Review

A Comprehensive Review of Biodegradable Polymer-Based Films and Coatings and Their Food Packaging Applications

School of Bioengineering and Food Technology, Shoolini University, Bajhol, Solan 173229, India
*
Authors to whom correspondence should be addressed.
Materials 2022, 15(17), 5899; https://doi.org/10.3390/ma15175899
Submission received: 27 July 2022 / Revised: 18 August 2022 / Accepted: 24 August 2022 / Published: 26 August 2022

Abstract

:
Food sectors are facing issues as a result of food scarcity, which is exacerbated by rising populations and demand for food. Food is ordinarily wrapped and packaged using petroleum-based plastics such as polyethylene, polyvinyl chloride, and others. However, the excessive use of these polymers has environmental and health risks. As a result, much research is currently focused on the use of bio-based materials for food packaging. Biodegradable polymers that are compatible with food products are used to make edible packaging materials. These can be ingested with food and provide consumers with additional health benefits. Recent research has shifted its focus to multilayer coatings and films-based food packaging, which can provide a material with additional distinct features. The aim of this review article is to investigate the properties and applications of several bio-based polymers in food packaging. The several types of edible film and coating production technologies are also covered separately. Furthermore, the use of edible films and coatings in the food industry has been examined, and their advantages over traditional materials are also discussed.

1. Introduction

Films and coatings are types of packaging materials used widely in the food industry for a variety of purposes. For example, they serve as protection against physical, chemical, as well as biological damage to food. They are also helpful in preventing the loss of aroma, flavor, antimicrobials, and antioxidants [1]. They prevent oxygen, carbon dioxide, and moisture loss, and are hence helpful in increasing the shelf life of food and improving the mechanical integrity and handling characteristics of food [2]. The production and usage of petroleum-based polymer-generated plastic for manufacturing coatings and films have increased over recent decades. According to Derraik et al. (2002), plastic can be defined as a synthetic or semisynthetic organic polymer having good barrier properties against moisture, oil, and gases, with strength characteristics and good resistant properties against stress and corrosion [3]. It is cheap, lightweight, and easy to carry and handle, making it highly convenient for daily use. Due to its abundant usage in various applications, the plastic industry in India is worth between 3000 and 4000 crores [4]. It is believed that half of all plastic products which are used in the food industry such as cutlery, plastic bags, coatings, and packaging material, are designed to be thrown away. Moreover, the world production of plastics grew from 1.5 million metric tons in 1950 to 359 million metric tons in 2018 [5]. According to Sabbah et al. (2017), more than 35 million tons of waste derived from various plastic products are produced each year in the world and unfortunately only 7% of these are recycled [6].
Moreover, due to the presence to toxic chemicals which are used in the manufacturing of plastic, its usage and disposal has resulted in hazardous effects related to environmental as well as human health [7]. The current scenario of plastic pollution indicates that approximately 400 thousand plastic bottles and about 700 thousand plastic bags are disposed of worldwide every minute [6]. As polymer is non-biodegradable by nature, it remains in the environment, leading to severe environmental as well as health hazards. Most plastics and other petrochemical polymers are considered “hard-to-degrade” because of their corrosion-resistant qualities, and they can remain in the environment for decades or even centuries [8]. One of the serious issues which can arise due to this is biomagnification, caused when a certain amount of toxic material (after leaching from the polymer into soil/bodies of water) reaches the food chain and its concentration level increases after each successive level in the food chain, creating a health hazard for various organisms. Other hazards include soil pollution, water pollution, air pollution, groundwater contamination, etc.
High-density polyethylene (HDPE), low-density polyethylene (LDPE), polyvinyl chloride (PVC), polystyrene (PS), polypropylene (PP), and polyethylene terephthalate (PET) are some of the most widely used and plentiful petrochemical-based polymers (Table 1), accounting for almost 90% of the total plastic output worldwide [7].
A study conducted by Patil et al. in (2018) demonstrated that India generated almost 15,000 tons of plastic waste every day [10]. This amount of plastic waste generation is a result of an increasing population, which reached 7.7 billion in 2019 and is expected to reach around 9.7 billion in 2050, as per UN reports published in 2019 [11]. As there is a high demand for packaged food, the demand for packaging material is also high [12]. This demand has led researchers to develop an appropriate packaging and coating material which can increase the shelf life of food, contribute to sustainable development through the utilization of waste, and also minimize the pollution caused by single-use plastic packaging materials.
As a result, the world is now focusing on bio-based edible films and coatings that can easily degrade after use, thereby also contributing to waste reduction. Biodegradable and edible films and coatings are an integral aspect of food packaging; they are formed from hydrocolloids such as proteins, polysaccharides, lipids, antimicrobial components, or a combination of these. They consist of a continuous thin layer (between 0.050 and 0.250 mm) which is safe for consumption along with food [13,14]. Films are mainly used to wrap food material, whereas coatings can be used directly on food products [15]. The types of materials used for the production of these films are mostly renewable biological sources, mainly consisting of starch, cellulose, hemicellulose, protein, gelatin, lipids, fibers, etc. Examples of such materials include corn, sorghum, rice, fruit and vegetable waste, and agricultural waste such as wood chips or bagasse. Waste produced by food industries such as cane molasses from the sugar industry, barley spent grain from breweries, etc., could be a good source of these bio-based films as they are produced throughout the processing of food from agricultural land to food processing units through to the consumer. They are easily available at a low cost and their usage would help in the waste utilization process [16]. However, unlike petroleum-based polymers, these materials do not offer good barrier and mechanical properties; therefore, some additives are also required to enhance these properties. A single layer of edible coating may not be sufficient to withstand all the barrier requirements; therefore, a multilayer coating consisting of a combination of more than two types of bio-based coating materials can improve its overall characteristics. In this context, nanotechnology has also been introduced to improve the mechanical strength and barrier properties of edible packaging materials [17]. Bio-based edible films and coatings are appropriate for packaging fruits, vegetables, dairy, and meat-based products at a commercial level. Although bio-based polymers are promising, the production cost is a key limitation for its practical use. One of the strategies to reduce costs is the mass production and increased awareness of biopolymer-based packaging. In addition, extra attention is required for water-insoluble bio-based polymers in order for them to be properly disposed of. Nowadays, research is mainly focused on the use of biodegradable edible coatings for fresh and minimally processed fruits and vegetables such as avocados [18], strawberries [19], pears [20], mangos [21], etc. The type of edible packaging material selected is dependent upon the type of food, for example, fruit, dairy, or meat, and the storage conditions, including temperature and relative humidity [22]. Because different foods have different qualities, each property must be safeguarded, diminished, or enhanced in order to maintain product safety. The manner in which the coating is applied is also very important both in terms of cost and efficacy [23].
The application of edible coatings and films on food products is not novel; it has been applied onto food products for the preservation of food for centuries. For instance, wax- and cellulose-based coatings on highly perishable foods such as meat, fruits, and vegetables have been applied since the 12th century in China [24,25]. Edible films and coatings act as a semi-permeable barrier, preventing microbes from entering the meal without changing the original contents. They increase the shelf life of food by lowering the moisture and reducing the dissolved component migration, gas exchange, oxidative reactions, and respiration rates [25,26]. However, they must give the coated product a suitable color, fragrance, taste, flavor, and texture [27,28]. The efficiency of edible films or coatings is determined by three aspects: (i) the biomaterials used, (ii) the strategic and functional parameters of their application to food products, and (iii) the food product’s specific requirements [23].
The current study’s goal is to examine a specific selection of conventional materials based on their qualities, their application on foods, and the special requirements of food products, as well as various preparation methods. We also give an overview of the current research work on biopolymers and their implications for food packaging.

2. Sources of Biodegradable Material

A vast range of packaging materials obtained from inexhaustible resources has been developed in the last few years. Many plant and animal by-products are high in polysaccharides and proteins, which can be used to make edible or biodegradable coatings and film compositions. Commercial opportunities exist for alternative and novel materials made from underutilized food items, renewable resources, and the valorization of agro-industrial and marine waste. In a circular economy, using these resources adds value to waste products and provides an enticing alternative to nonrenewable sources. Furthermore, the vast majority are not only biodegradable, but also edible. These by-products could come from underutilized foods, renewable resources, and the valorization of agro-industrial and marine wastes, among other sources. Husks, feathers, shells, skins, seeds, peels, stems, and leaves are examples of by-products with significant value potential [29]. As the natures of these polymers are hydrophilic, i.e., they attract water easily, they therefore exhibit poor water vapor barriers and mechanical properties in comparison to plastic materials. That is why current research is mainly focused on improving these properties of polymers by incorporating reinforcing agents such as nano particles, bioactive functional compounds, etc., to make them more water resistant, similarly to plastic materials, in order to meet the functionality requirements of food packaging materials [30]. The various types of bio-based polymers commonly used in food packaging are schematically tabulated in Figure 1.

2.1. Plant-Based Material

2.1.1. Flour of Grains and Legumes

There has been a lot of research into edible films and coatings based on polysaccharides or proteins from traditional crops and roots [24]. Figure 2 lists the various materials that can be used to produce films.
According to Tóth and Halász (2019), psyllium husk and its flour are excellent sources for the making of packaging film [31]. When comparing the mechanical and water vapor properties of edible film made from eggplant flour and corn starch to film made without corn starch, Nouraddini et al. (2018) concluded that the mechanical and water vapor qualities of the former were compromised [32]. Components such as lipids, fibers and proteins exist in the edible polymers, and this could be the reason for these compromised physical properties. It has been reported that after 14 days these films entirely decayed, which demonstrates their excellent biodegradability [13].
Legumes have high nutritional value, consisting of high amounts of starch proteins, lipids, vitamins, and minerals. Due to this, they could be an excellent source for film formulations. The research work of Montalvo-Paquini et al. (2018) was based on popular Mexican beans including alubia, flor de mayo, garbancillo, peruano, pinto, mantequilla and negro, and an extracted bean protein concentrate was utilized as a protein source for edible films [33]. Navy beans are one of the largest pulse crops in the USA. It is pea-sized white legume and contains a high total amylose content, which may increase the elastic modulus of films and hence help to decreasing the water vapor permeability. Therefore, Zhang and Li (2021) prepared a film from navy bean starch and concluded that it has better mechanical and water barrier properties when compared to corn starch [34]. Ochoa-Yepes et al. (2018) developed composite films from cassava starch films with the addition of a residue of lentil protein production [35]. These films were more water resistant and mechanically stable, and were fully degradable. Moreover, they were able to tolerate temperatures of up to 240 °C. Kocakulak et al. (2019) worked on the production of edible films made from chickpeas with the addition of gallic acid, which was tested using different pH levels (9 and 11). Their findings concluded that at pH 11, the films have higher antioxidant activity and have better mechanical strength as compared to composite films; they can therefore be used for wrapping foods which are prone to oxidation [36].

2.1.2. Fruits and Vegetables Residues

The food sector generates considerable amounts of solid residue each year. Furthermore, these residues are high in nutrients and bioactive substances, as well as biopolymers such polysaccharides and dietary fibers [37]. Biopolymers derived from food waste are known for their ability to create films, which is the subject of the current research. Fruit and vegetable purees have been widely used as components of hydrocolloid films and coatings in prior studies [38]. Fruit and vegetable wastes, which are typically processed into flour, show promise as they contain film-forming components [39]. Many research articles have been reported recently regarding the use of fruits and vegetables as ingredients in edible films and coatings [40,41,42,43]. New edible films, based on flour including orange, passion fruit, watermelon, lettuce, courgette, carrot, spinach, mint, taro, cucumber, and rocket residue, were investigated [39]. Notably, without the use of plasticizers, the scientists were able to produce uniform, flexible films with promising properties. Furthermore, the addition of flour created from potato skin residue increased mechanical resistance [13]. Erica Ayquipa-Cuellar et al. (2021) obtained edible films from prickly pear peel mucilage and potato husk starch [44]. The film showed good barrier properties and physico-chemical properties due to the presence of glycerol, which is used as plasticizer. Therefore, these films can be used to wrap fruits and vegetables. Plant residues are complex materials in general, and so depending on their composition and particle size, distinct residue fractions could have varied applications, such as for the use in dietary fiber or as primary components for edible films and coatings [13].

2.1.3. Gums

Gum arabic, gum karaya, gum ghatti, mesquite, and tragacanth gum are just a few of the natural, plant-derived gum exudates that have been found in recent decades. Gum Arabic (or acacia gum) is a polysaccharide obtained from the gummy exudate of the stems and branches of the species of the genus Acacia, most often of the species Acacia senegal (L.) Wild. var. senegal. Gum arabic can also be obtained from the following species: Acacia senegal, Acacia seyal, Acacia polyacantha, Acacia gerrardii, and Acacia laeta [45]; it is one of the oldest and most well-known natural gums, having been used for over 5000 years. Gum arabic has a wide range of applications in the food, paint, and textile industries because to its emulsifying, stabilizing, thickening, and binding properties [46]. Furthermore, gum Arabic has the potential to be used as a protective edible covering for the extension of the shelf life of food goods, such as pecan nuts, by eliminating their moist and oily appearance [47].
Almond gum, also known as Persian gum, is a new gum exudate obtained from the almond tree’s trunk and branches. Bashir and Haripriya (2016) compared gum arabic and almond gum and found that almond gum has better physical features than gum arabic, such as bulk density, oil holding capacity, flowability, and mineral content [48].
Guar gum is a biopolymer which is hydrophilic in nature and is made from the seeds of the Cyamopsis tetragonoloba plant. Because of the huge number of hydroxyl groups, guar gum can form a homogenous edible film that is nearly water soluble [49,50].
Xanthan gum is an extracellular heteropolysaccharide made from a pure Xanthomonas campestris culture by submerged aerobic fermentation [51,52]. It is employed as an additive to starch-based films, resulting in an increase in some of their mechanical qualities, due to its capacity to form very viscous solutions at low concentrations and its biodegradability [53].
Polysaccharide-gum-based edible films and coatings create a semi-permeable barrier. Although weight loss may occur and the rate of respiration at the surface may be slowed, this helps to maintain the nutritious value of fruits and vegetables. This form of edible coating not only extends the shelf life of fruits and vegetables and prevents quality deterioration during storage, but also protects them from pathogens [54,55].
Robles-Flores et al. (2018) produced edible coatings from Cajanus cajan seed protein isolate and gum, which were successfully employed in improving the quality of coated strawberries [56]. Pinho tree seed flour and starch are good sources of complex carbohydrates with outstanding film-forming characteristics [57].

2.1.4. Pectin

Pectin is the fibrous component extracted from plant cell walls. It is a complex anionic polysaccharide composed of β-1,4-linked α-d-galacturonic acid residues, where the uronic acid carboxyl is either fully (high methoxy pectin) or partially (low methoxy pectin) methyl-esterified [58,59,60]. Research findings suggest that films produced from pectin have excellent mechanical properties as the raw material of pectin can act as a natural plasticizer, which helps in improving the extensibility of films [61,62]. Because pectin-based films are poor moisture barriers, they are only suggested for low-moisture foods [54,63]. Recent studies on production and the use of active films based on pectin (HMP) or pectin-containing plant products (e.g., fruit, vegetable, and hibiscus purees) with several natural antimicrobials (e.g., carvacrol and cinnamaldehyde, the main ingredients of oregano and cinnamon oil, respectively) have revealed the efficacy of these materials (dose-dependent bactericidal activity) to reduce the growth of foodborne pathogens (e.g., E. coli O157:H7, S. enterica, Campylobacter jejuni and Listeria monocytogenes) on meat and poultry products [64,65,66]. Therefore, pectin-based films with some additives such as natural herbs can make them effective for high moisture food as well. Research findings by Sucheta et al. (2019) suggested that composite films based on a starch and pectin in ratio of 1:1 or 60:40 can improve the mechanical, thermal, and structural properties of edible films [67].

2.1.5. Starch and Cellulose

Starch is a low-cost carbohydrate-based polymer that is obtained from a wide range of crops. The granules of native starch have a granular form and are made up of a combination of amylopectin (75%) and amylose (25%). d-glucopyranosyl units in the linear molecule amylose are connected by a-1,4 bonds. Amylopectin is a very large, highly branched molecule that contains a-d-glucopyranosyl units that are connected by a-1,4 and a-1,6 bonds [68]. Starch is mainly found in plants in tubers, seeds, and roots. The other sources of starch which are of industrial use are obtained from maize, wheat, edible cassava, potato, amaranth, and quinoa [68,69]. Their membrane- and gel-forming properties are due to their linear structure, which forms hydrogen bonds between hydroxyl groups of two parallel oriented chains, which tends to reduce the affinity of polymer to water [70]. Edible films with higher amylose content have better film-forming properties, i.e., better mechanical strength, elongation, and gas barrier properties. Starch-based films can be a good source for edible films and coatings due to good barrier properties against gases, cohesive strength, and durability. Additionally, these are tasteless, odorless, colorless, and nontoxic in nature. The mechanical properties of these films are, however, compromised due to high water vapor permeability [24].
Cellulose is most abundant natural polymer comprising d-glucose units linked through β-1,4-glycosidic bonds. Due to the large number of intramolecular hydrogen bonds, cellulose is insoluble in water; therefore, it cannot be directly used for film formation. Cellulose is treated with an alkali to swell its cell wall so that it can become soluble in water. For this, a reaction with methyl chloride, chloroacetic acid, or propylene oxide is carried out to obtain methyl cellulose (MC), carboxymethyl cellulose (CMC), hydroxypropyl cellulose (HPC) or hydroxypropyl methyl cellulose (HPMC) [71]. According to Krochta et al. (1997) the characteristics of cellulose, including its gas and moisture barrier, were directly proportional to its molecular weight, and the higher the molecular weight, the better the properties [72]. Edible films made of CMC provide an effective barrier against oxygen and carbon dioxide, but they have poor water barrier properties [73,74]. Mixing carboxymethyl cellulose with other polymers, such as starch and chitosan, has also been discovered to exacerbate the inherent limitations of CMC [54].

2.1.6. Proteins

Proteins typically occur as either fibrous proteins or globular proteins. Because of the chain-to-chain contact, protein-based films or coatings are regarded as highly efficient oxygen blockers, even at low relative humidity (RH). Protein-based films are hydrophilic, which means they have low to moderate water barriers and lose their film-forming properties when exposed to a highly humid environment. They provide a good barrier against hydrophobic chemicals such as oil and aroma. Antimicrobial and antioxidant substances are also present in protein-based edible films [75]. Various globular proteins, such as soy protein, wheat gluten, whey protein, and maize zein, have been investigated by researchers for their ability to form films or coatings [24]. Zein from corn and soy has demonstrated good film- and coating-forming characteristics. Zein is a corn-extracted hydrophobic protein. It can be utilized as an active edible packaging material to preserve the quality and shelf life of food goods due to its inherent antibacterial and antioxidant capabilities [76]. Films and coatings from zein protein are formed by first drying the aqueous ethanol solution of zein followed by the addition of plasticizer to improve flexibility. These films are proven to have good moisture barrier properties [24,77]. Soy protein is another kind of plant protein which is obtained from the soyabean. It has been reported that boiling soy milk to remove the water content results in a soy protein film being formed [24]. The air-drying process also follows this step. Soy protein films have high gas barrier properties compared to lipid- and polysaccharide-based films. Wheat protein (gluten) also has film-forming properties due to its cohesiveness and elastic behavior. The purity of gluten affects the appearance and mechanical properties of films. The addition of plasticizers such as glycerol or sorbitol enhances the flexibility of films and coatings [76].

2.2. Animal-Based Material

2.2.1. Marine Algae

Alginate, carrageenan, and agar are polysaccharide-based products extracted from marine algae. Alginate, also known as sodium salt of alginic acid, is obtained from brown seaweed, and possesses the ability to form films [13,78]. Divalent cations such as Ca, Mg, Mn, Al, and Fe are utilized to make alginate coating materials, which are employed as gelling agents [79,80]. Alginate exhibits excellent film-forming properties, imparting a uniform, transparent, glossy look to films. Alginate films are impervious to oils and fats and have high water vapor permeability similar to other hydrophilic polysaccharide [71]. Compared to other biopolymers, alginate has an idiosyncratic colloidal property, which contains a stabilizing, thickening, suspending film or coating, producing a gel-forming and stabilizing emulsion [80,81]. Alginate provides a number of advantages, including reduced shrinkage, and the retention of moisture, food color, and odor [79]. Due to its moisture-retaining properties, it can be used to protect fruits and vegetables from the loss of turgor as moisture is lost from protected part of edible plant only after moisture is lost from the coating. Due to the good barrier properties against gases, alginate films are helpful in delaying lipid oxidation and senescence, and in reducing weight loss in fruits and vegetables [71].
Carrageenan is a natural hydrophilic polymer with a linear chain of partially sulfated galactans that have high membrane formation potential [82,83]; they are most commonly used as coatings [84,85]. Edible films based on iota carrageenan have good mechanical properties as they are emulsion stabilizers and can reduce oxygen transfer and limit surface dehydration and the deterioration of fruit flavor [86]; due to this, they can effectively protect vegetables and fruit against the loss of moisture and turgor, the oxidation of compounds and ageing processes, and can reduce the number of microorganism if combined with ascorbic acid [78].
Agar, extracted from red seaweed, is basically a combined form of agarose (gelling fraction) and agaropectin (non-gelling fraction) [87,88]. Agarose forms a supporting structure in the cell walls of red algae and is responsible for the gelling capabilities of agar, which makes it suited to the production of edible coatings on vegetables and fruit [89]. Agar is noted for its hydrophilic nature and ability to generate robust, thermo-reversible gels. Under normal conditions, agar-based films and coatings are clear, robust, and inflexible, and they are activated with water [90].

2.2.2. Chitosan and Chitin

Chitin is a biopolymer found in the exoskeletons of crustaceans (shrimps, oysters, krill, crabs, squid, and lobsters), the cell walls of filamentous fungi (Mucoraceae), and in other biological materials such as the exoskeletons of arachnids and insects (bumblebees, crickets, bees, silkworm larval skin) [91,92,93].
Chitosan is obtained by N-deacetylation of chitin in an alkaline environment [94]. It is a copolymer made up of β-(1-4)-2-acetamido-d-glucose and β-(1-4)-2-amino-d-glucose units, with the latter accounting for more than 60% of the total [95]. Chitosan is a nontoxic polymer consisting of antifungal, anti-allergenic, antimicrobial, and anti-tumor properties. Due to its properties such as selective gas permeability (only for CO2 and O2), good mechanical properties, biocompatibility, and biodegradability it is environmentally friendly and is considered a good film-forming material [96,97,98,99,100,101]. Due to its ability to regulate gas permeability, edible chitosan coatings are applied to the surface of fruits and vegetables to reduce their respiration rate [102]. However, its limitations include low water solubility, due to which it forms a rigid crystal structure; additionally, its high water vapor permeability is not useful for humid environments [95,98,103].

2.2.3. Collagen and Gelatin

Collagen, the most ubiquitous protein in the body, can be used for a variety of purposes [104,105]. Collagen is frequently combined with other biopolymers in packaging applications. The agar–alginate–collagen film with silver nanoparticles, for example, has outstanding antibacterial capabilities (against Listeria monocytogenes and Escherichia coli) as well as strong mechanical and water resistance [106]. According to a study conducted in 2017, collagen was crosslinked with keratin (a protein taken from wool, bird feathers, skin, or hair), which improved the thermal resistance and mechanical capabilities of the collagen-based film [107].
Gelatin is a hydrophilic protein-based polymer derived from the collagen present in animal skin (such as fish, pork, bovine) and bones [108,109,110]. Bovine gelatin films have been found to have a hydrophobic surface and adding chitin to the gelatin film boosts the hydrophobicity even more [111]. Anthocyanins derived from red cabbage were introduced into a fish gelatin film, which demonstrated not only antioxidant action, but also improved the mechanical and water resistance properties of the film [112].

2.2.4. Pullulan

Pullulan is an abundant homopolysaccharide consisting of maltotriose units connected to each other by an α-(1,6)-glycosidic bond. It is synthesized by the yeast-like fungus Aureo basidium pullulans and has various advantages over other polysaccharides in terms of generating edible films [113]. Pullulan films are tasteless, colorless, heat and oil-resistant, have low oxygen permeability, and can be combined with other biopolymers and plasticizers to modify their mechanical and gas barrier properties in a controlled way [114,115,116]. Pullulan’s efficacy as an edible covering for strawberries is comparable to that of alginate, which is commonly utilized in the field, according to a focused and comparative study reported previously [117]; however, it trails behind chitosan, which is also well-known in this regard [118,119]. A pullulan covering mixed with an ethanol extract of bee propolis delayed ripening and weight loss in blueberries, reduced microbiological contamination, and extended shelf life [120]. To date, few studies have focused on the impact of the mixture of pullulan-based edible coatings, anti-browning agents, and antibacterial agents for minimally processed products to increase their shelf lives [121,122].

2.2.5. Xanthan

The industrially important exopolysaccharide xanthan is obtained from phytopathogenic bacteria of the genus Xanthomonas (mostly X. campestris pv. campestris), is made from different monomers (glucose, mannose, and glucuronic acid with acetate or pyruvate group), and has gained widespread recognition for its excellent miscibility, rheological properties, and consistency under a wide range of external conditions [123]. A study by Li et al. in 2017 showed that xanthan alone can also be used as an edible coating for fruits such as strawberries and blueberries, hence increasing the shelf life of products coated with substances such as pullulan [117]. A targeted study comparing xanthan with other compounds as edible coatings for blueberries found a significant advantage of this exopolysaccharide [124] over the plant-based guar gum and gum Arabic, which are substantial ingredients in related fruit coatings [119,125,126]. Totad et al., in his studies in 2019, stated that xanthan reduces water loss and retains fruit firmness [124]. It also maintains the level of antioxidants, ascorbic acid, total phenols, and anthocyanin content. Its gelling and film-forming properties can be improved with the addition of lipids [127].

2.2.6. Gellan

Gellan, as with xanthan, is a kind of extracellular heteropolysaccharide generated by Sphingomonas bacteria. Gellan has a good film-forming capacity since it is soluble in water, insoluble in ethanol, and has excellent colloidal and gelling characteristics. However, it has been reported that an edible strawberry coating made of gellan with glycerol as a plasticizer, enriched with natural antimicrobials (particularly geraniol) significantly reduced microbial counts (mesophilic and psychrophilic bacteria, yeasts, and molds), improving the microbiological stability of the berries when compared to untreated samples [128].

2.2.7. Milk Protein

Milk proteins are of two types; caseins and whey proteins. Films made from milk proteins are flexible and transparent in nature. These films also carry active antimicrobial and antioxidant agents to enhance the quality of food. Films from casein are stable at different pH, temperature, and salt levels. These films can act as carriers for antioxidants, food coloring, or antibacterial compounds (food additives). To prepare these films, an aqueous caseinate solution is made followed by drying [129]. Whey protein is obtained by the precipitation of casein protein from milk. Compared to films formed by casein protein, whey protein films show more barrier properties as suggested by Mohamed et al. in his studies [129]. An antifungal whey-based film, which was resistant against Aspergillus niger (103 spores/mL), was prepared by Braber [130] and his colleagues. Chitosan was incorporated in low quantities and, as a plasticizer, glycerol was utilized. In order to neutralize the chitosan charges, sodium tripolyphosphate was added. Interestingly, the results showed that whey-based films can be formed with excellent water permeability and good flexibility if almond oil is incorporated into the film formation matrix [131]. Due to its barrier properties, a whey protein coating with oregano essential oil is applied to chicken breast meat to control the growth of spoilage-causing bacteria [132].

2.3. Other Materials

Lipids

Lipids are not exactly considered to be biopolymers and hence are not suitable for the formation of cohesive films and coatings for food. However, lipids serve as an outstanding barrier against moisture and they can therefore be used to make films and coatings in combination with polysaccharides and proteins, as emulsified particles or multilayer coatings with enhanced characteristics [15]. Lipids are able to block moisture due to their low polarity, and their ability to form films and coatings with other materials depends on the chemical arrangement, chemical structure, chain length, physical state, degree of saturation and hydrophobicity of molecules [133]. The incorporation of lipids in edible films and coatings not only enhance their barrier properties, but also enhance their flexibility, cohesiveness, and hydrophobicity, which thereby improves the sensory properties of foods such as aroma and freshness, appearance, and tenderness. The moisture-blocking property of lipids in edible films can improve the microbiological stability of foods which helps to increase the shelf life of foods [134].
Lipid-based compounds mainly consist of herbal waxes, surfactants, and acetylated monoglycerides, which act as protective coverings on food surfaces [24]. Paraffin wax, a lipid-based compound containing strong hydrocarbon mixtures, is obtained by fraction distillation from crude petroleum. It is a result of the catalytic polymerization of ethylene. Films and coatings made from paraffin wax have found potential applications for covering highly perishable foods such as fruits and vegetables, cheese, etc. Candelilla, carnauba, and beeswax are also used to form coatings on different food products as they can effectively block moisture and vapor and can also improve the appearance of food products [24].
The reaction of acetylated glycerol with acetic anhydride produces 1-stearodiacetin. This acetylated monoglyceride can be easily solidified into a bendy, wax-like solid from its molten state. Acetylated glycerol monostearate has ultimate flexibility as it can extend up to 800% of its length. These films and coatings are usually applied on chicken and meat cuts to inhibit moisture loss during storage [24].

3. Functional Material for Edible Films and Coatings

The development of packaging in the form of coatings and films made from food-grade biopolymers has progressed dramatically in the previous decade, resulting in a succession of discoveries that have led to the invention of a variety of edible packaging. When used on food goods, this form of coating, in addition to maintaining the stability of the products, also results in an improved product appearance by minimizing physical damage and scars and by improving the shine of the surface [135]. This coating has the ability to act as a barrier at the product surface, preventing moisture loss, gas smells, and solute movement, as well as offering some functional qualities to the finished product [136]. During film preparation, the following ingredients are incorporated, which are gradually released into the food items, thereby improving their physical and chemical qualities. Antimicrobials and antioxidants, when integrated into films and coatings, enable for the extension of food shelf life and protection against unfavorable phenomena such as oxidation, rancidity, degradation, and discoloration. Furthermore, nutrients, flavors, and colorants can be utilized as active agents to improve the nutritional content of food, by adding vitamins and minerals, as well as the appearance and taste of the food [137]. Some examples of functional materials which are incorporated into biofilms and coatings as reinforcing agents/additives are discussed below.

3.1. Nanomaterials

In food packaging, the term “nanoparticle” refers to a wide variety of materials including (but not limited to) carbon materials [138,139], metals [140,141], metal oxides [142,143], mixed metal oxides [144], and nanolayers [145,146,147]. These materials are used as nanocomposites with characteristic physical, chemical, and biological properties [89,148,149].
The purpose of nanoparticles is to improve the sturdiness, abrasion resistance, and efficiency as a moisture, water, light, and environmental gas barrier in standard polymers [150]. Several nanocomposites with improved functions, such as gas, temperature, and humidity resistance, mechanical strength, and flexibility, have been created using various combinations of polymers and nanofillers [151]. Inorganic nanomaterials such as clays, layered double hydroxides (LDH), layered silicates, salts, metal oxides and metallic NPs, cylindrical metal oxide nanotubes (NTs), or gold nanorods (AuNRs) are commonly used as nano reinforcements. Natural NPs such as cellulose nanocrystals (CNCs), cellulose nanoparticles (CNPs), zein NPs, and others have also been used in a variety of polymers. Organic nanoparticles are used for the targeted drug delivery of nutraceuticals in food. Three types of organic NPs are identified: lipid-based, polysaccharide-based, and protein-based [152,153,154]. These nanoparticles aid in the storage of food and the preservation of its freshness and quality [150].
Though nanotechnology in food science has been extensively developed it has yet to be adopted at a large scale, owing to concerns about health and the environment, particularly during the storage stages. Furthermore, due to the multifaceted interaction profiles, detecting nanomaterials in food products (whether released or reacting with food content) is still a difficult task [155,156]. Researchers are still working to incorporate nanoparticles along with other materials to enhance the properties of films. In 2019, Amjadi et al. formulated an active packaging material using chitosan nanofibers with zinc oxide (ZnO) nanoparticles [157]. Cheese was used in their work as the food model to test the efficiency of this bio-nanocomposite film. According to the data, active packaging drastically reduced the growth of inoculation bacteria. Jafarzadeh et al. used ZnO-NPs in semolina films in another study. Antimicrobial activity was found against E. coli, S. aureus, Candida albicans, and Aspergillus niger [158]. The antibacterial activity increased when the number of ZnO-NPs was increased. Antibacterial activity was also higher over Gram-positive bacteria than against Gram-negative bacteria. They also showed that these films may be used to package mozzarella cheese. According to Alizadeh-Sani et al., combining TiO2 with rosemary essential oil (REO) to make cellulose nanofiber (CNF) films increased antibacterial activity against Gram-positive bacteria such as S. aureus. L. monocytogenes against Gram-negative bacteria such as E. coli O157:H7, E. coli O157:H7, P. fluorescens and P. enteritidis [159].

3.2. Natural Bioactive Material

Bioactive materials are biomaterials that include active chemicals with antibacterial or antioxidant capabilities. Natural bioactive elements are added into films to strengthen their characteristics, hence enhancing methods for food preservation [160,161]. Animal and plant materials from various food industries, such as the fruit and vegetable, grain-processing, brewery and winery, dairy, marine, and meat industries, can be classified into bioactive components from food by-products based on their origin. Each sector generates a considerable amount of residue, including seeds, pulps, peels, leaves, and stems from plant by-products, and skin, bones, and shells from animal by-products, all of which contain valuable compounds such as phenolics, flavonoids, phytosterols, peptides, and other antimicrobial and antioxidant compounds. The fruit industry generates a variety of by-products that are high in phenolic acids and other phenolic compounds, carotenoids, or vitamins, all of which have antioxidant properties. The hydroxyl groups and conjugated double bonds in phenolic substances serve as powerful antioxidants, scavenging free radicals. In addition to scavenging free radicals, phenolic compounds chelate transition metal ions, recombine radicals, and act as electron transfers, resulting in stable products. As a result, plant extracts containing phenolic compounds with significant antioxidant activity are ideal candidates for the development of active food packaging. Many extracts from food by-products demonstrate antibacterial activity against food-related microbes in addition to their antioxidant activity. For example, pomegranate peel extracts (20 mg/mL) inhibited the growth of a variety of food-related bacteria, including Staphylococcus aureus and Bacillus cereus [162].

3.3. Essential Oils (EOs)

Plant-based essential oils have become a popular research topic in recent years because they include functional and active chemicals. These are extracted from different plant parts such as the stems, leaves, flowers, and roots, and they consist of aldehydes, monoterpenes, flavonoids, isoflavones, carotenoids, alkaloids, phenolic acids, terpenes, and aromatic and aliphatic compounds. They are hydrophobic in nature, with a distinct odor [163,164,165]. EOs are extracted from plants as a product of secondary metabolism. They are highly lipophilic, volatile, and prone to oxidation and thermal degradation. Due to their lipophilic nature EOs are immiscible in water.
Because essential oils are derived from natural sources, they are typically considered safe for human consumption and are regarded as GRAS (generally recognized as safe) by the Food and Drug Administration of the United States (US-FDA). Despite the fact that most essential oils are regarded as safe, their usage as food additives is restricted due to their strong aroma. EOs are generally added into films by entrapping or encapsulating them within the polymeric matrix, resulting in decreased volatility and thereby increased efficiency [166]. Recently, numerous studies have showed that the use of EOs in edible films and coatings can enhance their barrier and mechanical properties [167]. Cai et al. added thyme essential oil to starch film to improve its tensile strength and water resistance [168]. Martins et al. found that the incorporation of oregano essential oil increased the tensile strength and elasticity of rice starch films but reduced the solubility and water vapor permeability of the film in water [169]. Nisar et al. added clove essential oil to the citrus pectin film, which improved the water resistance of the composite films [170].

4. Fabrication of Edible Packaging Materials

In recent years, the majority of edible component research has been concentrated on composite or multicomponent films in order to better understand the essential benefits of each component while minimizing their drawbacks [171,172]. Composite packaging can be defined as the combination of more than one kind of packaging biomaterial to improve the characteristics of overall packaging. The primary goal of composite (heterogeneous) films and coatings is to improve permeability or mechanical qualities [15]. Polysaccharides and protein-based films have high gas barrier capabilities, but they demonstrate an insufficient water vapor barrier. Lipids, on the other hand, have a good water barrier but a bad gas barrier. That is why composite films are made by combining lipid-based materials with polysaccharides or a protein-based polymer matrix in order to enhance gas and water vapor barrier in the resulting films. Lipids in composite films may also help to increase water vapor and oxygen barrier characteristics [15]. The composite coatings can be formed as either bilayer or stable emulsions [24]. The lipid forms a second layer above the polysaccharide layer in bilayer coatings. The lipid is disseminated and entrapped in the supporting matrix of protein or polysaccharide in emulsion coatings [173].
The efficacy of lipid material in this type of coating is determined by the lipid structure, chemical arrangement, hydrophobicity, physical state, and interaction with the other components of the film. Four processes are involved in the preparation of bilayer films and coatings: two casting stages and two drying stages. Several studies have documented the advancement of composite edibles and coatings. These studies include the use of lipid and hydroxypropyl methyl cellulose composite coatings, methyl cellulose (MC) and lipid composite coatings, corn zein, methylcellulose and fatty acid composite coatings, gelatin and fatty acid composite coatings, gelatin and soluble starch composite coatings, and corn zein and corn starch composite coatings [24]. Table 2 summarizes the brief details regarding the biopolymer-based films and coatings for food packaging applications.
Table 2. Brief summary for biomaterials used in edible packaging.
Table 2. Brief summary for biomaterials used in edible packaging.
BiomaterialSource/DerivativePropertiesApplicationsReferences
Flour of grains and legumesCorn starch, chickpeas, lentils, etc.High content of starch and protein results in good film-forming properties.Used as an edible film for wrapping foods.[13]
Fruit and vegetable residuesPeel, pomace, seed fraction, etc.Films are malleable, water soluble, improved mechanical and barrier properties, enhanced mechanical resistance.Can be used as edible films and coatings for perishable food items.[13]
Plant gumsGum arabic, gum karaya, gum ghatti, mesquite, etc.Potential material for edible film formation, exhibits good physical, chemical, biological properties.Edible films and coatings on fruits such as strawberries, tomatoes, and pecan nuts.[13]
PectinCell wall of plantsActs as a natural plasticizer, good mechanical properties, poor barrier properties.Edible coating for fruits, vegetables, cheese, and meat products.[24]
StarchCorn, potato, wheat, rice, etc.Tasteless, clear, O2 and CO2 barrier, not soluble in water, poor mechanical properties.Wrapper and coatings after some modifications.[174]
CelluloseCarboxymethyl cellulose (CMC), cellulose acetate (CA), methyl cellulose, ethyl cellulose, hydroxypropyl, hydroxyethyl cellulose, cellophane, etc.Not moisture resistant, good mechanical properties.Used for packaging of meat products, confectionary, and cheese.[77]
ProteinWheat gluten and corn zein, soy proteinWater solubility, opacity, and mechanical and barrier properties,
Not soluble in water, but absorb water when they are submerged.
Can be used after modifications, used in glues, dyes, and paper coatings.[24,76]
Marine algaeAlginate, agar, carrageenanNatural binder in coating.
Poor water resistance, good barrier for oxygen, lipid, and oxidation of fat.
Edible coatings for fruits, vegetables, cheese, and meat products.[77]
ChitosanExoskeleton of crustaceans, fungal cell walls, and other animal sourcesGood mechanical properties, good barriers for oxygen transition, antimicrobial properties.Used in fruit coatings, cellophane packaging.[77]
Collagen and gelatinHair, skin, nails, bones, and ligaments of beef or fishTranslucent films, permeable to moisture.Used in the coating of sausage and other meat products.[29]
PullulanMicrobiological sourceThermal and oil resistance, low gas barrier.Used for food coatings.[175]
XanthanMicrobiological sourceExcellent solubility, good rheological properties and stability.Used in coatings for fruits such as strawberries, garden berries, and grapes.[176]
GellanMicrobiological sourceExhibits good gelling, colloidal, and antimicrobial properties, exhibits good water solubility.Used in edible films and coatings for fruits and vegetables.[176]
Milk proteinsCaseinate and whey proteinCasein-based films are opaque and water insoluble, but they absorb water, and have good mechanical properties; expensive.Can be used to coat highly perishable foods such as meat products.[177,178,179,180]
LipidAcetoglycerides, beeswax, surfactants, triglycerides, fatty acidsWeak mechanical properties, good barrier against moisture migration.Edible coatings for fruit and meat products.[77,181,182]
Natural bioactive materialFruit waste, agricultural waste (antioxidant and antimicrobial compound)Exhibits excellent antioxidant and antimicrobial properties.Can be used as an active agent in edible films such as agar-based films.[29]

5. Fabrication of Composite Films and Coatings

While creating edible films and coatings from different biomaterials, it is important to keep in mind the ability of films to adhere to food surfaces and the methods by which edible films and coatings should be applied to food products so that they do not deteriorate the quality of the food [183]. The difference between the application of edible films and coatings on food is that films are formed separately by different methods and then applied, whereas coatings are directly applied to the food materials. The simple or mixed usage of diverse carbohydrate, protein, or lipid components in various forms (coatings, single-layer, bilayer, or multilayer films) has been proposed for the manufacture of edible films and coatings with regulated barrier properties and is acceptable for high-moisture foods [184].

5.1. Film Fabrication Methods

Gontard et al. (1996) proposed the following mechanisms of edible films formation after his studies on wheat gluten films [185].
  • Simple coacervation: This occurs when a hydrocolloid dispersed in water precipitates or changes phase after solvent evaporation (drying), after the addition of a hydro-soluble non-electrolyte in which the hydrocolloid is insoluble (e.g., ethanol), or after pH adjustment and the addition of an electrolyte that causes salting out or cross-linking.
  • Complex coacervation: When two hydrocolloid solutions with opposite electron charges are combined, the polymer complex interacts and precipitates.
  • Gelation or thermal coagulation: This is a process in which a macromolecule is heated, creating denaturation, and then gelatin (e.g., proteins such as ovalbumin) or precipitation, or even the cooling of a hydrocolloid dispersion, causing gelation (e.g., gelatin or agar).
Edible films can be used as primary edible packaging materials by wrapping them around the food surface. The solubility of additives in biopolymers is a critical aspect in their effectiveness. The overall mechanical properties of the film are influenced by the cohesive forces between biopolymers. Different methods for film deposition on food products have been investigated by scientists. Film-forming biopolymers and additives should have their chemical and structural properties well understood and modified for the generation of films for specific applications [186]. Orally soluble films containing active ingredients have been generated as a result of recent technological advancements in edible film fabrication. Ingredients for oral hygiene, caffeine for alertness, minerals, and botanicals are examples of actives included in film strips. (Bilal et al., 2020). Suhag et al. (2020) discussed two methods for obtaining edible films from bio-based materials [187].

5.1.1. Solvent Casting Method

The casting process is a popular and inexpensive method of film preparation. To make a biopolymer film, this process entails three phases as presented in Figure 3 [188].
(i) Solubilization of biopolymer in a suitable solvent: Selection of suitable biopolymer for film formation is the first basic step in edible film formation. The selected polymer or mixture of polymers is now dissolved in suitable solvent and this step is known as solubilization. For example, ethanol is used to dissolve soy protein isolate polymer. The casting of the film is dependent on the solubility of polymer rather than a melting process [189,190].
(ii) Casting of the solution in the mold: In this step, the resulting solution is poured into a predetermined mold or Teflon-coated glass plate. The drying process allows the solvent to evaporate, resulting in a polymer layer that adheres to the mold.
(iii) Drying of casted solution: To enhance the intramolecular interaction between the polymer chains and obtain a proper microstructure of the film, the air-drying technique for casting edible film is critical [191]. Rapid drying of the casting solution should be avoided because it reduces the solvent concentration too quickly, restricting polymer chain mobility and the formation of intermolecular interactions in the film [181]. For the casting of films, air driers such as hot air ovens, tray dryers, microwaves, and vacuum driers are used to remove solvents and peel the film [192].
The film’s structure is determined by the composition of the casting solution, the thickness of the wet casting, and the temperature and relative humidity of the drying circumstances [181]. COGIN, Bio Envelop, Chris-Kraft Polymer Inc., GREENSOL, and ENAK are among the companies that use this approach to produce edible films on a commercial scale [187]. Because it is a wet process, the bonding between the molecules of biopolymer is strong, which results in homogeneous coating. Since the casting method is a low-temperature production method, there is no risk of molecular degradation as a result of temperature fluctuations [15].
The main advantage of the casting method of film production is the ease with which it may be manufactured without specialized tools and at a reasonable cost at a lab scale (Chen et al., 2008). Because most food-processing materials cannot be molded at higher temperatures without causing irreversible structural changes, the lower temperature during the processing steps is another advantage [187].
The following are the major limitations of the casting method: (i) limiting the forms (usually, the only forms that can appear are simple sheets and tubes); (ii) casting requires a long drying time, which is not feasible for commercial production [189]; (iii) one of the most difficult challenges is converting film production from laboratory to production scale because many variables, such as heating, and the combination of speed and temperature, can cause quality differences and prevent constant development for commercial scales [193].

5.1.2. Extrusion Method

The extrusion process is based on the polymers’ thermoplastic characteristics [80]. In general, the extrusion process can be separated into three zones as shown in Figure 4 [194].
(i) The feeding zone: The film component mix is first carried into the feeding zone and then compressed with air, then the biopolymer and additives are added to the extruder.
(ii) The kneading zone: Wherein materials are adequately combined with the help of an extruder screw.
(iii) The heating zone at the final part/exit from the machine: The oven is used to supply some heat in the heating zone. Here, biopolymer and additives are melted and mixed. A die is fixed at the extruder’s end, determining the shape and thickness of the extruded film.
Because this approach works best with a small amount of water or solvents, it is also known as a dry procedure. Plasticizers, on the other hand, are required to increase film flexibility [195]. Plasticizers such as polyethylene glycol or sorbitol are frequently extruded in amounts ranging from 10% to 60% by weight [181]. Due to the lack of solvent addition and evaporation phases, extrusion is preferable in commercial applications.
We can make a multilayered film with better overall qualities if we utilize more than one extruder. Co-extrusion is the term for this procedure. In comparison to single-layer extruded film, the finished co-extruded film will have combined and improved qualities. Mechanical, optical, and barrier problems can occur as a result of variances in the chemical–physical characteristics of each film-forming substance [181].
The advantage of the extrusion method is that it is a high-performance, low-cost, and efficient process that is employed in the food industry for commercial manufacturing [25,196]. Other benefits include the absence of solvents, the ease of the handling of high viscosity polymers, a wide range of processing conditions (temperatures of 70–500 °C and pressures of 0–500 bar), and the improved control of feed residence time and mixing degree [197]. The comparison between the two film-making methodologies is presented in Table 3.

6. Methods of Coating

The efficiency of a coating depends on the method used to coat fruits, vegetables, and other foods [25,198]. The techniques used for this (dipping, spraying, etc.) are determined by the type of the food to be coated, its surface qualities, and the coating’s objective. The adhesion process, which involves diffusion between the surface area of the food product and the coating solution, follows the coating operations [135,199]. Surface tension, density, shape, size, coating thickness, and other physical factors, as well as food product attributes, influence coating methods [200,201]. Coatings are applied on food in the form of liquid suspensions, emulsions, powders, and other forms. Drying, heating, chilling, and coagulation processes are used to change the covering layers of food ingredients [187].

6.1. Dip Coating

Dipping is the most popular way of coating a food product, which involves forming a thin film on the surface that works as a semipermeable membrane to control moisture loss and gas transmission (Lin and Zhao, 2007). Food products are dipped in a prepared film formation solution to cover the surfaces of fruits, vegetables, and meat products in this method. This process is divided into three phases [82,202].
Immersion and dwelling: This involve immersing the substrate at a steady speed in the prepared coating solution to ensure complete interaction between the coating solution and the product’s surface.
Evaporation: The component’s coating composition must be diluted. After dilution, a considerable amount of residual material of the coating is formed. After the solvent has evaporated and the extra liquid has been removed, a thin film is produced [200].
Deposition: In this step, the precursor solution of the thin layer is formed on the surface of food products such as fruits, vegetables, and meat products by deposition.
In a past study, dipping techniques were utilized to improve the shelf life and appearance of fruits and vegetables, as well as other food products [203,204,205]. Because the dipping procedure is usually relatively short, the evaporation of solvents from the coating and crosslinking solutions is overlooked. The dipping and draining times vary by study, although they usually last 30 s to 5 min. The method’s key benefit is that it coats the entire surface, even if it is intricate or rough [135].
The dipping method is extensively used to coat fresh vegetables with edible coatings. In general, fruits and vegetables are submerged for 5–30 s in the edible coating formulation, and most fruits are simple to coat [25]. Dipping freshly cut fruit in an antimicrobial-containing aqueous solution is the most effective technique to increase microbial stability. The most frequent way to prevent fresh fruit from browning is to use antioxidant treatments as dips after peeling and/or cutting [206]. Chitosan coating is carried out on frozen salmon fish using the dipping method. This coating prevents pathogenic bacteria from growing and extends the shelf life of the fish [207].

6.2. Spray Coating

The spraying method is commonly utilized in industries on a broad scale due its low cost and high quality of end product [208]. In this method, a liquid solution is applied onto food products by spraying.
The liquid solution is converted into small droplets when it is sprayed. These droplets will have larger surface area for the same amount of liquid solution. As a result, droplets will cover a larger portion of the substance [187]. With the use of nozzles, the spraying system distributes the coating solution by forming droplets over the specified food surface area. Because of the high spraying pressure (approximately 60–80 psi), the spraying technique requires less coating material to obtain effective coverage [135]. Furthermore, a thickness of 30 μm was best for guaranteeing that water vapor and mechanical qualities were maintained, and therefore this parameter must be carefully controlled [209]. This approach can be classified into the following types based on how the droplets form (Figure 5).
Air spray atomization: A high-velocity stream of air surrounds fluid flowing from a low-velocity tube in this spraying method. Fluid-air friction causes atomization by speeding up and disrupting the liquid fluid flow. A spray is created through the nozzle. To break up the cylindrical water jet into fine droplets, a cylindrical water jet (deflector) air jet is utilized. It is mostly utilized for a fine droplet spray on food and food goods. Due to the use of air for spraying and the reduction of water volumes for product coating, it is a cost-effective technology [187,210].
Airless atomization: Because the edible coating is applied to food goods using pressure rather than air spray atomization, it is also known as pressure atomization. High pressure through a small nozzle is used to apply the coating solution to food goods. The pressure is a critical parameter that must be kept below 3.5 bars to avoid the destruction of the film-forming mechanism [200].
Air-assisted airless atomization: This approach combines the benefits of both airless and air spraying. Because of the combination of both, it gives great efficiency and creates droplets. With a unique fluid nozzle tip similar to a regular airless tip, air-assisted airless spray guns partially atomize the fluid. Second, they employ small volumes of compressed air from the face and/or horns of the air nozzle they use to finish the atomization. As a result, the spray pattern is finely atomized and resembles that of a compressed air system. This technique’s gentle spray helps to reduce fog and waste. This method is both novel and effective for edible coatings on food goods, as well as for improving the preservation efficiency of fruits and vegetables [208].
The pressure, viscosity, surface temperature, and tension of the coating solution, as well as the spray nozzle shape and design, all affect spraying efficiency. The nozzle shape affects the flux rate, droplet size, distance, angle, and overlap rate [201]. The spray piston and nozzle, as well as the temperature, air, and fluid flow of the polymer, all have a role in controlling the final drop size and hence the coating quality [211]. The uniform coating, thickness control, multilayer application capability, avoidance of coating solution contamination, solution temperature control, and ability to deal with vast surface areas are all advantages of this technology. The fact that excessively viscous biopolymer cannot be sprayed is a major disadvantage of this approach. The dipping approach is preferred for high-viscous biopolymers [187,200].

6.3. Electro Spraying

Traditional coating processes result in high coating-material losses (about 50%) and a heterogeneous coating material distribution on the product surface. That is why a coating process that can efficiently deposit the film uniformly over uneven surfaces is required. Electrostatic coating, which originated from the paint industry, is a promising and effective coating approach for foods. It is a more advanced version of the traditional spraying approach that increases the effectiveness of liquid particulate transfer to food particles. Since it has a higher transfer efficiency and it is able to form reproducible coatings on a target surface, it is applied to food products to reduce the use of solvents and the production of waste. In addition to the paint industry, this technique is often applied in the pharmaceutical and automotive industries. Based on the type of coating material, this technique can be divided into two types: dry (powder) and wet (liquid) coating [212].

6.3.1. Electrostatic Powder Coating

This method was previously utilized in the automotive painting industry in 1960, before it finds its application in the snack food processing industry [213]. When compared to non-electrostatic coating, this process produces a more even, uniform, and reproducible coating with less waste or overuse of expensive food powders because the powder particles are charged and repel one another, resulting in an even dispersion throughout the target surface. During powder coating, wire electrodes in the coating chamber or at the end of a charging gun create an electrostatic field. The charging of powder by an electric field is the initial stage in electrostatic coating. Charged particles resist each other due to their identical charge, generating an even cloud across the target surface [214]. The powder is more broadly dispersed and has a higher transfer efficiency at higher charges [215]. Two mechanisms can be used to charge powder: corona charging and tribo-charging. Powder particles pass through an ion-rich zone and are charged based on their permittivity in corona charging. As a result of the charge difference, they are transported towards the target and deposited. Tribo-charging is another method that uses the frictional charge of powder that is delivered through a pipe made of a certain material, such as PTFE, metal, or other powder particles [213,216,217]. Because tribo-charging leaves less charge on particles than corona charging [218], corona charging is the preferred method for electrostatic powder coating [219]. When a pneumatic system is utilized, the air movement produces aerodynamic force in addition to gravity and Coulombic forces, which transports the charged powder particles from the dispenser to the target surface [213]. The coating performance, including transfer efficiency, dust, adhesion, evenness, and the functionality of the electrostatically coated product, is influenced by the physical properties of the powders, including particle size, shape, charge, flow characteristics, resistivity, and density, as well as the target properties. Food powder coating is used in several food processes, particularly in the snack food industry, to improve the appearance and flavor of products such as potato chips, cakes, doughnuts, pretzels, crackers, and shredded cheese, resulting in increased market acceptability [220].

6.3.2. Electrostatic Liquid Coating

Electrostatic coating, also known as electrohydrodynamic coating, can be used to apply liquids. This is one of the most important developing technologies for applying oils, flavors, and emulsions to foods [221]. A liquid is dispersed into fine droplets, ranging in size from 0.1 to 1000 mm, in this coating technique, where the electrostatic force charging the liquid’s surface causes the stream of liquid to split into droplets [222]. In electro spraying, the coating substance is charged while travelling through a nozzle attached to a high-voltage source. These charges (electrostatic forces) break up the liquid jet into micro-droplets by overcoming the liquid’s surface tension. These forces also cause the liquid to shear, resulting in a fine cone-jet [223]. Charged micro-droplets resist each other in the air, creating a liquid cloud. With the charging of droplets, the coalescence of droplets is eliminated, and uniform-sized droplets are created. These charged droplets are attracted to the grounded surface with a high transfer efficiency (about 80%) and release their charge after deposition [224,225].
Electro spraying has also been used to produce nanoparticles of various proteins (such as WPI, WPC) and folic acid in starch, which improves the characteristics of these materials [226,227,228]. Similarly, probiotics with homogeneous particle size and a high number of viable counts have been encapsulated [229,230]. Proteins, carbohydrates, and lipids, either alone or in combination, serve as encapsulating materials (in the form of gel or solutions).

6.4. Panning Method

The panning coating process was developed within Greek Arabian society and was first utilized for drug applications. The panning method consists of placing the food and other items to be coated in a large rotating bowl known as a pan (Figure 6). The coating solution is then drizzled or dusted on the surface of the food product in a spinning bowl, and the product is tumbled to evenly distribute the coating solution. Coating layers are dried using forced air at room temperature or higher [231,232]. Heat is generated by friction with cold air during the panning process of applying coating to food products. This process is ideal for coating foods and confectionary. This approach is able to coat a large number of round or oval-shaped food items in a single batch.
The pharmaceutical industry has recently used a revolutionary electrostatic dry powder pan coating procedure to coat the surface of capsules and tablets. It is a well-established and widely used technology for improving powder deposition quality and coating uniformity. It is a good approach for coating conductive materials with the coating material. A powerful electrostatic charge is applied to the substratum. The substance composed of the leading ion species of the opposite charge is sprayed on the charged substratum. Fully and uniformly covered corners are obtained on the substratum [187].

6.5. Fluidized Bed Processing Method

The food sector initially rejected this technology due to the high costs involved. When compared to other coating technologies, the fluidized bed requires a greater amount of coating solution due to the loss on the column wall during spraying. In food processing and research, the fluidized bed method of edible coating is frequently utilized. It is used to coat dry particles with thin layers of coating material that are extremely low density and/or small in size. In a fluidized coating process, the coating solution and suspension are sprayed onto the fluidized powder surface via a number of nozzles to form a shell-like structure. When a flow of liquid travels upward through a bed of particles at a sufficient speed to assist the particles without diverting them into the liquid stream, the process is known as fluidization. At this moment, the particle bed accepts the bubbling fluid’s characteristics, i.e., fluidization [200]. There are three types of fluidized bed processes: top spray, bottom spray, and rotating fluidized bed. However, in the food industry, traditional top spraying is more effective than other methods [233]. Because the powders in the conventional bed do not fluidize stably or form excessive agglomerations in smaller sizes, the particle matter in the fluidized bed should be larger than 100 μm [234,235].
Fluidized bed coating prevents the creation of coated product clusters, which is a typical problem in pan coating. Fluidized bed coating also displays good drying effectiveness and allows for the use of a smaller surfactant choice in comparison to dipping and panning forms [236]. It does, however, take less time to process, gives complete coverage, and reduces cluster formation [237].

7. Application of Bio-Based Films and Coatings in Food

The above-mentioned film forming materials and methods for the creation of films and coatings have important applications in the food sector. When compared to conventional plastic packaging, edible packaging provides a selective barrier for water and oxygen, extending the shelf life of food goods [238]. Films and coatings have different applications, which are briefly covered in the sections below.

7.1. Application of Films

Edible films are wrapped around the food surface and used as the principal edible packaging for perishable foods such as meat, poultry, and dairy. The application of bio-based film in food packaging is briefly presented in Table 4.
Table 4. Application of edible films included with active ingredients and their effects on food products.
Table 4. Application of edible films included with active ingredients and their effects on food products.
BiomaterialFood ProductMethodKey ResultsReferences
Starch–alginate films with stearic acidGround beef pattyCastingImproved barrier properties against moisture and helpful in preventing oxidation of lipids.[135]
Chitosan with essential oilChicken filletCastingExhibits antimicrobial and inhibitory activities against spoilage-causing microorganism.[239]
Carrageenan with olive leaf extractsLamb meatCastingGood antioxidant activity due to presence of phenol, exhibits antimicrobial activity against Escherichia coli, Coliform. Demonstrates lower water vapor permeability which enhances its shelf life.[240]
Chickpea with gallic acidHighly oxidative foodCastingAntioxidant activity, phenolic content, demonstrates low water vapor permeability and good mechanical properties.[36]
Gelatin/cellulose nanofibril with Ag nanoparticle and glycerolFruits and vegetablesCastingGood antimicrobial activity against various microorganisms such as E. coli and S. aureus.[241]
Corn starch with glycerolMangoExtrusionAble to maintain physical and chemical qualities of mango for up to 16 days at 12 °C.[242]
Whey protein isolate with oregano essential oil, garlic oil, nisin, natamycinKasar cheeseCastingEffective against Listeria monocytogenes, staphylococcus aureus and Escherichia coli.[243]
Zein/gelatin with tea polyphenolFruits and vegetablesCastingAntimicrobial properties, prevents browning, and controls weight loss in fruits and vegetables.[244]
Tapioca Starch/Chitosan NanoparticlesCherry tomatoesCastingAntimicrobial property against gram positive bacteria, improves shelf life.[245]
Sodium-caseinate ExtrusionGood mechanical properties, water vapor permeability, water soluble.[246]
Sweet potato starchBaby spinach leafCastingAntimicrobial against E. coli and S. typhimurium[247]
Sodium alginate is a brown algae-derived biopolymer based on natural polysaccharides. It is a hydrophilic biopolymer with excellent film-forming properties. It has an excellent oxygen barrier. These alginate films were originally employed to regulate the rate of respiration of fruits and vegetables, but they are now used to wrap meat products. These edible films, when combined with active and antimicrobial ingredients, help to extend the shelf life of meat products [248]. Chicken breast meat is packaged using an alginate-based edible film with black cumin oil added as an antimicrobial agent. When stored at 40 °C, this film inhibits the growth of Escherichia coli and the change in meat color for about 5 days.
When compared to polysaccharides and other protein-based films, edible films created from whey protein have greater gas barrier qualities. Whey protein-based films have a higher film-forming tendency. Whey protein is combined with additives such as plasticizer, glycerol, and pH adjustment agents. Whey-protein-based films are similarly transparent, allowing the buyer to see the cheese’s quality [130]. The whey protein matrix contains antimicrobial compounds. Bacteria and yeast will be inhibited by these substances. Antimicrobial agents applied directly to the cheese have a lower likelihood of activating than agents introduced to the whey protein matrix. Staphylococcus spp., Pseudomonas spp., Enterobacteriaceae, yeast, and mold did not grow appreciably after 60 days of storage at 4 °C when whey protein isolates containing antimicrobials such as natamycin and lactic acid were utilized for the packing of semi-hard bovine cheese [249].
To improve the storage life of strawberries, Mali and Grossmann [250] used yam starch films as packaging. The researchers found that starch films slowed the degradation of stored samples and minimized microbial contamination. In addition, coated strawberries had a 21 day shelf life compared to 14 days for untreated strawberries. The polyphenol and tannin content in pomegranate peel extracts incorporated into zein films (2.5–7.5 g/100 g zein) has been demonstrated to have dose-dependent antimicrobial activity against E. coli, Clostridium perfringens, Micrococcus luteus, Enterococcus faecalis, S. aureus, Proteus vulgaris, and Salmonella typhii microbial [251]. Up to 15 days of storage, these antimicrobial zein coatings protected Himalayan cheese from deterioration, as evidenced by a decrease in total bacterial, mold, and yeast counts. In vitro experiments showed antimicrobial activity against S. aureus, B. cereus, B. subtilis, and E. coli using aqueous extracts of grape seeds from winery production mixed into chitosan films [252]. These antimicrobial films were applied to chicken breast fillets, resulting in a considerable reduction in the total mesophilic aerobic and coliform bacteria in the product after 15 days of storage and boosting lipid oxidation inhibition.

7.2. Application of Coatings

Coatings, which are applied directly to food, act as a barrier against contamination, air, moisture, and other contaminants while also extending shelf life by improving barrier qualities. The application of bio-based polymer coating in food packaging is discussed in Table 5.
Table 5. Application of edible coatings incorporated with active ingredients and their effects on food products.
Table 5. Application of edible coatings incorporated with active ingredients and their effects on food products.
BiopolymerActive IngredientResultsReferences
Coconut protein and guar gumTransglutaminase enzyme (oxygen scavenger)Better barrier properties, improved mechanical properties, water vapor permeability and oxygen transfer rates.[253]
ChitosanAscorbic acidSuppresses browning activity and prolongs microbial and chemical shelf life of freshly cut apples.[254]
StarchAdiantum capillus-veneris extractHelps in preservation and microbial treatment of freshly cut apples.[255]
Gelatin, chitosan, and cassava starchHibiscus rosa-sinensis (plant mucilage)Antimicrobial properties.[256]
Carboxymethyl celluloseImpatiens balsamina L. extractCoating on “Xinyu” tangerines shows a delay in ripening, decreased decay rate, increased antioxidant activity.[257]
AlginateGreen tea extractImproves safety in strawberries and raspberries against food-borne pathogens.[258]
Aloe vera extract (pure and diluted)Applied on tomatoes; pure extract inhibits the growth of bacteria while diluted extract maintains the quality of tomatoes during storage.
It also helps to delay ripening.
[259]
ChitosanNano emulsion with lemon oil extractIncreased shelf life of food product up to 7 days.[260]
CarrageenanAscorbic acid/citric acid/
oxalic acid
Coating applied to apples; possess antifungal and antioxidant activities. Improves color and firmness of product.[121]
Gum ArabicLemongrass oil and cinnamon oilShows antimicrobial activity on coated fruits such as banana and papaya.[71]
Candelilla waxMineral oilPrevents weight loss and helps in the prevention of loss of color; retain firmness of fruits such as guava and persian lime.[24]
LipidStearic acid, polyglycerol polyricinoleate and butterProvides excellent barrier against moisture in hygroscopic candy tablets.[24]
Chitosan and pectinTrans-cinnamaldehyde, beta-cyclodextrin hydrateHelps in extending shelf life of freshly cut cantaloupe at 4 °C.[261]
Pectin and sodium alginateEssential oilPrevents weight loss, demonstrates antioxidant and antimicrobial activity, improves sensory characteristics in fruits such as raspberries and prevents discoloration.[57]
Chitosan and alginateResveratrolAntioxidant and antimicrobial activity, prevents oxidation in smoked sea bass fillets.[262]
Chitosan blended with gelatin-Effective antimicrobial activity against S. aureus and demonstrated a considerable decrease in count of aerobic and total coliform in perishable foods such as beef.[263]
Carboxy methyl celluloseApple peel (1%) and tartaric acid (0.75%)Prevents lipid oxidation and shows significant decrease in aerobic plate, yeast, and mold in fresh beef patties. Additionally, no negative impact on sensory characteristics is observed.[264]
Carboxy methyl celluloseAscorbic acidImproved water vapor resistance, significant reduction in polyphenol oxidase activity, able to retain freshness of carrots during storage period.[265]
Gelatin and GlucoseSorbitol and cysteineActs as probiotic coating on hake fish due to presence of Lactobacillus acidophilus and Bifidobacterium bifidum, resulting in enhancing shelf life up to 15 days at refrigerated conditions.[266]
Cassava starch, chitosan and gallic acidGlycerolIncreased shelf life of ham slices.[267]
K-Carrageenan and chitosanGlycerol and oriental mustard extractReduced contamination of Campylobacter jejuni in fresh chicken breast along with enhancement of shelf life.[268]
Hydroxypropyl methyl cellulose and chitosanBergamot essential oilObserves inhibitory action and control over respiration rate and weight loss on cold-stored grapes.[269]
Research is ongoing in food packaging to incorporate different ingredients into the polymer matrixes, which can add some value to the food product [137]. These ingredients could be any colorant, flavors, nutrients, antioxidants, or antimicrobial compounds [24]. These bioactive compounds act as carriers for active ingredients which allow for the controlled release of functional materials while restricting the undesirable reaction between food and that compound. This kind of packaging is known as active packaging, which enhances the organoleptic characteristics of food while also improving its shelf life and nutritional value [270]. These functional compounds improve the properties of food by interacting with other ingredients by migrating to the middle or onto the surface of food. Their role in coating depends on the morphology, the microstructure and the material of the film, the chemical composition and polarity of the active ingredients incorporated and on the nature of the food product. The safety prospects of this technology are under research since films and coatings may also have a negative impact on food products [271].
The mode of action of these edible coatings involves: (a) the controlled release of active ingredients into food and, (b) the scavenging of undesirable compounds (browning and ethylene) and gases (oxygen and carbon dioxide) from the packaging surface [137].
The mechanism of active packaging is shown in Figure 7. When these coatings are formulated, scavenging compounds are incorporated into the coatings. Oxygen scavengers are also used to prevent the browning reaction of fruits and vegetables. The most commonly used synthetic oxygen scavengers are ferrous oxide, catechol, nylon, ascorbic acid, sulphites, and certain other enzymes [137]. These compounds react with the oxygen present in the packaging and decrease its concentration inside the food [272]. Carbon dioxide can also be used as an oxygen scavenging material since it has antimicrobial effects and can also help to overcome the partial vacuum created by oxygen scavengers. Some of the carbon dioxide emitters/scavengers commonly used are calcium hydroxide, potassium hydroxide, silica gel, etc. [272].
Similarly, browning effects can affect the organoleptic properties of food and hence anti browning compounds are cross-linked within a biopolymer matrix which prolongs the shelf life of food products when the active coating is applied to the food surface [273]. Ethylene, produced during the ripening of fruits and vegetables, results in the accelerated ageing of products, leading to deteriorated quality. Potassium permanganate, which acts as an ethylene absorber, can be incorporated into polymer in small amounts since high amounts could be toxic and harmful for health if they come into direct contact with food [137].
In order to increase food safety and prevent contamination, antimicrobial agents are added to films. These ingredients are released by evaporation/diffusion based on their volatility after remaining on food surfaces at high concentrations during storage [270]. The antimicrobial agent selected for this purpose should be compatible with the food product. Chemical agents, including organic acids, ethanol, and metals, and natural agents, including bacteriocins, enzymes, essential oils, and plants extracts, are used as antimicrobial agents in films and coatings. These agents are available in the form of extracts, concentrates, and integrated ingredients [270,272]. Practically, the natural functional agents or bioactive natural compounds are a much safer option over the chemical agents due to their nontoxicity.
In food products, unpleasant flavors and odors occur due to fat and lipid oxidation, which makes food products unacceptable for consumers. It is also responsible for the degradation of polyunsaturated fatty acids and the formation of toxic aldehyde which causes nutritional loss and the spoilage of food product [271]. This oxidation can be reduced by the use of antioxidants, which prevent the formation of free radicals by intruding within the free radical chain mechanism which is responsible for the oxidation process. These antioxidants are incorporated into coatings materials and then applied by coating onto oxidation-sensitive perishable food items such as meat and poultry products [270].
Highly perishable items such as meat and fish, dairy products, as well as fruits and vegetables, are some of the potential applications for these coatings. The edible coating surrounding the meat product prevents shrinkage, inhibits microbiological development, and prevents meat discoloration and unpleasant oxidative flavors (Figure 8). A variety of edible biopolymers are utilized to cover meat products [274,275]. Spraying and dipping the meat product in the coating-forming fluid produces the edible coating. When active ingredients are added to polysaccharides, they form active packaging that interacts with meat products and the environment, extending the shelf life of the meat product. Because alginate films are translucent, the consumer can see the colors and quality of the meat. In comparison to putting beautiful food-related artwork on the package, it is also an important component since buyers can view the product they will buy. According to studies, packaging transparency has an impact on customer purchasing decisions and bulk purchases [276]. Seafood has a short shelf life since it is very perishable. Because of the surrounding environment, seafood becomes contaminated during transit and storage, resulting in foodborne diseases and a change in the quality and nutritional content of the items. It also decreases seafood acceptability among consumers [134]. Fresh rainbow trout fish with a gelatin-based coating enhanced with cinnamon as an active antimicrobial agent is less likely to develop bacteria and thereby has a longer shelf life [277].
Butter is a high-fat dairy product with a short shelf life due to lipid oxidation. When kept at 2–5 °C, a corn-starch-based edible covering incorporating ginger oil inhibits lipid oxidation [278]. The addition of extract from Satureja intermedia to an apricot (Prunus armeniaca) gum coating has an antifungal effect against Penicillium citrinum, Fusarium oxysporum, Aspergillus flavus, and Alternaria alternate. Furthermore, the application of these active components in actual food has been investigated. During 60 days of storage, this coating successfully reduced the degree of microbial contamination caused by fungus on wild almond kernels [279].
Fruits and vegetables are, by far, the most popular coated products. This is due to their perishable nature, which has a significant influence on storage quality. As a result, coating technology is a viable strategy for extending the acceptability of fruits and vegetables among consumers as well as their shelf life (Figure 8). Aloe vera gel (AVG) is a polysaccharide-based natural biopolymer produced from aloe vera. For water and oxygen transmission, this gel works as a semipermeable membrane. It reduces the rate of respiration in fruits and vegetables, keeping the weight of the food product constant. It possesses antimicrobial and antioxidant qualities, extending the shelf life of fruits and vegetables. When this coating is applied to fruits or vegetables, it depletes the oxygen required for their metabolism. As a result, ripening and ageing are postponed, and the fruit or vegetable has a longer shelf life, even if the human consumes the coating. When AVG is applied to freshly cut papaya stored at 28 °C, it minimizes weight loss and keeps the papaya firm [280].

8. Conclusions and Future Perspective

Increasing environmental concerns have prompted research into the use of biodegradable packaging materials to replace traditional ones. In 2019, the global plastics output was estimated to be around 368 million tonnes. Plastic demand is on the rise due to the availability of takeaway and quick delivery services. However, poor recycling has mirrored the rise in plastic manufacturing, as seen in the European Union’s production of 61.8 million tonnes of plastic in 2018, compared to the recycling of just 9.4 million tonnes (https://www.plasticseurope.org/en/resources/market-data, accessed on 1 August 2022). It is important to ensure that the technology utilized to make edible films and coatings can be scaled up to meet such huge demands. With present findings, procedures such as solvent casting cannot be applied on a wide scale, and so more study is needed in this field. Furthermore, the raw materials used should be easily available, and therefore an emphasis should be placed on the use of industrial by-products as raw materials to contribute to long-term development. In this review paper, we looked at diverse biopolymer sources, active agents, and by-products that can be used to make films and coatings. All of these materials are food-grade and have been regarded as GRAS by the US-FDA. The properties of these materials, such as their moisture barrier, gas barrier, and mechanical and tensile strength, have contributed towards the development of films with enhanced attributes which may extend the shelf life of food products. These coatings can be applied as a single layer or in multiple layers, and they can be made from a variety of materials, improving the overall qualities of coatings and films. These films and coatings are applied to food products in a variety of ways: solvent casting and extrusion are employed for film production, and spraying, dipping, panning, and other processes are used for coating formation. These are directly applied to food goods and can be consumed with them. These operate as physical, chemical, and biological barriers, extending the shelf life of highly perishable foods such as meat, fruits, and vegetables. However, it is necessary to concentrate on the practical consequences of scaling up technologies utilized in the development of films and coatings in order to replace conventional technologies by lowering production costs and making them affordable. To attain more benefits of biopolymer-based films and coatings in food packaging applications, cost is a key factor that needs to be reduced for the packing of everyday products. According to recent reports, the prices of biopolymer-based films are in the range of USD 3–3.5/kg [281]. Based on a report of Jining Mingsheng New Material Co., Ltd., China, the approximate total cost for making bioplastic-based film is USD 3.6/kg [282].

Author Contributions

Conceptualization, V.G., D.B. and S.R.; software, V.G. and D.B.; validation, V.G., D.B. and S.R.; formal analysis, V.G. and D.B.; investigation, V.G.; writing—original draft preparation, V.G.; writing—review and editing, D.B. and S.R.; visualization, D.B. and S.R.; supervision, D.B. and S.R.; project administration, S.R. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Díaz-Montes, E.; Castro-Muñoz, R. Edible Films and Coatings as Food-Quality Preservers: An Overview. Foods 2021, 10, 249. [Google Scholar] [CrossRef] [PubMed]
  2. Versino, F.; Lopez, O.V.; Garcia, M.A.; Zaritzky, N.E. Starch-Based Films and Food Coatings: An Overview. Starch-Staerke 2016, 68, 1026–1037. [Google Scholar] [CrossRef]
  3. Derraik, J. The Pollution of the Marine Environment by Plastic Debris: A Review. Mar. Pollut. Bull. 2002, 44, 842–852. [Google Scholar] [CrossRef]
  4. Kumbhar, V.; Masali, P. Biodegradable Cutlery Using MoringaPod Husk: An Alternative to Conventional Plastic Cutlery. Int. J. Innov. Sci. Res. Technol. 2020, 5, 900–903. [Google Scholar]
  5. Garside, M. Global Plastic Production from 1950 to 2018 (in Million Metric Tons). Statista 2019, 2018. [Google Scholar]
  6. Porta, R. Plastic Pollution and the Challenge of Bioplastics. J. Appl. Biotechnol. Bioeng. 2017, 2, 111. [Google Scholar] [CrossRef]
  7. De Souza Machado, A.A.; Kloas, W.; Zarfl, C.; Hempel, S.; Rillig, M.C. Microplastics as an Emerging Threat to Terrestrial Ecosystems. Glob. Chang. Biol. 2018, 24, 1405–1416. [Google Scholar] [CrossRef]
  8. Li, W.C.; Tse, H.F.; Fok, L. Plastic Waste in the Marine Environment: A Review of Sources, Occurrence and Effects. Sci. Total Environ. 2016, 566–567, 333–349. [Google Scholar] [CrossRef]
  9. Prashanthi, M.; Rajakumar, S. Integrated Water Manageent in India: Status and Future Prospects for Environmental Sustainability; Springer: Berlin/Heidelberg, Germany, 2016; ISBN 978-3-319-27226-9. [Google Scholar]
  10. Patil, H.N.; Sinhal, P. A Study on Edible Cutlery: An Alternative for Conventional Ones. Atithya J. Hosp. 2018, 4, 45–51. [Google Scholar]
  11. United Nations. World Population Prospects: The 2019 Revision, Highlights, Departement of Economic and Social Affairs; United Nations: New York, NY, USA, 2019. [Google Scholar]
  12. Sarkodie, S.A.; Strezov, V.; Weldekidan, H.; Asamoah, E.F.; Owusu, P.A.; Doyi, I.N.Y. Environmental Sustainability Assessment Using Dynamic Autoregressive-Distributed Lag Simulations—Nexus between Greenhouse Gas Emissions, Biomass Energy, Food and Economic Growth. Sci. Total Environ. 2019, 668, 318–332. [Google Scholar] [CrossRef]
  13. Galus, S.; Kibar, E.A.A.; Gniewosz, M.; Kraśniewska, K. Novel Materials in the Preparation of Edible Films and Coatings-A Review. Coatings 2020, 10, 674. [Google Scholar] [CrossRef]
  14. Jooyandeh, H. Whey Protein Films and Coatings: A Review. Pak. J. Nutr. 2011, 10, 296–301. [Google Scholar] [CrossRef]
  15. Kumar, L.; Ramakanth, D.; Akhila, K.; Gaikwad, K.K. Edible Films and Coatings for Food Packaging Applications: A Review. Environ. Chem. Lett. 2021, 20, 875–900. [Google Scholar] [CrossRef]
  16. Asgher, M.; Qamar, S.A.; Bilal, M.; Iqbal, H.M.N. Bio-Based Active Food Packaging Materials: Sustainable Alternative to Conventional Petrochemical-Based Packaging Materials. Food Res. Int. 2020, 137, 109625. [Google Scholar] [CrossRef]
  17. Trajkovska Petkoska, A.; Daniloski, D.; D’Cunha, N.M.; Naumovski, N.; Broach, A.T. Edible Packaging: Sustainable Solutions and Novel Trends in Food Packaging. Food Res. Int. 2021, 140, 109981. [Google Scholar] [CrossRef]
  18. Saucedo-Pompa, S.; Rojas-Molina, R.; Aguilera-Carbó, A.F.; Saenz-Galindo, A.; de La Garza, H.; Jasso-Cantú, D.; Aguilar, C.N. Edible Film Based on Candelilla Wax to Improve the Shelf Life and Quality of Avocado. Food Res. Int. 2009, 42, 511–515. [Google Scholar] [CrossRef]
  19. Sogvar, O.B.; Koushesh Saba, M.; Emamifar, A. Aloe Vera and Ascorbic Acid Coatings Maintain Postharvest Quality and Reduce Microbial Load of Strawberry Fruit. Postharvest Biol. Technol. 2016, 114, 29–35. [Google Scholar] [CrossRef]
  20. Dave, R.K.; Ramana Rao, T.V.; Nandane, A.S. Improvement of Post-Harvest Quality of Pear Fruit with Optimized Composite Edible Coating Formulations. J. Food Sci. Technol. 2017, 54, 3917–3927. [Google Scholar] [CrossRef]
  21. Tavassoli-Kafrani, E.; Gamage, M.V.; Dumée, L.F.; Kong, L.; Zhao, S. Edible Films and Coatings for Shelf Life Extension of Mango: A Review. Crit. Rev. Food Sci. Nutr. 2022, 62, 2432–2459. [Google Scholar] [CrossRef]
  22. Jeya, J.; Chandrasekaran, M.; Venkatesan, S.P.; Sriram, V.; Britto, J.G.; Mageshwaran, G.; Durairaj, R.B. Scaling up Difficulties and Commercial Aspects of Edible Films for Food Packaging: A Review. Trends Food Sci. Technol. 2020, 100, 210–222. [Google Scholar] [CrossRef]
  23. Bizymis, A.P.; Tzia, C. Edible Films and Coatings: Properties for the Selection of the Components, Evolution through Composites and Nanomaterials, and Safety Issues. Crit. Rev. Food Sci. Nutr. 2021. [Google Scholar] [CrossRef] [PubMed]
  24. Hassan, B.; Chatha, S.A.S.; Hussain, A.I.; Zia, K.M.; Akhtar, N. Recent Advances on Polysaccharides, Lipids and Protein Based Edible Films and Coatings: A Review. Int. J. Biol. Macromol. 2018, 109, 1095–1107. [Google Scholar] [CrossRef] [PubMed]
  25. Raghav, K.; Agarwal, N.; Saini, M. Edible Coating of Fruits and Vegetables: A Review. Int. J. Sci. Res. Mod. Educ. 2016, 1, 188–204. [Google Scholar]
  26. Artiga-Artigas, M.; Acevedo-Fani, A.; Martín-Belloso, O. Improving the Shelf Life of Low-Fat Cut Cheese Using Nanoemulsion-Based Edible Coatings Containing Oregano Essential Oil and Mandarin Fiber. Food Control 2017, 76, 1–12. [Google Scholar] [CrossRef] [Green Version]
  27. Jridi, M.; Abdelhedi, O.; Salem, A.; Kechaou, H.; Nasri, M.; Menchari, Y. Physicochemical, Antioxidant and Antibacterial Properties of Fish Gelatin-Based Edible Films Enriched with Orange Peel Pectin: Wrapping Application. Food Hydrocoll. 2020, 103, 105688. [Google Scholar] [CrossRef]
  28. Valencia-Chamorro, S.A.; Palou, L.; Delŕio, M.A.; Pérez-Gago, M.B. Antimicrobial Edible Films and Coatings for Fresh and Minimally Processed Fruits and Vegetables: A Review. Crit. Rev. Food Sci. Nutr. 2011, 51, 872–900. [Google Scholar] [CrossRef]
  29. Chiralt, A.; Menzel, C.; Hernandez-García, E.; Collazo, S.; Gonzalez-Martinez, C. Use of By-Products in Edible Coatings and Biodegradable Packaging Materials for Food Preservation. In Sustainability of the Food System: Sovereignty, Waste, and Nutrients Bioavailability; Academic Press: Cambridge, MA, USA, 2020. [Google Scholar]
  30. Cano, A.; Chafer, M.; Chiralt, A.; Gonzalez-Martinez, C. Strategies to Improve the Functionality of Starch-Based Films. In Handbook of Composites from Renewable Materials; John Wiley & Sons: Hoboken, NJ, USA, 2017; Volumes 1–8. [Google Scholar]
  31. Tóth, A.; Halász, K. Characterization of Edible Biocomposite Films Directly Prepared from Psyllium Seed Husk and Husk Flour. Food Packag. Shelf Life 2019, 20, 100299. [Google Scholar] [CrossRef]
  32. Nouraddini, M.; Esmaiili, M.; Mohtarami, F. Development and Characterization of Edible Films Based on Eggplant Flour and Corn Starch. Int. J. Biol. Macromol. 2018, 120, 1639–1645. [Google Scholar] [CrossRef]
  33. Montalvo-Paquini, C.; Avila-Sosa, R.; López-Malo, A.; Palou, E. Preparation and Characterization of Proteinaceous Films from Seven Mexican Common Beans (Phaseolus vulgaris L.). J. Food Qual. 2018, 2018, 9782591. [Google Scholar] [CrossRef]
  34. Zhang, Y.; Li, Y. Comparison of Physicochemical and Mechanical Properties of Edible Films Made from Navy Bean and Corn Starches. J. Sci. Food Agric. 2021, 101, 1538–1545. [Google Scholar] [CrossRef]
  35. Ochoa-Yepes, O.; Medina-Jaramillo, C.; Guz, L.; Famá, L. Biodegradable and Edible Starch Composites with Fiber-Rich Lentil Flour to Use as Food Packaging. Starch-Staerke 2018, 70, 1700222. [Google Scholar] [CrossRef]
  36. Kocakulak, S.; Sumnu, G.; Sahin, S. Chickpea Flour-Based Biofilms Containing Gallic Acid to Be Used as Active Edible Films. J. Appl. Polym. Sci. 2019, 136, 47704. [Google Scholar] [CrossRef]
  37. Roberta, M.S.A.; Mariana, S.L.F.; E’dira, C.B.A.G. Functional Capacity of Flour Obtained from Residues of Fruit and Vegetables. Int. Food Res. J. 2014, 21, 1675–1681. [Google Scholar]
  38. Pelissari, F.M.; Andrade-Mahecha, M.M.; do Amaral Sobral, P.J.; Menegalli, F.C. Comparative Study on the Properties of Flour and Starch Films of Plantain Bananas (Musa paradisiaca). Food Hydrocoll. 2013, 30, 681–690. [Google Scholar] [CrossRef]
  39. Andrade, R.M.S.; Ferreira, M.S.L.; Gonçalves, É.C.B.A. Development and Characterization of Edible Films Based on Fruit and Vegetable Residues. J. Food Sci. 2016, 81, E412–E418. [Google Scholar] [CrossRef]
  40. McHugh, T.H.; Senesi, E. Apple Wraps: A Novel Method to Improve the Quality and Extend the Shelf Life of Fresh-Cut Apples. J. Food Sci. 2000, 65, 480–485. [Google Scholar] [CrossRef]
  41. Sothornvit, R.; Pitak, N. Oxygen Permeability and Mechanical Properties of Banana Films. Food Res. Int. 2007, 40, 365–370. [Google Scholar] [CrossRef]
  42. Wang, X.; Kong, D.; Ma, Z.; Zhao, R. Effect of Carrot Puree Edible Films on Quality Preservation of Fresh-Cut Carrots. Irish J. Agric. Food Res. 2015, 54, 64–71. [Google Scholar] [CrossRef]
  43. Rangel-Marrón, M.; Mani-López, E.; Palou, E.; López-Malo, A. Effects of Alginate-Glycerol-Citric Acid Concentrations on Selected Physical, Mechanical, and Barrier Properties of Papaya Puree-Based Edible Films and Coatings, as Evaluated by Response Surface Methodology. LWT 2019, 101, 83–91. [Google Scholar] [CrossRef]
  44. Ayquipa-Cuellar, E.; Salcedo-Sucasaca, L.; Azamar-Barrios, J.A.; Chaquilla-Quilca, G. Assessment of Prickly Pear Peel Mucilage and Potato Husk Starch for Edible Films Production for Food Packaging Industries. Waste Biomass Valorization 2021, 12, 321–331. [Google Scholar] [CrossRef]
  45. Motlagh, S.; Ravines, P.; Karamallah, K.A.; Ma, Q. The Analysis of Acacia Gums Using Electrophoresis. Food Hydrocoll. 2006, 20, 848–854. [Google Scholar] [CrossRef]
  46. Patel, S.; Goyal, A. Applications of Natural Polymer Gum Arabic: A Review. Int. J. Food Prop. 2015, 18, 986–998. [Google Scholar] [CrossRef]
  47. Mahfoudhi, N.; Hamdi, S. Use of Almond Gum and Gum Arabic as Novel Edible Coating to Delay Postharvest Ripening and to Maintain Sweet Cherry (Prunus avium) Quality during Storage. J. Food Process. Preserv. 2015, 39, 1499–1508. [Google Scholar] [CrossRef]
  48. Bashir, M.; Haripriya, S. Assessment of Physical and Structural Characteristics of Almond Gum. Int. J. Biol. Macromol. 2016, 93, 476–482. [Google Scholar] [CrossRef]
  49. Aydogdu, A.; Radke, C.J.; Bezci, S.; Kirtil, E. Characterization of Curcumin Incorporated Guar Gum/Orange Oil Antimicrobial Emulsion Films. Int. J. Biol. Macromol. 2020, 148, 110–120. [Google Scholar] [CrossRef]
  50. Banegas, R.S.; Zornio, C.F.; De Borges, A.M.G.; Porto, L.C.; Soldi, V. Preparation, Characterization and Properties of Films Obtained from Cross-Linked Guar Gum. Polimeros 2013, 23, 182–188. [Google Scholar] [CrossRef]
  51. Arismendi, C.; Chillo, S.; Conte, A.; Del Nobile, M.A.; Flores, S.; Gerschenson, L.N. Optimization of Physical Properties of Xanthan Gum/Tapioca Starch Edible Matrices Containing Potassium Sorbate and Evaluation of Its Antimicrobial Effectiveness. LWT-Food Sci. Technol. 2013, 53, 290–296. [Google Scholar] [CrossRef]
  52. Ge, L.; Li, X.; Zhang, R.; Yang, T.; Ye, X.; Li, D.; Mu, C. Development and Characterization of Dialdehyde Xanthan Gum Crosslinked Gelatin Based Edible Films Incorporated with Amino-Functionalized Montmorillonite. Food Hydrocoll. 2015, 51, 129–135. [Google Scholar] [CrossRef]
  53. Guo, J.; Ge, L.; Li, X.; Mu, C.; Li, D. Periodate Oxidation of Xanthan Gum and Its Crosslinking Effects on Gelatin-Based Edible Films. Food Hydrocoll. 2014, 39, 243–250. [Google Scholar] [CrossRef]
  54. Al-Tayyar, N.A.; Youssef, A.M.; Al-Hindi, R.R. Edible Coatings and Antimicrobial Nanoemulsions for Enhancing Shelf Life and Reducing Foodborne Pathogens of Fruits and Vegetables: A Review. Sustain. Mater. Technol. 2020, 26, e00215. [Google Scholar] [CrossRef]
  55. Otoni, C.G.; Avena-Bustillos, R.J.; Azeredo, H.M.C.; Lorevice, M.V.; Moura, M.R.; Mattoso, L.H.C.; McHugh, T.H. Recent Advances on Edible Films Based on Fruits and Vegetables—A Review. Compr. Rev. Food Sci. Food Saf. 2017, 16, 1151–1169. [Google Scholar] [CrossRef] [PubMed]
  56. Robles-Flores, G.D.C.; Abud-Archila, M.; Ventura-Canseco, L.M.C.; Meza-Gordillo, R.; Grajales-Lagunes, A.; Ruiz-Cabrera, M.A.; Gutiérrez-Miceli, F.A. Development and Evaluation of a Film and Edible Coating Obtained from the Cajanus Cajan Seed Applied to Fresh Strawberry Fruit. Food Bioprocess Technol. 2018, 11, 2172–2181. [Google Scholar] [CrossRef]
  57. Daudt, R.M.; Avena-Bustillos, R.J.; Williams, T.; Wood, D.F.; Külkamp-Guerreiro, I.C.; Marczak, L.D.F.; McHugh, T.H. Comparative Study on Properties of Edible Films Based on Pinhão (Araucaria angustifolia) Starch and Flour. Food Hydrocoll. 2016, 60, 279–287. [Google Scholar] [CrossRef]
  58. Chen, Y.; Xu, L.; Wang, Y.; Chen, Z.; Zhang, M.; Chen, H. Characterization and Functional Properties of a Pectin/Tara Gum Based Edible Film with Ellagitannins from the Unripe Fruits of Rubus Chingii Hu. Food Chem. 2020, 325, 126964. [Google Scholar] [CrossRef] [PubMed]
  59. Dhall, R.K. Advances in Edible Coatings for Fresh Fruits and Vegetables: A Review. Crit. Rev. Food Sci. Nutr. 2013, 53, 435–450. [Google Scholar] [CrossRef]
  60. Roy, S.; Rhim, J.-W. Fabrication of Pectin/Agar Blended Functional Film: Effect of Reinforcement of Melanin Nanoparticles and Grapefruit Seed Extract. Food Hydrocoll. 2021, 118, 106823. [Google Scholar] [CrossRef]
  61. Jahromi, M.; Niakousari, M.; Golmakani, M.T.; Mohammadifar, M.A. Physicochemical and Structural Characterization of Sodium Caseinate Based Film-Forming Solutions and Edible Films as Affected by High Methoxyl Pectin. Int. J. Biol. Macromol. 2020, 165, 1949–1959. [Google Scholar] [CrossRef]
  62. Roy, S.; Rhim, J.-W. Preparation of Pectin/Agar-Based Functional Films Integrated with Zinc Sulfide Nano Petals for Active Packaging Applications. Colloids Surf. B Biointerfaces 2021, 207, 111999. [Google Scholar] [CrossRef]
  63. Ezati, P.; Roy, S.; Rhim, J.-W. Pectin/Gelatin-Based Bioactive Composite Films Reinforced with Sulfur Functionalized Carbon Dots. Colloids Surf. A Physicochem. Eng. Asp. 2021, 636, 128123. [Google Scholar] [CrossRef]
  64. Ravishankar, S.; Jaroni, D.; Zhu, L.; Olsen, C.; McHugh, T.; Friedman, M. Inactivation of Listeria Monocytogenes on Ham and Bologna Using Pectin-Based Apple, Carrot, and Hibiscus Edible Films Containing Carvacrol and Cinnamaldehyde. J. Food Sci. 2012, 77, M377–M382. [Google Scholar] [CrossRef]
  65. Mild, R.M.; Joens, L.A.; Friedman, M.; Olsen, C.W.; Mchugh, T.H.; Law, B.; Ravishankar, S. Antimicrobial Edible Apple Films Inactivate Antibiotic Resistant and Susceptible Campylobacter jejuni Strains on Chicken Breast. J. Food Sci. 2011, 76, M163–M168. [Google Scholar] [CrossRef] [PubMed]
  66. Lazaridou, A.; Biliaderis, C.G. Edible Films and Coatings with Pectin. In Pectin: Technological and Physiological Properties; Springer: Cham, Switzerland, 2020; pp. 99–123. [Google Scholar] [CrossRef]
  67. Sucheta; Rai, S.K.; Chaturvedi, K.; Yadav, S.K. Evaluation of Structural Integrity and Functionality of Commercial Pectin Based Edible Films Incorporated with Corn Flour, Beetroot, Orange Peel, Muesli and Rice Flour. Food Hydrocoll. 2019, 91, 127–135. [Google Scholar] [CrossRef]
  68. Basiak, E.; Lenart, A. Starch Coatings Used in Food Packaging Industry. Zywn. Nauk. Technol. Jakosc/Food. Sci. Technol. Qual. 2013, 20, 21–31. [Google Scholar] [CrossRef]
  69. Roy, S.; Rhim, J.-W. Starch/Agar-Based Functional Films Integrated with Enoki Mushroom-Mediated Silver Nanoparticles for Active Packaging Applications. Food Biosci. 2022, 49, 101867. [Google Scholar] [CrossRef]
  70. Guimarães, I.C.; dos Reis, K.C.; Menezes, E.G.T.; Rodrigues, A.C.; da Silva, T.F.; de Oliveira, I.R.N.; Vilas Boas, E.V.D.B.V. Cellulose Microfibrillated Suspension of Carrots Obtained by Mechanical Defibrillation and Their Application in Edible Starch Films. Ind. Crops Prod. 2016, 89, 285–294. [Google Scholar] [CrossRef]
  71. Kocira, A.; Kozłowicz, K.; Panasiewicz, K.; Staniak, M.; Szpunar-Krok, E.; Hortyńska, P. Polysaccharides as Edible Films and Coatings: Characteristics and Influence on Fruit and Vegetable Quality—A Review. Agronomy 2021, 11, 813. [Google Scholar] [CrossRef]
  72. Krochta, J.M.; Mulder, J.C. Scientific Status Summary: Edible and Biodegradable Polymer Films: Challenges and Opportunities. Food Technol. 1997, 51, 61–74. [Google Scholar]
  73. Li, H.; Shi, H.; He, Y.; Fei, X.; Peng, L. Preparation and Characterization of Carboxymethyl Cellulose-Based Composite Films Reinforced by Cellulose Nanocrystals Derived from Pea Hull Waste for Food Packaging Applications. Int. J. Biol. Macromol. 2020, 164, 4104–4112. [Google Scholar] [CrossRef]
  74. Roy, S.; Rhim, J.W. Carboxymethyl Cellulose-Based Antioxidant and Antimicrobial Active Packaging Film Incorporated with Curcumin and Zinc Oxide. Int. J. Biol. Macromol. 2020, 148, 666–676. [Google Scholar] [CrossRef]
  75. Pooja Saklani, P.S.; Nath, S.; Kishor Das, S.; Singh, S.M. A Review of Edible Packaging for Foods. Int. J. Curr. Microbiol. Appl. Sci. 2019, 8, 2885–2895. [Google Scholar] [CrossRef]
  76. Mihalca, V.; Kerezsi, A.D.; Weber, A.; Gruber-Traub, C.; Schmucker, J.; Vodnar, D.C.; Dulf, F.V.; Socaci, S.A.; Fărcaș, A.; Mureșan, C.I.; et al. Protein-Based Films and Coatings for Food Industry Applications. Polymers 2021, 13, 769. [Google Scholar] [CrossRef] [PubMed]
  77. Grujic, R.; Vukic, M.; Gojkovic, V. Application of Biopolymers in the Food Industry. In Advances in Applications of Industrial Biomaterials; Springer: Cham, Switzerland, 2017. [Google Scholar]
  78. Lin, D.; Zhao, Y. Innovations in the Development and Application of Edible Coatings for Fresh and Minimally Processed Fruits and Vegetables. Compr. Rev. Food Sci. Food Saf. 2007, 6, 60–75. [Google Scholar] [CrossRef]
  79. Borchard, W.; Kenning, A.; Kapp, A.; Mayer, C. Phase Diagram of the System Sodium Alginate/Water: A Model for Biofilms. Int. J. Biol. Macromol. 2005, 35, 247–256. [Google Scholar] [CrossRef] [PubMed]
  80. Dhanapal, A.; Rajamani, L.; Banu, M. Edible Films from Polysaccharides. Food Sci. Qual. 2012, 3, 9–18. [Google Scholar]
  81. Rhim, J.W. Physical and Mechanical Properties of Water Resistant Sodium Alginate Films. LWT-Food Sci. Technol. 2004, 37, 323–330. [Google Scholar] [CrossRef]
  82. Tavassoli-Kafrani, E.; Shekarchizadeh, H.; Masoudpour-Behabadi, M. Development of Edible Films and Coatings from Alginates and Carrageenans. Carbohydr. Polym. 2016, 137, 360–374. [Google Scholar] [CrossRef]
  83. Osorio, F.A.; Molina, P.; Matiacevich, S.; Enrione, J.; Skurtys, O. Characteristics of Hydroxy Propyl Methyl Cellulose (HPMC) Based Edible Film Developed for Blueberry Coatings. Procedia Food Sci. 2011, 1, 287–293. [Google Scholar] [CrossRef]
  84. Campos, C.A.; Gerschenson, L.N.; Flores, S.K. Development of Edible Films and Coatings with Antimicrobial Activity. Food Bioprocess Technol. 2011, 4, 849–875. [Google Scholar] [CrossRef]
  85. Roy, S.; Ezati, P.; Rhim, J.-W. Gelatin/Carrageenan-Based Functional Films with Carbon Dots from Enoki Mushroom for Active Food Packaging Applications. ACS Appl. Polym. Mater. 2021, 3, acsapm.1c01175. [Google Scholar] [CrossRef]
  86. Hambleton, A.; Perpiñan-Saiz, N.; Fabra, M.J.; Voilley, A.; Debeaufort, F. The Schroeder Paradox or How the State of Water Affects the Moisture Transfer through Edible Films. Food Chem. 2012, 132, 1671–1678. [Google Scholar] [CrossRef]
  87. Schmidt, É.C.; dos Santos, R.; Horta, P.A.; Maraschin, M.; Bouzon, Z.L. Effects of UVB Radiation on the Agarophyte Gracilaria Domingensis (Rhodophyta, Gracilariales): Changes in Cell Organization, Growth and Photosynthetic Performance. Micron 2010, 41, 919–930. [Google Scholar] [CrossRef] [PubMed]
  88. Roy, S.; Rhim, J.-W. Gelatin/Agar-Based Functional Film Integrated with Pickering Emulsion of Clove Essential Oil Stabilized with Nanocellulose for Active Packaging Applications. Colloids Surf. A Physicochem. Eng. Asp. 2021, 627, 127220. [Google Scholar] [CrossRef]
  89. Rhim, J.W. Effect of Clay Contents on Mechanical and Water Vapor Barrier Properties of Agar-Based Nanocomposite Films. Carbohydr. Polym. 2011, 86, 691–699. [Google Scholar] [CrossRef]
  90. Boziaris, I.S. Novel Food Preservation and Microbial Assessment Techniques; CRC Press: Boca Raton, FL, USA, 2014. [Google Scholar]
  91. Zhang, M.; Haga, A.; Sekiguchi, H.; Hirano, S. Structure of Insect Chitin Isolated from Beetle Larva Cuticle and Silkworm (Bombyx Mori) Pupa Exuvia. Int. J. Biol. Macromol. 2000, 27, 99–105. [Google Scholar] [CrossRef]
  92. Majtán, J.; Bíliková, K.; Markovič, O.; Gróf, J.; Kogan, G.; Šimúth, J. Isolation and Characterization of Chitin from Bumblebee (Bombus Terrestris). Int. J. Biol. Macromol. 2007, 40, 237–241. [Google Scholar] [CrossRef]
  93. Sajomsang, W.; Gonil, P. Preparation and Characterization of α-Chitin from Cicada Sloughs. Mater. Sci. Eng. C 2010, 30, 357–363. [Google Scholar] [CrossRef]
  94. Shahid-ul-Islam; Butola, B.S. Recent Advances in Chitosan Polysaccharide and Its Derivatives in Antimicrobial Modification of Textile Materials. Int. J. Biol. Macromol. 2019, 121, 905–912. [Google Scholar] [CrossRef]
  95. Elsabee, M.Z.; Abdou, E.S. Chitosan Based Edible Films and Coatings: A Review. Mater. Sci. Eng. C 2013, 33, 1819–1841. [Google Scholar] [CrossRef]
  96. Domard, A.; Domard, M. Chitosan: Structure-Properties Relationship and Biomedical Applications. In Polymeric Biomaterials, 2nd ed.; CRC Press: Boca Raton, FL, USA, 2002. [Google Scholar]
  97. Youssef, A.M.; Abdel-Aziz, M.S.; El-Sayed, S.M. Chitosan Nanocomposite Films Based on Ag-NP and Au-NP Biosynthesis by Bacillus Subtilis as Packaging Materials. Int. J. Biol. Macromol. 2014, 69, 185–191. [Google Scholar] [CrossRef]
  98. Chaudhary, S.; Kumar, S.; Kumar, V.; Sharma, R. Chitosan Nanoemulsions as Advanced Edible Coatings for Fruits and Vegetables: Composition, Fabrication and Developments in Last Decade. Int. J. Biol. Macromol. 2020, 152, 154–170. [Google Scholar]
  99. Pajak, P.; Fortuna, T.; Przetaczek-Roznowska, I. Protein- and Polysaccharide-Based Edible Packagings: Profile and Applications. Zywn. Nauk. Technol. Jakosc/Food. Sci. Technol. Qual. 2013, 20, 5–18. [Google Scholar] [CrossRef]
  100. Roy, S.; Rhim, J.-W. Genipin-Crosslinked Gelatin/Chitosan-Based Functional Films Incorporated with Rosemary Essential Oil and Quercetin. Materials 2022, 15, 3769. [Google Scholar] [CrossRef] [PubMed]
  101. Roy, S.; Rhim, J.-W. Effect of Chitosan Modified Halloysite on the Physical and Functional Properties of Pullulan/Chitosan Biofilm Integrated with Rutin. Appl. Clay Sci. 2021, 211, 106205. [Google Scholar] [CrossRef]
  102. Hajji, S.; Younes, I.; Affes, S.; Boufi, S.; Nasri, M. Optimization of the Formulation of Chitosan Edible Coatings Supplemented with Carotenoproteins and Their Use for Extending Strawberries Postharvest Life. Food Hydrocoll. 2018, 83, 375–392. [Google Scholar] [CrossRef]
  103. Candir, E.; Ozdemir, A.E.; Aksoy, M.C. Effects of Chitosan Coating and Modified Atmosphere Packaging on Postharvest Quality and Bioactive Compounds of Pomegranate Fruit Cv. ‘Hicaznar.’ Sci. Hortic. 2018, 235, 235–243. [Google Scholar] [CrossRef]
  104. Avila Rodríguez, M.I.; Rodríguez Barroso, L.G.; Sánchez, M.L. Collagen: A Review on Its Sources and Potential Cosmetic Applications. J. Cosmet. Dermatol. 2018, 17, 20–26. [Google Scholar]
  105. Felician, F.F.; Xia, C.; Qi, W.; Xu, H. Collagen from Marine Biological Sources and Medical Applications. Chem. Biodivers. 2018, 15, e1700557. [Google Scholar]
  106. Wang, L.F.; Rhim, J.W. Preparation and Application of Agar/Alginate/Collagen Ternary Blend Functional Food Packaging Films. Int. J. Biol. Macromol. 2015, 80, 460–468. [Google Scholar] [CrossRef]
  107. Wu, X.; Liu, Y.; Liu, A.; Wang, W. Improved Thermal-Stability and Mechanical Properties of Type I Collagen by Crosslinking with Casein, Keratin and Soy Protein Isolate Using Transglutaminase. Int. J. Biol. Macromol. 2017, 98, 292–301. [Google Scholar] [CrossRef]
  108. Yadav, S.; Mehrotra, G.K.; Bhartiya, P.; Singh, A.; Dutta, P.K. Preparation, Physicochemical and Biological Evaluation of Quercetin Based Chitosan-Gelatin Film for Food Packaging. Carbohydr. Polym. 2020, 227, 115348. [Google Scholar] [CrossRef]
  109. Roy, S.; Rhim, J.-W. Gelatin/Cellulose Nanofiber-Based Functional Films Added with Mushroom-Mediated Sulfur Nanoparticles for Active Packaging Applications. J. Nanostruct. Chem. 2022, 2022, 1–12. [Google Scholar] [CrossRef]
  110. Roy, S.; Rhim, J.-W. Preparation of Gelatin/Carrageenan-Based Color-Indicator Film Integrated with Shikonin and Propolis for Smart Food Packaging Applications. ACS Appl. Bio Mater. 2020, 4, 770–779. [Google Scholar] [CrossRef]
  111. Hanani, Z.A.N.; Yee, F.C.; Nor-Khaizura, M.A.R. Effect of Pomegranate (Punica granatum L.) Peel Powder on the Antioxidant and Antimicrobial Properties of Fish Gelatin Films as Active Packaging. Food Hydrocoll. 2019, 89, 253–259. [Google Scholar] [CrossRef]
  112. Uranga, J.; Etxabide, A.; Guerrero, P.; de la Caba, K. Development of Active Fish Gelatin Films with Anthocyanins by Compression Molding. Food Hydrocoll. 2018, 84, 313–320. [Google Scholar] [CrossRef]
  113. Roy, S.; Rhim, J.-W. Fabrication of Copper Sulfide Nanoparticles and Limonene Incorporated Pullulan/Carrageenan-Based Film with Improved Mechanical and Antibacterial Properties. Polymers 2020, 12, 2665. [Google Scholar] [CrossRef]
  114. Barcelos, M.C.S.; Vespermann, K.A.C.; Pelissari, F.M.; Molina, G. Current Status of Biotechnological Production and Applications of Microbial Exopolysaccharides. Crit. Rev. Food Sci. Nutr. 2020, 60, 1475–1495. [Google Scholar]
  115. Diab, T.; Biliaderis, C.G.; Gerasopoulos, D.; Sfakiotakis, E. Physicochemical Properties and Application of Pullulan Edible Films and Coatings in Fruit Preservation. J. Sci. Food Agric. 2001, 81, 988–1000. [Google Scholar] [CrossRef]
  116. Niu, B.; Shao, P.; Chen, H.; Sun, P. Structural and Physiochemical Characterization of Novel Hydrophobic Packaging Films Based on Pullulan Derivatives for Fruits Preservation. Carbohydr. Polym. 2019, 208, 276–284. [Google Scholar] [CrossRef]
  117. Li, L.; Sun, J.; Gao, H.; Shen, Y.; Li, C.; Yi, P.; He, X.; Ling, D.; Sheng, J.; Li, J.; et al. Effects of Polysaccharide-Based Edible Coatings on Quality and Antioxidant Enzyme System of Strawberry during Cold Storage. Int. J. Polym. Sci. 2017, 2017, 9746174. [Google Scholar] [CrossRef]
  118. Radev, R.; Pashova, S. Application of Edible Films and Coatings for Fresh Fruit and Vegetables. Qual.-Access Success 2020, 21, 108–112. [Google Scholar]
  119. Shit, S.C.; Shah, P.M. Edible Polymers: Challenges and Opportunities. J. Polym. 2014, 2014, 427259. [Google Scholar] [CrossRef] [Green Version]
  120. Pobiega, K.; Igielska, M.; Włodarczyk, P.; Gniewosz, M. The Use of Pullulan Coatings with Propolis Extract to Extend the Shelf Life of Blueberry (Vaccinium corymbosum) Fruit. Int. J. Food Sci. Technol. 2021, 56, 1013–1020. [Google Scholar] [CrossRef]
  121. Qi, H.; Hu, W.; Jiang, A.; Tian, M.; Li, Y. Extending Shelf-Life of Fresh-Cut “Fuji” Apples with Chitosan-Coatings. Innov. Food Sci. Emerg. Technol. 2011, 12, 62–66. [Google Scholar] [CrossRef]
  122. Roy, S.; Priyadarshi, R.; Rhim, J.W. Development of Multifunctional Pullulan/Chitosan-Based Composite Films Reinforced with ZnO Nanoparticles and Propolis for Meat Packaging Applications. Foods 2021, 10, 2789. [Google Scholar] [CrossRef] [PubMed]
  123. Sengupta, D.; Datta, S.; Biswas, D. Towards a Better Production of Bacterial Exopolysaccharides by Controlling Genetic as Well as Physico-Chemical Parameters. Appl. Microbiol. Biotechnol. 2018, 102, 1587–1598. [Google Scholar]
  124. Totad, M.G.; Sharma, R.R.; Sethi, S.; Verma, M.K. Effect of Edible Coatings on ‘Misty’ Blueberry (Vaccinium corymbosum) Fruits Stored at Low Temperature. Acta Physiol. Plant. 2019, 41, 183. [Google Scholar] [CrossRef]
  125. Salehi, F. Edible Coating of Fruits and Vegetables Using Natural Gums: A Review. Int. J. Fruit Sci. 2020, 20, S570–S589. [Google Scholar]
  126. Saleem, M.S.; Ejaz, S.; Anjum, M.A.; Nawaz, A.; Naz, S.; Hussain, S.; Ali, S.; Canan, İ. Postharvest Application of Gum Arabic Edible Coating Delays Ripening and Maintains Quality of Persimmon Fruits during Storage. J. Food Process. Preserv. 2020, 44, e14583. [Google Scholar] [CrossRef]
  127. Baraiya, N.S.; Ramana Rao, T.V.; Thakkar, V.R. Composite Coating as a Carrier of Antioxidants Improves the Postharvest Shelf Life and Quality of Table Grapes (Vitis vinifera L. var. Thompson Seedless). J. Agric. Sci. Technol. 2016, 18, 93–107. [Google Scholar]
  128. Tomadoni, B.; Moreira, M.R.; Pereda, M.; Ponce, A.G. Gellan-Based Coatings Incorporated with Natural Antimicrobials in Fresh-Cut Strawberries: Microbiological and Sensory Evaluation through Refrigerated Storage. LWT 2018, 97, 384–389. [Google Scholar] [CrossRef]
  129. Mohamed, S.A.A.; El-Sakhawy, M.; El-Sakhawy, M.A.-M. Polysaccharides, Protein and Lipid -Based Natural Edible Films in Food Packaging: A Review. Carbohydr. Polym. 2020, 238, 116178. [Google Scholar] [CrossRef] [PubMed]
  130. Vanden Braber, N.L.; Di Giorgio, L.; Aminahuel, C.A.; Díaz Vergara, L.I.; Martin Costa, A.O.; Montenegro, M.A.; Mauri, A.N. Antifungal Whey Protein Films Activated with Low Quantities of Water Soluble Chitosan. Food Hydrocoll. 2021, 110, 106156. [Google Scholar] [CrossRef]
  131. Galus, S.; Kadzińska, J. Whey Protein Edible Films Modified with Almond and Walnut Oils. Food Hydrocoll. 2016, 52, 78–86. [Google Scholar] [CrossRef]
  132. Umaraw, P.; Munekata, P.E.S.; Verma, A.K.; Barba, F.J.; Singh, V.P.; Kumar, P.; Lorenzo, J.M. Edible Films/Coating with Tailored Properties for Active Packaging of Meat, Fish and Derived Products. Trends Food Sci. Technol. 2020, 98, 10–24. [Google Scholar]
  133. Rhim, J.W.; Shellhammer, T.H. Lipid-Based Edible Films and Coatings. In Innovations in Food Packaging; Elsevier: Amsterdam, The Netherlands, 2005. [Google Scholar]
  134. Dehghani, S.; Hosseini, S.V.; Regenstein, J.M. Edible Films and Coatings in Seafood Preservation: A Review. Food Chem. 2018, 240, 505–513. [Google Scholar]
  135. Parreidt, T.S.; Müller, K.; Schmid, M. Alginate-Based Edible Films and Coatings for Food Packaging Applications. Foods 2018, 7, 170. [Google Scholar] [CrossRef] [Green Version]
  136. Murrieta-Martínez, C.L.; Soto-Valdez, H.; Pacheco-Aguilar, R.; Torres-Arreola, W.; Rodríguez-Felix, F.; Márquez Ríos, E. Edible Protein Films: Sources and Behavior. Packag. Technol. Sci. 2018, 31, 113–122. [Google Scholar]
  137. Ribeiro, A.M.; Estevinho, B.N.; Rocha, F. Preparation and Incorporation of Functional Ingredients in Edible Films and Coatings. Food Bioprocess Technol. 2021, 14, 209–231. [Google Scholar]
  138. Jafarzadeh, S.; Alias, A.K.; Ariffin, F.; Mahmud, S.; Najafi, A.; Sheibani, S. Characterization of a New Biodegradable Edible Film Based on Semolina Loaded with Nano Kaolin. Int. Food Res. J. 2017, 24, 304–309. [Google Scholar]
  139. Garavand, F.; Cacciotti, I.; Vahedikia, N.; Salara, A.R.; Tarhan, Ö.; Akbari-Alavijeh, S.; Shaddel, R.; Rashidinejad, A.; Nejatian, M.; Jafarzadeh, S.; et al. A Comprehensive Review on the Nanocomposites Loaded with Chitosan Nanoparticles for Food Packaging. Crit. Rev. Food Sci. Nutr. 2020, 62, 1383–1416. [Google Scholar]
  140. Cakmak, H.; Kumcuoglu, S.; Tavman, S. Production of Edible Coatings with Twin-Nozzle Electrospraying Equipment and the Effects on Shelf-Life Stability of Fresh-Cut Apple Slices. J. Food Process Eng. 2018, 41, e12627. [Google Scholar] [CrossRef]
  141. Pirozzi, A.; Del Grosso, V.; Ferrari, G.; Donsì, F. Edible Coatings Containing Oregano Essential Oil Nanoemulsion for Improving Postharvest Quality and Shelf Life of Tomatoes. Foods 2020, 9, 1605. [Google Scholar] [CrossRef] [PubMed]
  142. Dwivany, F.M.; Aprilyandi, A.N.; Suendo, V.; Sukriandi, N. Carrageenan Edible Coating Application Prolongs Cavendish Banana Shelf Life. Int. J. Food Sci. 2020, 2020, 8861610. [Google Scholar] [CrossRef] [PubMed]
  143. Hermawan, D.; Lai, T.K.; Jafarzadeh, S.; Gopakumar, D.A.; Hasan, M.; Owolabi, F.A.T.; Sri Aprilia, N.A.; Rizal, S.; Khalil, H.P.S.A. Development of Seaweed-Based Bamboo Microcrystalline Cellulose Films Intended for Sustainable Food Packaging Applications. BioResources 2019, 14, 3389–3410. [Google Scholar] [CrossRef]
  144. Biswas, M.C.; Tiimob, B.J.; Abdela, W.; Jeelani, S.; Rangari, V.K. Nano Silica-Carbon-Silver Ternary Hybrid Induced Antimicrobial Composite Films for Food Packaging Application. Food Packag. Shelf Life 2019, 19, 104–113. [Google Scholar] [CrossRef]
  145. Sobhan, A.; Muthukumarappan, K.; Wei, L.; Van Den Top, T.; Zhou, R. Development of an Activated Carbon-Based Nanocomposite Film with Antibacterial Property for Smart Food Packaging. Mater. Today Commun. 2020, 23, 101124. [Google Scholar] [CrossRef]
  146. Dairi, N.; Ferfera-Harrar, H.; Ramos, M.; Garrigós, M.C. Cellulose Acetate/AgNPs-Organoclay and/or Thymol Nano-Biocomposite Films with Combined Antimicrobial/Antioxidant Properties for Active Food Packaging Use. Int. J. Biol. Macromol. 2019, 121, 508–523. [Google Scholar] [CrossRef]
  147. Saedi, S.; Shokri, M.; Roy, S.; Rhim, J.-W. Silver Loaded Aminosilane Modified Halloysite for the Preparation of Carrageenan-Based Functional Films. Appl. Clay Sci. 2021, 211, 106170. [Google Scholar] [CrossRef]
  148. Alves, L.; Ferraz, E.; Gamelas, J.A.F. Composites of Nanofibrillated Cellulose with Clay Minerals: A Review. Adv. Colloid Interface Sci. 2019, 272, 101994. [Google Scholar] [CrossRef]
  149. Abu-Thabit, N.; Saeed Hakeem, A.; Mezghani, K.; Ratemi, E.; Elzagheid, M.; Umar, Y.; Primartomo, A.; Al Batty, S.; Kalam Azad, A.; Al Anazi, S.; et al. Preparation of pH-Indicative and Flame-Retardant Nanocomposite Films for Smart Packaging Applications. Sensors 2020, 20, 5462. [Google Scholar] [CrossRef]
  150. Alfei, S.; Marengo, B.; Zuccari, G. Nanotechnology Application in Food Packaging: A Plethora of Opportunities versus Pending Risks Assessment and Public Concerns. Food Res. Int. 2020, 137, 109664. [Google Scholar] [CrossRef] [PubMed]
  151. Raquez, J.M.; Habibi, Y.; Murariu, M.; Dubois, P. Polylactide (PLA)-Based Nanocomposites. Prog. Polym. Sci. 2013, 38, 1504–1542. [Google Scholar] [CrossRef]
  152. Peters, R.; ten Dam, G.; Bouwmeester, H.; Helsper, H.; Allmaier, G.; vd Kammer, F.; Ramsch, R.; Solans, C.; Tomaniová, M.; Hajslova, J.; et al. Identification and Characterization of Organic Nanoparticles in Food. TrAC-Trends Anal. Chem. 2011, 30, 100–112. [Google Scholar] [CrossRef]
  153. Roy, S.; Kim, H.C.; Kim, J.W.; Zhai, L.; Zhu, Q.Y.; Kim, J. Incorporation of Melanin Nanoparticles Improves UV-Shielding, Mechanical and Antioxidant Properties of Cellulose Nanofiber Based Nanocomposite Films. Mater. Today Commun. 2020, 24, 100984. [Google Scholar] [CrossRef]
  154. Łopusiewicz, Ł.; Macieja, S.; Śliwiński, M.; Bartkowiak, A.; Roy, S.; Sobolewski, P. Alginate Biofunctional Films Modified with Melanin from Watermelon Seeds and Zinc Oxide/Silver Nanoparticles. Materials 2022, 15, 2381. [Google Scholar] [CrossRef]
  155. Jafarzadeh, S.; Ariffin, F.; Mahmud, S.; Alias, A.K.; Hosseini, S.F.; Ahmad, M. Improving the Physical and Protective Functions of Semolina Films by Embedding a Blend Nanofillers (ZnO-Nr and Nano-Kaolin). Food Packag. Shelf Life 2017, 12, 66–75. [Google Scholar] [CrossRef]
  156. Hasan, M.; Chong, E.W.N.; Jafarzadeh, S.; Paridah, M.T.; Gopakumar, D.A.; Tajarudin, H.A.; Thomas, S.; Khalil, H.P.S.A. Enhancement in the Physico-Mechanical Functions of Seaweed Biopolymer Film via Embedding Fillers for Plasticulture Application-A Comparison with Conventional Biodegradable Mulch Film. Polymers 2019, 11, 210. [Google Scholar] [CrossRef]
  157. Amjadi, S.; Emaminia, S.; Nazari, M.; Davudian, S.H.; Roufegarinejad, L.; Hamishehkar, H. Application of Reinforced ZnO Nanoparticle-Incorporated Gelatin Bionanocomposite Film with Chitosan Nanofiber for Packaging of Chicken Fillet and Cheese as Food Models. Food Bioprocess Technol. 2019, 12, 1205–1219. [Google Scholar] [CrossRef]
  158. Jafarzadeh, S.; Rhim, J.W.; Alias, A.K.; Ariffin, F.; Mahmud, S. Application of Antimicrobial Active Packaging Film Made of Semolina Flour, Nano Zinc Oxide and Nano-Kaolin to Maintain the Quality of Low-Moisture Mozzarella Cheese during Low-Temperature Storage. J. Sci. Food Agric. 2019, 99, 2716–2725. [Google Scholar] [CrossRef]
  159. Alizadeh-Sani, M.; Khezerlou, A.; Ehsani, A. Fabrication and Characterization of the Bionanocomposite Film Based on Whey Protein Biopolymer Loaded with TiO2 Nanoparticles, Cellulose Nanofibers and Rosemary Essential Oil. Ind. Crops Prod. 2018, 124, 300–315. [Google Scholar] [CrossRef]
  160. Roy, S.; Rhim, J.-W. Anthocyanin Food Colorant and Its Application in PH-Responsive Color Change Indicator Films. Crit. Rev. Food Sci. Nutr. 2020, 61, 2297–2325. [Google Scholar] [CrossRef] [PubMed]
  161. Kim, H.-J.; Roy, S.; Rhim, J.-W. Gelatin/Agar-Based Color-Indicator Film Integrated with Clitoria Ternatea Flower Anthocyanin and Zinc Oxide Nanoparticles for Monitoring Freshness of Shrimp. Food Hydrocoll. 2022, 124, 107294. [Google Scholar] [CrossRef]
  162. Agourram, A.; Ghirardello, D.; Rantsiou, K.; Zeppa, G.; Belviso, S.; Romane, A.; Oufdou, K.; Giordano, M. Phenolic Content, Antioxidant Potential, and Antimicrobial Activities of Fruit and Vegetable by-Product Extracts. Int. J. Food Prop. 2013, 16, 1092–1104. [Google Scholar] [CrossRef]
  163. Kaya, M.; Ravikumar, P.; Ilk, S.; Mujtaba, M.; Akyuz, L.; Labidi, J.; Salaberria, A.M.; Cakmak, Y.S.; Erkul, S.K. Production and Characterization of Chitosan Based Edible Films from Berberis Crataegina’s Fruit Extract and Seed Oil. Innov. Food Sci. Emerg. Technol. 2018, 45, 287–297. [Google Scholar] [CrossRef]
  164. Ribeiro-Santos, R.; Andrade, M.; de Melo, N.R.; Sanches-Silva, A. Use of Essential Oils in Active Food Packaging: Recent Advances and Future Trends. Trends Food Sci. Technol. 2017, 61, 132–140. [Google Scholar] [CrossRef]
  165. Boukaew, S.; Prasertsan, P.; Sattayasamitsathit, S. Evaluation of Antifungal Activity of Essential Oils against Aflatoxigenic Aspergillus flavus and Their Allelopathic Activity from Fumigation to Protect Maize Seeds during Storage. Ind. Crops Prod. 2017, 97, 558–566. [Google Scholar] [CrossRef]
  166. Anis, A.; Pal, K.; Al-Zahrani, S.M. Essential Oil-Containing Polysaccharide-Based Edible Films and Coatings for Food Security Applications. Polymers 2021, 13, 575. [Google Scholar] [CrossRef]
  167. Atarés, L.; Chiralt, A. Essential Oils as Additives in Biodegradable Films and Coatings for Active Food Packaging. Trends Food Sci. Technol. 2016, 48, 51–62. [Google Scholar] [CrossRef]
  168. Cai, C.; Ma, R.; Duan, M.; Deng, Y.; Liu, T.; Lu, D. Effect of Starch Film Containing Thyme Essential Oil Microcapsules on Physicochemical Activity of Mango. LWT 2020, 131, 109700. [Google Scholar] [CrossRef]
  169. Martins, P.C.; Bagatini, D.C.; Martins, V.G. Oregano Essential Oil Addition in Rice Starch Films and Its Effects on the Chilled Fish Storage. J. Food Sci. Technol. 2021, 58, 1562–1573. [Google Scholar] [CrossRef]
  170. Nisar, T.; Wang, Z.C.; Yang, X.; Tian, Y.; Iqbal, M.; Guo, Y. Characterization of Citrus Pectin Films Integrated with Clove Bud Essential Oil: Physical, Thermal, Barrier, Antioxidant and Antibacterial Properties. Int. J. Biol. Macromol. 2018, 106, 670–680. [Google Scholar] [CrossRef] [PubMed]
  171. Kurek, M.; Galus, S.; Debeaufort, F. Surface, Mechanical and Barrier Properties of Bio-Based Composite Films Based on Chitosan and Whey Protein. Food Packag. Shelf Life 2014, 1, 56–67. [Google Scholar] [CrossRef]
  172. Galus, S.; Lenart, A.; Voilley, A.; Debeaufort, F. Effect of Oxidized Potato Starch on the Physicochemical Properties of Soy Protein Isolate-Based Edible Films. Food Technol. Biotechnol. 2013, 51, 403–409. [Google Scholar]
  173. Pérez-Gago, M.B.; Rhim, J.W. Edible Coating and Film Materials: Lipid Bilayers and Lipid Emulsions. In Innovations in Food Packaging, 2nd ed.; Elsevier: Amsterdam, The Netherlands, 2013. [Google Scholar]
  174. Gutiérrez, T.J.; Tapia, M.S.; Pérez, E.; Famá, L. Edible Films Based on Native and Phosphated 80:20 Waxy:Normal Corn Starch. Starch-Stärke 2015, 67, 90–97. [Google Scholar] [CrossRef]
  175. Kristo, E.; Biliaderis, C.G. Water Sorption and Thermo-Mechanical Properties of Water/Sorbitol-Plasticized Composite Biopolymer Films: Caseinate-Pullulan Bilayers and Blends. Food Hydrocoll. 2006, 20, 1057–1071. [Google Scholar] [CrossRef]
  176. Zikmanis, P.; Juhņeviča-Radenkova, K.; Radenkovs, V.; Segliņa, D.; Krasnova, I.; Kolesovs, S.; Orlovskis, Z.; Šilaks, A.; Semjonovs, P. Microbial Polymers in Edible Films and Coatings of Garden Berry and Grape: Current and Prospective Use. Food Bioprocess Technol. 2021, 14, 1432–1445. [Google Scholar] [CrossRef]
  177. Khwaldia, K.; Ferez, C.; Banon, S.; Desobry, S.; Hardy, J. Milk Proteins for Edible Films and Coatings. Crit. Rev. Food Sci. Nutr. 2004, 44, 239–251. [Google Scholar] [CrossRef]
  178. Khwaldia, K. Water Vapor Barrier And Mechanical Properties Of Paper-Sodium Caseinate And Paper-Sodium Caseinate-Paraffin Wax Films. J. Food Biochem. 2010, 34, 998–1013. [Google Scholar] [CrossRef]
  179. Gällstedt, M.; Brottmon, A.; Hedenqvist, M.S. Packaging-Related Properties of Protein- and Chitosan-Coated Paper. Packag. Technol. Sci. 2005, 18, 161–170. [Google Scholar] [CrossRef]
  180. Sadek, C.; Pauchard, L.; Schuck, P.; Fallourd, Y.; Pradeau, N.; Le Floch-Fouéré, C.; Jeantet, R. Mechanical Properties of Milk Protein Skin Layers after Drying: Understanding the Mechanisms of Particle Formation from Whey Protein Isolate and Native Phosphocaseinate. Food Hydrocoll. 2015, 48, 8–16. [Google Scholar] [CrossRef]
  181. Skurtys, O.; Acevedo, C.; Pedreschi, F.; Enronoe, J.; Osorio, F.; Aguilera, J.M. Food Hydrocolloid Edible Films and Coatings; Nova Science Publishers: Hauppauge, NY, USA, 2011. [Google Scholar]
  182. Krochta, J. Proteins as Raw Materials for Films and Coatings. In Protein-Based Films and Coatings; CRC Press: Boca Raton, FL, USA, 2002. [Google Scholar]
  183. Shahidi, F.; Hossain, A. Preservation of Aquatic Food Using Edible Films and Coatings Containing Essential Oils: A Review. Crit. Rev. Food Sci. Nutr. 2022, 62, 66–105. [Google Scholar] [CrossRef] [PubMed]
  184. Kouhi, M.; Prabhakaran, M.P.; Ramakrishna, S. Edible Polymers: An Insight into Its Application in Food, Biomedicine and Cosmetics. Trends Food Sci. Technol. 2020, 103, 248–263. [Google Scholar] [CrossRef]
  185. Redl, A.; Gontard, N.; Guilbert, S. Determination of Sorbic Acid Diffusivity in Edible Wheat Gluten and Lipid Based Films. J. Food Sci. 1996, 61, 116–120. [Google Scholar] [CrossRef]
  186. Kumari, M.; Mahajan, H.; Joshi, R.; Gupta, M. Development and Structural Characterization of Edible Films for Improving Fruit Quality. Food Packag. Shelf Life 2017, 12, 42–50. [Google Scholar] [CrossRef]
  187. Suhag, R.; Kumar, N.; Petkoska, A.T.; Upadhyay, A. Film Formation and Deposition Methods of Edible Coating on Food Products: A Review. Food Res. Int. 2020, 136, 109582. [Google Scholar] [CrossRef]
  188. Rhim, J.W.; Mohanty, A.K.; Singh, S.P.; Ng, P.K.W. Effect of the Processing Methods on the Performance of Polylactide Films: Thermocompression versus Solvent Casting. J. Appl. Polym. Sci. 2006, 101, 3736–3742. [Google Scholar] [CrossRef]
  189. Jensen, A.; Lim, L.T.; Barbut, S.; Marcone, M. Development and Characterization of Soy Protein Films Incorporated with Cellulose Fibers Using a Hot Surface Casting Technique. LWT-Food Sci. Technol. 2015, 60, 162–170. [Google Scholar] [CrossRef]
  190. Koide, Y.; Ikake, H.; Muroga, Y.; Shimizu, S. Effect of the Cast-Solvent on the Morphology of Cast Films Formed with a Mixture of Stereoisomeric Poly(Lactic Acids). Polym. J. 2013, 45, 645–650. [Google Scholar] [CrossRef]
  191. Sherrington, D.C. Introduction to Physical Polymer Science. React. Polym. 1993, 20, 217–218. [Google Scholar] [CrossRef]
  192. Cha, D.S.; Cooksey, K.; Chinnan, M.S.; Park, H.J. Release of Nisin from Various Heat-Pressed and Cast Films. LWT-Food Sci. Technol. 2003, 36, 209–213. [Google Scholar] [CrossRef]
  193. Karki, S.; Kim, H.; Na, S.J.; Shin, D.; Jo, K.; Lee, J. Thin Films as an Emerging Platform for Drug Delivery. Asian J. Pharm. Sci. 2016, 11, 559–574. [Google Scholar] [CrossRef] [Green Version]
  194. Cheng, Y.; Sun, C.; Zhai, X.; Zhang, R.; Zhang, S.; Sun, C.; Wang, W.; Hou, H. Effect of Lipids with Different Physical State on the Physicochemical Properties of Starch/Gelatin Edible Films Prepared by Extrusion Blowing. Int. J. Biol. Macromol. 2021, 185, 1005–1014. [Google Scholar] [CrossRef] [PubMed]
  195. Peressini, D.; Bravin, B.; Lapasin, R.; Rizzotti, C.; Sensidoni, A. Starch-Methylcellulose Based Edible Films: Rheological Properties of Film-Forming Dispersions. J. Food Eng. 2003, 59, 25–32. [Google Scholar] [CrossRef]
  196. Krishna, M.; Nindo, C.I.; Min, S.C. Development of Fish Gelatin Edible Films Using Extrusion and Compression Molding. J. Food Eng. 2012, 108, 337–344. [Google Scholar] [CrossRef]
  197. Liu, H.; Xie, F.; Yu, L.; Chen, L.; Li, L. Thermal Processing of Starch-Based Polymers. Prog. Polym. Sci. 2009, 34, 1348–1368. [Google Scholar] [CrossRef]
  198. Zhao, Y. Application of Commercial Coatings. In Edible Coatings and Films to Improve Food Quality, 2nd ed.; CRC Press: Boca Raton, FL, USA, 2011; pp. 291–332. [Google Scholar] [CrossRef]
  199. Senturk Parreidt, T.; Schmid, M.; Müller, K. Effect of Dipping and Vacuum Impregnation Coating Techniques with Alginate Based Coating on Physical Quality Parameters of Cantaloupe Melon. J. Food Sci. 2018, 83, 929–936. [Google Scholar] [CrossRef]
  200. Andrade, R.D.; Skurtys, O.; Osorio, F.A. Atomizing Spray Systems for Application of Edible Coatings. Compr. Rev. Food Sci. Food Saf. 2012, 11, 323–337. [Google Scholar] [CrossRef]
  201. Debeaufort, F.; Voilley, A. Lipid-Based Edible Films and Coatings. In Edible Films and Coatings for Food Applications; Springer: Berlin/Heidelberg, Germany, 2009; pp. 135–168. [Google Scholar] [CrossRef]
  202. Schneller, T.; Waser, R.; Kosec, M.; Payne, D. Chemical Solution Deposition of Functional Oxide Thin Films; Springer: Vienna, Austrua, 2013; pp. 1–796. [Google Scholar] [CrossRef]
  203. Mastromatteo, M.; Conte, A.; Del Nobile, M.A. Packaging Strategies to Prolong the Shelf Life of Fresh Carrots (Daucus carota L.). Innov. Food Sci. Emerg. Technol. 2012, 13, 215–220. [Google Scholar] [CrossRef]
  204. Hamzah, H.M.; Osman, A.; Tan, C.P.; Mohamad Ghazali, F. Carrageenan as an Alternative Coating for Papaya (Carica papaya L. Cv. Eksotika). Postharvest Biol. Technol. 2013, 75, 142–146. [Google Scholar] [CrossRef]
  205. Costa, M.J.; Cerqueira, M.A.; Ruiz, H.A.; Fougnies, C.; Richel, A.; Vicente, A.A.; Teixeira, J.A.; Aguedo, M. Use of Wheat Bran Arabinoxylans in Chitosan-Based Films: Effect on Physicochemical Properties. Ind. Crops Prod. 2015, 66, 305–311. [Google Scholar] [CrossRef]
  206. Rojas-Graü, M.A.; Soliva-Fortuny, R.; Martín-Belloso, O. Edible Coatings to Incorporate Active Ingredients to Fresh-Cut Fruits: A Review. Trends Food Sci. Technol. 2009, 20, 438–447. [Google Scholar] [CrossRef]
  207. Soares, N.M.; Fernandes, T.A.; Vicente, A.A. Effect of Variables on the Thickness of an Edible Coating Applied on Frozen Fish—Establishment of the Concept of Safe Dipping Time. J. Food Eng. 2016, 171, 111–118. [Google Scholar] [CrossRef]
  208. Kumar, N. Polysaccharide-Based Component and Their Relevance in Edible Film/Coating: A Review. Nutr. Food Sci. 2019, 49, 793–823. [Google Scholar] [CrossRef]
  209. Bravin, B.; Peressini, D.; Sensidoni, A. Development and Application of Polysaccharide-Lipid Edible Coating to Extend Shelf-Life of Dry Bakery Products. J. Food Eng. 2006, 76, 280–290. [Google Scholar] [CrossRef]
  210. Valdés, A.; Ramos, M.; Beltrán, A.; Jiménez, A.; Garrigós, M.C. State of the Art of Antimicrobial Edible Coatings for Food Packaging Applications. Coatings 2017, 7, 56. [Google Scholar] [CrossRef]
  211. Bergeron, V.; Bonn, D.; Martin, J.Y.; Vovelle, L. Controlling Droplet Deposition with Polymer Additives. Nature 2000, 405, 772–775. [Google Scholar] [CrossRef]
  212. Khan, M.K.I.; Nazir, A.; Maan, A.A. Electrospraying: A Novel Technique for Efficient Coating of Foods. Food Eng. Rev. 2017, 9, 112–119. [Google Scholar] [CrossRef]
  213. Bailey, A.G. The Science and Technology of Electrostatic Powder Spraying, Transport and Coating. J. Electrostat. 1998, 45, 85–120. [Google Scholar] [CrossRef]
  214. Amefia, A.E.; Abu-Ali, J.M.; Barringer, S.A. Improved Functionality of Food Additives with Electrostatic Coating. Innov. Food Sci. Emerg. Technol. 2006, 7, 176–181. [Google Scholar] [CrossRef]
  215. Meng, X.; Zhu, J.; Zhang, H. Influences of Different Powders on the Characteristics of Particle Charging and Deposition in Powder Coating Processes. J. Electrostat. 2009, 67, 663–671. [Google Scholar] [CrossRef]
  216. Luo, Y.; Zhu, J.; Ma, Y.; Zhang, H. Dry Coating, a Novel Coating Technology for Solid Pharmaceutical Dosage Forms. Int. J. Pharm. 2008, 358. [Google Scholar] [CrossRef] [PubMed]
  217. Pawar Avinash, S.; Bageshwar Deepak, V.; Khanvilkar Vineeta, V.; Kadam Vilasrao, J. Advances in Pharmaceutical Coatings. Int. J. ChemTech Res. 2010, 2, 16–22. [Google Scholar]
  218. Sumonsiri, N.; Barringer, S.A. Effect of Powder and Target Properties on Wrap around Effect during Coating. J. Food Sci. 2010, 75, E537–E543. [Google Scholar] [CrossRef]
  219. Mazumder, M.K.; Sims, R.A.; Biris, A.S.; Srirama, P.K.; Saini, D.; Yurteri, C.U.; Trigwell, S.; De, S.; Sharma, R. Twenty-First Century Research Needs in Electrostatic Processes Applied to Industry and Medicine. Chem. Eng. Sci. 2006, 61, 2192–2211. [Google Scholar] [CrossRef]
  220. Barringer, S.A.; Sumonsiri, N. Electrostatic Coating Technologies for Food Processing. Annu. Rev. Food Sci. Technol. 2015, 6, 157–169. [Google Scholar] [CrossRef] [PubMed]
  221. Abu-Ali, J.; Barringer, S.A. Optimization of Liquid Electrostatic Coating. J. Electrostat. 2008, 66, 184–189. [Google Scholar] [CrossRef]
  222. Watanabe, H.; Matsuyama, T.; Yamamoto, H. Experimental Study on Electrostatic Atomization of Highly Viscous Liquids. J. Electrostat. 2003, 57, 183–197. [Google Scholar] [CrossRef]
  223. Jaworek, A. Electrospray Droplet Sources for Thin Film Deposition. J. Mater. Sci. 2007, 42, 266–297. [Google Scholar] [CrossRef]
  224. Wilhelm, O.; Mädler, L.; Pratsinis, S.E. Electrospray Evaporation and Deposition. J. Aerosol Sci. 2003, 34, 815–836. [Google Scholar] [CrossRef]
  225. Xu, Y.; Hanna, M.A. Electrospray Encapsulation of Water-Soluble Protein with Polylactide. Effects of Formulations on Morphology, Encapsulation Efficiency and Release Profile of Particles. Int. J. Pharm. 2006, 320, 30–36. [Google Scholar] [CrossRef] [PubMed]
  226. Bock, N.; Dargaville, T.R.; Woodruff, M.A. Controlling Microencapsulation and Release of Micronized Proteins Using Poly(Ethylene Glycol) and Electrospraying. Eur. J. Pharm. Biopharm. 2014, 87, 366–377. [Google Scholar] [CrossRef] [PubMed]
  227. Pérez-Masiá, R.; López-Nicolás, R.; Periago, M.J.; Ros, G.; Lagaron, J.M.; López-Rubio, A. Encapsulation of Folic Acid in Food Hydrocolloids through Nanospray Drying and Electrospraying for Nutraceutical Applications. Food Chem. 2015, 168, 124–133. [Google Scholar] [CrossRef]
  228. Sousa, A.M.M.; Souza, H.K.S.; Uknalis, J.; Liu, S.C.; Gonçalves, M.P.; Liu, L. Electrospinning of Agar/PVA Aqueous Solutions and Its Relation with Rheological Properties. Carbohydr. Polym. 2015, 115, 348–355. [Google Scholar] [CrossRef] [PubMed]
  229. Gomez-Mascaraque, L.G.; Morfin, R.C.; Pérez-Masiá, R.; Sanchez, G.; Lopez-Rubio, A. Optimization of Electrospraying Conditions for the Microencapsulation of Probiotics and Evaluation of Their Resistance during Storage and In-Vitro Digestion. LWT-Food Sci. Technol. 2016, 69, 438–446. [Google Scholar] [CrossRef]
  230. Laelorspoen, N.; Wongsasulak, S.; Yoovidhya, T.; Devahastin, S. Microencapsulation of Lactobacillus Acidophilus in Zein-Alginate Core-Shell Microcapsules via Electrospraying. J. Funct. Foods 2014, 7, 342–349. [Google Scholar] [CrossRef]
  231. Pandey, P.; Turton, R.; Joshi, N.; Hammerman, E.; Ergun, J. Scale-up of Apan-Coating Process. AAPS PharmSciTech 2006, 7, E102–E132. [Google Scholar] [CrossRef]
  232. Dangaran, K.; Tomasula, P.M.; Qi, P. Structure and Function of Protein-Based Edible Films and Coatings. In Edible Films and Coatings for Food Applications; Springer: Berlin/Heidelberg, Germany, 2009. [Google Scholar]
  233. Jacquot, M.; Pernetti, M. Spray Coating and Drying Processes. In Fundamentals of Cell Immobilization Biotechnology; Wolters Kluwer: Alphen aan den Rijn, The Netherlands, 2004. [Google Scholar]
  234. Guignon, B.; Duquenoy, A.; Dumoulin, E.D. Fluid Bed Encapsulation of Particles: Principles and Practice. Dry. Technol. 2002, 20, 419–447. [Google Scholar] [CrossRef]
  235. Chen, Y.; Yang, J.; Mujumdar, A.; Dave, R. Fluidized Bed Film Coating of Cohesive Geldart Group C Powders. Powder Technol. 2009, 189, 466–480. [Google Scholar] [CrossRef]
  236. Solís-Morales, D.; Sáenz-Hernández, C.M.; Ortega-Rivas, E. Attrition Reduction and Quality Improvement of Coated Puffed Wheat by Fluidised Bed Technology. J. Food Eng. 2009, 93, 236–241. [Google Scholar] [CrossRef]
  237. Bertuzzi, M.A.; Slavutsky, A.M. Standard and New Processing Techniques Used in the Preparation of Films and Coatings at the Lab Level and Scale-Up. In Edible Films and Coatings: Fundamentals and Applications; CRC Press: Boca Raton, FL, USA, 2016. [Google Scholar]
  238. Cerqueira, M.A.P.R.; Pereira, R.N.C.; da Silva Ramos, O.L.; Teixeira, J.A.C.; Vicente, A.A. (Eds.) Edible Food Packaging: Materials and Processing Technologies; CRC Press: Boca Raton, FL, USA, 2017. [Google Scholar]
  239. Karimnezhad, F.; Razavilar, V.; Anvar, A.A.; Eskandari, S. Study the Antimicrobial Effects of Chitosan-Based Edible Film Containing the Trachyspermum Ammi Essential Oil on Shelf-Life of Chicken Meat. Microbiol. Res. 2017, 8, 7226. [Google Scholar] [CrossRef]
  240. Martiny, T.R.; Pacheco, B.S.; Pereira, C.M.P.; Mansilla, A.; Astorga–España, M.S.; Dotto, G.L.; Moraes, C.C.; Rosa, G.S. A Novel Biodegradable Film Based on κ-Carrageenan Activated with Olive Leaves Extract. Food Sci. Nutr. 2020, 8, 3147–3156. [Google Scholar] [CrossRef]
  241. Li, K.; Jin, S.; Li, J.; Chen, H. Improvement in Antibacterial and Functional Properties of Mussel-Inspired Cellulose Nanofibrils/Gelatin Nanocomposites Incorporated with Graphene Oxide for Active Packaging. Ind. Crops Prod. 2019, 132, 197–212. [Google Scholar] [CrossRef]
  242. Calderón-Castro, A.; Vega-García, M.O.; de Jesús Zazueta-Morales, J.; Fitch-Vargas, P.R.; Carrillo-López, A.; Gutiérrez-Dorado, R.; Limón-Valenzuela, V.; Aguilar-Palazuelos, E. Effect of Extrusion Process on the Functional Properties of High Amylose Corn Starch Edible Films and Its Application in Mango (Mangifera indica L.) Cv. Tommy Atkins. J. Food Sci. Technol. 2018, 55, 905–914. [Google Scholar] [CrossRef] [PubMed]
  243. Seydim, A.C.; Sarikus-Tutal, G.; Sogut, E. Effect of Whey Protein Edible Films Containing Plant Essential Oils on Microbial Inactivation of Sliced Kasar Cheese. Food Packag. Shelf Life 2020, 26, 100567. [Google Scholar] [CrossRef]
  244. Xia, C.; Wang, W.; Wang, L.; Liu, H.; Xiao, J. Multilayer Zein/Gelatin Films with Tunable Water Barrier Property and Prolonged Antioxidant Activity. Food Packag. Shelf Life 2019, 19, 76–85. [Google Scholar] [CrossRef]
  245. Shapi’i, R.A.; Othman, S.H.; Nordin, N.; Kadir Basha, R.; Nazli Naim, M. Antimicrobial Properties of Starch Films Incorporated with Chitosan Nanoparticles: In Vitro and in Vivo Evaluation. Carbohydr. Polym. 2020, 230, 115602. [Google Scholar] [CrossRef]
  246. Belyamani, I.; Prochazka, F.; Assezat, G. Production and Characterization of Sodium Caseinate Edible Films Made by Blown-Film Extrusion. J. Food Eng. 2014, 121, 39–47. [Google Scholar] [CrossRef]
  247. Issa, A.; Ibrahim, S.A.; Tahergorabi, R. Impact of Sweet Potato Starch-Based Nanocomposite Films Activated with Thyme Essential Oil on the Shelf-Life of Baby Spinach Leaves. Foods 2017, 6, 43. [Google Scholar] [CrossRef]
  248. Kontominas, M.G. Use of Alginates as Food Packaging Materials. Foods 2020, 9, 1440. [Google Scholar] [CrossRef]
  249. Ramos, Ó.L.; Pereira, J.O.; Silva, S.I.; Fernandes, J.C.; Franco, M.I.; Lopes-da-Silva, J.A.; Pintado, M.E.; Malcata, F.X. Evaluation of Antimicrobial Edible Coatings from a Whey Protein Isolate Base to Improve the Shelf Life of Cheese. J. Dairy Sci. 2012, 95, 6282–6292. [Google Scholar] [CrossRef]
  250. Mali, S.; Grossmann, M.V.E. Effects of Yam Starch Films on Storability and Quality of Fresh Strawberries (Fragaria Ananassa). J. Agric. Food Chem. 2003, 51, 7005–7011. [Google Scholar] [CrossRef] [PubMed]
  251. Mushtaq, M.; Gani, A.; Gani, A.; Punoo, H.A.; Masoodi, F.A. Use of Pomegranate Peel Extract Incorporated Zein Film with Improved Properties for Prolonged Shelf Life of Fresh Himalayan Cheese (Kalari/Kradi). Innov. Food Sci. Emerg. Technol. 2018, 48, 25–32. [Google Scholar] [CrossRef]
  252. Sogut, E.; Seydim, A.C. The Effects of Chitosan and Grape Seed Extract-Based Edible Films on the Quality of Vacuum Packaged Chicken Breast Fillets. Food Packag. Shelf Life 2018, 18, 13–20. [Google Scholar] [CrossRef]
  253. Sorde, K.L.; Ananthanarayan, L. Effect of Transglutaminase Treatment on Properties of Coconut Protein-Guar Gum Composite Film. LWT 2019, 115, 108422. [Google Scholar] [CrossRef]
  254. Özdemir, K.S.; Gökmen, V. Effect of Chitosan-Ascorbic Acid Coatings on the Refrigerated Storage Stability of Fresh-Cut Apples. Coatings 2019, 9, 503. [Google Scholar] [CrossRef]
  255. Hashemi, S.M.B.; Zahabi, N.; Rezaee, Z.; Maherani, Z.; Boghori, P.; Keshavarz, Z. Evaluation of a Starch-Based Edible Film as Carrier of Adiantum Capillus-Veneris Extract to Improve the Shelf Life of Fresh-Cut Pears. J. Food Saf. 2016, 36, 291–298. [Google Scholar] [CrossRef]
  256. Vignesh, R.M.; Nair, B.R. Improvement of Shelf Life Quality of Tomatoes Using a Novel Edible Coating Formulation. Plant Sci. Today 2019, 6, 84–90. [Google Scholar] [CrossRef]
  257. Chen, C.; Peng, X.; Zeng, R.; Wan, C.; Chen, M.; Chen, J. Physiological and Biochemical Responses in Cold-Stored Citrus Fruits to Carboxymethyl Cellulose Coating Containing Ethanol Extract of Impatiens balsamina L. Stems. J. Food Process. Preserv. 2017, 41, e12999. [Google Scholar] [CrossRef]
  258. Falcó, I.; Flores-Meraz, P.L.; Randazzo, W.; Sánchez, G.; López-Rubio, A.; Fabra, M.J. Antiviral Activity of Alginate-Oleic Acid Based Coatings Incorporating Green Tea Extract on Strawberries and Raspberries. Food Hydrocoll. 2019, 87, 611–618. [Google Scholar] [CrossRef] [Green Version]
  259. García, M.A.; Ventosa, M.; Díaz, R.; Falco, S.; Casariego, A. Effects of Aloe Vera Coating on Postharvest Quality of Tomato. Fruits 2014, 69, 117–126. [Google Scholar] [CrossRef]
  260. Sessa, M.; Ferrari, G.; Donsì, F. Novel Edible Coating Containing Essential Oil Nanoemulsions to Prolong the Shelf Life of Vegetable Products. Chem. Eng. Trans. 2015, 43, 55–60. [Google Scholar] [CrossRef]
  261. Martiñon, M.E.; Moreira, R.G.; Castell-Perez, M.E.; Gomes, C. Development of a Multilayered Antimicrobial Edible Coating for Shelf-Life Extension of Fresh-Cut Cantaloupe (Cucumis melo L.) Stored at 4 °C. LWT-Food Sci. Technol. 2014, 56, 341–350. [Google Scholar] [CrossRef]
  262. Martínez, O.; Salmerón, J.; Epelde, L.; Vicente, M.S.; de Vega, C. Quality Enhancement of Smoked Sea Bass (Dicentrarchus labrax) Fillets by Adding Resveratrol and Coating with Chitosan and Alginate Edible Films. Food Control 2018, 85, 168–176. [Google Scholar] [CrossRef]
  263. Lagos, M.J.B.; Sobral, P.J.D.A. Application of Active Films with Natural Extract for Beef Hamburger Preservation. Cienc. Rural 2019, 49, e20180797. [Google Scholar] [CrossRef]
  264. Shin, S.H.; Chang, Y.; Lacroix, M.; Han, J. Control of Microbial Growth and Lipid Oxidation on Beef Product Using an Apple Peel-Based Edible Coating Treatment. LWT-Food Sci. Technol. 2017, 84, 183–188. [Google Scholar] [CrossRef]
  265. Kowalczyk, D.; Skrzypek, T.; Łupina, K. Effect of Carboxymethyl Cellulose/Candelilla Wax Edible Coating Incorporated with Ascorbic Acid on the Physicochemical and Sensory Qualities of Prepackaged Minimally Processed Carrots (Daucus carota L.) during Cold Storage. J. Food Process. Preserv. 2020, 44, e14713. [Google Scholar] [CrossRef]
  266. López De Lacey, A.M.; López-Caballero, M.E.; Gómez-Estaca, J.; Gómez-Guillén, M.C.; Montero, P. Functionality of Lactobacillus acidophilus and Bifidobacterium bifidum incorporated to edible coatings and films. Innov. Food Sci. Emerg. Technol. 2012, 16, 277–282. [Google Scholar] [CrossRef]
  267. Zhao, Y.; Teixeira, J.S.; Gänzle, M.M.; Saldaña, M.D.A. Development of antimicrobial films based on cassava starch, chitosan and gallic acid using subcritical water technology. J. Supercrit. Fluids 2018, 137, 101–110. [Google Scholar] [CrossRef]
  268. Olaimat, A.N.; Fang, Y.; Holley, R.A. Inhibition of Campylobacter jejuni on fresh chicken breasts by κ-carrageenan/chitosan-based coatings containing allyl isothiocyanate or deodorized oriental mustard extract. Int. J. Food Microbiol. 2014, 187, 77–82. [Google Scholar] [CrossRef]
  269. Sanchez-Gonzalez, L.; Pastor, C.; Vargas, M.; Chiralt, A.; Gonzalez-Martinez, C.; Chafer, M. Effect of hydroxypropylmethylcellulose and chitosan coatings with and without bergamot essential oil on quality and safety of cold-stored grapes. Postharvest Biol. Technol. 2011, 60, 57–63. [Google Scholar] [CrossRef]
  270. Calva-Estrada, S.J.; Jiménez-Fernández, M.; Lugo-Cervantes, E. Protein-Based Films: Advances in the Development of Biomaterials Applicable to Food Packaging. Food Eng. Rev. 2019, 11, 78–92. [Google Scholar] [CrossRef]
  271. Ganiari, S.; Choulitoudi, E.; Oreopoulou, V. Edible and Active Films and Coatings as Carriers of Natural Antioxidants for Lipid Food. Trends Food Sci. Technol. 2017, 68, 70–82. [Google Scholar] [CrossRef]
  272. Sharma, R.; Ghoshal, G. Emerging Trends in Food Packaging. Nutr. Food Sci. 2018, 48, 764–779. [Google Scholar] [CrossRef]
  273. Parreidt, T.S.; Lindner, M.; Rothkopf, I.; Schmid, M.; Müller, K. The Development of a Uniform Alginate-Based Coating for Cantaloupe and Strawberries and the Characterization of Water Barrier Properties. Foods 2019, 8, 203. [Google Scholar] [CrossRef]
  274. Gaikwad, K.K.; Singh, S.; Negi, Y.S.; Lee, Y.S. The Effect of Trans-Polyisoprene/LDPE Based Active Films on Oxidative Stability in Roasted Peanuts. J. Food Meas. Charact. 2020, 14, 1857–1864. [Google Scholar] [CrossRef]
  275. Ustunol, Z. Edible Films and Coatings for Meat and Poultry. In Edible Films and Coatings for Food Applications; Springer: Berlin/Heidelberg, Germany, 2009. [Google Scholar]
  276. Puscaselu, R.; Gutt, G.; Amariei, S. The Use of Edible Films Based on Sodium Alginate in Meat Product Packaging: An Eco-Friendly Alternative to Conventional Plastic Materials. Coatings 2020, 10, 166. [Google Scholar]
  277. Andevari, G.T.; Rezaei, M. Effect of Gelatin Coating Incorporated with Cinnamon Oil on the Quality of Fresh Rainbow Trout in Cold Storage. Int. J. Food Sci. Technol. 2011, 46, 2305–2311. [Google Scholar] [CrossRef]
  278. Arshad, R.; Sameen, A.; Huma, N.; Zia, M.A. Exploring the Potential of Active Edible Coating on the Shelf Stability of Dairy Products. Pak. J. Agric. Sci. 2020, 57, 237–244. [Google Scholar] [CrossRef]
  279. Hashemi, S.M.B.; Raeisi, S. Evaluation of Antifungal and Antioxidant Properties of Edible Coating Based on Apricot (Prunus armeniaca) Gum Containing Satureja Intermedia Extract in Fresh Wild Almond (Amygdalus scoparia) Kernels. J. Food Meas. Charact. 2018, 12, 362–369. [Google Scholar] [CrossRef]
  280. Mendy, T.K.; Misran, A.; Mahmud, T.M.M.; Ismail, S.I. Application of Aloe Vera Coating Delays Ripening and Extend the Shelf Life of Papaya Fruit. Sci. Hortic. 2019, 246, 769–776. [Google Scholar] [CrossRef]
  281. Available online: https://www.gminsights.com/industry-analysis/biopolymer-films-market (accessed on 1 August 2022).
  282. Xiong, S.J.; Pang, B.; Zhou, S.J.; Li, M.K.; Yang, S.; Wang, Y.Y.; Shi, Q.; Wang, S.F.; Yuan, T.Q.; Sun, R.C. Economically competitive biodegradable PBAT/lignin composites: Effect of lignin methylation and compatibilizer. ACS Sustain. Chem. Eng. 2020, 8, 5338–5346. [Google Scholar] [CrossRef]
Figure 1. Different sources of biomaterials.
Figure 1. Different sources of biomaterials.
Materials 15 05899 g001
Figure 2. Grain and legume flours used to produce films and coatings [13].
Figure 2. Grain and legume flours used to produce films and coatings [13].
Materials 15 05899 g002
Figure 3. Step-by-step showing fabrication of edible films by solvent casting method.
Figure 3. Step-by-step showing fabrication of edible films by solvent casting method.
Materials 15 05899 g003
Figure 4. Extrusion technique used for the formation of films.
Figure 4. Extrusion technique used for the formation of films.
Materials 15 05899 g004
Figure 5. (a) Air spray atomization, (b) Air-assisted airless atomization [187]. (Reprinted with permission).
Figure 5. (a) Air spray atomization, (b) Air-assisted airless atomization [187]. (Reprinted with permission).
Materials 15 05899 g005
Figure 6. Panning method of edible coating.
Figure 6. Panning method of edible coating.
Materials 15 05899 g006
Figure 7. Mechanism of active packaging on a tangerine.
Figure 7. Mechanism of active packaging on a tangerine.
Materials 15 05899 g007
Figure 8. Application of edible coatings on perishable foods and its benefits.
Figure 8. Application of edible coatings on perishable foods and its benefits.
Materials 15 05899 g008
Table 1. Food packaging application from thermoplastics [9].
Table 1. Food packaging application from thermoplastics [9].
Thermoplastic MaterialAbbreviationPackaging ApplicationPros and Cons
Polyethylene terephthalatePETWater/juice/soft drink bottles, food jars, microwavable containers, plastic filmsGood mechanical strength and barrier properties, but low heat resistance and susceptible to oxidation
PolypropylenePPDrinking bottles for milk, food containersGood chemical and moisture barrier, difficult to recycle
Polyvinyl chloridePVCPlastic bags, frozen foods, stretch films, container lidsFlexible, cost effective, difficult to recycle, but low heat resistance as adipates in PVC leach into food
PolystyrenePSTake-away clamshells, meat trays, bottle caps, strawsEasily recyclable, hard and brittle, but poor chemical resistance, can leach out into food when food is stored
Low-density polyethyleneLDPDisposable cups, plates, and spoons; bread bagsGood chemical resistance, relatively permeable to oxygen but poor odor barrier
High-density polyethyleneHDPCustom packaging, grocery bags, water/milk/juice containers, cereal and snack linersGood moisture barrier, but poor gas barrier and low heat resistance
Table 3. Outline comparing dry and wet methods of film formation [187].
Table 3. Outline comparing dry and wet methods of film formation [187].
Sl. No.Type of MethodFilm FormationAdvantageDisadvantageApplication
1.Solvent casting method (Wet)Biomaterial is dissolved in suitable solvent (e.g., ethanol, hexane) then cast into a mold followed by drying.Low cost, ease of operation, fewer defects in film (homogeneous packaging), good optical purity, transparency, excellent flatness, and isotropic orientation.Limitation of shapes, entrapment of toxic solvent in polymer, long drying period.Apples, strawberries, quail eggs, cheese slices, etc.
2.Extrusion method (Dry)Biomaterial is mixed with solvent and then feed with the help of compressed air; it is then kneaded and heated in the machine, followed by the formation of the finished film.Short duration of heating, low energy consumption, good mechanical, and optical properties, cheap and highly efficient, no use of solvent.Can process materials that can tolerate high temperatures; high investment, and maintenance cost.Mangos, soyabean oil, sausage
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Gupta, V.; Biswas, D.; Roy, S. A Comprehensive Review of Biodegradable Polymer-Based Films and Coatings and Their Food Packaging Applications. Materials 2022, 15, 5899. https://doi.org/10.3390/ma15175899

AMA Style

Gupta V, Biswas D, Roy S. A Comprehensive Review of Biodegradable Polymer-Based Films and Coatings and Their Food Packaging Applications. Materials. 2022; 15(17):5899. https://doi.org/10.3390/ma15175899

Chicago/Turabian Style

Gupta, Vatsla, Deblina Biswas, and Swarup Roy. 2022. "A Comprehensive Review of Biodegradable Polymer-Based Films and Coatings and Their Food Packaging Applications" Materials 15, no. 17: 5899. https://doi.org/10.3390/ma15175899

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop