Epitaxial Integration of Dirac Semimetals with Si(001)
Next Article in Special Issue
Structure and Anharmonicity of α- and β-Sb2O3 at Low Temperature
Previous Article in Journal
Friction Stir Welding of Non-Heat Treatable Al Alloys: Challenges and Improvements Opportunities
Previous Article in Special Issue
Characterization, Kinetic Using Deconvolution Techniques and Thermodynamic Study of Synthetic MgHPO4·3H2O
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Photocatalytic Azo Dye Degradation Using Graphite Carbon Nitride Photocatalyst and UV-A Irradiation

1
Chemistry Department, Faculty of Science, University of Ha’il, P.O. Box 2440, Ha’il 81451, Saudi Arabia
2
Bharat Ratna Prof. CNR Rao Research Centre, P. G. Department of Chemistry, Basaveshwar Science College, Bagalkot 587101, India
3
Department of Engineering Physics, K.L.E Institute of Technology, Hubballi 580030, India
4
School of Mechanical Engineering, KLE Technological University, Vidya Nagar, Hubballi 580031, India
5
Center of Excellence for Advanced Materials Research, King Abdulaziz University, Jeddah 21589, Saudi Arabia
6
Department of Chemistry, Faculty of Science, Motherhood University, Roorkee 247661, India
7
School of Chemical Engineering, Dr. Vishwanath Karad MIT World Peace University, Pune 411038, India
8
Department of Chemistry, School of Engineering, Presidency University, Bangalore 560064, India
9
Department of Chemistry, Bharath Institute of Higher Education and Research (BIHER), Selaiyur, Chennai 600073, India
*
Author to whom correspondence should be addressed.
Crystals 2023, 13(4), 577; https://doi.org/10.3390/cryst13040577
Submission received: 27 February 2023 / Revised: 21 March 2023 / Accepted: 23 March 2023 / Published: 28 March 2023
(This article belongs to the Special Issue Recent Developments of Inorganic Crystalline Materials)

Abstract

:
The photocatalytic degradation of Acid Red 26 was examined utilizing a graphitic carbon nitride (g-C3N4) catalyst and a UV-A light in this study. We investigated how successfully the photocatalytic approach removed Acid Red 26 from synthetic and actual municipal wastewater. Both aqueous matrices allowed for extremely high clearance rates. Wastewater degraded at a slower rate than the other matrices, this might be ascribed to the wastewater’s complicated chemical composition. Using a liquid chromatography-mass spectrometry (LC-MS), the IPs in both synthetic and actual municipal effluent were determined. The photocatalytic degradation mechanisms of Acid Red 26 are hypothesised to comprise oxidation, dealkylation, and methoxy group cleavage based on the observed intermediate products (IPs). Using proven scavengers, we were also able to investigate the role of reactive species in the degradation process and illustrate the significance of h+ and O2 in the reaction. Chlorococcum sp. and Dunaliella tertiolecta microalgae were also utilised to assess the development of ecotoxicity. We observed low toxicity throughout the process when clean water was used as the matrix, with no production of hazardous IPs. In the case of actual municipal wastewater, there was an early rise in toxicity, which scientists believe was caused by the matrix’s chemical make-up. To lower the toxicity, a heterogeneous photocatalysis was used, and at the end of the treatment, nearly full detoxification was obtained.

1. Introduction

Aquatic pollution can be derived from chemicals that are released into water bodies through various sources, such as industrial effluents, agricultural runoff, textile industry, hazardous dye waste, and household waste. Chemical pollution can harm aquatic organisms, ecosystems, and human health. Heavy metals, insecticides, medicines, and industrial chemicals are some of the most frequent chemical contaminants encountered in aquatic habitats. Heavy metals, such as mercury, lead, and cadmium are hazardous to aquatic organisms and can build up in the food chain, causing biomagnification. Pesticides, such as herbicides and insecticides, can harm aquatic creatures and disrupt the ecosystem’s balance [1,2]. Pharmaceuticals and personal care items, such as antibiotics and hormones, can also infiltrate bodies of water and impact aquatic organisms, and the long-term implications of low-level exposure to these chemicals remain unknown. Industrial chemicals, such as polychlorinated biphenyls (PCBs) and dioxins are persistent organic pollutants that can linger in the environment for a long time and harm aquatic organisms and human health [3,4]. Chemical pollution prevention and control necessitate effective management and regulation of their use and disposal, the development and use of safer alternatives, and the adoption of treatment technologies to remove these pollutants from bodies of water. Furthermore, public awareness and education are required to decrease inappropriate chemical disposal and encourage responsible environmental practices. Pharmaceutical and textile chemical species enter aquatic systems in amounts ranging from ng/L to μg/L; yet, even at such low levels, they pose a toxicological hazard to live species [5,6].
Azo dyes are synthetic dyes with one or more azo groups (-N=N-) as the chromophore, giving them their distinctive colours [6]. They are frequently utilised as colourants in the textile, food, cosmetic, and pharmaceutical industries. Azo dyes are poisonous, and some of them can induce allergic responses or cancer; hence, their usage is strictly regulated in many countries. Azo dyes contribute significantly to water contamination, particularly in underdeveloped nations where laws are low or non-existent [7,8]. Azo dyes can linger in the environment for a long time and are potentially hazardous to aquatic life. Moreover, some azo dyes can degrade into aromatic amines, which are carcinogenic and may endanger human health. To address the issue of azo dye pollution, some governments have imposed restrictions on the use of these dyes and efforts to create safer and more sustainable alternatives are ongoing [9,10,11,12].
Acid Red 26 is a synthetic azo dye that is widely used as a colorant in a variety of industries, such as textiles, leather, paper, and food. Acid Red A, Acid Brilliant Scarlet 3R, and C.I. 16150 are some of the alternative names for it. Acid Red 26 is a water-soluble dye that is typically red to reddish-brown in colour but when combined with other dyes, it can generate pink and orange shades [13,14]. Acid Red 26, similar to other azo dyes, has been linked to environmental pollution and probable health hazards, and its usage is restricted in several countries. Acid Red 26 is deemed environmentally harmful due to its ability to produce contamination and harm to aquatic life. When released into bodies of water, it might persist for long periods of time and may not decompose easily, potentially leading to bioaccumulation in the food chain. Furthermore, Acid Red 26 may cause oxygen depletion in bodies of water, which can result in the death of fish and other aquatic species. Many countries control its usage and discharge into the environment in order to prevent or lessen these negative consequences [15,16,17].
Acid Red 26 can be broken down in a variety of ways, including biological, chemical, and physical processes. Biodegradation, for example, uses microorganisms to break down the colour into less hazardous chemicals. Chemical processes, such as ozonation, advanced oxidation, and reduction can also degrade the dye by destroying the azo link, which is responsible for its colour [18,19,20]. Adsorption and membrane filtration, for example, can remove colour from the water by trapping it on a surface or selectively permitting it to pass through a membrane. However, the efficiency of these procedures is affected by a number of parameters, including the starting dye concentration, the type of water matrix, and the treatment circumstances [21]. As a result, while selecting a suitable degradation method for Acid Red 26, these variables, as well as the potential environmental impact of the degradation products, should be taken into account.
Acid Red 26 is photodegradable, which means it can be broken down into less dangerous chemicals using light. Acid Red 26 photodegradation usually includes the use of ultraviolet (UV) radiation, which can cleave the azo link, resulting in the production of smaller, less complicated molecules [22]. The starting concentration of the dye, the intensity and wavelength of the light, the presence of additional chemicals in the aqueous matrix, and the kind and concentration of the photocatalyst all influence photodegradation efficiency. While photodegradation can be a successful method for treating Acid Red 26 in water, it should be used with caution due to the potential environmental impact of the degradation products as well as the safety of the UV light and the photocatalysts [23].
A multilayer polymeric semiconductor, g-C3N4, is made up of carbon, nitrogen, and hydrogen atoms that are metal-free. Because of its unusual electrical and optical properties, it is a promising material for a variety of applications, such as photocatalysis, energy conversion, and optoelectronics [24]. As g-C3N4 absorbs visible light, it is an effective photocatalyst for the breakdown of organic contaminants and the creation of hydrogen from water. Furthermore, g-C3N4 is stable, non-toxic, and simple to synthesise using low-cost precursors, making it an appealing alternative to the standard photocatalysts, such as TiO2 [25]. However, characteristics, such as its shape, crystallinity, and surface qualities, which vary according on the synthesis method utilised, can have an impact on its performance and stability.
Due to its unusual electrical and optical properties, g-C3N4 has been widely researched as a catalyst for numerous chemical reactions, including photocatalysis. Additionally, g-C3N4 can absorb visible light as a photocatalyst, allowing it to stimulate the breakdown of organic contaminants, the creation of hydrogen from water, and other photo-driven reactions [26,27]. Furthermore, g-C3N4 can operate as a heterogeneous catalyst for a variety of chemical transformations under heat circumstances, including alcohol oxidation, amination, and coupling reactions. Modifying the surface characteristics of g-C3N4 as a catalyst, doping with other elements, or creating composite materials with other catalysts or supports can all improve its efficacy as a catalyst. However, issues, such as a limited catalytic activity, poor stability, and difficulty in large-scale synthesis remain, necessitating additional study and development [28,29,30,31].
In addition, g-C3N4 has demonstrated considerable promise as a photocatalyst in a variety of environmental and energy applications [28,29,30,31,32]. As a photocatalyst, g-C3N4 may absorb visible light, allowing it to enhance photo-driven processes, such as organic pollutant degradation, hydrogen synthesis from water, and carbon dioxide reduction. The use of g-C3N4 as a photocatalyst has a number of advantages, including non-toxicity, low cost, and stability in ambient circumstances [33]. Furthermore, by altering its structure, such as doping with other elements, its bandgap energy can be altered, which can improve its photocatalytic performance [34]. However, the photocatalytic efficacy of g-C3N4 can be influenced by parameters, such as crystallinity, shape, and surface characteristics, which can vary depending on the synthesis process used [35]. Researchers have also investigated the formation of g-C3N4-based composite materials with other photocatalysts or supports to improve their photocatalytic efficiency. Overall, the use of g-C3N4 as a photocatalyst is a promising field of research that has the potential to help develop sustainable and clean energy systems [35].
When it comes to photodegradation of reactive azo dyes, ultraviolet (UV) radiation outperforms visible light in several ways. As UV radiation has more energy than visible light, it can more easily break the chemical bonds between the dye molecules and release the dye. This improves its ability to decompose the colour into less hazardous chemicals. The fact that UV light is absorbed by the dye molecules’ chromophoric groups promotes photodegradation of reactive azo dyes. Additionally, because of its selectivity, the dye may be degraded faster and with less energy lost due to unintended reactions. UV light can quickly destroy reactive azo dyes, usually within minutes or hours, depending on the strength of the radiation and the dye’s properties. Its rapid breakdown may reduce the treatment’s duration and power requirements, making it less expensive [36]. There are no waste products: As far as we know, UV photodegradation does not produce any toxic by-products that could endanger wildlife or humans. This guarantees that the method can be used without fear of polluting or contaminating the environment. To sum up, UV radiation’s benefits make it a viable approach for the photodegradation of reactive azo dyes, especially in industrial and wastewater treatment applications where vast quantities of dye-contaminated water need to be treated rapidly and effectively [37,38].
However, the ecotoxicity assessment of the photocatalytic treatment, identification of the intermediate products (IPs), and use of g-C3N4 catalysts for AR-26 azo dye degradation under different matrix environments have yet to be explored. The major goal of this study was to see if a g-C3N4 catalyst could be utilised to photocatalyze the degradation of the AR-26 azo dye in the presence of UV-A irradiation, and if so, what IPs were formed. The toxicity was further assessed using the microalgae Chlorococcum sp. and Dunaliella tertiolecta. Furthermore, the function of the reactive species in degradation was assessed.

2. Materials and Methods

2.1. Chemicals and Reagents

We obtained our azo dye Acid Red 26 from Loba Chemie (Mumbai, India). The photocatalyst in this case was graphitic carbon nitride (g-C3N4) [8,32]. The physical properties of the graphite carbon nitride measured in the laboratory are tabulated in Table 1; these were thought to be important for this study. As for the solvents, Fisher Chemical provided HPLC-grade acetonitrile, isopropanol, methanol, and water (Mumbai, India). p-benzoquinone, formic acid, Cyanobacteria BG-11 were provided by Freshwater Solution, and Guillard’s (F/2) Marine Water Enrichment Solution was obtained from Sigma-Aldrich (Bangalore, India). We used purified water and treated wastewater matrices. Table 2 lists some of the properties of the wastewater measured in the laboratory. The remaining reagents were all of analytical quality. Throughout the experiment, double-distilled water was used.

2.2. Photocatalytic Experiments

Experiments on photocatalysis were carried out utilising a setup that includes four Philips black light tubes (with a peak emission of 356 nm). The photoreactor was a 250 mL cylindrical quartz cell. The 100 mL of reference sample and pollutant samples were taken for the experiment. A typical experiment included the following parameters: [AR-24]0 = 1 mg/L; [g-C3N4] = 300 mg/L. To reach the adsorption equilibrium, the suspensions were maintained in the dark for 45 min prior to initiating the radiation. Under these conditions, the actinometer potassium ferroxalate was utilised on a regular basis to determine that the photon flux (I0) entering the solution was 1.1 ± 0.03 μEinstein/s [39,40]. The catalyst particles were collected and discarded using a PVDF membrane filter with 0.22 m pore size (Millex-GV).

2.3. Scavenging Experiments

Scavengers, similar to isopropanol, p-benzoquinone, and methanol are frequently used to identify reactive oxygen species (ROS) in chemical reactions. The ability of these scavengers to quench or scavenge specific ROS can be evaluated by adding them at specific concentrations, and the contribution of each ROS to the degradation process can be determined. In this case, isopropanol is frequently used to scavenge hydroxyl radicals (HO), p-benzoquinone for superoxide anion radicals (O2•−), and methanol for positive holes (h+). We can determine the relative contribution of each ROS to the degradation by adding these scavengers at specified concentrations and evaluating the degradation process. The contribution of hydroxyl radicals (HO), superoxide anion radicals (O2), and positive holes (h+) in the decomposition processes was explored by using scavengers, such as isopropanol (0.1 M), p-benzoquinone (0.2 mM), and methanol (0.1 M) [41].

2.4. Analytical Methods

Using a Dionex (Make: Thermo Scientific, Waltham, MA, USA, Model: Ultimate 3000 UHPLC) equipped with an AcclaimTM RSLC 120 C18 capillary column, the amount of Acid Red 26 in the sample was computed (Thermo Scientific, Waltham, MA, USA). The mobile phase consisted of 0.15 mL/min of acetonitrile (80%) and distilled water containing 0.1% formic acid (20%) at a constant flow rate. This detection was conducted at the maximum pollutant λmax concentration.

2.5. HPLC/MS Analysis

The HPLC-MS is a useful analytical tool for analysing photodegradation products in a variety of matrices, including environmental samples, polymers, pharmaceuticals, and food. Photodegradation is the breakdown of molecules under the influence of light, which can result in the formation of a variety of photoproducts. The HPLC-MS technique is used to identify and quantify photodegradation products as well as to assess the degree of degradation. The technique involves using high-performance liquid chromatography (HPLC) to separate the photodegradation products and then using mass spectrometry to detect the individual components (MS). Using an ion trap mass spectrometer (Bruker, Billerica, MA, USA) attached to an HPLC/MS system (Cecil Instruments Limited, Bath, BA2 9AP, London, UK) allowed us to identify the presence of IPs in the samples.

2.6. Algal Biotest

The bioassays were carried out on Chlorococcum sp. (strain SAG 22.83) and Dunaliella tertiolecta (CCAP19/6B) under sterile conditions and constant lighting according to the OECD 201 protocol [35] (4300 lux). Freshwater (BG-11) and saltwater (F/2) algae were cultured. The tests began with a consistent supply of logarithmic growth cells (1 × 104 cells/mL), which was maintained by transferring stock algal cultures to conical flasks using the appropriate media (final volume 100 mL). At each stage, samples were collected and examined in duplicate cultures for 96 h while being constantly stirred. The cells were counted using a Neubauer haemocytometer. The growth rate (μ) and the percentage of the growth rate inhibition were then computed. The data are presented in the form of a mean standard deviation.

2.7. UV-Visible Spectrophotometric Analysis

The photodegradation of the dye can be monitored by measuring changes in the absorbance spectrum of the solution over time. Typically, the absorbance of the dye at a specific wavelength is measured at regular intervals, and the percentage degradation of the dye is calculated based on the decrease in absorbance over time. The UV-Visible spectroscopy is a useful technique for a photodegradation analysis of dyes because it is a non-destructive, non-invasive, and highly sensitive method. Additionally, it is relatively easy to perform, and the equipment required is widely available in many laboratories [42].
The reaction mixture was pipetted out and analysed for composition at regular intervals. To track the reaction development, spectrophotometric (Make: Systronics, Model: 118, Mumbai, India) measurements were obtained at the maximum of the reaction mixture using a spectrometric quartz cell (1 cm in path length). As the reaction develops, the absorbance of the reaction mixture decreases. According to the Beer–Lambert rule, a dye’s absorbance is proportional to its concentration.
A = e c l
where e is the molar absorption coefficient and l is the absorption cell thickness. Given that the molar absorption coefficient (e) and cell thickness (l) remain constant, there is a linear relationship between the concentration of the dye in the reaction mixture and its absorbance over time. The initial rate technique was used to investigate the kinetics of these processes. The plane mirror technique was used to establish the initial reaction rate (da/dt)i of each set, which entailed constructing a graph between the absorbance values at matching periods and measuring the slope of the curve.

3. Results and Discussion

3.1. XRD

The g-C3N4 particles’, as prepared XRD patterns, are displayed in Figure 1. The g-C3N4 diffraction peaks are located at 8.1° and 25.5° for the (100) and (002) planes, respectively, as shown in Figure 1. These two peaks are most likely caused by an interplanar gap between the tri-s-triazine unit and the conjugated aromatic system [42,43]. This enabled the synthesis of g-C3N4.

3.2. TGA

The findings of a TGA examination of the behaviour of g-weight-change C3N4 are provided. The heating rate was 5 °C/min, and the temperature ranged from room temperature to 700 °C. The first peak, induced by water and solvent desorption, developed between 100 and 300 degrees Celsius, as shown in Figure 2. The second peak temperature of 400 to 600 degrees Celsius is produced by the combustion of g-C3N4 in air. Even at the optimal testing temperature of 300 °C, the test results demonstrate that g-C3N4 was not broken down.

3.3. Photocatalytic Degradation Kinetics

Photodegradation, or the breakdown of organic molecules using ultraviolet (UV) radiation, is a common approach for dealing with environmental toxins present in water and air. The UV radiation photochemically reacts with the organic molecules, which may lessen their toxicity by reducing their molecular weight. UV (ultraviolet) light is classified into three wavelength ranges: UV-A (320–400 nm), UV-B (280–320 nm), and UV-C (280 nm) (100–280 nm).
UV-A (ultraviolet-A) light is frequently used to produce photodeterioration for a variety of reasons, including: (a) Accessibility: The most prevalent and readily available type of UV radiation from the sun is ultraviolet A (UV-A). Artificial UV sources, such as UV lights, can easily generate it, (b) UV-A has a stronger penetrating potential than the other UV spectrum regions. Deeper penetration into the water or treated item results in a more efficient photodegradation, (c) UV-A is less harmful to humans and the environment than UV-B and UV-C. UV-C, for example, it is ideal for photodegradation but can harm humans by causing skin and eye damage and polluting the environment, (d) As UV-A requires less energy to produce than UV-B and UV-C, it is more cost-effective for industrial-scale photodegradation, (e) UV-A light is a promising option for photodegradation applications due to its accessibility, penetrating power, low environmental impact, and efficient energy use.
Prior to researching the AR-26 photocatalytic degradation, the initial control examinations (adsorption and UV photolysis) were performed in pure water, the findings are shown in Figure 3. The equilibrium was attained after 30 min, and approximately 14% of the AR-26 was eliminated utilising the adsorption studies. The UV-Vis spectra of AR-26 explains the little drop (~6.3%) in AR-26 caused by photolysis under UV-A light. Direct photolysis under UV-A light was not expected under the conditions utilised since the AR-26 does not absorb at 356 nm (the maximum emission wavelength of the chosen irradiation source).
The findings of the examination of the g-photocatalytic C3N4 activity under a UV-A source in both the pure water and treated wastewater are shown in Figure 4. According to the photocatalytic analysis, when the g-C3N4 is exposed to light with an energy greater than its bandgap (~2.844 eV), it becomes activated and creates a photo-induced electron-hole pair (e − h+) and other reactive species that are responsible for the destruction of the AR-26. The AR-26 degradation kinetics (rate constants, half-lives, and correlation coefficients) are presented in both matrices and are shown in Table 3. The experimental data was fitted using pseudo-first order reaction kinetics. Both matrices achieved significant reductions (Figure 4). The degrading percentages in pure water were around 86.0 after 60 min, while in treated wastewater they were around 68.0 after 180 min [8,13].
Pure water showed a faster rate of deterioration than the effluent water. Specifically, the half-life of the AR-26 in pure water was determined to be t1/2 = 22.84 min minutes at a rate constant of k = 3.05 × 10−2/min. A significantly slower depreciation of the AR-26 was seen in the effluent water (k = 0.7 × 10−2/min and t1/2 = 98.91 min).
This pattern demonstrates the significant influence of the water matrix composition on the photocatalytic performance. The organic and inorganic components (e.g., Cl−1, HCO3−1, NO3−1, SO4−2) that coexist in effluent water may influence the photocatalytic activity, primarily as reactive species scavengers [44,45]. The adsorption of the effluent water components onto the surface of a catalyst can change the surface charges and reduce the number of active sites [46]. However, the metal ions in the effluent water may have a negative impact on the photocatalytic efficiency. Cu+2, Zn+2, Fe+3, and Al+3 were found to have an inhibiting effect on the photocatalytic performance under the experimental conditions studied. The results are tabulated in Figure 5. The metal ions may influence the photocatalytic degradation by (i) preventing O2 from being reduced by photogenerated conduction electrons; hence, inhibiting the generation of reactive oxygen species [47], and (ii) altering the pollutant adsorption. The degradation of the AR-26 was examined using effluent water as a matrix, and the effect of pH was measured under similar conditions and the results were plotted in Figure 6. The AR-26 was most successfully removed at a neutral pH (about 7.8). The used catalyst was discovered to have a pH-PZC of roughly 5.0. The catalyst surface is negatively charged if the value is less than or equal to this threshold; otherwise, it is positively charged. The AR-26 (pKa 9.46) molecules are largely protonated at pH 7.8 in a similar way. Under the testing conditions, the highest removal is accomplished due to the electrostatic attractions between the AR-26 and the negatively charged catalyst’s surface. At pH = 4, however, the breakdown is significantly hindered due to the electrostatic repulsion between the positively charged catalyst molecules and the negatively charged AR-26 molecules. Under pH = 10, some electrostatic repulsion between the negatively charged catalysts and the partly negative charged AR-26 molecules might be assumed to verify the minor reduction in the degradation observed.

3.4. Role of Reactive Species to the Degradation Mechanism

To determine the presence of HO, h+, and O2, isopropanol (IPA), methanol (MeOH), and p-benzoquinone (p-Bqn) were used. The scavengers were selected because of their consistently high reaction rates with their target species. As it has a high-rate constant reaction with the radical, equal to 2.1 × 109 L/mol/s, the IPA is recognized to be an excellent HO scavenger [23,24]. MeOH reacts with HO at a rate of 1.1 × 109 L/mol/s [20,25], making it efficient against both HO and h+. The rate constant for quenching O2•−1 by para-benzoquinone (p-Bqn) is 1.8 × 109 L/mol/s [20]. The pseudo-first order rate constants and the degradation profiles in the presence of the scavengers are shown in Table 4 and Figure 7, respectively.
Graphitic carbon nitride (g-C3N4) has a conduction band edge potential in the range of −1.1 to −0.6 V relative to a conventional hydrogen electrode at room temperature. In the conduction band of g-C3N4, 0.94 eV of energy is needed to create superoxide radicals (O2) from O2. This is roughly equivalent to a potential of −0.4 V with respect to the normalised hydrogen electrode. In light of the above, it may be concluded that g-conduction C3N4’s band edge potential is certainly high enough to generate superoxide radicals from O2.
MeOH achieved the largest decrease (94.2%) because it can neutralize both HO and h+. The fact that IPA only generated a 42.7% inhibition highlights both the limited contribution of HO and the major participation of h+. This is consistent with the literature’s findings: Because the VB edges of g-C3N4 catalysts are still less positive than the OH/HO redox potential (1.99 eV vs. NHE) [48], the formation of HO via direct water or OH oxidation by holes is discouraged during activation. The experiments in acetonitrile verified the significance of h+ (data not shown). The inhibition rate increased to 73.8% when p-Bqn was added. The superoxide anions were found to directly oxidize organic pollutants. The reactions [49] that additionally comprise O2-O2•−1 and result in the formation of HO are as follows:
O2−1 + H+→HO2
2HO2→O2 + H2O2
H2O2 + O2−1→HO + OH + O2
Our results support those of a recent study [46], which used g-C3N4-based catalysts in the photocatalytic destruction of refractory pollutants. The key species reported to be involved in this process were h+ and O2. The proposed photocatalytic mechanism, as observed in the prior work, is based on the formation of electron-hole pairs in the valence and conduction bands of g-C3N4. The e on the CB may convert O2 to O−2·O2•−1, while the holes (h+) in the VB actively contribute to the degrading process in g-C3N4. O2•−1.

3.5. Photocatalytic Degradation Mechanism

Using mass spectrometry and interpreting mass spectra collected in positive ionisation mode, we were able to establish which IPs are formed during the early stages of the photocatalytic reactions in both pure water and wastewater. Three IPs were identified structurally in both matrices using molecular and fragment ions as shown in Table 5.
Figure 6 depicts one of three potential paths. In the first, the methoxy group of AR-26 is removed, resulting in AMI1. In addition to our findings, Skibiski et al., 2011 [50,51] discovered this IP during the photodegradation of the studied pharmaceutical. AR-26 was discovered through the photocatalytic treatment of an effluent mixture containing it. The first step in the dealkylation pathway, the alternative metabolic route, is cleavage of the ethyl group attached to the N atom. Through the third pathway, an oxygen transfer mechanism results in the formation of a signature N-oxide IP. N-oxide was discovered to be a characteristic IP while treating AR-26 using photolysis [51] and heterogeneous photocatalysis. The absence of hydroxylated IPs support the reports that HO plays only a minor role in the degradation mechanism. Prior research on the photocatalytic degradation of AR-26 containing effluent mixtures [52] is consistent with the proposed degradation pathways. The possible route of Acid Red 26’s decomposition is shown in Figure 8.
The formation of the IP was also tracked during the photocatalytic process. According to Figure 9, the IPs in pure water (Figure 9a) and effluent water (Figure 9b) reached their maximal area in 20 and 60 min, respectively. The space occupied by the three IPs in both matrices shrunk substantially after that. Before full mineralization, the rings can be split, permitting the generation of IPs with low molecular weight. After extensive usage of heterogeneous photocatalysis, formic and acetic acid, both with low molecular weights, were identified.

3.6. Ecotoxicity Evolution

The toxicity to microalgae was measured over time in both saltwater and freshwater environments (Figure 10 and Figure 11). As shown, pure water showed little toxicity at 0 min into the process (Figure 10a and Figure 11a). In comparison, after 72 h of contact with an untreated AR-26 solution in effluent water (0 min), the growth rates of both microalgae were inhibited by nearly 25%. (Figure 10b and Figure 11b). This matrix’s composition, which may be toxic for the exposed microalgae, may explain the significant growth inhibition rates found in effluent water. Toxicity tests on an early wastewater sample verified this, with an inhibition rate of 18.1%. The obtained results were in accordance with the previously reported literature and found essentially the same patterns [44,53]. It was discovered that the earliest stages of the photocatalytic treatment only slightly increased the toxicity in both matrices. There is a connection between the emergence of these IPs and the observed increase. Notably, in pure water and effluent water, the IPs developed most strongly at 20 and 60 min, respectively, implying that these intervals are critical for growth inhibition. The photocatalytic degradation of numerous pollutants in aqueous matrices by various AOPs has also been reported to have increased the toxicity in the early stages, which is consistent with our findings [53]. However, the Ips play a modest role in the overall toxicity. In all cases, the percentage of inhibition was significantly reduced after photocatalytic treatment. This clearly demonstrates that g-C3N4-based heterogeneous photocatalysis can occur without the generation of dangerous IPs. It also efficiently reduces the harmful impacts of municipal wastewater.

3.7. A Catalytic Investigation into the Oxidation of Azo Dyes

The oxidation of azo dyes i.e., AR-26 was examined using g-C3N4 to determine the catalytic efficacy of g-C3N4. The UV-A irradiation on the samples was carried out for a period of 45 min. The decomposition of the azo dyes was tracked using a kinetic spectrophotometric analysis. Figure 12 depicts the UV-vis spectrum of the AR-26 breakdown. AR-26 has a maximum absorption wavelength of 510 nm. New bands at 245 and 273 nm indicate dye degradation in this case as well.

3.8. Recyclability and Photostability

Five photocatalysis cycles were carried out to test the photocatalyst’s reusability. Figure 13 depicts many samples of the photographs. Figure 13 shows that the efficiency of the photocatalysis remains constant after five rounds. Furthermore, as shown in Figure 13, the XRD measurements performed after the photocatalytic phenomena show that the crystalline structure of g-C3N4 has not altered in comparison to before the photocatalytic process was carried out.
The specifics of sample collection and the reusable process may vary depending on the photocatalyst being tested and the experimental protocol used. Sample collection: It is essential to collect representative samples of the photocatalyst before and after each cycle of the reusability test. The samples were collected using two distinct techniques. First, the samples were allowed to settle down after the experiment via sedimentation. After the catalyst material had settled, the photodegraded AR-26 sample in water was decanted. Second, the photocatalyst at the bottom was washed three times with distilled water, then once with methanol using a filtration technique with Whatman No: 41 filter paper. The reusable process should be designed in such a way that the photocatalyst is fully recovered and can be reused without loss of activity. The process may include washing the photocatalyst with water and methanol solvent to remove any adsorbed or reacted species, followed by drying in an oven and calcination at 350 °C to regenerate the photocatalyst.
The XRD and TGA measurements were performed before and after five cycles of photocatalytic activity to provide insight into the stability of the g-C3N4 photocatalyst. Figure 14 compares the XRD and TGA curves before and after the photodegradation experiment and shows that the g-C3N4 structure was unaffected. The TGA was used to determine that no change in the thermal properties occurred before or after the experiment, and the results were positive. This is depicted in Figure 15.

4. Conclusions

The present study reports the photocatalytic breakdown of the azo dye AR-26 using UV-A irradiation and g-C3N4 as a photocatalyst in pure water and effluent water. Both matrices have rather high removal rates. Effluent water has a complex composition, which comprises both inorganic and organic compounds, explaining why it degrades more slowly. The scavenging tests confirmed the importance of h+ and O2•−1 in the reaction process. The photocatalytic degradation of the examined drug was discovered to comprise oxidation, dealkylation, and cleavage of the methoxy group. When pure water was employed as a media, the microalgae Chlorococcum sp. and Dunaliella tertiolecta showed no growth inhibition and hence a low toxicity from the beginning and throughout the photocatalytic process. However, when effluent water was used as a matrix, the number of reported side effects rose. However, after 180 min, the effects appeared to have disappeared. The results showed that AR-26 may be successfully eliminated using heterogeneous photocatalysis, such as g-C3N4 without the production of harmful IPs. As g-C3N4 reacts to visible light and may thus be activated by solar light, heterogeneous photocatalysis using g-C3N4 is viewed as a potential technique for pharmaceutical elimination after an effective separation of the photocatalyst or its immobilisation on suitable substrates.

Author Contributions

Conceptualization, S.N.M.; Methodology, M.B.P. and D.M.; Validation, S.A.A.-Z., S.N.M., A.A.O., D.M., A.K., N.S.T. and M.A.; Formal analysis, A.Y.P., A.A.O. and A.S.; Investigation, A.Y.P., D.M. and N.S.T.; Resources, A.K. and A.S.; Data curation, A.Y.P. and N.S.T.; Writing—original draft, S.A.A.-Z., M.B.P., S.N.M., N.M., V.G., A.S. and M.A.; Writing—review & editing, A.A.O., N.M. and A.K. All authors have read and agreed to the published version of the manuscript.

Funding

This research has been funded by the Scientific Research Deanship at the University of Ha’il-Saudi Arabia through project number RG-21 032.

Data Availability Statement

Not Applicable.

Acknowledgments

This research has been funded by the Scientific Research Deanship at the University of Ha’il-Saudi Arabia through project number RG-21 032. Authors thanks to the Vision Group for Science and Technology (VGST), Govt. of Karnataka, Bengaluru, India.

Conflicts of Interest

The authors here declare that there is no conflict of interest regarding the publication of this research article.

References

  1. Calisto, V.; Esteves, V.I. Psychiatric Pharmaceuticals in the Environment. Chemosphere 2009, 77, 1257–1274. [Google Scholar] [CrossRef] [PubMed]
  2. Fatta-Kassinos, D.; Meric, S.; Nikolaou, A. Pharmaceutical Residues in Environmental Waters and Wastewater: Current State of Knowledge and Future Research. Anal. Bioanal. Chem. 2011, 399, 251–275. [Google Scholar] [CrossRef]
  3. Kanakaraju, D.; Glass, B.D.; Oelgemöller, M. Titanium Dioxide Photocatalysis for Pharmaceutical Wastewater Treatment. Environ. Chem. Lett. 2014, 12, 27–47. [Google Scholar] [CrossRef]
  4. Rivera-Utrilla, J.; Sánchez-Polo, M.; Ferro-García, M.Á.; Prados-Joya, G.; Ocampo-Pérez, R. Pharmaceuticals as Emerging Contaminants and Their Removal from Water. A Review. Chemosphere 2013, 93, 1268–1287. [Google Scholar] [CrossRef]
  5. aus der Beek, T.; Weber, F.A.; Bergmann, A.; Hickmann, S.; Ebert, I.; Hein, A.; Küster, A. Pharmaceuticals in the Environment-Global Occurrences and Perspectives. Environ. Toxicol. Chem. 2016, 35, 823–835. [Google Scholar] [CrossRef]
  6. Ziarani, G.M.; Moradi, R.; Lashgari, N.; Kruger, H.G. Azo Dyes. In Metal-Free Synthetic Organic Dyes; Elsevier: Amsterdam, The Netherlands, 2018; Chapter 4; pp. 47–93. [Google Scholar]
  7. Chung, K.T. Azo dyes and human health: A review. J. Environ. Sci. Health C Environ. Carcinog. Ecotoxicol. Rev. 2016, 34, 233–261, Erratum in J. Environ. Sci. Health C Environ. Carcinog. Ecotoxicol. Rev. 2017, 35, 67. [Google Scholar] [CrossRef] [PubMed]
  8. Benkhaya, S.; M’rabet, S.; El Harf, A. Classifications, properties, recent synthesis and applications of azo dyes. Heliyon 2020, 6, E03271. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  9. Ozturk, E.; Cinperi, N.C. Water efficiency and wastewater reduction in an integrated woolen textile mill. J. Clean. Prod. 2018, 201, 686–696. [Google Scholar] [CrossRef]
  10. Hassan, M.M.; Carr, C.M. A critical review on recent advancements of the removal of reactive dyes from dyehouse effluent by ion-exchange adsorbents. Chemosphere 2018, 209, 201–219. [Google Scholar] [CrossRef]
  11. Abe, F.R.; Soares, A.M.; de Oliveira, D.P.; Gravato, C.A. Toxicity of dyes to zebrafish at the biochemical level: Cellular energy allocation and neurotoxicity. Environ. Pollut. 2018, 235, 255–262. [Google Scholar] [CrossRef]
  12. Du, C.F.; Xue, Y.T.; Wu, Z.S.; Wu, Z.L. Microwave-assisted one-step preparation of macadamia nut shell-based activated carbon for efficient adsorption of Reactive Blue. New J. Chem. 2017, 41, 15373–15383. [Google Scholar] [CrossRef]
  13. Kim, S.-H.; Choi, P.-P. Enhanced Congo red dye removal from aqueous solutions using iron nanoparticles: Adsorption, kinetics, and equilibrium studies. Dalton Trans. 2017, 46, 15470–15479. [Google Scholar] [CrossRef]
  14. Yu, B.; He, L.; Wang, Y.; Cong, H. Multifunctional PMMA@Fe3O4@DR Magnetic Materials for Efficient Adsorption of Dyes. Materials 2017, 10, 1239. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  15. Zhang, B.; Zhang, T.; Zhang, Z.; Xie, M. Hydrothermal synthesis of a graphene/magnetite/montmorillonite nanocomposite and its ultrasonically assisted methylene blue adsorption. J. Mater. Sci. 2019, 54, 11037–11055. [Google Scholar] [CrossRef]
  16. González-Alfaro, Y.; Aranda, P.; Fernandes, F.; Wicklein, B.; Darder, M.; Ruiz-Hitzky, E. Multifunctional Porous Materials Through Ferrofluids. Adv. Mater. 2011, 23, 5224–5228. [Google Scholar] [CrossRef]
  17. Darder, M.; González-Alfaro, Y.; Aranda, P.; Ruiz-Hitzky, E. Silicate-based multifunctional nanostructured materials with magnetite and Prussian blue: Application to cesium uptake. RSC Adv. 2014, 4, 35415–35421. [Google Scholar] [CrossRef]
  18. Huang, G.; Kang, W.; Geng, Q.; Xing, B.; Liu, Q.; Jia, J.; Zhang, C. One-Step Green Hydrothermal Synthesis of Few-Layer Graphene Oxide from Humic Acid. Nanomaterials 2018, 8, 215. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  19. Singh, S.P.; Li, Y.; Zhang, J.; Tour, J.M.; Arnusch, C.J. Sulfur-Doped Laser-Induced Porous Graphene Derived from Polysulfone-Class Polymers and Membranes. ACS Nano 2018, 12, 289–297. [Google Scholar] [CrossRef] [PubMed]
  20. Gómez-Carnota, D.; Barriada, J.L.; Rodríguez-Barro, P.; Sastre de Vicente, M.E.; Herrero, R. Sustainable Low-Cost Phosphorus Recovery Using Nanostructured Materials with Reusability Potential. Nanomaterials 2023, 13, 1167. [Google Scholar] [CrossRef]
  21. Aboutaleb, W.A.; El-Salamony, R.A. Effect of Fe2O3-CeO2 nanocomposite synthesis method on the Congo red dye photodegradation under visible light irradiation. Mater. Chem. Phys. 2019, 236, 121724. [Google Scholar] [CrossRef]
  22. Patil, S.M.; Deshmukh, S.P.; More, K.V.; Shevale, V.B.; Delekar, S.D. Sulfated TiO2/WO3 nanocomposite: An efficient photocatalyst for degradation of Congo red and methyl red dyes under visible light irradiation. Mater. Chem. Phys. 2019, 225, 247–255. [Google Scholar] [CrossRef]
  23. Mancuso, A.; Blangetti, N.; Sacco, O.; Freyria, F.S.; Bonelli, B.; Esposito, S.; Sannino, D.; Vaiano, V. Photocatalytic Degradation of Crystal Violet Dye under Visible Light by Fe-Doped TiO2 Prepared by Reverse-Micelle Sol–Gel Method. Nanomaterials 2023, 13, 270. [Google Scholar] [CrossRef] [PubMed]
  24. Dong, J.; Zhang, Y.; Hussain, M.I.; Zhou, W.; Chen, Y.; Wang, L.-N. g-C3N4: Properties, Pore Modifications, and Photocatalytic Applications. Nanomaterials 2022, 12, 121. [Google Scholar] [CrossRef] [PubMed]
  25. Obregon, S.; Vazquez, A.; Ruiz-Gomez, M.A.; Rodriguez-Gonzalez, V. SBA-15 assisted preparation of mesoporous g-C3N4 for photocatalytic H2 production and Au3+ fluorescence sensing. Appl. Surf. Sci. 2019, 488, 205–212. [Google Scholar] [CrossRef]
  26. Ong, W.J.; Tan, L.L.; Ng, Y.H.; Yong, S.T.; Chai, S.P. Graphitic Carbon Nitride (g-C3N4)-Based Photocatalysts for Artificial Photosynthesis and Environmental Remediation: Are We a Step Closer to Achieving Sustainability? Chem. Rev. 2016, 116, 7159–7329. [Google Scholar] [CrossRef]
  27. Bairamis, F.; Konstantinou, I.; Petrakis, D.; Vaimakis, T. Enhanced Performance of Electrospun Nanofibrous TiO2/g-C3N4 Photocatalyst in Photocatalytic Degradation of Methylene Blue. Catalysts 2019, 9, 880. [Google Scholar] [CrossRef] [Green Version]
  28. Wen, J.; Xie, J.; Chen, X.; Li, X. A Review on g-C3N4-Based Photocatalysts. Appl. Surf. Sci. 2017, 391, 72–123. [Google Scholar] [CrossRef]
  29. Liu, J.; Wei, X.; Sun, W.; Guan, X.; Zheng, X.; Li, J. Fabrication of S-Scheme CdS-g-C3N4-Graphene Aerogel Heterojunction for Enhanced Visible Light Driven Photocatalysis. Environ. Res. 2021, 197, 111136. [Google Scholar] [CrossRef]
  30. Liu, D.; Li, C.; Zhao, C.; Zhao, Q.; Niu, T.; Pan, L.; Xu, P.; Zhang, F.; Wu, W.; Ni, T. Facile Synthesis of Three-Dimensional Hollow Porous Carbon Doped Polymeric Carbon Nitride with Highly Efficient Photocatalytic Performance. Chem. Eng. J. 2022, 438, 135623. [Google Scholar] [CrossRef]
  31. Liu, D.; Li, C.; Ge, J.; Zhao, C.; Zhao, Q.; Zhang, F.; Ni, T.; Wu, W. 3D Interconnected g-C3N4 Hybridized with 2D Ti3C2 MXene Nanosheets for Enhancing Visible Light Photocatalytic Hydrogen Evolution and Dye Contaminant Elimination. Appl. Surf. Sci. 2022, 579, 152180. [Google Scholar] [CrossRef]
  32. Leelavathi, H.; Muralidharan, R.; Abirami, N.; Tamizharasan, S.; Sankeetha, S.; Kumarasamy, A.; Arulmozhi, R. Construction of Step-Scheme g-C3N4/Co/ZnO Heterojunction Photocatalyst for Aerobic Photocatalytic Degradation of Synthetic Wastewater. Colloids Surf. A Physicochem. Eng. Asp. 2023, 656, 130449. [Google Scholar] [CrossRef]
  33. Bairamis, F.; Konstantinou, I. Wo3 Fibers/g-C3N4 Z-Scheme Heterostructure Photocatalysts for Simultaneous Oxidation/Reduction of Phenol/Cr (Vi) in Aquatic Media. Catalysts 2021, 11, 792. [Google Scholar] [CrossRef]
  34. Pei, X.; An, W.; Zhao, H.; He, H.; Fu, Y.; Shen, X. Enhancing Visible-Light Degradation Performance of g-C3N4 on Organic Pollutants by Constructing Heterojunctions via Combining Tubular g-C3N4 with Bi2O3 Nanosheets. J. Alloys Compd. 2023, 934, 167928. [Google Scholar] [CrossRef]
  35. John, A.; Rajan, M.S.; Thomas, J. Carbon Nitride-Based Photocatalysts for the Mitigation of Water Pollution Engendered by Pharmaceutical Compounds. Environ. Sci. Pollut. Res. 2021, 28, 24992–25013. [Google Scholar] [CrossRef] [PubMed]
  36. Go, S.; Kim, J.; Park, S.S.; Kim, M.; Lim, H.; Kim, J.-Y.; Lee, D.-W.; Im, J. Synergistic Use of Hyperspectral UV-Visible OMI and Broadband Meteorological Imager MODIS Data for a Merged Aerosol Product. Remote Sens. 2020, 12, 3987. [Google Scholar] [CrossRef]
  37. Kim, J.; Lee, J.; Lee, H.C.; Higurashi, A.; Takemura, T.; Song, C.H. Consistency of the aerosol type classification from satellite remote sensing during the Atmospheric Brown Cloud–East Asia Regional Experiment campaign. J. Geophys. Res. Atmos. 2007, 112, D22. [Google Scholar] [CrossRef]
  38. Torres, O.; Ahn, C.; Chen, Z. Improvements to the OMI near-UV aerosol algorithm using A-train CALIOP and AIRS observations. Atmos. Meas. Tech. 2013, 6, 3257–3270. [Google Scholar] [CrossRef] [Green Version]
  39. Baxendale, J.H.; Bridge, N.K. The photoreduction of some ferric compounds in aqueous solution. J. Phys. Chem. 1955, 59, 783–788. [Google Scholar] [CrossRef]
  40. Calvert, J.; Pitts, J.N. Liquid–Phase Chemical Actinometry Using Potassium Ferrioxalate. In Photochemistry; John Wiley: New York, NY, USA, 1966; pp. 783–786. [Google Scholar]
  41. Spyrou, A.; Tzamaria, A.; Dormousoglou, M.; Skourti, A.; Vlastos, D.; Papadaki, M.; Antonopoulou, M. The overall assessment of simultaneous photocatalytic degradation of Cimetidine and Amisulpride by using chemical and genotoxicological approaches. Sci. Total Environ. 2022, 838, 156140. [Google Scholar] [CrossRef] [PubMed]
  42. Al-Zahrani, S.A.; Patil, M.B.; Mathad, S.N.; Patil, A.Y.; Otaibi, A.A.; Masood, N.; Mansour, D.; Khan, A.; Manikandan, A.; Syafri, E. Photocatalytic Degradation of Textile Orange 16 Reactive Dye by ZnO Nanoparticles Synthesized via Green Route Using Punica Granatum Leaf Extract. Crystals 2023, 13, 172. [Google Scholar] [CrossRef]
  43. Dai, H.; Zhang, S.; Xu, G.; Peng, Y.; Gong, L.; Li, X.; Li, Y.; Lin, Y.; Chen, G. Highly photoactive heterojunction based on g-C3N4 nanosheets decorated with dendritic zinc (II) phthalocyanine through axial coordination and its ultrasensitive enzyme-free sensing of choline. RSC Adv. 2014, 4, 58226–58230. [Google Scholar] [CrossRef]
  44. Antonopoulou, Μ.; Hela, D.; Konstantinou, I. Photocatalytic degradation kinetics, mechanism and ecotoxicity assessment of tramadol metabolites in aqueous TiO2 suspensions. Sci. Total Environ. 2016, 545–546, 476–485. [Google Scholar] [CrossRef]
  45. Calza, P.; Hadjicostas, C.; Sakkas, V.A.; Sarro, M.; Minero, C.; Medana, C.; Albanis, T.A. Photocatalytic transformation of the antipsychotic drug risperidone in aqueous media on reduced graphene oxide—TiO2 composites. Appl. Catal. B Environ. 2016, 183, 96–106. [Google Scholar] [CrossRef]
  46. Konstas, P.S.; Kosma, C.; Konstantinou, I.; Albanis, T. Photocatalytic Treatment of Pharmaceuticals in Real Hospital Wastewaters for Effluent Quality Amelioration. Water 2019, 11, 2165. [Google Scholar] [CrossRef] [Green Version]
  47. Chen, C.; Li, X.; Ma, W.; Zhao, J.; Hidaka, H.; Serpone, N. Effect of Transition Metal Ions on the TiO2-Assisted Photodegradation of Dyes under Visible Irradiation: A Probe for the Interfacial Electron Transfer Process and Reaction Mechanism. J. Phys. Chem. B 2002, 106, 318–324. [Google Scholar] [CrossRef]
  48. Papailias, I.; Todorova, N.; Giannakopoulou, T.; Ioannidis, N.; Boukos, N.; Athanasekou, C.P.; Dimotikali, D.; Trapalis, C. Chemical vs thermal exfoliation of g-C3N4 for NOx removal under visible light irradiation. Appl. Cat. B Environ. 2018, 239, 16–26. [Google Scholar] [CrossRef]
  49. Kobkeatthawin, T.; Chaveanghong, S.; Trakulmututa, J.; Amornsakchai, T.; Kajitvichyanukul, P.; Smith, S.M. Photocatalytic Activity of TiO2/g-C3N4 Nanocomposites for Removal of Monochlorophenols from Water. Nanomaterials 2022, 12, 2852. [Google Scholar] [CrossRef] [PubMed]
  50. Xu, T.; Wang, D.; Dong, L.; Shen, H.; Lu, W.; Chen, W. Graphitic carbon nitride co-modified by zinc phthalocyanine and graphene quantum dots for the efficient photocatalytic degradation of refractory contaminants. Appl. Catal. B Environ. 2019, 244, 96–106. [Google Scholar] [CrossRef]
  51. Skibiński, R. Identification of photodegradation product of amisulpride by ultra-high-pressure liquid chromatography–DAD/ESI-quadrupole time-of-flight-mass spectrometry. J. Pharm. Biomed. Anal. 2011, 56, 904–910. [Google Scholar] [CrossRef]
  52. Lasyal, R.; Hoel, A. Facile synthesis of IrO2 nanoclusters and their application as catalysts in the degradation of azo dyes. Turk. J. Chem. 2018, 42, 941–957. [Google Scholar]
  53. Gomes, J.F.; Lopes, A.; Gmurek, M.; Quinta-Ferreira, R.M.; Martins, R.C. Study of the influence of the matrix characteristics over the photocatalytic ozonation of parabens using Ag-TiO2. Sci. Total Environ. 2019, 646, 1468–1477. [Google Scholar] [CrossRef] [PubMed]
Figure 1. X-ray diffraction (XRD) patterns of the graphitic carbon nitride (g-C3N4).
Figure 1. X-ray diffraction (XRD) patterns of the graphitic carbon nitride (g-C3N4).
Crystals 13 00577 g001
Figure 2. Thermogravimetry–differential thermal analysis (TGA) profiles of g-C3N4.
Figure 2. Thermogravimetry–differential thermal analysis (TGA) profiles of g-C3N4.
Crystals 13 00577 g002
Figure 3. Photolysis of AR-26 via adsorption and photolysis using UV-A light in pure water ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Figure 3. Photolysis of AR-26 via adsorption and photolysis using UV-A light in pure water ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Crystals 13 00577 g003
Figure 4. Degradation of AR-26 via photocatalysis in pure water and effluent water exposed to UV-A light ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Figure 4. Degradation of AR-26 via photocatalysis in pure water and effluent water exposed to UV-A light ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Crystals 13 00577 g004
Figure 5. A comparison study of the photocatalytic degradation of AR-26 in pure water ([AR-26]0 = 1 mg/L, [metal ion]0 = 10 mg/L, [g-C3N4] = 300 mg/L) with and without metal ions.
Figure 5. A comparison study of the photocatalytic degradation of AR-26 in pure water ([AR-26]0 = 1 mg/L, [metal ion]0 = 10 mg/L, [g-C3N4] = 300 mg/L) with and without metal ions.
Crystals 13 00577 g005
Figure 6. pH-dependent effects on photocatalytic degradation of AR-26 in effluent water ([AR-26]0 = 1 mg/L, [g-C3N4] = 300 mg/L).
Figure 6. pH-dependent effects on photocatalytic degradation of AR-26 in effluent water ([AR-26]0 = 1 mg/L, [g-C3N4] = 300 mg/L).
Crystals 13 00577 g006
Figure 7. In the presence of scavengers, photocatalytic degradation of AR-26 was observed ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L; [IPA] = 0.1 M; [MeOH] = 0.1 M; [p-Bqn] = 0.2 mM, matrix: pure water).
Figure 7. In the presence of scavengers, photocatalytic degradation of AR-26 was observed ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L; [IPA] = 0.1 M; [MeOH] = 0.1 M; [p-Bqn] = 0.2 mM, matrix: pure water).
Crystals 13 00577 g007
Figure 8. A possible route of Acid Red 26’s decomposition.
Figure 8. A possible route of Acid Red 26’s decomposition.
Crystals 13 00577 g008
Figure 9. A comparison of the IP generation patterns in (a) pure water and (b) effluent water during the photocatalytic degradation of AR-26 ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Figure 9. A comparison of the IP generation patterns in (a) pure water and (b) effluent water during the photocatalytic degradation of AR-26 ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Crystals 13 00577 g009
Figure 10. Toxicity changes during photocatalysis with AR-26 in (a) pure water and (b) effluent water at ([AR-26]0 = 1 mg/L and 300 mg/L, respectively).
Figure 10. Toxicity changes during photocatalysis with AR-26 in (a) pure water and (b) effluent water at ([AR-26]0 = 1 mg/L and 300 mg/L, respectively).
Crystals 13 00577 g010
Figure 11. Toxicological changes in Dunaliella tertiolecta during photocatalysis in (a) pure water and (b) conventional water ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Figure 11. Toxicological changes in Dunaliella tertiolecta during photocatalysis in (a) pure water and (b) conventional water ([AR-26]0 = 1 mg/L; [g-C3N4] = 300 mg/L).
Crystals 13 00577 g011
Figure 12. UV-vis spectra showing the degradation of Acid Red-26.
Figure 12. UV-vis spectra showing the degradation of Acid Red-26.
Crystals 13 00577 g012
Figure 13. The degradation profile of g-C3N4 for five cycles.
Figure 13. The degradation profile of g-C3N4 for five cycles.
Crystals 13 00577 g013
Figure 14. XRD curves of g-C3N4 before and after the photodegradation experiment.
Figure 14. XRD curves of g-C3N4 before and after the photodegradation experiment.
Crystals 13 00577 g014
Figure 15. TGA curves of g-C3N4 before and after the photodegradation experiment.
Figure 15. TGA curves of g-C3N4 before and after the photodegradation experiment.
Crystals 13 00577 g015
Table 1. Physical properties of graphite carbon nitride.
Table 1. Physical properties of graphite carbon nitride.
Sl. No.PropertyValue
1BET Surface area36 m2/g
2particle size30 nm
3Energy gap (Eg)~2.84 eV
Table 2. Treated wastewater characteristics.
Table 2. Treated wastewater characteristics.
Sl. No.PropertyValue
1pH7.5± 0.3
2Conductivity310.72 ± 10 μS/cm
3Total suspended solids1.88 ± 0.31 mg/L
4COD18.1 ± 1.89 mg/L
5PO43− 3.87 ± 0.05 mg/L
6SO42−32.4 ± 1.44 mg/L
7NO325.3 ± 0.77 mg/L
Table 3. (AR-26) photocatalytic degradation in pure water and effluent water: various kinetic parameters (rate constants, correlation coefficients (R2), half-lives (t1/2)).
Table 3. (AR-26) photocatalytic degradation in pure water and effluent water: various kinetic parameters (rate constants, correlation coefficients (R2), half-lives (t1/2)).
MatrixK × 10−2 (min−1)t1/2 (min)R2
Pure water3.1123.120.9524
Effluent water0.7299.120.9821
Table 4. Photocatalytic degradation of AR-26 in the presence of scavengers: kinetic parameters (rate constants, correlation coefficients (R2), and percentages of inhibition (% Δk)).
Table 4. Photocatalytic degradation of AR-26 in the presence of scavengers: kinetic parameters (rate constants, correlation coefficients (R2), and percentages of inhibition (% Δk)).
ScavengerK × 10−2 (min−1)R2% Δk
Without Scavenger3.110.9524-
IPS1.770.982142.3
Methanol0.240.939192.9
p-Bpo0.830.981374.1
Table 5. The detected IPs’ in mass (in terms of [M + H]+) and chemical formulae.
Table 5. The detected IPs’ in mass (in terms of [M + H]+) and chemical formulae.
IP’s[M + H]+Molecular Formula
AMI435C18H12O7N2S2
AMI-1330C10H4O7N2S2
AMI-2270C10H7O5N2S
AMI-3241C10H8O5S
AMI-4170C8H8O4
AMI-5152C8H8O3
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Al-Zahrani, S.A.; Patil, M.B.; Mathad, S.N.; Patil, A.Y.; Al Otaibi, A.; Masood, N.; Mansour, D.; Khan, A.; Gupta, V.; Topare, N.S.; et al. Photocatalytic Azo Dye Degradation Using Graphite Carbon Nitride Photocatalyst and UV-A Irradiation. Crystals 2023, 13, 577. https://doi.org/10.3390/cryst13040577

AMA Style

Al-Zahrani SA, Patil MB, Mathad SN, Patil AY, Al Otaibi A, Masood N, Mansour D, Khan A, Gupta V, Topare NS, et al. Photocatalytic Azo Dye Degradation Using Graphite Carbon Nitride Photocatalyst and UV-A Irradiation. Crystals. 2023; 13(4):577. https://doi.org/10.3390/cryst13040577

Chicago/Turabian Style

Al-Zahrani, Salma A., Mallikarjunagouda B. Patil, Shridhar N. Mathad, Arun Y. Patil, Ahmed Al Otaibi, Najat Masood, Dorsaf Mansour, Anish Khan, Vikas Gupta, Niraj S. Topare, and et al. 2023. "Photocatalytic Azo Dye Degradation Using Graphite Carbon Nitride Photocatalyst and UV-A Irradiation" Crystals 13, no. 4: 577. https://doi.org/10.3390/cryst13040577

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop