Correlation between Microstructure and Chemical Composition of Zinc Oxide Gas Sensor Layers and Their Gas-Sensitive Properties in Chlorine Atmosphere
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Communication

Highly Fast Response of Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky Diode-Based Hydrogen Sensors

1
Department of Nanotechnology and Advanced Materials Engineering and HMC, Sejong University, Seoul 05006, Korea
2
National Nanofab Center, Korea Advanced Institute of Science and Technology, 291 Daehak-ro, Yuseong-gu, Daejeon 34141, Korea
3
NINT (National Institute for Nanomaterials Technology), Pohang University of Science and Technology, Pohang 37673, Korea
4
Department of Electronic Engineering, Semyung University, Chungcheongbuk-do 27136, Korea
*
Author to whom correspondence should be addressed.
These authors contribute equally to this work.
Sensors 2021, 21(4), 1042; https://doi.org/10.3390/s21041042
Submission received: 28 December 2020 / Revised: 25 January 2021 / Accepted: 31 January 2021 / Published: 3 February 2021
(This article belongs to the Collection Gas Sensors)

Abstract

:
Herein, the fabrication of a novel highly sensitive and fast hydrogen (H2) gas sensor, based on the Ta2O5 Schottky diode, is described. First, Ta2O5 thin films are deposited on silicon carbide (SiC) and silicon (Si) substrates via a radio frequency (RF) sputtering method. Then, Pd and Ni are respectively deposited on the front and back of the device. The deposited Pd serves as a H2 catalyst, while the Ni functions as an Ohmic contact. The devices are then tested under various concentrations of H2 gas at operating temperatures of 300, 500, and 700 °C. The results indicate that the Pd/Ta2O5 Schottky diode on the SiC substrate exhibits larger concentration and temperature sensitivities than those of the device based on the Si substrate. In addition, the optimum operating temperature of the Pd/Ta2O5 Schottky diode for use in H2 sensing is shown to be about 300 °C. At this optimum temperature, the dynamic responses of the sensors towards various concentrations of H2 gas are then examined under a constant bias current of 1 mA. The results indicate a fast rise time of 7.1 s, and a decay of 18 s, for the sensor based on the SiC substrate.

1. Introduction

Hydrogen (H2) gas detection is widely used in various fields such as environmental monitoring, domestic/industrial safety control, seismic surveillance, semiconductor technology, and chemical/industrial process control (e.g., in nuclear reactors and coal mines). However, the colorless, odorless, and toxic nature of hydrogen gas renders it undetectable by the human eyes or nose, while its readily diffusive, highly flammable, corrosive, and explosive nature can result in disastrous consequences in the event of a leakage. Therefore, the development of a simple and efficient H2 sensor with high sensitivity, selectivity, and reliability, along with a rapid response and wide working temperature range, remains a significant challenge.
Numerous approaches have been adopted to design and develop hydrogen-based sensors with various structures and mechanisms, including hollow architectures such as spheres [1,2], nanowires/nanofibers [3,4], nanorods [5], hemispheres [6], and inorganic tubes [7]. For improved sensing performance, various synthetic methods have been used to control the morphology and structure so as to provide a high surface-to-volume ratio, easy electron/ion diffusion, large penetration depth, and fast response/recovery times [8]. Various semiconducting metal oxides have been used in the fabrication of resistive H2 sensor applications, including n-type (TiO2, WO3, ZrO2, CeO2, In2O3, Nb2O5, ZnO and SnO2) [9,10,11,12,13,14,15], p-type (CuO, CoO, Co3O4 and NiO) [16,17,18,19], or multilayered metal oxides decorated with noble metal catalysts such as gold (Au), platinum (Pt), ruthenium (Ru), or palladium (Pd) based compounds such as Pd/WO3, Pd/V2O5, Pd/SnO2, and Pd/ZnO. Although these precious metal catalysts exhibit superior room-temperature hydrogen solubility, many metal oxides or semiconductors are not commercially viable due to excessive power consumption, instability, poor selectivity, sensitivity, and accuracy at high operating temperatures. Moreover, a significant drawback in the use of Pd metal as a highly-sensitive hydrogen detector is the strong tendency for its electrical resistance to exhibit hysteresis due to the facile adsorption of hydrogen into the Pd structure [20,21]. In view of these challenges, recent research is focusing on the replacement of metal oxide-based materials to achieve high sensitivity and selectivity along with a higher response under a range of working H2 concentrations, as well as improved cost effectiveness and reproducibility.
Recently, two-dimensional (2D) materials have attracted much interest due to their unique structural and extraordinary sensing properties [22,23]. In addition, previous studies have reported that doping and creating defects are two effective methods for enhancing the sensing or catalytic performance of 2D materials [24,25]. For example, much progress has been made in the development of sensors for NH3, SO2, NO2, and CO2 gases based on layered transition metal dichalcogenides (LTMDs) such as GeSe [26], graphene and reduced graphene oxide (RGO) [27,28], phosphorene [29], MoS2 [30], WS2 [31,32], and vanadium carbide MXene (V2CTx) [33]. However, while the research into 2D materials for H2-based sensors has produced significant success, the study is still in its infancy and few reports have been published. Moreover, the attainment of a satisfactory performance remains hampered by the complicated fabrication process, insufficient hydrogen sensitivity/detection, lower response time, and shorter desorption time.
In addition, while bare Si cannot meet the requirements for application in severe environments, the three-times wider bandgap of the group-III nitride silicon carbide (SiC) (3.26 eV) enables operation at temperatures of up to 1000 °C along with an excellent thermal conductivity of 3.0–4.9 W/cm K. Moreover, the high stability of the carbon/silicon bonding, the low diffusion coefficient, and the critical electric field over eight times that of silicon, enable the production of SiC-based electronic devices with low power loss, thus potentially increasing the battery life [34]. Furthermore, the ease of fabrication of the SiC-based gas sensors on a smaller chip, to provide a lighter-weight device that can operate at high or low temperature, has aroused growing research interest. Therefore, the development of a SiC-based hydrogen sensor is an attractive challenge.
In view of the above-mentioned challenges and recent achievements, SiC has been selected for investigation as a H2 based sensor in the present work. Herein, Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky diode type hydrogen sensors are fabricated by radio frequency (RF) sputtering and thermal annealing, and their dynamic response times are observed under various H2 gas concentrations and at various temperatures (300, 500, and 700 °C). The results indicate an optimum operating temperature of 300 °C and, under this optimum condition, the Ta2O5/SiC-based sensor performs exceptionally well, showing excellent sensitivity along with fast rise and fall times of 7 s and 18 s, respectively. These results are significantly better than those previously reported for H2 sensors [35,36] and suggest that the Pd/Ta2O5/SiC-based Schottky diode is a promising candidate for H2 sensing applications. To the best of the present authors’ knowledge, few reports on a Pd/Ta2O5/SiC-based Schottky diode aimed specifically at H2 gas sensing have been published [37,38,39].

2. Experimental

2.1. Material Synthesis and Device Fabrication

Impurities were ultrasonically removed from the polished and unpolished sides of the substrates by immersing them sequentially in acetone, methanol, isopropyl alcohol, and deionized (DI) water for 5 min each. Thin layers of Ta2O5 were deposited on the silicon (Si) and silicon carbide (SiC) substrates via radio frequency (RF) sputtering. The natural oxide layer on the unpolished surface of the substrates was removed by buffered oxide etching (BOE) for 10 s, then the samples were rinsed with DI water and dried with N2. Nickel (Ni; 100 nm) was deposited as a bottom electrode by sputtering for 30 min at a power of 150 W, followed by rapid thermal processing (RTP) at 950 °C to make an ohmic contact. Next, palladium (Pd) was deposited on the Ta2O5 thin film using a shadow mask, as shown in Figure 1. In this step, a Pd metal electrode was used as a catalyst for the chemisorption of hydrogen onto the surface because Pd is known to have a very high solubility for hydrogen.

2.2. Material Characterization

The crystallinity of the thin films was examined by X-ray diffraction (XRD; Ultima IV, Rigaku Corp., Akishima, Tokyo, Japan) at room temperature under Cu-Kα radiation (0.154 nm) at a potential of 40 kV, a current of 40 mA, and a scan rate of 5°/min in the range of 2θ = 10–80°. In addition, X-ray photoelectron spectroscopy (XPS; PHI 5000 Versa Probe, Ulvac-PHI, Kanagawa,Japan) under Al Kα at 25 W and 6.7 × 10−8 Pa was used to confirm the chemical composition and binding energy of the Ta2O5 film. The morphology of the films was examined via atomic force microscopy (AFM; Vecco Dimension 3100, Veeco Probes Co., Santa Barbara, USA), and the thicknesses and elemental profile of the fabricated device were determined by HRTEM and EDS.

2.3. Electrical Characterization

The electrical characterization was performed under an atmosphere of hydrogen and argon using a Keithley Instruments Model 4200A-SCS (Tektronix Co., Oregon,USA) current-voltage (I-V) meter parameter analyzer while varying the temperature from 300 to 700 °C. Hydrogen gas was injected along with the carrier gas (Ar) via a mass flow controller (MFC) at various hydrogen concentrations of up to 5000 ppm. As the H2 concentration increases from 0 to 5000 ppm, the H2 molecules become dissociated into hydrogen atoms at the surface of the Pd catalyst and are subsequently adsorbed onto the Ta2O5 surface. This lowers the Schottky barrier height (SBH) and increases the forward current under the elevated temperatures of 300, 500, and 700 °C. The sensitivity of a sensor is defined as the ratio of the sensor resistance under the argon environment (Ra) to the resistance in pure H2 gas (Rg).

3. Results and Discussion

3.1. Structural Properties

The Schottky diode hydrogen (H2) sensor, consisting of the Ta2O5 dielectric layer deposited on the SiC substrate, a Pd electrode/catalyst, and an Ni back electrode for ohmic contact, is shown schematically in Figure 2a. In addition, the setup for the electrical measurements is shown schematically in Figure 2b.
The sharp interface between the Ta2O5 (198.5 nm) and SiC is revealed by the TEM image in Figure 3a. The cross-sectional HRTEM image that was used for the EDS elemental mappings of the device is presented in Figure 3b, and the mappings are presented in Figure 3c–g. The corresponding EDS spectrum is provided in Figure S1a of the Supporting Information. The presence of the elements Si, C, O, and Ta provides clear evidence of the Ta2O5 film on the SiC substrate.
The XRD analysis in Figure S1b clearly reveals the (001), (110), (111), (002), (020), and (200) lattice planes of the Ta2O5 orthorhombic crystalline phase, thus confirming its formation due to the annealing process at 700 °C under an Ar atmosphere. By contrast, the XRD spectra of the films that were deposited at room temperature (RT), 300 and 500 °C exhibit broad humps with no sharp peaks, thus indicating the amorphous structures of these films.
The AFM images of the Ta2O5 layers on the SiC and Si substrates are presented in Figure S2a,b, respectively. Here, the surface of the Ta2O5 film that was grown on the SiC substrate is seen to be rougher than that grown on the Si substrate. In detail, the average roughness of the Ta2O5 layer on the SiC and Si substrates is 0.645 and 0.484 nm, respectively.
The Ta 4f XPS spectra of the Ta2O5 thin film deposited on the SiC and Si substrates are presented in Figure S1c, and the corresponding O (1s) spectra are presented in Figure S1d. For both samples, the two peaks located at the binding energies of 26.42 and 28.31 eV in the Ta (4f) spectra are respectively assigned to the Ta (4f7/2) and Ta (4f5/2) core levels of the Ta5+ cations, while the sharp peak located at 531.62 eV in the O (1 s) spectra is associated with the TaO chemical bond [40].

3.2. H2 Sensor Performances

As the operating temperature is a crucial parameter for gas sensing devices, the electrical and H2 gas sensing performances of the Pd/Ta2O5 Schottky diodes on the SiC and Si substrates were examined under the range of conditions described in Section 2.3. The results in Figure S3 indicate significant response values for both devices at a temperature of 300 °C, whereas poor responses are obtained at lower temperatures due to the slower chemical reaction between the adsorbed H2 molecules and the film surface. Moreover, at operating temperatures much higher than 300 °C, the absorbed gas molecules can escape before reaction can occur, so that a poor response is again observed illustrated in Figure S4. These results indicate that the optimum operating temperature for application of the Pd/Ta2O5 Schottky diode to H2 sensing is ~300 °C.
The rectifying diode characteristics of the Si- and SiC-Pd/Ta2O5 Schottky diodes in the presence and absence of H2 gas at 300 °C are presented in Figure 4. The typical linear I-V curves of the SiC- and Si-based devices are presented in Figure 4a,b, respectively, and the corresponding logarithmic plots are presented in Figure 4c,d. Thus, at a fixed voltage, a significant increase in the forward current is observed as the concentration of H2 gas is increased from 0 to 5000 ppm. This is explained by the lowering of the SBH due to the dissociation of the H2 molecules into individual hydrogen atoms at the surface of the Pd catalyst, and their subsequent adsorption onto the Ta2O5 surface. However, the results in Figure 4 also indicate that the sensor that was fabricated on the SiC substrate displays a much higher response than that of the device on the Si substrate.
In addition, the sensitivities of the SiC- and Si-based sensors towards various concentrations of H2 gas at the optimum operating temperature of 300 °C are presented in Figure 4e,f, respectively. From this analysis, the resistances of each device at various H2 concentrations were extracted and the ratio of the sensor resistance under the argon environment (Ra) to the resistance in pure H2 gas (Rg) was considered as the sensitivity of the sensor. The results indicated that the SiC-based Pd/Ta2O5 Schottky diode is much more sensitive than the Si-based device towards H2 gas at high operating temperature.
These results can be explained by the large bandgap of the SiC sensor (4.4 eV) [39], which is responsible for minimizing the probability of electron-hole recombination at the Schottky diode junction and, thus, enabling the sensor to function with great stability under harsh temperature conditions. In addition, the higher roughness of the Ta2O5 thin film on the SiC substrate (as revealed by the AFM image) may further assist the adsorption of H2 atoms at the Ta2O5 surface.
Finally, the dynamic responses of the sensors towards various concentrations of hydrogen gas under a constant bias current at 300 °C are indicated in Figure 5. Here, the SiC sensor exhibits a rapid rise in dynamic response from 10% to 90% in 7.1 s, and a decay from 90% to 10% in 18 s. These results clearly indicate that the SiC sensor has a higher sensitivity towards H2 than does the Si-based sensor. Moreover, the results indicate that the response and recovery times of the sensor are highly dependent on the hydrogen concentration.

4. Conclusions

In summary, Pd/Ta2O5 Schottky diodes were fabricated on SiC and Si substrates via radio frequency (RF) magnetron sputtering, and their comparative H2 sensing performances were examined in detail under various high temperature conditions. Characterization by atomic force microscopy (AFM) revealed that the roughness of the deposited Ta2O5 film is higher on SiC than on Si. In addition, the resistance of each device was measured at various concentrations of H2 gas. The results revealed that the Pd/Ta2O5 Schottky diode on the SiC substrate is more sensitive than that on the Si substrate. Moreover, the transient responses of the sensors towards various concentrations of H2 gas were investigated, and the SiC-based device exhibited a fast rise time of 7.1 s along with a decay time of 18 s. These results clearly indicate that the sensor based on the SiC substrate has a higher sensitivity towards H2 than that based on the Si substrate. The results further suggest that the Pd/Ta2O5/SiC-based Schottky diode is a rapidly responsive and highly sensitive device for H2 sensing under harsh temperature conditions, thus making it a promising candidate for H2 sensing applications.

Supplementary Materials

The following are available online at https://www.mdpi.com/1424-8220/21/4/1042/s1.

Author Contributions

Designed, carried out experiments, analyzed data, and co-wrote paper, M.H. and W.J. Analyzed data, I.-S.K., K.-K.C., S.H.A.J. and M.A. Co-wrote paper and analyzed data, A.A., T.H. and S.H. Supervised by J.J. All authors have read and agreed to the published version of the manuscript.

Funding

This research was supported by the Nano Material Technology Development Program through the National Research Foundation of Korea (NRF) funded by the Ministry of science, ICT & Future Planning (2016M3A7B4909942, 2016R1D1A1B01015047, 2015M3A7B7045194 as well as NRF-2020R1A6A1A03043435).

Data Availability Statement

No new data were created or analyzed in this study. Data sharing is not applicable to this article.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Zhang, J.; Liu, J.; Peng, Q.; Wang, X.; Li, Y. Nearly monodisperse Cu2O and CuO nanospheres: Preparation and applications for sensitive gas sensors. Chem. Mater. 2006, 18, 867–871. [Google Scholar] [CrossRef]
  2. Caihong, W.; Chu, X.; Wu, M. Highly sensitive gas sensors based on hollow SnO2 spheres prepared by carbon sphere template method. Sens. Actuators B Chem. 2007, 120, 508–513. [Google Scholar] [CrossRef]
  3. Liao, L.; Zhang, Z.; Yan, B.; Zheng, Z.; Bao, Q.; Wu, T.; Li, C.M.; Shen, Z.; Zhang, J.; Gong, H. Multifunctional CuO nanowire devices: P-type field effect transistors and CO gas sensors. Nanotechnology 2009, 20, 085203. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Kolmakov, A.; Klenov, D.; Lilach, Y.; Stemmer, S.; Moskovits, M. Enhanced gas sensing by individual SnO2 nanowires and nanobelts functionalized with Pd catalyst particles. Nano Lett. 2005, 5, 667–673. [Google Scholar] [CrossRef]
  5. Ruan, Q.-J.; Zhang, W.-D. Preparation and gas sensing properties of p-type La-Bi-Fe-O nanorods. Mater. Lett. 2008, 62, 4303–4305. [Google Scholar] [CrossRef]
  6. Yang, D.-J.; Yang, S.-C.; Hong, J.-M.; Lee, H.; Kim, I.-D. Size-dependent photovoltaic property in hollow hemisphere array based dye-sensitized solar cells. J. Electroceram. 2010, 24, 200–204. [Google Scholar] [CrossRef]
  7. Choi, S.-H.; Ankonina, G.; Youn, D.-Y.; Oh, S.-G.; Hong, J.-M.; Rothschild, A.; Kim, I.-D. Hollow ZnO nanofibers fabricated using electrospun polymer templates and their electronic transport properties. ACS Nano 2009, 3, 2623–2631. [Google Scholar] [CrossRef]
  8. Constantinoiu, I.; Viespe, C. Development of Pd/TiO2 Porous Layers by Pulsed Laser Deposition for Surface Acoustic Wave H2 Gas Sensor. Nanomaterials 2020, 10, 760. [Google Scholar] [CrossRef] [Green Version]
  9. Sen, S.; Bhandarkar, V.; Muthe, K.; Roy, M.; Deshpande, S.; Aiyer, R.; Gupta, S.; Yakhmi, J.; Sahni, V. Highly sensitive hydrogen sulphide sensors operable at room temperature. Sens. Actuators B Chem. 2006, 115, 270–275. [Google Scholar] [CrossRef]
  10. Zhang, C.; Boudiba, A.; Navio, C.; Bittencourt, C.; Olivier, M.-G.; Snyders, R.; Debliquy, M. Highly sensitive hydrogen sensors based on co-sputtered platinum-activated tungsten oxide films. Int. J. Hydrog. Energy 2011, 36, 1107–1114. [Google Scholar] [CrossRef]
  11. Miura, N.; Sato, T.; Anggraini, S.A.; Ikeda, H.; Zhuiykov, S. A review of mixed-potential type zirconia-based gas sensors. Ionics 2014, 20, 901–925. [Google Scholar] [CrossRef] [Green Version]
  12. Li, Z.; Yan, S.; Wu, Z.; Li, H.; Wang, J.; Shen, W.; Wang, Z.; Fu, Y. Hydrogen gas sensor based on mesoporous In2O3 with fast response/recovery and ppb level detection limit. Int. J. Hydrog. Energy 2018, 43, 22746–22755. [Google Scholar] [CrossRef]
  13. Motaung, D.E.; Mhlongo, G.H.; Makgwane, P.R.; Dhonge, B.P.; Cummings, F.R.; Swart, H.C.; Ray, S.S. Ultra-high sensitive and selective H2 gas sensor manifested by interface of n–n heterostructure of CeO2-SnO2 nanoparticles. Sens. Actuators B Chem. 2018, 254, 984–995. [Google Scholar] [CrossRef]
  14. Phanichphant, S. Semiconductor metal oxides as hydrogen gas sensors. Procedia Eng. 2014, 87, 795–802. [Google Scholar] [CrossRef] [Green Version]
  15. Wang, Z.; Hu, Y.; Wang, W.; Zhang, X.; Wang, B.; Tian, H.; Wang, Y.; Guan, J.; Gu, H. Fast and highly-sensitive hydrogen sensing of Nb2O5 nanowires at room temperature. Int. J. Hydrog. Energy 2012, 37, 4526–4532. [Google Scholar] [CrossRef]
  16. Kosc, I.; Hotovy, I.; Rehacek, V.; Griesseler, R.; Predanocy, M.; Wilke, M.; Spiess, L. Sputtered TiO2 thin films with NiO additives for hydrogen detection. Appl. Surf. Sci. 2013, 269, 110–115. [Google Scholar] [CrossRef]
  17. Steinebach, H.; Kannan, S.; Rieth, L.; Solzbacher, F. H2 gas sensor performance of NiO at high temperatures in gas mixtures. Sens. Actuators B Chem. 2010, 151, 162–168. [Google Scholar] [CrossRef]
  18. Liu, Y.; Fu, Q.; Stephanopoulos, M. Preferential oxidation of CO in H2 over CuO-CeO2 catalysts. Catal. Today 2004, 93, 241–246. [Google Scholar] [CrossRef]
  19. Wen, Z.; Zhu, L.; Li, Y.; Zhang, Z.; Ye, Z. Mesoporous Co3O4 nanoneedle arrays for high-performance gas sensor. Sens. Actuators B Chem. 2014, 203, 873–879. [Google Scholar] [CrossRef]
  20. Mohd Chachuli, S.A.; Hamidon, M.N.; Mamat, M.; Ertugrul, M.; Abdullah, N.H. A hydrogen gas sensor based on TiO2 nanoparticles on alumina substrate. Sensors 2018, 18, 2483. [Google Scholar] [CrossRef] [Green Version]
  21. Yoon, J.-H.; Kim, B.-J.; Kim, J.-S. Design and fabrication of micro hydrogen gas sensors using palladium thin film. Mater. Chem. Phys. 2012, 133, 987–991. [Google Scholar] [CrossRef]
  22. Fowler, J.D.; Allen, M.J.; Tung, V.C.; Yang, Y.; Kaner, R.B.; Weiller, B.H. Practical chemical sensors from chemically derived graphene. ACS Nano 2009, 3, 301–306. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  23. Schedin, F.; Geim, A.K.; Morozov, S.V.; Hill, E.; Blake, P.; Katsnelson, M.; Novoselov, K.S. Detection of individual gas molecules adsorbed on graphene. Nat. Mater. 2007, 6, 652–655. [Google Scholar] [CrossRef] [PubMed]
  24. Zhang, Y.-H.; Chen, Y.-B.; Zhou, K.-G.; Liu, C.-H.; Zeng, J.; Zhang, H.-L.; Peng, Y. Improving gas sensing properties of graphene by introducing dopants and defects: A first-principles study. Nanotechnology 2009, 20, 185504. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  25. Chen, X.-P.; Yang, N.; Ni, J.-M.; Cai, M.; Ye, H.-Y.; Wong, C.K.; Leung, S.Y.; Ren, T.-L. Density-functional calculation of methane adsorption on graphenes. IEEE Electron. Device Lett. 2015, 36, 1366–1368. [Google Scholar] [CrossRef]
  26. Liu, L.; Yang, Q.; Wang, Z.; Ye, H.; Chen, X.; Fan, X.; Zhang, G. High selective gas detection for small molecules based on germanium selenide monolayer. Appl. Surf. Sci. 2018, 433, 575–581. [Google Scholar] [CrossRef]
  27. Zhang, Z.; Zou, X.; Xu, L.; Liao, L.; Liu, W.; Ho, J.; Xiao, X.; Jiang, C.; Li, J. Hydrogen gas sensor based on metal oxide nanoparticles decorated graphene transistor. Nanoscale 2015, 7, 10078–10084. [Google Scholar] [CrossRef]
  28. Lange, U.; Hirsch, T.; Mirsky, V.M.; Wolfbeis, O.S. Hydrogen sensor based on a graphene–palladium nanocomposite. Electrochim. Acta 2011, 56, 3707–3712. [Google Scholar] [CrossRef]
  29. Kou, L.; Frauenheim, T.; Chen, C. Phosphorene as a superior gas sensor: Selective adsorption and distinct I–V response. J. Phys. Chem. Lett. 2014, 5, 2675–2681. [Google Scholar] [CrossRef] [Green Version]
  30. Baek, D.-H.; Kim, J. MoS2 gas sensor functionalized by Pd for the detection of hydrogen. Sens. Actuators B Chem. 2017, 250, 686–691. [Google Scholar] [CrossRef]
  31. Ouyang, C.; Chen, Y.; Qin, Z.; Zeng, D.; Zhang, J.; Wang, H.; Xie, C. Two-dimensional WS2-based nanosheets modified by Pt quantum dots for enhanced room-temperature NH3 sensing properties. Appl. Surf. Sci. 2018, 455, 45–52. [Google Scholar] [CrossRef]
  32. Kuru, C.; Choi, D.; Kargar, A.; Liu, C.H.; Yavuz, S.; Choi, C.; Jin, S.; Bandaru, P.R. High-performance flexible hydrogen sensor made of WS2 nanosheet–Pd nanoparticle composite film. Nanotechnology 2016, 27, 195501. [Google Scholar] [CrossRef] [PubMed]
  33. Lee, E.; VahidMohammadi, A.; Yoon, Y.S.; Beidaghi, M.; Kim, D.-J. Two-dimensional vanadium carbide MXene for gas sensors with ultrahigh sensitivity toward nonpolar gases. ACS Sens. 2019, 4, 1603–1611. [Google Scholar] [CrossRef] [PubMed]
  34. Soo, M.T.; Cheong, K.Y.; Noor, A.F.M. Advances of SiC-based MOS capacitor hydrogen sensors for harsh environment applications. Sens. Actuators B Chem. 2010, 151, 39–55. [Google Scholar] [CrossRef]
  35. Yu, J.; Chen, G.; Li, C.X.; Shafiei, M.; Ou, J.; du Plessis, J.; Kalantar-zadeh, K.; Lai, P.T.; Wlodarski, W. Hydrogen gas sensing properties of Pt/Ta2O5 Schottky diodes based on Si and SiC substrates. Procedia Eng. 2010, 5, 147–151. [Google Scholar] [CrossRef]
  36. Joo, S.-J.; Choi, J.H.; Kim, S.J.; Kim, S.-C. Pd/Ta2O5/SiC Schottky-diode hydrogen sensors formed by using rapid thermal oxidation of Ta thin films. J. Korean Phys. Soc. 2013, 63, 1794–1798. [Google Scholar] [CrossRef]
  37. Kim, S.; Choi, J.; Jung, M.; Joo, S.; Kim, S. Silicon carbide-based hydrogen gas sensors for high-temperature applications. Sensors 2013, 13, 13575–13583. [Google Scholar] [CrossRef]
  38. Kim, S. Capacitance response characteristics of hydrogen sensor with tantalum oxide dielectric layer. Int. J. Hydrog. Energy 2018, 43, 19810–19815. [Google Scholar] [CrossRef]
  39. Chen, L.-Y.; Hunter, G.W.; Neudeck, P.G.; Bansal, G.; Petit, J.B.; Knight, D. Comparison of interfacial and electronic properties of annealed Pd/SiC and Pd/SiO2/SiC Schottky diode sensors. J. Vac. Sci. Technol. A 1997, 15, 1228–1234. [Google Scholar] [CrossRef]
  40. Atanassova, E.; Tyuliev, G.; Paskaleva, A.; Spassov, D.; Kostov, K. XPS study of N2 annealing effect on thermal Ta2O5 layers on Si. Appl. Surf. Sci. 2004, 225, 86–99. [Google Scholar] [CrossRef]
Figure 1. Fabrication procedure for the Pd/Ta2O5/SiC H2 sensor device.
Figure 1. Fabrication procedure for the Pd/Ta2O5/SiC H2 sensor device.
Sensors 21 01042 g001
Figure 2. Schematic diagrams of (a) the Pd/Ta2O5/SiC H2 sensor, and (b) the setup for the electrical measurements.
Figure 2. Schematic diagrams of (a) the Pd/Ta2O5/SiC H2 sensor, and (b) the setup for the electrical measurements.
Sensors 21 01042 g002
Figure 3. The HRTEM and EDS analysis of the fabricated device: (a) a cross-sectional HRTEM image indicating the film thickness; (b) the cross-sectional HRTEM image used for the EDS mapping analysis; (cg) EDS elemental mappings of: (c) combined elements (d)carbon (C), (e) oxygen (O), (f) silicon (Si), and (g) tantalum (Ta).
Figure 3. The HRTEM and EDS analysis of the fabricated device: (a) a cross-sectional HRTEM image indicating the film thickness; (b) the cross-sectional HRTEM image used for the EDS mapping analysis; (cg) EDS elemental mappings of: (c) combined elements (d)carbon (C), (e) oxygen (O), (f) silicon (Si), and (g) tantalum (Ta).
Sensors 21 01042 g003
Figure 4. The rectifying diode characteristics of the Pd/Ta2O5 Schottky diodes as H2 sensors: (a) and (b) the typical linear I-V curves of the device on (a) the SiC substrate, and (b) the Si substrate, in the presence and absence of H2 gas; (c) and (d) the corresponding logarithmic I-V curves; (e) and (f) the corresponding responses (Ra/Rg) of the sensors as a function of H2 concentration.
Figure 4. The rectifying diode characteristics of the Pd/Ta2O5 Schottky diodes as H2 sensors: (a) and (b) the typical linear I-V curves of the device on (a) the SiC substrate, and (b) the Si substrate, in the presence and absence of H2 gas; (c) and (d) the corresponding logarithmic I-V curves; (e) and (f) the corresponding responses (Ra/Rg) of the sensors as a function of H2 concentration.
Sensors 21 01042 g004
Figure 5. The time-dependent behavior (response and recovery time) of (a) the Pd/Ta2O5/SiC device and (b) the Pd/Ta2O5/SiC device under various H2 concentrations at 300 °C. Rising and recovery time Vs H2 concentration for (c) Pd/Ta2O5/SiC device and (d) the Pd/Ta2O5/Si device
Figure 5. The time-dependent behavior (response and recovery time) of (a) the Pd/Ta2O5/SiC device and (b) the Pd/Ta2O5/SiC device under various H2 concentrations at 300 °C. Rising and recovery time Vs H2 concentration for (c) Pd/Ta2O5/SiC device and (d) the Pd/Ta2O5/Si device
Sensors 21 01042 g005
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Hussain, M.; Jeong, W.; Kang, I.-S.; Choi, K.-K.; Jaffery, S.H.A.; Ali, A.; Hussain, T.; Ayaz, M.; Hussain, S.; Jung, J. Highly Fast Response of Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky Diode-Based Hydrogen Sensors. Sensors 2021, 21, 1042. https://doi.org/10.3390/s21041042

AMA Style

Hussain M, Jeong W, Kang I-S, Choi K-K, Jaffery SHA, Ali A, Hussain T, Ayaz M, Hussain S, Jung J. Highly Fast Response of Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky Diode-Based Hydrogen Sensors. Sensors. 2021; 21(4):1042. https://doi.org/10.3390/s21041042

Chicago/Turabian Style

Hussain, Muhammad, Woonyoung Jeong, Il-Suk Kang, Kyeong-Keun Choi, Syed Hassan Abbas Jaffery, Asif Ali, Tassawar Hussain, Muhammad Ayaz, Sajjad Hussain, and Jongwan Jung. 2021. "Highly Fast Response of Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky Diode-Based Hydrogen Sensors" Sensors 21, no. 4: 1042. https://doi.org/10.3390/s21041042

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.