, N.J.; Yun, J.S.; Park, H.H.; et al. Transparent Electrodes with Enhanced Infrared Transmittance for Semitransparent and Four-Terminal Tandem Perovskite Solar Cells. ACS Appl. Mater. Interfaces 2021, 13, 30497–30503. [Google Scholar] [CrossRef] [PubMed]
  88. Park, H.H. Transparent Electrode Techniques for Semitransparent and Tandem Perovskite Solar Cells. Electron. Mater. Lett. 2021, 17, 1–15. [Google Scholar] [CrossRef]
  89. Park, H.H.; Song, S.; Seo, J. Perspective: Approaches for layers above the absorber in perovskite solar cells for semitransparent and tandem applications. Mater. Today Energy 2021, 21, 100729. [Google Scholar] [CrossRef]
Nanomaterials 12 00112 g001a 550Nanomaterials 12 00112 g001b 550
Figure 1. NiOx-incorporated PSCs: (a) Illustration of vertical recrystallization method. (b) Illuminated current density-voltage (J-V) scans of perovskite with various MACl treatments. (c) Stability comparison of pristine and MACl-treated FAPbI3 under 1 SUN light soaking at maximum power point tracking (MPPT) at ~25 °C or 85 °C. Reproduced from the work of [21] with permission from the Royal Society of Chemistry, 2017.
Figure 1. NiOx-incorporated PSCs: (a) Illustration of vertical recrystallization method. (b) Illuminated current density-voltage (J-V) scans of perovskite with various MACl treatments. (c) Stability comparison of pristine and MACl-treated FAPbI3 under 1 SUN light soaking at maximum power point tracking (MPPT) at ~25 °C or 85 °C. Reproduced from the work of [21] with permission from the Royal Society of Chemistry, 2017.
Nanomaterials 12 00112 g001aNanomaterials 12 00112 g001b
Nanomaterials 12 00112 g002a 550Nanomaterials 12 00112 g002b 550
Figure 2. NiOx-incorporated PSCs: (a) Schematic illustration of the band alignment and transfer process. (b) Illuminated J-V scans of PSCs with different electrodes. (c) Evolution of average photovoltaic performance parameters as a function of time at room temperature and (d) at a constant temperature of 60 °C. Reproduced from the work of [60], with permission from the American Chemical Society, 2018.
Figure 2. NiOx-incorporated PSCs: (a) Schematic illustration of the band alignment and transfer process. (b) Illuminated J-V scans of PSCs with different electrodes. (c) Evolution of average photovoltaic performance parameters as a function of time at room temperature and (d) at a constant temperature of 60 °C. Reproduced from the work of [60], with permission from the American Chemical Society, 2018.
Nanomaterials 12 00112 g002aNanomaterials 12 00112 g002b
Nanomaterials 12 00112 g003 550
Figure 3. NiOx-incorporated PSC: (a) Schematic illustration of the device structure. (b) Illuminated J-V scan of the champion device. Efficiency at the maximum power point (inset). (c) Efficiency (black), current density (JMPP, red), and voltage (VMPP, blue) for a single-junction PSC device with no encapsulation for 1000 h of MPPT. Reproduced from the work of [61], with permission from the Nature Publishing Group, 2017.
Figure 3. NiOx-incorporated PSC: (a) Schematic illustration of the device structure. (b) Illuminated J-V scan of the champion device. Efficiency at the maximum power point (inset). (c) Efficiency (black), current density (JMPP, red), and voltage (VMPP, blue) for a single-junction PSC device with no encapsulation for 1000 h of MPPT. Reproduced from the work of [61], with permission from the Nature Publishing Group, 2017.
Nanomaterials 12 00112 g003
Nanomaterials 12 00112 g004 550
Figure 4. NiOx-incorporated PSC: (a) Schematic illustration of the device structure. (b) Illuminated J-V scans of the champion device with various ETLs. (c) Efficiency evolution over 500 h for devices passivated with 50 nm of Al2O3 under continuous 1 SUN illumination with a 420 nm cutoff UV filter at room temperature in ambient air (20–60% relative humidity). (d) Efficiency evolution over 500 h for PSC with AZO and 50 nm of Al2O3 near the MPPT under 1 SUN illumination with a 420 nm cutoff UV filter at 85 °C in ambient air. Reproduced from [23], with permission from Wiley, 2018.
Figure 4. NiOx-incorporated PSC: (a) Schematic illustration of the device structure. (b) Illuminated J-V scans of the champion device with various ETLs. (c) Efficiency evolution over 500 h for devices passivated with 50 nm of Al2O3 under continuous 1 SUN illumination with a 420 nm cutoff UV filter at room temperature in ambient air (20–60% relative humidity). (d) Efficiency evolution over 500 h for PSC with AZO and 50 nm of Al2O3 near the MPPT under 1 SUN illumination with a 420 nm cutoff UV filter at 85 °C in ambient air. Reproduced from [23], with permission from Wiley, 2018.
Nanomaterials 12 00112 g004
Nanomaterials 12 00112 g005 550
Figure 5. CuSCN-incorporated PSC: (a) Cross-sectional scanning electron microscopy (SEM) of the PSC device stack. (b) Illuminated J-V scan of the champion device. The VOC vs. illumination intensity with an ideality factor of 1.50 (inset). (c) Efficiency evolution of unencapsulated devices at MPPT for 1000 h under 1 SUN at 60 °C in nitrogen. Reproduced from the work of [34], with permission from the American Association for the Advancement of Science, 2017.
Figure 5. CuSCN-incorporated PSC: (a) Cross-sectional scanning electron microscopy (SEM) of the PSC device stack. (b) Illuminated J-V scan of the champion device. The VOC vs. illumination intensity with an ideality factor of 1.50 (inset). (c) Efficiency evolution of unencapsulated devices at MPPT for 1000 h under 1 SUN at 60 °C in nitrogen. Reproduced from the work of [34], with permission from the American Association for the Advancement of Science, 2017.
Nanomaterials 12 00112 g005
Nanomaterials 12 00112 g006 550
Figure 6. CuI-incorporated PSC: (a) Energy level diagram of each layer in the PSC. (b) Illuminated J-V scan of the champion device. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere. Reproduced from the work of [36], with permission from the Royal Society of Chemistry, 2016.
Figure 6. CuI-incorporated PSC: (a) Energy level diagram of each layer in the PSC. (b) Illuminated J-V scan of the champion device. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere. Reproduced from the work of [36], with permission from the Royal Society of Chemistry, 2016.
Nanomaterials 12 00112 g006
Nanomaterials 12 00112 g007 550
Figure 7. CuOx-incorporated PSC: (a) Schematic illustration of the PSC device structure. (b) Illuminated J-V scan of the champion device. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere. Reproduced from the work of [38], with permission from the Royal Society of Chemistry, 2016.
Figure 7. CuOx-incorporated PSC: (a) Schematic illustration of the PSC device structure. (b) Illuminated J-V scan of the champion device. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere. Reproduced from the work of [38], with permission from the Royal Society of Chemistry, 2016.
Nanomaterials 12 00112 g007
Nanomaterials 12 00112 g008 550
Figure 8. Cu2O-incorporated PSC: (a) Schematic illustration of the band alignment and carrier extraction. (b) Illuminated J-V scans of the PSC with various HTLs. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere for over 30 days. Reproduced from the work of [41], with permission from Wiley, 2019.
Figure 8. Cu2O-incorporated PSC: (a) Schematic illustration of the band alignment and carrier extraction. (b) Illuminated J-V scans of the PSC with various HTLs. (c) Efficiency evolution of unencapsulated devices in ambient atmosphere for over 30 days. Reproduced from the work of [41], with permission from Wiley, 2019.
Nanomaterials 12 00112 g008
Nanomaterials 12 00112 g009a 550Nanomaterials 12 00112 g009b 550
Figure 9. Cu2O-CuSCN-incorporated PSC: (a) Schematic illustration of the device architecture. (b) Illuminated J-V scans of the PSC with various HTLs. (c) Efficiency evolution of encapsulated devices for over 720 h at 85 °C, 85% relative humidity. Reproduced from the work of [42], with permission from the American Chemical Society, 2020.
Figure 9. Cu2O-CuSCN-incorporated PSC: (a) Schematic illustration of the device architecture. (b) Illuminated J-V scans of the PSC with various HTLs. (c) Efficiency evolution of encapsulated devices for over 720 h at 85 °C, 85% relative humidity. Reproduced from the work of [42], with permission from the American Chemical Society, 2020.
Nanomaterials 12 00112 g009aNanomaterials 12 00112 g009b
Nanomaterials 12 00112 g010 550
Figure 10. CuCrO2-incorporated PSC: (a) Schematic illustration of the device architecture and band energy levels. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Efficiency evolution of unencapsulated devices for over 60 days under ambient conditions at room temperature and >40% relative humidity. Reproduced from the work of [12], with permission from the Royal Society of Chemistry, 2018.
Figure 10. CuCrO2-incorporated PSC: (a) Schematic illustration of the device architecture and band energy levels. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Efficiency evolution of unencapsulated devices for over 60 days under ambient conditions at room temperature and >40% relative humidity. Reproduced from the work of [12], with permission from the Royal Society of Chemistry, 2018.
Nanomaterials 12 00112 g010
Nanomaterials 12 00112 g011a 550Nanomaterials 12 00112 g011b 550
Figure 11. CuCrO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Efficiency evolution of unencapsulated devices under 1 SUN in an argon atmosphere. Reproduced from the work of [44], with permission from Wiley, 2018.
Figure 11. CuCrO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Efficiency evolution of unencapsulated devices under 1 SUN in an argon atmosphere. Reproduced from the work of [44], with permission from Wiley, 2018.
Nanomaterials 12 00112 g011aNanomaterials 12 00112 g011b
Nanomaterials 12 00112 g012a 550Nanomaterials 12 00112 g012b 550
Figure 12. CuGaO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Normalized efficiency evolution of unencapsulated devices under ambient atmosphere (25 °C, 30–55% relative humidity). Reproduced from the work of [47], with permission from Wiley, 2017.
Figure 12. CuGaO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Normalized efficiency evolution of unencapsulated devices under ambient atmosphere (25 °C, 30–55% relative humidity). Reproduced from the work of [47], with permission from Wiley, 2017.
Nanomaterials 12 00112 g012aNanomaterials 12 00112 g012b
Nanomaterials 12 00112 g013 550
Figure 13. Mesoporous-CuGaO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with different HTLs. (c) Normalized efficiency evolution of unencapsulated devices at 85 °C in a nitrogen atmosphere. Reproduced from the work of [48], with permission from Wiley, 2018.
Figure 13. Mesoporous-CuGaO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with different HTLs. (c) Normalized efficiency evolution of unencapsulated devices at 85 °C in a nitrogen atmosphere. Reproduced from the work of [48], with permission from Wiley, 2018.
Nanomaterials 12 00112 g013
Nanomaterials 12 00112 g014a 550Nanomaterials 12 00112 g014b 550
Figure 14. CuFeO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with different HTLs. (c) Normalized PCE evolution of unencapsulated devices under continuous 1 SUN illumination, MPPT in a nitrogen atmosphere. Normalized PCE decay over time in various (d) humidity and (e) temperature conditions. Reproduced from the work of [49], with permission from the American Chemical Society, 2019.
Figure 14. CuFeO2-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scans of the champion cells with different HTLs. (c) Normalized PCE evolution of unencapsulated devices under continuous 1 SUN illumination, MPPT in a nitrogen atmosphere. Normalized PCE decay over time in various (d) humidity and (e) temperature conditions. Reproduced from the work of [49], with permission from the American Chemical Society, 2019.
Nanomaterials 12 00112 g014aNanomaterials 12 00112 g014b
Nanomaterials 12 00112 g015a 550Nanomaterials 12 00112 g015b 550
Figure 15. CuS-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scan of the champion cell. (c) Normalized PCE evolution of unencapsulated devices as a function of storage time in ambient air for PSCs with various HTLs. Reproduced from the work of [50], with permission from the American Chemical Society, 2016.
Figure 15. CuS-incorporated PSC: (a) Energy band diagram with respect to the vacuum level. (b) Illuminated J-V scan of the champion cell. (c) Normalized PCE evolution of unencapsulated devices as a function of storage time in ambient air for PSCs with various HTLs. Reproduced from the work of [50], with permission from the American Chemical Society, 2016.
Nanomaterials 12 00112 g015aNanomaterials 12 00112 g015b
Nanomaterials 12 00112 g016a 550Nanomaterials 12 00112 g016b 550
Figure 16. LiCoO2-incorporated PSC: (a) Schematic illustration of fabrication steps of PSC with LiCoO2 as the HTL. (b) Illuminated J-V scans of the champion cell. (c) Normalized PCE evolution of unencapsulated devices as a function of storage time with various temperatures in an inert atmosphere. Reproduced from the work of [53], with permission from the Royal Society of Chemistry, 2018.
Figure 16. LiCoO2-incorporated PSC: (a) Schematic illustration of fabrication steps of PSC with LiCoO2 as the HTL. (b) Illuminated J-V scans of the champion cell. (c) Normalized PCE evolution of unencapsulated devices as a function of storage time with various temperatures in an inert atmosphere. Reproduced from the work of [53], with permission from the Royal Society of Chemistry, 2018.
Nanomaterials 12 00112 g016aNanomaterials 12 00112 g016b
Nanomaterials 12 00112 g017a 550Nanomaterials 12 00112 g017b 550
Figure 17. Cu:CrOx-incorporated PSC: (a) Cross-sectional SEM of PSC device stack. (b) J-V scans of the champion cells with various HTLs. (c) Normalized PCE evolution of unencapsulated devices as a function of storage in a dry box with 30% relative humidity at 20 °C. Reproduced from the work of [54], with permission from Elsevier, 2018.
Figure 17. Cu:CrOx-incorporated PSC: (a) Cross-sectional SEM of PSC device stack. (b) J-V scans of the champion cells with various HTLs. (c) Normalized PCE evolution of unencapsulated devices as a function of storage in a dry box with 30% relative humidity at 20 °C. Reproduced from the work of [54], with permission from Elsevier, 2018.
Nanomaterials 12 00112 g017aNanomaterials 12 00112 g017b
Nanomaterials 12 00112 g018 550
Figure 18. Cs:VOx-incorporated PSC: (a) Illustration of the PSC device stack. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Normalized PCE evolution as a function of storage time in ambient air with 10–20% relative humidity at 25–30 °C for devices without encapsulation. Reproduced from the work of [59] (https://pubs.acs.org/doi/abs/10.1021/acsomega.7b01944 accessed on 15 December 2021), with permission from the American Chemical Society, 2018.
Figure 18. Cs:VOx-incorporated PSC: (a) Illustration of the PSC device stack. (b) Illuminated J-V scans of the champion cells with various HTLs. (c) Normalized PCE evolution as a function of storage time in ambient air with 10–20% relative humidity at 25–30 °C for devices without encapsulation. Reproduced from the work of [59] (https://pubs.acs.org/doi/abs/10.1021/acsomega.7b01944 accessed on 15 December 2021), with permission from the American Chemical Society, 2018.
Nanomaterials 12 00112 g018
Table
Table 1. Summary of inorganic HTL-based perovskite solar cells.
Table 1. Summary of inorganic HTL-based perovskite solar cells.
MaterialMethodStructureDevice StackJSC
(mA/cm2)		VOC
(V)		FF
(%)		η
(%)		Institute, Year [Ref]
NiOSputteringn-i-pFTO/TiO2/MAPbI3−xClx/NiOx/Ni17.90.7753.07.3TMU, 2015 [17]
NiOSpin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/MAPbI3−xClx/NiOx/Au19.50.8853.19.1Peking, 2017 [18]
NiOPLDp-i-nITO/NiOx/MAPbI3/PCBM/LiF/Al20.21.0681.317.3KRICT, 2015 [19]
NiOSolution Processp-i-nITO/NiOx/MAPbI3/C60/Bis-C60/Ag21.81.0378.417.6Hong Kong UST, UW, 2016 [20]
Li,Mg:NiOxSpray Coatingp-i-nFTO/Li,Mg:NiOx/FAPbI3/PCBM/TiOx/Ag23.11.1081.420.7NIMS, 2017 [21]
NiOSpatial ALDp-i-nITO/NiOx/FA0.2MA0.8PbI3/PC61BM/Al 23.01.0881.017.1Cambridge, 2018 [22]
NiO ALDp-i-nFTO/NiO/Cs0.05MA0.95PbI3/PCBM/BCP/AZO/Ag/Al2O322.51.0380.818.8SKKU, 2018 [23]
NiOPEALDp-i-nITO/NiO/Cs0.05(FA0.83MA0.17)Pb(I0.83Br0.17)3/C60/BCP/Cu21.81.0773.417.1Eindhoven, 2019 [24]
Cu:NiOxCombustion sol-gelp-i-nITO/Cu:NiOx/MAPbI3/Bis-C60/C60/Ag22.21.0576.017.7UW, 2015 [25]
Cu:NiOxSpin Coatingp-i-nFTO/Cu:NiOx/MAPbI3−xClx/PC61BM/ZrAcac/Al23.71.1277.120.1CAS, 2017 [26]
Li0.05Mg0.15Ni0.8OSpray Pyrolysisp-i-nFTO/Li0.05Mg0.15Ni0.8O/MAPbI3/Ti(Nb)Ox/Ag22.81.1177.119.6NIMS, 2017 [27]
Li:NiOxSpin Coatingp-i-nITO/Li:NiOx/MAPbI3−xClx/PCBM/Al21.81.1273.618.0Los Alamos, 2018 [28]
Cs:NiOxSpin Coatingp-i-nFTO/Cs:NiOx/MAPbI3/PCBM/ZrAcac/Ag21.81.1279.319.4Southern UST, 2017 [29]
Mg:NiOxSputteringp-i-nITO/Mg:NiOx/MAPbI3/PCBM/ZnMgO/Al21.31.0879.018.2Hong Kong UST,2017 [30]
Co:NiOxSpin Coatingp-i-nFTO/Co:NiOx/MAPbI3/PCBM/Ag20.51.0979.817.8NTU, 2020 [31]
CuSCNDoctor bladingn-i-pFTO/bl-TiO2/mp-TiO2/(FAPbI3)0.85(MAPbBr3)0.15/CuSCN/Au21.81.1069.016.6EPFL, 2016 [32]
CuSCNSpin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/(FAPbI3)0.85(MAPbBr3)0.15/CuSCN/Au23.11.0475.318.0UNIST, 2016 [33]
CuSCNSpin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/CsFAMAPbI3−xBrx/CuSCN/rGO/Au23.41.1477.520.4EPFL, 2017 [34]
CuIRapid Doctor Bladingn-i-pFTO/bl-TiO2/MAPbI3/CuI/Graphite16.70.7857.07.5Monash, 2015 [35]
CuISpin Coatingp-i-nITO/CuI/MAPbI3/C60/BCP/Ag22.81.0173.016.8Peking, 2016 [36]
CuI-CuSCNElectrodepositionp-i-nITO/CuI/CuSCN/MAPbI3/PC61BM/C20.31.1078.020.4Allagappa, 2021 [37]
CuOxSpin Coatingp-i-nITO/CuOx/MAPbI3/C60/BCP/Ag23.20.9974.417.1Peking 2016 [38]
CuOxSpin Coatingp-i-nFTO/CuOx/MAPbI3−xClx/PCBM/C60/BCP/Ag22.51.1175.819.0Peking, 2016 [39]
CuOxSpin Coatingp-i-nITO/CuOx/MAPbI3/PC61BM/ZnO/Al22.41.0376.017.4Zhejiang, 2017 [40]
Cu2O QDSpin Coatingn-i-pFTO/bl-TiO2/Cs0.05FA0.81MA0.14PbI2.55Br0.45/Cu2O/Au22.21.1574.218.9Southern UST, 2019 [41]
Cu2O-CuSCNSpin Coatingn-i-pITO/SnO2/Cs0.05(FA0.85MA0.15)0.95PbI2.55Br0.45/Cu2O-CuSCN/Au23.21.0578.419.2SNU, 2020 [42]
CuAlO2Sputteringp-i-nITO/CuAlO2/PEDOT:PSS/MAPbI3−xClx/PCBM/Ag22.00.8875.014.5Soochow, 2016 [43]
CuCrO2Spin Coatingp-i-nITO/CuCrO2/MAPbI3/PCBM/BCP/Ag21.91.0781.019.0City Univ. Hong Kong, 2018 [44]
CuCrO2Spin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/Cs0.05(MA0.15FA0.85)0.95Pb(I0.85Br0.15)3/CuCrO2/ Au23.21.0469.016.7Mehmetbey, 2018 [12]
Mg: CuCrO2Spin Coatingp-i-nFTO/Mg: CuCrO2/MAPbI3/PCBM/BCP/Ag18.41.0071.313.1SKKU, 2018 [45]
Mg: CuCrO2Spin Coatingp-i-nITO/Mg: CuCrO2/MAPbI3/C60/BCP/Ag19.41.0171.914.1UT Dallas, 2019 [46]
CuGaO2Spin Coatingn-i-pFTO/bl-TiO2/MAPbI3−xClx/CuGaO2/Au21.71.1177.018.5UW, 2017 [47]
CuGaO2Spin Coatingp-i-nFTO/NiOx/mp-CuGaO2/CsFAPb(I,Br)3/PC61BM/BCP/Ag22.21.1380.020.0Shanxi Normal Univ., 2018 [48]
CuFeO2Spin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/CsFAMA/CuFeO2/Au23.61.0165.015.6KMU, 2019 [49]
CuSSpin Coatingp-i-nITO/CuS/MAPbI3/C60/BCP/Ag22.31.0271.216.2BNL, 2016 [50]
CoOxSpin Coatingp-i-nITO/CoOx/MAPbI3/PCBM/Ag20.30.9575.514.5Hokkaido Univ., 2016 [51]
Co3O4Screen Printingn-i-pFTO/bl-TiO2/mp-TiO2/ZrO2/MAPbI3/Co3O4/C23.40.8864.013.3NTU, 2018 [52]
LiCoO2Sputteringp-i-nITO/LiCoO2/MAPbI3/C60/BCP/Ag22.51.0680.019.1NCU, 2018 [53]
Cu:CrOxSpin Coatingp-i-nFTO/Cu:CrOx/MAPbI3/PCBM/BCP/Ag21.41.0876.017.7Wuhan Univ., 2018 [54]
MoOxThermal Evaporationp-i-nITO/MoO3/MAPbI3/PCBM/Ag18.80.9971.013.1NTUT, 2016 [55]
Ti:MoO2Spin Coatingn-i-pFTO/bl-TiO2/mp-TiO2/MAPbI3/Ti:MoO2/Au20.11.0277.315.8Kyung Hee Univ., 2017 [56]
MoOx:RGOSpin Coatingp-i-nITO/MoOx:RGO/MAPbI3/PCBM/BCP/Ag21.01.1277.018.2NU, 2020 [57]
VOxPost-Treatmentn-i-pFTO/bl-TiO2/mp-TiO2/ZrO2/MAPbI3/VOx/C24.20.9568.515.8Huazhong UST, 2019 [58]
Cs:VOxSpun-Castp-i-nITO/Cs:VOx/MAPbI3/PC61BM/BCP/Ag20.70.9276.514.5South China Univ. Tech., 2018 [59]
Table
Table 2. Summary of stability of inorganic HTL-based perovskite solar cells.
Table 2. Summary of stability of inorganic HTL-based perovskite solar cells.
HTLDevice StackEncapsulatedConditionsContinuous 1 SUN Illumination?Durationη
Maintained		Institute, Year [Ref]
NiOxFTO/NiOx/MAPbI3/PCBM/CNT:PEIY60 °C, 60% N500 h85%Tsinghua, 2018 [60]
NiOxITO/NiO/Cs0.17FA0.83Pb(Br0.17I0.83)3/LiF/PC60BM/SnO2/ZnSnOx/ITO/LiF/AgN35 °C, 40%, MPPTY1000 h100%Stanford, 2017 [61]
NiOxFTO/NiOx/Cs0.05MA0.95PbI3/PCBM/BCP/ ALD-AZO/AgYRT, 20–60%,/85 °C, MPPTY500 h99.5/87%SKKU, 2018 [23]
Li,Mg:NiOxFTO/Li,Mg:NiOx/FAPbI3/PCBM/TiOx/AgYRT, MPPTY500 h>85%NIMS, 2017 [21]
CuSCNFTO/bl-TiO2/mp-TiO2/CsFAMAPbI3–xBrx/CuSCN/rGO/AuN60 °C, N2, MPPTY1000 h>95%EPFL, 2017 [34]
CuIITO/CuI/MAPbI3/C60/BCP/AgN25%, RTN300 h93%Peking, 2016 [36]
CuOxITO/CuOx/MAPbI3/C60/BCP/AgNAirN200 h~90%Peking, 2016 [38]
Cu2O QDFTO/bl-TiO2/Cs0.05FA0.81MA0.14PbI2.55Br0.45/Cu2O/AuN30%, AirN720 h>90%Southern UST, 2019 [41]
Cu2O-CuSCNITO/SnO2/Cs0.05(FA0.85MA0.15)0.95PbI2.55Br0.45/Cu2O-CuSCN/AuY85 °C, 85%N720 h>90%SNU, 2020 [42]
CuCrO2ITO/CuCrO2/MAPbI3/PCBM/BCP/AgNArY1000 h~95%City Univ. Hong Kong, 2018 [44]
CuCrO2FTO/bl-TiO2/mp-TiO2/Cs0.05(MA0.15FA0.85)0.95Pb(I0.85Br0.15)3/ CuCrO2/ AuNRT, N2, MPPTY500 h88%Mehmetbey, 2018 [12]
CuGaO2FTO/NiOx/mp-CuGaO2/CsFAPb(I,Br)3/PC61BM/BCP/AgN85 °C, N2,N1000 h>80%Shanxi Normal Univ., 2018 [48]
CuGaO2FTO/bl-TiO2/MAPbI3−xClx/CuGaO2/AuN25 °C, 30–55%, N720 h>90%UW, 2017 [47]
CuFeO2FTO/bl-TiO2/mp-TiO2/CsFAMA/CuFeO2/AuNN2, MPPTY1000 h85%KMU, 2019 [49]
CuSITO/CuS/MAPbI3/C60/BCP/AgNAirN260 h>90%BNL, 2016 [50]
LiCoO2ITO/LiCoO2/MAPbI3/C60/BCP/AgN90 °C, Inert AtmosphereN120 h>90%NCU, 2018 [53]
Cu:CrOxFTO/Cu:CrOx/MAPbI3/PCBM/BCP/AgN20 °C, 30%,N190 h>70%Wuhan Univ., 2018 [54]
Cs:VOxITO/Cs:VOx/MAPbI3/PC61BM/BCP/AgNRT, 50–70%, AirN720 h94%South China Univ. Tech., 2018 [59]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Park, H.H. Efficient and Stable Perovskite Solar Cells Based on Inorganic Hole Transport Materials. Nanomaterials 2022, 12, 112. https://doi.org/10.3390/nano12010112

AMA Style

Park HH. Efficient and Stable Perovskite Solar Cells Based on Inorganic Hole Transport Materials. Nanomaterials. 2022; 12(1):112. https://doi.org/10.3390/nano12010112

Chicago/Turabian Style

Park, Helen Hejin. 2022. "Efficient and Stable Perovskite Solar Cells Based on Inorganic Hole Transport Materials" Nanomaterials 12, no. 1: 112. https://doi.org/10.3390/nano12010112

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop