Next Article in Journal
Mg2+ and Cu2+ Charging Agents Improving Electrophoretic Deposition Efficiency and Coating Adhesion of Nano-TbF3 on Sintered Nd-Fe-B Magnets
Next Article in Special Issue
Near-Infrared Reflective Polymer Films Based on UV-327-Doped Zinc Oxide Nanoparticles
Previous Article in Journal
In Vitro Degradation of Mg-Doped ZrO2 Bioceramics at the Interface with Xerostom® Saliva Substitute Gel
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 7
10.3390/ma16072681
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Additives on Electrochromic Properties of Nanocrystalline Tungsten Oxide Films Prepared by Complexation-Assisted Sol–Gel Method

by
Dan Zhou
*,
Zhibo Tong
,
Hongmei Xie
,
Jiaotong Sun
and
Fenggui Chen
Chongqing Key Laboratory of Extraordinary Bond Engineering and Advanced Materials Technology, College of Materials Science and Engineering, Yangtze Normal University, Chongqing 408100, China
*
Author to whom correspondence should be addressed.
Materials 2023, 16(7), 2681; https://doi.org/10.3390/ma16072681
Submission received: 5 March 2023 / Revised: 21 March 2023 / Accepted: 26 March 2023 / Published: 28 March 2023
(This article belongs to the Special Issue Recent Progress of Materials for Smart Windows)
Browse Figures
Versions Notes

Abstract

:
To improve the electrochromic (EC) properties of sol–gel-derived WO3 films, a series of organic small molecules, such as dopamine (DA), catechol, tyramine, phenol and 2-phenylethylamine, were added into peroxotungstic acid precursor sols as structure-directing additives, and five modified WO3 films were prepared by a simple and low-cost complexation-assisted sol–gel method. The effects of the above additives on the EC properties of the modified WO3 films have been studied in detail. Compared with the pure WO3 polycrystalline film, all the modified films combine the advantages of nanocrystalline and amorphous phases and show higher EC properties attributed to the unique nanocrystal-embedded amorphous structure. The results indicate that different additives with different numbers and types of functional groups (hydroxyl and amino groups) can change the microstructure, morphology, and thus electrochemical and EC properties of the films in various degrees. The additives, in order of their strong interactions with the sols, are DA, catechol, tyramine, phenol and 2-phenylethylamine, primarily depending on the number of hydroxyl groups. Of all the additives, DA with both catechol hydroxyl and amino groups shows the most positive effect; that is, the WO3 film modified with DA exhibits the best EC properties in terms of contrast, switching speed, stability, and coloration efficiency.

1. Introduction

In recent years, under the background of sustainable development, the electrochromic (EC) smart window has been considered as a promising energy-conservation and emission-reduction device for green buildings, vehicles, etc. and received more and more attention [1,2]. EC materials, the most important component of a smart window, can change their optical properties (absorption, reflectance, transmittance, etc.) reversibly under a small applied voltage, and they have also been widely applied to energy-saving displays and antiglare automobile rear-view mirrors, in addition to smart windows, which are thought to be one of the most potential green energy-saving materials [3,4,5].
Transition metal oxides are commonly used as EC materials [3,5,6]. Among them, tungsten oxide (WO3) is the most studied and extremely attractive one due to its high transmittance contrast, thermal and photo stability, good ionic and electronic conductivity, and improved lifetime of the devices. Many techniques can be used to prepare WO3 EC films, including chemical vapor deposition (CVD) [7], sputtering [8], evaporation [9] and so on. However, the WO3 films produced by the above methods are expensive and inefficient because of the special equipment and high vacuum conditions, impeding their commercial applications. Therefore, the sol–gel method [10,11,12], a wet-chemical route, is attractive and regarded as an alternative owing to its low cost, simplicity, repeatable process, and uniform and large-area film formation. Moreover, during the sol–gel process, the microstructure, crystal size, porosity and composition of the deposited films can be easily controlled by optimizing various preparation parameters or introducing additives into the sols [13], which will affect the kinetics, durability and coloration efficiency of the thin films [14].
The EC performances of the WO3 films prepared by the traditional sol–gel method, however, are still not good enough for actual use, such as inadequate optical contrast, switching time, long-term electrochemical cycling stability or coloration efficiency. Many researchers have tried to adjust and control the structures/morphology of the sol–gel-derived WO3 films by using organic additives to improve their EC performances. Research works can be mainly divided into two categories: one is to add pore-forming templates (polymers or surfactants) into the sol and then remove the templates through heat treatment or solvent extraction [15,16,17,18]. The obtained high-porosity WO3 films possess a very large specific surface area, which can increase the color response speed and optical contrast. However, the stability of the high-porosity structure decreases [19], because part of the structure is easily destroyed or collapsed during the heat treatment process or the surface erosion rate is accelerated during the electrochemical cycling test. The other is to add a large amount of alcohols, organic acids or other organic compounds into the precursor sols to increase the contrast and switching speed [20,21]. Unfortunately, this kind of method cannot effectively enhance the combination property of the films and may bring some environmental and health problems. Therefore, it is highly desirable to develop sol–gel-derived WO3 EC films with excellent optical contrast, switching time, cycling stability, and coloration efficiency satisfying practical requirements.
It has been demonstrated that the EC properties of the films are greatly affected by the structure and morphology. It is well known that an amorphous WO3 film is characterized by a short switching time, high coloration efficiency and high contrast due to its loose structure and large surface area [13,18,21]. However, because an amorphous film has many structural defects, the electrochemical properties of the film will irreversible deteriorate during the EC cycling. On the other hand, a highly crystalline WO3 film shows high electrochemical stability owing to its compact and ordered structure, but it may be too dense for ions diffusion and intercalation, leading to a slow response time or low contrast. A number of efforts have been undertaken to overcome the problems and combine the advantages of the two structures in nanoscale [22].
In our previous work, a complexation-assisted sol–gel method was proposed in order to improve the EC properties of traditional sol–gel-derived WO3 films, in which a small amount of dopamine (DA) was added into peroxotungstic acid (PTA) precursor sol to produce PTA–DA complex sol [23]. The DA molecules suppressed the formation of very large WO3 particles in the precursor sol and inhibited the formation of a highly stressed polycrystalline structure during annealing. The DA-modified WO3 films exhibited much higher optical contrast, coloration efficiency, switching speed, and excellent long-term cycling stability (up to 35,000 cycles) than the pure WO3 film due to nanocrystal surrounded by amorphous matrix.
So far, however, very little work has been completed to investigate the function of different additives or complexing agents during the preparation and application of the sol–gel-derived WO3 films in detail. In this paper, therefore, a series of organic small molecules, such as DA, catechol (CA), tyramine (TA), phenol (Ph) and 2-phenylethylamine (PEA), are added into PTA precursor sol as structure-directing additives, and a variety of modified WO3 films are prepared by a simple and low-cost complexation-assisted sol–gel method to study the effects of the above additives containing different numbers and types of functional groups (hydroxyl and amino groups) on the structure, morphology, electrochemical and EC properties of the modified WO3 films.

2. Materials and Methods

2.1. Materials

DA hydrochloride (98%), CA (99%), TA hydrochloride (98%), Ph (≥99%), PEA hydrochloride (98%), 30% H2O2, lithium perchlorate (LiClO4) (99.9%), propylene carbonate (PC) (≥98%), acetone (98%) and isopropanol (99%) were obtained from Shanghai Aladdin Chemical Reagent Co., Ltd. (Shanghai, China). Tungsten powder (≥99%) was received from Merck KGaA (Darmstadt, Germany). Conducting indium tin oxide-coated glass (ITO glass, <7 Ω/□) was purchased from Zhuhai Kaivo Optoelectronic Technologies Co. (Zhuhai, China).

2.2. Preparation of the Modified WO3 Films

Prior to use, the ITO glass was cleaned with detergent, deionized H2O, acetone, and isopropanol for 10 min in an ultrasonic bath, respectively. Then, the ITO glass was further cleaned by a plasma treatment for 5 min to improve their hydrophilicity.
The modified WO3 films were produced through our previous complexation-assisted sol–gel method [23] with slight modification. First, 20 mmol tungsten powder was added in 60 mL 30% H2O2 solution at 0 °C under continuously magnetic stirring to form a colorless transparent PTA, which was followed by a reflux at 60 °C for 6 h to decompose of excess peroxide. After slow stirring for one week, 3.3 mmol DA was introduced into the PTA sol to obtain concentrated yellow PTA/DA complex sol after heating at 60 °C for 10 h. The PTA/DA sol was coated on the cleaned ITO glass by spin-coating technology, and the as-prepared film was dried at 60 °C for 1 h followed by annealing at 300 °C for 2 h to form the modified WO3/DA film. The film thickness was controlled at about 200 nm. Meanwhile, other modified WO3 films by adding CA, TA, Ph, and PEA were prepared in the same way, respectively. The as-prepared films are denoted as WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C, and WO3/PEA-300 °C, respectively. For comparison, the pure WO3-300 °C film was also prepared under the similar conditions except in the absence of additives.
For Fourier transform infrared spectroscopy (FTIR) characterization, xerogel samples were obtained by drying the PTA and PTA/additive complex sols in vacuum oven at 60 °C for 24 h and marked as WO3, WO3/DA, WO3/CA, WO3/TA, WO3/Ph and WO3/PEA xerogels, respectively.

2.3. Characterization of the Modified WO3 Films

The UV-Vis absorption spectra (400–800 nm) of various sols and films were obtained on a UV-VIS-NIR spectrophotometer (Shimadzu UV-3600, Tokyo, Japan). The FTIR spectra of the xerogels and films from 400 to 4000 cm−1 were recorded on a Nicolet is5 FTIR spectrometer (Thermo Fisher Scientific, Waltham, MA, USA). The morphology and microstructure of the films were observed by a field-emission scanning electron microscope (FESEM, ZEISS GeminiSEM 300, Oberkochen, Germany) and a transmission electron microscope (TEM, JEOL-2100F, Tokyo, Japan). X-ray diffraction (XRD) analyses of all the samples were characterized by a Shimadzu XRD-6100 diffractometer with an X-ray wavelength of 1.542 Å (Cu Kα radiation, 40 kV and 30 mA) over a 2-theta range of 10–60°.

2.4. Measurement of Electrochemical and EC Properties

The electrochemical properties of the films were tested using a three-electrode system with LiClO4/PC (1 mol/L) as a electrolyte, Pt sheet as a counter-electrode, Ag/AgCl as a reference electrode, and the prepared films coated on ITO glass as working electrodes. Nyquist plots of the films were performed using an AUTOLAB PGSTAT 302N potentiostat/galvanostat analyzer (Eco Chemie) at a perturbation voltage of 10 mV in the frequency range of 10 kHz to 10 mHz. Cyclic voltammetry (CV) plots were collected on an AUTOLAB analyzer at a scan rate of 100 mV s−1 from −1.0 to +1.0 V, and all current densities were normalized to the geometric surface area of the electrodes.
EC properties (visible spectra (400–800 nm) and dynamic switching curves at 720 nm) of the films were recorded on a Shimadzu UV-3600 spectrophotometer in combination with an AUTOLAB analyzer by applying constant potentials and square-wave potentials (oscillating between +1.0 V and −1.0 V at a time step of 50 s), respectively.

3. Results and Discussion

3.1. Preparation and Characterization of the Modified WO3 Films

In order to study the effects of the additives, that is, different numbers and types of functional groups (hydroxyl and amino groups), on the structure, morphology, electrochemical and EC properties of WO3 films prepared by the sol–gel method, DA, CA, TA, Ph, and PEA were selected as additives and added into the PTA precursor sols to produce a variety of modified WO3 films. Figure 1 displays the structural formulas of these five additives or their hydrochlorides. DA contains both catechol hydroxyl and amino functional groups in which the catechol units are well known to show quite strong affinity to various kinds of metals/metal ions [24], and the amino groups are mainly in the form of ammonium salt. The catechol hydroxyl groups of DA can bind uncoordinated tungsten atoms on the surface of PTA colloid nanoparticles strongly via the deprotonated O, O’ sites [25,26,27] in monodentate, bidentate, or chelated modes [28]. There is also the possibility of hydrogen bonding between the hydroxyl groups on DA and O atoms on PTA. CA has catechol hydroxyl groups and no amino group. TA possesses one hydroxyl group and one amino group. Meanwhile, both Ph and PEA are monofunctional compounds, containing only one hydroxyl group and one amino group, respectively.
A nearly colorless and transparent PTA sol was formed after one-week stirring of the reactive mixture of tungsten powder and H2O2, as shown in the photo of the inset of Figure 2. When the additives were introduced into the sols, respectively, the color of the complex sols immediately darkened significantly (inset of Figure 2), indicating an instantaneous formation of charge-transfer complexes due to the strong complexation, hydrogen bonding, or electrostatic interaction between the functional groups of the additives and tungsten or oxygen atoms of PTA colloidal nanoparticles. Furthermore, as can be seen from Figure 2, UV-Vis absorption spectra of these complex sols show a red-shift and enhanced intensity compared with that of the pure PTA sol, which is similar to the phenomenon observed from DA-TiO2 complexes [29,30].
To prove the successful preparation of the complex sols and study the interactions between the PTA sol and the additives, all the PTA and complex sols were dried in a vacuum oven at 60 °C for 24 h to form xerogels, and the FTIR spectra of the xerogels are compared in Figure 3A. As can be seen from Curve a of Figure 3A, the broad absorption band of the pure WO3 xerogel at wavenumbers around 3500 cm−1 is caused by the stretching vibration υ(OH) of water and hydroxyl adsorbed or incorporated in the xerogel, and the peak at 1629 cm−1 can be attributed to the in-plane bending vibration δ(HOH) of water molecules [31]. In addition, the pure WO3 xerogel shows key characteristic absorption bands of amorphous WO3, for example, the peaks corresponding to the stretching vibration of terminal W=O bonds (975 cm−1) on the surface of the nanoparticles and micro-voids of the xerosol [32], the stretching vibration of bridging peroxide W–O–O–W (882 cm−1), the W–O–W bridging mode of the W–O6 corner-sharing octahedral (644 cm−1), and the W−O deformation mode (562 cm−1) [10,31,32,33]. After addition of the additives, besides those from WO3, some new bands appear, such as a series of weak bands at 1100–1600 cm−1 attributed to the N−H, C−H, C−N, C−C, and aromatic C−C bonds due to the additives, as shown in Curve b–f. In addition, broad and strong bands at 3247, 3237, and 3206 cm−1 occur corresponding to the stretching vibration of N−H of DA, TA and PEA for Curve b, d and f, respectively. DA, TA and PEA all contain an amino group but different numbers of hydroxyl groups. The DA molecule has two adjacent hydroxyl groups that can preferentially bind tungsten strongly via the deprotonated O, O′ sites and the interaction between the amino group and PTA may be very limited. The TA molecule has only one hydroxyl group to link tungsten, and the PEA molecule has no hydroxyl group and thus may only form hydrogen bonding or an electrostatic interaction between NH2 or NH3+ groups on PEA and O atoms on the xerogel, which consequently causes these stretching vibration bands of N−H to shift to lower frequencies. Therefore, it is inferred that the interaction order, in which the additives are preferentially bonded with the xerogel, may be the catechol hydroxyl groups, hydroxyl group, and aliphatic side chain (NH2 or NH3+). Certainly, these newly emerging peaks imply the coexistence of tungsten oxide and organic additives. The superposition of the bending vibration of water molecules in WO3 xerogel and O−H and/or N−H bonds in complex xerogels makes the peaks stronger and wider, which shift to lower wavenumbers (from 1629 cm−1 to about 1620 cm−1) owing to the interaction of the additives and PTA. Moreover, after the addition of DA and CA into the PTA sol, both the terminal W=O peaks of these two complex xerogels move in the lower wavenumber direction (from 975 cm−1 for the WO3 xerogel to 970 cm−1 for WO3/DA and WO3/CA serogels) because the catechol hydroxyl groups of DA and CA are bidentate, showing a relatively strong complexation with W atoms, while the W=O peak positions of other complex xerogels containing monodentate change little. The peaks of the WO3 complex xerogels corresponding to the stretching vibrations of W–O–W bands and the W−O deformation mode downshift obviously from 644 cm−1 to about 630 cm−1 and from 562 cm−1 to about 550 cm−1, respectively, further verifying the formation of the complexes by the interactions between phenolic hydroxyl groups or amino groups (NH2 or NH3+) of the additives and W or O species of PTA. In addition, oxidation products of the additives containing phenolic hydroxyl groups (DA, CA, TA and Ph), such as quinone, were also found according to the weak bands at about 1700–1770 cm−1, meaning some of the phenolic hydroxyl groups were also oxidized slightly during the complexation process.
After spin-coating of all the PTA and complex sols and then annealing at 300 °C for 2 h, the obvious decrease in the intensity or even disappearance of W=O and W−O−O−W absorption bands of the WO3-300 °C and modified films (Curve a-f in Figure 3B) can be attributed to the aging and condensation of WO6 octahedral units at their corners to form a W–O–W network [33]. Furthermore, the loss of structural and absorbed water when heating at 300 °C results in the weakening of the bands at ~3500 cm−1 and ~1630 cm−1. The absorbance bands at ~1400 cm−1 can be ascribed to the W–OH bending vibration. At the same time, the weak bands attributed to the additives at 1100–1600 cm−1 disappear due to the burning off organic additives after annealing at 300 °C for 2 h. On the other hand, the intensity increase in the W–O–W band and well-defined double bands at 813 cm−1 and 758 cm−1 for the WO3-300 °C film (Curve a in Figure 3B) reveal the crystalline structure of WO3. In contrast, the absence of the double bands and the obvious broad bands at 600–670 cm−1 in Curve b–f indicate that the dominant structure of the films modified by the additives is different from crystalline one of the WO3-300 °C film.
The structures and morphologies of the WO3 films were studied by electron microscopes. Figure S1 shows FESEM images of the WO3-300 °C and modified films, revealing that all the films present relatively smooth, uniform and close-packed surfaces.
The TEM images of all the films can be seem from Figure 4. Different from the WO3-300 °C film exhibiting uniform polycrystalline structure (Figure 4A), the modified films show that WO3 nanocrystals are uniformly separated from each other and distributed in an amorphous WO3 matrix (Figure 4B–F). The amorphous matrix surrounding the WO3 nanocrystals may act as ion transport channels and increase reactive active sites during the EC process, which is beneficial for the diffusion of the electrolyte into the nanocrystals [10] and the improvement of the optical contrast and switching response. Meanwhile, the amorphous phase in the nanocrystal-embedded films may also serve as buffer layers to accommodate the volume change produced by ion insertion/extraction [18] and avoid bond breakage during electrochemical cycling. The amorphous and nanocrystalline regions were uniformly distributed, which may decrease the stress concentration and inhibit erosion produced by high local stress, contributing to high cycling stability [23]. According to Figure 4B–F, the estimated particle sizes of the crystalline grains increase gradually in the range of from about 5 to 20 nm in the following order: WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C. Due to the high coordination ability of catechol hydroxyl groups on metals, the strong complexation of catechol additives (such as DA and CA) can limit the size of colloidal particles and destroy the structure order of particles to a certain extent, which results in the formation of more uniform and finer nanocrystals distributed in an amorphous matrix after heat treatment at 300 °C. Compared with CA, DA also contains NH3+, which can help PTA colloidal particles to better disperse in colloid and thus stabilize colloid solution. However, the complexation ability of monodentate additives (TA, Ph and PEA) is slightly poor, especially for PEA containing only one amino group without hydroxyl group, resulting in the formation of relatively large and heterogeneous nanocrystals after annealing. Different numbers and types of functional groups in the additives may have different effects on the microstructure and morphology of the films, therefore, and will ultimately result in a large difference in the properties of the films including EC property. Moreover, according to TEM images, clear lattice fringes of nanocrystals can be seen for the WO3-300 °C and modified films, and the lattice spacing values (3.83, 3.77, and 3.66 Å) perfectly fit monoclinic WO3 (JCPDS 43-1035), corresponding to the d-spacing of (002), (020), and (200) planes.
Figure 5 shows XRD patterns of ITO glass, WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C, and WO3/PEA-300 °C films coated on ITO glass. After annealing at 300 °C for 2 h, the WO3-300 °C film displays several relatively intense and distinct diffraction peaks at 2θ = 23.2, 23.7, 24.4 and 34.2° in Curve b corresponding to (002), (020), (200) and (202) planes, respectively, indexed to the monoclinic crystalline WO3 (JCPDS Card No.43-1035). However, for the modified films (Curve c-g), only weak and broad humps appear in the 2θ region from 20° to 30° in addition to several characteristic peaks of the ITO substrate, as shown in Curve a. During the preparation of the modified films, the additives may inhibit crystal growth, causing the generation of the small WO3 nanocrystals embedded in an amorphous matrix, which is in agreement with the FTIR and TEM results, which broaden and weaken the diffraction peaks. Therefore, it is difficult to observe distinct diffraction peaks [30,34].

3.2. Electrochemical Properties of the Modified WO3 Films

The electrochemical properties of the films during ion insertion/extraction were studied by using CV. Figure 6A displays the CV curves of the WO3-300 °C and modified WO3 films tested at a scan rate of 100 mV s−1 between −1.0 and +1.0 V. For all the films, the CV curves are similar in shape, but the modified films exhibit a higher peak current density and CV integral area than the WO3-300 °C film, and the order of the modified films from high to low is roughly WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C. Therefore, the modified films have more electrochemical active mass and higher ion/electron storage capacity, that is, more ions/electrons are involved at the interface between the films and electrolyte than the WO3-300 °C film, and thus, it is deduced that the modified films will show better EC performances due to the nanocrystal-embedded amorphous structure.
Electrochemical impedance spectroscopy (EIS) was applied to further investigate the electrochemical behaviors of the modified WO3 films and provided information on the interfaces of charge transfer and ion diffusion. The Nyquist plots of the WO3-300 °C and modified WO3 films can be seen in Figure 6B. Compared with the WO3-300 °C, the modified WO3 films (especially WO3/DA-300 °C) exhibit smaller intercepts of the curves at the X-axis and depressed arc diameters in the high-frequency region (the inset of Figure 6B) and higher slopes in the low-frequency region (except WO3/PEA-300 °C), meaning lower series resistance and charge-transfer resistance and a higher diffusion rate of Li+ ion for ion insertion into and extraction from the films [35,36,37]. The results indicate that the nanocrystal-embedded amorphous phase structure of the modified films is more beneficial to both Li+ ion diffusion and charge transfer compared with the compact polycrystalline structure of WO3-300 °C.

3.3. EC properties of the Modified WO3 Films

The EC process of WO3 films involves the double injection/extraction of cations and electrons into/from the films and the color switches between blue and transparent. EC properties of the pure WO3-300 °C and modified films were tested and compared as shown in Figure 7 and Table 1. Transmittance contrast or modulation, ΔT, is defined as the difference in the transmittance between the bleached and the colored states at a certain wavelength. According to UV-vis transmittance spectra (Figure 7A–F), ∆T values of the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films at a wavelength of 720 nm are about 51, 75, 72, 66, 64, and 56%, respectively, as listed in Table 1. Compared with the pure WO3-300 °C film, all the modified WO3 films possess much higher optical contrasts (∆T) because the nanocrystal-embedded amorphous structure produced by the additives can provide more active sites and higher ion/electron storage capacity than the compact polycrystalline structure. Therefore, as we can see from the aforementioned test results related to the characterization and electrochemical properties, different numbers and types of functional groups in the additives may ultimately result in a large difference in the EC properties of the films by changing the microstructure and morphology of the films. In other words, the addition of the additives with more hydroxyl groups produces the modified WO3 films with better performances.
Coloration efficiency (CE) is defined as the change in optical density (ΔOD) measured at a certain wavelength (λ) per unit charge (Q) inserted into or extracted from the EC films, namely, CE = ΔOD(λ)/(Q/A) = log(Tb/Tc)/q [38], where q is the charge density (injected/ejected charge Q per unit electrode area A), and Tb and Tc represent the transmittances in the bleached and colored states. Coloration efficiency is also an important characteristic parameter for evaluating EC performance. The coloration efficiency values were calculated to be 66, 90, 85, 81, 77 and 70 cm2 C−1 for the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films, respectively, as listed in Table 1. The much higher coloration efficiency values of the modified WO3 films than that of WO3-300 °C film can be ascribed to their more efficient Li+ ion diffusion and charge transfer in the nanocrystal-embedded amorphous structure. In general, high coloration efficiency provides a large optical contrast with a small charge insertion or extraction, which is beneficial to improving the cycle life of the EC materials, just as our previous work proved that the WO3/DA-300 °C film displays excellent stability up to 35,000 cycles [23]. All the modified films exhibit the unique nanocrystal-embedded amorphous structure as shown in TEM images, which consequently help to greatly improve cycling stability of all the modified films.
The switching times, namely coloration and bleaching times, mean the times required for a 90% change in the transmittance contrast during the coloring/bleaching processes, which have been measured from switching curves of the films in Figure 7G and can be seen in Table 1. The switching times for the WO3/DA-300 °C film are 10 s for bleaching and 15 s for coloration, while the switching times for the modified WO3 film are almost all less than them, indicating that using the additives can accelerate the dynamic response of WO3 films. The reason is that the modified WO3 films with nanocrystal-embedded amorphous structure possess a much shorter diffusion length of ions due to a larger amorphous region and easier access of a larger amount of Li+ ions than the WO3-300 °C film with a polycrystalline structure, which can consequently speed up the ion diffusion and charge transfer. Of all the films, the WO3/DA-300 °C film shows the shortest switching time (3 s for bleaching and 7 s for coloration), because it possesses the smallest nanocrystals uniformly distributed in an amorphous WO3 matrix which may act as ion transport channels and increase reactive active sites during EC process, which is beneficial for the diffusion of the electrolyte into the nanocrystals and the speeding up of the switching response. For most films, the bleaching times are less than the coloration times, showing that the double extraction of cations and electrons from the films is easier and faster than injection into the films.
As we all know, the structure and morphology of WO3 films greatly affects EC performance, and amorphous and crystalline WO3 films exhibit quite different EC performances from each other [39]. In this study, the introduction of the additives into the precursor PTA sol and the application of an appropriate annealing process promote the formation of nanocrystal-embedded amorphous structure having the merits of both amorphous and crystalline WO3 films. All the modified films possess higher EC properties than the pure WO3 polycrystalline film, roughly in descending order: the WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films. The strong complexation ability (with W atoms) of DA and CA bidentate additives containing catechol hydroxyl groups limits the size of complex colloidal particles and destroys the structure order of particles to a certain extent, resulting in the formation of more uniform and finer nanocrystals surrounded with an amorphous matrix after heat treatment. On the other hand, among them, DA has the best effect in enhancing the EC properties of the films because it also contains NH3+ in addition to catechol hydroxyl groups, which can be better dispersed in colloid and thus stabilize colloid solution. TA, PEA and Ph, however, are monodentate additives and show slightly poor complexation ability, resulting in the formation of relatively large and uneven nanocrystals. Especially, PEA contains only one amine group without a hydroxyl group, and the film modified by PEA shows relatively poorer EC performance than other modified films.

4. Conclusions

In summary, a series of organic small molecules (DA, CA, TA, Ph and PEA) containing different numbers of hydroxyl and amino groups were added to the PTA sols as structure-directing additives, and a variety of modified WO3 films were consequently prepared by a simple and low-cost complexation-assisted sol–gel method. Compared with the pure WO3 polycrystalline film, all the modified films combine the advantages of nanocrystalline and amorphous phases and show higher EC properties owing to the unique nanocrystal-embedded amorphous structure. It is worth noting that the additives with different numbers and types of functional groups show different interactions with PTA sol, which affect the size, shape and stability of the complex colloidal particles and consequently change the structures and morphologies of the WO3 films from a polycrystalline to nanocrystal-embedded amorphous structure with different grain sizes, finally improving the electrochemical and EC properties of the modified WO3 films in different degrees. The additives, in order of their interactions with the sol, are DA, CA, TA, Ph and PEA, primarily depending on the number of hydroxyl groups followed by the number of amino group. Of all the additives, DA with catechol hydroxyl and amino groups shows the most positive effect, that is, the WO3/DA-300 °C film exhibits the best EC performances.
Furthermore, the study indicates that the modified WO3 films with excellent EC properties prepared by a simple and low-cost complexation-assisted sol–gel method show great application potential for EC devices. The effects of more additives with other functional groups on the microstructure, morphology, and thus EC properties of the WO3 films should be further studied in the future to reveal the relationship between structure and performance of the WO3 films and further improve the complexation-assisted sol–gel method.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ma16072681/s1, Figure S1: FESEM images of (A) WO3-300 °C, (B) WO3/DA-300 °C, (C) WO3/CA-300 °C, (D) WO3/TA-300 °C, (E) WO3/Ph-300 °C, and (F) WO3/PEA-300 °C films.

Author Contributions

Conceptualization, D.Z.; methodology, D.Z. and Z.T.; validation, H.X. and J.S.; preparation, D.Z.; characterization, F.C.; writing—original draft preparation, D.Z.; writing—review and editing, F.C.; supervision, D.Z. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Chongqing Research Program of Basic Research and Frontier Technology (cstc2019jcyj-msxmX0510) and the Research Project of Yangtze Normal University (2017KYQD39).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

All data are available from the corresponding author.

Acknowledgments

The authors would like to thank Qihuang Deng for the XRD characterization. This work was financially supported by the Chongqing Research Program of Basic Research and Frontier Technology (cstc2019jcyj-msxmX0510) and the Research Project of Yangtze Normal University (2017KYQD39).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Zhang, Y.; Liang, X.; Jiang, T.; Liu, H.; Fu, Y.; Zhang, D.; Geng, Z. Amorphous/crystalline WO3 dual phase laminated films: Fabrication, characterization and evaluation of their electrochromic performance for smart window applications. Sol. Energy Mater. Sol. Cells 2022, 244, 111820. [Google Scholar] [CrossRef]
  2. Luo, Y.; Jin, H.; Lu, Y.; Zhu, Z.; Dai, S.; Huang, L.; Zhuang, X.; Liu, K.; Huang, L. Potential Gradient-Driven Fast-Switching Electrochromic Device. ACS Energy Lett. 2022, 7, 1880–1887. [Google Scholar] [CrossRef]
  3. Niklasson, G.A.; Granqvist, C.G. Electrochromics for smart windows: Thin films of tungsten oxide and nickel oxide, and devices based on these. J. Mater. Chem. 2007, 17, 127–156. [Google Scholar] [CrossRef] [Green Version]
  4. Wang, J.; Zhang, L.; Yu, L.; Jiao, Z.; Xie, H.; Lou, X.W.; Sun, X.W. A bi-functional device for self-powered electro-chromic window and self-rechargeable transparent battery applications. Nat. Commun. 2014, 5, 4921. [Google Scholar] [CrossRef] [Green Version]
  5. Thakur, V.K.; Ding, G.Q.; Ma, J.; Lee, P.S.; Lu, X.H. Hybrid Materials and Polymer Electrolytes for Electrochromic Device Applications. Adv. Mater. 2012, 24, 4071–4096. [Google Scholar]
  6. Wu, C.-L.; Wang, C.-K.; Lin, C.-K.; Wang, S.-C.; Huang, J.-L. Electrochromic properties of nanostructured tungsten oxide films prepared by surfactant-assisted sol–gel process. Surf. Coat. Technol. 2013, 231, 403–407. [Google Scholar] [CrossRef]
  7. Gesheva, K.; Szekeres, A.; Ivanova, T. Optical properties of chemical vapor deposited thin films of molybdenum and tungsten based metal oxides. Sol. Energy Mater. Sol. Cells 2003, 76, 563–576. [Google Scholar] [CrossRef]
  8. Subrahmanyam, A.; Karuppasamy, A. Optical and electrochromic properties of oxygen sputtered tungsten oxide (WO3) thin films. Sol. Energy Mater. Sol. Cells 2007, 91, 266–274. [Google Scholar] [CrossRef]
  9. Baek, Y.; Yong, K. Controlled Growth and Characterization of Tungsten Oxide Nanowires Using Thermal Evaporation of WO3 Powder. J. Phys. Chem. C 2007, 111, 1213–1218. [Google Scholar] [CrossRef]
  10. Lin, F.; Cheng, J.; Engtrakul, C.; Dillon, A.C.; Nordlund, D.; Moore, R.G.; Weng, T.-C.; Williams, S.K.R.; Richards, R.M. In situ crystallization of high performing WO3-based electrochromic materials and the importance for durability and switching kinetics. J. Mater. Chem. 2012, 22, 16817–16823. [Google Scholar] [CrossRef]
  11. Gillaspie, D.T.; Tenent, R.C.; Dillon, A.C. Metal-oxide films for electrochromic applications: Present technology and future directions. J. Mater. Chem. 2010, 20, 9585–9592. [Google Scholar] [CrossRef]
  12. Cronin, J.; Tarico, D.; Tonazzi, J.; Agrawal, A.; Kennedy, S. Microstructure and properties of sol-gel deposited WO3 coatings for large area electrochromic windows. Sol. Energy Mater. Sol. Cells 1993, 29, 371–386. [Google Scholar] [CrossRef]
  13. Taylor, D.J.; Cronin, J.P.; Allard, L.F.; Birnie, D.P. Microstructure of laser-fired, sol-gel-derived tungsten oxide films. Chem. Mater. 1996, 8, 1396–1401. [Google Scholar]
  14. Shchegolkov, A.V.; Jang, S.-H.; Shchegolkov, A.V.; Rodionov, Y.V.; Sukhova, A.O.; Lipkin, M.S. A Brief Overview of Electrochromic Materials and Related Devices: A Nanostructured Materials Perspective. Nanomaterials 2021, 11, 2376. [Google Scholar] [CrossRef]
  15. Wang, W.; Pang, Y.; Hodgson, S.N.B. Preparation, characterisation and electrochromic property of mesostructured tungsten oxide films via a surfactant templated sol–gel process from tungstic acid. J. Sol-Gel Sci. Technol. 2010, 54, 19–28. [Google Scholar] [CrossRef] [Green Version]
  16. Badilescu, S.; Ashrit, P.V. Study of sol-gel prepared nanostructured WO3 thin films and composites for electro-chromic applications. Solid State Ion. 2003, 158, 187–197. [Google Scholar] [CrossRef]
  17. Baeck, S.H.; Choi, K.S.; Jaramillo, T.F.; Stucky, G.D.; McFarland, E.W. Enhancement of photocatalytic and electrochromic properties of electrochemically fabricated mesoporous WO3 thin films. Adv. Mater. 2003, 15, 1269. [Google Scholar] [CrossRef]
  18. Fang, Y.; Sun, X.; Cao, H. Influence of PEG additive and annealing temperature on structural and electrochromic properties of sol–gel derived WO3 films. J. Sol-Gel Sci. Technol. 2011, 59, 145–152. [Google Scholar] [CrossRef]
  19. He, J.; Yang, X.; Evans, D.; Duan, X. New methods to remove organic templates from porous materials. Mater. Chem. Phys. 2003, 77, 270–275. [Google Scholar] [CrossRef]
  20. Cronin, J.P.; Tarico, D.J.; Agrawal, A.; Zhang, R.L. Method for Depositing High Performing Electrochromic Layers. U.S. Patent 5277986, 11 January 1994. [Google Scholar]
  21. Deepa, M.; Saxena, T.; Singh, D.; Sood, K.; Agnihotry, S. Spin coated versus dip coated electrochromic tungsten oxide films: Structure, morphology, optical and electrochemical properties. Electrochim. Acta 2006, 51, 1974–1989. [Google Scholar] [CrossRef]
  22. Shi, Y.; Sun, M.; Zhang, Y.; Cui, J.; Wang, Y.; Shu, X.; Qin, Y.; Tan, H.H.; Liu, J.; Wu, Y. Structure modulated amorphous/crystalline WO3 nanoporous arrays with superior electrochromic energy storage performance. Sol. Energy Mater. Sol. Cells 2020, 212, 110579. [Google Scholar] [CrossRef]
  23. Zhou, D.; Che, B.; Kong, J.; Lu, X. A nanocrystalline tungsten oxide electrochromic coating with excellent cycling stability prepared via a complexation-assisted sol–gel method. J. Mater. Chem. C 2016, 4, 8041–8051. [Google Scholar] [CrossRef]
  24. Wang, Z.; Zou, Y.; Li, Y.; Cheng, Y. Metal-Containing Polydopamine Nanomaterials: Catalysis, Energy, and Theranostics. Small 2020, 16, 1907042. [Google Scholar]
  25. Nielson, A.J.; Griffith, W.P. Complexes of osmium(VI) with catechol and substituted catechols. J. Chem. Soc. Dalton Trans. 1978, 1501–1506. [Google Scholar] [CrossRef]
  26. Griffith, W.P.; Pumphrey, C.A.; Rainey, T.A. Catecholato complexes of ruthenium, iridium, rhenium, molybdenum, and tungsten. J. Chem. Soc.-Dalton Trans. 1986, 1125–1128. [Google Scholar] [CrossRef]
  27. Elhendawy, A.M.; Griffith, W.P.; Pumphrey, C.A. Complexes of osmium, uranium, molybdenum, and tungsten with the catechol amines adrenaline, noradrenaline, dopamine, dopa, and iso-proterenol. J. Chem. Soc.-Dalton Trans. 1988, 1817–1821. [Google Scholar] [CrossRef]
  28. Urdaneta, I.; Keller, A.; Atabek, O.; Palma, J.L.; Finkelstein-Shapiro, D.; Tarakeshwar, P.; Mujica, V.; Calatayud, M. Dopamine Adsorption on TiO2 Anatase Surfaces. J. Phys. Chem. C 2014, 118, 20688–20693. [Google Scholar]
  29. Kleiman-Shwarsctein, A.; Laursen, A.B.; Cavalca, F.; Tang, W.; Dahl, S.; Chorkendorff, I. A general route for RuO2 deposition on metal oxides from RuO4. Chem. Commun. 2012, 48, 967–969. [Google Scholar] [CrossRef] [Green Version]
  30. Valverde-Aguilar, G.; Prado-Prone, G.; Vergara-Aragon, P.; Garcia-Macedo, J.; Santiago, P.; Rendon, L. Photoconductivity studies on nanoporous TiO2/dopamine films prepared by sol-gel method. Appl. Phys. A-Mater. Sci. Process. 2014, 116, 1075–1084. [Google Scholar]
  31. Daniel, M.F.; Desbat, B.; Lassegues, J.C.; Gerand, B.; Figlarz, M. Infrared and raman-study of WO3 tungsten trioxides and WO3, XH2O tungsten trioxide hydrates. J. Solid State Chem. 1987, 67, 235–247. [Google Scholar]
  32. Santato, C.; Odziemkowski, M.; Ulmann, M.; Augustynski, J. Crystallographically Oriented Mesoporous WO3 Films: Synthesis, Characterization, and Applications. J. Am. Chem. Soc. 2001, 123, 10639–10649. [Google Scholar] [CrossRef] [PubMed]
  33. Orel, B.; Groselj, N.; Krasovec, U.O.; Jese, R.; Georg, A. IR spectroscopic investigations of gasochromic and elec-trochromic sol-gel—Derived peroxotungstic acid/ormosil composite and crystalline WO3 films. J. Sol-Gel Sci. Technol. 2002, 24, 5–22. [Google Scholar] [CrossRef]
  34. Dalavi, D.S.; Devan, R.S.; Patil, R.A.; Patil, R.S.; Ma, Y.-R.; Sadale, S.B.; Kim, I.; Kim, J.-H.; Patil, P.S. Efficient electrochromic performance of nanoparticulate WO3 thin films. J. Mater. Chem. C 2013, 1, 3722–3728. [Google Scholar] [CrossRef]
  35. Huang, H.; Tian, J.; Zhang, W.; Gan, Y.; Tao, X.; Xia, X.; Tu, J. Electrochromic properties of porous NiO thin film as a counter electrode for NiO/WO3 complementary electrochromic window. Electrochim. Acta 2011, 56, 4281–4286. [Google Scholar] [CrossRef]
  36. Cong, S.; Tian, Y.; Li, Q.; Zhao, Z.; Geng, F. Single-Crystalline Tungsten Oxide Quantum Dots for Fast Pseudocapacitor and Electrochromic Applications. Adv. Mater. 2014, 26, 4260–4267. [Google Scholar] [PubMed]
  37. Kondalkar, V.V.; Mali, S.S.; Kharade, R.R.; Khot, K.V.; Patil, P.B.; Mane, R.M.; Choudhury, S.; Patil, P.S.; Hong, C.K.; Kim, J.H.; et al. High performing smart electrochromic device based on honeycomb nanostructured h-WO3 thin films: Hydrothermal assisted synthesis. Dalton Trans. 2015, 44, 2788–2800. [Google Scholar] [CrossRef]
  38. Amb, C.M.; Dyer, A.L.; Reynolds, J.R. Navigating the Color Palette of Solution-Processable Electrochromic Polymers. Chem. Mater. 2011, 23, 397–415. [Google Scholar]
  39. Quy, V.H.V.; Jo, I.-R.; Kang, S.-H.; Ahn, K.-S. Amorphous-crystalline dual phase WO3 synthesized by pulsed-voltage electrodeposition and its application to electrochromic devices. J. Ind. Eng. Chem. 2021, 94, 264–271. [Google Scholar] [CrossRef]
Materials 16 02681 g001 550
Figure 1. Structural formulas of (A) DA hydrochloride, (B) CA, (C) TA hydrochloride, (D) Ph and (E) PEA hydrochloride.
Figure 1. Structural formulas of (A) DA hydrochloride, (B) CA, (C) TA hydrochloride, (D) Ph and (E) PEA hydrochloride.
Materials 16 02681 g001
Materials 16 02681 g002 550
Figure 2. UV-Vis absorption spectra of the PTA, PTA/DA, PTA/CA, PTA/TA, PTA/Ph, and PTA/PEA sols. The inset showing the photos of these sols.
Figure 2. UV-Vis absorption spectra of the PTA, PTA/DA, PTA/CA, PTA/TA, PTA/Ph, and PTA/PEA sols. The inset showing the photos of these sols.
Materials 16 02681 g002
Materials 16 02681 g003 550
Figure 3. (A) FTIR spectra of (a) WO3, (b) WO3/DA, (c) WO3/CA, (d) WO3/TA, (e) WO3/Ph and (f) WO3/PEA xerogels, and (B) FTIR spectra of (a) WO3-300 °C, (b) WO3/DA-300 °C, (c) WO3/CA-300 °C, (d) WO3/TA-300 °C, (e) WO3/Ph-300 °C and (f) WO3/PEA-300 °C films.
Figure 3. (A) FTIR spectra of (a) WO3, (b) WO3/DA, (c) WO3/CA, (d) WO3/TA, (e) WO3/Ph and (f) WO3/PEA xerogels, and (B) FTIR spectra of (a) WO3-300 °C, (b) WO3/DA-300 °C, (c) WO3/CA-300 °C, (d) WO3/TA-300 °C, (e) WO3/Ph-300 °C and (f) WO3/PEA-300 °C films.
Materials 16 02681 g003
Materials 16 02681 g004 550
Figure 4. TEM images of (A) WO3-300 °C, (B) WO3/DA-300 °C, (C) WO3/CA-300 °C, (D) WO3/TA-300 °C, (E) WO3/Ph-300 °C, and (F) WO3/PEA-300 °C films.
Figure 4. TEM images of (A) WO3-300 °C, (B) WO3/DA-300 °C, (C) WO3/CA-300 °C, (D) WO3/TA-300 °C, (E) WO3/Ph-300 °C, and (F) WO3/PEA-300 °C films.
Materials 16 02681 g004
Materials 16 02681 g005 550
Figure 5. X-ray diffraction (XRD) patterns of (a) ITO glass, (b) WO3-300 °C, (c) WO3/DA-300 °C, (d) WO3/CA-300 °C, (e) WO3/TA-300 °C, (f) WO3/Ph-300 °C, and (g) WO3/PEA-300 °C films.
Figure 5. X-ray diffraction (XRD) patterns of (a) ITO glass, (b) WO3-300 °C, (c) WO3/DA-300 °C, (d) WO3/CA-300 °C, (e) WO3/TA-300 °C, (f) WO3/Ph-300 °C, and (g) WO3/PEA-300 °C films.
Materials 16 02681 g005
Materials 16 02681 g006 550
Figure 6. (A) CV curves tested at a scan rate of 100 mV s−1 between −1.0 and +1.0 V and (B) Nyquist plots of the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films in 1 mol/L LiClO4/PC at frequency from 100 kHz to 10 mHz using a perturbation amplitude of 10 mV at the potential of 0 V.
Figure 6. (A) CV curves tested at a scan rate of 100 mV s−1 between −1.0 and +1.0 V and (B) Nyquist plots of the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films in 1 mol/L LiClO4/PC at frequency from 100 kHz to 10 mHz using a perturbation amplitude of 10 mV at the potential of 0 V.
Materials 16 02681 g006
Materials 16 02681 g007 550
Figure 7. UV-vis transmittance spectra at different potentials of (A) pure WO3-300 °C, (B) WO3/DA-300 °C, (C) WO3/CA-300 °C, (D) WO3/TA-300 °C, (E) WO3/Ph-300 °C, and (F) WO3/PEA-300 °C films at the potentials of −1.0, −0.8, +0.5, +0.8 and +1.0 V, as shown in green, violet, blue, red and black lines, respectively, (G) switching curve comparison between the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C, and WO3/PEA-300 °C films at λ720nm (+1.0 V/−1.0 V, 100 s per cycle), and (H) the photo of the WO3/DA-300 °C films in the bleached and colored states respectively.
Figure 7. UV-vis transmittance spectra at different potentials of (A) pure WO3-300 °C, (B) WO3/DA-300 °C, (C) WO3/CA-300 °C, (D) WO3/TA-300 °C, (E) WO3/Ph-300 °C, and (F) WO3/PEA-300 °C films at the potentials of −1.0, −0.8, +0.5, +0.8 and +1.0 V, as shown in green, violet, blue, red and black lines, respectively, (G) switching curve comparison between the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C, and WO3/PEA-300 °C films at λ720nm (+1.0 V/−1.0 V, 100 s per cycle), and (H) the photo of the WO3/DA-300 °C films in the bleached and colored states respectively.
Materials 16 02681 g007
Table
Table 1. EC properties of the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films at λ720nm.
Table 1. EC properties of the WO3-300 °C, WO3/DA-300 °C, WO3/CA-300 °C, WO3/TA-300 °C, WO3/Ph-300 °C and WO3/PEA-300 °C films at λ720nm.
The Films∆T 1
(%)		∆T 2
(%)		CE
(cm2 C−1)		Bleaching Time 2 (s)Coloration Time 2 (s)
WO3-300 °C51 ± 152 ± 166 ± 110 ± 115 ± 1
WO3/DA-300 °C75 ± 175 ± 190 ± 13 ± 17 ± 1
WO3/CA-300 °C72 ± 171 ± 185 ± 15 ± 110 ± 1
WO3/TA-300 °C66 ± 166 ± 181 ± 16 ± 113 ± 1
WO3/Ph-300 °C64 ± 163 ± 177 ± 19 ± 19 ± 1
WO3/PEA-300 °C56 ± 155 ± 170 ± 19 ± 115 ± 1
1 Obtained from UV-Vis transmittance spectra in Figure 7A–F; 2 Obtained from switching curves in Figure 7G.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Zhou, D.; Tong, Z.; Xie, H.; Sun, J.; Chen, F. Effects of Additives on Electrochromic Properties of Nanocrystalline Tungsten Oxide Films Prepared by Complexation-Assisted Sol–Gel Method. Materials 2023, 16, 2681. https://doi.org/10.3390/ma16072681

AMA Style

Zhou D, Tong Z, Xie H, Sun J, Chen F. Effects of Additives on Electrochromic Properties of Nanocrystalline Tungsten Oxide Films Prepared by Complexation-Assisted Sol–Gel Method. Materials. 2023; 16(7):2681. https://doi.org/10.3390/ma16072681

Chicago/Turabian Style

Zhou, Dan, Zhibo Tong, Hongmei Xie, Jiaotong Sun, and Fenggui Chen. 2023. "Effects of Additives on Electrochromic Properties of Nanocrystalline Tungsten Oxide Films Prepared by Complexation-Assisted Sol–Gel Method" Materials 16, no. 7: 2681. https://doi.org/10.3390/ma16072681

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop