Next Article in Journal
Influence of Silver Nanoparticles on the Growth of Ascitic and Solid Ehrlich Adenocarcinoma: Focus on Copper Metabolism
Next Article in Special Issue
Recent Advances in Biocompatible Ionic Liquids in Drug Formulation and Delivery
Previous Article in Journal
Tubeimoside-2 Triggers Methuosis in Hepatocarcinoma Cells through the MKK4–p38α Axis
Previous Article in Special Issue
Role and Recent Advancements of Ionic Liquids in Drug Delivery Systems
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of Ionic Liquid on Silver-Nanoparticle-Complexed Ganoderma applanatum and Its Topical Film Formulation

1
Department of Pharmaceutical Chemistry, College of Pharmacy, Rangsit University, Muang 12000, Pathum Thani, Thailand
2
Department of Pharmaceutical Technology, Faculty of Pharmaceutical Sciences, Prince of Songkla University, Hat-Yai 90112, Songkhla, Thailand
3
Drug and Herbal Product Research and Development Center, College of Pharmacy, Rangsit University, Muang 12000, Pathum Thani, Thailand
4
Cosmetic Technology and Dietary Supplement Products Program, Faculty of Agro and Bio Industry, Thaksin University, Ban Pa Phayom 93210, Phatthalung, Thailand
*
Author to whom correspondence should be addressed.
Pharmaceutics 2023, 15(4), 1098; https://doi.org/10.3390/pharmaceutics15041098
Submission received: 29 January 2023 / Revised: 18 March 2023 / Accepted: 27 March 2023 / Published: 29 March 2023
(This article belongs to the Special Issue Ionic Liquids in Pharmaceutical and Biomedical Applications)

Abstract

:
Imidazolium-based ionic liquids have been widely utilized as versatile solvents for metal nanoparticle preparation. Silver nanoparticles and Ganoderma applanatum have displayed potent antimicrobial activities. This work aimed to study the effect of 1-butyl-3-methylimidazolium bromide-based ionic liquid on the silver-nanoparticle-complexed G. applanatum and its topical film. The ratio and conditions for preparation were optimized by the design of the experiments. The optimal ratio was silver nanoparticles: G. applanatum extract: ionic liquid at 97:1:2, and the conditions were 80 °C for 1 h. The prediction was corrected with a low percentage error. The optimized formula was loaded into a topical film made of polyvinyl alcohol and Eudragit®, and its properties were evaluated. The topical film was uniform, smooth, and compact and had other desired characteristics. The topical film was able to control the release of silver-nanoparticle-complexed G. applanatum from the matrix layer. Higuchi’s model was used to fit the kinetic of the release. The skin permeability of the silver-nanoparticle-complexed G. applanatum was improved by about 1.7 times by the ionic liquid, which might increase solubility. The produced film is suitable for topical applications and may be utilized in the development of potential future therapeutic agents for the treatment of diseases.

1. Introduction

Because silver nanoparticles have many uses in different fields, such as biomedical sciences, drug delivery, and cosmetics, their synthesis is now very common. The optical and catalytic properties of silver nanoparticles, for example, depend on the size and shape of the particles produced. As a result, numerous researchers have noted the production of silver nanoparticles in various shapes that have numerous applications in areas such as medicine [1]. A few years ago, silver and its compounds were used in medicine as a bactericidal agent that is safe and non-toxic. A number of physical and chemical techniques for creating silver nanoparticles have been developed, but biological techniques, including employing plant and fungus material, are far simpler, less risky, and more environmentally benign [2]. The green synthesis of silver nanoparticles utilizing Ganoderma applanatum extract as a reducing and capping agent, also called “silver-nanoparticle-complexed G. applanatum”, followed by the structural and morphological characterization of the generated silver nanoparticles. G. applanatum has high antioxidant capacity and antimicrobial qualities, which include antibacterial and antifungal activities against pathogenic bacteria, which have led to its use in ethnomedicine [3,4,5]. Hence, silver-nanoparticle-complexed G. applanatum may demonstrate antibacterial and antifungal potentials.
One Ganoderma species is the widely distributed perennial bracket fungus known as G. applanatum. Traditional Asian medicines have primarily used the macrofungus genus Ganoderma, which belongs to the family Ganodermataceae, as a source of medicinal mushrooms rather than food to treat a variety of ailments. It has high genetic diversity [6]. G. applanatum is a higher-order medicinal basidiomycete mushroom that combats cancer in a variety of ways [7,8,9]. Microbial infection is a problem for both the global healthcare and agricultural sectors. In order to overcome this, it is essential to develop novel antimicrobial agents with a range of characteristics, such as antimicrobial potency, high compatibility, and low toxicity [10,11,12]. In this study, we synthesized silver nanoparticles using G. applanatum extract and an ionic liquid and characterized the generated silver nanoparticles. However, the obtained silver-nanoparticle-complexed G. applanatum has restricted permeability, making it difficult to develop effective topical and transdermal formulations for these substances. Ionic liquids have been interested in their possible use in pharmaceutics and medicine as a penetration enhancer because they have been reported to have biological properties.
Ionic liquids have long hydrophobic tails and typically exhibit activity similar to that of surfactants. Ionic liquids are capable of producing a wide range of molecular assemblies, including reverse micelles, regular micelles, and vesicles [13]. Through the fluidization of the lipid bilayer or the disruption of cellular structure, as well as through the creation of permeation routes, surface active ionic liquids have demonstrated great potential for facilitating drug transport across the skin or avoiding the physical barrier of the stratum corneum [14]. Numerous studies have been conducted to understand the underlying mechanisms of the action of ionic liquids because it has been demonstrated that they facilitate drug permeation through the skin [15,16,17,18]. The chemical composition of ionic liquids is implicated in several mechanisms. An ionic liquid’s level of permeation is particularly influenced by its structure. The transdermal permeation of the diltiazem-free base is significantly enhanced by treatment with all ionic liquids, and the levels of diltiazem hydrochloride in the receiving phase have been found to vary significantly depending on the ionic liquid structure. The best enhancer for both salt and free base drug forms is N-dodecyldabco bromide, despite it having some toxicity. The cytotoxicity and enhancer activity of N-methyl-N-decylmorpholinium bromide, in contrast, are well-balanced [19]. The traditional O/W and W/O emulsions with two ionic liquids, hydrophilic 1-hexyl-3-methylimidazolium chloride, and hydrophobic 1-butyl-3-methylimidazolium hexafluorophosphate components, have been created. There is a penetration improvement when ionic liquids are present. In particular, lipophilic substances have been estimated to have greater efficiency in penetrating into the deeper skin layers in comparison to hydrophobic 1-butyl-3-methylimidazolium hexafluorophosphate [20].
The silver-nanoparticle-complexed G. applanatum with ionic liquid as an active drug will thus be loaded in the topical film. A topical film is applied to a specific area of the body, usually the skin, to treat fungal infections by killing or stopping the growth of dangerous fungi on the skin. Topical drug delivery systems are external dosage forms that are administered to the skin. The physical states of topical dosage forms are then further divided into solid, liquid, and semisolid categories. Although topical drugs are meant to work locally, they can potentially have systemic effects [21].
In this study, silver nanoparticles and G. applanatum extracts were synthesized by the green technique to produce the nanoparticles. The 1-butyl-3-methylimidazolium bromide-based ionic liquid was incorporated into the silver-nanoparticle-complexed G. applanatum. The ratios of ingredients and the conditions for preparation were optimized by the design of the experiments. The particle size was a dependent variable for optimization. The characteristics of the optimized recipe of the silver-nanoparticle-complexed G. applanatum were investigated. The silver-nanoparticle-complexed G. applanatum was loaded into the topical film formulation. Folding endurance, Fourier-transform infrared spectroscopy (FTIR), a differential scanning calorimeter (DSC), thermogravimetric analysis (TGA), an X-ray diffractometer (XRD), a scanning electron microscope (SEM), and transmission electron microscopy (TEM) were all employed. The effects of the content of 1-butyl-3-methylimidazolium bromide on silver-nanoparticle-complexed G. applanatum release and permeation were assessed.

2. Materials and Methods

2.1. Preparation of G. applanatum Extract

G. applanatum (Figure 1) was taken in August 2022 in the forest region of Rattanaburi District, Surin Province, Thailand (15°18′11.7″ N 103°50′52.4″ E). Niran Vipunngern, taxonomist, Department of Pharmacognosy, College of Pharmacy, Rangsit University, identified the morphology of G. applanatum. The voucher specimen of G. applanatum was submitted to the Drug and Herbal Product Research and Development Center, College of Pharmacy, Rangsit University, and was given the identification number JS-GA1-08-2022. To avoid microbiological contamination, the fresh G. applanatum was carefully rinsed 2–3 times with flowing distilled water and then with 99.8% pure ethanol. The samples were immediately sliced into small pieces and dried in the shade at room temperature for six to seven days. An electric blender was used to obtain a fine-powdered form from dried materials.
In a beaker, 5 g of G. applanatum powder was extracted with 200 mL of methanol. After this, the extraction was carried out in a fume hood with a microwave oven (MS23F300EEK/ST model, triple distribution system, Samsung Electronics Co., Ltd., Selangor, Malaysia). To avoid overheating the extraction solvent, 60 s of intermittent microwave radiation (“on”) was followed by 60 s of non-heating (“off”). As a result, the total extraction time for each cycle was 120 s. In the four microwave-assisted extraction cycles, the microwave-assisted extraction power was 450 watts. The extraction solution had a temperature of 76 ± 2 °C, as measured with a glass laboratory thermometer. Following the separation process, the liquid phase was filtered through 0.45 μm Whatman No. 1 filter paper before being concentrated using a rotary evaporator at 40–60 °C under vacuum. The crude G. applanatum extracts were stored in a fume hood until their weights were constant and they were protected from light. The phytochemical screening found carbohydrates, glycosides, proteins, alkaloids, steroids, triterpenes, phenols, flavonoids, tannins, saponins, and lipids in G. applanatum extracts, findings which will be followed up on in a currently unpublished manuscript.

2.2. Biosynthesis of Silver-Nanoparticle-Complexed G. applanatum

Our approach for producing silver-nanoparticle-complexed G. applanatum was slightly modified from the prior method used [22]. Silver-nanoparticle-complexed G. applanatum was prepared by combining 15 mg/mL of G. applanatum extract and ionic liquid with 0.1 M silver nitrate (169.87 g/mol) solution in different mass ratios (as shown in Table 1), stabilizing the solution with starch soluble, and then stirring it on a hot plate at 80 °C with a magnetic stirrer for 2 h. The solution was then cooled to room temperature. The ratios of silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) were prepared, optimized, and predicted (Table 1) by the Design-Expert® program (Stat-Ease, Inc., Minneapolis, MN, USA). The computer-generated linear model is presented as Equation (1). Then, the optimized ratio formula shown in Table 1 was used to optimize and predict the temperature (X4) and time (X5) for the preparation of silver-nanoparticle-complexed G. applanatum (Table 2). The computer-generated linear model is presented as Equation (2).
Yi = b0 + b1X1 + b2X2 + b3X3
Yi = b0 + b4X4 + b5X5
where Yi is the reasonable response (dependent variable) related to each factor level combined effect, b0 is an intercept, b1 to b5 are approximated regression coefficients calculated from the observed experimental values of Yi, and X1, X2, X3, X4, and X5 are the coded levels of the independent variables. The primary effects (X1, X2, X3, X4, and X5) reflect the typical outcomes of varying each factor from a low to a high level. The dependent variable (hydrodynamic particle diameter) and independent variables (silver nanoparticles, G. applanatum extract, ionic liquid, temperature, and time) were used for silver-nanoparticle-complexed G. applanatum preparation.

2.2.1. Particle Size

The silver-nanoparticle-complexed G. applanatum was diluted ten times with ultrapure water before particle size measurement was carried out using NanoPlus-3 (Micromeritics, Particulate Systems, Norcross, GA, USA). The particle size of the sample was determined using dynamic light scattering. Each sample was measured three times.

2.2.2. UV–Vis Spectra

A color change first indicated the presence of silver-nanoparticle-complexed G. applanatum. A UV/Visible scanning spectrophotometer (UV-1800, Shimadzu Corporation, Kyoto, Japan) was used at 420 nm with spectra ranging from 300 to 700 nm at room temperature, confirming the detection of G. applanatum by silver nanoparticles.

2.2.3. Antioxidant Activity Assay

The scavenging activity of 2,2-diphenyl-1-picrylhydrazyl hydrate (DPPH) (%) was determined using a previously published method [23]. In a 96-well plate, 100 microliters of the sample and quercetin were prepared and diluted, 100 L of DPPH was added, and the mixture was incubated in a dark room for 30 min. After mixing for 10 s, the reduction in color intensity caused by free radicals was measured at 517 nm. Quercetin concentrations ranging from 0.031 to 0.50 mg/mL were used. A sample with concentrations ranging from 0.031 to 1.00 mg/mL was then prepared. Data from three replicates were used to calculate the mean.
The total antioxidant content of the sample was also determined using the ferric reducing antioxidant power (FRAP) assay. In a 96-well plate, 20 microliters of the sample and ferrous sulfate heptahydrate were prepared and diluted, 180 L of FRAP reagent was then added, and the mixture was incubated at 37 °C for 6 min. Sample absorbance was measured at 593 nm. Concentrations of ferrous sulfate heptahydrate ranging from 0 to 278 µM were employed. The sample was prepared at concentrations ranging from 0 to 1 mg/mL. Data for three replicates were used to calculate the mean total antioxidant content based on IC50.

2.2.4. SEM and TEM

The sample was dropped on a copper stub and then kept at room temperature to evaporate the solvent. The sample was characterized by SEM, which was connected to an Everhart–Thornley detector (FESEM, Apreo, FEI, Amsterdam, The Netherlands).
The sample was fixed in 2.5% glutaraldehyde at room temperature overnight and then dehydrated in gradient alcohol (10–95%) for 20 min, followed by absolute alcohol for 2–5 min. The final specimen was coated with monolayer platinum to make the surface conduct. Field emission TEM was performed on a Thermo Scientific Talos F200i (FEI, Thermo Fisher Scientific, Waltham, MA, USA) operated at 200 kV accelerating voltage, and an AMT XR41-B 4-megapixel (2048 × 2048) CCD camera was used to image the sample.

2.3. Preparation of Topical Film Loaded with Silver-Nanoparticle-Complexed G. applanatum

A 10% w/w polyvinyl alcohol (PVA) solution was prepared in distilled water. PVA pellets (Mw 195,000, Sigma-Aldrich, St. Louis, MO, USA) were dissolved in hot distilled water and stirred continuously with a magnetic bar. The solution was allowed to cool to room temperature before being adjusted to 10% w/w with distilled water. Four grams of Eudragit® NM 30D (Jebsen & Jessen NutriLife, Bangkok, Thailand) and two grams of glycerin (P.C. drug center, Bangkok, Thailand) were combined in twenty grams of 10% w/w PVA solution. Two grams of silver-nanoparticle-complexed G. applanatum were then slowly incorporated into the polymer solution. About 25 g of the solution was poured into a Petri dish and dried at 70 ± 2 °C in a hot air oven (model JSOF-100, Gongju-City, Korea) until a complete film was obtained.

2.3.1. Characterization of Topical Film Loaded with Silver-Nanoparticle-Complexed G. applanatum

Folding Endurance

Folding the film sample repeatedly in the same area until it broke was used to test its folding endurance. The folding endurance was determined by counting the number of folds carried out before the film sample broke [24,25].

FTIR Spectrum

FTIR spectrometer (Vertex70, Bruker, Berlin, Germany) was used to examine the sample. The sample was scanned at a resolution of 4 cm−1 with 16 scans over a wavenumber region of 400–4000 cm−1. FTIR spectrum was recorded in absorption mode.

DSC

DSC equipment (DSC3+, METTLER TOLEDO, Greifensee, Switzerland) was used to examine the temperature behavior of the film sample at a rate of 10 °C/min from 25 °C to 400 °C. After being placed on an aluminum pan, the film sample was hermetically sealed. The DSC curves of the thermal properties of the film sample were obtained and reported.

TGA

TGA was performed in a TGA/DSC3+ (METTLER TOLEDO, Greifensee, Switzerland) from 50 to 650 °C under a nitrogen atmosphere (100 mL/min). Samples (5–10 mg) were analyzed in a TGA pan at a heating rate of 10 °C/min. TGA thermograms were produced, and the DTG was calculated.

XRD

An XRD instrument (Empyrean, PANalytical, Almelo, The Netherlands) was used to examine the crystallinity of the film sample. The operating voltage of the generator was 40 kV, and the current of the X-ray source was 45 mA with a stepped angle of 0.02°/s in the angular range of 5–40°.

SEM

An SEM connected to an Everhart–Thornley detector (FESEM, Apreo, FEI, Eindhoven, The Netherlands) was used to examine the cross-sectional morphology of the film sample. The produced film sample was directly coated with gold after being put on a copper stub.

2.3.2. Determination of the Content of Silver-Nanoparticle-Complexed G. applanatum in Topical Film

A total of 1 cm × 1 cm was taken from five different locations of the topical film loaded with silver-nanoparticle-complexed G. applanatum, which divided the film into small pieces. The sample was soaked in distilled water for 30 min before being sonicated. The solution was collected and diluted with distilled water to the appropriate concentration before being measured with a UV/Visible scanning spectrophotometer (UV-1800, Shimadzu Corporation, Kyoto, Japan) at 420 nm with spectra ranging from 300 to 700 nm at room temperature. The drug content average and standard deviation were reported.

2.3.3. In Vitro Release of Silver-Nanoparticle-Complexed G. applanatum from Topical Film

A total of 2 cm × 2 cm of topical film loaded with silver-nanoparticle-complexed G. applanatum was applied on the donor compartment of vertical Franz diffusion cells (EMFDC06, Orchid Scientific, Maharashtra, India) with an effective diffusion area of 1.77 cm2. The Franz cells were equipped with a dialysis cellulose membrane (MWCO: 3500 Da, CelluSep® T4, Membrane Filtration Product, Inc., Seguin, TX, USA), which was soaked overnight in a receptor medium at 32 ± 0.5 °C before use. The receptor medium was 12 mL of isotonic phosphate-buffered solution at pH 7.4 with a water jacket at 37 ± 0.5 °C, which was stirred constantly at 600 rpm with a magnetic stirrer. One mL of the receptor medium was withdrawn at 0.5, 1, 2, 4, 6, 8, 10, 12, and 24 h, and then this was immediately replaced by an equal volume of fresh isotonic phosphate-buffered solution at pH 7.4. The content of silver-nanoparticle-complexed G. applanatum was analyzed by the UV/Visible scanning spectrophotometer (UV-1800, Shimadzu Corporation, Kyoto, Japan), which was operated at 420 nm using spectra ranging from 300 to 700 nm at room temperature. The experiments for each sample were performed in triplicate.

2.3.4. Kinetic Models

Different mathematical models, namely the zero-order, first-order, and Higuchi empirical models, and the semi-empirical Korsmeyer–Peppas model, were used to characterize the silver-nanoparticle-complexed G. applanatum release kinetics. DDSolver was used to assess the kinetic models based on four models [26] following Equations (3)–(6).
Zero - order   model   Q t = Q 0 +   K 0 t
First - order   model   ln   Q t = ln   Q 0 K 1 t
Higuchi s   model   Q t = K H t
Korsmeyer Peppas   model   Q t Q 0 = K KP t n
where Q0 was the amount of initial drug and Qt was the amount of drug release or permeation in time (t).

2.3.5. In Vitro Permeation of Silver-Nanoparticle-Complexed G. applanatum from Topical Film

The 2 cm × 2 cm sample of topical film loaded with silver-nanoparticle-complexed G. applanatum was applied on the donor compartment of the vertical Franz diffusion cells (EMFDC06, Orchid Scientific, India) with an effective diffusion area of 1.77 cm2. The Franz cells were equipped with a dead pig ear skin sample that varied from 300 to 450 μm in thickness, which was soaked overnight in a receptor medium at 32 ± 0.5 °C before use. The receptor medium was 12 mL of isotonic phosphate-buffered solution at pH 7.4 with a water jacket at 37 ± 0.5 °C, which was stirred constantly at 600 rpm with a magnetic stirrer. One mL of the receptor medium was withdrawn at 0.5, 1, 2, 4, 6, 8, 10, 12, and 24 h, with this immediately being replaced by an equal volume of fresh isotonic phosphate-buffered solution at pH 7.4. The content of silver-nanoparticle-complexed G. applanatum was analyzed by the UV/Visible scanning spectrophotometer (UV-1800, Shimadzu Corporation, Kyoto, Japan), which was operated at 420 nm using spectra ranging from 300 to 700 nm at room temperature. The experiments for each sample were performed in triplicate.
The dead pig ear skin samples were taken out of the diffusion cells at the end of the in vitro skin permeation experiment and washed twice with 1 mL of distilled water to remove any residual residue from the skin’s surface. Every skin sample was divided into small pieces before being extracted in distilled water by homogenization and being sonicated for 60 min. Samples were centrifuged, and the supernatant was collected and then filtered through 0.45 µm syringe filters; the samples were then analyzed with the UV/Visible scanning spectrophotometer.

3. Results and Discussion

3.1. Optimization of Composition and Preparation Conditions of Silver-Nanoparticle-Complexed G. applanatum

For the preparation of the silver-nanoparticle-complexed G. applanatum, the particle size was optimized by the Design-Expert® program. Figure 2 shows the predicted ratios of the silver nanoparticles, G. applanatum extract, and ionic liquid in different combinations (Table 1). The linearity plot of the model ratios of the components’ predicted values vs. actual values is shown in Figure 3, which indicates a great correlation between the linear model and the data. The actual equation used to predict each dependent variable was Y = 421.03 − 3.73 (silver nanoparticles) + 23.19 (G. applanatum extract) + 1.69 (ionic liquid). The optimal ratio of the silver nanoparticles, G. applanatum extract, and the ionic liquid were 97:1:2. The ANOVA findings, which had an adequate precision of 8.3733, confirmed the model’s significance. Both the “predicted R-squared” value of 0.9994 and the “adjusted R-squared” value of 0.9430 were quite accurate. The probability of obtaining a significant “model F-value” due to noise was 0.01%, and the model’s F-value of 8.21 indicated that the model was significant. Furthermore, the signal-to-noise ratio was measured, and the range of the predicted values at the design points was compared to the average prediction error (a ratio larger than four is regarded as acceptable) [27]. As this ratio was found to be greater than four, this demonstrated that the model was suitable for predicting the findings inside the design space without the need for additional trials. The prediction value of the particle size for this optimal ratio was 85.87 nm. Next, the optimal ratio was then produced once again under the usage conditions of preparing the sample at 80 °C and agitating it for 2 h using a magnetic stirrer. This repeated preparation produced particles with a size of 91.50 ± 7.78 nm. [(Experimental value-predicted value/experimental value) × 100] was used to calculate the percent error of the prediction, which was found to be 6.15%.
After the optimal ratio of the silver nanoparticles, G. applanatum extract, and ionic liquid at 97:1:2 was accepted, the preparation conditions were next optimized and forecasted by the Design-Expert® program (Table 2). Figure 4a,b show the 3D response surface and contour plot of the predicted preparation conditions for the silver-nanoparticle-complexed G. applanatum. Figure 4c shows the linearity plot of the model for the preparation conditions as predicted values versus actual values, which showed a good correlation between the linear model and the data. The formula of Y = 138.47 − 0.75 (Temperature) − 14.25 (Time) was utilized to forecast each dependent variable. The ANOVA findings, which had an adequate precision of 11.0224, verified the significance of the model. The “predicted R-squared” value of 0.9896 and the “adjusted R-squared” value of 0.9802 were both extremely precise. The model’s F-value of 15.19 indicated that the model was significant, and the probability of a significant “model F-value” being obtained due to noise was 0.01%. The model was suitable for predicting the results inside the design space without the need for further trials, as shown by the fact that the ratio, in this case, was higher than four. The optimal preparation conditions for the silver-nanoparticle-complexed G. applanatum involved stirring the mixture at 80 °C for 1 h. Under these optimal preparation conditions, the predicted particle size was 93.06 nm. The optimal ratio for the silver-nanoparticle-complexed G. applanatum was then created again under the same conditions, which included preparing the mixture at 80 °C and stirring it for an hour with a magnetic stirrer. Particles measuring 97.50 ± 9.19 nm were obtained from this repeated preparation. The percent error of the prediction, which was found to be 4.55%, was calculated as [(Experimental value-predicted value/experimental value) × 100].
In summary, the Design-Expert® program’s optimization of the composition and preparation conditions of the silver nanoparticles was successful in demonstrating the low percent error of the prediction—less than 10%—which was satisfactory; this optimization was therefore accepted and used for the subsequent experiments. The 97:1:2 ratio of the silver nanoparticles: G. applanatum extract: ionic liquid was prepared by heating the mixture to 80 °C and stirring it for an hour with a magnetic stirrer to produce the silver-nanoparticle-complexed G. applanatum, which was utilized in the subsequent experiments. The synthesized silver-nanoparticle-complexed G. applanatum was observed the color changes and its characterizations were evaluated.
To effectively develop silver nanoparticles, capping and reducing agents, as well as reaction conditions, are required. On the other hand, the significant variations in the biochemical components of each G. applanatum fungal species may have a massive influence on the silver nanoparticle biosynthesis procedure. The availability of produce enzymes that catalyze the reducing and capping processes of silver nanoparticles is thought to make eukaryotic organisms, such as plants, fungi, protists, and algae, suitable candidates for the “green synthesis” of silver nanoparticles [6,28,29,30]. Consequently, the current work focused on the “green synthesis” of silver nanoparticles utilizing G. applanatum extract as a reducing and capping agent, followed by the structural and morphological characterization of the generated silver nanoparticles. The silver nanoparticles were prepared again under the optimized conditions: the ratio between the silver nanoparticles: G. applanatum extract: ionic liquid was 97:1:2, and the mixture was stirred on a hot plate at 80 °C with a magnetic stirrer for 2 h. The varied colors of the prepared solution are shown in Figure 5. The solution of pure G. applanatum extract was light orange color (Figure 5a). Silver nitrate, which was utilized as the starting solution in the preparation, was clear and colorless, but the silver nanoparticles using 0.07 M of NaBH4 as a reducing agent were a light yellow color (Figure 5b, left). The color changes, which indicated the creation of these nanoparticles, were due to the surface plasmon resonance of the silver nanoparticles [30]. The silver-nanoparticle-complexed G. applanatum, which was clear and dark brown (Figure 5b, right), was prepared using G. applanatum extract in place of the 0.07 M of NaBH4.

3.1.1. UV–Vis Spectra

The formation of silver-nanoparticle-complexed G. applanatum was observed using UV–visible spectroscopy. In previous studies, this approach has worked well for identifying surface plasmon resonance peaks. When the Ag electron is in the transmission band, it begins to vibrate in resonance with a specific wavelength of the light source, resulting in surface plasmon resonance peaks in silver nanoparticles [31]. The UV–visible absorption spectra of nanoparticles are shown in Figure 6, with the surface plasmon resonance peaking (maximum peak) at 419.5 nm for the silver nanoparticles without G. applanatum extract (Figure 6a) and 405.5 nm for the silver-nanoparticle-complexed G. applanatum (Figure 6b). The G. applanatum extract had high unexplained absorption in this UV–visible wavelength, suggesting that the extract might include several compounds (Figure 6d). Generally, silver nanoparticles have been found to have a significant and wide surface plasmon resonance peak between 410 and 450 nm, which was previously thought to be caused by spherical nanoparticles [10,32,33]. The primary absorption of the silver nanoparticle band was displaced to a lower absorption wavelength when the silver-nanoparticle-complexed G. applanatum was created, demonstrating that the synthesized silver-nanoparticle-complexed G. applanatum was an agglomeration and might have had various sizes and shapes. Furthermore, asymmetry and broadness were visible in the peak absorption of the silver-nanoparticle-complexed G. applanatum. This could have been affected by the incubation period and higher temperature, which have been found in a previous study to substantially increase the creation of silver-nanoparticle-complexed G. applanatum [6]. Additionally, the extracts may have led to an increase in agglomeration. The asymmetry and broadness of the peak absorption increased when the silver-nanoparticle-complexed G. applanatum was stored at room temperature for 1 month, which might have enhanced the agglomeration and size of the particles. However, it was observed that the maximum absorption at 405.5 nm did not change the unique absorption of the silver-nanoparticle-complexed G. applanatum (Figure 6c). The equation for the calibration curve for the silver-nanoparticle-complexed G. applanatum at 2.5–80 µg/mL was y = 0.0112x + 0.0282, and the linear regression coefficient (R2) was 0.9984. For this research work, this calibration curve was employed.

3.1.2. Antioxidant Activity Assay

The IC50 antioxidant activity of the selected silver-nanoparticle-complexed G. applanatum determined from the DPPH assay was 419 ± 0.016 µg/mL, whereas the IC50 of quercetin (positive control) was 141 ± 0.004 µg/mL. The IC50 antioxidant activity of the selected silver-nanoparticle-complexed G. applanatum determined from the FRAP assay was 500 ± 0.04 µg/mL, whereas the IC50 of quercetin (positive control) was 88.12 ± 13.5 µg/mL.

3.1.3. SEM

SEM and TEM images of the silver-nanoparticle-complexed G. applanatum that was produced under optimal conditions are shown in Figure 7. It was found that the particles of the silver-nanoparticle-complexed G. applanatum formed in spherical nanoparticles with a size of 18.64 ± 5.32 nm that were distributed on the stub (Figure 7a). Further information on the shape of the silver-nanoparticle-complexed G. applanatum was also presented by TEM photograph. The TEM investigation of the silver-nanoparticle-complexed G. applanatum, which had an average diameter of 21.61 ± 6.53 nm, also confirmed their spherical shape (Figure 7b). From the above section, the particle size of the silver-nanoparticle-complexed G. applanatum that was produced under optimal conditions was 97.50 ± 9.19 nm. Because the effect of a hydrodynamic diameter could be seen in the particle, which was measured by dynamic light scattering using the NanoPlus-3 instrument. Since this layer affects the particle’s movement, the so-called hydrodynamic particle diameter is often larger than that measured, for instance, using SEM and TEM. The liquid’s electrical conductivity is one of several variables that affect the layer’s thickness. The hydrodynamic particle diameter of the primary particles or agglomerates in the liquid is critical for determining the behavior of nanoelements in a fluid [34]. Thus, its particle size could be bigger than that determined by other methods such as SEM and TEM. Moreover, the XRD crystalline size of the silver-nanoparticle-complexed G. applanatum was supported by both the SEM and TEM data.

3.2. Preparation of Topical Film Loaded with Silver-Nanoparticle-Complexed G. applanatum

After the silver-nanoparticle-complexed G. applanatum was successfully prepared and investigated under the abovementioned optimal conditions, it was loaded in a topical film consisting of PVA, Eudragit® NM 30D as a polymer matrix, and glycerin as a plasticizer. The characterizations of a topical film were followed.

3.2.1. Characterization of Topical Film Loaded with Silver-Nanoparticle-Complexed G. applanatum

Folding Endurance

The blank film was a smooth, translucent, colorless yellow (Figure 8, left). The loading of the silver-nanoparticle-complexed G. applanatum caused the topical film to become more yellow (Figure 8, right). This occurred due to the silver-nanoparticle-complexed G. applanatum’s characteristic color (Figure 5, right). The test for the folding endurance of film involves repeatedly folding a piece of the film until it breaks, demonstrating that the film will remain intact when applied to the skin [35]. In this study, the blank film and topical film were found to have folding endurance values of 716 ± 26 and 712 ± 24 folds, respectively. The addition of silver-nanoparticle-complexed G. applanatum is no significant effect on the folding endurance. However, the produced topical film was able to adhere effectively to the skin throughout all periods of usage.

FTIR Spectrum

FTIR is a helpful technique for investigating the core–shell morphology of produced silver-nanoparticle-complexed G. applanatum. The method also extensively shows the chemical bonds and molecular structures involved in the stabilization and capping of silver-nanoparticle-complexed G. applanatum, as well as Ag+ bio-reduction [6]. The presence of a capping agent alongside the nanoparticles was found by the FTIR spectra shown in Figure 9a, which showed absorption bands at various wavenumbers. Table 3 provides a summary of the peak identification of the silver-nanoparticle-complexed G. applanatum. The presence of a capping agent alongside the nanoparticles was demonstrated by the absorption bands in the FTIR spectra at 3444, 2923, 1642, 1377, and 1024 cm−1. The main transmittance peaks of G. applanatum might have been located at 1024 cm−1. The primary absorption peaks of the blank film, which contained PVA, Eudragit® NM 30D, and glycerin as ingredients, are shown in Figure 9b and Table 3. The primary absorption peaks of the topical film loaded with silver-nanoparticle-complexed G. applanatum (Figure 9c) were similar to those of the blank film (Figure 9b). This occurred because there was a smaller quantity of silver-nanoparticle-complexed G. applanatum than blank film; consequently, the topical film showed characteristics more similar to the blank film. However, a wider absorption was found at 3309 cm−1 for the topical film. This might have been the consequence of combining the characteristics of the silver-nanoparticle-complexed G. applanatum and the blank film.

DSC

The main endothermic peaks of the silver-nanoparticle-complexed G. applanatum, blank film, and topical film were seen at 257.17, 286.50, and 294.17 °C, respectively, which can be interpreted as melting points (Figure 10). The minor endothermic peak of the topical film, which was seen at 229.50 °C, was broadened and shifted to lower temperatures in its curves, which was consistent with the presence of the silver-nanoparticle-complexed G. applanatum. Furthermore, there were no interactions or changes in the chemical structure of the topical film seen in the FTIR spectrum (Figure 9). Therefore, the silver-nanoparticle-complexed G. applanatum was often effectively entrapped in the topical film, with only minor shifts occurring in terms of widening or shifting towards a lower temperature of melting endothermic. These minor changes may just have been the result of the components being mixed, which reduces their purity but does not necessarily indicate a potential incompatibility.

TGA

The major weight losses of the silver-nanoparticle-complexed G. applanatum, blank film, and topical film were seen at 275.17, 335.17, and 336.89 °C, respectively (Figure 11), which may have been correlated with the DSC results. The topical film showed weight loss in the silver-nanoparticle-complexed G. applanatum at 250.73 °C. Therefore, this may have corroborated the presence of silver-nanoparticle-complexed G. applanatum in the topical film. Even though this weight loss was just a slight change, it had no effect because all the components of the topical film were compatible.

XRD

Silver nanoparticles have been found in the literature to have crystal characteristics at 38.23°, 44.42°, 64.44°, and 77.37° (2θ), which correspond to the fcc planes (111), (200), (220), and (311), respectively, [10,36], whereas in this study, the crystal characteristics of the silver-nanoparticle-complexed G. applanatum were found at 7.55°, 13.02°, 19.85°, 27.87°, 32.27°, 38.17°, 44.24°, 46.23°, 64.46°, and 76.73° (2θ). The silver-nanoparticle-complexed G. applanatum displayed the distinctive crystal properties of silver nanoparticles (Figure 12a). Thus, the silver nanoparticles’ composition in the silver-nanoparticle-complexed G. applanatum was verified. PVA, the main polymer in the composition of the topical film, which was detected at 2θ = 19.15°, was apparent in the blank film through its main semi-crystalline characteristics (Figure 12b). Strong intramolecular and intermolecular hydrogen connections exist between PVA and the main chain because of the OH groups’ binding to the major chain [24,25]. In this study, because the silver-nanoparticle-complexed G. applanatum was present in significantly lower amounts than the blank film in the topical film, the topical film showed a semi-crystalline structure that was more closely related to the characteristics of the blank film (Figure 12c).

SEM

The cross-sectional morphologies of the blank film and topical film (magnified by 5000×) are shown in Figure 10b and Figure 13a, respectively. The image shown in Figure 13c, which was magnified by 100,000×, portrays the cross-sectional morphology of the topical film. The blank film had a smooth, compact layer that was absent of porosity, cracks, and cavities (Figure 13a). The layer of the topical film was denser than that of the blank film and had a roughness devoid of pores, cracks, and cavities (Figure 13b). However, the cross-sectional morphology of the topical film did not show the particles of the silver-nanoparticle-complexed G. applanatum; therefore, it was magnified at a factor of 100,000× (Figure 13c). The particles of the silver-nanoparticle-complexed G. applanatum were found to have small particles that were distributed throughout the topical film. Therefore, it can be assumed that the topical film had silver particles within it.

3.2.2. Determination of the Content of Silver-Nanoparticle-Complexed G. applanatum in Topical Film

The topical film was produced with a silver-nanoparticle-complexed G. applanatum concentration of 49.09 ± 9.25 µg/cm2. In a previous study, a nanocomposite film with a surface area of 15 cm2 was found to contain 540 µg of silver content, had good mechanical strength and stability under storage for easy handling in an aqueous medium, and exhibited high trace metal sorption activity when subjected to optimum chemical conditions [37]. Therefore, in this study, the quantity of silver-nanoparticle-complexed G. applanatum in the topical film, which had a surface area of 15 cm2, was estimated to be 736.31 ± 138.82 µg, meaning it could be effectively used in applications. Additionally, this quantity in the topical film was more potent than the IC50 estimate.

3.2.3. In Vitro Release of Silver-Nanoparticle-Complexed G. applanatum from Topical Film

Figure 14 shows the release profiles of the silver-nanoparticle-complexed G. applanatum from the solution and topical film. The silver-nanoparticle-complexed G. applanatum was able to quickly diffuse and be released from the solution into the receptor medium within 2 h. This occurred because the solution was easily dispersed in water and rapidly passed through the cellulose dialysis membrane. Furthermore, the silver-nanoparticle-complexed G. applanatum was easily released from the topical film. When the receptor medium entered the polymer matrix, there was a chance that the matrix would have swelled or eroded, which would then have caused the diffusion of the active compound or its dissolution [38]. For the silver-nanoparticle-complexed G. applanatum without ionic liquid, distilled water was used in place of the ionic liquid during the preparation procedure; it was subsequently mixed with the topical film. It was found that its release profile from the topical film did not show significant differences from the original silver-nanoparticle-complexed G. applanatum.

3.2.4. Kinetic Models

The release of silver-nanoparticle-complexed G. applanatum from their formula was evident, as shown by a comparison of the R2 values of the zero-order, first-order, and Higuchi models (as shown in Table 4), wherein the R2 value of the Higuchi model was higher in both cases than the values of the zero-order and first-order models. Additionally, it was clear that the release of the silver-nanoparticle-complexed G. applanatum was controlled by both diffusion and dissolution mechanisms, which suggests that the drug was released from the topical film [39]. The Higuchi model, as the most precise model, was used to estimate the release rates of the silver-nanoparticle-complexed G. applanatum from the solution and the topical film. The release rate of the silver-nanoparticle-complexed G. applanatum from the solution was higher than its release rates from the topical films, which were correlated with the release profile (Figure 14). These findings were due to the fact that the silver-nanoparticle-complexed G. applanatum was able to diffuse and be released from the solution into the receptor media within 2 h. The release rate of the silver-nanoparticle-complexed G. applanatum from the topical film was decreased from 30.942 ± 2.444 %/ min to 30.060 ± 2.757 %/ min when the ionic liquid was replaced with distilled water. Thus, there is no effect when replacing the ionic liquid with distilled water.
The release of the silver-nanoparticle-complexed G. applanatum from the topical films showed diffusion exponent n-values of 0.440 and 0.478, according to the Korsmeyer–Peppas model. Because the diffusion exponent n-values were less than 0.5, Fickian diffusion was utilized to describe how the silver-nanoparticle-complexed G. applanatum was released from the topical films. When the polymer relaxation time is significantly longer than the typical solvent diffusion period, the process of solute transport is referred to as Fickian diffusion [38,40,41]. In conclusion, in this study, it was shown that the release of the silver-nanoparticle-complexed G. applanatum from the topical films was most probably caused by a diffusion-controlled process.

3.2.5. In Vitro Permeation of Silver-Nanoparticle-Complexed G. applanatum from Topical Film

An in vitro permeation investigation was carried out to evaluate the potential for silver-nanoparticle-complexed G. applanatum dispersions to permeate the dermis and epidermis of dead pig ear skin. The permeation of potentially topical drugs is often assessed using in vitro methods involving skin taken from an animal. The stratum corneum’s permeability characteristics, which may be thought of as the rate-limiting stage for skin absorption, remain unaltered after its removal from the body, allowing for direct comparison [42]. In this study, less than 5% of the silver-nanoparticle-complexed G. applanatum’s in vitro skin permeation through the dead pig ear skin into the receptor medium was detected after 24 h of testing, suggesting there was a low amount of silver-nanoparticle-complexed G. applanatum permeation. The stratum corneum acted as a barrier to the silver-nanoparticle-complexed G. applanatum’s permeation through the dead pig ear skin, in contrast to the in vitro release investigation [38,43]. These findings are consistent with other studies, which found that when skin is assessed with intact tissue, fewer silver nanoparticles are found in the receptor compartment [42,44]. Figure 15 shows the accumulation of the silver-nanoparticle-complexed G. applanatum following complete in vitro skin permeation. The quantity of silver-nanoparticle-complexed G. applanatum that accumulated in the dead pig ear skin after the 24-h in vitro permeation study was 28.77 ± 4.68 μg/cm2 (58.61 ± 9.53 %), while the quantity of the silver-nanoparticle-complexed G. applanatum without ionic liquid that accumulated was 17.30 ± 4.86 μg/cm2 (34.09 ± 9.57 %). Meanwhile, the amount of silver-nanoparticle-complexed G. applanatum deposition in the topical film was lower than that of the silver-nanoparticle-complexed G. applanatum without ionic liquid. Thus, it was evident from the diffusion investigation that for the small-sized silver-nanoparticle-complexed G. applanatum, more nanoparticles retained localized in the skin, and fewer of these penetrated the receptor compartment. According to studies on silver [42] and metallic [45] nanoparticles, small nanoparticles may penetrate the skin’s stratum corneum and hair follicle orifices and reach the stratum corneum’s deepest levels while remaining outside the skin’s surface. These studies hypothesized that because these nanoparticles have such a localizing impact on the skin, they will be useful in topical applications that reduce toxic effects.
In addition to their traditional uses as synthesis catalysts and solvents in chemistry, ionic drugs have been used in pharmaceutical applications in order to improve the dissolution, solubility, and bioavailability of drugs. When making an ionic liquid, inactive counter ions are typically used [46,47]. In the current investigation, an ionic liquid based on 1-butyl-3-methylimidazolium bromide appeared to demonstrate some efficacy in increasing silver-nanoparticle-complexed G. applanatum skin permeability, namely by approximately 1.7 fold. The cause of this improvement was the lipid extraction of the ionic liquid based on 1-butyl-3-methylimidazolium bromide, which might also have diffused into the stratum corneum, reduced the inter-lipid interactions, and extracted the lipids into the ionic liquid reservoir on the skin surface, thereby increasing the silver-nanoparticle-complexed G. applanatum permeation into the skin. Similar to this research, ionic liquids have recently been used to solve the permeability and solubility issues that the majority of drugs designed for skin delivery experience [48,49].

4. Conclusions

The purpose of this work was to develop and investigate the effect of ionic liquid based on 1-butyl-3-methylimidazolium bromide on the silver-nanoparticle-complexed G. applanatum loaded into a topical film. The experiments carried out employed the best ratio and preparation conditions. The optimal ratio of silver nanoparticles: G. applanatum extract: ionic liquid was set at 97:1:2, with the mixture incubating for an hour at 80 °C. As the prediction had a low percentage error, it was verified. The silver-nanoparticle-complexed G. applanatum solution was transparent and dark brown. The maximum peak absorption of the silver-nanoparticle-complexed G. applanatum was detected in the UV–visible absorption spectra at 405.5 nm. The optimized silver-nanoparticle-complexed G. applanatum was loaded into a topical film made of PVA and Eudragit®, and its properties were evaluated. When the silver-nanoparticle-complexed G. applanatum was loaded into the topical film, the film became yellow. The topical film had many desired properties, as well as being uniform, smooth, and compact. Furthermore, silver-nanoparticle-complexed G. applanatum was detected in the topical film. The topical film’s components were all compatible; therefore, even if there were small changes to any of them, they had no effect. It was calculated that there was 736.31 ± 138.82 µg of silver-nanoparticle-complexed G. applanatum in the topical film, which had a surface area of 15 cm2. This product may be utilized for effective applications. Furthermore, the concentration in the topical film was more potent than the IC50 estimation. The topical film also had control over the matrix-layer-mediated release of the silver-nanoparticle-complexed G. applanatum. The release kinetic was fitted using the Higuchi model. It was demonstrated that a diffusion-controlled process was most likely to be responsible for the release of the silver-nanoparticle-complexed G. applanatum from the topical films. In a 24-h in vitro permeation investigation, the quantity of the silver-nanoparticle-complexed G. applanatum that accumulated in the dead pig ear skin was 28.77 ± 4.68 μg/cm2 (58.61 ± 9.53 %), whereas the quantity of the silver-nanoparticle-complexed G. applanatum without ionic liquid that accumulated was 17.30 ± 4.86 μg/cm2 (34.09 ± 9.57 %). Thus, ionic liquid based on 1-butyl-3-methylimidazolium bromide, which might improve solubility, increased the skin accumulation of the silver-nanoparticle-complexed G. applanatum by about 1.7 times. Furthermore, it was clear from the research that the silver-nanoparticle-complexed G. applanatum remained in the skin rather than penetrating the receptor compartment. The produced film is appropriate for topical applications and may be used in the development of potential future pharmaceutical products for the treatment of diseases.

Author Contributions

Conceptualization, W.P. and J.S.; methodology, P.M., C.M., T.W. and N.D.; software, C.M.; validation, J.S., P.M. and C.M.; formal analysis, J.S., P.M. and C.M.; investigation, J.S., N.D. and P.M.; resources, C.M. and N.D.; data curation, W.P., J.S., P.M., N.D., T.W. and C.M.; writing—original draft preparation, P.M., C.M., W.P. and J.S.; writing—review and editing, W.P. and J.S.; visualization, J.S.; supervision, J.S.; project administration, J.S.; funding acquisition, J.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Research Institute of Rangsit University, Thailand, grant number 25/2565.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors would like to thank the research assistants Kridsada Suwanna, Wachirawit Pisanpathom, Jessada Prasomkij, and Chanchai Suwanlaong. The Eudragit® used in this study was provided by Jebsen & Jessen NutriLife Ltd., for which the authors are grateful.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Sharma, V.K.; Yngard, R.A.; Lin, Y. Silver nanoparticles: Green synthesis and their antimicrobial activities. Adv. Colloid Interface Sci. 2009, 145, 83–96. [Google Scholar] [CrossRef] [PubMed]
  2. Beyene, H.D.; Werkneh, A.A.; Bezabh, H.K.; Ambaye, T.G. Synthesis paradigm and applications of silver nanoparticles (AgNPs), a review. Sustain. Mater. Technol. 2017, 13, 18–23. [Google Scholar] [CrossRef]
  3. Tsivileva, O.; Pankratov, A.; Misin, V.; Zavyalov, A.; Volkov, V.; Tsymbal, O.; Yurasov, N.; Nikitina, V.E. Antioxidant properties of the artist’s conk medicinal mushroom, Ganoderma applanatum (Agaricomycetes), upon cultivation with para-substituted phenolic compounds and tea leaf extracts. Int. J. Med. Mushrooms 2018, 20, 549–560. [Google Scholar] [CrossRef] [PubMed]
  4. Elkhateeb, W.; Daba, G.; El-Dein, A.; Sheir, D.; Fayad, W.; Shaheen, M.; Elmahdy, E.; Wen, T.-C. Insights into the in-vitro hypocholesterolemic, antioxidant, antirotavirus, and anticolon cancer activities of the methanolic extracts of a Japanese lichen, Candelariella vitellina, and a Japanese mushroom, Ganoderma applanatum. Egypt. Pharm. J. 2020, 19, 67–73. [Google Scholar] [CrossRef]
  5. Mohammadifar, S.; Fallahi Gharaghoz, S.; Asef Shayan, M.R.; Vaziri, A. Comparison between antioxidant activity and bioactive compounds of Ganoderma applanatum (Pers.) Pat. and Ganoderma lucidum (Curt.) P. Karst from Iran. Iran. J. Plant Physiol. 2020, 11, 3417–3424. [Google Scholar] [CrossRef]
  6. Jogaiah, S.; Kurjogi, M.; Abdelrahman, M.; Hanumanthappa, N.; Tran, L.-S.P. Ganoderma applanatum-mediated green synthesis of silver nanoparticles: Structural characterization, and in vitro and in vivo biomedical and agrochemical properties. Arab. J. Chem. 2019, 12, 1108–1120. [Google Scholar] [CrossRef]
  7. Jeong, Y.-T.; Yang, B.-K.; Jeong, S.-C.; Kim, S.-M.; Song, C.-H. Ganoderma applanatum: A promising mushroom for antitumor and immunomodulating activity. Phytother. Res. 2008, 22, 614–619. [Google Scholar] [CrossRef]
  8. Sun, X.; Zhao, C.; Pan, W.; Wang, J.; Wang, W. Carboxylate groups play a major role in antitumor activity of Ganoderma applanatum polysaccharide. Carbohydr. Polym. 2015, 123, 283–287. [Google Scholar] [CrossRef]
  9. Elkhateeb, W.A.; Zaghlol, G.M.; El-Garawani, I.M.; Ahmed, E.F.; Rateb, M.E.; Abdel Moneim, A.E. Ganoderma applanatum secondary metabolites induced apoptosis through different pathways: In vivo and in vitro anticancer studies. Biomed. Pharmacother. 2018, 101, 264–277. [Google Scholar] [CrossRef] [Green Version]
  10. Suksaeree, J.; Thuengernthong, A.; Pongpichayasiri, K.; Maneewattanapinyo, P.; Settharaksa, S.; Pichayakorn, W. Formulation and evaluation of matrix type transdermal patch containing silver nanoparticles. J. Polym. Environ. 2018, 26, 4369–4375. [Google Scholar] [CrossRef]
  11. Qin, Y.; Xiong, L.; Li, M.; Liu, J.; Wu, H.; Qiu, H.; Mu, H.; Xu, X.; Sun, Q. Preparation of bioactive polysaccharide nanoparticles with enhanced radical scavenging activity and antimicrobial activity. J. Agric. Food Chem. 2018, 66, 4373–4383. [Google Scholar] [CrossRef] [PubMed]
  12. Vijayan, R.; Joseph, S.; Mathew, B. Eco-friendly synthesis of silver and gold nanoparticles with enhanced antimicrobial, antioxidant, and catalytic activities. IET Nanobiotechnol. 2018, 12, 850–856. [Google Scholar] [CrossRef] [PubMed]
  13. Ali, M.K.; Moshikur, R.M.; Wakabayashi, R.; Moniruzzaman, M.; Kamiya, N.; Goto, M. Biocompatible ionic liquid surfactant-based microemulsion as a potential carrier for sparingly soluble drugs. ACS Sustain. Chem. Eng. 2020, 8, 6263–6272. [Google Scholar] [CrossRef]
  14. Zhuang, W.; Hachem, K.; Bokov, D.; Javed Ansari, M.; Taghvaie Nakhjiri, A. Ionic liquids in pharmaceutical industry: A systematic review on applications and future perspectives. J. Mol. Liq. 2022, 349, 118145. [Google Scholar] [CrossRef]
  15. Kubota, K.; Shibata, A.; Yamaguchi, T. The molecular assembly of the ionic liquid/aliphatic carboxylic acid/aliphatic amine as effective and safety transdermal permeation enhancers. Eur. J. Pharm. Sci. 2016, 86, 75–83. [Google Scholar] [CrossRef] [PubMed]
  16. Zakrewsky, M.; Mitragotri, S. Therapeutic RNAi robed with ionic liquid moieties as a simple, scalable prodrug platform for treating skin disease. J. Control. Release 2016, 242, 80–88. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  17. Park, H.J.; Prausnitz, M.R. Lidocaine-ibuprofen ionic liquid for dermal anesthesia. AIChE J. 2015, 61, 2732–2738. [Google Scholar] [CrossRef]
  18. Wang, C.; Zhu, J.; Zhang, D.; Yang, Y.; Zheng, L.; Qu, Y.; Yang, X.; Cui, X. Ionic liquid—Microemulsions assisting in the transdermal delivery of Dencichine: Preparation, in-vitro and in-vivo evaluations, and investigation of the permeation mechanism. Int. J. Pharm. 2018, 535, 120–131. [Google Scholar] [CrossRef]
  19. Monti, D.; Egiziano, E.; Burgalassi, S.; Chetoni, P.; Chiappe, C.; Sanzone, A.; Tampucci, S. Ionic liquids as potential enhancers for transdermal drug delivery. Int. J. Pharm. 2017, 516, 45–51. [Google Scholar] [CrossRef] [PubMed]
  20. Dobler, D.; Schmidts, T.; Klingenhöfer, I.; Runkel, F. Ionic liquids as ingredients in topical drug delivery systems. Int. J. Pharm. 2013, 441, 620–627. [Google Scholar] [CrossRef]
  21. Priyanka, K.; Kumar, G.; Uttam Singh, B. Novel herbal topical patch containing Curcumin and Arnica montana for the treatment of osteoarthritis. Curr. Rheumatol. Rev. 2020, 16, 43–60. [Google Scholar] [CrossRef]
  22. Dandapat, S.; Kumar, M.; Ranjan, R.; Sinha, M.P. Ganoderma applanatum extract mediated synthesis of silver nanoparticles. Braz. J. Pharm. Sci. 2022, 58, e19173. [Google Scholar] [CrossRef]
  23. Li, M.-X.; Bai, X.; Ma, Y.-P.; Zhang, H.-X.; Nama, N.; Pei, S.-J.; Du, Z.-Z. Cosmetic potentials of extracts and compounds from Zingiber cassumunar Roxb. rhizome. Ind. Crops Prod. 2019, 141, 111764. [Google Scholar] [CrossRef]
  24. Pichayakorn, W.; Monton, C.; Sampaopan, Y.; Panrat, K.; Suksaeree, J. Fabrication and characterization of buccal film loaded self-emulsifying drug delivery system containing Lysiphyllum strychnifolium stem extracts. AAPS PharmSciTech 2022, 23, 194. [Google Scholar] [CrossRef]
  25. Pichayakorn, W.; Maneewattanapinyo, P.; Panrat, K.; Monton, C.; Suksaeree, J. Formulation design of oral strip-films based on PVA/PVP polymer blends for nicotine delivery. J. Polym. Environ. 2022, 30, 4479–4491. [Google Scholar] [CrossRef]
  26. Zhang, Y.; Huo, M.; Zhou, J.; Zou, A.; Li, W.; Yao, C.; Xie, S. DDSolver: An add-in program for modeling and comparison of drug dissolution profiles. AAPS J. 2010, 12, 263–271. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Costa, S.; Barroso, M.; Castañera, A.; Dias, M. Design of experiments, a powerful tool for method development in forensic toxicology: Application to the optimization of urinary morphine 3-glucuronide acid hydrolysis. Anal. Bioanal. Chem. 2010, 396, 2533–2542. [Google Scholar] [CrossRef] [PubMed]
  28. Quester, K.; Ávalos Borja, M.; Castro Longoria, E. Controllable biosynthesis of small silver nanoparticles using fungal extract. J. Biomat. Nanobiotechnol. 2016, 7, 118–125. [Google Scholar] [CrossRef] [Green Version]
  29. Li, X.; Xu, H.; Chen, Z.-S.; Chen, G. Biosynthesis of nanoparticles by microorganisms and their applications. J. Nanomater. 2011, 2011, 270974. [Google Scholar] [CrossRef] [Green Version]
  30. Rahi, D.K.; Madhurika, B. Biosynthesis of silver nanoparticles by Ganoderma applanatum, evaluation of their antibacterial and antibiotic activity enhancing potential. World J. Pharma. Pharm. 2015, 4, 1234–1247. [Google Scholar]
  31. Ullah, H.; Wilfred, C.D.; Shaharun, M.S. Synthesis of silver nanoparticles using ionic-liquid-based microwave-assisted extraction from Polygonum minus and photodegradation of methylene blue. J. Chin. Chem. Soc. 2017, 64, 1164–1171. [Google Scholar] [CrossRef]
  32. Dong, Y.; Zhu, H.; Shen, Y.; Zhang, W.; Zhang, L. Antibacterial activity of silver nanoparticles of different particle size against Vibrio Natriegens. PLoS ONE 2019, 14, e0222322. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  33. Jyoti, K.; Baunthiyal, M.; Singh, A. Characterization of silver nanoparticles synthesized using Urtica dioica Linn. leaves and their synergistic effects with antibiotics. J. Rad. Res. Appl. Sci. 2016, 9, 217–227. [Google Scholar] [CrossRef] [Green Version]
  34. Menéndez-Manjón, A.; Chichkov, B.N.; Barcikowski, S. Influence of water temperature on the hydrodynamic diameter of gold nanoparticles from laser ablation. J. Phys. Chem. C 2010, 114, 2499–2504. [Google Scholar] [CrossRef]
  35. Alsofany, J.M.; Hamza, M.Y.; Abdelbary, A.A. Fabrication of nanosuspension directly loaded fast-dissolving films for enhanced oral bioavailability of olmesartan medoxomil: In vitro characterization and pharmacokinetic evaluation in healthy human volunteers. AAPS PharmSciTech 2018, 19, 2118–2132. [Google Scholar] [CrossRef]
  36. Singh, S.; Bharti, A.; Meena, V.K. Structural, thermal, zeta potential and electrical properties of disaccharide reduced silver nanoparticles. J. Mater. Sci. Mater. Electron. 2014, 25, 3747–3752. [Google Scholar] [CrossRef]
  37. Djerahov, L.; Vasileva, P.; Karadjova, I.; Kurakalva, R.M.; Aradhi, K.K. Chitosan film loaded with silver nanoparticles—Sorbent for solid phase extraction of Al(III), Cd(II), Cu(II), Co(II), Fe(III), Ni(II), Pb(II) and Zn(II). Carbohydr. Polym. 2016, 147, 45–52. [Google Scholar] [CrossRef]
  38. Monton, C.; Sampaopan, Y.; Pichayakorn, W.; Panrat, K.; Suksaeree, J. Herbal transdermal patches made from optimized polyvinyl alcohol blended film: Herbal extraction process, film properties, and in vitro study. J. Drug Deliv. Sci. Technol. 2022, 69, 103170. [Google Scholar] [CrossRef]
  39. Suksaeree, J.; Waiprib, R.; Pichayakorn, W. Improving the hydrophilic properties of deproteinized natural rubber latex films for lidocaine transdermal patches by starch blending. J. Polym. Environ. 2022, 30, 1574–1586. [Google Scholar] [CrossRef]
  40. Fu, Y.; Kao, W.J. Drug release kinetics and transport mechanisms of non-degradable and degradable polymeric delivery systems. Expert Opin. Drug Deliv. 2010, 7, 429–444. [Google Scholar] [CrossRef]
  41. Olejnik, A.; Kapuscinska, A.; Schroeder, G.; Nowak, I. Physico-chemical characterization of formulations containing endomorphin-2 derivatives. Amino Acids 2017, 49, 1719–1731. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  42. Dhar, S.; Murawala, P.; Shiras, A.; Pokharkar, V.; Prasad, B.L.V. Gellan gum capped silver nanoparticle dispersions and hydrogels: Cytotoxicity and in vitro diffusion studies. Nanoscale 2012, 4, 563–567. [Google Scholar] [CrossRef] [PubMed]
  43. Sampaopan, Y.; Suksaeree, J. Formulation development and pharmaceutical evaluation of Lysiphyllum strychnifolium topical patches for their anti-inflammatory potential. AAPS PharmSciTech 2022, 23, 116. [Google Scholar] [CrossRef]
  44. Larese, F.F.; D’Agostin, F.; Crosera, M.; Adami, G.; Renzi, N.; Bovenzi, M.; Maina, G. Human skin penetration of silver nanoparticles through intact and damaged skin. Toxicology 2009, 255, 33–37. [Google Scholar] [CrossRef]
  45. Baroli, B.; Ennas, M.G.; Loffredo, F.; Isola, M.; Pinna, R.; Arturo López-Quintela, M. Penetration of metallic nanoparticles in human full-thickness skin. J. Investig. Dermatol. 2007, 127, 1701–1712. [Google Scholar] [CrossRef]
  46. Miwa, Y.; Hamamoto, H.; Ishida, T. Lidocaine self-sacrificially improves the skin permeation of the acidic and poorly water-soluble drug etodolac via its transformation into an ionic liquid. Eur. J. Pharm. Biopharm. 2016, 102, 92–100. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  47. Marrucho, I.; Branco, L.; Rebelo, L. Ionic liquids in pharmaceutical applications. Annu. Rev. Chem. Biomol. Eng. 2014, 5, 527–546. [Google Scholar] [CrossRef]
  48. Tanner, E.E.L.; Ibsen, K.N.; Mitragotri, S. Transdermal insulin delivery using choline-based ionic liquids (CAGE). J. Control. Release 2018, 286, 137–144. [Google Scholar] [CrossRef]
  49. Wu, X.; Chen, Z.; Li, Y.; Yu, Q.; Lu, Y.; Zhu, Q.; Li, Y.; An, D.; Qi, J.; Wu, W. Improving dermal delivery of hydrophilic macromolecules by biocompatible ionic liquid based on choline and malic acid. Int. J. Pharm. 2019, 558, 380–387. [Google Scholar] [CrossRef]
Figure 1. The appearance of G. applanatum in different forms.
Figure 1. The appearance of G. applanatum in different forms.
Pharmaceutics 15 01098 g001
Figure 2. (left) 3D response surface and (right) contour plot of model conditions of silver-nanoparticle-complexed G. applanatum: silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) as independent variables, and particle size as a dependent variable. (a) X3 = 2, (b) X3 = 4, and (c) X3 = 6.
Figure 2. (left) 3D response surface and (right) contour plot of model conditions of silver-nanoparticle-complexed G. applanatum: silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) as independent variables, and particle size as a dependent variable. (a) X3 = 2, (b) X3 = 4, and (c) X3 = 6.
Pharmaceutics 15 01098 g002aPharmaceutics 15 01098 g002b
Figure 3. Predicted versus actual plots of model conditions of silver-nanoparticle-complexed G. applanatum: silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) as independent variables, and particle size as a dependent variable.
Figure 3. Predicted versus actual plots of model conditions of silver-nanoparticle-complexed G. applanatum: silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) as independent variables, and particle size as a dependent variable.
Pharmaceutics 15 01098 g003
Figure 4. (a) 3D response surface, (b) contour plot, and (c) predicted versus actual plots of model conditions of silver-nanoparticle-complexed G. applanatum: temperature (X4) and time (X5) as independent variables and particle size as a dependent variable.
Figure 4. (a) 3D response surface, (b) contour plot, and (c) predicted versus actual plots of model conditions of silver-nanoparticle-complexed G. applanatum: temperature (X4) and time (X5) as independent variables and particle size as a dependent variable.
Pharmaceutics 15 01098 g004
Figure 5. (a) Solution of pure G. applanatum extract and (b) silver nanoparticles were synthesized under optimal conditions: (left) without G. applanatum extract and (right) with G. applanatum extract.
Figure 5. (a) Solution of pure G. applanatum extract and (b) silver nanoparticles were synthesized under optimal conditions: (left) without G. applanatum extract and (right) with G. applanatum extract.
Pharmaceutics 15 01098 g005
Figure 6. UV–Vis spectra of (a) silver nanoparticles without G. applanatum extract synthesized under optimal conditions, (b) silver-nanoparticle-complexed G. applanatum synthesized under optimal conditions, (c) silver-nanoparticle-complexed G. applanatum synthesized under optimal conditions after storage at room temperature for 1 month, and (d) G. applanatum extract.
Figure 6. UV–Vis spectra of (a) silver nanoparticles without G. applanatum extract synthesized under optimal conditions, (b) silver-nanoparticle-complexed G. applanatum synthesized under optimal conditions, (c) silver-nanoparticle-complexed G. applanatum synthesized under optimal conditions after storage at room temperature for 1 month, and (d) G. applanatum extract.
Pharmaceutics 15 01098 g006
Figure 7. (a) SEM: 200,000× and (b) TEM: 74,000× images of silver-nanoparticle-complexed G. applanatum produced under optimal conditions.
Figure 7. (a) SEM: 200,000× and (b) TEM: 74,000× images of silver-nanoparticle-complexed G. applanatum produced under optimal conditions.
Pharmaceutics 15 01098 g007
Figure 8. (left) Blank film and (right) topical film containing silver-nanoparticle-complexed G. applanatum.
Figure 8. (left) Blank film and (right) topical film containing silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g008
Figure 9. FTIR spectra of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Figure 9. FTIR spectra of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g009
Figure 10. DSC thermograms of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Figure 10. DSC thermograms of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g010
Figure 11. (a) TGA and (b) DTG thermograms of silver-nanoparticle-complexed G. applanatum, blank film, and topical film containing silver-nanoparticle-complexed G. applanatum.
Figure 11. (a) TGA and (b) DTG thermograms of silver-nanoparticle-complexed G. applanatum, blank film, and topical film containing silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g011
Figure 12. XRD patterns of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Figure 12. XRD patterns of (a) silver-nanoparticle-complexed G. applanatum, (b) blank film, and (c) topical film containing silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g012
Figure 13. Cross-sectional morphologies of the blank film (a) at 5000× and topical film containing silver-nanoparticle-complexed G. applanatum (b) at 5000× and (c) 100,000×.
Figure 13. Cross-sectional morphologies of the blank film (a) at 5000× and topical film containing silver-nanoparticle-complexed G. applanatum (b) at 5000× and (c) 100,000×.
Pharmaceutics 15 01098 g013
Figure 14. Release profile of silver-nanoparticle-complexed G. applanatum from the topical film.
Figure 14. Release profile of silver-nanoparticle-complexed G. applanatum from the topical film.
Pharmaceutics 15 01098 g014
Figure 15. Silver-nanoparticle-complexed G. applanatum accumulation in dead pig ear skin and topical film: (a) content and (b) percentage of silver-nanoparticle-complexed G. applanatum.
Figure 15. Silver-nanoparticle-complexed G. applanatum accumulation in dead pig ear skin and topical film: (a) content and (b) percentage of silver-nanoparticle-complexed G. applanatum.
Pharmaceutics 15 01098 g015
Table 1. Ratio optimization of silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) by the Design-Expert® program (Stat-Ease, Inc.).
Table 1. Ratio optimization of silver nanoparticles (X1), G. applanatum extract (X2), and ionic liquid (X3) by the Design-Expert® program (Stat-Ease, Inc.).
SampleSilver NanoparticlesG. applanatum ExtractIonic Liquid
(X1)(X2)(X3)
1.19114
1.29714
1.39134
1.49734
1.59122
1.69722
1.79126
1.89726
1.99412
1.109432
1.119416
1.129436
1.139424
Table 2. Condition optimization for ratio optimization shown in Table 1 by the Design-Expert® program (Stat-Ease, Inc.).
Table 2. Condition optimization for ratio optimization shown in Table 1 by the Design-Expert® program (Stat-Ease, Inc.).
SampleTemperature (°C)Time (h)
(X4)(X5)
2.1401
2.2402
2.3403
2.4601
2.5602
2.6603
2.7801
2.8802
2.9803
Table 3. Identification of the main peaks from reported FTIR spectra.
Table 3. Identification of the main peaks from reported FTIR spectra.
Wavenumber (cm−1)Peak Assignment
Silver-nanoparticle-complexed G. applanatum
3444O–H stretching in alcohol and phenol and N–H stretching in primary and secondary amide
2923C–H stretching
1642C=N stretching in amide and C=O stretching in an unsaturated aromatic carboxylic acid
1457C=O and N–O stretching in ester and nitro groups
1377C–O stretching in an aromatic compound
1024C–F stretching in fluroalkanes
936C=C stretching in alkanes and O–H stretching
Blank film
3309O–H stretching
2938, 2892C–H stretching
1730C=O stretching in ester
1443C–H bending
1241C–O stretching or –O–CH2–C
1110C–C stretching and C–H bending
1036C–O stretching and C–H bending
848O–H bending
Table 4. Kinetic models of release for the silver-nanoparticle-complexed G. applanatum profiles from their formula.
Table 4. Kinetic models of release for the silver-nanoparticle-complexed G. applanatum profiles from their formula.
R2nRelease Rate
(KH) * (%/ min )
Zero OrderFirst Order Higuchi Korsmeyer–Peppas
Silver-nanoparticle-complexed G. applanatum from the solution0.96510.98990.9909-69.254 ± 7.566
Silver-nanoparticle-complexed G. applanatum from the topical film0.93790.99230.99320.44030.942 ± 2.444
Silver-nanoparticle-complexed G. applanatum from the topical film (without ionic liquid)0.93260.98760.98860.47830.060 ± 2.757
* Calculated from the Higuchi model.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Maneewattanapinyo, P.; Pichayakorn, W.; Monton, C.; Dangmanee, N.; Wunnakup, T.; Suksaeree, J. Effect of Ionic Liquid on Silver-Nanoparticle-Complexed Ganoderma applanatum and Its Topical Film Formulation. Pharmaceutics 2023, 15, 1098. https://doi.org/10.3390/pharmaceutics15041098

AMA Style

Maneewattanapinyo P, Pichayakorn W, Monton C, Dangmanee N, Wunnakup T, Suksaeree J. Effect of Ionic Liquid on Silver-Nanoparticle-Complexed Ganoderma applanatum and Its Topical Film Formulation. Pharmaceutics. 2023; 15(4):1098. https://doi.org/10.3390/pharmaceutics15041098

Chicago/Turabian Style

Maneewattanapinyo, Pattwat, Wiwat Pichayakorn, Chaowalit Monton, Nattakan Dangmanee, Thaniya Wunnakup, and Jirapornchai Suksaeree. 2023. "Effect of Ionic Liquid on Silver-Nanoparticle-Complexed Ganoderma applanatum and Its Topical Film Formulation" Pharmaceutics 15, no. 4: 1098. https://doi.org/10.3390/pharmaceutics15041098

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop